Title of Invention

METHOD FOR MAKING METAL OXIDES

Abstract A method of producing porous complex oxides includes the steps of providing a mixture of a) precursor elements suitable to produce the complex oxide; or b) one or more precursor elements suitable to produce particles of the complex oxide and one or more metal oxide particles; and c) a particulate carbon-containing pore-forming material selected to provide pore sizes in the range of approximately 7 nm to 250 nm, and treating the mixture to (i) form the porous complex oxide in which two or more of the precursor elements from (a) above or one or more of the precursor elements and one or more of the metals in the metal oxide particles from (b) above are incorporated into a phase of the complex metal oxide and the complex metal oxide has grain sizes in the range of about 1 nm to 150 nm; and (ii) remove the pore-forming material under conditions such that the porous structure and composition of the complex oxide is substantially preserved. The method may be used to produce non-refractory metal oxides as well.
Full Text FORM 2
THE PATENTS ACT, 1970
(39 of 1970)
&
THE PATENTS RULES, 2003
COMPLETE SPECIFICATION
(See section 10, rule 13)
“METHOD FOR MAKING METAL OXIDES”
VERY SMALL PARTICLE COMPANY PTY LTD., an Australian company of 31 Westgate Street, Wacol, Queensland 4076, Australia
The following specification particularly describes the invention and the manner in which it is to be performed.

WO 2005/070819 PCT/AU2005/000081
Method for making metal oxides
1. Field of the Invention
The present invention generally relates to complex oxide materials. Complex oxides are oxides that contain two or more different metallic elements. They are useful for a variety of purposes, including as catalysts and a wlde range of electronic materials. In preferred embodiments, the invention relates to a method for making porous complex oxides with improved high temperature stability. In another aspect, the present invention also relates to a method for making porous non-refractory oxides
2. Description of Related Art
10 In general, the crystal structures of oxides containing several different metallic
elements are more complex than those of simple oxides such as AI2O3 and Si02. In addition, achieving phase purity (i.e. the presence of a desired crystal phase or phases and the absence of undesired phases) in these complex compounds is typically very difficult. This is because these complex crystal structures are very sensitive to variations
15 in chemical composition.
It follows therefore, that to achieve uniform and consistent properties critical to
many applications, it is necessary to ensure a homogeneous dispersion of elements that
lead to the desired purity of the complex oxide. One difficulty that arises in achieving such
a homogeneous distribution of elements is the different ways in which individual elements
20 can behave during processing.
For example, precipitation and reaction rates may vary widely for each element, causing segregation in methods such as co-precipitation and sol-gel processing. Different elements can also respond very differently to temperature and atmosphere. For example, many metallic elements used to form complex oxides have relatively low melting points. If a sufficiently reducing atmosphere is present during heat treatment, these elements may be present in metallic rather than oxide form, and melt. Such melting can lead to severe segregation, the extensive formation of impurity phases, and loss of surface area.
Despite these difficulties various methods for production of complex oxides are known in the art.
30 Such methods include:
• 'Shake and bake'
♦ Co-precipitation

WO 2005/070819 PCT/AU2005/000081
3
• Thermal evaporative and spraying techniques
• Polymer-complexing methods
• Sol-gel
'Shake and bake' methods are the crudest and simplest An example is described
in US Patent 5,932,146. Different oxide powders, each containing one or more required elements, are simply mixed together, ground and then fired at high temperatures to
enable homogenous mixing of different elements via diffusion. The problem with this
method is that the starting material is very 'inhomogeneous; very high sintering
temperatures are therefore required to obtain homogeneity. Often intermediate grinds are
also necessary. High sintering temperatures greatly diminish surface area, and long
sintering times, high temperatures and intermediate grinds lead to very high processing
costs. It may not even be possible to obtain some desired phases and phase purities
using this method.
Co-precipitation methods can provide a more homogeneous precursor for
15 relatively simple metal oxides. Examples are described in Applied Catalysis A: General,
235, pp 79-92, 2002 (Zhang-Steenwinkel, Beckers and Bliek) and J. of Power Sources,
86, pp 395-400, 2000 (Mode, Sammes & Tompsett). These methods have the
disadvantage of being very problematic with multiple elements. It is common for different
elements to precipitate at different rates, therefore for some materials, inhomogeneity is a
20 major problem, and reasonably high sintering temperatures are still required. For
example, the method of Zhang-Steenwinkel et al. required temperatures in excess of
800°C to form proper crystalline phases, and that of Morie et al. required 1000°C. In
addition, precipitation agents that are necessary to achieve proper precipitation and
chemical homogeneity are often expensive.
25 The majority of thermal evaporative and spraying techniques have more relevance
to the production of oxide films or coatings. These include techniques such as gas condensation processing, chemical vapour condensation, plasma spray and spray pyrolysis. The most important of these techniques for bulk processing is spray pyrolysis (Messing et at. 1994).
30 Spray pyrolysis is a process for producing powders of metals or oxides by the
thermal decomposition of metal salts or organometallic solutions. The solutions are first converted to aerosols by passing through atomising spray nozzles or through ultrasonic transducers. The aerosol is then sprayed into a heated zone or onto a heated surface

WO 2005/070819 PCT/AU2005/000081
sufficiently hot to cause evaporation of the solvent and subsequent precipitation of the metal or oxide.
Generally, in a spray pyrolysis process, changing aerosol decomposition parameters by varying reaction temperature and carrier gas composition are basic operating variables. In addition, solution properties such as precursor composition, concentration, or the addition of a co-solvent may be crucial to achieve the desired product composition and morphology. Limitations of the spray pyrolysis process include difficulty in controlling phase proportions, low production rates and formation of low-density hollow particles.
10 Polymer-complex methods can also provide reasonably homogeneous
distributions of elements for relatively simple oxides. An example for La-based perovskites is described in Key Engineering Materials, 206-213, pp 1349-52.2002 (Popa & Kakihana). The main problem with such methods is that the polymers used can be prone to exothermic firing. This can make processing difficult Also, for multi-element compounds,
15 some elements may not complex with the polymer, and therefore a homogeneous distribution of elements cannot be obtained.
Sol-gel methods generally require carefully controlled processing conditions to form homogeneous precursors. Examples of sol-gel methods for La-Ca-Mn perovskites are described in J. SoLGei Scfence and Technology 25, pp 147-157, 2002 (Mathur & Shen), and Chemistry of Materials 14, pp 1981-88, 2002 (Pohl and WestJn). Sol-gel can become extremely difficult as the complexity of the compounds increase, and some elements are simply not suitable to sol-gel methods at all. Sol-gel is typically difficult to scale up and the required raw materials can be very expensive.
United States patent Number 6,752,979 in the name of the present applicants describes a method for producing complex metal oxides with homogeneously distributed elements. This method has been proven for a wide range of different complex oxides. The. method provides phase-pure oxides with high surface areas, using low processing temperatures.
In addition to correct oxide crystal structure and homogenous distribution of elements, in many applications the porosity that exists between sintered grains of oxide is very important to performance. Larger, interconnected pores (> ~ 1//m) are typically desirable for applications that require good fluid (gas or liquid) transfer. For example, methods are known that can provide large pores in oxides for solid oxide fuel cell electrodes (e.g. United States patents 4,883,497 and 6,017,647). Most of these methods

WO 2005/070819 PCT/AU2005/000081
use various pore-formers, i.e. materials that can be leached or burned out. of the ceramic material. The pore formers are typically greater than 1jtim to enable pores of this size to form. Pores of this size are too big to significantly increase the surface area of a material.
Materials with a substantial number of small pores ( Pores in the Intermediate' size range (-7 nm to ~ 250 nm) may also be useful for improving fluid flow, and are small enough to contribute significantly to surface area They have been thought to improve the high temperature stability of some simple metal oxides. United States patent 6,139,814 describes a method for making Ce-based oxides with
15 improved high temperature stability. Whilst the reason for the thermal stability is not known for certain, the patent speculates that the stability is owed, at toast in part, to the presence of average pore sizes that fie in the *mesoscale' range (example shows average pore size around 9 nm). The method of *814 involves absorbing a liquid solution of metal ions into the pores of a structured cettutosic material, e.g. fitter paper. The liquid is dried,
20 and the material fired to remove the cellulose. Thus the solid forms in the pores of the cellulose, and the pores of the cellulose 'pattern' the solid. This method, however, has several disadvantages. Very high organic metal oxide ratios are used (up to >100:1), which, together with the relatively high cost of suitable cellulose materials, result in expensive processing. Absorption of liquid into solids like paper is also a clumsy process
25 to scale up. Finally, simply drying out solutions of metal Ions to form solids is not ideal for creating the homogeneous distributions of different elements that are required for more complex materials.
A method for preparing silica with pores around the 10 nm size range Is described in J. Porous Materials 7, p435-441, 2000 (Ermakova et ah). Various carbon matrices were impregnated with a silica gel, and dried then burned out Increased pore sizes were obtained using this method. Improved thermal stabilities were obtained when catalytic filamentous carbon was used as the source of carbon. Pores from other, more spherical carbon particles were not tested for thermal stability. Unfortunately the sol-gel method used Is not desirable for forming many perovskite materials, particularly at oornmercial

WO 2005/070819 PCT/AU2005/000081
scale. Also, impregnation of solids is an awkward method to scale up. Another problem is that the ratio of carbon material to oxide is quite high (up to 30). This increases the expense of production, decreases production rates, and exacerbates problems with impurity elements in the carbon.
5 United States patent 4,624,773 describes a process for catalytic cracking of
hydrocarbon feedstock. Part of the process is to make alumino-siicate materials with pores preferably from 100 to 600 nm to improve the flow of gas into the catalyst The method involves making a gel of alumina and silica, and mixing in reticulated carbon particles having length of about 50 to 3000 nm. After the alumino-silicate solid is formed, carbon particles are burned out to form pores in the desired size range. This method requires that the smaller pores in the alumino-silicate zeolite structures, that provide high surface areas, are unaffected by the burnout
The gel technique used in this method to form the alumino-silicate solid is not suited to more complex materials that require higher chemical homogeneity, particularly at
15 commercial scale. Also, the pores created to maximize gas flow are larger than that required to create thermally stable surface area. Finally, carbon is a strong reducing agent and is extensively used m minerals processing to reduce oxides to metal. While this may not be an issue with oxides of aluminium and silicon, since these oxides are very stable and difficult to reduce, the oxides of many other metals, including metals commonly used
20 in complex oxides, are more likely to be reduced by carbon. The reduribillity of different elements is commonly represented in Effingham Diagrams. Oxides towards the bottom of the diagram, such as A! are difficult to reduce, while those at the top are much easier to reduce. Metals such as iron, nickel, cobalt manganese, chromium and potassium are much more reducible than AI. Ellingham diagrams also show the reducing effects of
25 carbon, and particularly of carbon monoxide in the heat treatment atmosphere.
In processing of complex oxides, particularly heat treatment, the presence of metals can create severe difficulties due to segregation and/or inability to form required oxide phases with other elements. Therefore it is not clear whether intimate mixtures of carbon particles and oxides or oxide precursors at mesoscale will allow proper development of required phases. Also, the presence of metals or other reduced oxide forms can greatly increase sintering, leading to severe loss of surface area and poor thermal stability.
An example of the problems associated with incorporation of carbon-based material into oxide precursors in outlined in J. of Materials Science 35 (2000), p5639-

WO 2005/070819 PCT/AU20O5/0O0O81
5644, which describes a method for forming Lao.8Sr0.2Co03 material using cellulose which was burned out. It was found that if carbon dioxide was not removed quickly enough, carbonates would form in the bulk and hence much higher catenation temperatures were needed to obtain phase purity.
5 GB 2 093 816 by Asia Oil Company Ltd and Mitsubishi Chemical Industries Ltd
describes a method for producing a porous refractory inorganic oxide product GB 2 093 816 provides a porous refractory inorganic oxide product which has a pore distribution having a dear peak between 10nm and 100nm in diameter and a pore capacity (porosity) of 0.11cc/g or more between 10nm and 50nm in radius which is obtained by shaping a
10 mixture of carbon black and a refectory inorganic oxide and/or a precursor of refractory
inorganic oxide, drying a product, firing it in an oxygen-containing gas flow while burning said carbon black.
It is apparent that GB 2 093 816 is limited to producing refractory inorganic oxide
products. The typical refractory inorganic oxides used in GB 2 093 816 in dude inorganic
15 oxides such as alumina, sllica, titania, zirconia, thoria, boria, zeolite and day. The actual
examples given in GB 2 093 816 only show the formation of refractory inorganic oxides
incorporating alumina, silica, titania, silica alumina, boria, zeolite, kaoline, and sepioltte.
The examples given in GB 2 093 816 all used solid particulate starting materials to obtain mixed oxide products, except for Example 10, which used titanium tetrachloride as
a precursor for a precipitation reaction to form titania. The product of example 10 was titania, not a mixed oxide.
GB 2 093 816 used carbon black having an average diameter of 15-300nm. GB 2
093 816 also states that the final firing temperature in the step of burning out the carbon black is about 500°C or higher,[but] the upper limit is not critical as far as the porous refractory inorganic oxide product does not lose the activity for the support or catalyst
The processing conditions and starting materials used in GB 2 093 816 would
require relatively high processing temperatures to obtain a complex oxide matrix which induded a mixture of metals. Such processing conditions are dearly not disdosed in GB 2 093 816, confirming that complex metal oxide phases would not be formed. Consequently, the present inventors believe that the so-called mixed inorganic oxides formed in GB 2 093 816 would, in fad, consist of a mixture of separate grains or particles of the feed materials, with each separate grain or partide incorporating only one of the feed materials therein. Thus, GB 2 093 816 does not produce complex metal oxide phases that include two or more of the separate metals from the different precursor

WO 2005/070819

PCT/AU2005/000081


Ingredients used to form the particles.
Review of the prior art highlights the absence of a proven, commercially viable method for producing complex metal oxide materials with pores in the size range of approximately 7nm to 250r»m.
5 There is also great need for complex oxide materials with improved thermal
stability, and a method of manufacturing such materials.
Brief Description of the invention
In a first aspect the present invention provides a method of producing porous complex oxides, the method including providing a mixture of
10 a) precursor elements suitable to produce the complex oxide; or
b) one or more precursor elements suitable to produce particles of the complex oxide and one or more metal oxide particles; and
c) a particulate carbon-containing pore-forming material selected to provide pore sizes in the range of approximately 7 nm to 250 nm,
15 and treating the mixture to
i) form the porous complex oxide in which two or more of the precursor
elements from (a) above or one or more of the precursor elements andone
or more of the metals in the metal oxide particles from (b) above are
incorporated into a phase of the complex metal oxide and the complex
metal oxide has grain sizes in the range of about 1 nm to 150 nm; and
if) remove the pore-forming material under conditions such that the porous structure and composition of the complex oxide is substantially preserved.
Unlike the method described in GB 2 093 816 which leads to the formation of metal oxide phases that simply mirror the phases of the metal oxide particles used as feed
25 particles in that process or which produces a metal oxide phase containing only a single refractory metal from a precursor element, the process of the present invention produces a complex metal oxide phase that incorporates two or more metals (and in some embodiments, many more than two metals) from the precursors or from the precursors and metal oxide particles used as feed materials into the metal oxide phase. It will be
30 understood that the metal oxide phase comprises a matrix of the mete! oxide, with the matrix comprising an oxide structure incorporating the two or more metals. Suitably, the two or more metals are homogeneously distributed throughout the complex metal oxide

WO 2005/070819 PCT/AU2005/000081
9 -*-
phase.
Suitably, a single phase complex metal oxide is formed. However, the present invention also encompasses the formation of a phase of a complex metal oxide and one or more phases of other metal oxides, or the formation of two or more complex metal oxide phases, either with or without any other metal oxide phases being formed. More suitably, each complex metal oxide phase that is formed is a phase pure phase, that is, that phase includes only the desired crystal phase and the absence of undesired crystal phases.
The complex metal oxide may contain two or more metals, such as two or metals selected from the group consisting of metals of atomic number 3,4,11,12,19 to 32,37 to 51, 55 to 84 and 87 to 103. In one embodiment, the two or more metals in the complex metal oxide may include at least one non-refractory metal, such as at least one metal selected from those metals of atomic number 3,4,11,19-21, 23-32, 37-39,41-51, 55-84 and 87-103. In this embodiment, the metal oxide, to addition to containing the non- refractory metals specified above, may also contain other metals such as Ti, Al, Zr, and Mg-
It has surprisingly been found that the porous complex oxides so formed exhibit significantly increased pore volume or surface area with enhanced high temperature stability, such as enhanced high temperature stability to the temperature range of approximately 750°C to 1000°C. The complex oxides suitably further exhibit a substantially homogeneous composition within each phase. Applicants have surprisingly found that complex oxides formed with grain sizes in the above range, together with pore sizes in the above range, have high initial surface areas combined with increased thermal stability of surface area.
25 Applicants have found that if the grain size of the complex oxide is greater than
150 nm, then the material may not have sufficient surface area. Similarly if the pore sizes are greater than approximately 250 nm, sufficient surface area may not be obtained after high temperature ageing. If the pore size is less than approximately 10 nm, high surface area may be obtained, however the pores and therefore surface area may not be
30 thermally stable at elevated temperature.
Unlike GB 2 093 816, the method of the present invention can be used to form non-refractory complex metal oxide phases. The present inventors have surprisingly found that the method of the present invention does not have to be restricted to producing refractory oxides that are difficult to reduce. In contrast, all of the examples of GB 2 093

WO 2005/070819 PCT/AU2005/000081
816 produce oxide phases of alumina, silica, titania, silica-alumina, bona, zeolite, kaoline, or sepiolite. Ail of these metal oxide phases are extremely unreactjve and very difficult to reduce with carbon.
In this aspect of the present invention, the complex oxides so formed may be of any suitable type. The complex metal oxide phase may be a perovskite. The crystal structure is that of the mineral Perovskite', chemical formula CaTiO3. There are numerous different compounds with the perovskite crystal structure, including SrTiO3, Yba2Cu3Ox superconductor, and many La-based perovskites mat are useful as catalysts and as electrodes in solid oxide fuel cells. La-based perovskites include LaMn03, LaCo03, 10 LaFeO3, and LaGa03
Various substitutions of different elements into the oxide lattice may be made to
obtain desired physical properties. For example with perovskites, substitutions may be on
the A site (e.g. Sr for La in LaMrt03) and/or on the B site (e.g. Ni for Mn in LaMn03).
Multiple elemental substitutions on either or both sites can be made to further tailor
physical properties for specific applications. For example, a perovskite composition
where Ln is approximately
, is described in US patent 5,932,146 as being useful for solid oxide fuel cell electrodes.
There are numerous other examples of complex oxides that are being developed for a wide range of applications and the present invention is equally applicable thereto.
The precursor elements useful in the mixture of the present invention may be of any suitable type, depending on the complex oxide to be formed. Any suitable source of metals and metal cations may be used. Mixtures of metals and metal compounds including one or more of oxides, acetates, carbonates, nitrates and the like may be used.
25 The mixture of precursor elements, or complex oxide, and pore-forming material
may be of any suitable type. The mixture may be a solid phase mixture, or formed as a solution, dispersion or the like.
In one embodiment the precursor elements and pore-forming material may be mixed to form a solid phase mixture and the complex oxide being subsequently formed by suitable heat treatment, as discussed below.
In a further embodiment, complex oxide particles may be formed from suitable precursor elements and the pore-forming material mixed with the complex oxide particles to form a mixture.

WO 2005/070819 PCT/AU2005/000081
11
The mixture may alternatively be provided as a solution or dispersion. For . example, a solid phase mixture may first be formed and then dispersed or dissolved in a suitable solvent.
In a further embodiment the precursor element mixture may first be formed In solution and the pore-forming material subsequently added to the solution. Alternatively the precursor elements and at least a portion of pore-forming material may be mixed to form a solid phase mixture and the mixture dissolved in a suitable solvent
Most suitably, the pre-cursor elements form part of a solution that Is mixed with the pore forming material and the metal oxide particles (if used).
10 Where a dispersion or solution is formed, any suitable solvent may be used.
Although inorganic and organic solvents, such as acids (e.g. hydrochloric or nitric acid), ammonia, alcohols, ethers and ketones may be used, water is the preferred solvent
The mixture may preferably include a surfactant The surfactant may be of any suitable type. A surfactant of the type described in International patent application publication number WO 02/42201, to applicants, the entire disclosure of which is incorporated herein by reference, have been found to be suitable.
Some examples include Brij C16H33(OCH2)2CH2H, designated C18 EO2(Aldrich); Brij 30, C12E04, (Aldrich); Brij 56, C10EO10, (Aldrich); Brij 58, C18EO20, (Aldrich); Brij 76, CwEO10, (Aldrich); Brij 78, C10EO20. (Aldrich); Brij 97. C18H36EO10, (Aldrich); Brij 35, C-
20 12EO23, (Aldrich), Triton X-100, CH3C(CH3)2W2CHC^)2C6H4(OC«2CH2)xOH,x = 10(av), (Aldrich); Triton X-114, CH3C(CH3)2CH2C(CH3)2C6H4(OCH)2CH2)50H (Aldrich); Tween 20, poly(ethylene oxide) (20) sorbitan monokayrate (Aldrich); Tween 40, poly(ethytene oxide) (20) sorbitan monopalmitate (Aldrich); Tween 60, polyethylene oxide) (20) sorbitan monostearate (Aldrich); Tween, pory(ethylene oxide) (20) sorbitan monooleate (Aldrich);
25 and Span 40, sorbitan monopalmitate (Aldrich), Terital TMN 6, CH3CH(CH3)CH(CH3)CH2CH2CH(CH3)(OCH2CH2)6OH (Fulka); Tergital TMN 10, CH3CH(CH3)CH(CH3)CH2CH2CH(CH3)(OCH2CH2)1oOH (Fulka); block copolymers having a poly(ethylene oxide)-poly(propylene oxide)-poly(ethylene oxide) (EO-PO-EO) sequence centered on a (hydrophobic) pory(propylene glycol) nucleus terminated by two primary
30 hydroxyl groups; Pluronic L121 («*«, - 4400), EO5PO70EO.5 (BASF); Pluronic L64 U**=2900), EP13PO30EO13 (BASF); Pluronic P65 (mdv=3400), EP20PO30EO20 (BASF); Pluronic P85 {^ = 4600), EO26PO39EO26 (BASF); Pluronic P103 (mdv= 4950), E017PO56EO17 (BASF); Pluronic P123 (A^ = 5800), E02oP07oE02o, (Aldrich); Pluronic F68 W„ = 8400), EO80PO30EO80 (BASF); Pluronic F127 W, (Mav= 12 600), EO106PO70EO106

WO 2005/070819 PCT/AU2005/000081
(BASF); Pluronic F88 (Mav= 11 400),EOW)P039EOioo (BASF); Pluronic 25R4 (Mav = 3600),
»
PO19E033pOi9 (BASF); star diblock copolymers having four EO„-POm chains (or in reverse, the four PO„-EOm chains) attached to an ethylenediamine nucleus, and terminated by secondary hydroxy! groups; Tetronic 908 {MAV = 25 000), (EO113PO22)NCH2CH2PonsEO22)2 (BASF); Tetronic 901 (Mav=4700), (EO3PO18)2NCH2CHzNCPOttEOaJz (BASF); and Tetronic 90R4 (Mav = 7240), (P019E01e)2 NCH2CH2N(E016POi9)2 (BASF).
The above surfactants are non-ionic surfactants. Other surfactants that can be used include:
10 Anionic surfactant
Alcohol Ethoxycarboxylates (R-(O-CH2-H2)x-O-CH-2-CH2-OH) (NEODOX AEC)
Akyl Ethoxy Carboxylic Acids (R-(0-CH2-CH2)x-O-CH2-CO2H) (EMPICOL C)
Sodium dodecy! sulfate CH3(CH2)iiOS03NA
There appears to be several manufacturers. Sigma is an example. 15 Cationic surfactants:
Ctetyltrirnethylammonium chloride CH3(CH2)sWCHafeCI Aldrich
Cetyttrimethylarnmonium bromide CH3(CH2)15N(CH3)3BT Aldrich
Cetytpyridinium chloride C21H36NC1 Sigma.
This list should not be considered to be exhaustive.
20 The pore-forming particles may be of any suitable type. The particles should be of
a suitable size to generate pore sizes in the "Intermediate range" (e.g. pores of diameter approximately 7 nm to approximate 250 nm, preferably approximately 10 nm to approximately 150 nm). Pore-forming particles in the range of approximately 7 nm to 300 nm, preferably approximately 10 nm to 150 nm, more preferably approximately 10 nm
25 to approximately 100 nm, may be used. Carbon particles, preferably carbon black particles, are preferred.
The carbon-containing particles used as pore formers in the method of the present
Invention are believed to facilitate formation of pores of the desired size range by
providing regions where the precursors/precursors and metal oxide particles are
30 prevented from residing whilst the complex metal oxide phase or phases are formed,
followed by subsequent removal of the pore forming particles. Thus, nano-scale pore

WO 2005/070819 PCT/AU2005/000081
13
forming particles are required. This should be distinguished from other methods which use porous carton-containing substrates (such as titer paper or activated carbon) to adsorb liquid phase precursor mixtures followed by removal of the substrate. The size of the substrates used in those methods are typically many orders of magnitude larger than the size of the pore forming particles used in the present invention. Such prior art methods are very difficult to scale up beyond laboratory scale.
In an especially preferred embodiment of the present invention, carbon black is used as the pore forming particles.
The pore-forming particles are preferably removed by heat treatment
10 The components required to form the complex oxide should be homogeneously
dispersed to form the mixture of precursor elements. The elements may be mixed by any suitable method known in the prior art The pore-forming particles should also be dispersed in the mixture, using methods known in prior art including high-speed shearing devices, ultrasonic equipment, roll mills, ball mills, sand mills and the like. Applicants have
15 found that better dispersion of carbon-containing pore forming particles at this stage results in more carbon-containing pore forming particles being intimately mixed with the precursor, and thus more pores being present in the desired size range. In a further preferred embodiment, air is removed from the carbon-containing pore forming particles by vacuum, prior to mixing with the liquid. The liquid is then mixed with the carbon using
20 dispersion methods. This leads to even better dispersions of carbon particles in the solution, intimate mixing of even more carbon particles in the precursor, and more pores in the preferred size range.
The pore-forming particles may, in whole, or in part, be inducted in the mixture prior to dispersion.
25 The treating of the mixture to form the complex oxide may be of any suitable type
which will provide a complex oxide having a substantially homogeneous composition.
The porous complex oxide formation may accordingly, in one embodiment, include two basic steps:
1. Production of particles that are comprised of a mixture of a complex oxide or
30 complex oxide precursor elements and carbon particles.
2. Heat treatment of the particles from step (1) to form the desired oxide phase from
the precursor if a precursor is used, and to substantially remove (e.g. bum out) the
carbon particles to create pores.

WO 2005/070819 PCT/AU2005/006081
Steps (1) and (2) may take place sequentially or contemporaneously.
In step 1, the elements in the oxide precursor should be homogeneously dispersed. If they are not homogeneously dispersed, very high temperatures may be required to evenly disperse the elements and form the correct phase, and such temperatures can decrease the amounts and sizes of pores, or eliminate pores altogether. If the elements are substantially inhornogeneous, required phases and/or phase purities, and grains in the correct size range, will not be attainable.
At least some of the carbon particles should preferably be intimately mixed with the oxide or oxide precursor. If no carbon particles are intimately mixed with the oxide or oxide precursor, and instead the carbon particles are present merely as large agglomerates with no oxide or oxide precursor within the agglomerates, then pores of the correct size may not form. The size of the carbon particles, and the volume of these particles, may be chosen to suit the desired pore size and pore volume.
Any method suitable for producing oxides or oxide precursors with a substantially
homogeneous distribution of elements may be used in the method of the present
invention, provided that carbon particles of the right size may be added to the method, so
that at least some of the carbon particles are intimately mixed with the precursor, and that
the method can produce the oxide with the correct grain size.
Accordingly, in a preferred embodiment of the present invention, the method
further includes the preliminary steps of providing a solution of complex oxide precursor elements including metal cations, a source of carbon particles and a non-tonic, cationic or anionic surfactant, mixing the solution, surfactant and carbon particles such that surfactant micelles are formed and the mixture forms a substantially homogeneous dispersion and heating the mixture to form the complex metal oxide under conditions in which the carbon particles are substantially removed.
In a further preferred embodiment, an oxide precursor may be prepared according to the method described in United States patent number 6,752,979 to applicants, the entire disclosure of which is incorporated herein by reference. This method consists of the following steps:
30 a) preparing a solution containing one or more metal cations;
b) mixing the solution from step (a) with surfactant under conditions such that surfactant micelles are formed within the solution to thereby form a micellar liquid; and

WO 2005/070819 PCT/AU2e05/©00©81

c) heating the micellar liquid from step b) above to form metal oxide, the heating step being undertaken at a temperature and for a period of time to remove the surfactant and thereby form metal oxide particles having a disordered pore structure.
5 In a preferred embodiment of the present invention, carbon black particles are
added either to the solution from a), or the mixture from b), and the heat treatment also substantially removes (bums out) the carbon particles. Preferably the carbon particles are added to the solution of step a), prior to mixing.
In a further preferred embodiment, carbon particles are intimately mixed with the
10 solution of cations in step a), or with the mixture from step b), or both, by methods as
discussed above. Preferably, the carbon black particles are dispersed within the initial
solution and/or the solution-surfactant mixture by either high-speed shearing, sonication.
vacuuation of the particles prior to addition to liquid, or a combination of these.
in a further preferred embodiment, the mixture of complex oxide and carbon particles may be provided by mixing the carbon particles with complex oxide particles, the convex oxide particles have a size range
Alternatively, or in addition, the complex oxide may be formed utilizing the methods Known in the art The complex oxide may be produced utilizing a polymer-complex method, a co-precipitation method or sol-gel method, thermal evaporative method,
20 hydrothermal method or any other suitable method or combination thereof. Examples of such methods are given in US patent no 6139816 (Liu et a!), US patent no 5879715 (Higgens et al), US patent no 5770172 (Linehan et al), US patent no 5698483 (Ong et al), US patent no 6328947 (Monden et al), US patent no 5778950 (Imamura et al) and US patent application publication number 2005/0008777 (McCfeskey et al). The entire
25 disclosure of the above referenced patents and patent applications are herein incorporated by cross reference. The method of the first aspect of the present invention is especially suitable for use in methods for making metal oxides in which a solution containing one or more precursors is mixed with a surfactant or a polymer and is subsequently treated, typically by heating, to form the complex metal oxide.
30 The heat treatment step in the method of the present invention may be carried out
using any suitable equipment known in the art, for example: tube, belt or muffle furnaces, fluid bed furnaces, multiple hearth furnaces, rotary calciners, heated substrates, thermal sprays, spray calciners, etc.

WO 2005/070819 PCT/AU2005/000081

If the oxide or oxide precursor consists of individual particles that are not connected, then the heat treatment should be such that some connections form between the particles prior to carbon burnout If this network is not formed prior to carbon burnout, the pores will collapse.
5 The heat treatment then removes ("bum out") the carbon to create the pores, and
transforms the oxide precursor to the desired oxide crystal structure.
The heating step results in the formation of the metal oxide and the pore structure of the particles. Unlike prior art processes for producing complex metal oxides, the method of the present invention suitably only requires a relatively low applied temperature. Indeed, applied temperatures of less than about 350°C have been found to be suitable in experimental work conducted to date. Preferably, the maximum applied temperature reached in step (c) does not exceed about 750°C, more preferably about 650*0, most preferably about 300°C-350*C.
The heating step may involve a rapid heating to the maximum desired
15 temperature, or it may involve a much more closely controlled heat treatment regime.
Accordingly, in a further preferred embodiment of the present invention, the heat treatment step includes
subjecting the dispersion to a heat treatment profile over a predetermined time to a desired maximum temperature.
20 For example, the heating step may be carried out under a controlled atmosphere.
The heating step may involve heating to a drying temperature (generally below the boiling temperature of the mixture) to dry the mixture, followed by a slow ramp up to the maximum applied temperature, or followed by a series of incremental increases to intermediate temperatures before ultimately reaching the maximum applied temperature.
25 The duration of the heating step may vary widely, with a preferred time in step (c) being from 15 minutes to 24 hours, more preferably 15 minutes to 2 hours even more preferably 15 minutes to 1 hour.
The heat treatment profile may range from approximately 100°C to 750°C, preferably approximately 100°C to 650"C, more preferably 100°C to 300°C. It will be appreciated that the heat treatment profile selected will depend on the particular composition of the complex oxide being treated.
The heat treatment step is preferably conducted under increased oxygen conditions. This may be achieved by providing a suitable airflow within the heating

WO 2005/070819 PCT/AU2005/000081
environment
In a preferred embodiment, the heat treatment should encourage penetration of oxygen into the particles during the carbon burnout phase. Preferred equipment includes fluid bed furnaces and the like. A smaller oxide or oxide precursor/carbon particle size also encourages penetration of oxygen. Applicants have found that better penetration of oxygen leads to better thermal stabilities. Without being held to any particular theory, applicants believe that better oxygen penetration leads to more complete removal of carbon at a lower temperature, and thus maintains a more oxidising atmosphere. Less oxygen leads to retention of carbon at higher temperature, and trapping of reducing gases
10 such as carbon monoxide, leading to a very reducing environment This may lead to some metal formation and retention of this metal to quite high temperatures, which can cause sintering and loss of surface area. Oxygen penetration can be encouraged by causing the oxides to move relative to an oxygen-containing atmosphere to thereby reduce the thickness of the boundary layer around the oxides and thus increase the rate of diffusion
15 of oxygen into the oxide. Processing the oxides in a fluidised bed furnace or in a furnace having an oxygen-containing atmosphere flowing therethrough is suitable.
Furthermore, a heat treatment that allows bum out of carbon at lower temperatures eg. at temperatures of approximately 100°C to 750°C, preferably approximately 100"C to 650°C, more preferably approdimately 100°C to 300°C is preferred. Bum out at sufficiently high temperatures can cause an uncontrolled exothermic bum off of the carbon , which severely diminishes the surface area. Also applicants believe that retention of carbon to high temperatures diminishes high temperature stability by the mechanisms previously discussed.
Close control of the bum out step should be maintained in order to avoid excursions out of the desired temperature profile of the burnout step. For example, close monitoring of the temperature during bum out could be used. If an undesired increase in the temperature is observed (indicating excess energy production due to an increase in the rate of exothermic burning of carbon), the atmosphere supplied to the furnace may be controlled by reducing the partial pressure of oxygen. One way of achieving this outcome is to inject extra nitrogen or other inert or non-reactive gas. This not only reduces the partial pressure of oxygen, it also acts to cool the furnace. As it is also desired to maintain an oxidizing atmosphere during bum out of the carbon containing pore formers, this method of controlling the temperature should be used only where rapid response to an impending temperature excursion is required, or where it is apparent that an excursion

WO 2005/070819

PCT/AU2005/000081


has occurred and it is necessary to quickly reduce or stop the oxidation of carbon (for example, for safety reasons). Alternatively, additional cooling may be provided. Instead of closely monitoring the temperature during burn out, it may also be possible to obtain satisfactory results by maintaining the temperature during bum out below a specified maximum temperature. The specified maximum temperature can vary widely in accordance with the particular complex metal oxide being formed. As a further alternative, the method of the present invention may be operated under specified operating conditions (such as oxygen flow rate and furnace cooling) and a quality control protocol maintained that rejects any unacceptable product The presence of unacceptable
10 product may be determined by testing of the product or by a monitoring technique that monitors one or more operating parameters and rejects any product formed if the one or more parameters moves outside of a specified range of values. For example, a simple thermocouple may be used to monitor the maximum temperature reached during the method and if the maximum temperature exceeds a specified maximum, the product may
15 be rejected, or if a visual inspection shows that the mixture or product is red hot during processing, the product may be rejected.
In a second aspect of the present invention, there is provided a porous complex oxide material, wherein the complex oxide material exhibits high temperature stability and including an oxide composition represented by the general formula:
20
wherein
A is a mixture of lanthanide elements;
B is a divalent or monovalent cation;
M is an element or mixture of elements selected from the group consisting of 25 elements of an atomic number from 22 to 32,40 to 51, and 73 to 83; and
x is a number in the range 0.1 Preferably, the complex oxide material is made by the method of the first aspect of the present invention.
The complex oxide material may be of the correct phase (e.g. single phase or
30 multiple phase) with an initial surface area greater than approximately 15m2/g, preferably
greater than approximately 20m2/g, more preferably greater than approximately 30m2/g,
and a surface area after ageing for 2 hours at 1000°C in air greater than approximately

WO 2005/070819 PCT/AU200S/000081
5m2/g, preferably greater than approximately 10m2/g, more preferably greater than approximately 15m2/g.
The complex oxide material may exhibit a substantially homogeneous composition.
The complex oxide material may include a perovskite material.
5 The complex oxide material may generally exhibit an average grain size of
approximately 2 nm to approximately 150 nm, preferably approximately 2 to 100 nm and has pores ranging in size from approximately 7 nm to approximately 250 nm, more preferably approximately 10 nm to approximately 150 nm. However, the average grain and pore size of the complex oxide materials may vary, depending on the specific complex oxide selected.
For example, for a complex oxide material of the CeZr02 type, average grain size may preferably fad at the lower end of the range, e.g. at approximately 2 to 50 nm, more preferably approximately 2 to 10 ran, with pores In the range of approximately 7 nm to 50 nm, more preferably approximately 7 nm to 30 nm.
15 A complex oxide material of the lanthanum manganate type may exhibit an
average grain size of approximately 2 nm to 100 ran, more preferably approximately 2 to 30 nm, with pores in the range of approximately 15 run to 200 nm, more preferably approximately 15 nm to 150 ran.
More preferably, the complex oxide material may exhibit a substantially disperse 20 pore size range.
In a third aspect the present invention provides a method of producing porous non-refractory metal oxide, the method including providing a mixture of
a) one or more precursor elements suitable to produce the non-refractory
metal oxide, particles of non-refractory oxide, oxide particles that are
25 precursors of the nor-refractory oxides, or mixtures of two or more thereof;
and
b) a particulate carbon-containing pore-forming material selected to provide
pore sizes in the range of approximately 7 nm to 250 nm,
and treating the mixture to
30 i) form the porous non-refractory metal oxide and the non-refractory metal
oxide has grain sizes in the range of about 1 nm to 150 nm; and

WO 2005/070819 PCT/AU2005/000081
20
ii) remove the pore-forming material under conditions such that the porous structure and composition of the non-refractory metal oxide is substantially preserved.
Suitably, in step (i) above, one or more of the precursor elements from (a) above 5 are incorporated into a phase of the non-refractory metal oxide
The one or more precursor elements may include one or more metal compounds including one or more metals selected from those metals of atomic number 3, 4, 11, 19-21, 23-32, 37-39, 41-51, 55-84 and 87-103. The one or more metal compounds may be oxides, acetates, carbonates, nitrates and the like.
10 Unlike the first aspect of the present invention, the method of the third aspect of
the present invention encompasses the formation of porous metal oxides of the specified grain size and pore size that has only a single metal in the oxide phase (i.e. not a complex oxide). However, the third aspect of the present invention is restricted to forming non-refractory metal oxides. It is a very surprising result that such r»n-refractory metal oxides
15 can be formed in this manner because the presence of the carbon-containing pore forming particles was thought to be likely to cause reduction of the non-refractory metal oxide during the step of removing the pore forming particles which, of course, would destroy or substantial compromise the metal oxide phase. However, the present inventors have discovered that the method of the third aspect of the present invention can,
20 in fact, form such non-refractory metal oxides.
In one embodiment, the method of the third aspect of the present invention provides the precursor elements) as a solution or dispersion. For example, a solid phase mixture may first be formed and then dispersed or dissolved in a suitable solvent.
In one embodiment the precursor elements and pore-forming material may be mixed to form a solid phase mixture and the oxide being subsequently formed by suitable heat treatment, as discussed below.
In a further embodiment, oxide particles may be formed from suitable precursor elements and the pore-forming material mixed with the oxide particles to form a mixture.
The mixture may alternatively be provided as a solution or dispersion. For
30 example, a solid phase mixture may first be formed and then dispersed or dissolved in a
suitable solvent
In a further embodiment, the precursor elements) may first be formed in solution and the pore-forming material subsequently added to the solution. Alternatively the

WO 2005/070819 PCI7AU200S/000081
--20--
precursor elements and at least a portion of pore-forming material may be mixed to form a solid phase mixture and the mixture dissolved in a suitable solvent
Where a dispersion or solution is formed, any suitable solvent may be used. Although inorganic and organic solvents, such as acids (e.g. hydrochloric or nitric acid), ammonia, alcohols, ethers and ketones may be used, water is the preferred solvent
The method of the third aspect of the present invention is especially suitable for use in methods for making metal oxides in which a solution containing one or more precursors is mixed with a surfactant or a polymer and is subsequently treated, typically by heating, to form the metal oxide.
10 Other features of embodiments of the third aspect of the present invention are as
described with reference to various embodiments of the present invention and, for convenience and brevity, need not be described again.
The method of the third aspect of the present invention has been used to make copper oxide that exhibits a large specific surface area. Other oxides, both complex oxides and oxides containing a single metal species, have also been made by the method of the second aspect of tile invention.
The methods of the first and third aspects of the present invention are particularly suited to making metal oxide powders.
20 Description of the drawings
Figure 1 shows pore size distributions from materials prepared in Examples 1 and 2, following heat treatment to 650°C;
Figure 2 shows surface areas obtained after heat treatment at 650°C and 800°C, as a function of La203 content for examples 18-22;
25 Figure 3 shows pore volumes obtained after heat treatment at 650°C as a function of La2Oa content for examples 18-22
Figures 4a and 4b show XRD patterns of CeO.45ZrO.45LaO.10x heat treated to 450°C a) prepared without carbon (example 28) and b) with carbon (example 29)
Figures 5a and 5b show XRD patterns of Ce0.45Zr0.45La0.1Ox heat treated to 800°C a) 30 prepared without carbon (example 28) and b) with carbon (example 29)

WO 2005/070819 PCT/AU2005/000081
EXAMPLES Example 1
Lao.8Sr0.2Ni0.04Pdao6Mno.9O3 was prepared according to the following method. A solution was prepared by dissolving 149g La(N03)3.6H20, 18.2g SrCNO3)2 6.86g Pd(N03)2.x H2O , 2.04g NiCO3 and 138.3g of Mn{N03)2 in water solution containing 233g/l Mn, in a solution comprised of 135g water and 12g HNO3(70%). 119g of this solution was mixed with 72g Brij 30 surfactant The mixture was heated slowly to 300°C. The dried product was then heat-treated 0.5h at 300°C, 350°C, 400°C, 450°C, 500°C, 600°C and 650°C in a tube furnace with airflow.
10 XRD showed the material was single-phase perovskite. The surface area obtained
after this heat treatment was 17.&irVg. Fig. 1 shows the pore size distribution. TEM showed the average grain size was ~50nm. After heat treatment for 2h at 1000°C, the surface area was 6.901^.
15 Example 2
was prepared in the same manner as example 1, except that 16.15g of carbon black (Cabot Monarch 1300, average primary particle size 13 run, DBP oil absorption 100cc/g, nitrogen surface area 560rrrVg) was mixed into the solution with a magnetic stirrer, prior to mixing with surfactant This solution/carbon black
20 mixture was dispersed by a high-speed shearer, then mixed with surfactant, then dispersed again. The heat treatment applied was identical to example 1.
XRD showed the material was single-phase perovskite. The surface area obtained after the heat treatment was 24.7rrrVg. Fig. 1 shows the pore size distribution. TEM showed the average grain size was ~50nm. After heat treatment for 2h at 1000°C, the
25 surface area was 10.04m2/g.
It will be noted that incorporation of the carbon black has provided significantly more large pores, and the material is more stable at high temperature.
Example 3
30 Lao.8Sro.2Nio.04Pdo.06Mno.BO3 was prepared in the same manner as example 2, except that the heat treatment consisted of placing material heated to 300°C directly at 1000°C. After heat treatment for 2h at 1000°C, the surface area was 1.9m2/g.

WO 2005/070819 PCT/AU2005/000081
-23"-
This example shows that incorporation of carbon black in the perovskite precursor is not in itself sufficient to provide high temperature stability. The heat treatment conditions used in this example caused the destruction of the surface area of the material. It is postulated that the large step change in temperature used in this example caused an
5 uncontrolled burnout of carbon from the oxide, which led to localised regions of very high temperature. This is postulated to have caused sintering and reduction of the metal oxide. In other words, the composition and pore structure of the metal oxide was not maintained during carbon bum out.
10 Example 4
Lao.8Sr0^Nio.o4Pdoj»Mno.o03 was prepared in the same manner as example 3, except that no airflow was present in the tube furnace. The remainder of the procedure was the same.
XRD showed the material was perovskite phase. The full width half maximum
15 (FWHM)of the peaks was similar to FWHMs of peaks in examples 1 and 2, indicating that
the grain sizes were similar (i.e. around 50nm). The surface area obtained after this heat treatment was 22.1m2^. After heat treatment for 2h at 1000°C, the surface area was 9.1 m2/g.
Comparison of this result with that from example 2 (10.2m2/g) shows the beneficial
20 effect of increased oxygen during the heat treatment The present inventors believe that less oxygen provides reducing conditions in the furnace, which can lead to formation of metal in the material. This can cause sintering and a reduction in surface area and pores.
Examples 5-8
25 La0.8Sr0.2Nia04Pdo.06MN0.6O3 was prepared in similar manner to example 2, with
varying amounts of carbon black (Raven 850).
XRD showed the materials were perovskite phase, and peak FWHMs were similar to examples 1 and Z
The surface areas, pore volumes and pore size distributions are shown in Table 1 30 and were clearly dependent upon the amount of carbon black used.

WO 2005/070819 PCT/AU2005/000081
-24-
Table l

Example Amount ofcarbon black(9) Surface areaat650°C(m2/g) Pore volume2-200nm dia.(cc.g) Pore volume 10-200nm dia. (cc.g) Pore volume50-200nm dia.(cc.g)
5 8 37 0.22 0.2 0.1
6 16 44 0.33 0.31 0.18
7 32 44 0.34 0.32 0.22
8 48 51 0.41 0.39 0.25
Examples 9-11 LaasSro2ie2PoVoeMrto.sOs examples with different carbon blacks
Examples showing the effect of using different types of carbon black pore formers
5 on surface areas and pore structures obtained for the complex oxide Lao8STo.2Nio.04Pdoo6Mno.9O3-
Oxides were formed using the method described in example 2, except that different types of carbon black were used.
XRD showed that all compounds were perovskite structure, and peak FWHMs
10 were similar to examples 1 and 2 indicating that the grain sizes were around 50rm Results for surface areas and pore structures obtained are shown in Table 2.
Table 2

Example Carbon Black Surface Area m*/g Pore Volumes cc/g
Type Particle Size (nm) OilAbsorption(cc/g) 650°C 1000°C 3-200nm >10nm >50 nm
9 Monarch 280 45 137 25 11.3 0.17 0.16 0.10
10 Monarch 1300 13 100 23 9.8 0.22 0.21 0.14
11 Mogul L 24 62 32 12.0 0.25 0.23 0.16

WO 2005/070819 PCT/AO2005/000081
-25-
Examples 12-13
In examples 12 and 13, LaaosSr0.2Nio.o4Pdo.o6Mnoa03 was prepared in the same manner as examples 1 and 2 respectively (without carbon and with carbon) except that polyethylene
5 glycol (molecular weight 4000) was used instead of surfactant XRDs showed perovskite phase, and a minor impurity peak example 12. The surface areas and pore volumes are shown in table 3. The incorporation of carbon has dearly increased the number of larger pores.
Table 3

Example Surface Area mz/g Pore Volumes cc/g
650°C 3-200rtm >10nm >50nm
12 17.5 0.12 0.105 0.04
13 31.7 0.22 0.2 0.15
10
Examples 14-15
Lao.8Sr0.2Nio.o4Pdao$Mno.903 was prepared via a co-predpitation technique, examples 14 and 15 carried out with and without carbon (17.8g Monarch 1300), respectively. A solution was prepared in the same manner as example 1. Another solution
15 was prepared by dissolving 55g of ammonium oxalate in 960g of water. These solutions were combined by slowly adding each solution into a stirred vessel to produce predpitates. The precipitates were washed, filtered and dried at ~100°C, then heat treated in the same manner as example 1.
XRDs showed perovskite phase and some separate peaks. The surface areas and
20 pore volumes are shown in table 4.
Clearly the effect of carbon on the pore distribution is very much smaller than observed in the examples using surfactant and polyethylene glycol. Without being held to any particular theory, the inventors believe that the larger liquid volumes, often required for co-predpitation, result in very disperse predpitates particles and carbon particles. This
25 may make it very difficult to sufficiently disperse the carbon partides amongst the predpitates to produce the desired pores.

WO 2005/070819

PCT/AB2005/000081

-26--
Table 4

Example Surface Area m*/g Pore Volumes cc/g
650°C 3-200nm 10nm >50nm
14 19 0.105 0.09 0.025
15 17 0.115 0.11 0.06
5 Examples 16-21 Ce00.54Zrft^H-a«jwPrum06Ox examples with different types of carbon Mack
These examples show the effect of using different types of carbon black pore formers on surface areas and pore structures obtained for the complex oxide Ceos4Zro.37Lao.03Pro.06Qx.
10 Oxides of composition Cea54Zr0^7Lao.o3Pro^60JC were prepared by dissolving
appropriate amounts of cerium nitrate, zirconium carbonate, lanthanum nitrate and praseodymium nitrate in a water/nitric acid solution. 33g of carbon black was dispersed in the solution using a high speed shearer, 70g of Erunon LA4 surfactant was added and the rnixture was dispersed again. The mixture was heated slowly to 300°C. The dried product
15 was then neat-treated for 0.5h at 300°C, 350°C, 400°C, 450°C, 500°C, 600°C and 650°C in a tube furnace with airflow.
XRD showed the samples were single phase, and TEM showed the average grain size of the material prepared in these examples to be approximately 5-10nm after heating to 650°C. Other examples exhibited similar XRD peak FWHMs, indicating similar grain
20 sizes.
Surface areas and pore volumes for the samples with different carbon blacks are shown in Table 5 below, together with particle size and oil absorption values for the carbon blacks. Also shown are surface areas obtained after heat treatment for 2h at 1000°C.

WO 2005/070819 PCT/AU2005/000081
27
-26-
Table 5

Example Carbon Black Surface Area Pore Volumes cc/g
Type Particle Size (nm) OilAbsorption(cc/g) 650°C 1000°C 3-200nm >10nm >50nm
12 Monarch 280 45 137 101 13.9 0.3 0.2 0.12
13 Raven 2500 13 65 k 112 17 0.41 0.32 0.14
14 Raven 1190 21 62 116 18.4 0.43 0.33 0.17
15 Raven 410 101 68 108 12.7 028 0.175 0.09
16 Raven 850 34 75 110 19.5 0.38 0.33 0.15
17 Raven 460 67 61 99 18.3 0.40 0.3 0.17

Clearly the pore structure and surface area can be altered by use of carbon blacks with 5 different morphological features.
Examples 22-26 Examples with excess La content
La0.8Sr0.2Mno.eNio.MPdooeOa + La2Os materials were prepared in a similar manner to
previous examples. The amount of la^D3 was varied between 2.5wt% and 20wt%. XRD
10 showed perovskite phase, plus increasing amounts of La2O3 phase with increasing excess

WO 2005/070819 POYAU2005/000081
28
La203. Figures 2 and 3 show surface areas obtained after heat treatment at 650°C and 8O0°C, as a function of La2O3 content
This example illustrates that the pore structure of the oxide composition may be altered by incorporation of varying amounts of a second phase.
5 Example 27 excess CeO2 (7t>)
Lao.eSro.2Nio.o4Pdo.08Mn0.9O3 + 10wt% Ce02 was made In a similar manner to example 1. This composition was chosen specifically to provide a perovskite phase and a separate Ce02 phase (this amount of excess Ce02 is unable to be incorporated into the perovskite phase). XRD showed the material was perovskite phase and Ce02. The
10 surface area obtained was 28.9m2/g, and the volume of pores between 3nm and 200nm was 0.26cc/g, between 10nm and 200nm the pore volume was - 0.25cc/g, and between 50nm and 200nm it was ~0.175cc/g. After heat treatment for 2h at 1000°C the surface area was 11.7m2/g.
Examples 28 and 29 Ce*49Zro.45La0.1Ox via hydrothermal method
15 Ceo.45Zro.45Lao.1Ox was prepared using a hydrothermal method similar to known
methods for similar compounds.
49.3g of cerium (IV) ammonium nitrate, 27.4g of zirconium carbonate and 8.66g of lanthanum nitrate were dissolved in a solution containing 940g waiter and 63g nitric acid (70%). This mixture was heated for ~24h at ~95°C, causing precipitates to form. 150ml of
20 ammonia solution (%) was finally added and the precipitates were washed, separated via filtration, and dried at ~ 100°C. Heat treatment was then carried out The temperature was increased from 150 °C, with 0.5h steps at 150°C, 200 °C, 250 °C, 300 °C, 350 °C, 400 °C, and 450 °C. The surface area following this heat treatment was 145 m2/g. Pore volumes are shown in table 6 and the XRD is shown in figure 4.
25 Comparative example 29
Ceo.45Zro.45Lao.1Ox was prepared in the same manner as example 28 except that 32g of Raven 850 carbon black was added to the solution and dispersed with a high speed shearer. The hydrothermal heating and heat treatments were then carried out in the same manner. The surface area of this sample was ~ 100mz/g. Pore volumes are shown
30 KI Table 6 and the XRD is shown in Figure 4. In comparison to example 28, it can be seen that incorporation of carbon has increased the volume of larger pores. However the XRDs

WO 2005/070819 PCT/AU2005/000081
show that the incorporation of carbon has resulted in the formation of an oxide having somewhat separated phases that are ceria-rich and zirconia-rich. This is demonstrated by the double peaks, with the separate peaks shifted towards the Ce02 and Zr02 peak positions. Thus the carbon has affected the hydrothermal precipitation process, causing
5 significant separation of the different elemental species and increasing the pore volume. This effect is shown even more dearly in figure 5, which shows XRDs of both example compounds that were given an additional heat treatment of 0.5h at 800°C.
Table 6

Example e Surface Area m*/g Pore Volumes cc/g
650°C 3-200nm >10nm >50 nm
28 145 0J2 0.04 0
29 100 0.39 0.31 0.15
10 Examples 30-32 CuO
CuO was made using similar methods to previous examples. Example 30 was heat treated slowly to 350°C, with 0.5h holds at 150°C, 200°C, 250°C, 300°C and 350°C. Example 31 was heat treated similarly, however it was observed that this sample considerably overheated during heat treatment, exhibiting a red glow in areas indicating
15 that the sample experienced much higher temperatures than 350°C. Example 32 had a slower heat treatment, with an additional step for 1h at 225°C. This heat treatment was found to produce material with more consistent properties and high temperature excursions were not observed.
XRDs for all materials exhibited CuO phase only. The surface areas and pore 20 volumes obtained are listed in Table 7.
Table 7

Example Surface Area Pore Volumes cc/g
650°C 3-200nm >10nm >5f> nm

WO 2005/070819 PCT/A1J2005/000081

30 96 02. 0.11 0.04
31 57.4 0.13 0.1 0.04
32 130 0.25 0.18 0.065

5
10

These examples show, surprisingly, heat-sensitive materials can be produced using the methods of the present invention, using appropriate heat treatment
It will be understood that the invention disclosed and defined in this specification extends to or alternative combinations of two or more of the individual features mentioned or evident from the text or drawings. AH of these different combinations constitute various alternative aspects of the invention.
It will also be understood that the term "comprises' (or its grammatical variants) as used in this specification is equivalent to the term Induded" and should not be taken as excluding the presence of other elements or features.

31
We Claim:
1. A method of producing porous complex oxides, the method including
providing a mixture of:
a) precursor elements suitable to produce the complex oxide; or
b) one or more precursor elements suitable to produce particles of the complex oxide and one or more metal oxide particles; and
c) a particulate carbon-containing pore-forming material selected to provide pore sizes in the range of approximately 7 nm to 250 nm;
wherein at least one of the precursor elements is present in the form of a
solution,
and treating the mixture to
(i) form the porous complex oxide in which two or more of the precursor
elements from (a) above or one or more of the precursor elements and one or
more of the metals in the metal oxide particles from (b) above are
incorporated into a phase of the complex metal oxide and the complex metal
oxide has grain sizes in the range of about 1 nm to 150 nm; and
(ii) remove the pore-forming material under conditions such that the
porous structure and composition of the complex oxide is substantially
preserved.
2. A method as claimed in claim 1, wherein said pore forming material has a particle size falling within the range of from about 7 nm to about 300 nm
3. A method as claimed in claim 1 wherein the mixture further includes a surfactant or a polymer.
4. A method as claimed in claim 1 wherein a single phase complex metal oxide is formed.
5. A method as claimed in claim 1 wherein a phase of a complex metal oxide and one or more phases of other metal oxides are formed.

6. A method as claimed in claim 1 wherein two or more complex metal oxide phases, either with or without any other metal oxide phases, are formed.
7. A method as claimed in claim 1 wherein each complex metal oxide phase that is formed is a phase pure phase.
8. A method as claimed in claim 1 wherein the pore-forming particles have a particle size in the range of approximately 10 nm to 150 nm.
9. A method as claimed in claim 1 wherein the pore-forming particles have a partide size in the range of approximately 10 nm to approximately 100 nm.
10. A method as claimed in claim 1 wherein the pore forming particles are particles of carbon black.
11. A method as claimed in claim 1 wherein components used to form the complex oxide are homogeneously dispersed to form the mixture of precursor elements.
12. A method as claimed in claim 11 wherein the pore-forming partides are dispersed in the mixture using a method selected from high-speed shearing, ultrasonic mixing, roll milling, ball milling or sand milling.
13. A method as claimed in claim 1 wherein air is removed from the carbon-containing pore forming partides by vacuum, prior to forming the mixture.
14. A method as claimed in claim 1 wherein the method includes the steps of providing a solution of complex oxide precursor elements including metal cations, a source of carbon particles and a non-ionic, cationic or anionic surfactant, mixing the solution, surfactant and carbon particles to form the mixture such that surfactant micelles are formed and the mixture forms a substantially homogeneous dispersion and heating the mixture to form the complex metal oxide under conditions in which the carbon particles are substantially removed.

33
15. A method as claimed in claim 14 wherein the method includes the steps of:
a) preparing a solution containing one or more metal cations;
b) mixing the solution from step (a) with surfactant under conditions such that surfactant micelles are formed within the solution to thereby form a micellar liquid; and
c) heating the micellar liquid from step (b) above to form metal oxide, the heating step being undertaken at a temperature and for a period of time to remove the surfactant and thereby form metal oxide particles having a disordered pore structure.
wherein carbon blank particles are added either to the solution form (a) or the mixture from (b) and the heat treatment also substantially removes (burns out) the carbon black particles.
16. A method as claimed in claim 15 wherein the carbon particles are added to the solution of step (a) prior to mixing.
17. A method as claimed in claim 1 wherein the step of treating the mixture to form the complex metal oxide and remove the carbon-containing particles comprises heating the mixture to a temperature in the range of form about 100*C to about 750/C.
18. A method as claimed in claim 17 wherein the temperature falls within the range of 100'C to about 650"C.
19. A method as claimed in claim 17 wherein the temperature falls within the range of 100°C to about 300*C.
20. A method as claimed in claim 1 wherein one or more of temperature, cooling rate or partial pressure of oxygen is controlled during the heat treatment step to minimize or avoid reduction of the complex metal oxide during removal of the carbon containing particles.

34
21. A method as claimed in claim 20 wherein the temperature is controlled such that a specified maximum temperature is not exceeded during removal of the carbon containing particles.
22. A method as claimed in claim 1 wherein the metal oxide contains two or more metals of atomic number 3, 4, 11, 12, 19 to 32, 37 to 51, 55 to 84 and 87 to 103.
23. A method of producing porous metal oxide, the method including providing a mixture of:

a) one or more precursor elements suitable to produce the non-refractory metal oxide, at least one of the one or more precursor elements being in the form of a solution; and
b) a particulate carbon-containing pore-forming material selected to provide pore sizes in the range of approximately 7 nm to 250 nm; and
c) a surfactant or a polymer,
and treating the mixture to:
(i) form the porous metal oxide in which the non-refractory metal oxide has grain sizes in the range of about 1 nm to 150 nm; and
(ii) remove the pore-forming material under conditions such that the porous structure and composition of the metal oxide is substantially preserved.
24. A method as claimed in claim 23 wherein the method includes the steps of:
preparing a solution containing one or more metal cations;
mixing the solution with surfactant under conditions such that surfactant micelles are formed within the solution to thereby form a micellar liquid; and heating the micellar liquid to form metal oxide, the heating step being undertaken at a temperature for a period of time to remove the surfactant and thereby form metal oxide particles,
wherein carbon black particles are added to the solution and the heat treatment also substantially removes (burns out) the carbon black particles.

35

25. A method as claimed in claim 23 wherein said pore forming material has a particle size falling within the range of from about 7 nm to about 300 nm.
26. A method of producing porous complex oxides; and a method of producing porous metal oxide substantially as herein described with reference to the foregoing examples and accompanying drawings.
Dated this 31 day of July 2006
OMANA RAMAKRISHNAN
Of K&S PARTNERS
AGENT FOR THE APPLICANT(S)

36
METHOD FOR MAKING METAL OXIDES
ABSTRACT
A method for producing porous complex oxides includes the steps of providing a mixture of a) precursor elements suitable to produce the complex oxide; or b) one or more precursor elements suitable to produce particles of the complex oxide and one or more metal oxide particles; and c) a particulate carbon-containing pore-forming material selected to provide pore sizes \n the range of approximately 7 nm to 250 nm, and treating the mixture to (i) form the porous complex oxide in which two or more of the precursor elements from (a) above or one or more of the precursor elements and one or more of the metals in the metal oxide particles from (b) above are incorporated into a phase of the complex metal oxide and the complex metal oxide has grain sizes in the range of about 1 nm to 150 nm; and (ii) remove the pore-forming material under conditions such that the porous structure and composition of the complex oxide is substantially preserved. The method may be used to produce non-refractory metal oxides as well.

Documents:

921-MUMNP-2006-ABSTRACT(25-01-2011).pdf

921-MUMNP-2006-ABSTRACT(5-4-2010).pdf

921-MUMNP-2006-ABSTRACT(GRANTED)-(6-8-2012).pdf

921-mumnp-2006-abstract.doc

921-mumnp-2006-abstract.pdf

921-mumnp-2006-cancelled pages(3-11-2006).pdf

921-MUMNP-2006-CANCELLED PAGES(5-4-2010).pdf

921-MUMNP-2006-CLAIMS(AMENDED)-(25-01-2011).pdf

921-MUMNP-2006-CLAIMS(AMENDED)-(5-4-2010).pdf

921-MUMNP-2006-CLAIMS(GRANTED)-(6-8-2012).pdf

921-mumnp-2006-claims.pdf

921-mumnp-2006-claims.rtf

921-mumnp-2006-correspondance-recieved.pdf

921-MUMNP-2006-CORRESPONDENCE(12-12-2011).pdf

921-mumnp-2006-correspondence(14-1-2008).pdf

921-MUMNP-2006-CORRESPONDENCE(22-4-2010).pdf

921-mumnp-2006-correspondence(ipo)-(19-01-2011).pdf

921-MUMNP-2006-CORRESPONDENCE(IPO)-(6-8-2012).pdf

921-mumnp-2006-description (complete).pdf

921-MUMNP-2006-DESCRIPTION(GRANTED)-(6-8-2012).pdf

921-MUMNP-2006-DRAWING(25-01-2011).pdf

921-MUMNP-2006-DRAWING(5-4-2010).pdf

921-MUMNP-2006-DRAWING(GRANTED)-(6-8-2012).pdf

921-MUMNP-2006-FORM 1(25-01-2011).pdf

921-mumnp-2006-form 1(3-11-2006).pdf

921-mumnp-2006-form 1(3-8-2006).pdf

921-MUMNP-2006-FORM 1(5-4-2010).pdf

921-mumnp-2006-form 18(14-1-2008).pdf

921-MUMNP-2006-FORM 2(GRANTED)-(6-8-2012).pdf

921-MUMNP-2006-FORM 2(TITLE PAGE)-(25-01-2011).pdf

921-MUMNP-2006-FORM 2(TITLE PAGE)-(5-4-2010).pdf

921-MUMNP-2006-FORM 2(TITLE PAGE)-(GRANTED)-(6-8-2012).pdf

921-mumnp-2006-form 26(3-11-2006).pdf

921-MUMNP-2006-FORM 3(25-01-2011).pdf

921-mumnp-2006-form 3(3-8-2006).pdf

921-MUMNP-2006-FORM 3(5-4-2010).pdf

921-mumnp-2006-form 5(3-8-2006).pdf

921-MUMNP-2006-FORM PCT-IB-304(22-4-2010).pdf

921-MUMNP-2006-FORM PCT-IB-304(25-01-2011).pdf

921-mumnp-2006-form-1.pdf

921-mumnp-2006-form-2.doc

921-mumnp-2006-form-2.pdf

921-mumnp-2006-form-3.pdf

921-mumnp-2006-form-5.pdf

921-mumnp-2006-form-pct-ipea-401.pdf

921-mumnp-2006-pct-search-report.pdf

921-MUMNP-2006-PETITION UNDER RULE 137(5-4-2010).pdf

921-MUMNP-2006-REPLY TO EXAMINATION REPORT(25-01-2011).pdf

921-MUMNP-2006-REPLY TO EXAMINATION REPORT(5-4-2010).pdf

921-mumnp-2006-wo international publication report(3-8-2006).pdf

abstract1.jpg


Patent Number 253592
Indian Patent Application Number 921/MUMNP/2006
PG Journal Number 32/2012
Publication Date 10-Aug-2012
Grant Date 06-Aug-2012
Date of Filing 03-Aug-2006
Name of Patentee VERY SMALL PARTICLE COMPANY PTY LTD
Applicant Address 31 Westgate Street, Wacol, Queensland 4076,
Inventors:
# Inventor's Name Inventor's Address
1 Jose Antonio Alarco Unit 1,44 Payne Street, Indooroopilly,QLD 4068,
2 Peter Cade Talbot 1 Welcome Street,Chapel Hill, QLD 4069,
3 Geoffrey Alan Edwards 27 Keywest Avenue, Coolum Beach,QLD 4573,
PCT International Classification Number C01B13/14, C04B38/06
PCT International Application Number PCT/AU2005/000081
PCT International Filing date 2005-01-24
PCT Conventions:
# PCT Application Number Date of Convention Priority Country
1 60/538,867 2004-01-23 U.S.A.
2 60/582,905 2004-06-25 U.S.A.