Title of Invention	"ANTICORROSION COATING COMPOSITION IN AQUEOUS DISPERSION COMPRISING AN ORGANIC TITANATE AND/OR ZIRCONATE "
Abstract	The present invention relates to an anticorrosion coating composition for metallic parts based on particulate metal in aqueous dispersion comprising an organic titanate or zirconate compatible in aqueous phase or in organic phase, optionally a silane-based binder, and water. The present invention likewise relates to an anticorrosion coating of metallic parts obtained from the coating composition according to the invention as well as metallic substrate provided with this anticorrosion coating. The invention additionally relates to an aqueous composition of C1-C8 tetraalkyl titanate, intended for the preparation of a coating composition of a metallic substrate in aqueous dispersion.

Title of Invention

"ANTICORROSION COATING COMPOSITION IN AQUEOUS DISPERSION COMPRISING AN ORGANIC TITANATE AND/OR ZIRCONATE "

Abstract

The present invention relates to an anticorrosion coating composition for metallic parts based on particulate metal in aqueous dispersion comprising an organic titanate or zirconate compatible in aqueous phase or in organic phase, optionally a silane-based binder, and water. The present invention likewise relates to an anticorrosion coating of metallic parts obtained from the coating composition according to the invention as well as metallic substrate provided with this anticorrosion coating. The invention additionally relates to an aqueous composition of C1-C8 tetraalkyl titanate, intended for the preparation of a coating composition of a metallic substrate in aqueous dispersion.

Full Text	Anticorrosion coating composition in aqueous dispersion comprising an organic titanate and/or zirconate The present invention relates to an antlcorrosion coating composition for metal parts, which is based on particulate metal in aqueous dispersion comprising an organic titanate or zirconate compatible' in aqueous phase or in organic phase, optionally a silane-based binder, and water. In the sense of the present invention, the expressions "titanate(s) compatible in organic phase" and "zirconate(s) compatible in organic phase" are understood as meaning every organic titanate and zirconate not compatible with water, that is to say not soluble in an aqueous composition and which in addition is sensitive to moisture and to water (hydrolysis reaction). In the sense of the present invention, the expressions "titanate(s) compatible in aqueous phase" and "zirconate (s) compatible in aqueous phase" are understood as meaning every organic titanate and zirconate compatible with water, that is to say soluble or emulsifiable or dispersible in an aqueous composition. These are generally organic titanates and -organic zirconates which have been stabilized by chelation. They are likewise named "chelated (organic) titanate(s)" and "chelated (organic) zirconate(s)". The organic titanates, as well as the organic zirconates, compatible in organic phase can be used in anhydrous compositions as catalysts, reticulating agents, surface-treatment agents, adhesion promoters or anticorrosion agents. However, these organic titanates, as well as the organic zirconates, have the disadvantage of being very sensitive to water and to moisture inasmuch as they are hydrolysed very rapidly. For example, in the case of the hydrolysis of tetra-n-butyl titanate, the following reactions occurre: 1) conversion of the organic titanate to hydrated titanium oxide Ti(OH)4: Ti(OC4H9)4 + 4H20 --> Ti(OH)4 + 4C4H9OH o 2) then, formation of titanium dioxide TiO2: Ti(OH)4 --> Ti02 + 2H20 In order to avoid the formation of titanium dioxide, the titanates and zirconates compatible in organic phase must thus be employed under rigorously anhydrous conditions. Consequently, the preparation of anhydrous compositions comprising a titanate or a zirconate compatible in organic phase is accompanied by very constraining handling precautions if it is wished to avoid the hydrolysis of the organic titanate to titanium dioxide on contact with air, moisture or traces of water. The moisture .resistance of titanates or zirconates compatible in organic phase can be improved by substituting two alkoxy groups by chelating agents. These chelating agents contain functional groups containing oxygen or nitrogen atoms which happen to stabilize the organic titanate or zirconate. These organic titanates or zirconates in chelated form can likewise be soluble in water, preferably in the presence of a weak acid of the acetic acid type. For example, the patent US 4 495 156 describes titanates in aqueous chelated form (TYZOR AA which is a titanate compatible in organic phase, TYZOR LA and TYZOR TE which are titanates compatible in aqueous phase) which allow the adhesion to a substrate of a composition comprising them to be improved. The hydrolysis rate of the organic titanates and zirconates depends on the size and the complexity of the alkyl group (the more the size of the alkyl group increases, the more the hydrolysis rate decreases) . This is the reason why the organic titanates and zirconates in chelated form are less sensitive to hydrolysis than . the tetraalkyl titanates or the tetra-alkyl zirconates. The patent US 4 224 213 describes coating compositions comprising a short-chain alkyl silicate of formula Si(OR)4, a short-chain alkyl titanate or zirconate and zinc powder. This coating composition is reticulated by reaction of the silicate and the titanate with moisture from the air.' The examples of this patent teach that the addition of silicate allows the moisture resistance of organic titanates to be improved. This coating composition is an organic composition which does not contain any water. The silicate, contrary to the silane, does not allow the adhesion of a composition comprising it to a substrate. The patent EP 0 808 883 describes an aqueous coating composition based on particulate metal, free from chromium, intended to be applied to a substrate. This composition, once applied to the substrate, undergoes hardening in heat in order to provide the said substrate with protection against corrosion. In order to increase the corrosion resistance of this coated substrate, the coated substrate can optionally be coated with a supplementary layer comprising, for example, a silica material. Surprisingly, the inventors have succeeded in incorporating into an aqueous composition organic titanates and/or organic zirconates, whether they are in -chelated or non-chelated form and compatible or not compatible in aqueous phase. They have likewise discovered that the application to a metallic substrate of an aqueous coating composition based on particulate metal comprising- organic titanates and/or organic zirconates allows the resistance to corrosion of the substrate to be improved. The anticorrosion results being sufficient, a substrate coated by such a composition does not need any supplementary layer of anticorrosion coating. In addition, a coating is obtained whose flexibility and resistance to shocks is of very good quality, which is particularly advantageous in the case of anticorrosion coating of screws. The present invention relates to an anticorrosion coating composition of metal parts based on particulate metal in aqueous dispersion comprising, in the following proportions (percentages by mass): - an organic titanate and/or zirconate : 0.3 to 24%; - a particulate metal or a mixture of particulate metals : 10 to 40%; •• a silane-baaed binder : 1 to 25%; - water : q.s.p. 100%; with the condition that the sum of the organic titanate and/or the organic zirconate and of the silane-based binder is between 5 and 25%. The composition advantageously comprises 0.5 to 19% by weight, with respect to the total weight of the composition, of organic titanate and/or zirconate and 1 to 20% by weight, with respect to the total weight of the composition, of silane-based binder, on condition that the sum of organic titanate and/or zirconate and silane-based binder is between 7 and 20% by weight, with respect to the total weight of the composition. The organic titanates can be chosen from the group constituted by the organic titanates compatible in organic phase and the organic titanates compatible in aqueous phase. The titanates compatible in organic phase are advantageously C1-C8 tetraalkyl titanates which can be represented by the following formula (I'): R4-0-Ti-0-R2 O R3 in which Rl, R2, R3 and R4 independently represent an optionally substituted C1-C8 alkyl radical. The C1-C8 tetraalkyl titanate is advantageously chosen from the group comprising tetraethyl titanate (TET, Ti(OC2Hs)4), tetra-n-butyl titanate (TnBT, Ti(OC4H9)4) and octylene glycol titanate (OGT, Ti (O2CBHi7) 4) . The organic titanates compatible in organic phase can likewise be organic titanates in chelated form not compatible with water. As examples of organic titanabes in chelated form not compatible with water (compatible in organic phase), it is especially possible to cite those marketed by Dupont de Nemours under the name TYZOR® AA (titanium acetylacetonate) or TYZOR® DC (diisopropoxy bisethylacetoacetato titanate). The titanates compatible in aqueous phase are advantageously chelated titanates, which can be represented by the following general formula (II): (Formula Removed) in which R and R' independently of one another represent an optionally substituted C1-C8 allcyl radical, X and X' independently represent a functional group comprising an oxygen or nitrogen atom, and Y and Y' independently represent a hydrocarbon chain having 1 to 4 carbon atoms . X and X' advantageously represent an amino or lactate radical . The organic titanate in chelated form compatible in aqueous phase is advantageously chosen from the group constituted by the triethanolamine titanates (TYZOR® TE and TEP marketed by Dupont de Nemours) . As an example of organic titanates in chelated form compatible in aqueous phase, it is likewise possible to cite those marketed by Dupont de Nemours under the name TYZOR® TA (alkanolamine titanate in chelated form) and TYZOR® LA (chelate of titanate and lactic acid) . The organic zirconate can be chosen from the group constituted by the zirconates compatible in organic phase and the zirconates compatible in aqueous phase. The organic zirconates compatible in organic phase are advantageously C1-C10 tetraalkyl zirconates, which can be represented by the following formula (I) : (Formula Removed) in which Rl, R2, R3 and R4 independently represent an optionally substituted C1-C10 alkyl radical . The C1-C10 tetraalkyl zirconate is advantageously chosen from the group constituted by tetra-n-propyl zirconate and tetra-n- butyl zirconate. The organic zirconates compatible in organic phase can likewise be organic zirconates in chelated form not compatible with water. As an example of an organic zirconate in chelated form not compatible with water (compatible in organic phase), it is especially possible to cite those marketed by Dupont de Nemours under the name TYZOR® ZEC (chelated diethyl citrate zirconate). The organic zirconates compatible in aqueous phase are advantageously chelated zirconates which can be represented by the following general formula (II): in which R and R' independently of one another represent an optionally substituted Ci-Ci0 alkyl radical, X and X' independently represent a functional group comprising an oxygen or nitrogen atom, and Y and Y' independently represent a hydrocarbon chain having 1 to 4 carbon atoms. X and X' advantageously represent an amino radical. The chelated organic zirconate can advantageously be triethanolamine zirconate (TYZOR® TEAZ marketed by Dupont de Nemours) . As an example of an organic zirconate in chelated form compatible in aqueous phase, it is likewise possible to cite that marketed by Dupont de Nemours under the name TYZOR® LAZ (chelate of zirconate and lactic acid). The particulate metal of the coating composition can be chosen from the group constituted by the metallic pigments such as aluminium, manganese, nickel, titanium, stainless steel, zinc, their alloys, as well as their mixtures. The particulate metal is advantageously chosen from zinc and aluminium, as well as their alloys and their mixtures or their alloys with manganese, magnesium, tin or Galfan. The particulate metal present in the composition is advantageously in powder form, different homogeneous or heterogeneous geometric structures, especially spherical, lamellar, lenticular forms or other specific forms. The particulate metal advantageously has a particle size of less than 100 µm, even more advantageously less than 40 µm. When the particulate metal is an alloy or a mixture of zinc and aluminium, the aluminium can optionally be present in very small quantities, for example 1 to 5% by weight of the particulate metal, while at the same time nevertheless providing a coating of shiny appearance. Customarily, the aluminium represents at least 10% by weight of the particulate metal, thus the weight ratio of the aluminium to the zinc is of the order of 1:9. On the other hand, for reasons of economy, the aluminium does not represent more than approximately 50% by weight of the total zinc and aluminium, so that the weight ratio of the aluminium to the zinc can reach 1:1. The content of particulate metal of the coating composition will not exceed approximately 40% by weight of the total weight of the composition in order to maintain the best coating appearance and will customarily represent at least 10% by weight in order to obtain a shiny coating appearance. The metal can contain in minor quantity one or more solvents, for example dipropylene glycol and/or white spirit, especially when the metal has been prepared in lamellar form. The particulate metals containing solvents are customarily used in the form of pastes, which can be used directly with other ingredients of the composition. However, the particulate metals can likewise be used in a dry form in the coating composition. The said silane-based binder advantageously comprises a silane carrying at least one hydrolysable function in hydroxyl function chosen from a C1-C4, preferably C1-C2, alkoxy radical. The silane advantageously carries three hydrolysable functions in hydroxyl function, preferably identical. The silane can additionally carry an epoxy (oxirane) function, which favours the reticulation and adhesion to the substrate. "Hydrolysable function in hydroxyl function" is understood as meaning any chemical function capable of reacting with water in order to be converted into a hydroxyl function -OH. The silanes, in the compositions of the present invention, serve as binding agents. They likewise allow the coating bath to be stabilized against a harmful autogenous reaction. The silane seems to bind arid passivate the particulate metal, so that the stability of the bath of the coating composition is improved. In addition, it allows the adhesion of the coating and its resistance to corrosion to be improved. The silane advantageously represents 3 to 20% by weight of the total weight of the composition. The silane is advantageously easily dispersed in the aqueous medium and is, preferably, soluble in such a medium. The silane used is advantageously a silane with an epoxy function chosen from di- or trimethoxysilane with an epoxy function and di- or triethoxysilane with an epoxy function, as well as their mixtures, in particular like beta- (3,4-epoxycyclohexyl) ethyl - trimethoxysilane, 4-(trimethoxysilyl)butane-l, 2-epoxide or gamma-glycidoxypropyltrimethoxysilane. If the organic titanate and/or zirconate used is an organic titanate and/or zirconate compatible in aqueous phase, the silane is advantageously introduced in quantities such that the proportions by mass, in the final composition, of organic titanate and/or zirconate compatible in aqueous phase:silane are between 95:5 and 5:95. The anticorrosion composition can be prepared by mixing an organic phase, especially comprising the silane and the particulate metal, with an aqueous phase, especially comprising water and the silane. The organic titanate and/or zirconate compatible in aqueous phase can be introduced either into the aqueous phase or into the organic phase. When the organic titanate and/or zirconate compatible in aqueous phase is introduced into the organic phase, it is possible to substitute the silane, normally present in the organic phase, by this organic titanate and/or zirconate. The proportions by mass, expressed in dry parts, of organic titanate and/or zirconate and of silane are advantageously between 1:19 and 2:1, more advantageously between 1:16 and 1:8. When the organic titanate and/or zirconate compatible in aqueous phase is introduced into the aqueous phase, it is advantageously first co-hydrolysed with the silane, normally present in the aqueous phase. The mass proportions of organic titanate and/or zirconate and of silane during the co-hydrolysis are advantageously between 0.12 and 0.36, expressed in dry parts. The optimal conditions for the co-hydrolysis are obtained for a ratio by mass of 0.24 titanate and/or zirconate for 1 silane, the ratios being expressed in dry parts. In order to co-hydrolyse the organic titanate and/or zirconate and the silane, the organic titanate and/or zirconate is introduced into the silane, in an appropriate ratio, then they are co-hydrolysed by addition of 200 to 500% of water. It would appear that the duration of the co-hydrolysis reaction, that is to say the waiting time which follows the addition of the water, for example 30 or 90 min, does not have any influence on the properties of the co-hydrolysate obtained. If, instead of co-hydrolysing the silane and the organic titanate and/or zirconate compatible in aqueous phase, they are each hydrolysed separately, less satisfactory results are obtained in terms of product stability. The addition of organic titanate and/or zirconate compatible in aqueous phase in the aqueous phase of the anticorrosion composition improves the anticorrosion properties of this composition more than if this titanate and/or zirconate had been added in the organic phase. If the organic titanate and/or zirconate used is a titanate and/or zirconate compatible in organic phase, advantageously a Ci-CB tetraalkyl titanate and/or zirconate, the silane is advantageously introduced in quantities such that the proportions by mass, in the final composition, of titanate and/or zirconate compatible in organic phase/silane are between 60/40 and 5/95, advantageously between 50/50 and 10/90. The liquid medium of the coating composition is virtually always water or a combination of water and organic solvent. Other solvents can optionally be used but, preferably, only in very small quantities. Typically, the composition comprises 28 to 65% by weight of water, with respect to the total weight of the composition. According to an advantageous embodiment of the invention, the coating composition additionally comprises 1 to 30% by weight of organic solvent or of a mixture of organic solvents, with respect to the total weight of the composition. The organic solvents are advantageously chosen from the group constituted by the glycolic solvents such as the glycol ethers, in particular diethylene glycol, triethylene glycol and dipropylene glycol, the acetates, propylene glycol, polypropylene glycol, nitropropane, the alcohols, the ketones, propylene glycol methyl ether, 2,2,4-trimethyl-l,3-pentanediol isobutyrate .(texanol), white spirit, as well as their mixtures. Dipropylene glycol is particularly advantageous, especially for reasons of economy and of protection of the environment. The quantity of solvents is advantageously lower than 25% by weight, even more advantageously lower than 16% by weight, with respect to the total weight of the composition. When the metallic particles have been prepared in lamellar form in a solvent, the particulate metal resulting can be in the form of paste. It can then form a part of the organic solvent of the composition according to the invention. According to an advantageous embodiment of the invention, the coating composition additionally comprises 0.1 to 7% by weight of molybdenum oxide, with respect to the total weight of the composition. The presence of molybdenum oxide MoOa in the anticorrosion coating composition allows control of the sacrificial protection exerted by the particulate metal in suspension in the composition to be improved. The molybdenum oxide Mo03 is preferably used in an essentially pure orthorhombic crystalline form having a content of molybdenum of greater than approximately 60% by mass. Advantageously, the molybdenum oxide Mo03 will be used in the anticorrosion compositions in the form of particles of dimensions of between 5 and 200 µm. According to an advantageous embodiment of the invention, the coating composition additionally comprises 0.5 to 10% by weight of a reinforcing agent of the anticorrosion properties of the composition chosen from the group constituted by yttrium, zirconium, lanthanum, cerium, praseodymium, in the form of oxides or of salts. The said reinforcing agent of the anticorrosion properties of the composition is advantageously yttrium oxide Y203 or cerium chloride. The said reinforcing agent of the anticorrosion properties of the composition can advantageously be combined with the abovementioned molybdenum oxide, in a mass ratio 0.25 properties: Mo03 agent of the anticorrosion properties: Mo03 advantageously 0.5 properties: Mo03 According to an advantageous embodiment, the coating composition additionally comprises a corrosion inhibitor pigment or corrosion inhibitor pigments such as the tri- or polyphosphate of aluminium, the phosphates, the molybdates, the silicates and borates of zinc, strontium, calcium, barium and their mixtures, at levels of the order of 0.2 to 4% by weight, with respect to the total weight of the coating composition. The coating composition according to the invention can additionally comprise a thickening agent. The thickening agent is advantageously chosen from the group constituted by the cellulosic derivatives such as hydroxymethylcellulose, hydroxyethylcellulose, hydroxy-propylcellulose, cellulose acetobutyrate, xanthan gum, the associative thickeners of polyurethane or acrylic type, the silicates such as the optionally treated silicates of magnesium and/or of lithium or the organophilic clays as well as their mixtures. The content of thickening agent is advantageously lower than 7% by weight with respect to the total weight -of the composition, advantageously between 0.005 and 7% by weight with respect to the total weight of the composition. The coating composition according to the invention can likewise comprise a wetting agent, in a content advantageously lower than 4% by weight, more advantageously between 0.1 and 4% by weight, with respect to the total weight of the composition. The composition according to the invention can also comprise a pH stabilizer such as boric acid, metaboric acid, tetraboric acid and boron oxide or boron salts. The composition can comprise, with respect to the total weight of the composition, 0.1 to 10% by weight, advantageously 0.2 to 5% by weight and even more advantageously 0.4 to 0.8% by weight, of pH stabilizer. The composition can likewise comprise a pH modifier, generally chosen from the oxides and the hydroxides of alkali metals, advantageously lithium and sodium, the oxides and the hydroxides of metals belonging to groups IIA and I IB of the Periodic Table, such as the compounds of strontium, calcium, barium, magnesium and zinc. The pH modifier can likewise be a carbonate or a nitrate of the abovementioned metals. The composition according to the invention can likewise comprise phosphates, substituents containing phosphorus, such as ferrophosphate (pigment), non-organic salts, in quantities lower than 2% by weight with respect to the weight of the composition. The composition according to the invention is advantageously free from chromium VI. The composition can, however, contain chromium in soluble or non-soluble form such as, for example, metallic chromium or chromium of oxidation state III. The composition has good stability on storage, confirming the protective role of the silane towards a harmful reaction of the particulate metal with other ingredients of the composition. The silane likewise allows organic titanate to be stabilized. The present invention likewise relates to the coating obtained by application of the coating composition according to the invention to a substrate, advantageously by spraying, soaking-draining or soaking-centrifugation, the coating layer then being subjected to a baking operation, preferably at a temperature of between 180°C and 350°C, for approximately 10 to 60 minutes, by supply of thermal energy, such as by convection or infrared, or for approximately 30 seconds to 5 minutes by induction. According to an advantageous embodiment, the anticorrosion coating will result from an application operation involving, prior to a baking operation, a drying operation of the coated metallic parts, by supply of thermal energy, such as by convection, infra-red or induction, at a temperature of between 30 and 250°C, advantageously of the order of 70°C, in convection or in infrared for 10 to 30 minutes on line or for approximately 30 seconds to 5 minutes by induction. Before coating, it is judicious in the majority of cases to eliminate the foreign matter from the surface of the substrate, especially by cleaning and careful degreasing. Under these conditions, the thickness of the dry coating film thus applied is between 3 um (11 g/m2) and 30 um (110 g/m2) and preferably between 4 um (15 g/m2) and 12 um (45 g/m2) , more particularly between 5 um (18 g/m2) and 10 um (40 g/m2) . The present invention also extends to the metallic substrate, preferably of steel or steel coated with zinc or with a base layer of zinc deposited by different application methods including mechanical deposition, to cast iron and aluminium, provided with an anticorrosion coating according to the invention applied with the aid of the abovementioned compositions. The metallic substrate can be previously treated, for example by a treatment with chromate or with phosphate. Thus, the substrate can be pretreated in order to have, for example, a phosphate coating of iron in a quantity of 0.1 to 1 g/m2 or a phosphate coating of zinc in a quantity of 1.5 to 4 g/m2. The present invention likewise relates to an aqueous composition of Ci-C8 tetraalkyl titanate and/or of CI-CB tetraalkyl zirconate, intended for the preparation of a coating composition for a metallic substrate in aqueous dispersion, prepared from a water-soluble organic solvent, a binder containing a silane carrying at least one hydrolysable function in hydroxyl function, a Ci-C8 tetraalkyl titanate and/or zirconate and water, in the following proportions (percentages by mass): - water-soluble organic solvent : 0 to 20% - silane-based binder : 20 to 50% - Ci-C8 tetraalkyl titanate and/or zirconate : 5 to 25% - water : 40 to 70% In the context of the present invention, that is to say when the silane is found in the presence of CI-CB tetraalkyl titanate and/or zirconate, it would appear that the silane, in hydrolysed form before condensation, is capable of reacting with the abovementioned hydrated titanium oxide and/or zirconate in order to give a partially stable polymeric chain containing silicon and titanium and/or zirconate atoms. The silane then appears capable of stabilizing the Ci-C8 tetraalkyl titanate and/or zirconate. The chemical reactions could be written as follows: (1) Hydrolysis of the silane: R-Si(OR')3 + 3 H20 ** R-Si(OH)3 -f 3 R'OH (2) Conversion of the organic titanate or zirconate to hydrated titanium or zirconium oxide: X-(OR")4 -f 4 H20 » X(OH)4 + 4 R'OH (3) Reaction between the hydrated titanium or zirconium oxide and the hydrolysed silane: 2 R-Si(OH)3 + X(OH)4 * X(OH)2.2 [R-SiO(OH)23 The silane and the organic titanate or zirconate thus associate in order to form the following partial polymeric chain: X(OH)2.2 [R-SiO(OH)2] The reaction can continue and lead to the formation of a polymeric chain of the following formula (III) : (Formula Removed) in which X represents Ti or Zr. The water-soluble organic solvent is advantageously chosen from the group constituted by the glycolic solvents such as the glycol ethers, in particular diethylene glycol, triethylene glycol and dipropylene glycol, the acetates, propylene glycol, the alcohols, the ketones, propylene glycol ether, as well as their mixtures. The silane carrying at least one hydrblysable function in hydroxyl function contained in the binder is advantageously chosen from a C^-Ci, even more advantageously Ci-C2, alkoxy radical. In addition, this silane advantageously carries an epoxy function. The said silane is preferably chosen from di- or trimethoxysilane with an epoxy function and di- or triethoxysilane with an epoxy function, as well as their mixtures, in particular gamma-glycidoxypropyl-trimethoxysilane or beta-(3,4-epoxycyclohexyl)ethyl-trimethoxysilane. The CI-CB tetraalkyl titanate is advantageously chosen from the group comprising tetra-ethyl titanate (TET), tetra-n-butyl titanate (TnBT) and octyleneglycol titanate (OGT) and the Ci-Ca tetraalkyl zirconate is chosen from the group comprising tetra-n-propyl zirconate and tetra-n-butyl zirconate. In the aqueous composition, the ratio by mass of Ci-Ca tetraalkyl titanate and/or zirconate with respect to the silane is from 60/40 maximum, advantageously to 50/50 maximum, advantageously to 40/60 maximum. The aqueous composition of Ci-Ca tetraalkyl titanate and/or CH-CB tetraalkyl zirconate can be prepared by mixing the silane-based binder, the said titanate or zirconate and, if necessary, the said water-soluble organic solvent, with a small quantity of water and then, by continuous progressive addition, at a low rate, of the remaining quantity of water. In this stabilized form, the Ci-C8 tetraalkyl titanate and/or zirconate can, for example, then be introduced into a coating composition for a metallic substrate in aqueous phase, especially an anticorrosion coating composition based on particulate metal in aqueous dispersion, while limiting the formation of titanium dioxide. The present invention finally relates to the use of the aqueous composition of C1-C8 tetraalkyl titanate and/or C1- C8 tetraalkyl zirconate defined above in pretreatment for coatings or adhesives (polyurethane, acrylic, rubber...). This composition can also be used in posttreatment as a sealer based on metallic particles. This composition can likewise be used in passivation treatment for substrates based on steel, zinc, aluminium or steel covered with a zinc-based coating. This composition can finally be used in an additive in order to improve the adhesion of the coatings or adhesives (polyurethane, acrylic, rubber, ...) in aqueous phase. The examples below show ways in which the present invention can be employed, but do not limit the present invention in any fashion. Preparation of the test panels; Unless indicated otherwise, the test panels are typically stainless steel panels with a low carbon content, laminated in the cold. They can be prepared first of all by immersion in a cleaning solution. Then, the panels can be wiped with a cleaning pad and then rinsed with water and again immersed in the cleaning solution. After removal of the solution, the panels are rinsed with tap water and dried. Application of the coating to the test panels and weight of the coating; The clean parts are coated, in a typical fashion, by dipping then into the coating composition, by withdrawing and draining the composition in excess of this, several times with a moderate stirring action, and then by immediate baking or drying at ambient temperature or pre-hardening at a moderate temperature until the coating is dry to the touch and thus baked. The coating weights (mg/cm2) are determined by comparative weighing before and after coating. Test of resistance to corrosion (ISO 9227) and estimation; The resistance to corrosion of coated parts is measured by means of the standard salt projection test (saline mist) for paints and varnishes ISO 9227. In this test, the parts are placed in a chamber maintained at a constant temperature where they are exposed to a fine projection, (mist) of a 5% saline solution during specific periods of time, rinsed with water and dried. The extent of corrosion of the parts tested can be expressed in the form of the percentage of red rust. Example 1; composition based on organic titanate compatible in organic phase (Table Removed) Zinc in the form of paste to approximately 32% in white spirit 2 Alu Chromal VIII powder marketed by Eckart Werke 3 Y-glycidoxypropyltrimethoxysilane (Crompton) 4 sodium silicate (Rhodia) SlS Ethoxylated nonylphenol of R40 or of R95, supplier Oxiteno SA (Brazil) 7 Kelzan/Rhodopol 23 from Rhodia 8 supplier DuPont de Nemours s supplier Lavollee 10 supplier Cognis SA Example 2; composition based on organic titanate compatible in organic phase (Table Removed) Example 4; process for preparation of an aqueous composition of tetrabutyl titanate, organic titanate compatible in organic phase: The following reagents are mixed in order: a) 30.00 g of DPG (dipropylene glycol) b) 50.00 g of silane A-187 c) 20.00 g of TBT (tetrabutyl titanate) The solution obtained is allowed to stand for 24 hours. The silane, introduced into the DPG before the TnBT, reacts with the water optionally present in the DPG. An uncontrolled reaction of the organic titanate with the water optionally present in the DPG is thus avoided. 100.00 g of water (=100.00 ml) are added respecting the following procedure: i) add 0.125 ml of water dropwise and then allow the solution to stand for 10 minutes; ii) repeat step i) 5 times; iii) add the remaining quantity of water at a rate of 0.25 ml of water/minute/3 pulses, or approximately 0.083 ml of water every 20 seconds. An aqueous composition of colourless organic titanate is obtained. Small crystals can appear; it is assumed that these are silica crystals. The total duration of the preparation of the aqueous composition of organic titanate is approximately 7 h 30 min. The aqueous composition of organic titanate is allowed to stand for at least 24 hours before optionally being introduced into a composition of anticorrosion coating. Example 5; process for preparation of an aqueous composition of organic titanate compatible in organic phase: The process proceeds in the same fashion as in example 4 except that the quantity of TnBT introduced is 30.00 g. An aqueous composition of colourless or sometimes slightly yellow organic titanate is obtained. Example 6; process for preparation of an aqueous composition of organic titanate compatible in organic phase: The process proceeds in the same fashion as in example 4 except that the quantity of TnBT introduced is 40.00 g. An aqueous composition of colourless or sometimes slightly yellow organic titanate is obtained. Example 7; process for preparation of an aqueous composition of organic titanate compatible in organic phase: The process proceeds in. the same fashion as in example 4 except that the quantity of TnBT introduced is 40.00 g and the quantity of silane A 187 introduced is 70.00 g. An aqueous composition of colourless or sometimes slightly yellow organic titanate is obtained. Example 8: corrosion resistance of a coating composition according to the invention based on organic titanate compatible in organic phase The aqueous composition of organic titanate obtained in example 6 is introduced into an anticorrosion coating composition. Table 6 below indicates the formulation of the composition thus obtained and that of an anticorrosion coating composition of the prior art which do not contains organi c tit anat e. (Table Removed) The characteristics of composition A are reported in table 7 below: (Table Removed) The resistance of the two compositions to the saline mist is compared. The resistance values to the saline mist measured are summarized in table 8 below. (Table Removed) Satisfactory results for resistance to the saline mist are thus observed for the coating composition according to the invention. In fact, for a layer density of 24 g/m2, it is possible to attain a duration of resistance to the saline mist of greater than 1000 hours whereas for a composition without organic titanate the duration of resistance to the .saline mist is only 312 hours. The addition of organic titanate allows the corrosion resistance of the coating to be at least tripled under these conditions. Example 9; composition based on organic titanate compatible in organic phase The addition of small quantities of organic titanate (10, 20 or 30 g/kg) allows the quantity of silane and of molybdenum oxide to be introduced to be decreased, which allows a limitation of the costs, while conserving good anticorrosion results. In the following examples of compositions (table 9) , the quantity of silane is reduced to 44% by weight and the quantity of molybdenum oxide is reduced to 20% by weight, with respect to the quantities conventionally- introduced into anticorrosion coating compositions. (Table Removed) The values of resistance to the saline mist measured are summarized in table 10 below. (Table Removed) Example 10; process of introduction of chelated organic titanates or zirconates, compatible in aqueous phase, into an aqueous phase - co-hydrolysis with the silane: a) titanates i) preparation of the aqueous phase; 10 parts by weight of TYZOR® TEP (supplied by DuPont de Nemours, 60% dry extract) and 25 parts by weight of silane A-187 are mixed with magnetic stirring for one hour. 113 parts by weight of water are then added rapidly and the magnetic stirring is maintained for one hour. This mixture is then introduced into an aqueous composition constituted of 350 parts by weight of water, 8.8 parts by weight of sodium silicate, 8.2 parts by weight of boric acid and 9 parts by weight of molybdenum oxide. ii) composition of the organic phase; The organic phase contains: wetting agent of ethoxylated nonylphenol type (CECA) 13 wetting agent of ethoxylated nonylphenol type (CECA) 14 80% Chromal VIII in dipropylene glycol, marketed by Eckart Werke 15 hydrocarbon-type antifoam (Schwegman) 16 Y2O3 of purity equal to 99.99% 17 anti-sedimentation agent of silica type (Degussa) iii) results of the saline mist tests: - Bath according to the invention: anticorrosion coating composition according to the invention: the organic and aqueous phases obtained (steps ii) and i), respectively) are mixed. Reference bath: reference composition: The aqueous phase of the reference composition contains: Water 463 parts by weight Sodium silicate 20 N 32 8.8 parts by weight Boric acid 8.2 parts by weight Molybdenum oxide 9 parts by weight Silane A 187 31 parts by weight The organic phase of the reference composition has the same composition as the organic phase of the bath according to the invention (step ii)) . The saline mist tests are carried out after an ageing of the baths, according to the invention and reference, of the order of 48 hours. The results obtained are given in table 11 below: (Table Removed) a V + CM: saline mist results after the screws had been subjected to the mechanical shocks of vibrations and falls. b 2 x G: saline mist results after the screws or the plates had been subjected twice to chipping, that is to say a spattering of impacts. ° Sacrificial protection: number of hours of exposure to the saline mist, without red rust after incision of the coating to the metal. d notation 5: results corresponding to less than 1% of red rust on surface. e notation 4.8: results corresponding to less than 5% of red rust on surface. Table 11 makes it appear clear that the introduction of chelated organic titanate, compatible in aqueous phase, co- hydrolysed with the silane in the coating compositions increases the good behaviour to saline mist of the samples treated by these compositions. We Claim: 1. Anticorrosion coating composition of metallic parts based on particulate metal in aqueous dispersion comprising, in the following proportions (percentages by mass): - an organic titanate and/or zirconate: 0.3 to 24%; - a particulate metal or a mixture of particulate metals: 10 to 40%; - a silane-based binder : 1 to 25%; - water: q.s.p. 100%; wherein the sum of the organic titanate and/or zirconate and of the silane-based binder is between 5 and 25%; and wherein the organic titanate is selected from the group constituted by C1-C8 tetraalkyle titanate of formula: (Formula Removed) in which R1, R2, R3 and R4 independently represent an optionally substituted C1-C8 alkyl radical, and wherein the organic zirconate is selected from the group constituted by C1-C10 tetraalkyle zirconate of formula: (Formula Removed) in which R1, R2, R3 and R4 independently represent an optionally substituted C1-C10 alkyl radical. 2. The composition as claimed claim 1, wherein the C1-C8 tetraalkyl titanate, is chosen from the group consisting of tetraethyl titanate, tetra-n-butyl titanate and octylene glycol titanate, and the C1-C10 tetraalkyl zirconate, is chosen from the group consisting of tetra- n-propyl zirconate and tetra-n-butyl zirconate. 3. The composition as claimed in any one of the preceding claims, wherein the particulate metal is chosen from zinc and aluminium, as well as their alloys and their mixtures or their alloys with manganese, magnesium, tin or Galfan. 4. The composition as claimed in any one of the preceding claims, wherein the silane-based binder comprises a silane carrying at least one hydrolysable function in hydroxyl function chosen from a C1-C4 alkoxy radical. 5. The composition as claimed in any one of the preceding claims, wherein the silane additionally carries an epoxy function. 6. The composition as claimed in claim 5, wherein the silane is chosen from di- or trimethoxysilane with an epoxy function or di- or triethoxysilane with an epoxy function, as well as their mixtures, in particular gamma- . glycidoxypropyltrimethoxysilane or beta-(3,4-epoxycyclohexyl) ethyltrimethoxysilane. 7. The composition as claimed in any one of the preceding claims, wherein it additionally comprises 1 to 30% by weight of organic solvent or of a mixture of organic solvents, with respect to the total weight of the composition. 8. The composition as claimed in claim 7, wherein the organic solvent is chosen from the group constituted by the glycolic solvents such as the glycol ethers, in particular diethylene glycol, triethylene glycol and dipropylene glycol, the acetates, propylene glycol, polypropylene glycol, nitropropane, the alcohols, the ketones, propylene glycol methyl ether, 2,2,4-trimethyl-l,3-pentanediol isobutyrate (texanol), white spirit, as well as their mixtures. 9. The composition as claimed in any one of the preceding claims, wherein said composition additionally comprises 0.1 to 7% by weight of molybdenum oxide, with respect to the total weight of the composition. 10. The composition as claimed in any one of the preceding claims, wherein said composition additionally comprises 0.5 to 10% by weight, with respect to the total weight of the composition, of a reinforcing agent of the anticorrosion properties chosen from the group constituted by yttrium, zirconium, lanthanum, cerium, praseodymium, in the form of oxides or of salts, advantageously yttrium oxide Y2O3, or 0.2 to 4% by weight, with respect to the total weight of the composition, of a corrosion inhibitor pigment such as aluminium triphosphate. 11. The composition as claimed in any one of the preceding claims, wherein the composition additionally comprises a thickening agent, advantageously 0.005 to 7% by weight with respect to the total weight of the composition, and/or a wetting agent, advantageously 0.1 to 4% by weight with respect to the total weight of the composition. 12. Anticorrosion coating of metallic parts, wherein said coating is obtained from a coating composition as claimed in any one of claims 1 to 11, by spraying, soaking-draining or soaking-centrifugation, the coating layer then being subjected to a baking operation by supply of thermal energy, such as by convection, infrared or induction, preferably carried out at a temperature of between 180°C and 350°C, for approximately 10 to 60 minutes by convection or infra-red, or for 30 seconds to 5 minutes by induction. 13. Anticorrosion coating of metallic parts as claimed in claim 12, wherein, prior to a baking operation, the coated metallic parts are subjected to a drying operation by supply of thermal energy, such as by convection, infrared or induction, especially at a temperature of between 30 and 250°C by convection or approximately 10 to 30 minutes on line or by induction for 30 seconds to 5 minutes. 14. Anticorrosion coating of metallic parts as claimed in claims 12 or 13, wherein said coating is applied to the metallic parts to be protected, with a thickness of the dry film of between 3 µm (11 g/m2) and 30 µm (110 g/m2) and preferably between 4 µm (15 g/m2) and 12 µm (45 g/m2), more particularly between 5 µm (18 g/m2) and 10 µm (40 g/m2). 15. Metallic substrate, preferably of steel or of zinc-coated steel or of a base layer of zinc deposited by different methods of application including mechanical deposition, of cast-iron or of aluminium, provided with an anticorrosion coating as claimed in any one of claims 12 to 14. 16. Aqueous composition of C1-C8 tetraalkyl titanate and/or zirconate intended for the preparation of a coating composition as claimed in any one of claim 1 to 11 for a metallic substrate in aqueous dispersion, prepared from a water-soluble organic solvent, from a binder containing a silane carrying at least one hydrolysable function in hydroxyl function, from a titanate or zirconate compatible in organic phase and from water, in the following proportions (percentages by mass): - water-soluble organic solvent: 0 to 20% - silane-based binder : 20 to 50% - C1-C8 tetraalkyl titanate and/orzirconate: 5 to 25% -water: qsp 100%. 17. Composition as claimed in claim 16, wherein the water-soluble organic solvent is chosen from the group constituted by the glycolic solvents such as the glycol ethers, in particular diethylene glycol, triethylene glycol and dipropylene glycol, the acetates, propylene glycol, propylene glycol methyl ether, the alcohols, the ketones, as well as their mixtures. 18. Composition as claimed in claims 16 and 17, wherein the binder comprises a silane carrying at least one hydrolysable function in hydroxyl function chosen from a C1-C4 alkoxy radical. 19. Composition as claimed in any one of claims 16 to 18, wherein the silane additionally carries an epoxy function. 20. Composition as claimed in claim 19, wherein the silane is chosen from di- or trimethoxysilane with an epoxy function and di- or triethoxysilane with an epoxy function, as well as their mixtures, in particular gamma-glycidoxy-propyltrimethoxysilane or beta-(3,4-epoxycyclohexyl)-ethyltrimethoxysilane. 21. Composition as claimed in any one of claims 16 to 20, wherein the C1-C8 tetraalkyl titanate is advantageously chosen from the group comprising tetraethyl titanate, tetra-n-butyl titanate and octylene glycol titanate, and the C1-C8 tetraalkyl zirconate is advantageously chosen from the group comprising tetra-n-propyl zirconate and tetra-n-butyl zirconate. 22. The composition as claimed in any one of claims 16 to 21, for use in pre-treatment for adhesives or coatings, in post-treatment as a sealer based on metallic particles, in passivation treatment for substrates based on steel, zinc, aluminium or steel covered with a zinc-based coating, or in an additive for improving the adhesion of coatings or adhesives in aqueous phase.

Full Text

Anticorrosion coating composition in aqueous dispersion comprising an organic titanate and/or zirconate
The present invention relates to an antlcorrosion coating composition for metal parts, which is based on particulate metal in aqueous dispersion comprising an organic titanate or zirconate compatible' in aqueous phase or in organic phase, optionally a silane-based binder, and water.
In the sense of the present invention, the expressions "titanate(s) compatible in organic phase" and "zirconate(s) compatible in organic phase" are understood as meaning every organic titanate and zirconate not compatible with water, that is to say not soluble in an aqueous composition and which in addition is sensitive to moisture and to water (hydrolysis reaction).
In the sense of the present invention, the expressions "titanate(s) compatible in aqueous phase" and "zirconate (s) compatible in aqueous phase" are understood as meaning every organic titanate and zirconate compatible with water, that is to say soluble or emulsifiable or dispersible in an aqueous composition. These are generally organic titanates and -organic zirconates which have been stabilized by chelation. They are likewise named "chelated (organic) titanate(s)" and "chelated (organic) zirconate(s)". The organic titanates, as well as the organic zirconates, compatible in organic phase can be used in anhydrous compositions as catalysts, reticulating agents, surface-treatment agents, adhesion promoters or anticorrosion agents. However, these organic titanates, as well as the organic zirconates, have the disadvantage of being very sensitive to water and to moisture inasmuch as they are hydrolysed very rapidly. For example, in the case of the

hydrolysis of tetra-n-butyl titanate, the following reactions occurre:
1) conversion of the organic titanate to hydrated titanium
oxide Ti(OH)4:
Ti(OC4H9)4 + 4H20 --> Ti(OH)4 + 4C4H9OH
o
2) then, formation of titanium dioxide TiO2:
Ti(OH)4 --> Ti02 + 2H20
In order to avoid the formation of titanium dioxide, the titanates and zirconates compatible in organic phase must thus be employed under rigorously anhydrous conditions. Consequently, the preparation of anhydrous compositions comprising a titanate or a zirconate compatible in organic phase is accompanied by very constraining handling precautions if it is wished to avoid the hydrolysis of the organic titanate to titanium dioxide on contact with air, moisture or traces of water.
The moisture .resistance of titanates or zirconates
compatible in organic phase can be improved by substituting
two alkoxy groups by chelating agents. These chelating
agents contain functional groups containing oxygen or
nitrogen atoms which happen to stabilize the organic
titanate or zirconate. These organic titanates or
zirconates in chelated form can likewise be soluble in
water, preferably in the presence of a weak acid of the
acetic acid type. For example, the patent US 4 495 156
describes titanates in aqueous chelated form (TYZOR AA
which is a titanate compatible in organic phase, TYZOR LA
and TYZOR TE which are titanates compatible in aqueous
phase) which allow the adhesion to a substrate of a
composition comprising them to be improved.
The hydrolysis rate of the organic titanates and zirconates depends on the size and the complexity of the alkyl group

(the more the size of the alkyl group increases, the more the hydrolysis rate decreases) . This is the reason why the organic titanates and zirconates in chelated form are less sensitive to hydrolysis than . the tetraalkyl titanates or the tetra-alkyl zirconates.
The patent US 4 224 213 describes coating compositions comprising a short-chain alkyl silicate of formula Si(OR)4, a short-chain alkyl titanate or zirconate and zinc powder. This coating composition is reticulated by reaction of the silicate and the titanate with moisture from the air.' The examples of this patent teach that the addition of silicate allows the moisture resistance of organic titanates to be improved. This coating composition is an organic composition which does not contain any water. The silicate, contrary to the silane, does not allow the adhesion of a composition comprising it to a substrate.
The patent EP 0 808 883 describes an aqueous coating composition based on particulate metal, free from chromium, intended to be applied to a substrate. This composition, once applied to the substrate, undergoes hardening in heat in order to provide the said substrate with protection against corrosion. In order to increase the corrosion resistance of this coated substrate, the coated substrate can optionally be coated with a supplementary layer comprising, for example, a silica material.
Surprisingly, the inventors have succeeded in incorporating into an aqueous composition organic titanates and/or organic zirconates, whether they are in -chelated or non-chelated form and compatible or not compatible in aqueous phase. They have likewise discovered that the application to a metallic substrate of an aqueous coating composition

based on particulate metal comprising- organic titanates and/or organic zirconates allows the resistance to corrosion of the substrate to be improved. The anticorrosion results being sufficient, a substrate coated by such a composition does not need any supplementary layer of anticorrosion coating. In addition, a coating is obtained whose flexibility and resistance to shocks is of very good quality, which is particularly advantageous in the case of anticorrosion coating of screws.
The present invention relates to an anticorrosion coating composition of metal parts based on particulate metal in aqueous dispersion comprising, in the following proportions (percentages by mass):
- an organic titanate and/or zirconate : 0.3 to 24%;
- a particulate metal or a mixture of particulate metals :
10 to 40%;
•• a silane-baaed binder : 1 to 25%;
- water : q.s.p. 100%;
with the condition that the sum of the organic titanate and/or the organic zirconate and of the silane-based binder is between 5 and 25%.
The composition advantageously comprises 0.5 to 19% by weight, with respect to the total weight of the composition, of organic titanate and/or zirconate and 1 to 20% by weight, with respect to the total weight of the composition, of silane-based binder, on condition that the sum of organic titanate and/or zirconate and silane-based binder is between 7 and 20% by weight, with respect to the total weight of the composition.
The organic titanates can be chosen from the group constituted by the organic titanates compatible in organic phase and the organic titanates compatible in aqueous

phase.
The titanates compatible in organic phase are advantageously C1-C8 tetraalkyl titanates which can be represented by the following formula (I'):
R4-0-Ti-0-R2 O R3
in which Rl, R2, R3 and R4 independently represent an optionally substituted C1-C8 alkyl radical. The C1-C8 tetraalkyl titanate is advantageously chosen from the group comprising tetraethyl titanate (TET, Ti(OC2Hs)4), tetra-n-butyl titanate (TnBT, Ti(OC4H9)4) and octylene glycol titanate (OGT, Ti (O2CBHi7) 4) .
The organic titanates compatible in organic phase can likewise be organic titanates in chelated form not compatible with water. As examples of organic titanabes in chelated form not compatible with water (compatible in organic phase), it is especially possible to cite those marketed by Dupont de Nemours under the name TYZOR® AA (titanium acetylacetonate) or TYZOR® DC (diisopropoxy bisethylacetoacetato titanate).
The titanates compatible in aqueous phase are advantageously chelated titanates, which can be represented by the following general formula (II):
(Formula Removed)
in which R and R' independently of one another represent an optionally substituted C1-C8 allcyl radical, X and X' independently represent a functional group comprising an oxygen or nitrogen atom, and Y and Y' independently represent a hydrocarbon chain having 1 to 4 carbon atoms . X and X' advantageously represent an amino or lactate radical .
The organic titanate in chelated form compatible in aqueous phase is advantageously chosen from the group constituted by the triethanolamine titanates (TYZOR® TE and TEP marketed by Dupont de Nemours) . As an example of organic titanates in chelated form compatible in aqueous phase, it is likewise possible to cite those marketed by Dupont de Nemours under the name TYZOR® TA (alkanolamine titanate in chelated form) and TYZOR® LA (chelate of titanate and lactic acid) .
The organic zirconate can be chosen from the group constituted by the zirconates compatible in organic phase and the zirconates compatible in aqueous phase. The organic zirconates compatible in organic phase are advantageously C1-C10 tetraalkyl zirconates, which can be represented by the following formula (I) :
(Formula Removed)
in which Rl, R2, R3 and R4 independently represent an optionally substituted C1-C10 alkyl radical . The C1-C10 tetraalkyl zirconate is advantageously chosen from the group constituted by tetra-n-propyl zirconate and tetra-n-
butyl zirconate.
The organic zirconates compatible in organic phase can likewise be organic zirconates in chelated form not compatible with water. As an example of an organic zirconate in chelated form not compatible with water (compatible in organic phase), it is especially possible to cite those marketed by Dupont de Nemours under the name TYZOR® ZEC (chelated diethyl citrate zirconate). The organic zirconates compatible in aqueous phase are advantageously chelated zirconates which can be represented by the following general formula (II):
in which R and R' independently of one another represent an optionally substituted Ci-Ci0 alkyl radical, X and X' independently represent a functional group comprising an oxygen or nitrogen atom, and Y and Y' independently represent a hydrocarbon chain having 1 to 4 carbon atoms. X and X' advantageously represent an amino radical. The chelated organic zirconate can advantageously be triethanolamine zirconate (TYZOR® TEAZ marketed by Dupont de Nemours) . As an example of an organic zirconate in chelated form compatible in aqueous phase, it is likewise possible to cite that marketed by Dupont de Nemours under the name TYZOR® LAZ (chelate of zirconate and lactic acid).
The particulate metal of the coating composition can be chosen from the group constituted by the metallic pigments such as aluminium, manganese, nickel, titanium, stainless
steel, zinc, their alloys, as well as their mixtures. The particulate metal is advantageously chosen from zinc and aluminium, as well as their alloys and their mixtures or their alloys with manganese, magnesium, tin or Galfan. The particulate metal present in the composition is advantageously in powder form, different homogeneous or heterogeneous geometric structures, especially spherical, lamellar, lenticular forms or other specific forms. The particulate metal advantageously has a particle size of less than 100 µm, even more advantageously less than 40 µm. When the particulate metal is an alloy or a mixture of zinc and aluminium, the aluminium can optionally be present in very small quantities, for example 1 to 5% by weight of the particulate metal, while at the same time nevertheless providing a coating of shiny appearance. Customarily, the aluminium represents at least 10% by weight of the particulate metal, thus the weight ratio of the aluminium to the zinc is of the order of 1:9. On the other hand, for reasons of economy, the aluminium does not represent more than approximately 50% by weight of the total zinc and aluminium, so that the weight ratio of the aluminium to the zinc can reach 1:1. The content of particulate metal of the coating composition will not exceed approximately 40% by weight of the total weight of the composition in order to maintain the best coating appearance and will customarily represent at least 10% by weight in order to obtain a shiny coating appearance.
The metal can contain in minor quantity one or more solvents, for example dipropylene glycol and/or white spirit, especially when the metal has been prepared in lamellar form. The particulate metals containing solvents are customarily used in the form of pastes, which can be used directly with other ingredients of the composition.
However, the particulate metals can likewise be used in a dry form in the coating composition.
The said silane-based binder advantageously comprises a silane carrying at least one hydrolysable function in hydroxyl function chosen from a C1-C4, preferably C1-C2, alkoxy radical. The silane advantageously carries three hydrolysable functions in hydroxyl function, preferably identical. The silane can additionally carry an epoxy (oxirane) function, which favours the reticulation and adhesion to the substrate. "Hydrolysable function in hydroxyl function" is understood as meaning any chemical function capable of reacting with water in order to be converted into a hydroxyl function -OH.
The silanes, in the compositions of the present invention, serve as binding agents. They likewise allow the coating bath to be stabilized against a harmful autogenous reaction. The silane seems to bind arid passivate the particulate metal, so that the stability of the bath of the coating composition is improved. In addition, it allows the adhesion of the coating and its resistance to corrosion to be improved. The silane advantageously represents 3 to 20% by weight of the total weight of the composition. The silane is advantageously easily dispersed in the aqueous medium and is, preferably, soluble in such a medium. The silane used is advantageously a silane with an epoxy function chosen from di- or trimethoxysilane with an epoxy function and di- or triethoxysilane with an epoxy function, as well as their mixtures, in particular like beta- (3,4-epoxycyclohexyl) ethyl - trimethoxysilane, 4-(trimethoxysilyl)butane-l, 2-epoxide or gamma-glycidoxypropyltrimethoxysilane. If the organic titanate and/or zirconate used is an organic
titanate and/or zirconate compatible in aqueous phase, the silane is advantageously introduced in quantities such that the proportions by mass, in the final composition, of organic titanate and/or zirconate compatible in aqueous phase:silane are between 95:5 and 5:95.
The anticorrosion composition can be prepared by mixing an organic phase, especially comprising the silane and the particulate metal, with an aqueous phase, especially comprising water and the silane. The organic titanate and/or zirconate compatible in aqueous phase can be introduced either into the aqueous phase or into the organic phase.
When the organic titanate and/or zirconate compatible in aqueous phase is introduced into the organic phase, it is possible to substitute the silane, normally present in the organic phase, by this organic titanate and/or zirconate. The proportions by mass, expressed in dry parts, of organic titanate and/or zirconate and of silane are advantageously between 1:19 and 2:1, more advantageously between 1:16 and 1:8.
When the organic titanate and/or zirconate compatible in aqueous phase is introduced into the aqueous phase, it is advantageously first co-hydrolysed with the silane, normally present in the aqueous phase. The mass proportions of organic titanate and/or zirconate and of silane during the co-hydrolysis are advantageously between 0.12 and 0.36, expressed in dry parts. The optimal conditions for the co-hydrolysis are obtained for a ratio by mass of 0.24 titanate and/or zirconate for 1 silane, the ratios being expressed in dry parts.
In order to co-hydrolyse the organic titanate and/or zirconate and the silane, the organic titanate and/or zirconate is introduced into the silane, in an appropriate
ratio, then they are co-hydrolysed by addition of 200 to 500% of water. It would appear that the duration of the co-hydrolysis reaction, that is to say the waiting time which follows the addition of the water, for example 30 or 90 min, does not have any influence on the properties of the co-hydrolysate obtained. If, instead of co-hydrolysing the silane and the organic titanate and/or zirconate compatible in aqueous phase, they are each hydrolysed separately, less satisfactory results are obtained in terms of product stability.
The addition of organic titanate and/or zirconate compatible in aqueous phase in the aqueous phase of the anticorrosion composition improves the anticorrosion properties of this composition more than if this titanate and/or zirconate had been added in the organic phase. If the organic titanate and/or zirconate used is a titanate and/or zirconate compatible in organic phase, advantageously a Ci-CB tetraalkyl titanate and/or zirconate, the silane is advantageously introduced in quantities such that the proportions by mass, in the final composition, of titanate and/or zirconate compatible in organic phase/silane are between 60/40 and 5/95, advantageously between 50/50 and 10/90.
The liquid medium of the coating composition is virtually always water or a combination of water and organic solvent. Other solvents can optionally be used but, preferably, only in very small quantities. Typically, the composition comprises 28 to 65% by weight of water, with respect to the total weight of the composition.
According to an advantageous embodiment of the invention, the coating composition additionally comprises 1 to 30% by weight of organic solvent or of a mixture of organic
solvents, with respect to the total weight of the composition. The organic solvents are advantageously chosen from the group constituted by the glycolic solvents such as the glycol ethers, in particular diethylene glycol, triethylene glycol and dipropylene glycol, the acetates, propylene glycol, polypropylene glycol, nitropropane, the alcohols, the ketones, propylene glycol methyl ether, 2,2,4-trimethyl-l,3-pentanediol isobutyrate .(texanol), white spirit, as well as their mixtures.
Dipropylene glycol is particularly advantageous, especially for reasons of economy and of protection of the environment. The quantity of solvents is advantageously lower than 25% by weight, even more advantageously lower than 16% by weight, with respect to the total weight of the composition. When the metallic particles have been prepared in lamellar form in a solvent, the particulate metal resulting can be in the form of paste. It can then form a part of the organic solvent of the composition according to the invention.
According to an advantageous embodiment of the invention, the coating composition additionally comprises 0.1 to 7% by weight of molybdenum oxide, with respect to the total weight of the composition. The presence of molybdenum oxide MoOa in the anticorrosion coating composition allows control of the sacrificial protection exerted by the particulate metal in suspension in the composition to be improved. The molybdenum oxide Mo03 is preferably used in an essentially pure orthorhombic crystalline form having a content of molybdenum of greater than approximately 60% by mass. Advantageously, the molybdenum oxide Mo03 will be used in the anticorrosion compositions in the form of particles of dimensions of between 5 and 200 µm.
According to an advantageous embodiment of the invention,
the coating composition additionally comprises 0.5 to 10%
by weight of a reinforcing agent of the anticorrosion
properties of the composition chosen from the group
constituted by yttrium, zirconium, lanthanum, cerium,
praseodymium, in the form of oxides or of salts. The said
reinforcing agent of the anticorrosion properties of the
composition is advantageously yttrium oxide Y203 or cerium
chloride. The said reinforcing agent of the anticorrosion
properties of the composition can advantageously be
combined with the abovementioned molybdenum oxide, in a
mass ratio 0.25 properties: Mo03 agent of the anticorrosion properties: Mo03 advantageously 0.5 properties: Mo03 According to an advantageous embodiment, the coating composition additionally comprises a corrosion inhibitor pigment or corrosion inhibitor pigments such as the tri- or polyphosphate of aluminium, the phosphates, the molybdates, the silicates and borates of zinc, strontium, calcium, barium and their mixtures, at levels of the order of 0.2 to 4% by weight, with respect to the total weight of the coating composition.
The coating composition according to the invention can additionally comprise a thickening agent. The thickening agent is advantageously chosen from the group constituted by the cellulosic derivatives such as hydroxymethylcellulose, hydroxyethylcellulose, hydroxy-propylcellulose, cellulose acetobutyrate, xanthan gum, the associative thickeners of polyurethane or acrylic type, the silicates such as the optionally treated silicates of magnesium and/or of lithium or the organophilic clays as
well as their mixtures. The content of thickening agent is advantageously lower than 7% by weight with respect to the total weight -of the composition, advantageously between 0.005 and 7% by weight with respect to the total weight of the composition.
The coating composition according to the invention can likewise comprise a wetting agent, in a content advantageously lower than 4% by weight, more advantageously between 0.1 and 4% by weight, with respect to the total weight of the composition.
The composition according to the invention can also comprise a pH stabilizer such as boric acid, metaboric acid, tetraboric acid and boron oxide or boron salts. The composition can comprise, with respect to the total weight of the composition, 0.1 to 10% by weight, advantageously 0.2 to 5% by weight and even more advantageously 0.4 to 0.8% by weight, of pH stabilizer.
The composition can likewise comprise a pH modifier, generally chosen from the oxides and the hydroxides of alkali metals, advantageously lithium and sodium, the oxides and the hydroxides of metals belonging to groups IIA and I IB of the Periodic Table, such as the compounds of strontium, calcium, barium, magnesium and zinc. The pH modifier can likewise be a carbonate or a nitrate of the abovementioned metals.
The composition according to the invention can likewise comprise phosphates, substituents containing phosphorus, such as ferrophosphate (pigment), non-organic salts, in quantities lower than 2% by weight with respect to the weight of the composition.
The composition according to the invention is advantageously free from chromium VI. The composition can, however, contain chromium in soluble or non-soluble form
such as, for example, metallic chromium or chromium of oxidation state III.
The composition has good stability on storage, confirming the protective role of the silane towards a harmful reaction of the particulate metal with other ingredients of the composition. The silane likewise allows organic titanate to be stabilized.
The present invention likewise relates to the coating obtained by application of the coating composition according to the invention to a substrate, advantageously by spraying, soaking-draining or soaking-centrifugation, the coating layer then being subjected to a baking operation, preferably at a temperature of between 180°C and 350°C, for approximately 10 to 60 minutes, by supply of thermal energy, such as by convection or infrared, or for approximately 30 seconds to 5 minutes by induction. According to an advantageous embodiment, the anticorrosion coating will result from an application operation involving, prior to a baking operation, a drying operation of the coated metallic parts, by supply of thermal energy, such as by convection, infra-red or induction, at a temperature of between 30 and 250°C, advantageously of the order of 70°C, in convection or in infrared for 10 to 30 minutes on line or for approximately 30 seconds to 5 minutes by induction. Before coating, it is judicious in the majority of cases to eliminate the foreign matter from the surface of the substrate, especially by cleaning and careful degreasing. Under these conditions, the thickness of the dry coating film thus applied is between 3 um (11 g/m2) and 30 um (110 g/m2) and preferably between 4 um (15 g/m2) and 12 um (45 g/m2) , more particularly between 5 um (18 g/m2) and 10 um (40 g/m2) . The present invention also extends to the metallic
substrate, preferably of steel or steel coated with zinc or with a base layer of zinc deposited by different application methods including mechanical deposition, to cast iron and aluminium, provided with an anticorrosion coating according to the invention applied with the aid of the abovementioned compositions.
The metallic substrate can be previously treated, for example by a treatment with chromate or with phosphate. Thus, the substrate can be pretreated in order to have, for example, a phosphate coating of iron in a quantity of 0.1 to 1 g/m2 or a phosphate coating of zinc in a quantity of 1.5 to 4 g/m2.
The present invention likewise relates to an aqueous composition of Ci-C8 tetraalkyl titanate and/or of CI-CB tetraalkyl zirconate, intended for the preparation of a coating composition for a metallic substrate in aqueous dispersion, prepared from a water-soluble organic solvent, a binder containing a silane carrying at least one hydrolysable function in hydroxyl function, a Ci-C8 tetraalkyl titanate and/or zirconate and water, in the following proportions (percentages by mass):
- water-soluble organic solvent : 0 to 20%
- silane-based binder : 20 to 50%
- Ci-C8 tetraalkyl titanate and/or zirconate : 5 to 25%
- water : 40 to 70%
In the context of the present invention, that is to say when the silane is found in the presence of CI-CB tetraalkyl titanate and/or zirconate, it would appear that the silane, in hydrolysed form before condensation, is capable of reacting with the abovementioned hydrated titanium oxide and/or zirconate in order to give a partially stable polymeric chain containing silicon and
titanium and/or zirconate atoms. The silane then appears capable of stabilizing the Ci-C8 tetraalkyl titanate and/or zirconate. The chemical reactions could be written as follows:
(1) Hydrolysis of the silane:
R-Si(OR')3 + 3 H20 ** R-Si(OH)3 -f 3 R'OH
(2) Conversion of the organic titanate or zirconate to
hydrated titanium or zirconium oxide:
X-(OR")4 -f 4 H20 *» X(OH)4 + 4 R'OH
(3) Reaction between the hydrated titanium or
zirconium oxide and the hydrolysed silane:
2 R-Si(OH)3 + X(OH)4 ** X(OH)2.2 [R-SiO(OH)23
The silane and the organic titanate or zirconate thus associate in order to form the following partial polymeric chain: X(OH)2.2 [R-SiO(OH)2]
The reaction can continue and lead to the formation of a polymeric chain of the following formula (III) :
(Formula Removed)
in which X represents Ti or Zr.
The water-soluble organic solvent is advantageously chosen from the group constituted by the glycolic solvents such as the glycol ethers, in particular diethylene glycol, triethylene glycol and dipropylene glycol, the acetates, propylene glycol, the alcohols, the ketones, propylene glycol ether, as well as their mixtures.
The silane carrying at least one hydrblysable function in hydroxyl function contained in the binder is advantageously
chosen from a C^-Ci, even more advantageously Ci-C2, alkoxy radical. In addition, this silane advantageously carries an epoxy function. The said silane is preferably chosen from di- or trimethoxysilane with an epoxy function and di- or triethoxysilane with an epoxy function, as well as their mixtures, in particular gamma-glycidoxypropyl-trimethoxysilane or beta-(3,4-epoxycyclohexyl)ethyl-trimethoxysilane.
The CI-CB tetraalkyl titanate is advantageously chosen from the group comprising tetra-ethyl titanate (TET), tetra-n-butyl titanate (TnBT) and octyleneglycol titanate (OGT) and the Ci-Ca tetraalkyl zirconate is chosen from the group comprising tetra-n-propyl zirconate and tetra-n-butyl zirconate. In the aqueous composition, the ratio by mass of Ci-Ca tetraalkyl titanate and/or zirconate with respect to the silane is from 60/40 maximum, advantageously to 50/50 maximum, advantageously to 40/60 maximum.
The aqueous composition of Ci-Ca tetraalkyl titanate and/or CH-CB tetraalkyl zirconate can be prepared by mixing the silane-based binder, the said titanate or zirconate and, if necessary, the said water-soluble organic solvent, with a small quantity of water and then, by continuous progressive addition, at a low rate, of the remaining quantity of water.
In this stabilized form, the Ci-C8 tetraalkyl titanate and/or zirconate can, for example, then be introduced into a coating composition for a metallic substrate in aqueous phase, especially an anticorrosion coating composition based on particulate metal in aqueous dispersion, while limiting the formation of titanium dioxide.
The present invention finally relates to the use of the aqueous composition of C1-C8 tetraalkyl titanate and/or C1-
C8 tetraalkyl zirconate defined above in pretreatment for coatings or adhesives (polyurethane, acrylic, rubber...). This composition can also be used in posttreatment as a sealer based on metallic particles. This composition can likewise be used in passivation treatment for substrates based on steel, zinc, aluminium or steel covered with a zinc-based coating. This composition can finally be used in an additive in order to improve the adhesion of the coatings or adhesives (polyurethane, acrylic, rubber, ...) in aqueous phase.
The examples below show ways in which the present invention can be employed, but do not limit the present invention in any fashion.
Preparation of the test panels;
Unless indicated otherwise, the test panels are typically stainless steel panels with a low carbon content, laminated in the cold. They can be prepared first of all by immersion in a cleaning solution. Then, the panels can be wiped with a cleaning pad and then rinsed with water and again immersed in the cleaning solution. After removal of the solution, the panels are rinsed with tap water and dried.
Application of the coating to the test panels and weight of the coating;
The clean parts are coated, in a typical fashion, by dipping then into the coating composition, by withdrawing and draining the composition in excess of this, several times with a moderate stirring action, and then by immediate baking or drying at ambient temperature or pre-hardening at a moderate temperature until the coating is dry to the touch and thus baked. The coating weights

(mg/cm2) are determined by comparative weighing before and after coating.
Test of resistance to corrosion (ISO 9227) and estimation; The resistance to corrosion of coated parts is measured by means of the standard salt projection test (saline mist) for paints and varnishes ISO 9227. In this test, the parts are placed in a chamber maintained at a constant temperature where they are exposed to a fine projection, (mist) of a 5% saline solution during specific periods of time, rinsed with water and dried. The extent of corrosion of the parts tested can be expressed in the form of the percentage of red rust.
Example 1; composition based on organic titanate compatible in organic phase
(Table Removed)
Zinc in the form of paste to approximately 32% in white spirit
2 Alu Chromal VIII powder marketed by Eckart Werke
3 Y-glycidoxypropyltrimethoxysilane (Crompton)
4 sodium silicate (Rhodia)
SlS Ethoxylated nonylphenol of R40 or of R95, supplier Oxiteno SA (Brazil)
7 Kelzan/Rhodopol 23 from Rhodia
8 supplier DuPont de Nemours
s supplier Lavollee
10 supplier Cognis SA
Example 2; composition based on organic titanate compatible in organic phase
(Table Removed)
Example 4; process for preparation of an aqueous composition of tetrabutyl titanate, organic titanate compatible in organic phase:
The following reagents are mixed in order:
a) 30.00 g of DPG (dipropylene glycol)
b) 50.00 g of silane A-187

c) 20.00 g of TBT (tetrabutyl titanate)
The solution obtained is allowed to stand for 24 hours. The silane, introduced into the DPG before the TnBT, reacts with the water optionally present in the DPG. An uncontrolled reaction of the organic titanate with the water optionally present in the DPG is thus avoided. 100.00 g of water (=100.00 ml) are added respecting the following procedure:
i) add 0.125 ml of water dropwise and then allow the solution to stand for 10 minutes; ii) repeat step i) 5 times;
iii) add the remaining quantity of water at a rate of 0.25 ml of water/minute/3 pulses, or approximately 0.083 ml of water every 20 seconds.
An aqueous composition of colourless organic titanate is obtained. Small crystals can appear; it is assumed that these are silica crystals.
The total duration of the preparation of the aqueous composition of organic titanate is approximately 7 h 30 min.
The aqueous composition of organic titanate is allowed to stand for at least 24 hours before optionally being introduced into a composition of anticorrosion coating.
Example 5; process for preparation of an aqueous composition of organic titanate compatible in organic phase:
The process proceeds in the same fashion as in example 4 except that the quantity of TnBT introduced is 30.00 g. An aqueous composition of colourless or sometimes slightly yellow organic titanate is obtained.
Example 6; process for preparation of an aqueous composition of organic titanate compatible in organic phase:
The process proceeds in the same fashion as in example 4 except that the quantity of TnBT introduced is 40.00 g. An aqueous composition of colourless or sometimes slightly yellow organic titanate is obtained.
Example 7; process for preparation of an aqueous composition of organic titanate compatible in organic phase:
The process proceeds in. the same fashion as in example 4 except that the quantity of TnBT introduced is 40.00 g and the quantity of silane A 187 introduced is 70.00 g. An aqueous composition of colourless or sometimes slightly yellow organic titanate is obtained.
Example 8: corrosion resistance of a coating composition according to the invention based on organic titanate compatible in organic phase
The aqueous composition of organic titanate obtained in example 6 is introduced into an anticorrosion coating composition. Table 6 below indicates the formulation of the composition thus obtained and that of an anticorrosion coating composition of the prior art which do not contains organi c tit anat e.
(Table Removed)
The characteristics of composition A are reported in table 7 below:
(Table Removed)
The resistance of the two compositions to the saline mist is compared. The resistance values to the saline mist measured are summarized in table 8 below.
(Table Removed)
Satisfactory results for resistance to the saline mist are thus observed for the coating composition according to the invention. In fact, for a layer density of 24 g/m2, it is possible to attain a duration of resistance to the saline mist of greater than 1000 hours whereas for a composition without organic titanate the duration of resistance to the .saline mist is only 312 hours. The addition of organic titanate allows the corrosion resistance of the coating to be at least tripled under these conditions.
Example 9; composition based on organic titanate compatible in organic phase
The addition of small quantities of organic titanate (10, 20 or 30 g/kg) allows the quantity of silane and of
molybdenum oxide to be introduced to be decreased, which allows a limitation of the costs, while conserving good anticorrosion results.
In the following examples of compositions (table 9) , the quantity of silane is reduced to 44% by weight and the quantity of molybdenum oxide is reduced to 20% by weight, with respect to the quantities conventionally- introduced into anticorrosion coating compositions.
(Table Removed)

The values of resistance to the saline mist measured are summarized in table 10 below.

(Table Removed)

Example 10; process of introduction of chelated organic titanates or zirconates, compatible in aqueous phase, into an aqueous phase - co-hydrolysis with the silane:
a) titanates
i) preparation of the aqueous phase;
10 parts by weight of TYZOR® TEP (supplied by DuPont de Nemours, 60% dry extract) and 25 parts by weight of silane A-187 are mixed with magnetic stirring for one hour. 113 parts by weight of water are then added rapidly and the magnetic stirring is maintained for one hour. This mixture is then introduced into an aqueous composition constituted of 350 parts by weight of water, 8.8 parts by weight of sodium silicate, 8.2 parts by weight of boric acid and 9 parts by weight of molybdenum oxide. ii) composition of the organic phase; The organic phase contains:
wetting agent of ethoxylated nonylphenol type (CECA)
13 wetting agent of ethoxylated nonylphenol type (CECA)
14 80% Chromal VIII in dipropylene glycol, marketed by Eckart Werke
15 hydrocarbon-type antifoam (Schwegman)
16 Y2O3 of purity equal to 99.99%
17 anti-sedimentation agent of silica type (Degussa)
iii) results of the saline mist tests:
- Bath according to the invention: anticorrosion
coating composition according to the invention: the
organic and aqueous phases obtained (steps ii) and
i), respectively) are mixed.
Reference bath: reference composition:
The aqueous phase of the reference composition contains:
Water 463 parts by weight
Sodium silicate 20 N 32 8.8 parts by weight
Boric acid 8.2 parts by weight
Molybdenum oxide 9 parts by weight
Silane A 187 31 parts by weight
The organic phase of the reference composition has the same composition as the organic phase of the bath according to the invention (step ii)) .
The saline mist tests are carried out after an ageing of the baths, according to the invention and reference, of the order of 48 hours. The results obtained are given in table 11 below:
(Table Removed)
a V + CM: saline mist results after the screws had been
subjected to the mechanical shocks of vibrations and falls.
b 2 x G: saline mist results after the screws or the plates
had been subjected twice to chipping, that is to say a
spattering of impacts.
° Sacrificial protection: number of hours of exposure to
the saline mist, without red rust after incision of the
coating to the metal.
d notation 5: results corresponding to less than 1% of red
rust on surface.
e notation 4.8: results corresponding to less than 5% of
red rust on surface.
Table 11 makes it appear clear that the introduction of
chelated organic titanate, compatible in aqueous phase, co-
hydrolysed with the silane in the coating compositions
increases the good behaviour to saline mist of the samples
treated by these compositions.

We Claim:
1. Anticorrosion coating composition of metallic parts based on particulate metal in
aqueous dispersion comprising, in the following proportions (percentages by mass):
- an organic titanate and/or zirconate: 0.3 to 24%;
- a particulate metal or a mixture of particulate metals: 10 to 40%;
- a silane-based binder : 1 to 25%;
- water: q.s.p. 100%;
wherein the sum of the organic titanate and/or zirconate and of the silane-based binder is between 5 and 25%; and
wherein the organic titanate is selected from the group constituted by C1-C8 tetraalkyle titanate of formula:
(Formula Removed)
in which R1, R2, R3 and R4 independently represent an optionally substituted C1-C8 alkyl
radical,
and wherein the organic zirconate is selected from the group constituted by C1-C10
tetraalkyle zirconate of formula:
(Formula Removed)
in which R1, R2, R3 and R4 independently represent an optionally substituted C1-C10 alkyl radical.
2. The composition as claimed claim 1, wherein the C1-C8 tetraalkyl titanate, is chosen
from the group consisting of tetraethyl titanate, tetra-n-butyl titanate and octylene glycol
titanate, and the C1-C10 tetraalkyl zirconate, is chosen from the group consisting of tetra-
n-propyl zirconate and tetra-n-butyl zirconate.
3. The composition as claimed in any one of the preceding claims, wherein the particulate metal is chosen from zinc and aluminium, as well as their alloys and their mixtures or their alloys with manganese, magnesium, tin or Galfan.
4. The composition as claimed in any one of the preceding claims, wherein the silane-based binder comprises a silane carrying at least one hydrolysable function in hydroxyl function chosen from a C1-C4 alkoxy radical.
5. The composition as claimed in any one of the preceding claims, wherein the silane additionally carries an epoxy function.
6. The composition as claimed in claim 5, wherein the silane is chosen from di- or trimethoxysilane with an epoxy function or di- or triethoxysilane with an epoxy function, as well as their mixtures, in particular gamma- . glycidoxypropyltrimethoxysilane or beta-(3,4-epoxycyclohexyl) ethyltrimethoxysilane.
7. The composition as claimed in any one of the preceding claims, wherein it additionally comprises 1 to 30% by weight of organic solvent or of a mixture of organic solvents, with respect to the total weight of the composition.
8. The composition as claimed in claim 7, wherein the organic solvent is chosen from the group constituted by the glycolic solvents such as the glycol ethers, in particular diethylene glycol, triethylene glycol and dipropylene glycol, the acetates, propylene glycol, polypropylene glycol, nitropropane, the alcohols, the ketones, propylene glycol methyl ether, 2,2,4-trimethyl-l,3-pentanediol isobutyrate (texanol), white spirit, as well as their mixtures.
9. The composition as claimed in any one of the preceding claims, wherein said composition additionally comprises 0.1 to 7% by weight of molybdenum oxide, with respect to the total weight of the composition.
10. The composition as claimed in any one of the preceding claims, wherein said composition additionally comprises 0.5 to 10% by weight, with respect to the total
weight of the composition, of a reinforcing agent of the anticorrosion properties chosen from the group constituted by yttrium, zirconium, lanthanum, cerium, praseodymium, in the form of oxides or of salts, advantageously yttrium oxide Y2O3, or 0.2 to 4% by weight, with respect to the total weight of the composition, of a corrosion inhibitor pigment such as aluminium triphosphate.
11. The composition as claimed in any one of the preceding claims, wherein the composition additionally comprises a thickening agent, advantageously 0.005 to 7% by weight with respect to the total weight of the composition, and/or a wetting agent, advantageously 0.1 to 4% by weight with respect to the total weight of the composition.
12. Anticorrosion coating of metallic parts, wherein said coating is obtained from a coating composition as claimed in any one of claims 1 to 11, by spraying, soaking-draining or soaking-centrifugation, the coating layer then being subjected to a baking operation by supply of thermal energy, such as by convection, infrared or induction, preferably carried out at a temperature of between 180°C and 350°C, for approximately 10 to 60 minutes by convection or infra-red, or for 30 seconds to 5 minutes by induction.
13. Anticorrosion coating of metallic parts as claimed in claim 12, wherein, prior to a baking operation, the coated metallic parts are subjected to a drying operation by supply of thermal energy, such as by convection, infrared or induction, especially at a temperature of between 30 and 250°C by convection or approximately 10 to 30 minutes on line or by induction for 30 seconds to 5 minutes.
14. Anticorrosion coating of metallic parts as claimed in claims 12 or 13, wherein said coating is applied to the metallic parts to be protected, with a thickness of the dry film of between 3 µm (11 g/m2) and 30 µm (110 g/m2) and preferably between 4 µm (15 g/m2) and 12 µm (45 g/m2), more particularly between 5 µm (18 g/m2) and 10 µm (40 g/m2).
15. Metallic substrate, preferably of steel or of zinc-coated steel or of a base layer of zinc deposited by different methods of application including mechanical deposition, of cast-iron or of aluminium, provided with an anticorrosion coating as claimed in any one of claims 12 to 14.
16. Aqueous composition of C1-C8 tetraalkyl titanate and/or zirconate intended for the
preparation of a coating composition as claimed in any one of claim 1 to 11 for a
metallic substrate in aqueous dispersion, prepared from a water-soluble organic solvent,
from a binder containing a silane carrying at least one hydrolysable function in hydroxyl
function, from a titanate or zirconate compatible in organic phase and from water, in the
following proportions (percentages by mass):
- water-soluble organic solvent: 0 to 20%
- silane-based binder : 20 to 50%
- C1-C8 tetraalkyl titanate and/orzirconate: 5 to 25% -water: qsp 100%.

17. Composition as claimed in claim 16, wherein the water-soluble organic solvent is chosen from the group constituted by the glycolic solvents such as the glycol ethers, in particular diethylene glycol, triethylene glycol and dipropylene glycol, the acetates, propylene glycol, propylene glycol methyl ether, the alcohols, the ketones, as well as their mixtures.
18. Composition as claimed in claims 16 and 17, wherein the binder comprises a silane carrying at least one hydrolysable function in hydroxyl function chosen from a C1-C4 alkoxy radical.
19. Composition as claimed in any one of claims 16 to 18, wherein the silane additionally carries an epoxy function.
20. Composition as claimed in claim 19, wherein the silane is chosen from di- or trimethoxysilane with an epoxy function and di- or triethoxysilane with an epoxy function, as well as their mixtures, in particular gamma-glycidoxy-propyltrimethoxysilane or beta-(3,4-epoxycyclohexyl)-ethyltrimethoxysilane.
21. Composition as claimed in any one of claims 16 to 20, wherein the C1-C8 tetraalkyl titanate is advantageously chosen from the group comprising tetraethyl titanate, tetra-n-butyl titanate and octylene glycol titanate, and the C1-C8 tetraalkyl zirconate is advantageously chosen from the group comprising tetra-n-propyl zirconate and tetra-n-butyl zirconate.
22. The composition as claimed in any one of claims 16 to 21, for use in pre-treatment for adhesives or coatings, in post-treatment as a sealer based on metallic particles, in passivation treatment for substrates based on steel, zinc, aluminium or steel covered with a zinc-based coating, or in an additive for improving the adhesion of coatings or adhesives in aqueous phase.

"ANTICORROSION COATING COMPOSITION IN AQUEOUS DISPERSION COMPRISING AN ORGANIC TITANATE AND/OR ZIRCONATE "