Indian Patents. 252503:METHOD OF CLEANING MONODISPERSE POLYMER PARTICLES

Title of Invention	METHOD OF CLEANING MONODISPERSE POLYMER PARTICLES
Abstract	A process for the preparation of monodisperse polymer particles which are formed by contacting monomers with aqueous dispersions comprising monodisperse swellable seed polymers/oligomers, and initiating polymerisation in the presence of a steric stabiliser. The resulting swollen seed particles are characterised by the particle mode diameter.

Full Text	This invention relates to a method of cleaning monodisperse polymer particles, in particular particles produced by swelling a seed polymer (or oligomer) particle in aqueous dispersion and polymerizing a monomer within the swollen seed particles, which method comprises contacting said monodisperse polymer particles with butyl acetate. Monodisperse polymer particles (i.e. particles with a coefficient of, variation of less than 10%, preferably less than 5% and' more preferably less than 3%) have been commercially available for several years and find applications in many technical fields, e.g. in pharmaceuticals, in separation processes, as toners, as filters, as spacers, etc. Polymer beads may be produced by diffusing a monomer and a polymerisation initiator (or catalyst) into polymer seeds in an aqueous dispersion. The seeds swell and following initiation of polymerization, e.g. by heating to activate the initiator, larger polymer particles are produced. The maximum volume increase due to swelling and polymerization is about x5 or less. The late Professor John Ugelstad found that the capacity of the seeds to swell could be increased to a volume increase of xl25 or even more if an organic compound with relatively low molecular weight and low water solubility is diffused into the seeds before the bulk of the monomer is used to swell the seeds. The effect is based on entropy and not particularly in the chemical nature of the organic compound. Conveniently the polymerisation initiator may be used for this purpose. Organic solvents, e.g. acetone or a relatively small portion of the monomer, may be used to enhance diffusion of the organic compound Into the seeds. This "Ugelstad polymerization process", which is described for example in EP-B-3905 {Sinter) and US-A-4530956 (Ugelstad), may be used to produce monodisperse particles, if necessary carrying out several swelling and polymerization stages to reach the desired particle size. WO 92/16581 (Cornell Research Foundation) also describes the preparation of monodisperse particles, particularly macroporous polymer beads. The process described uses a three phase emulsion containing soluble polymer particles, a monomer phase, and water. The three phase emulsion also includes an emulsifier and a suspension stabiliser. The polymer particles undergo swelling absorbing the monomer which is then polymerized. In' this process the soluble polymer seed particles act as both shape/size regulators and as a porogen. The initial (i.e. before swelling) particles have a diameter of from about 0.5 to 10 /zm, 2 to 5 jun being most preferred, and are produced by conventional techniques, such as emulsion or dispersion polymerization. In a simplified version of the Ugelstad process the enhanced capacity for swelling may be achieved simply by the use of oligomeric seed particles, e.g. where the oligomer weight average molecular weight corresponds to up to 50 monomer units or up to 5000 Dalton. The processes described in EP-B-3905 and US-A-4530956 (the disclosures of which are hereby incorporated by reference) and the simplified Ugelstad process are relatively complex and inefficient. The processes described in WO 92/16581 do not especially improve upon those disclosed in EP-B-3905 and US-A-4530956. The essence of WO 92/15681 would appear to be the production of macroporous polymer beads of substantially uniform size, the macroporosity being achieved through extraction of the (initially) soluble polymer from the resultant insoluble expanded beads. It' is well known in the art that addition of steric stabilizers to dispersion polymerizations of polymer seeds can be useful in controlling size of beads; this feature of /WO 92/16581, therefore, appears to represent nothing more than the arbitrary introduction of an obvious and well-known advantageous process feature into the process of the invention. There is a need for improvements to all these processes, in particular improvements which make it easier to produce monodisperse polymer particles with different chemical or physical characteristics. It is important to use a polymeric steric stabilizer in the aqueous phase in order to avoid agglomeration of desired-sized particles and formation of undersized particles in the polymerization stage. Surprisingly it has been found that where the swelling generates particles below 25um in size undersized particle formation is essentially avoided by the use of polyvinylpyrrolidone (PVP) as a steric stabilizer whereas where the swelling generates particles above 5^m in size cellulose ethers function effectively as steric stabilizers. While PVP can be used to stabilize particles above 16fm it is especially preferred for use with particles up to 16jan. Thus viewed from one aspect the invention provides a process for the preparation of monodisperse polymer particles which process comprises: 1) either (a) forming an aqueous dispersion comprising (i) monodisperse swellable seed polymer (or oligoraer) particles, (ii) droplets comprising an organic compound (e.g. a polymerization initiator) with a molecular weight below 5000 Dalton and a water solubility at 25 °C of less than 10"2g/L, (iii) an anionic surfactant, and, optionally, (iv) an organic solvent in which said organic compound is soluble, and (b) allowing said organic compound to diffuse into said seed particles C£ (a) forming an aqueous dispersion comprising monodisperse swellable seed oligomer particles and preferably an anionic surfactant; 2) contacting the aqueous dispersion of seed particles with a monomer which, where said organic compound is present, is at least ten times more water soluble than said organic compound, and if required a water-soluble steric stabilizer, if required a porogen, and if required a polymerization initiator, and allowing said monomer to diffuse into said seed particles to form an aqueous dispersion of swollen seed particles; and 3} initiating polymerization of said monomer in an aqueous dispersion of swollen seed particles, characterised in.' that where the mode diameter of said swollen particles is greater than 5jnn then the aqueous phase of said aqueous dispersion of swollen seed particles during polymerization further contains as a steric stabilizer a water soluble cellulose ether or in that where said mode diameter of said swollen particles is in the range 1 to 25um the aqueous phase of said aqueous dispersion of swollen seed particles during polymerization further contains as a steric stabilizer polyvinylpyrrolidone. Alternatively, the process feature 2) above may instead involve contacting the aqueous dispersion of seed particles with a monomer which, where said organic compound is present, is at least ten times more water soluble than said organic compound, and allowing said monomer to diffuse into said seed particles to form an aqueous dispersion of swollen seed particles, and if required adding a water-soluble steric stabilizer, if required adding a porogen, and if required adding a polymerization initiator. In the above process, the mode diameter of said swollen particles is preferably more than 15um where the aqueous phase of said aqueous dispersion of swollen seed particles during polymerization further contains as a steric stabilizer a water soluble cellulose ether. Where water soluble cellulose ethers are used when forming the swollen particles, the mode diameter of the swollen particles will preferably be less than 200 /im. The PVP preferably has a weight average molecular weight of 10 to 2000 kD, more preferably 25 to 1500 kD, especially 30 to 1000 kD. Where the swollen particles have sizes at the lower end of the 1 to 25/zm range it is preferred to use lower molecular weight PVP and where the swollen particles have sizes at the upper end of that range it;' is preferred to use higher molecular weight PVP. Thus for example 20 to 80 kD, e.g. 30 kD PVP is particularly suitable for swollen particle sizes of up to 8/zm while 900 to 1500 kD PVP is particularly suitable for swollen particle sizes above 8/im. Examples of suitable such PVP include PVP K30 and PVP K90 (available for example from International Speciality Products and from Fluka). Examples of suitable cellulose ethers include alkyl celluloses, preferably Cj.4-alkyl celluloses; and (hydroxyalkyl)alkyl celluloses, preferably (hydroxy-Ci_4 - alkyl )C!_4- alkyl celluloses, more preferably (hydroxy-Cj.4-alkyl) methyl celluloses. Typically, these cellulose ethers have weight average molecular weights in the range 10 to 100 kD, especially 15 to 80 kD. Such materials are available commercially in a range of different degrees of substitution and molecular weight, e.g. as Benecel MP 333C, Benecel MP 651C, Culmihal MHPC 1500, Culminal MHPC 400, Walocel MK 400 PFV and Methocel K100. Cellulose ethers which generate a viscosity when in 2% aqueous solution at 21°C of 50 to 150 mPa.s are especially preferred. In the present invention, the size increase by volume (i.e. the ratio of the volume of the swollen particles to the volume of the seed particles) is between 30 and 1000 times. ' It is a preferred embodiment that the corresponding ratio with regard to the increase in diameter is not less than 3.5. It should be noted that the process steps recited above may represent the final swelling and polymerization stage or an intermediate swelling and polymerizatiofi stage in an Ugelstad polymerization process for preparing monodisperse polymer particles. The mixture which comprises the monomer (or mixture of monomers) is preferably in the form of an aqueous dispersion when it is contacted with the polymer particles. Where a polymerization initiator is contacted with the aqueous dispersion of polymer particles this.too is preferably in the form of an aqueous emulsion, preferably also containing a polymerizable or non-polymerizable organic solvent, e.g. alcohols (particularly Cj_ Figure 1 shows the degree of swelling (by volume) of dispersed particles produced in Examples 15-17, from water to THF and from water to butyl acetate. In the Ugelstad polymerization process the initial substantially monodisperse seed polymer particles may conveniently be produced by emulsion polymerization. We have found that particularly suitable initial seed particles may be produced by effecting that, emulsion polymerization under substantially oxygen-free conditions. Thus viewed from a further aspect the invention provides a process for the preparation of monodisperse polymer particles which comprises: 1) preparing monodisperse swellable seed particles by emulsion polymerization under substantially oxygen-free conditions; 2) where said seed particles are non-oligomeric (and optionally where they are oligomeric), (a) contacting said seed particles with an aqueous dispersion comprising an organic compound (e.g. a polymerization initiator) with a molecular weight below 5000 Dalton and a water solubility at 25°C of less than lOg/L, an anionic surfactant and, optionally an organic solvent in which said organic compound is soluble, and (b) allowing said organic compound to diffuse into said seed particles; 3) contacting the aqueous dispersion of seed particles with a monomer which, where said organic compound is used, is at least ten times more water soluble than said organic compound and allowing said monomer to diffuse into said seed particles to form an aqueous dispersion of swollen seed particles, and if required adding a water-soluble steric stabilizer, if required adding a porogen, and if required adding a polymerization initiator; and 4) initiating polymerization of said monomer in an aqueous dispersion containing a steric stabilizer in the continuous phase. If desired the resulting particles may be further swollen and polymerized to obtain larger monodisperse polymer or oligomer particles. Where any of these stages produces swollen particles having sizes from 1 to 25^m polyvinyIpyrrolidone is preferably used as the steric stabilizer and if it produces swollen particles having sizes above 15/zm a cellulose ether is preferably used as the steric stabilizer. A cellulose ether may also be used as steric stabilizer where the mode diameter of said swollen particles is from 5 to 15 //m. Where the swollen particles have particle sizes below 5^m, and especially below 2/im, and especially where the organic compound used is a polymerization initiator, it is convenient to use as the surfactant a C^.,% alkyl sulphate or sulphonate, especially a dodecyl sulphate, e.g. sodium dodecyl sulphate, as this serves as both stabilizer and.initiator uptake promoter. Where the seed particles have mode particle diameters below 1/zm, the surfactant is especially preferably sodium dodecyl sulphate. Where the monomer is an amino-functionalized monomer (or where two or more monomers are used and one comonomer is an amino functionalized monomer), it is preferred to add the initiator after the seed particles have been swollen and thus to use as the organic compound (ie. substance I of EP-B-3905) a non-initiator, e.g. a material such as dioctyladipate. For such amino monomers, the initiator is preferably an azo compound, e.g. 2,2'-azobis-(2-methylbutyronitrile) or azo-bis-dimethylvaleronitrile. For other monomers, especially vinyl monomers (e.g. styrene) and acrylic monomers, it is preferred to use a peroxide initiator (e.g. dibenzoyl peroxide, lauroyl peroxide, t-butyl-peroxybenzoate, t-butyl-peroxypivalate and, especially, dioctanoyl peroxide) and to use the initiator as the organic compound which promotes swelling of the seed particles. Generally, it is preferred to use polymerization initiators that are activated by heat. In this way the initiator and monomer may be brought together within the swollen seed particles at a temperature below that of which polymerization occurs and the aqueous dispersion may then be heated to the temperature at which polymerization is to take place, e.g. 50 to 90°C, more generally 60 to 85°C. During the polymerization, the aqueous dispersion goes through a sticky state and the dispersion should be stirred as gently as possible while still sufficient to maintain a homogeneous dispersion. In the final swelling and polymerization stage, it is preferred to raise the temperature, e.g. to 70 to 95°C, at the end of the polymerization stage so as to reduce the quantity of residual monomer. Following preparation of the monodisperse polymer particles of the desired size (which may require two or more swelling and polymerization cycles, e.g. up to 10 such cycles), the polymer particles' surfaces may be derivatised as desired, e.g. by reaction with bifunctional reagents (e.g. diamines) which react with functional groups present in monomers used in the final polymerization stage and serve to introduce the desired functional groups, e.g. amine, carboxyl, epoxy, hydroxyl, etc. Such functional groups may likewise be introduced by the use of a functionalised monomer or comonomer, e.g. glycidyl methacrylate, HEMA, MMA or aminostyrene. Such groups are advantageous as the resultant particles are particularly suitable for end uses in applications such as combinatorial chemistry, peptide synthesis, supported catalysts and chromatographic separation. Depending on their desired end use, the monodisperse polymer particles may be coated (e.g. with metallic coatings); they may have materials, e.g. magnetic crystals, specific binding partners (e.g. antibodies, avidin or streptavidin, etc.), or catalysts bound to their surface or deposited in pores or on the surface; or they may be expanded (e.g. using blowing agents). The swelling and polymerization stages are performed in aqueous dispersion in the presence of materials, e.g. surfactants, stabilizers, organic solvents, etc., which it is desirable to remove from the particles. Likewise, where the polymerization produces a cross-linked polymer it may be desirable to remove linear polymers or oligomers which formed the seed particles, for example to avoid leakage during use in chromatography. Generally a water-miscible organic solvent in which the cross-linked polymer is insoluble, or an aqueous solution of such a solvent, may be used for this. However it is particularly suitable to use butyl acetate in this regard in view of its surprising effectiveness in removing undesired residues from the Ugelstad polymerization process. This use forms a further aspect of the present invention. Viewed from this aspect the invention provides a method of cleaning monodisperse polymer particles, in particular particles produced by swelling a seed polymer or oligomer particle in aqueous dispersion and polymerizing a monomer within the swollen seed particles, which method comprises contacting said monodisperse polymer particles with butyl acetate, e.g. by washing or rinsing with butyl acetate or a solution thereof. The initial polymer seed (i.e. the particles not produced by the Ugelstad swelling and polymerization technique) is preferably prepared by dispersion or emulsion polymerization, in the latter case especially preferably under substantially oxygen-free conditions (e.g. under an inert gas atmosphere, for example a noble gas such as argon, helium, etc.), and with an oxygen content in the aqueous phase of between 0 and 5 ppm, more especially between 0 and 3 ppm, preferably between 0 and 2 ppm, particularly between 0.01 and 2 ppm. This can be achieved by boiling the water before use or, more preferably by purging liquid reagents with nitrogen. When purging liquid reagents with nitrogen, the length of time required depends upon the volume to be purged. For example, when purging a 2 litre vessel, a purging time of between 1 to 50 minutes is preferred, especially preferably purging for at least 10 minutes. The aqueous phase in the emulsion polymerization contains an anionic surfactant stabilizer, e.g. an CH.,6 alkyl sulphate such as a decylsulphate, e.g. sodium decylsulphate. This is preferably present at a concentration below its critical micelle concentration. The unswollen initial seed preferably has a mode particle diameter in the range 0.2 to 1/im, especially 0.3 to 0.7/im, more especially 0.4 to 0.6pim. This can be achieved by mixing monomer, water and surfactant, heating (e.g. to 80°C) and charging with initiator under / vigorous stirring. The initial seeds produced by emulsion polymerization are preferably styrene polymers. Subsequent seeds may conveniently be polymeric or oligomeric. In the process steps recited above for the processes of the invention, where the polymerization initiator is used as the organic compound (i.e. as substance I of the process of EP-B-3905) it is preferably an organic peroxide, e.g. tert-butyl peroxyneodecanoate or more especially dioctanoyl peroxide (OOP) and it is preferably formed into a fine emulsion using water, the anionic surfactant (preferably sodium dodecyl sulphate or a sulfonate) and an organic solvent, e.g. acetone. The monomer may be but preferably is not used as a solvent for the peroxide initiator; if it is used as a solvent it is preferred that only a relatively small amount of the monomer be used. In general, emulsification is preferably effected using a high pressure mixer (e.g. a pressure homogenizer) , or a rotor stator mixer, to give a mode droplet diameter in the range 0.05 to 5/zm, more preferably 0.05 to 0.5/zm, especially 0.05 to 0.3jan. During emulsifications, the surfactant is preferably present above its critical micelle concentration, e.g. at a concentration of 3 to 10 g/L, more preferably 4 to 6 g/L (the critical micelle concentration for sodium dodecyl sulphate is about 2.5 g/L). However during polymerization stages, the surfactant is preferably present below its critical micelle concentration, e.g. at less than 1.5 g/L, conveniently 0.1 to 1.0 g/L. This can be achieved either by dilution, for example, with water after emulsion foi-mation but before polymerization initiation. Alternatively, the desired concentration may be achieved by dilution, for example with water or a solution of a steric stabilizer after emulsion formation but before polymerization initiation. As a further / alternative, the desired concentration may be realised by adding an appropriately diluted solution of steric stabilizer prior to emulsion formation. During the uptake of the organic compound by the polymer seed particles, the temperature of the dispersion is preferably maintained between 20 and 50°C as precipitation may occur at lower temperatures and new particles may form at higher temperatures. Generally temperatures of 25 °C ± 2°C are preferred. During this uptake phase the dispersion is preferably stirred. The time required for uptake is dependant on the seed diameter, the quantity and nature of the organic compound, the emulsion droplet size and the quantity and nature of surfactant and organic solvent. Generally a period of 1 to 5 days, more particularly 2 to 3 days, will be sufficient. Where the organic compound is an initiator it is important that uptake be at least substantially complete so as to avoid out-of-size particles. The organic solvent concentration in the dispersion during organic compound uptake is conveniently 5 to 15% w/w. The monomers and comonomers used in the process of the invention are preferably vinyl monomers (e.g. styrene), acrylic monomers and methacrylate monomers and monomers copolymerizable therewith, e.g. styrene, divinylbenzene (DVB), ethyl vinyl benzene, vinyl pyridine, amino-styrene, methyl-styrene, ethylene dimethacrylate, (EDMA), hydroxyethylmethacrylate (HEMA), methyl methacrylate (MMA), glycidyl methacrylate (GMA), vinyl benzyl chloride (VBC), vinylchloride (VC) , dimethyl styrene, ethyl styrene, ethyl-methyl-styrene, p-chlorostyrene, 2,4-dichlorostyrene, acrylic acid, methyl acrylate, ethyl acrylate, butylacrylate, methacrylic acid, ethyl methylmethacrylate, maleic acid, maleic anhydride, dimethyl maleate, diethyl maleate, dibutyl maleate, fumaric acid, dimethyl fumarate, diethyl fumarate -.'and acrylonitrile . In the process of the invention the initial polymer seed, e.g. made by emulsion polymerization, is a polymer. Especially preferably, the initial polymer seed is a styrene homo or copolymer, e.g. a styrene homopolymer or a styrene-divinyl benzene copolymer. Most preferably, initial seeds prepared by emulsion polymerization will be homopolymers, especially polystyrene. Initial seeds prepared by other techniques, e.g. dispersion polymerization may be hbmopolymers or copolymers, and may be oligomeric or polymeric. Such seeds typically may be 1 to 10 /zm in mode diameter and optionally may contain some cross-linker. Initial seeds used in this invention which are produced by emulsion polymerization, on the other hand, are typically of less than or equal to about l ^im in diameter. Intermediate seeds may be either polymer or oligomer seeds. Throughout this application, oligomer is intended to refer to polymers having low weight average molecular weight (for example up to 5000 Daltons, e.g. 1000 to 4000 D, especially 1500. to 3000 D), corresponding for example up to 50, more particularly 10 to 25 monomer units. Oligomer seeds have the advantage that their swelling capacity is generally much greater than that of the longer chain polymers. For intermediate or larger sized seeds, e.g. having a mode particle diameter of about l^m or above before swelling, it may be desirable to incorporate a chain transfer agent, e.g. a halogenated alkane as described by Ugelstad in US-A-4186120. This has the advantage of producing a polymer with a bimodal molecular weight distribution in the polymerization stage. The lower molecular weight component results in the particles produced in that polymerization stage having a greater swelling capacity for subsequent swelling and polymerization.stages. As an alternative to the use of a chain transfer agent, a high initiator concentration may be used in oligomer production. In this regard, the techniques of US-A-4530956 (Ugelstad), the disclosure of which is incorporated by reference, may be used. It is also preferred to include a water-soluble polymerization inhibitor (e.g. potassium iodide) in the aqueous phase to prevent nucleation of particles. Where a porous product is desired, then a porogen should be incorporated in the swollen seed particles, preferably in at least the final swelling and polymerization stage. As porogens can be used organic substances which are not polymerized in the polymerization stage and which can be removed from the particles after polymerization thereby producing porous particles. Porogens can also be used as blowing agents - particles impregnated with such materials, on heating may expand as the porogen vaporizes. Examples of suitable porogens include organic acids, alcohols, esters, aromatic solvents, optionally substituted aliphatic hydrocarbons having up to 12 carbons, e.g. toluene, cyclohexanol, butyl acetate, propane, pentane, cyclopentane, cyclobutane, heptane, methyl chloride, ethyl chloride, dichlorodifluoromethane, etc. Toluene and n-heptane are preferred, especially in a volume ratio of 1:10 to 10:1, more particularly 1:4 to 4:1. Th e porogen is conveniently introduced in admixture with the monomer. By the use of a combination of porogens, at least one of which is a solvent for the polymer produced in the polymerization stage and at least one of which is a not a solvent for that polymer, it is possible to achieve a desired pore size distribution in the resulting porous particles. Thus for example for vinyl polymers (e.g. styrene) toluene can be used as a solvent porogen and n-heptane as a non-solvent porogen. The use of the term "solvent" in this specific context is not intended to convey that the swollen particles are capable of dissolving fully in this solvent, or that the swollen particles are incapable of dissolving to any extent whatsoever in the non-sol vent porogen. Thus the combination of the two types of porogen enables the desired pore size distribution .in the resulting porous particles to be achieved. This use of a porogen combination forms a further aspect of the invention. Viewed from this aspect the invention provides a process for the preparation of porous monodisperse polymer particles which process comprises: 1) either (a) forming an aqueous dispersion comprising (i) monodisperse swellable seed polymer (or oligomer) particles, (ii) droplets comprising an organic compound (e.g. a polymerization initiator) with a molecular weight below 5000 Dal ton and a water solubility at 25 °C of less than 10~2g/L, (iii) an anionic surfactant, and, optionally, (iv) an organic solvent in which said organic compound is soluble; and (b) allowing said organic compound to diffuse into said seed particles, (a) forming an aqueous dispersion comprising monodisperse swellable seed oligomer particles and preferably an anionic surfactant; 2) contacting the aqueous dispersion of seed particles with a monomer which, where said organic compound is present, is at least ten times more water soluble than said organic compound, and allowing said monomer to diffuse into said seed particles to form an aqueous dispersion of swollen seed particles and if required adding a water-soluble steric stabilizer, if required adding ,'a porogen, and if required adding a polymerization initiator; and 3) initiating polymerization of said monomer in an aqueous dispersion of swollen seed particles, characterised in that said swollen seed particles contain at least two porogens, at least one of which is a solvent for the polymer produced in step (3) and at least one of which is not a solvent for the polymer produced in step (3). In this aspect, the ratio with regard to increase in diameter is preferably greater than or equal to 4.5. In general, a cross-linking monomer (such as divinylbenzene) can be used as 0 to 100% w/w of the monomer diffused into the seeds, for example as at least 30% for the production of porous particles and up to 0.5% for the production of very highly swellable particles. In the preparation of porous particles and many other particles, it is necessary to include a crosslinking agent or alternatively to use as a monomer or comonomer a compound with more than one polymerization site, e.g. a compound with more than one polymerizable carbon-carbon double bond, for example a diene such as divinyl benzene, or compounds such as hexanediol dimethacrylate, trimethylol propane trimethacrylate and divinyl benzyl ether. Particularly desirably the monodisperse polymer particles produced according to the invention are 30 to 100% divinyl benzene, more especially 60 to 95%, particularly 70 to 90%, more particularly 75 to 82% (where the percentages are by weight of divinylbenzene monomer residue relative to the total monomer residue). It has been found that the Ugelstad processes can be used particularly effectively to produce functionalized or functionalizable monodisperse particles where the monomer dispersed into the seeds in at least one swelling stage, preferably the final stage, comprises at least two acrylic or methacrylic acid or ester monomers, more preferably at least one being glycidyl methacrylate. Viewed from a further aspect therefore the invention provides a process for the preparation of monodisperse polymer particles which process comprises: 1) either (a) forming an aqueous dispersion comprising (i) monodisperse swellable seed polymer (or oligomer) particles, (ii) droplets comprising an organic compound (e.g. a polymerization initiator) with a molecular weight below 5000 Dalton and a water solubility at 25°C of less than 10"2g/L, (iii) an anionic surfactant, and, optionally, (iv) an organic solvent in which said organic compound is soluble; and (b) allowing said organic compound to diffuse into said seed particles; (a) forming an aqueous dispersion comprising monodisperse swellable seed oligomer particles and preferably an anionic surfactant; 2) contacting the aqueous dispersion of seed particles with a monomer which, where said organic compound is present, is at least ten times more water soluble than said organic compound, and allowing said monomer to diffuse into said seed particles to form an aqueous dispersion of swollen seed particles and if required adding a water-soluble steric stabilizer, if required adding a porogen, and if required adding a polymerization initiator; and 3} initiating polymerization of said monomer in an aqueous dispersion of swollen seed particles, characterised in that said monomer comprises at least two acrylic or methacrylic acid or ester monomers, more preferably at least one being glycidyl methacrylate. In this aspect, the ratio with regard to increase in diameter is preferably greater than or equal to 4.5. Coefficient,'of variation (CV) is determined in percentage as CV = 100 x standard deviation mean where mean is the mean particle diameter and standard deviation is the standard deviation in particle size. CV is preferably calculated on the main mode, ie. by fitting a monomodal distribution curve to the detected particle size distribution. Thus some particles below or above mode size may be discounted in the calculation which may for example be based on about 90%, more usually about 99V of total particle number (of detectable particles that is). Such a determination of CV is performable on a Coulter Counter Channelizer 256 particle size analyser. Embodiments of the invention are illustrated further by the following non-limiting Examples: EXAMPLE 1 Porous croeslinked polystyrene particles, 30fun 1400g of water, 84g of dioctanoyl peroxide (DOP), 140g of acetone and 7g of sodium dodecyl sulphate (SDS) were homogenized in a two stage Manton Gaulin homogenizer with 3BOkg/cm2 in the first stage and 100kg/cm2 in the second stage for 8-9 min. After homogenization 178.ig of the emulsion were charged with a seed suspension of monodisperse oligomeric styrene particles having a particle diameter of 5pim. There were used 21.9g of seed suspension containing 19.8g of water and 2.Ig of oligomeric particles. After stirring for 3 days at 25°C, 180.8g of the activated seed particles were charged with an emulsion containing l€83g ..'of water, 0. 6g of sodium dodecyl sulfate (SDS), 2.6gof Methocel K100 (HPMCHydroxy Propyl Methyl Cellulose), 117g of 80% divinylbenzene (DVB) [ie. 80% by weight DVB, 20% by weight ethyl vinyl benzene and other byproducts of DVB production] , 223g of porogen {toluene:n-heptane in a 1:2 volume ratio). The emulsion was homogenized at 330kg/cm2 in the first stage and 50kg/cm2 in the second stage for 6-7 min. After swelling for 15 hrs at 25°C, 5.3g of methocel K100 dissolved in 788g of water were charged to the reactor. The dispersion was then polymerized for 10 hrs at 70°C. A monodisperse suspension was formed having a particle diameter of 30/zm. The particles were separated from the liquid phase by flotation and the liquid phase was discharged. The particles were then cleaned with 2 litres of methanol by stirring for 1 hour followed by sedimentation. After sedimentation the liquid phase was discharged, new methanol (2 litres) was charged and the described procedure was repeated 4 times. The particle suspension was then sieved through a 100/xm sieving cloth. Then the particle suspension was diafiltered with 6 litres of butylacetate followed by 6.7 litres of methanol. Finally the particles were cleaned by sedimentation and discharging of the liquid phase, with 2 litres of methanol minimum 3 times. The final product was 30/jro polymer particles in a clear liquid phase without impurities. EXAMPLE 2 Porous acrylic particles, 30/xm 1400g of water, 84g of DOP, 140g of acetone and 7g of SDS were homogenized in a two stage Wanton Gaul in homogenizer witty 380kg/cm2 in the first stage and 100kg/cm2 in the second stage for 8-9 tnin. After homogenization, 88 ..4g of the emulsion were charged with a seed suspension of monodisperse oligomeric styrene particles having a particle diameter of 5/im. There were used 9.6g of seed suspension containing 8.75g of water and 0.85g of oligomeric particles. After stirring for 3 days at 25°C, 89g of the activated seed particles were charged with an emulsion containing 844g of water, l,3g of Methocel K100, 44.9g of ethylene dimethylacrylate (EDMA), 11.4g of hydroxy ethyl methacrylate (HEMA) , 113g of porogen (cyclohexanol: butylacetate in a 1:1 volume ratio) . The mixture was emulsified with a Ultra Turrax at maximum speed for 10 min. After swelling for 2 hrs at 25°C, 0.4g of potassium iodide (KI) dissolved in 395g of water were charged to the reactor and the dispersion was then polymerized for 1 hr at 50°C, 3 hrs at 60°C and 1 hr at 70°C. A monodisperse suspension was formed having a particle diameter of 30/zm. EXAMPLE 3 Solid polystyrene particles, 20/zm 1400g of water, 84g of DOP, 140g of acetone and 7g of SDS were homogenized in a two stage Wanton Gaulin homogenizer with 380kg/cnr in the first stage and lOOkg/cnv in the second stage for 8-9 min. After homogenization 159g of the emulsion were charged with a seed suspension of monodisperse oligomeric styrene particles having a particle diameter of 5/im. There were used 43.9g of seed suspension containing 39.7g of water and 4.2g of oligomeric particles. / After stirring for 2 days at 25°C, 184.4g of the activated seed particles were charged with an emulsion containing 836g of water, l-5g of Methocel K100, 348.8g styrene. The emulsion was homogenized at 400kg/cm2 in the first stage and 100kg/cm2 in the second stage for 4-5 min. After swelling for 2 hrs at 25°C, 3g of Methocel K100 dissolved in 427g of water were charged to the reactor and then the dispersion was polymerized for l hr at 60°C and 9 hrs at 70°C. A monodisperse suspension was formed having a particle diameter of 20jim. EXAMPLE 4 Solid crosslinked polystyrene particles, 54/un 1400g of water, 42g of DOP, 222g of acetone and 7g of SDS were homogenized in a two stage Manton Gaulin homogenizer with 400kg/cm in the first stage and lOOkg/cm2 in the second stage for 8-9 min. After homogenization 159g of the emulsion were charged with a seed suspension of monodisperse oligomeric styrene particles having a particle diameter of 9.5pim. There were used 17.6g of the seed suspension containing 16.6g of water and ig of oligomeric particles. After stirring for 3 days at 25°C, 146.3g of the activated seed particles were charged with an emulsion containing 1198g of water, 2.5g of Methocel K100, 228g styrene, 7.3g 65% DVB. The emulsion was homogenized at 400kg/cnr in the first stage and I00kg/cm' in the second stage for 5-6 min. After swelling for 1 hour at 25°C, 0.5g of Methocel KlOO and 0.5g KI dissolved in 500g of water were charged to the reactor and -then the dispersion was polymerized for 1 hr at 60°C and 9 hrs at 70°C. A monodisperse particle suspension was formed having a particle diameter of 54/xni. EXAMPLE 5 Solid crosslinked polystyrene particles, 15jun 1400g of water, 84g of DOP, 140g of acetone and 7g of SDS were homogenized in a two stage Manton Gaulin homogenizer with 400kg/cm2 in the first stage and lOOkg/cm2 in the second stage for 8-9 min. After homogenization 75,8g of the emulsion were charged with a seed suspension of monodisperse oligomeric styrene particles having a particle diameter of 3.2^m. There were used 22g of the seed suspension containing 20g of water and 2g of oligomeric particles. After stirring for l day at 25°C, 85g of the activated seed particles were charged with an emulsion containing 784g of water, 1.25g of SDS, 204.3g styrene, 0.37g of 80% DVB. The emulsion was homogenized at 400kg/cm2 in the first stage and 100kg/cm2 in the second stage for 4-5 min. After swelling for 5 hrs at 25°C, 15g of PVP K90 (Poly Vinyl Pyrolidone) and 0.4g of potassium iodide dissolved in 702g of water were charged to the reactor and then the dispersion was polymerized for 1 hr at 60°C and 9 hrs at 70°C. A monodisperse suspension was formed having a particle diameter of I5jim. EXAMPLE 6 Porous croEslinked polystyrene particles, 4.5/im 4970g of water, 248.5g of DOP and 24.85g of SDS were homogenized in a two stage Manton Gaulin homogenizer with 400kg/cm' in' the first stage and 100kg/cm2 in the second stage for 25 min. After homogenization 3947.6g of the emulsion were charged with a seed suspension of monodisperse oligomeric styrene particles having a particle diameter of Ijim. There were used 1691.2g of the seed suspension containing 1555.2g of water and 136.Og of oligomeric particles. After stirring for 20 hrs at 25°C, 5126.2g of the activated seed particles were charged with an emulsion containing 42576g of water, 26.47g of SDS, 536.5g of PVP K-30, 2989.7g of 62.5% DVB, 1991.7g of styrene and 4727.Og of porogen (toluene). The emulsion was homogenized at 380kg/cm2 in the first stage and 100kg/cm2 in the second stage for 30 min. After swelling for 20 hrs at 25°C, 42026.4g of water were charged to the reactor and then the dispersion was polymerized for 1 hr at 60°C, 4 hrs at 70°C and 2.5 hrs at 80°C. A monodisperse suspension was formed having a particle diameter of 4.5/im. EXAMPLE 7 Porous croeslixxked polystyrene particles, 2.8/nn ?630g of water, 214.4g of OOP, 291.9g of acetone and 14.73g of SDS were homogenized in a two stage Manton 3aulin homogenizer with 400kg/cnr in the first stage and lOOkg/cnr' in the second stage for 25 min. hfter homogenization 2994.6g of the emulsion were charged with a seed suspension of monodisperse polystyrene particles having a particle diameter of 0.5/im. There were used 341.3g of seed suspension containing 290.4g of water and 50.9g of polymeric particles. . ,' After stirring for 20 hrs at 25°C, 3032.6g of the activated seed particle suspension were charged with an emulsion containing 43375.Ig of water, 31.42g of SDS, 1412.7g of PVP K-30, 2989.6g of 62.9% DVB, 1998.2g of styrene and 4780.7g of porogen (toluene). The emulsion was homogenized at 380kg/cm2 in the first stage and 100kg/cm2 in the second stage for 60 min. After swelling for 20 hrs at 25°C, 42379.7g of water were charged to the reactor and then the dispersion was polymerized for 1 hr at 60°C, 4 hrs at 70°C and 2.5 hrs at 80°C. A monodisperse suspension was formed having a particle diameter of 2.8/zm. EXAMPLE 8 Porous crosslinked polystyrene particles, 2.6pm 1548g of water, 16g of PVP-K30, 2.4g SDS, 176.6g of 63% DVB, 44g of styrene, 204.6g of porogen (toluene) and 5.6g of 2, 2' -azobis (2-methylbutyronitrile) (AMBN) were homogenized in a two stage Manton Gaulin homogenizer with 400kg/cm2 in the first stage and I00kg/cm2 in the second stage for 35 min. After homogenization 1013.4g of the emulsion were charged with a seed suspension of monodisperse oligomeric styrene particles having a particle diameter of 0.65ptm. There were used 40.4g of seed suspension containing 36.8g of water and 3.58g of oligomeric particles. After swelling for 20 hrs at 25°C, 8g PVP K-30, and 0.8g of potassium iodide dissolved in 794g of water were charged to the reactor and then the dispersion was polymerized for 1 hr at 60°C, 4 hrs at 70°C and 2.5 hrs at 80°C. A monodisperse suspension was formed having a particle diameter of 2.6/im. EXAMPLE 9 Preparation of initial seed particles, O.Bjon 280g styrene was extracted with. 500ml 10 wt.% sodium hydroxide and then washed with water to pH7 and then flushed with argon for 10 min. In a 2L rector 1400g of water and 0.53g of borax were heated to 80°C, and lOOg water was evaporated off to remove oxygen. Then 0.56g sodium decyl sulphate in 50ml boiled water was charged and stirred for 10 min, then the washed and substantially oxygen free styrene was charged and stirred for 15 min. Then 0.84g potassium peroxodisulphate was charged in 100ml boiled water. The mixture was kept at 80°C in an argon atmosphere for 13 hours. A monodisperse suspension of polymeric particles was formed having a particle diameter of 0.5/itn. EXAMPLE 10 Solid methacrylic particles with amine groups, 6fun 900g of water, 90g of DOP, 90g of acetone and 5.4g of SDS were homogenized in a two stage Manton Gaulin homogenizer with 380kg/cm2 in the first stage and 100kg/cm2 in the second stage for 6-7 min. After homogenization 77.Og of the emulsion were charged with a seed suspension of monodisperse oligomeric styrene particles having a particle diameter of ijzm. There were used 14.5g of seed suspension containing 13.2g of water and 1.3g of oligomeric particles. After stirring for 1 day at 25°C, 83,3g of the activated seed particles were charged with 864.6g of water, 2.Og of SDS, 158.9g of methyl methacrylate (MMA) , 45.4g glycidyl methacrylate (GMA) and 22.7g ethylene glycol-dimethacrylate . t'EDMA) . After swelling for 15 hrs at 25°C, 788g of water were charged to the reactor and then the dispersion was polymerized for 6 hfs at 70°C. Then 38.4g ethylenediamine were charged to the reactor and then reaction was allowed to proceed for 18 hrs. A monodisperse suspension was formed having a particle diameter of 6/m. EXAMPLE 11 Core and shell particles, 10/xm Step l 1200g of water, 120g of DOP, 24Og of acetone and 7.2g of SDS were homogenized in a two stage Manton Gaulin homogenizer with 400kg/cm2 in the first stage and 100kg/cm2 in the second stage for 7-8 min. After homogenization 83g of the emulsion were charged with a seed suspension of monodisperse polystyrene particles having a particle diameter of 2nm. There were used 7.9g of the seed suspension containing 6.5g of water and 1.4g of polymeric particles. After stirring for 1 day at 25°C, acetone was removed by evaporation under vacuum and 71g of the activated seed particles were charged with 907g of water, 2 . Ig of SDS, 138.4g of methylstyrene, 34,6g of 55% DVB. After swelling for 20 hrs at 25°C, 0.4g of KI dissolved in 647g of water were charged to the reactor and then polymerized for 5 hrs at 70°C (core). Then the batch was cooled down to 25°C. Step_. 2. 550g of the suspension of step 1 was taken and the aqueous was charged with O.lg of Methocel J 75MS (Hydroxy Propyl Methyl Cellulose), O.OSg of KI and O.lg of SDS dissolved in 230g of water. To this batch was added a mixture of 15.6g MMA, 12.5g of GMA and 3. Ig of EDMA. After stirring for 2 hrs at 25°C; the temperature was raised to 65°C for 1 hr and further to 70°C for 5 hrs. The final mixture was monodisperse and contained particles having a diameter of about 10/zm. EXAMPLE 12 Solid polystyrene particles with chlorine groups, 200 jun 1370g of water, 82g of DOP, 205g of acetone and 8.2g of SDS were homogenized in a two stage Manton Gaulin homogenizer with 400kg/cm2 in the first stage and 100kg/cm2 in the second stage for 8-9 min. After homogenization, 166g of the emulsion were charged with a seed suspension of monodisperse oligomeric styrene particles having a particle diameter of 7i/«n. There were used 79g of the seed suspension containing 71.2g of water and 7.8g of oligomeric particles. After stirring for 2 days at 25 °C, 222g of the activated seed particles were charged with an emulsion containing 1583g of water, 8.Sg of Methocel K100, 124.4g styrene, 3g of 62.8% DVB, 58.5g of Vinyl Benzyl Chloride (VBC). The emulsion was homogenized at 400kg/cnr in the first stage and lOOkg/cnv' in the second stage for 5-6 min. After swelling for 1 hr at 25°C, the temperature was raised to 60°C for 1 hr and further to 70°C for 10 hrs. A monodisperse suspension was formed having a particle diameter of 200/xm. EXAMPLE 13 Porous crosslinked polystyrene particles containing amine functionality, 30pm 1500g of water, 119g of bis (2-ethylhexyl) adipate, 152g of acetone and 8g of sodium dodecyl sulphate (SDS) were homogenized in a two stage Manton Gaulin homogenizer at 400kg/cm2 in the first stage and 100kg/cm2 in the second stage for 8-9 min. After homogenizat ion, 499g of the emulsion was charged with a seed suspension of monodisperse oligomeric styrene particles having a particle diameter of Sfim. 93g of a seed suspension containing 8g of oligomeric particles and 85g of water was used. After stirring at 45°C for 1 day, 96.9g of the seed suspension containing activated seed particles were charged to 1097.7g of an emulsion containing 798.3g of water, l.2g of Methocel K-100, 0.3g,of sodium dodecyl sulphate 34.74g of 80% divinylbenzene (DVB) [i.e. 80% by weight DVB, 20% by weight ethyl vinyl benzene and other byproducts in DVB production], 52.8g of styrene, 4.2g of 2, 2 '-azobis{2-methylbutyronitrile) and 205.7g of toluene. The emulsion was homogenized at 400kg/cm/in the first stage and 100kg/cm2 in the second stage for 8-9 min. After swelling at 25°C for 0.5 hours, a mixture of 299. 8g of water, 0 . 5g of Methocel K-100, O.lg of sodium dodecyl sulphate and 5 . Ig of 4 -amino-styrene was charged and the swelling continued for additional 3 hours. 506. 2g of water and 3.37g of Methocel K-100 were then charged to the reactor. The dispersion was then polymerized for 1 hour at 60°C and 17 hours at 70°C, yielding a suspension of particles having a diameter of The particles we're cleaned as described in Example 1. EXAMPLE 14 Porous cr os Blinked polystyrene particles containing amine functionality, 3 850g of water, 110. 50g of bis (2-ethylhexyl) adipate, 141. 95g of acetone and 4.25g of sodium dodecyl sulphate (SDS) were homogenized in a two stage Manton Gaul in homogenizer at 400kg/cm2 in the first stage and 100kg/cm2 in the second stage for 8-9 min. After horoogenization, 102. 68g of the emulsion was charged with a seed suspension of monodisperse oligomeric styrene particles having a particle diameter of 5/m. 27.21g of seed suspension containing l.71g of oligomeric particles and 26. 2g of water was used. After stirring at 45°C for 24 hours, 87.06g of the seed suspension containing activated seed particles were charged to 1436.08g of an emulsion containing 1035.84g of water, l.SBg of Methocel K-100, 0.5g of sodium dodecyl sulphate, 53.41g of 80% divinylbenzene (DVB) [i.e. 80% by weight DVB, 20% by weight ethyl vinyl benzene and other byproducts in DVB production], 56.07g of styrene, 6.7ig of 2 ,2 ' -azobis (2-methylbutyronitrile) , 269. 41g of toluene and 12.56g of 4 -amino-styrene. The etnulsion was homogenized without addition of 4-amino-styrene at 400kg/cnr' in the first stage and lOOkg/cnr in the second stage for 8-9 min before the emulsion was mixed with 4 -amino- styrene . After swelling at 27°C for 1 hour, a mixture of 473. 69g of water and 3.16g of Methocel K-100 was then charged to the reactor. The dispersion was then polymerized for 1 hour at 60°C and 10 hours at 70°C, yielding a suspension of particles having a diameter of 30/im. / The particles were cleaned as described in Example 1. EXAMPLE 15 Crosslinked polystyrene particles containing amine functionality, 32 1380g of water, 179g of bis (2-ethylhexyl)adipate, 230g of acetone and 7g of sodium dodecyl sulphate (SDS) were homogenized in a two stage Manton Gaulin homogenizer at 400 kg/cm3 in the first stage and 100 kg/cnr1 in the second stage for 10-12 minutes. After homogenization 292g of the emulsion was charged with a seed suspension of monodisperse oligomeric styrene particles having a particle diameter of 5 /zm. 79g of seed suspension containing 7g of oligomeric particles and 72g of water was used. After stirring at 45°C for 1 day, 52. 5g of the seed suspension containing activated seed particles were charged to 850. 5g of an emulsion containing 0 . 9g of Methocel K-100, 0.3g of sodium dodecyl sulphate (SDS), 2.lg of divinylbenzene (DVB) [i.e. 80% by weight DVB, 20% by weight ethyl vinyl benzene and other byproducts in DVB production), 174. Ig of styrene, 58. 7g of amino styrene, and 12 . 9g of 2, 2 ' -azobis (2-methylbutyro- nitrile). The mixture was emulsified tor 10 minutes by using an Ultra Turax mixer. After swelling at 27°C for 1 hour, 281.6g of water and 1. 9g of Methocel K-100 were charged to the reactor. The dispersion was then polymerized for 1 hour at 60°C and 10 hours at 70°C, yielding a suspension of particles having diameter of 32 jim. The particles were cleaned as described in Example 1. Diameter was measured on particles dispersed in water, butylacetate and tetrahydrofuran respectively. EXAMPLE 16 Croeslinked polystyrene particles containing amine functionality, 35 /an 1380g of water, 179g of bis (2-ethylhexyl) adipate, 230g of acetone and 7g of sodium dodecyl sulphate (SDS) were homogenized in a two stage Wanton Gaulin homogenizer at 400 kg/cm3 in the first stage and 100 kg/cm3 in the second stage for 10-12 minutes. After homogenization, 292g of the emulsion was charged with a seed suspension of monodisperse oligomeric styrene particles having a particle diameter of 5 fxm. 79g of seed suspension containing 7g of oligomeric particles and 72g of water was used. After stirring at 45°C for 1 day, 52.2g of the seed suspension containing activated seed particles were charged to 850.5g of an emulsion containing 0. 9g of Methocel K-100, 0.3g of sodium dodecyl sulphate (SDS), 5.9g of divinylbenzene (DVB) [i.e. 80% by weight DVB, 20% by weight ethyl vinyl benzene and other byproducts in DVB production], 166.Og of styrene, 63.Og of amino styrene and 12.9g of 2,2'-azobis(2-methylbutyro- nitrile) . The mixture was emulsified for 10 minutes by using an Ultra Turax mixer. After swelling at 27°C for 1 hour, 281. 6g of water and 1 . 9g of Methocel K-100 were charged to the reactor. The dispersion was then polymerized for 1 hour at 60°C and 10 hours at 70°C, yielding a suspension of particles having diameter of 35 /im. The particles were cleaned as described in Example 1. / Diameter was measured on particles dispersed in water, butylacetate and tetrahydrofuran respectively. EXAMPLE 17 Crosslinked polystyrene particles containing amine functionality, 35 1380g of water, 179g of bis (2-ethylhexyl) adipate, 230g of acetone and 7g of sodium dodecyl sulphate (SDS) were homogenized in a two stage Manton Gaulin hotnogenizer at 400 kg/cm3 in the first stage and 100 kg/cm3 in the second stage for 10-12 minutes. After hotnogenization, 292g of the emulsion was charged with a seed suspension of monodisperse oligomeric styrene particles having a particle diameter of 5 /m. 79g of seed suspension containing 7g of oligomeric particles and 72g of water was used. After stirring at 45°C for 1 day, 52. 2g of the seed suspension containing activated seed particles were charged to 850. 5g of an emulsion containing 0 . 9g of Methocel K-100, 0.3g of sodium dodecyl sulphate (SDS), 8 . 8g of divinylbenzene (DVB) [i.e. 80% by weight DVB, 20% by weight ethyl vinyl benzene and other byproducts in DVB production], 167. 3g of styrene, 58. 7g of amino styrene, and 12. 9g of 2, 2 ' -azobis (2-methylbutyro- nitrile) . The mixture was emulsified for 10 minutes by using an Ultra Turax mixer. After swelling at 27°C for 1 hour, 281.6g of water and 1. 9g of Methocel K-100 were charged to the reactor. The dispersion was then polymerized for 1 hour at 60°C and 10 hours at 70°C, yielding a suspension of particles having diameter of 35 /xm. The particles were cleaned as described in Example 1. / Particle diameter was measured on particles dispersed in water, butyl acetate and tetrahydrofuran respectively. Elemental analysis showed a content of 3.0 wt.% nitrogen and 0.38 wt.% oxygen. EXAMPLE 18 Further functionalisation of amine-functionalised particles with carboxyl and amide functionality Sg of the particles produced in Example 17 in methanol were washed with dioxane (3 x 180 ml). 2.07g of succinic anhydride was added to the dioxane suspension (96g) . The mixture was heated and mechanically stirred at 40°C for 3 hours. The particles were washed with dioxane (2 x 200 ml), methanol (100 ml) and dioxane (200 ml). IT spectra showed a broad peak at 1750 to 1650 cm"1 which indicates formation of both amide and carboxylic acid groups. Elemental analysis of dried particles showed a content of 2.5 wt.% nitrogen and 9.3 wt.% oxygen. This indicates an amine conversion near 100%. EXAMPLE 19 Further functionalisation of amine-functionalised particles with amide functionality 5g of the particles produced in Example 17 in methanol were washed with dioxane Ir spectra showed a peak at 1685 cm"! which indicates formation of ami'de groups. Elemental analysis of dried particles showed a content of 13.2 wt% bromine indicating a conversion of 96%. EXAMPLE 20 Porous crosslinked polystyrene particles, 5.0 fan 2020. Og of water, 202. Og of DOP, 202 ..Og of acetone and 10.10g of SDS were homogenized in a two stage Manton Gaulin homogenizer with 400 kg/cm2 in the first stage and 100 kg/cm2 in the second stage for 10 minutes. After homogenization, 1429.3 g of the emulsion were charged with a seed suspension of monodisperse oligomeric styrene particles having particle diameter of 0.9 /im. There were used 372.8g of seed suspension containing 34l.lg of water and 31.7g of oligomeric particles. After stirring for 23 hours at 25°C, 581.3g of the activated seed suspension were charged with an emulsion containing 7053.9g of water, 18.Og of Methocel K-100, 883.Og of 80% divinylbenzene (DVB) [i.e. 80% by weight DVB, 20% by weight ethyl vinyl benzene and other byproducts in DVB production], 168.1 g of toluene and 525.6g of n-heptane. The emulsion was homogenized in a two stage Wanton Gaulin homogenizer with 400 kg/cm" in the first stage and lOOkg/cnr in the second stage for 30 minutes. After swelling for 20 hrs at 25°C, 3234.2g of water and 35.9g of Methocel K-100 were charged to the reactor and then the dispersion was polymerized for 1 hour at 60°C and 10 hours at 70°C. A monodisperse suspension was formed having a particle diameter of 5 /zm. The particles were cleaned as described in Example 1. WE CLAIM (1) A method of cleaning monodisperse polymer particles produced by swelling a seed polymer (or oligomer) particle in aqueous dispersion and polymerizing a monomer within the swollen seed particles, which method comprises: 1) forming an aqueous dispersion comprising monodisperse swellable seed oligomer or polymer particles and an anionic surfactant; 2) contacting the aqueous dispersion of seed particles with a monomer selected from styrene, divinylbenzene (DVB), ethyl vinyl benzene, amino-styrene, methyl-styrene, ethylene dimethacrylate, (EDMA), hydroxyethylmethacrylate (HEMA), methyl methacrylate (MMA), glycidyl methacrylate (GMA), vinyl benzyl chloride (VBC), dimethyl styrene, ethyl styrene, ethyl-methyl-styrene, acrylic acid, butylacrylate, and methacrylic acid and allowing said monomer to diffuse into said seed particles to form an aqueous dispersion of swollen seed particles; 3) initiating polymerization of said monomer in said aqueous dispersion of swollen seed particles; and 4) contacting the swollen seed particles containing the polymerized monomer with butyl acetate to clean said particles thereby removing surfactants, stabilizers and organic solvents employed during polymerisation as well as any linear polymers or oligomers formed. (2) A method as claimed in claim 1 wherein contacting the polymerized monomer with butyl acetate comprise washing or rinsing the polymer particles with said butyl acetate.

Full Text

This invention relates to a method of cleaning monodisperse polymer particles, in particular particles produced by swelling a seed polymer (or oligomer) particle in aqueous dispersion and polymerizing a monomer within the swollen seed particles, which method comprises contacting said monodisperse polymer particles with butyl acetate.
Monodisperse polymer particles (i.e. particles with a coefficient of, variation of less than 10%, preferably less than 5% and' more preferably less than 3%) have been commercially available for several years and find applications in many technical fields, e.g. in pharmaceuticals, in separation processes, as toners, as filters, as spacers, etc.
Polymer beads may be produced by diffusing a monomer and a polymerisation initiator (or catalyst) into polymer seeds in an aqueous dispersion. The seeds swell and following initiation of polymerization, e.g. by heating to activate the initiator, larger polymer particles are produced. The maximum volume increase due to swelling and polymerization is about x5 or less. The late Professor John Ugelstad found that the capacity of the seeds to swell could be increased to a volume increase of xl25 or even more if an organic compound with relatively low molecular weight and low water solubility is diffused into the seeds before the bulk of the monomer is used to swell the seeds. The effect is based on entropy and not particularly in the chemical nature of the organic compound. Conveniently the polymerisation initiator may be used for this purpose. Organic solvents, e.g. acetone or a relatively small portion of the monomer, may be used to enhance diffusion of the organic compound Into the seeds. This "Ugelstad polymerization process", which is described for example in EP-B-3905 {Sinter) and US-A-4530956 (Ugelstad), may be used to produce monodisperse particles, if necessary
carrying out several swelling and polymerization stages to reach the desired particle size.
WO 92/16581 (Cornell Research Foundation) also describes the preparation of monodisperse particles, particularly macroporous polymer beads. The process described uses a three phase emulsion containing soluble polymer particles, a monomer phase, and water. The three phase emulsion also includes an emulsifier and a suspension stabiliser. The polymer particles undergo swelling absorbing the monomer which is then polymerized. In' this process the soluble polymer seed particles act as both shape/size regulators and as a porogen. The initial (i.e. before swelling) particles have a diameter of from about 0.5 to 10 /zm, 2 to 5 jun being most preferred, and are produced by conventional techniques, such as emulsion or dispersion polymerization.
In a simplified version of the Ugelstad process the enhanced capacity for swelling may be achieved simply by the use of oligomeric seed particles, e.g. where the oligomer weight average molecular weight corresponds to up to 50 monomer units or up to 5000 Dalton.
The processes described in EP-B-3905 and US-A-4530956 (the disclosures of which are hereby incorporated by reference) and the simplified Ugelstad process are relatively complex and inefficient. The processes described in WO 92/16581 do not especially improve upon those disclosed in EP-B-3905 and US-A-4530956. The essence of WO 92/15681 would appear to be the production of macroporous polymer beads of substantially uniform size, the macroporosity being achieved through extraction of the (initially) soluble polymer from the resultant insoluble expanded beads. It' is well known in the art that addition of steric stabilizers to dispersion polymerizations of polymer seeds can be useful in controlling size of beads; this feature of /WO 92/16581, therefore, appears to represent

nothing more than the arbitrary introduction of an obvious and well-known advantageous process feature into the process of the invention.
There is a need for improvements to all these processes, in particular improvements which make it easier to produce monodisperse polymer particles with different chemical or physical characteristics.
It is important to use a polymeric steric stabilizer in the aqueous phase in order to avoid agglomeration of desired-sized particles and formation of undersized particles in the polymerization stage. Surprisingly it has been found that where the swelling generates particles below 25um in size undersized particle formation is essentially avoided by the use of polyvinylpyrrolidone (PVP) as a steric stabilizer whereas where the swelling generates particles above 5^m in size cellulose ethers function effectively as steric stabilizers. While PVP can be used to stabilize particles above 16fm it is especially preferred for use with particles up to 16jan.
Thus viewed from one aspect the invention provides a process for the preparation of monodisperse polymer particles which process comprises:
1) either
(a) forming an aqueous dispersion comprising (i) monodisperse swellable seed polymer (or oligoraer) particles, (ii) droplets comprising an organic compound (e.g. a polymerization initiator) with a molecular weight below 5000 Dalton and a water solubility at 25 °C of less than 10"2g/L, (iii) an anionic surfactant, and, optionally, (iv) an organic solvent in which said organic compound is soluble,
and (b) allowing said organic compound to diffuse into said seed particles
C£ (a) forming an aqueous dispersion comprising monodisperse swellable seed oligomer particles and preferably an anionic surfactant;

2) contacting the aqueous dispersion of seed particles with a monomer which, where said organic compound is present, is at least ten times more water soluble than said organic compound, and if required a water-soluble steric stabilizer, if required a porogen, and if required a polymerization initiator, and allowing said monomer to diffuse into said seed particles to form an aqueous dispersion of swollen seed particles; and
3} initiating polymerization of said monomer in an aqueous dispersion of swollen seed particles, characterised in.' that
where the mode diameter of said swollen particles is greater than 5jnn then the aqueous phase of said aqueous dispersion of swollen seed particles during polymerization further contains as a steric stabilizer a water soluble cellulose ether
or in that where said mode diameter of said swollen particles is in the range 1 to 25um the aqueous phase of said aqueous dispersion of swollen seed particles during polymerization further contains as a steric stabilizer polyvinylpyrrolidone.
Alternatively, the process feature 2) above may instead involve contacting the aqueous dispersion of seed particles with a monomer which, where said organic compound is present, is at least ten times more water soluble than said organic compound, and allowing said monomer to diffuse into said seed particles to form an aqueous dispersion of swollen seed particles, and if required adding a water-soluble steric stabilizer, if required adding a porogen, and if required adding a polymerization initiator.
In the above process, the mode diameter of said swollen particles is preferably more than 15um where the aqueous phase of said aqueous dispersion of swollen seed particles during polymerization further contains as a steric stabilizer a water soluble cellulose ether.
Where water soluble cellulose ethers are used when

forming the swollen particles, the mode diameter of the swollen particles will preferably be less than 200 /im.
The PVP preferably has a weight average molecular weight of 10 to 2000 kD, more preferably 25 to 1500 kD, especially 30 to 1000 kD. Where the swollen particles have sizes at the lower end of the 1 to 25/zm range it is preferred to use lower molecular weight PVP and where the swollen particles have sizes at the upper end of that range it;' is preferred to use higher molecular weight PVP. Thus for example 20 to 80 kD, e.g. 30 kD PVP is particularly suitable for swollen particle sizes of up to 8/zm while 900 to 1500 kD PVP is particularly suitable for swollen particle sizes above 8/im. Examples of suitable such PVP include PVP K30 and PVP K90 (available for example from International Speciality Products and from Fluka).
Examples of suitable cellulose ethers include alkyl celluloses, preferably Cj.4-alkyl celluloses; and (hydroxyalkyl)alkyl celluloses, preferably (hydroxy-Ci_4 - alkyl )C!_4- alkyl celluloses, more preferably (hydroxy-Cj.4-alkyl) methyl celluloses. Typically, these cellulose ethers have weight average molecular weights in the range 10 to 100 kD, especially 15 to 80 kD. Such materials are available commercially in a range of different degrees of substitution and molecular weight, e.g. as Benecel MP 333C, Benecel MP 651C, Culmihal MHPC 1500, Culminal MHPC 400, Walocel MK 400 PFV and Methocel K100. Cellulose ethers which generate a viscosity when in 2% aqueous solution at 21°C of 50 to 150 mPa.s are especially preferred.
In the present invention, the size increase by volume (i.e. the ratio of the volume of the swollen particles to the volume of the seed particles) is between 30 and 1000 times. ' It is a preferred embodiment that the corresponding ratio with regard to the increase in diameter is not less than 3.5.

It should be noted that the process steps recited above may represent the final swelling and polymerization stage or an intermediate swelling and polymerizatiofi stage in an Ugelstad polymerization process for preparing monodisperse polymer particles.
The mixture which comprises the monomer (or mixture of monomers) is preferably in the form of an aqueous dispersion when it is contacted with the polymer particles. Where a polymerization initiator is contacted with the aqueous dispersion of polymer particles this.too is preferably in the form of an aqueous emulsion, preferably also containing a polymerizable or non-polymerizable organic solvent, e.g. alcohols (particularly Cj_ Figure 1 shows the degree of swelling (by volume) of dispersed particles produced in Examples 15-17, from water to THF and from water to butyl acetate.
In the Ugelstad polymerization process the initial substantially monodisperse seed polymer particles may conveniently be produced by emulsion polymerization. We

have found that particularly suitable initial seed particles may be produced by effecting that, emulsion polymerization under substantially oxygen-free conditions. Thus viewed from a further aspect the invention provides a process for the preparation of monodisperse polymer particles which comprises:
1) preparing monodisperse swellable seed
particles by emulsion polymerization under substantially
oxygen-free conditions;
2) where said seed particles are non-oligomeric
(and optionally where they are oligomeric), (a)
contacting said seed particles with an aqueous
dispersion comprising an organic compound (e.g. a
polymerization initiator) with a molecular weight below
5000 Dalton and a water solubility at 25°C of less than
lOg/L, an anionic surfactant and, optionally an organic
solvent in which said organic compound is soluble, and
(b) allowing said organic compound to diffuse into said
seed particles;
3) contacting the aqueous dispersion of seed
particles with a monomer which, where said organic
compound is used, is at least ten times more water
soluble than said organic compound and allowing said
monomer to diffuse into said seed particles to form an
aqueous dispersion of swollen seed particles, and if
required adding a water-soluble steric stabilizer, if
required adding a porogen, and if required adding a
polymerization initiator; and
4) initiating polymerization of said monomer in
an aqueous dispersion containing a steric stabilizer in
the continuous phase.
If desired the resulting particles may be further swollen and polymerized to obtain larger monodisperse polymer or oligomer particles. Where any of these stages produces swollen particles having sizes from 1 to 25^m polyvinyIpyrrolidone is preferably used as the steric stabilizer and if it produces swollen particles

having sizes above 15/zm a cellulose ether is preferably used as the steric stabilizer. A cellulose ether may also be used as steric stabilizer where the mode diameter of said swollen particles is from 5 to 15 //m. Where the swollen particles have particle sizes below 5^m, and especially below 2/im, and especially where the organic compound used is a polymerization initiator, it is convenient to use as the surfactant a C^.,% alkyl sulphate or sulphonate, especially a dodecyl sulphate, e.g. sodium dodecyl sulphate, as this serves as both stabilizer and.initiator uptake promoter. Where the seed particles have mode particle diameters below 1/zm, the surfactant is especially preferably sodium dodecyl sulphate.
Where the monomer is an amino-functionalized monomer (or where two or more monomers are used and one comonomer is an amino functionalized monomer), it is preferred to add the initiator after the seed particles have been swollen and thus to use as the organic compound (ie. substance I of EP-B-3905) a non-initiator, e.g. a material such as dioctyladipate. For such amino monomers, the initiator is preferably an azo compound, e.g. 2,2'-azobis-(2-methylbutyronitrile) or azo-bis-dimethylvaleronitrile. For other monomers, especially vinyl monomers (e.g. styrene) and acrylic monomers, it is preferred to use a peroxide initiator (e.g. dibenzoyl peroxide, lauroyl peroxide, t-butyl-peroxybenzoate, t-butyl-peroxypivalate and, especially, dioctanoyl peroxide) and to use the initiator as the organic compound which promotes swelling of the seed particles.
Generally, it is preferred to use polymerization initiators that are activated by heat. In this way the initiator and monomer may be brought together within the swollen seed particles at a temperature below that of which polymerization occurs and the aqueous dispersion may then be heated to the temperature at which polymerization is to take place, e.g. 50 to 90°C, more

generally 60 to 85°C. During the polymerization, the aqueous dispersion goes through a sticky state and the dispersion should be stirred as gently as possible while still sufficient to maintain a homogeneous dispersion.
In the final swelling and polymerization stage, it is preferred to raise the temperature, e.g. to 70 to 95°C, at the end of the polymerization stage so as to reduce the quantity of residual monomer.
Following preparation of the monodisperse polymer particles of the desired size (which may require two or more swelling and polymerization cycles, e.g. up to 10 such cycles), the polymer particles' surfaces may be derivatised as desired, e.g. by reaction with bifunctional reagents (e.g. diamines) which react with functional groups present in monomers used in the final polymerization stage and serve to introduce the desired functional groups, e.g. amine, carboxyl, epoxy, hydroxyl, etc. Such functional groups may likewise be introduced by the use of a functionalised monomer or comonomer, e.g. glycidyl methacrylate, HEMA, MMA or aminostyrene. Such groups are advantageous as the resultant particles are particularly suitable for end uses in applications such as combinatorial chemistry, peptide synthesis, supported catalysts and chromatographic separation.
Depending on their desired end use, the monodisperse polymer particles may be coated (e.g. with metallic coatings); they may have materials, e.g. magnetic crystals, specific binding partners (e.g. antibodies, avidin or streptavidin, etc.), or catalysts bound to their surface or deposited in pores or on the surface; or they may be expanded (e.g. using blowing agents).
The swelling and polymerization stages are performed in aqueous dispersion in the presence of materials, e.g. surfactants, stabilizers, organic solvents, etc., which it is desirable to remove from the

particles. Likewise, where the polymerization produces a cross-linked polymer it may be desirable to remove linear polymers or oligomers which formed the seed particles, for example to avoid leakage during use in chromatography. Generally a water-miscible organic solvent in which the cross-linked polymer is insoluble, or an aqueous solution of such a solvent, may be used for this. However it is particularly suitable to use butyl acetate in this regard in view of its surprising effectiveness in removing undesired residues from the Ugelstad polymerization process. This use forms a further aspect of the present invention. Viewed from this aspect the invention provides a method of cleaning monodisperse polymer particles, in particular particles produced by swelling a seed polymer or oligomer particle in aqueous dispersion and polymerizing a monomer within the swollen seed particles, which method comprises contacting said monodisperse polymer particles with butyl acetate, e.g. by washing or rinsing with butyl acetate or a solution thereof.
The initial polymer seed (i.e. the particles not produced by the Ugelstad swelling and polymerization technique) is preferably prepared by dispersion or emulsion polymerization, in the latter case especially preferably under substantially oxygen-free conditions (e.g. under an inert gas atmosphere, for example a noble gas such as argon, helium, etc.), and with an oxygen content in the aqueous phase of between 0 and 5 ppm, more especially between 0 and 3 ppm, preferably between 0 and 2 ppm, particularly between 0.01 and 2 ppm. This can be achieved by boiling the water before use or, more preferably by purging liquid reagents with nitrogen. When purging liquid reagents with nitrogen, the length of time required depends upon the volume to be purged. For example, when purging a 2 litre vessel, a purging time of between 1 to 50 minutes is preferred, especially preferably purging for at least 10 minutes.

The aqueous phase in the emulsion polymerization contains an anionic surfactant stabilizer, e.g. an CH.,6 alkyl sulphate such as a decylsulphate, e.g. sodium decylsulphate. This is preferably present at a concentration below its critical micelle concentration.
The unswollen initial seed preferably has a mode particle diameter in the range 0.2 to 1/im, especially 0.3 to 0.7/im, more especially 0.4 to 0.6pim. This can be achieved by mixing monomer, water and surfactant, heating (e.g. to 80°C) and charging with initiator under
/
vigorous stirring. The initial seeds produced by emulsion polymerization are preferably styrene polymers. Subsequent seeds may conveniently be polymeric or oligomeric.
In the process steps recited above for the processes of the invention, where the polymerization initiator is used as the organic compound (i.e. as substance I of the process of EP-B-3905) it is preferably an organic peroxide, e.g. tert-butyl peroxyneodecanoate or more especially dioctanoyl peroxide (OOP) and it is preferably formed into a fine emulsion using water, the anionic surfactant (preferably sodium dodecyl sulphate or a sulfonate) and an organic solvent, e.g. acetone. The monomer may be but preferably is not used as a solvent for the peroxide initiator; if it is used as a solvent it is preferred that only a relatively small amount of the monomer be used.
In general, emulsification is preferably effected using a high pressure mixer (e.g. a pressure homogenizer) , or a rotor stator mixer, to give a mode droplet diameter in the range 0.05 to 5/zm, more preferably 0.05 to 0.5/zm, especially 0.05 to 0.3jan. During emulsifications, the surfactant is preferably present above its critical micelle concentration, e.g. at a concentration of 3 to 10 g/L, more preferably 4 to 6 g/L (the critical micelle concentration for sodium

dodecyl sulphate is about 2.5 g/L). However during polymerization stages, the surfactant is preferably present below its critical micelle concentration, e.g. at less than 1.5 g/L, conveniently 0.1 to 1.0 g/L. This can be achieved either by dilution, for example, with water after emulsion foi-mation but before polymerization initiation. Alternatively, the desired concentration may be achieved by dilution, for example with water or a solution of a steric stabilizer after emulsion formation but before polymerization initiation. As a further
/
alternative, the desired concentration may be realised by adding an appropriately diluted solution of steric stabilizer prior to emulsion formation.
During the uptake of the organic compound by the polymer seed particles, the temperature of the dispersion is preferably maintained between 20 and 50°C as precipitation may occur at lower temperatures and new particles may form at higher temperatures. Generally temperatures of 25 °C ± 2°C are preferred.
During this uptake phase the dispersion is preferably stirred. The time required for uptake is dependant on the seed diameter, the quantity and nature of the organic compound, the emulsion droplet size and the quantity and nature of surfactant and organic solvent. Generally a period of 1 to 5 days, more particularly 2 to 3 days, will be sufficient. Where the organic compound is an initiator it is important that uptake be at least substantially complete so as to avoid out-of-size particles.
The organic solvent concentration in the dispersion during organic compound uptake is conveniently 5 to 15% w/w.
The monomers and comonomers used in the process of the invention are preferably vinyl monomers (e.g. styrene), acrylic monomers and methacrylate monomers and monomers copolymerizable therewith, e.g. styrene, divinylbenzene (DVB), ethyl vinyl benzene, vinyl

pyridine, amino-styrene, methyl-styrene, ethylene dimethacrylate, (EDMA), hydroxyethylmethacrylate (HEMA), methyl methacrylate (MMA), glycidyl methacrylate (GMA), vinyl benzyl chloride (VBC), vinylchloride (VC) , dimethyl styrene, ethyl styrene, ethyl-methyl-styrene, p-chlorostyrene, 2,4-dichlorostyrene, acrylic acid, methyl acrylate, ethyl acrylate, butylacrylate, methacrylic acid, ethyl methylmethacrylate, maleic acid, maleic anhydride, dimethyl maleate, diethyl maleate, dibutyl maleate, fumaric acid, dimethyl fumarate, diethyl fumarate -.'and acrylonitrile .
In the process of the invention the initial polymer seed, e.g. made by emulsion polymerization, is a polymer. Especially preferably, the initial polymer seed is a styrene homo or copolymer, e.g. a styrene homopolymer or a styrene-divinyl benzene copolymer. Most preferably, initial seeds prepared by emulsion polymerization will be homopolymers, especially polystyrene. Initial seeds prepared by other techniques, e.g. dispersion polymerization may be hbmopolymers or copolymers, and may be oligomeric or polymeric. Such seeds typically may be 1 to 10 /zm in mode diameter and optionally may contain some cross-linker. Initial seeds used in this invention which are produced by emulsion polymerization, on the other hand, are typically of less than or equal to about l ^im in diameter.
Intermediate seeds may be either polymer or oligomer seeds. Throughout this application, oligomer is intended to refer to polymers having low weight average molecular weight (for example up to 5000 Daltons, e.g. 1000 to 4000 D, especially 1500. to 3000 D), corresponding for example up to 50, more particularly 10 to 25 monomer units. Oligomer seeds have the advantage that their swelling capacity is generally much greater than that of the longer chain polymers.

For intermediate or larger sized seeds, e.g. having a mode particle diameter of about l^m or above before swelling, it may be desirable to incorporate a chain transfer agent, e.g. a halogenated alkane as described by Ugelstad in US-A-4186120. This has the advantage of producing a polymer with a bimodal molecular weight distribution in the polymerization stage. The lower molecular weight component results in the particles produced in that polymerization stage having a greater swelling capacity for subsequent swelling and polymerization.stages.
As an alternative to the use of a chain transfer agent, a high initiator concentration may be used in oligomer production. In this regard, the techniques of US-A-4530956 (Ugelstad), the disclosure of which is incorporated by reference, may be used.
It is also preferred to include a water-soluble polymerization inhibitor (e.g. potassium iodide) in the aqueous phase to prevent nucleation of particles.
Where a porous product is desired, then a porogen should be incorporated in the swollen seed particles, preferably in at least the final swelling and polymerization stage. As porogens can be used organic substances which are not polymerized in the polymerization stage and which can be removed from the particles after polymerization thereby producing porous particles. Porogens can also be used as blowing agents - particles impregnated with such materials, on heating may expand as the porogen vaporizes. Examples of suitable porogens include organic acids, alcohols, esters, aromatic solvents, optionally substituted aliphatic hydrocarbons having up to 12 carbons, e.g. toluene, cyclohexanol, butyl acetate, propane, pentane, cyclopentane, cyclobutane, heptane, methyl chloride, ethyl chloride, dichlorodifluoromethane, etc. Toluene and n-heptane are preferred, especially in a volume ratio of 1:10 to 10:1, more particularly 1:4 to 4:1.

Th e porogen is conveniently introduced in admixture with the monomer.
By the use of a combination of porogens, at least one of which is a solvent for the polymer produced in the polymerization stage and at least one of which is a not a solvent for that polymer, it is possible to achieve a desired pore size distribution in the resulting porous particles. Thus for example for vinyl polymers (e.g. styrene) toluene can be used as a solvent porogen and n-heptane as a non-solvent porogen. The use of the term "solvent" in this specific context is not intended to convey that the swollen particles are capable of dissolving fully in this solvent, or that the swollen particles are incapable of dissolving to any extent whatsoever in the non-sol vent porogen. Thus the combination of the two types of porogen enables the desired pore size distribution .in the resulting porous particles to be achieved. This use of a porogen combination forms a further aspect of the invention. Viewed from this aspect the invention provides a process for the preparation of porous monodisperse polymer particles which process comprises:
1) either
(a) forming an aqueous dispersion comprising (i) monodisperse swellable seed polymer (or oligomer) particles, (ii) droplets comprising an organic compound (e.g. a polymerization initiator) with a molecular weight below 5000 Dal ton and a water solubility at 25 °C of less than 10~2g/L, (iii) an anionic surfactant, and, optionally, (iv) an organic solvent in which said organic compound is soluble;
and (b) allowing said organic compound to diffuse into said seed particles,

(a) forming an aqueous dispersion comprising monodisperse swellable seed oligomer particles and preferably an anionic surfactant;
2) contacting the aqueous dispersion of seed
particles with a monomer which, where said organic
compound is present, is at least ten times more water
soluble than said organic compound, and allowing said
monomer to diffuse into said seed particles to form an
aqueous dispersion of swollen seed particles and if
required adding a water-soluble steric stabilizer, if
required adding ,'a porogen, and if required adding a
polymerization initiator; and
3) initiating polymerization of said monomer in
an aqueous dispersion of swollen seed particles,
characterised in that said swollen seed particles
contain at least two porogens, at least one of which is
a solvent for the polymer produced in step (3) and at
least one of which is not a solvent for the polymer
produced in step (3).
In this aspect, the ratio with regard to increase in diameter is preferably greater than or equal to 4.5.
In general, a cross-linking monomer (such as divinylbenzene) can be used as 0 to 100% w/w of the monomer diffused into the seeds, for example as at least 30% for the production of porous particles and up to 0.5% for the production of very highly swellable particles.
In the preparation of porous particles and many other particles, it is necessary to include a crosslinking agent or alternatively to use as a monomer or comonomer a compound with more than one polymerization site, e.g. a compound with more than one polymerizable carbon-carbon double bond, for example a diene such as divinyl benzene, or compounds such as hexanediol dimethacrylate, trimethylol propane trimethacrylate and divinyl benzyl ether. Particularly desirably the monodisperse polymer particles produced

according to the invention are 30 to 100% divinyl benzene, more especially 60 to 95%, particularly 70 to 90%, more particularly 75 to 82% (where the percentages are by weight of divinylbenzene monomer residue relative to the total monomer residue).
It has been found that the Ugelstad processes can be used particularly effectively to produce functionalized or functionalizable monodisperse particles where the monomer dispersed into the seeds in at least one swelling stage, preferably the final stage, comprises at least two acrylic or methacrylic acid or ester monomers, more preferably at least one being glycidyl methacrylate. Viewed from a further aspect therefore the invention provides a process for the preparation of monodisperse polymer particles which process comprises:
1) either
(a) forming an aqueous dispersion comprising (i) monodisperse swellable seed polymer (or oligomer) particles, (ii) droplets comprising an organic compound (e.g. a polymerization initiator) with a molecular weight below 5000 Dalton and a water solubility at 25°C of less than 10"2g/L, (iii) an anionic surfactant, and, optionally, (iv) an organic solvent in which said organic compound is soluble;
and (b) allowing said organic compound to diffuse into said seed particles;
(a) forming an aqueous dispersion comprising monodisperse swellable seed oligomer particles and preferably an anionic surfactant;
2) contacting the aqueous dispersion of seed particles with a monomer which, where said organic compound is present, is at least ten times more water soluble than said organic compound, and allowing said monomer to diffuse into said seed particles to form an aqueous dispersion of swollen seed particles and if

required adding a water-soluble steric stabilizer, if required adding a porogen, and if required adding a polymerization initiator; and
3} initiating polymerization of said monomer in an aqueous dispersion of swollen seed particles, characterised in that said monomer comprises at least two acrylic or methacrylic acid or ester monomers, more preferably at least one being glycidyl methacrylate.
In this aspect, the ratio with regard to increase in diameter is preferably greater than or equal to 4.5.
Coefficient,'of variation (CV) is determined in percentage as
CV = 100 x standard deviation mean
where mean is the mean particle diameter and standard deviation is the standard deviation in particle size. CV is preferably calculated on the main mode, ie. by fitting a monomodal distribution curve to the detected particle size distribution. Thus some particles below or above mode size may be discounted in the calculation which may for example be based on about 90%, more usually about 99V of total particle number (of detectable particles that is). Such a determination of CV is performable on a Coulter Counter Channelizer 256 particle size analyser.
Embodiments of the invention are illustrated further by the following non-limiting Examples:
EXAMPLE 1
Porous croeslinked polystyrene particles, 30fun
1400g of water, 84g of dioctanoyl peroxide (DOP), 140g of acetone and 7g of sodium dodecyl sulphate (SDS) were homogenized in a two stage Manton Gaulin homogenizer with 3BOkg/cm2 in the first stage and 100kg/cm2 in the

second stage for 8-9 min.
After homogenization 178.ig of the emulsion were charged with a seed suspension of monodisperse oligomeric styrene particles having a particle diameter of 5pim. There were used 21.9g of seed suspension containing 19.8g of water and 2.Ig of oligomeric particles.
After stirring for 3 days at 25°C, 180.8g of the activated seed particles were charged with an emulsion containing l€83g ..'of water, 0. 6g of sodium dodecyl sulfate (SDS), 2.6gof Methocel K100 (HPMC*Hydroxy Propyl Methyl Cellulose), 117g of 80% divinylbenzene (DVB) [ie. 80% by weight DVB, 20% by weight ethyl vinyl benzene and other byproducts of DVB production] , 223g of porogen {toluene:n-heptane in a 1:2 volume ratio). The emulsion was homogenized at 330kg/cm2 in the first stage and 50kg/cm2 in the second stage for 6-7 min.
After swelling for 15 hrs at 25°C, 5.3g of methocel K100 dissolved in 788g of water were charged to the reactor. The dispersion was then polymerized for 10 hrs at 70°C. A monodisperse suspension was formed having a particle diameter of 30/zm.
The particles were separated from the liquid phase by flotation and the liquid phase was discharged. The particles were then cleaned with 2 litres of methanol by stirring for 1 hour followed by sedimentation. After sedimentation the liquid phase was discharged, new methanol (2 litres) was charged and the described procedure was repeated 4 times. The particle suspension was then sieved through a 100/xm sieving cloth. Then the particle suspension was diafiltered with 6 litres of butylacetate followed by 6.7 litres of methanol. Finally the particles were cleaned by sedimentation and discharging of the liquid phase, with 2 litres of

methanol minimum 3 times.
The final product was 30/jro polymer particles in a clear liquid phase without impurities.
EXAMPLE 2
Porous acrylic particles, 30/xm
1400g of water, 84g of DOP, 140g of acetone and 7g of SDS were homogenized in a two stage Wanton Gaul in homogenizer witty 380kg/cm2 in the first stage and 100kg/cm2 in the second stage for 8-9 tnin.
After homogenization, 88 ..4g of the emulsion were charged with a seed suspension of monodisperse oligomeric styrene particles having a particle diameter of 5/im. There were used 9.6g of seed suspension containing 8.75g of water and 0.85g of oligomeric particles.
After stirring for 3 days at 25°C, 89g of the activated seed particles were charged with an emulsion containing 844g of water, l,3g of Methocel K100, 44.9g of ethylene dimethylacrylate (EDMA), 11.4g of hydroxy ethyl methacrylate (HEMA) , 113g of porogen (cyclohexanol: butylacetate in a 1:1 volume ratio) . The mixture was emulsified with a Ultra Turrax at maximum speed for 10 min.
After swelling for 2 hrs at 25°C, 0.4g of potassium iodide (KI) dissolved in 395g of water were charged to the reactor and the dispersion was then polymerized for 1 hr at 50°C, 3 hrs at 60°C and 1 hr at 70°C. A monodisperse suspension was formed having a particle diameter of 30/zm.
EXAMPLE 3
Solid polystyrene particles, 20/zm

1400g of water, 84g of DOP, 140g of acetone and 7g of SDS were homogenized in a two stage Wanton Gaulin homogenizer with 380kg/cnr in the first stage and lOOkg/cnv in the second stage for 8-9 min.
After homogenization 159g of the emulsion were charged with a seed suspension of monodisperse oligomeric styrene particles having a particle diameter of 5/im. There were used 43.9g of seed suspension containing 39.7g of water and 4.2g of oligomeric particles.
/
After stirring for 2 days at 25°C, 184.4g of the activated seed particles were charged with an emulsion containing 836g of water, l-5g of Methocel K100, 348.8g styrene. The emulsion was homogenized at 400kg/cm2 in the first stage and 100kg/cm2 in the second stage for 4-5 min.
After swelling for 2 hrs at 25°C, 3g of Methocel K100 dissolved in 427g of water were charged to the reactor and then the dispersion was polymerized for l hr at 60°C and 9 hrs at 70°C. A monodisperse suspension was formed having a particle diameter of 20jim.
EXAMPLE 4
Solid crosslinked polystyrene particles, 54/un
1400g of water, 42g of DOP, 222g of acetone and 7g of SDS were homogenized in a two stage Manton Gaulin homogenizer with 400kg/cm* in the first stage and lOOkg/cm2 in the second stage for 8-9 min.
After homogenization 159g of the emulsion were charged with a seed suspension of monodisperse oligomeric styrene particles having a particle diameter of 9.5pim. There were used 17.6g of the seed suspension containing 16.6g of water and ig of oligomeric particles.

After stirring for 3 days at 25°C, 146.3g of the activated seed particles were charged with an emulsion containing 1198g of water, 2.5g of Methocel K100, 228g styrene, 7.3g 65% DVB. The emulsion was homogenized at 400kg/cnr in the first stage and I00kg/cm' in the second stage for 5-6 min.
After swelling for 1 hour at 25°C, 0.5g of Methocel KlOO and 0.5g KI dissolved in 500g of water were charged to the reactor and -then the dispersion was polymerized for 1 hr at 60°C and 9 hrs at 70°C. A monodisperse particle suspension was formed having a particle diameter of 54/xni.
EXAMPLE 5
Solid crosslinked polystyrene particles, 15jun
1400g of water, 84g of DOP, 140g of acetone and 7g of SDS were homogenized in a two stage Manton Gaulin homogenizer with 400kg/cm2 in the first stage and lOOkg/cm2 in the second stage for 8-9 min.
After homogenization 75,8g of the emulsion were charged with a seed suspension of monodisperse oligomeric styrene particles having a particle diameter of 3.2^m. There were used 22g of the seed suspension containing 20g of water and 2g of oligomeric particles.
After stirring for l day at 25°C, 85g of the activated seed particles were charged with an emulsion containing 784g of water, 1.25g of SDS, 204.3g styrene, 0.37g of 80% DVB. The emulsion was homogenized at 400kg/cm2 in the first stage and 100kg/cm2 in the second stage for 4-5 min.
After swelling for 5 hrs at 25°C, 15g of PVP K90 (Poly Vinyl Pyrolidone) and 0.4g of potassium iodide dissolved

in 702g of water were charged to the reactor and then the dispersion was polymerized for 1 hr at 60°C and 9 hrs at 70°C. A monodisperse suspension was formed having a particle diameter of I5jim.
EXAMPLE 6
Porous croEslinked polystyrene particles, 4.5/im
4970g of water, 248.5g of DOP and 24.85g of SDS were homogenized in a two stage Manton Gaulin homogenizer with 400kg/cm' in' the first stage and 100kg/cm2 in the second stage for 25 min.
After homogenization 3947.6g of the emulsion were charged with a seed suspension of monodisperse oligomeric styrene particles having a particle diameter of Ijim. There were used 1691.2g of the seed suspension containing 1555.2g of water and 136.Og of oligomeric particles.
After stirring for 20 hrs at 25°C, 5126.2g of the activated seed particles were charged with an emulsion containing 42576g of water, 26.47g of SDS, 536.5g of PVP K-30, 2989.7g of 62.5% DVB, 1991.7g of styrene and 4727.Og of porogen (toluene). The emulsion was homogenized at 380kg/cm2 in the first stage and 100kg/cm2 in the second stage for 30 min.
After swelling for 20 hrs at 25°C, 42026.4g of water were charged to the reactor and then the dispersion was polymerized for 1 hr at 60°C, 4 hrs at 70°C and 2.5 hrs at 80°C. A monodisperse suspension was formed having a particle diameter of 4.5/im.
EXAMPLE 7
Porous croeslixxked polystyrene particles, 2.8/nn

?630g of water, 214.4g of OOP, 291.9g of acetone and 14.73g of SDS were homogenized in a two stage Manton 3aulin homogenizer with 400kg/cnr in the first stage and lOOkg/cnr' in the second stage for 25 min.
hfter homogenization 2994.6g of the emulsion were charged with a seed suspension of monodisperse polystyrene particles having a particle diameter of 0.5/im. There were used 341.3g of seed suspension containing 290.4g of water and 50.9g of polymeric particles. . ,'
After stirring for 20 hrs at 25°C, 3032.6g of the activated seed particle suspension were charged with an emulsion containing 43375.Ig of water, 31.42g of SDS, 1412.7g of PVP K-30, 2989.6g of 62.9% DVB, 1998.2g of styrene and 4780.7g of porogen (toluene). The emulsion was homogenized at 380kg/cm2 in the first stage and 100kg/cm2 in the second stage for 60 min.
After swelling for 20 hrs at 25°C, 42379.7g of water were charged to the reactor and then the dispersion was polymerized for 1 hr at 60°C, 4 hrs at 70°C and 2.5 hrs at 80°C. A monodisperse suspension was formed having a particle diameter of 2.8/zm.
EXAMPLE 8
Porous crosslinked polystyrene particles, 2.6pm
1548g of water, 16g of PVP-K30, 2.4g SDS, 176.6g of 63% DVB, 44g of styrene, 204.6g of porogen (toluene) and 5.6g of 2, 2' -azobis (2-methylbutyronitrile) (AMBN) were homogenized in a two stage Manton Gaulin homogenizer with 400kg/cm2 in the first stage and I00kg/cm2 in the second stage for 35 min.
After homogenization 1013.4g of the emulsion were

charged with a seed suspension of monodisperse oligomeric styrene particles having a particle diameter of 0.65ptm. There were used 40.4g of seed suspension containing 36.8g of water and 3.58g of oligomeric particles.
After swelling for 20 hrs at 25°C, 8g PVP K-30, and 0.8g of potassium iodide dissolved in 794g of water were charged to the reactor and then the dispersion was polymerized for 1 hr at 60°C, 4 hrs at 70°C and 2.5 hrs at 80°C. A monodisperse suspension was formed having a particle diameter of 2.6/im.
EXAMPLE 9
Preparation of initial seed particles, O.Bjon
280g styrene was extracted with. 500ml 10 wt.% sodium hydroxide and then washed with water to pH7 and then flushed with argon for 10 min. In a 2L rector 1400g of water and 0.53g of borax were heated to 80°C, and lOOg water was evaporated off to remove oxygen. Then 0.56g sodium decyl sulphate in 50ml boiled water was charged and stirred for 10 min, then the washed and substantially oxygen free styrene was charged and stirred for 15 min. Then 0.84g potassium peroxodisulphate was charged in 100ml boiled water. The mixture was kept at 80°C in an argon atmosphere for 13 hours. A monodisperse suspension of polymeric particles was formed having a particle diameter of 0.5/itn.
EXAMPLE 10
Solid methacrylic particles with amine groups, 6fun
900g of water, 90g of DOP, 90g of acetone and 5.4g of SDS were homogenized in a two stage Manton Gaulin homogenizer with 380kg/cm2 in the first stage and 100kg/cm2 in the second stage for 6-7 min.

After homogenization 77.Og of the emulsion were charged with a seed suspension of monodisperse oligomeric styrene particles having a particle diameter of ijzm. There were used 14.5g of seed suspension containing 13.2g of water and 1.3g of oligomeric particles.
After stirring for 1 day at 25°C, 83,3g of the activated seed particles were charged with 864.6g of water, 2.Og of SDS, 158.9g of methyl methacrylate (MMA) , 45.4g glycidyl methacrylate (GMA) and 22.7g ethylene glycol-dimethacrylate . t'EDMA) .
After swelling for 15 hrs at 25°C, 788g of water were charged to the reactor and then the dispersion was polymerized for 6 hfs at 70°C. Then 38.4g ethylenediamine were charged to the reactor and then reaction was allowed to proceed for 18 hrs. A monodisperse suspension was formed having a particle diameter of 6/m.
EXAMPLE 11
Core and shell particles, 10/xm
Step l
1200g of water, 120g of DOP, 24Og of acetone and 7.2g of SDS were homogenized in a two stage Manton Gaulin homogenizer with 400kg/cm2 in the first stage and 100kg/cm2 in the second stage for 7-8 min.
After homogenization 83g of the emulsion were charged with a seed suspension of monodisperse polystyrene particles having a particle diameter of 2nm. There were used 7.9g of the seed suspension containing 6.5g of water and 1.4g of polymeric particles.
After stirring for 1 day at 25°C, acetone was removed by evaporation under vacuum and 71g of the activated seed

particles were charged with 907g of water, 2 . Ig of SDS, 138.4g of methylstyrene, 34,6g of 55% DVB.
After swelling for 20 hrs at 25°C, 0.4g of KI dissolved in 647g of water were charged to the reactor and then polymerized for 5 hrs at 70°C (core). Then the batch was cooled down to 25°C.
Step_. 2.
550g of the suspension of step 1 was taken and the
aqueous was charged with O.lg of Methocel J 75MS
(Hydroxy Propyl Methyl Cellulose), O.OSg of KI and O.lg
of SDS dissolved in 230g of water. To this batch was
added a mixture of 15.6g MMA, 12.5g of GMA and 3. Ig of
EDMA.
After stirring for 2 hrs at 25°C; the temperature was raised to 65°C for 1 hr and further to 70°C for 5 hrs. The final mixture was monodisperse and contained particles having a diameter of about 10/zm.
EXAMPLE 12
Solid polystyrene particles with chlorine groups, 200 jun
1370g of water, 82g of DOP, 205g of acetone and 8.2g of SDS were homogenized in a two stage Manton Gaulin homogenizer with 400kg/cm2 in the first stage and 100kg/cm2 in the second stage for 8-9 min.
After homogenization, 166g of the emulsion were charged with a seed suspension of monodisperse oligomeric styrene particles having a particle diameter of 7i/«n. There were used 79g of the seed suspension containing 71.2g of water and 7.8g of oligomeric particles.
After stirring for 2 days at 25 °C, 222g of the activated seed particles were charged with an emulsion containing

1583g of water, 8.Sg of Methocel K100, 124.4g styrene, 3g of 62.8% DVB, 58.5g of Vinyl Benzyl Chloride (VBC). The emulsion was homogenized at 400kg/cnr in the first stage and lOOkg/cnv' in the second stage for 5-6 min.
After swelling for 1 hr at 25°C, the temperature was raised to 60°C for 1 hr and further to 70°C for 10 hrs. A monodisperse suspension was formed having a particle diameter of 200/xm.
EXAMPLE 13
Porous crosslinked polystyrene particles containing
amine functionality, 30pm
1500g of water, 119g of bis (2-ethylhexyl) adipate, 152g of acetone and 8g of sodium dodecyl sulphate (SDS) were homogenized in a two stage Manton Gaulin homogenizer at 400kg/cm2 in the first stage and 100kg/cm2 in the second stage for 8-9 min.
After homogenizat ion, 499g of the emulsion was charged with a seed suspension of monodisperse oligomeric styrene particles having a particle diameter of Sfim. 93g of a seed suspension containing 8g of oligomeric particles and 85g of water was used.
After stirring at 45°C for 1 day, 96.9g of the seed suspension containing activated seed particles were charged to 1097.7g of an emulsion containing 798.3g of water, l.2g of Methocel K-100, 0.3g,of sodium dodecyl sulphate 34.74g of 80% divinylbenzene (DVB) [i.e. 80% by weight DVB, 20% by weight ethyl vinyl benzene and other byproducts in DVB production], 52.8g of styrene, 4.2g of 2, 2 '-azobis{2-methylbutyronitrile) and 205.7g of toluene. The emulsion was homogenized at 400kg/cm/in the first stage and 100kg/cm2 in the second stage for 8-9 min.

After swelling at 25°C for 0.5 hours, a mixture of 299. 8g of water, 0 . 5g of Methocel K-100, O.lg of sodium dodecyl sulphate and 5 . Ig of 4 -amino-styrene was charged and the swelling continued for additional 3 hours. 506. 2g of water and 3.37g of Methocel K-100 were then charged to the reactor. The dispersion was then polymerized for 1 hour at 60°C and 17 hours at 70°C, yielding a suspension of particles having a diameter of
The particles we're cleaned as described in Example 1.
EXAMPLE 14
Porous cr os Blinked polystyrene particles containing
amine functionality, 3
850g of water, 110. 50g of bis (2-ethylhexyl) adipate, 141. 95g of acetone and 4.25g of sodium dodecyl sulphate (SDS) were homogenized in a two stage Manton Gaul in homogenizer at 400kg/cm2 in the first stage and 100kg/cm2 in the second stage for 8-9 min.
After horoogenization, 102. 68g of the emulsion was charged with a seed suspension of monodisperse oligomeric styrene particles having a particle diameter of 5/m. 27.21g of seed suspension containing l.71g of oligomeric particles and 26. 2g of water was used.
After stirring at 45°C for 24 hours, 87.06g of the seed suspension containing activated seed particles were charged to 1436.08g of an emulsion containing 1035.84g of water, l.SBg of Methocel K-100, 0.5g of sodium dodecyl sulphate, 53.41g of 80% divinylbenzene (DVB) [i.e. 80% by weight DVB, 20% by weight ethyl vinyl benzene and other byproducts in DVB production], 56.07g of styrene, 6.7ig of 2 ,2 ' -azobis (2-methylbutyronitrile) , 269. 41g of toluene and 12.56g of 4 -amino-styrene. The

etnulsion was homogenized without addition of 4-amino-styrene at 400kg/cnr' in the first stage and lOOkg/cnr in the second stage for 8-9 min before the emulsion was mixed with 4 -amino- styrene .
After swelling at 27°C for 1 hour, a mixture of 473. 69g of water and 3.16g of Methocel K-100 was then charged to the reactor. The dispersion was then polymerized for 1 hour at 60°C and 10 hours at 70°C, yielding a suspension
of particles having a diameter of 30/im.
/
The particles were cleaned as described in Example 1.
EXAMPLE 15
Crosslinked polystyrene particles containing amine
functionality, 32
1380g of water, 179g of bis (2-ethylhexyl)adipate, 230g of acetone and 7g of sodium dodecyl sulphate (SDS) were homogenized in a two stage Manton Gaulin homogenizer at 400 kg/cm3 in the first stage and 100 kg/cnr1 in the second stage for 10-12 minutes.
After homogenization 292g of the emulsion was charged with a seed suspension of monodisperse oligomeric styrene particles having a particle diameter of 5 /zm. 79g of seed suspension containing 7g of oligomeric particles and 72g of water was used.
After stirring at 45°C for 1 day, 52. 5g of the seed suspension containing activated seed particles were charged to 850. 5g of an emulsion containing 0 . 9g of Methocel K-100, 0.3g of sodium dodecyl sulphate (SDS), 2.lg of divinylbenzene (DVB) [i.e. 80% by weight DVB, 20% by weight ethyl vinyl benzene and other byproducts in DVB production), 174. Ig of styrene, 58. 7g of amino styrene, and 12 . 9g of 2, 2 ' -azobis (2-methylbutyro-

nitrile). The mixture was emulsified tor 10 minutes by using an Ultra Turax mixer.
After swelling at 27°C for 1 hour, 281.6g of water and 1. 9g of Methocel K-100 were charged to the reactor. The dispersion was then polymerized for 1 hour at 60°C and 10 hours at 70°C, yielding a suspension of particles having diameter of 32 jim.
The particles were cleaned as described in Example 1. Diameter was measured on particles dispersed in water, butylacetate and tetrahydrofuran respectively.
EXAMPLE 16
Croeslinked polystyrene particles containing amine
functionality, 35 /an
1380g of water, 179g of bis (2-ethylhexyl) adipate, 230g of acetone and 7g of sodium dodecyl sulphate (SDS) were homogenized in a two stage Wanton Gaulin homogenizer at 400 kg/cm3 in the first stage and 100 kg/cm3 in the second stage for 10-12 minutes.
After homogenization, 292g of the emulsion was charged with a seed suspension of monodisperse oligomeric styrene particles having a particle diameter of 5 fxm. 79g of seed suspension containing 7g of oligomeric particles and 72g of water was used.
After stirring at 45°C for 1 day, 52.2g of the seed suspension containing activated seed particles were charged to 850.5g of an emulsion containing 0. 9g of Methocel K-100, 0.3g of sodium dodecyl sulphate (SDS), 5.9g of divinylbenzene (DVB) [i.e. 80% by weight DVB, 20% by weight ethyl vinyl benzene and other byproducts in DVB production], 166.Og of styrene, 63.Og of amino styrene and 12.9g of 2,2'-azobis(2-methylbutyro-

nitrile) . The mixture was emulsified for 10 minutes by using an Ultra Turax mixer.
After swelling at 27°C for 1 hour, 281. 6g of water and 1 . 9g of Methocel K-100 were charged to the reactor. The dispersion was then polymerized for 1 hour at 60°C and 10 hours at 70°C, yielding a suspension of particles having diameter of 35 /im.
The particles were cleaned as described in Example 1.
/ Diameter was measured on particles dispersed in water,
butylacetate and tetrahydrofuran respectively.
EXAMPLE 17
Crosslinked polystyrene particles containing amine
functionality, 35
1380g of water, 179g of bis (2-ethylhexyl) adipate, 230g of acetone and 7g of sodium dodecyl sulphate (SDS) were homogenized in a two stage Manton Gaulin hotnogenizer at 400 kg/cm3 in the first stage and 100 kg/cm3 in the second stage for 10-12 minutes.
After hotnogenization, 292g of the emulsion was charged with a seed suspension of monodisperse oligomeric styrene particles having a particle diameter of 5 /m. 79g of seed suspension containing 7g of oligomeric particles and 72g of water was used.
After stirring at 45°C for 1 day, 52. 2g of the seed suspension containing activated seed particles were charged to 850. 5g of an emulsion containing 0 . 9g of Methocel K-100, 0.3g of sodium dodecyl sulphate (SDS), 8 . 8g of divinylbenzene (DVB) [i.e. 80% by weight DVB, 20% by weight ethyl vinyl benzene and other byproducts in DVB production], 167. 3g of styrene, 58. 7g of amino styrene, and 12. 9g of 2, 2 ' -azobis (2-methylbutyro-

nitrile) . The mixture was emulsified for 10 minutes by using an Ultra Turax mixer.
After swelling at 27°C for 1 hour, 281.6g of water and 1. 9g of Methocel K-100 were charged to the reactor. The dispersion was then polymerized for 1 hour at 60°C and 10 hours at 70°C, yielding a suspension of particles having diameter of 35 /xm.
The particles were cleaned as described in Example 1.
/ Particle diameter was measured on particles dispersed in
water, butyl acetate and tetrahydrofuran respectively.
Elemental analysis showed a content of 3.0 wt.% nitrogen and 0.38 wt.% oxygen.
EXAMPLE 18
Further functionalisation of amine-functionalised
particles with carboxyl and amide functionality
Sg of the particles produced in Example 17 in methanol were washed with dioxane (3 x 180 ml). 2.07g of succinic anhydride was added to the dioxane suspension
(96g) . The mixture was heated and mechanically stirred at 40°C for 3 hours. The particles were washed with dioxane (2 x 200 ml), methanol (100 ml) and dioxane
(200 ml). IT spectra showed a broad peak at 1750 to 1650 cm"1 which indicates formation of both amide and carboxylic acid groups.
Elemental analysis of dried particles showed a content of 2.5 wt.% nitrogen and 9.3 wt.% oxygen. This indicates an amine conversion near 100%.
EXAMPLE 19
Further functionalisation of amine-functionalised
particles with amide functionality

5g of the particles produced in Example 17 in methanol were washed with dioxane Ir spectra showed a peak at 1685 cm"! which indicates formation of ami'de groups.
Elemental analysis of dried particles showed a content of 13.2 wt% bromine indicating a conversion of 96%.
EXAMPLE 20
Porous crosslinked polystyrene particles, 5.0 fan
2020. Og of water, 202. Og of DOP, 202 ..Og of acetone and 10.10g of SDS were homogenized in a two stage Manton Gaulin homogenizer with 400 kg/cm2 in the first stage and 100 kg/cm2 in the second stage for 10 minutes.
After homogenization, 1429.3 g of the emulsion were charged with a seed suspension of monodisperse oligomeric styrene particles having particle diameter of 0.9 /im. There were used 372.8g of seed suspension containing 34l.lg of water and 31.7g of oligomeric particles.
After stirring for 23 hours at 25°C, 581.3g of the activated seed suspension were charged with an emulsion containing 7053.9g of water, 18.Og of Methocel K-100, 883.Og of 80% divinylbenzene (DVB) [i.e. 80% by weight DVB, 20% by weight ethyl vinyl benzene and other byproducts in DVB production], 168.1 g of toluene and 525.6g of n-heptane. The emulsion was homogenized in a

two stage Wanton Gaulin homogenizer with 400 kg/cm" in the first stage and lOOkg/cnr in the second stage for 30 minutes.
After swelling for 20 hrs at 25°C, 3234.2g of water and 35.9g of Methocel K-100 were charged to the reactor and then the dispersion was polymerized for 1 hour at 60°C and 10 hours at 70°C. A monodisperse suspension was formed having a particle diameter of 5 /zm.
The particles were cleaned as described in Example 1.

WE CLAIM
(1) A method of cleaning monodisperse polymer particles produced by swelling
a seed polymer (or oligomer) particle in aqueous dispersion and polymerizing a
monomer within the swollen seed particles, which method comprises:
1) forming an aqueous dispersion comprising monodisperse swellable
seed oligomer or polymer particles and an anionic surfactant;
2) contacting the aqueous dispersion of seed particles with a monomer
selected from styrene, divinylbenzene (DVB), ethyl vinyl benzene,
amino-styrene, methyl-styrene, ethylene dimethacrylate, (EDMA),
hydroxyethylmethacrylate (HEMA), methyl methacrylate (MMA), glycidyl
methacrylate (GMA), vinyl benzyl chloride (VBC), dimethyl styrene,
ethyl styrene, ethyl-methyl-styrene, acrylic acid, butylacrylate, and
methacrylic acid and allowing said monomer to diffuse into said seed
particles to form an aqueous dispersion of swollen seed particles;
3) initiating polymerization of said monomer in said aqueous dispersion of
swollen seed particles; and
4) contacting the swollen seed particles containing the polymerized
monomer with butyl acetate to clean said particles thereby removing surfactants, stabilizers and organic solvents employed during polymerisation as well as any linear polymers or oligomers formed.
(2) A method as claimed in claim 1 wherein contacting the polymerized
monomer with butyl acetate comprise washing or rinsing the polymer particles
with said butyl acetate.

Documents:

3872-delnp-2005-abstract.pdf

3872-delnp-2005-assignment.pdf

3872-delnp-2005-Claims-(16-03-2010).pdf

3872-delnp-2005-Claims-(22-12-2009).pdf

3872-delnp-2005-Claims-(30-12-2011).pdf

3872-delnp-2005-claims.pdf

3872-DELNP-2005-Correspondence Others-(09-05-2011).pdf

3872-DELNP-2005-Correspondence Others-(29-06-2011).pdf

3872-delnp-2005-Correspondence Others-(30-12-2011).pdf

3872-DELNP-2005-Correspondence-Others (26-10-2009).pdf

3872-delnp-2005-Correspondence-Others-(16-03-2010).pdf

3872-delnp-2005-Correspondence-Others-(22-12-2009).pdf

3872-delnp-2005-correspondence-others.pdf

3872-delnp-2005-Description (Complete)-(22-12-2009).pdf

3872-delnp-2005-description (complete).pdf

3872-delnp-2005-drawings.pdf

3872-DELNP-2005-Form-1 (26-10-2009).pdf

3872-DELNP-2005-Form-1-(29-06-2011).pdf

3872-delnp-2005-form-1.pdf

3872-delnp-2005-form-18.pdf

3872-DELNP-2005-Form-2-(29-06-2011).pdf

3872-delnp-2005-form-2.pdf

3872-delnp-2005-form-3.pdf

3872-delnp-2005-form-5.pdf

3872-DELNP-2005-GPA (26-10-2009).pdf

3872-delnp-2005-gpa.pdf

« Previous Patent

Next Patent »

Patent Number

252503

Indian Patent Application Number

3872/DELNP/2005

PG Journal Number

21/2012

Publication Date

25-May-2012

Grant Date

18-May-2012

Date of Filing

30-Aug-2005

Name of Patentee

INVITROGEN DYNAL AS

Applicant Address

ULLERNCHAUSEEN 52, 0379 OSLO, NORWAY

Inventors:

#	Inventor's Name	Inventor's Address
1	PETTERSEN, HENNING	KIRKEGATE 33, N-2000 LILLESTRØM, NORWAY
2	STAALE, SOLVEIG MARIE	ØSTLIFARET 42, N-1476 RASTA, NORWAY
3	NORDBØ, SILJE STEINBAKK	ULLEVALSVEIEN 56D, N-0454 OSLO, NORWAY

PCT International Classification Number

C08F 257/02

PCT International Application Number

PCT/GB00/01334

PCT International Filing date

2000-04-10

PCT Conventions:

#	PCT Application Number	Date of Convention	Priority Country
1	9908163.0	1999-04-09	U.K.
2	0007008.6	2000-03-22	U.K.