Title of Invention

METHOD FOR MANUFACTURING EPITAXIAL WAFER

Abstract The invention relates to a method for manufacturing an epitaxial wafer comprising : a step of providing a single crystal ingot;a step of slicing a silicon single crystal ingot to obtain a thin discoid wafer; a step of supplying an etchant to the wafer surface by rotating the wafer in a horizontal direction; a smoothing step of controlling supply of the etchant in accordance with a shape of the wafer and spreading the supplied etchant on the entire surface of the rotating wafer by a centrifugal force to smooth the wafer surface, wherein the supply of the acid etchant to the surface of the wafer is carried out by measuring the shape of the wafer by detecting means, and storing the shape of the wafer in a memory and controlling a position of a nozzle for supplying an acid etching and a discharge time of an acid etchant from the nozzle in accordance with the stored shape of the wafer, and on the basis of the control; and an epitaxial layer forming step of forming an epitaxial layer formed of a silicon single crystal on the surface of the wafer based on epitaxial growth.
Full Text DESCRIPTION
METHOD FOR MANUFACTURING EPITAXIAL WAFER
TECHNICAL FIELD
[0001]
The present invention relates to a method for
manufacturing an epitaxial wafer that applies an etchant to
a surface of a semiconductor wafer to smooth the surface,
thereby improving efficiency of formation of an epitaxial
layer.
BACKGROUND ART
[0002]
As shown in FIG. 13, in a conventional manufacturing
process for an epitaxial layer, a distal end and a proximal
end of a grown silicon single crystal ingot are cut off to
provide a block shape, an outer diameter of the ingot is
ground in order to uniform a diameter of the ingot so that
a block body can be obtained, an orientation flat or an
orientation notch is formed to this block body to indicate
a specific crystal orientation, and then the block body is
sliced with a predeterminedl angle with respect to a rod
axis direction (a step 1). A wafer peripheral portion of
the sliced wafer is chamfered to avoid a crack or a chip of
the wafer peripheral portion (a step 2). Subsequently,
double disk surface grinding (which will be referred to as

DDSG hereinafter) that allows both front and rear surfaces
of the silicon wafer to be ground is applied as a smoothing
step (a step 3). Then, single disk surface grinding (which
will be referred to as SDSG hereinafter) that allows the
front surface alone of the wafer to be ground or allows the
front and rear surfaces of the wafer to be ground one by
one is carried out (a step 4). Subsequently, double disk
surface polishing (which will be referred to as DSP
hereinafter) that allows both the front and rear surfaces
of the wafer to be simultaneously polished is effected (a
step 5). Then, single disk surface polishing (which will
be referred to as SMP hereinafter) that allows the front
surface alone of the wafer to be polished or allows the
front and rear surfaces of the wafer to be polished one by
one is carried out (a step 6). Further, when an epitaxial
layer made of a silicon single crystal is formed on the
surface of the wafer by epitaxial growth (a step 7), a
desired epitaxial wafer can be obtained.
[0003]
However, the conventional manufacturing process has
the following problem.
When machining processing, e.g., slicing or grinding
is applied, a mechanical damage or a machining scratch is
necessarily formed on the wafer. Since an epitaxial layer
forming step based on epitaxial growth is a process that
emphasizes a scratch or a damage (a distortion of a crystal
lattice) present on the wafer surface, a crystal defect,

e.g., a dislocation or a stacking fault occurs in the
epitaxial layer with a defective part caused due to
machining processing such as grinding as a starting point,
and this defect is elicited as a surface defect on an
epitaxial layer surface in some cases. Furthermore, when a
scratch or a machining damage caused due to machining
processing is serious, a slip may occur in the formed
epitaxial layer. Moreover, since the number of steps to
manufacture an epitaxial layer is large, a throughput is
reduced and a cost is increased.
[0004]
In order to solve this problem, there is disclosed a
method for manufacturing a silicon epitaxial wafer
characterized by performing a vapor growth step of growing
a silicon single crystal thin film from vapor on a silicon
single crystal substrate; a step of effecting water
polishing; and a polishing step using an abrasive in the
mentioned order (see, e.g., Patent Document 1). In this
method disclosed in Patent Document 1, a silicon single
crystal substrate before the vapor growth step is obtained
as follows. First, a silicon single crystal ingot is cut
into a block, subjected to external-diameter grinding, and
then sliced. Subsequently, outer rims on both surfaces of
the sliced silicon single crystal wafer are chamfered, and
then both the surfaces are lapped by using a loose abrasive.
The lapping wafer is immersed in an etchant to chemically
etch both the surfaces, thereby obtaining a chemically

etched wafer. This chemically etched wafer is determined
as the silicon single crystal substrate, and a silicon
single crystal thin film is grown from vapor on this
substrate. In the method disclosed in Patent Document 1,
occurrence of a scratch defect due to a protruding defect
formed on the surface of the vapor-grown silicon single
crystal thin film can be suppressed, and a height of this
protruding defect can be reduced.
Patent Document 1: Japanese Examined Patent
Application Publication No. 2002-43255 (claim 1, paragraphs
[0006] and [0013] to [0015])
DISCLOSURE OF INVENTION
PROBLEM TO BE SOLVED BY THE INVENTION
[0005]
However, in the manufacturing method disclosed in
Patent Document 1, since immersion type etching is carried
out, an entire wafer surface is uniformly etched, control
over a removal amount in a wafer plane to effect shape
control, e.g., obtaining a predetermined surface shape
cannot be performed in a wafer plane, and hence a surface
state, e.g., a flatness degree is hard to be improved even
though it may become worse before lapping/grinding at the
previous step. Further, smoothing processing based on
machining, e.g., lapping is applied before vapor growth of
the silicon single crystal thin film, a mechanical damage
or a processing scratch necessarily occurs on the wafer,

and occurrence of a surface defect or a slip formed on an
epitaxial layer cannot be sufficiently reduced even though
subsequent water polishing or polishing using an abrasive
is applied.
It is an object of the present invention to provide a
method for manufacturing an epitaxial layer that applies an
etchant to a surface of a semiconductor wafer to smooth the
surface, thereby reducing occurrence of a surface defect or
a slip formed on an epitaxial layer.
MEANS FOR SOLVING PROBLEM
[0006]
The present inventors have revealed that performing a
smoothing step of applying an etchant to a silicon wafer
under specific conditions or an epitaxial layer forming
step allows reducing occurrence of a surface defect or a
slip formed on an epitaxial layer.
The present invention provides a method for
manufacturing an epitaxial layer comprising: a smoothing
step of controlling application of an etchant in accordance
with a surface shape of a silicon wafer to smooth the wafer
surface; and an epitaxial layer forming step of forming an
epitaxial layer formed of a silicon single crystal on the
surface of the wafer based on epitaxial growth.
EFFECT OF THE INVENTION
[0007]

The method for manufacturing an epitaxial layer
according to the present invention can demonstrate an
effect that controlling application of an etchant to a
wafer surface in accordance with a shape of the wafer
surface allows smoothing the wafer surface. Furthermore,
since the smoothing processing for the wafer surface is
chemical processing that applies an etchant to the wafer
without including a mechanical element and a scratch or a
damage rarely occurs on the wafer, occurrence of a surface
defect or a slip formed on an epitaxial layer due to
machining can be decreased.
BRIEF DESCRIPTION OF DRAWINGS
[0008]
FIG. 1 is a view showing a method for manufacturing an
epitaxial wafer according to an embodiment of the present
invention;
FIG. 2 is a view showing a method for manufacturing an
epitaxial wafer according to another embodiment of the
present invention;
FIG. 3 is a view showing a method for manufacturing an
epitaxial wafer according to still another embodiment of
the present invention;
FIG. 4 is a view showing a single-wafer processing
type etching device;
FIG. 5 is a view showing a surface defect evaluation
result in a surface layer of an epitaxial layer according

to Example 1;
FIG. 6 is a view showing a surface defect evaluation
result in a surface layer of an epitaxial layer according
to Example 2;
FIG. 7 is a view showing a surface defect evaluation
result in a surface layer of an epitaxial layer according
to Example 3;
FIG. 8 is a view showing a surface defect evaluation
result in a surface layer of an epitaxial layer according
to Comparative Example 1;
FIG. 9 is a view showing a topograph of the epitaxial
wafer according to Example 1 imaged based on X-ray
topography;
FIG. 10 is a view showing a topograph of the epitaxial
wafer according to Example 2 imaged based on X-ray
topography;
FIG. 11 is a view showing a topograph of the epitaxial
wafer according to Example 3 imaged based on X-ray
topography;
FIG. 12 is a view showing a topograph of the epitaxial
wafer according to Comparative Example 1 imaged based on X-
ray topography; and
FIG. 13 is a view showing a conventional method for
manufacturing an epitaxial wafer.
EXPLANATIONS OF LETTERS OR NUMERALS
[0009]

11 slicing
12 smoothing processing
13 epitaxial layer formation
14 mirror polishing
BEST MODE(S) FOR CARRYING OUT THE INVENTION
[0010]
The best mode for carrying out the present invention
will now be described with reference to the accompanying
drawings.
First, a distal end and a proximal end of a grown
silicon single crystal ingot are cut off to provide a block
shape, and an external diameter of the ingot is ground to
uniform a diameter of the ingot, thereby providing a block
body. An orientation flat or an orientation notch is
formed to this block body to indicate a specific crystal
orientation. After this process, as shown in FIG. 1, the
block body is sliced with a predetermined angle with
respect to a rod axis direction (a step 11).
[0011]
Irregular layers on front and rear surfaces of a thin
discoid silicon wafer produced in a process such as slicing
are ground down by machining, e.g., grinding or lapping to
enhance a flatness degree of the front and rear surfaces of
the wafer and a parallelism degree of the wafer in a
conventional manufacturing process for a wafer, but in a
manufacturing method according to this embodiment, this

smoothing step based on machining is not performed, and
application of an etchant is first controlled in accordance
with a silicon wafer surface shape after slicing, whereby
the wafer surface is smoothed (a step 12) .
[0012]
At the smoothing step 12, irregular layers on both
front and rear surfaces of the silicon wafer produced at a
step of, e.g., slicing are smoothed by etching to enhance a
flatness degree of the front and rear surfaces of the wafer
and a parallelism degree of the wafer. Furthermore, an
affected layer introduced due to a machining process, e.g.,
block cutting, external-diameter grinding, or the slicing
step 11 is completely removed. Moreover, the use of an
acid etchant as an etchant utilized in smoothing allows
controlling surface roughness of the wafer.
[0013]
This smoothing step 12 is carried out by using such an
etching device 20 as shown in FIG. 4.
The single-wafer processing etching device 20 depicted
in FIG. 4 has a stage 22 that supports a wafer 21, and a
rotation driving source 24, e.g., a motor that is connected
with the stage 22 via a rotary shaft 23 and drives the
stage 22 to rotate through the rotary shaft 23, and these
members constitute wafer rotating means 25.
[0014]
Moreover, the single-wafer processing etching device
20 has etchant supplying means 26 for supplying an etchant,

a nozzle 27 that receives the etchant from this etchant
supplying means 26 and belches out the etchant to the wafer
21, a nozzle base portion 28 that movably supports this
nozzle 27, and a guide portion 29 that restricts a
position/movement of the nozzle base portion 28, and these
members constitute nozzle position controlling means 30.
To the nozzle base portion 28 are provided a mechanism that
adjusts an angle of the nozzle 27 with respect to the
nozzle base portion 28, a mechanism that adjusts a height
position of a distal end of the nozzle 27 from the wafer 21,
and a mechanism that switches discharge/non-discharge of
the etchant from the nozzle 27, and these members
constitute discharge state controlling means 31.
[0015]
Additionally, the single-wafer processing etching
device 20 has controlling means 32 that controls the number
of revolutions of the rotation driving source 24 to set a
water revolution number, controls the etchant supplying
means 26 to specify a supply state of the etchant, and
controls the nozzle position controlling means 30 and the
discharge state controlling means 31 to set a state/a
position of the nozzle 27. This controlling means 32 has
an arithmetic portion 33, e.g., a CPU and a plurality of
memories 34, 35.... Reference numeral 36 denotes wafer
surface detecting means that utilizes laser reflection on
the wafer surface based on a laser reflection mode to
measure irregularities on the wafer surface. The detecting

means 36 may measure a wafer surface shape as an
independent device without being disposed in the single-
wafer processing etching device 20.
[0016]
The etchant supplying means 26 supplies an acid
etchant to the nozzle 27. The etchant supplying means 26
may previously mix acids at a predetermined mixing ratio to
prepare the acid etchant and then supply the acid etchant
to the nozzle 31, or it may separately supply acids to the
nozzle 31 and then mix them near the nozzle 31.
In the nozzle position controlling means 30, the guide
portion 29 that restricts movement of the nozzle base
portion 28 runs through a rotational center of the wafer 21
and supports the nozzle base portion 28 so that the nozzle
27 can move in a radial direction of the wafer 21. The
guide portion 29 may have a configuration by which the
nozzle base portion 28 can move in a length direction
thereof. A position of the nozzle 27 with respect to the
rotational center of the wafer 21 can be set based on a
movement position of the nozzle base portion 28 in the
length direction of the guide portion 29. The nozzle base
portion 2 8 has a mechanism that moves in the length
direction of the guide portion 29.
[0017]
Further, the guide portion 29 may have a structure in
which one end thereof is provided to run through the
rotational center of the wafer 21 whilst the other end

thereof is supported to be rotatable in a horizontal
direction and the nozzle 27 that moves when the guide
portion 29 is horizontally swiveled can move in an in-plane
direction of the wafer 21.
The discharge state controlling means 31 has angle
adjusting means that is provided at the nozzle base portion
28 and adjusts an angle of the nozzle 27 with respect to
the nozzle base portion 28, height adjusting means for
adjusting a height position of the distal end of the nozzle
27 from the wafer 21, and a valve body that switches
discharge/non-discharge of the etchant from the nozzle 27.
Furthermore, supply from the etchant supplying means 26 may
be switched without providing the valve body.
[0018]
The controlling means 32 has at least a memory that
stores a surface shape of the wafer 21 before processing, a
memory that stores a position of the nozzle 27 and an
etching state, a memory that stores a discharge amount of
the etchant and an etching state, and a memory that stores
a shape of the wafer 21 serving as a reference after
processing as the memories 34, 35 ..., and has the
arithmetic portion 33 that calculates these contents to
obtain movement of the nozzle 27 and a discharge state of
the etchant. It is to be noted that the memories 34 and 35
use the detecting means 36 to detect a surface status of
the wafer 21 before processing, and store this data.
Incidentally, in regard to this memory data, the detecting

means may detect a surface status in accordance with each
wafer to be processed and resultant data may be stored, or
the detecting means may detect a surface status every given
number of wafers on behalf of other wafers and resultant
data may be stored, or a convex portion of a given wafer
may be detected in accordance with each ingot, or data
defined in accordance with each category of wafers may be
used.
[0019]
In order to smooth the wafer 21 in the single-wafer
processing etching device 20 according to this embodiment,
the detecting means 36 is first used to divide a surface of
the wafer 21 into a plurality of regions and measure a
surface shape, this detection data is input to the
controlling means 32 for controlling a shape of the wafer
21, and this detection data is stored in the memories 34
and 35.
Then, the wafer 21 is supported on the stage 22, and
the rotation driving source 24 drives this stage 22 to
rotate under control by the controlling means 32.
Furthermore, the controlling means 32 allows the
etchant supplying means 26 to supply an etchant having a
predetermined composition to the nozzle 27, controls the
nozzle position controlling means 30 and the discharge
state controlling means 31 to control a state/a position
and a discharge time of the nozzle 27 so that the etchant
is belched out to the wafer 21.

[0020]
Horizontal movement of the nozzle 27 is carried out by
oscillation along an arc described by horizontal driving
over the nozzle 27 in a radial direction of the wafer from
the wafer center at a speed of approximately 0.1 to 20
mm/second with an end of the nozzle 27 being determined as
a supporting point, or carried out by reciprocation in the
radial direction of the wafer from the wafer center. The
etchant supplied to an upper surface of the wafer 21
gradually moves from a water center side toward a wafer
outer rim side by a centrifugal force of rotation of the
wafer while etching an affected layer on the wafer surface,
and scatters as droplets from the outer rim of the wafer.
[0021]
The etchant used at the smoothening step 12 is an
aqueous solution containing hydrofluoric acid, nitric acid,
and phosphoric acid. Moreover, a mixing ratio of
hydrofluoric acid, nitric acid, and phosphoric acid
contained in the aqueous solution is defined as
hydrofluoric acid:nitric acid:phosphoric acid=0.5 to 40%:5
to 50%:5 to 70% in weight%. When this mixing ratio is
adopted, a viscosity degree of the etchant becomes 2 to 40
mPa.sec and a surface tension of the etchant becomes 50 to
70 dyne/cm, and hence this is preferable to improve
flatness degrees of front and rear surfaces of the wafer
and a parallelism degree of the wafer. When the viscosity
degree is less than a lower limit value, the viscosity of

the liquid is too low, the etchant that has dropped onto
the upper surface of the wafer is immediately blown out
from the wafer surface by the centrifugal force, and the
etchant cannot uniformly and sufficiently come into contact
with the wafer surface, whereby assuring a sufficient
etching removal amount takes time, resulting in a reduction
in productivity. When the viscosity degree exceeds an
upper limit value, the etchant that has dropped onto the
wafer surface stays on the wafer supper surface for a long
time beyond necessity, and hence an in-plane and an outer
peripheral shapes of the wafer cannot be controlled,
resulting in an inconvenience of deterioration in the wafer
flatness degree. When the surface tension is less than the
lower limit value, the etchant that has dropped onto the
wafer upper surface is immediately blown out from the wafer
surface by the centrifugal force, it cannot uniformly and
sufficiently come into contact with the wafer surface,
whereby assuring a sufficient etching removal amount takes
time, resulting in a reduction in productivity. When the
surface tension exceeds an upper limit value, the etchant
that has dropped onto the wafer surface stays on the wafer
upper surface for a long time beyond necessity, and hence
an in-plane and an outer peripheral shapes of the wafer
cannot be controlled, resulting in an inconvenience of
deterioration in the wafer flatness degree. As a mixing
ratio of hydrofluoric acid, nitric acid, phosphoric acid,
and water contained in the etchant, 5 to 20%:20 to 40%:20

to 40%:20 to 40% is preferable. When this mixing ratio is
adopted, a viscosity degree of the etchant becomes 10 to 20
mPa.sec and a surface tension of the etchant becomes 55 to
60 dyne/cm. As a supply amount of the etchant from the
nozzle 27, 2 to 30 liters/minute is preferable. 5 to 30
liters/minute is preferable as a supply amount of the acid
etchant when a width of the silicon wafer is to 20 liters/minute is preferable as a supply amount of the
acid etchant when a width of the silicon wafer is 4»200 mm.
[0022]
A rotating speed of the wafer 21 at the smoothing step
12 is defined to fall within a range of approximately 100
to 2000 rpm. It is to be noted that an optimum rotating
speed slightly varies depending on a diameter of the wafer
21, a viscosity degree of the etchant, a supply position of
the etchant based on horizontal movement of the nozzle 27,
or a supply flow rate of the etchant to be supplied. When
the rotating speed is less than a lower limit value, an in-
plane and an outer peripheral shapes of the wafer cannot be
controlled to result in an inconvenience of deterioration
in a wafer flatness degree and, when the rotating speed exceeds an upper limit value, the etchant that has dropped
onto the wafer surface is immediately blown out from the
wafer surface by the centrifugal force, and it cannot
uniformly and sufficiently come into contact with the wafer
surface, whereby assuring a sufficient etching removal
amount takes time, reducing productivity. When a width of

the silicon wafer is 1500 rpm is preferable, and 600 rpm is more preferable.
When a width of the silicon wafer is ϕ200 mm, a rotating
speed of 300 to 2000 rpm is preferable, and 800 rpm is more
preferable.
[0023]
Moreover, at this smoothing step 12, when one surface
of the wafer is etched and then the other surface of the
wafer is etched, a parallelism degree of the wafer required
to evenly etch both the front and rear surfaces of the
wafer can be enhanced. After etching one surface of the
wafer 21, the wafer 21 is spun while supplying a rinse
agent, e.g., pure water to the upper surface of the wafer
21 from a non-illustrated rinse agent supply nozzle so that
the etchant remaining on the surface of the wafer 21 is
removed. After cleaning, in a state where supply of the
rinse agent is stopped, the wafer 21 is spun to be dried
while supplying an inert gas, e.g., a nitrogen gas.
Subsequently, the wafer 21 is turned over, the wafer 21 is
held on the stage 22 in such a manner that the surface of
the wafer 21 that has not been subjected to
etching/cleaning/drying processing becomes an upper surface,
and etching processing, rinse agent cleaning processing,
and drying processing are likewise carried out.
[0024]
In regard to an etching removal amount at this
smoothing step 12, 10 to 150 urn is preferable as a total

removal amount of the front and rear surfaces of the wafer,
wherein 5 to 75 µm is a removal amount for one surface.
When the etching removal amount is set to fall within this
range, a flatness degree of the front and rear surfaces of
the wafer and a parallelism degree of the wafer can be
enhanced. Additionally, at steps following this smoothing
step 12, when mirror polishing is applied, a polishing
removal amount at a mirror polishing step can be greatly
reduced as compared with that in a conventional wafer
manufacturing process. When the etching removal amount is
less than a lower limit value, a flatness degree of the
front and rear surfaces of the wafer and a parallelism
degree of the wafer required as a product cannot be
obtained, wafer surface roughness cannot be sufficiently
reduced and, when the etching removal amount exceeds an
upper limit value, the wafer flatness degree is
deteriorated, and productivity in wafer manufacture is
degraded. When the smoothing step 12 is carried out under
the above-described conditions, a high flatness degree can
be achieved without effecting a smoothing step using
machining based on grinding or the like that is a necessary
step in the conventional wafer manufacturing process.
[0025]
It is to be noted that the example where the smoothing
step using machining based on, e.g., lapping or grinding is
omitted has been explained in conjunction with this
embodiment, but the sliced wafer may be subjected to

lapping processing or surface grinding processing before
the smoothing step 12 depending on the wafer shape after
slicing in order to reduce a throughput per wafer, e.g., an
etching use amount at the smoothing step 12. Even in this
case, performing the smoothing step 12 allows reducing
occurrence of a surface defect or a slip formed on an
epitaxial layer due to machining.
[0026]
Subsequently, an epitaxial layer formed of a silicon
single crystal is formed on the surface of the wafer by
epitaxial growth (a step 13). It is preferable for the
epitaxial layer to be formed by a CVD method in view of
crystallinity or mass productivity thereof, simplicity of a
device, easiness of forming various kinds of device
structures, and others. Epitaxial growth of silicon by the
CVD method is carried out by introducing a raw material gas
containing silicon, e.g., SiCl4, SiHCl3, SiH2Cl2, or SiH4
together with an H2 gas into a reactor and precipitating on
the surface of the wafer silicon generated by thermal
decomposition or reduction of the raw material gas.
[0027]
Controlling application of an etchant to the wafer
surface in accordance with a shape of the wafer surface in
this manner enables accurately smoothing the wafer surface
and, since the smoothing processing for the wafer surface
is chemical processing of applying an etchant to the wafer
without including a mechanical element, occurrence of a

surface defect or a slip formed on the epitaxial layer due
to machining can be reduced while causing almost no scratch
or damage on the wafer. The epitaxial wafer can be
obtained in accordance with this embodiment, wherein a
difference between a maximum value of a wafer thickness and
a minimum value of the same is not greater than 1 µm when
an entire surface of the wafer is measured.
[0028]
Further, according to this embodiment, it is
preferable to further include a mirror polishing step 14
between the smoothing step 12 and the epitaxial layer
forming step 13 as shown in FIG. 2, or after the epitaxial
layer forming step 13 as shown in FIG. 3. Furthermore,
since etching as chemical processing is carried out at the
smoothing step 12, a grinding mark or undulation generated
by effecting mechanical smoothing processing such as
grinding is not produced, and hence much polishing removal
amount does not have to be taken at the mirror polishing
step 14, thus reducing the polishing removal amount. As
compared with a conventional manufacturing method, a
surface quality can be improved, and occurrence of a
surface defect can be further suppressed. The mirror
polishing step 14 may be a step based on SMP of polishing
the front and rear surfaces of the wafer one by one or a
step based on DSP of simultaneously polishing the front and
rear surfaces of the wafer. Moreover, in order to improve
micro-roughness of a wafer main surface on which a device

is formed, SMP may be carried out with respect to the main
surface of the wafer subjected to DSP. When performing the
mirror polishing 14 between the smoothing step 12 and the
epitaxial layer forming step 13, a polishing removal amount
that is not smaller than 0.01 µm but not greater than 5 µm
per surface is preferable or a polishing removal amount
that is not smaller than 0.1 µm but not greater than 1 µm
is more preferable per surface in SMP. Additionally, in
DSP, a polishing removal amount that is not smaller than
0.5 µm but not greater than 20 µm is preferable or a
polishing removal amount that is not smaller than 0.5 µM
but not greater than 15 µm is more preferable as a total
polishing removal amount on both the front and rear
surfaces. Further, when performing DSP after the epitaxial
layer forming step 13, a polishing removal amount that is
not smaller than 0.02 µm but not greater than 1 µm is
preferable or a polishing removal amount that is not
smaller than 0.1 µm but not greater than 0.5 µm is more
preferable as a total polishing removal amount on both the
front and rear surfaces.
[0029]
It is to be noted that a cleaning step may be of
course provided before or after each step in this
embodiment. Furthermore, as cleaning after the smoothing
step 12 and before the epitaxial layer forming step 13, it
is particularly preferable to perform cleaning using a
cleaning fluid having an oxidation reducing effect and then

carry out cleaning using a hydrofluoric acid solution in
order to efficiently remove a remaining ion.
EXAMPLES
[0030]
Examples according to the present invention will now
be described in detail together with comparative examples.

A silicon wafer of ϕ300 mm cut out from a silicon
single crystal ingot was first prepared. Then, the single-
wafer processing etching device depicted in FIG. 4 was used
to perform single-wafer processing etching with respect to
the silicon wafer. As an etchant, an acid etchant
containing hydrofluoric acid, nitric acid, phosphoric acid,
and water at a mixing ratio of hydrofluoric acid:nitric
acid:phosphoric acid:water=7%:30%:35%:28% in weight% was
used. Moreover, a wafer rotating speed and a flow rate of
the etchant to be supplied in etching were respectively
controlled to 600 rpm and 5.6 liters/minute, and etching
was effected for 90 seconds. An etching removal amount in
single-wafer processing etching was 30 µm on one surface.
After etching, pure wafer was supplied to the wafer surface
to perform cleaning while spinning the wafer, and nitrogen
was sprayed to the wafer surface to dry the wafer surface.
Subsequently, the wafer was turned over, and single-wafer
processing etching was carried out with respect to the rear
surface of the wafer under the same conditions.

Then, an epitaxial layer formed of a silicon single
crystal was formed with a thickness of 2 µm on the surface
of the wafer by epitaxial growth, thus obtaining an
epitaxial wafer.
[0031]

A silicon wafer of ϕ300 mm cut out from a silicon
single crystal ingot was first prepared. Then, the single-
wafer processing etching device depicted in FIG. 4 was used
to perform single-wafer processing etching with respect to
the silicon wafer. As an etchant, an acid etchant
containing hydrofluoric acid, nitric acid, phosphoric acid,
and water at a mixing ratio of hydrofluoric acid:nitric
acid:phosphoric acid:water=7%:30%:35%:28% in weight% was
used. Moreover, a wafer rotating speed and a flow rate of
the etchant to be supplied in etching were respectively
controlled to 600 rpm and 5.6 liters/minute, and etching
was effected for 90 seconds. An etching removal amount in
single-wafer processing etching was 30 µm on one surface.
After etching, pure wafer was supplied to the wafer surface
to perform cleaning while spinning the wafer, and nitrogen
was sprayed to the wafer surface to dry the wafer surface.
Subsequently, the wafer was turned over, and single-wafer
processing etching was carried out with respect to the rear
surface of the wafer under the same conditions.
Then, SMP of polishing the front and rear surfaces of
the wafer subjected to single-wafer processing one by one

was carried out. A polishing removal amount based on this
SMP was 0.5 µm on one surface, and a total polishing
removal amount was 1.0 µm on both the front and rear
surfaces. Furthermore, an epitaxial layer formed of a
silicon single crystal was formed with a thickness of 2 µm
on the surface of the wafer by epitaxial growth, thus
obtaining an epitaxial wafer.
[0032]

A silicon wafer of ϕ300 mm cut out from a silicon
single crystal ingot was first prepared. Then, the single-
wafer processing etching device depicted in FIG. 4 was used
to perform single-wafer processing etching with respect to
the silicon wafer. As an etchant, an acid etchant
containing hydrofluoric acid, nitric acid, phosphoric acid,
and water at a mixing ratio of hydrofluoric acid:nitric
acid:phosphoric acid:water=7%:30%:35%:28% in weight% was
used. Moreover, a wafer rotating speed and a flow rate of
the etchant to be supplied in etching were respectively
controlled to 600 rpm and 5.6 liters/minute, and etching
was effected for 90 seconds. An etching removal amount in
single-wafer processing etching was 30 µm on one surface.
After etching, pure wafer was supplied to the wafer surface
to perform cleaning while spinning the wafer, and nitrogen
was sprayed to the wafer surface to dry the wafer surface.
Subsequently, the wafer was turned over, and single-wafer
processing etching was carried out with respect to the rear

surface of the wafer under the same conditions.
Then, an epitaxial layer formed of a silicon single
crystal was formed with a thickness of 2 µm on the surface
of the wafer by epitaxial growth, thus obtaining an
epitaxial wafer. Moreover, SMP of polishing the front and
rear surfaces of this epitaxial wafer one by one was
carried out. A polishing removal amount based on this SMP
was 0.5 µm on one surface, and a total polishing removal
amount was 1.0 µm on both the front and rear surfaces.
[0033]

A silicon wafer of ϕ300 mm cut out from a silicon
single crystal ingot was first prepared. Then, as a
smoothing step, a non-illustrated grinder was used to
perform double disk surface grinding (which will be
referred to as DDSG hereinafter) with respect to front and
rear surfaces of the silicon wafer. A removal amount at
this DDSG step was 30 µm on one surface. Subsequently, the
non-illustrated grinder was used to perform a single disk
surface grinding step (which will be referred to as a SDSG
step hereinafter), and a removal amount at this SDSG step
was 20 µm on one surface.
Then, DSP of simultaneously polishing the front and
rear surfaces of the wafer was effected. A polishing
removal amount based on this DSP was 10 µm. on one surface,
and a total polishing removal amount was 20 µm on both the
front and rear surfaces. Subsequently, SMP of polishing

the front and rear surfaces of the wafer one by one was
carried out. A polishing removal amount based on this SMP
was 0.5 µm on one surface, and a total polishing removal
amount was 1.0 µm on both the front and rear surfaces.
Additionally, an epitaxial layer formed of a silicon single
crystal was formed with a thickness of 2 µm on the surface
of the wafer by epitaxial growth, thereby obtaining an
epitaxial wafer.
[0034]

A particle measuring device (SP1 manufactured by KLA-
Tencor Corporation) was used to measure each particle that
is present on the wafer surface and equal to or above 0.09
µm with respect to the epitaxial wafer obtained by each of
Examples 1 to 3 and Comparative Example 1. FIGS. 5 to 8
show its result.
[0035]
As apparent from FIGS. 5 to 8, 9 particles were
measured per wafer in Example 1, 11 particles were measured
per wafer in Example 2, 10 particles were measured per
wafer in Example 3, and 29 particles were measured per
wafer in Comparative Example 1, respectively. In the
wafers according to Examples 1 to 3, there is no large
difference in surface defect density irrespective of a
wafer that was not subjected to mirror polishing or a wafer
that was subjected to mirror polishing, and hence excellent
results were obtained. On the other hand, in Comparative

Example 1, although a large defect like a slip was not
observed, it was revealed that there is a difference in
surface defective density when microscopically compared.
[0036]

A non-contact surface roughness meter (MP3100
manufactured by Chapman) was used to measure wafer surface
roughness with respect to the epitaxial wafer obtained by
each of Examples 1 to 3 and Comparative Example 1. Table 1
shows its result.
[0037]

[0038]
As apparent from Table 1, in the wafer according to
Example 1 formed without the smoothing step based on
machining, a result of the surface roughness smaller than
that of the wafer according to Comparative Example 1 as a
conventional method was obtained. Further, in each of the
wafer according to Example 2 and the wafer according to
Example 3 subjected to mirror polishing, the surface
roughness is smaller than that of the wafer according to
Example 1 that was not subjected to mirror polishing, and

it was revealed that an excellent result can be obtained
when mirror polishing is carried out.
[0039]
Comparative Test 3>
The epitaxial wafer obtained in each of Examples 1 to
3 and Comparative Example 1 was imaged based on X-ray
topography. FIGS. 9 and 12 show obtained topographs.
[0040]
As apparent from FIGS. 9 to 12, a large defect, e.g.,
a slip or a dislocation that can be observed based on X-ray
topography was not observed in all the epitaxial wafers
according to Examples 1 to 3 and Comparative Example 1.
INDUSTRIAL APPLICABILITY
[0041]
The method for manufacturing an epitaxial wafer
according to the present invention can efficiently form an
epitaxial layer by applying an etchant to a surface of a
semiconductor wafer to smooth the surface.

We Claim:
1. A method for manufacturing an epitaxial wafer comprising:
a smoothing step of smoothing a surface of a silicon wafer by
controlling supply of an etchant to the silicon wafer surface in
accordance with a surface shape of the wafer; and
an epitaxial layer forming step of forming an epitaxial layer formed of
a silicon single crystal on the smoothed surface of the wafer based on
epitaxial growth,
characterized in that: the smoothing step is carried out after a slicing
step of slicing a silicon single crystal ingot to obtain a single thin
discoid wafer, and is carried out by rotating in a horizontal direction
the single thin discoid wafer obtained by slicing a silicon single crystal
ingot and supplying the acid etchant to the surface of the rotating
wafer to spread the supplied acid etchant on the entire surface of the
wafer by a centrifugal force,
and the supply of the acid etchant to the surface of the wafer is
carried by measuring a surface shape of the wafer by detecting
means, storing the measured surface shape of the wafer in a memory
and controlling a position of a nozzle for supplying an acid etchant and
a discharge time of an acid etchant from the nozzle in accordance with
the stored surface shape of the wafer, and on the basis of the control.

2. The method for manufacturing an epitaxial wafer as claimed in claim 1,
comprising a mirror polishing step between the smoothing step and the
epitaxial layer forming step or after the epitaxial layer forming step.
3. The method for manufacturing an epitaxial wafer as claimed in claim 1 or
2, wherein the acid etchant is an aqueous solution constituted of hydrofluoric
acid, nitric acid, and phosphoric acid and containing hydrofluoric acid, nitric
acid, and phosphoric acid at a mixing ratio of hydrofluoric acid:nitric
acid:phosphoric acid = 0.5 to 40%:5 to 50%:5 to 70% in weight%.
4. The method for manufacturing an epitaxial wafer as claimed in any one
of claims 1 to 3 wherein front and rear surfaces of the silicon wafer are
smoothed.
5. The method for manufacturing an epitaxial wafer as claimed in any one of
claims 1 to 4 wherein, when an entire surface of a manufactured epitaxial
wafer is measured, a difference between a maximum value and a
minimum value of a thickness of the wafer is not greater than 1 µm.


ABSTRACT

TITLE " METHOD FOR MANUFACTURING EPITAXIAL WAFER"
The invention relates to a method for manufacturing an epitaxial wafer
comprising : a step of providing a single crystal ingot;a step of slicing a silicon
single crystal ingot to obtain a thin discoid wafer; a step of supplying an etchant
to the wafer surface by rotating the wafer in a horizontal direction; a smoothing
step of controlling supply of the etchant in accordance with a shape of the wafer
and spreading the supplied etchant on the entire surface of the rotating wafer by
a centrifugal force to smooth the wafer surface, wherein the supply of the acid
etchant to the surface of the wafer is carried out by measuring the shape of the
wafer by detecting means, and storing the shape of the wafer in a memory and
controlling a position of a nozzle for supplying an acid etching and a discharge
time of an acid etchant from the nozzle in accordance with the stored shape of
the wafer, and on the basis of the control; and an epitaxial layer forming step of
forming an epitaxial layer formed of a silicon single crystal on the surface of the
wafer based on epitaxial growth.

Documents:

02546-kolnp-2008-abstract.pdf

02546-kolnp-2008-claims.pdf

02546-kolnp-2008-correspondence others.pdf

02546-kolnp-2008-description complete.pdf

02546-kolnp-2008-drawings.pdf

02546-kolnp-2008-form 1.pdf

02546-kolnp-2008-form 2.pdf

02546-kolnp-2008-form 3.pdf

02546-kolnp-2008-form 5.pdf

02546-kolnp-2008-international publication.pdf

02546-kolnp-2008-international search report.pdf

02546-kolnp-2008-others pct form.pdf

02546-kolnp-2008-pct priority document notification.pdf

02546-kolnp-2008-pct request form.pdf

2546-KOLNP-2008-(02-08-2011)-FORM 13.pdf

2546-KOLNP-2008-(13-07-2012)-CORRESPONDENCE.pdf

2546-KOLNP-2008-(16-09-2011)-CORRESPONDENCE.pdf

2546-KOLNP-2008-(16-09-2011)-FORM 13.pdf

2546-KOLNP-2008-(17-01-2012)-AMANDED CLAIMS.pdf

2546-KOLNP-2008-(17-01-2012)-CORRESPONDENCE.pdf

2546-KOLNP-2008-ABSTRACT-1.1.pdf

2546-KOLNP-2008-ABSTRACT-1.2.pdf

2546-KOLNP-2008-AMANDED CLAIMS.pdf

2546-KOLNP-2008-CLAIMS.pdf

2546-KOLNP-2008-CORRESPONDENCE 1.2.pdf

2546-KOLNP-2008-CORRESPONDENCE 1.3.pdf

2546-KOLNP-2008-CORRESPONDENCE OTHERS 1.1.pdf

2546-KOLNP-2008-CORRESPONDENCE-1.4.pdf

2546-KOLNP-2008-CORRESPONDENCE-1.5.pdf

2546-KOLNP-2008-CORRESPONDENCE-1.6.pdf

2546-KOLNP-2008-DESCRIPTION (COMPLETE)-1.1.pdf

2546-KOLNP-2008-DESCRIPTION (COMPLETE)-1.2.pdf

2546-KOLNP-2008-DRAWINGS-1.1.pdf

2546-KOLNP-2008-DRAWINGS-1.2.pdf

2546-KOLNP-2008-EXAMINATION REPORT.pdf

2546-KOLNP-2008-FORM 1.pdf

2546-KOLNP-2008-FORM 13-1.1.pdf

2546-KOLNP-2008-FORM 13-1.2.pdf

2546-KOLNP-2008-FORM 13.pdf

2546-KOLNP-2008-FORM 18.pdf

2546-KOLNP-2008-FORM 2-1.1.pdf

2546-KOLNP-2008-FORM 2-1.2.pdf

2546-KOLNP-2008-FORM 26-1.1.pdf

2546-KOLNP-2008-FORM 26.pdf

2546-KOLNP-2008-FORM 3 1.1.pdf

2546-KOLNP-2008-FORM 3-1.2.pdf

2546-KOLNP-2008-FORM 3-1.3.pdf

2546-KOLNP-2008-FORM 5-1.2.pdf

2546-KOLNP-2008-FORM 5.pdf

2546-KOLNP-2008-GRANTED-ABSTRACT.pdf

2546-KOLNP-2008-GRANTED-CLAIMS.pdf

2546-KOLNP-2008-GRANTED-DESCRIPTION (COMPLETE).pdf

2546-KOLNP-2008-GRANTED-DRAWINGS.pdf

2546-KOLNP-2008-GRANTED-FORM 1.pdf

2546-KOLNP-2008-GRANTED-FORM 2.pdf

2546-KOLNP-2008-GRANTED-SPECIFICATION.pdf

2546-KOLNP-2008-INTERNATIONAL SEARCH REPORT.pdf

2546-KOLNP-2008-OTHERS-1.2.pdf

2546-KOLNP-2008-OTHERS-1.3.pdf

2546-KOLNP-2008-OTHERS.pdf

2546-KOLNP-2008-PA.pdf

2546-KOLNP-2008-PCT REQUEST 1.1.pdf

2546-KOLNP-2008-PCT SEARCH REPORT 1.1.pdf

2546-KOLNP-2008-PETITION UNDER RULE 137.pdf

2546-KOLNP-2008-PRIORITY DOCUMENT.pdf

2546-KOLNP-2008-REPLY TO EXAMINATION REPORT.pdf

2546-KOLNP-2008-SPECIFICATION-1.2.pdf

2546-KOLNP-2008-TRANSLATED COPY OF PRIORITY DOCUMENT.pdf

abstract-02546-kolnp-2008.jpg


Patent Number 253610
Indian Patent Application Number 2546/KOLNP/2008
PG Journal Number 32/2012
Publication Date 10-Aug-2012
Grant Date 06-Aug-2012
Date of Filing 23-Jun-2008
Name of Patentee SUMCO CORPORATION
Applicant Address 2-1, SHIBAURA 1-CHOME, MINATO-KU, TOKYO
Inventors:
# Inventor's Name Inventor's Address
1 KOYATA, SAKAE C/O SUMCO CORPORATION, 2-1, SHIBAURA 1-CHOME, MINATO-KU, TOKYO 1058634
2 MURAYAMA, KATSUHIKO C/O SUMCO CORPORATION, 2-1, SHIBAURA 1-CHOME, MINATO-KU, TOKYO 1058634
3 KATOH, TAKEO C/O SUMCO CORPORATION, 2-1, SHIBAURA 1-CHOME, MINATO-KU, TOKYO 1058634
4 HASHII, TOMOHIRO C/O SUMCO CORPORATION, 2-1, SHIBAURA 1-CHOME, MINATO-KU, TOKYO 1058634
5 TAKAISHI, KAZUSHIGE C/O SUMCO CORPORATION, 2-1, SHIBAURA 1-CHOME, MINATO-KU, TOKYO 1058634
PCT International Classification Number C30B 29/06
PCT International Application Number PCT/JP2007/051031
PCT International Filing date 2007-01-24
PCT Conventions:
# PCT Application Number Date of Convention Priority Country
1 2006-021902 2006-01-31 Japan