Title of Invention

"PROCESS FOR THE PREPARATION OF AMMONIA AND CATALYST THEREFORE"

Abstract Process for the preparation of ammonia comprising contacting ammonia synthesis gas with one or more catalysts, atleast one catalyst having supported ruthenium as the active catalytic material supported on a nitride on a secondary support.
Full Text

This invention relates to a process for the synthesis of ammonia at high plant pressures and capacities by contacting ammonia synthesis gas with an ammonia catalyst based on ruthenium. The process can be applied in new plants as well as in revamp situations.
BACKGROUND OF THE INVENTION
The first ammonia synthesis loops all used axial flow converters. Due to the axial flow configuration, larger catalyst particles, typically iron based catalysts, were used (typically 6-12°mm) resulting in pressure drops of 15-20 Dar around the synthesis loop and significant rate limitations due to mass transport restrictions.
En the 1950s, steam reforming at pressures of ,0.5 to 15 oars was introduced in USA, thereby significantly reducing the capital cost of the plants. Until around 1950, plant ::apacities were expanded by installation of parallel lines of about 70-12 0 MTPD (Metric Tons Per Day) units. With a Eew exceptions, the synthesis process ran at pressures of about 3 00 to 3 50 bars.
En the period from 1965 to 1985, the concept of integrated plant design was pioneered. This was achieved through construction of large single-train plants with high degrees of energy integration. This resulted in most new plants being Dased on steam reforming at pressures of 15-30 bars and in ammonia synthesis loops containing catalyst beds operating around 140-220 bars with iron based catalysts. Use of inherently more active, smaller catalyst particles (down to 1.5-3 mm) was made possible through the invention of radial

flow and horizontal converters. This decreased the pressure drop in the synthesis loop to around 9-10 bar and at the same time essentially removed the significant mass-transport limitations of the reaction rate.
In the period from 1985 until today, larger plants have been constructed with some improvements, which have led to specific energy consumption down to approximately 2 8 GJ/ton of ammonia product. The first commercial non-iron ammonia synthesis catalyst was introduced in the KAAP process of M. W. Kellogg. The promoted ruthenium catalyst on a special graphitised carbon support was claimed to be significantly more active than the traditional promoted iron catalyst. New significantly improved ruthenium catalysts have been reported. DK patent application No. PA 2000 01052, which is incorporated herein by reference, discloses a barium promoted ruthenium catalyst on magnesium oxide support. Ba-Ru/MgO has been claimed to be more active than the commercial Ru catalyst and it exhibited stable activity for 1000 hours at 750°C at 50 bars. US patent application No. 09/692,037, which is inco3rporated herein by reference, discloses a barium promoted ruthenium catalyst on a boron nitride support, Ba-Ru/BN. This catalyst has unprecedented activity and stability and was developed through insight into both the optimal ruthenium crystal size and the influence of the support on the catalytic activity.
Boron nitride (occasionally known as "white graphite") is a very attractive support material for ruthenium-based ammonia synthesis catalyst. Boron nitride is iso-electronic with carbon, and boron nitride exists just like carbon in several allotropic forms. It has almost the same structure

as graphite, except for a different stacking of the individual layers, but it is completely stable towards hydro-genation under all conditions relevant to industrial ammonia synthesis. At the same time, boron nitride is known for its high temperature resistance.
The Ba-Ru/BN catalyst has proved completely stable in 5000 hours operation at 100 bar and 550°C in an equilibrated 3:1 dihydrogen/dinitrogen mixture. In Fig. 1, the activity and stability of this catalyst is compared to a similar catalyst supported on high surface area graphite. The boron nitride-supported catalyst is stable also at significantly higher pressures and temperatures.
The activities of the Ru/BN and Ru/C catalysts are measured at 400°C. Ru/BN is aged at 550oC and Ru/graphite at 450°C.
Ba-Ru/BN exhibits the same reaction kinetics as barium promoted ruthenium on a carbon support Ba-Ru/C. Compared to promoted iron catalysts this means less inhibition by ammonia, lower dihydrogen reaction order and higher activation energy.
The choice of front-end, ammonia synthesis converter and loop configuration has been changed to allow reduced specific investments and to lower the energy consumption. Furthermore, the plant capacities have increased.
Table 1 shows a comparison between various known ammonia synthesis loop configurations.


Since there is still a demand for increased plant capacities, it is important to be able to build even larger plants. This requires an increased pressure in the synthesis loop, e.g. 2 00 bars simply to reduce the equipment and pipe sizes. Utilising more active catalysts would also as-sist in reducing equipment sizes. The Ru catalyst on the BN support is perfectly suited for these conditions since it is completely stable towards hydrogenation, which could be a severe problem with carbon supported catalysts at the higher dihydrogen pressures.
Since the current world scale grass root plants provide approximately 2,000 MTPD (2,205 STPD (Short Tons Per Day)) of ammonia, it would be desirable if plants producing above 4,500 MTPD (4,961 STPD) could be built. This is due to the

investment per ton of ammonia being approximately 20% lower in such a large plant.
It appears that with the currently available technology, the capacity limitation is around 3,000 MTPD (3,308 STPD) of ammonia.
These problems are, however, solved by the process and
catalyst of the invention herein.
■■ * « •
SUMMARY OF THE INVENTION
The present invention is directed to the synthesis of ammonia from dinitrogen and dihydrogen in a process that is especially suited for plants with large capacities and high pressures.
Another object of the invention is to provide a process for ammonia synthesis, whereby the specific energy consumption has been reduced.
It is a further object of the invention to provide a catalyst for ammonia synthesis.
These objectives are achieved by the process of the invention, which concerns a process for the preparation of ammonia from ammonia synthesis gas by contacting the synthesis gas with one or more catalysts, at least one catalyst having supported ruthenium as the active catalytic material supported on a nitride on a secondary support.

The invention also concerns a catalyst active in the preparation of ammonia from ammonia synthesis gas according to the above process comprising ruthenium as the active catalytic material supported on a nitride on a secondary support.
Traditionally, a two-bed radial flow converter has been installed in many plants. However, in order to boost the capacity of the plant a higher conversion in the ammonia synthesis loop is required. This can be achieved by adding in series a converter downstream of the existing converter.
Using a conventional iron-based ammonia synthesis catalyst will typically require a catalyst volume in the second converter of a similar size as or even larger than that in the existing main converter. Installing such a big converter in an existing plant is most often a problem due to space limitations in the synthesis loop area.
By being able to use the much more active ruthenium catalyst on a nitride on a secondary support, the size of the second converter can be reduced significantly, and then sufficient space is available for introducing the second converter. Furthermore, the equipment cost will decrease significantly.
Promoted ruthenium catalysts supported on boron nitride are completely stable during catalytic ammonia synthesis as they are not susceptible to hydrogenation under industrial conditions.

Boron nitride (BN) can be obtained as a high surface area material with a surface area larger than 25 m^ per gram, and shaped into suitable carriers by methods known in the art.
The ruthenium catalyst supported on BN is therefore suitable for revamping existing ammonia synthesis loops operating at high pressure due to the high stability of the BN carrier. For primarily grass root ammonia plants, the benefit lies in the potential for building large capacity plants and lower equipment costs.
The nitride of silicon, Si3N4, also has properties similar to those mentioned for nitride of boron and this material is therefore also suitable as a support for ruthenium as the active catalytic material in ammonia synthesis.
In accordance with the invention, the nitrides of boron or silicon are placed on a secondary support. This secondary support can for example be alumina, silica or magnesium aluminium spinel. Promoted ruthenium catalysts, supported on nitrides of either boron or silicon and with a secondary support material, are completely stable during catalytic ammonia synthesis.
DETAILED DESCRIPTION OF THE INVENTION
The catalyst of the invention is based on ruthenium as the active component and the ruthenium is supported on a nitride on a secondary support. The nitride can be boron nitride or silicon nitride. Boron nitride is a relatively expensive material since the raw materials for producing bo-

ron nitride are quite costly. In addition the processing steps require high temperatures in corrosive atmospheres. Consequently specialised, expensive equipment is required.
Support materials based on oxides are relatively inexpensive and in the catalyst of the invention, the nitride material has been partially replaced by an oxide support material to produce a much less expensive catalyst. The catalyst of the invention is prepared by covering an inexpensive support such as an oxide support with boron or silicon nitride.
This is done by impregnation of the oxide support with for instance a boron precursor followed by nitridation. It requires that a sufficient amount of boron is introduced by impregnation and that the support material, maintains a high surface area (higher than 25 m^/g) after nitridation, which is typically conducted at high temperatures.
Examples of secondary supports that can be used in the catalyst of the invention are alumina, silica, and magnesium oxide and magnesium aluminium spinel.
The nitride-covered secondary support material is significantly less expensive than for instance pure boron nitride, while exhibiting the same stability and overall activity.
The advantages of producing ammonia under high pressure using a ruthenium catalyst on BN or silicon nitride on a secondary support material are:
• plant capacities can be increased without the use of very large reactors and equipment cost can be decreased.

• existing plant capacities can be increased.
• space (plot area) can be utilised efficiently, e.g. by-replacing large converters with smaller converters containing the ruthenium catalyst on a nitride support.
The following examples illustrate the preparation of the
catalyst of the invention and its application in an ammonia
preparation process as compared to a conventional process
utilising a conventional ammonia catalyst.
• • * •
EXAMPLES
Example 1
Preparation of nitride covered secondary support material.
Extrudates of high surface area magnesium, aluminium spinel with a surface area of 180 m2/g are calcined at 500°C and impregnated with 5 wt% of boron. The extrudates are then dried and nitrided by flowing ammonia at 1 atm over the extrudates at 900°C or at llOO^C. After nitridation, the sample treated at 900°C had a surface area of l00m2/g, while the sample treated at ll00oC had a surface area of 15m2/g.
A study of the samples using high-resolution transmission electron microscopy (TEM) at two different resolutions showed that the spinel crystals nitrided at ll00oC are covered with boron nitride. Fig. 2 shows that the spinel crystals are covered with boron nitride, while a higher resolution, as shown in Fig. 3 shows that the boron nitride almost completely covers every spinel crystal. Approximately 5-6 layers of boron nitride are seen to surround the spinel crystals.

4
Figs. 4 and 5 show TEM images of the spinel sample nitrided at 900°C. It is seen that at this temperature the spinel crystals are covered with boron nitride. Fewer nitride layers are formed and some of the spinel crystals are not completely covered. It is, however, possible to compensate for this by increasing the boron concentration.
Preparation of catalyst.
Several nitride covered spinel samples prepared as described above were impregnated with ruthenium nitroso nitrate. The impregnated samples were dried at 80°C and reduced in a flow of dihydrogen at 450°C. The samples were then promoted with barium by impregnation with aqueous solutions of barium nitrate.
The resulting catalysts had ruthenium concentrations between 4-15 wt%, with barium content of 5-18 wt%. The particle densities were between 0.8 and 1.2 ml/g.
The catalysts had an overall activity similar to that of ruthenium on boron nitride, but were much cheaper to prepare .
Example 2 (Comparison Example)
Ammonia preparation - conventional process.
Fig, 6 depicts a current process for the preparation of ammonia from make-up synthesis gas consisting of hydrogen and nitrogen. The capacity is 2 050 MTPD.
The ammonia synthesis loop depicted in Fig. 6 comprises an ammonia reactor 10, a number of heat exchangers and chillers 1-7, a product ammonia separator 8 and a recirculation

compressor 9. The heat exchangers and chillers 1-7 are used for recovery of the reaction heat and cooling of the reactor effluent to condense the product ammonia.
In the present case the ammonia reactor 10 is a two bed radial flow converter with a catalyst volume of 82 m^.
As the ammonia reaction is an equilibrium reaction only approximately 25% of the hydrogen and nitrogen content of the converter feed gas stream 18 is converted into ammonia during passage through the reactor. Furthermore, as the reaction is exothermic, the temperature increases from 245°C to 460^'C, The operating conditions of the reactor are shown in Table 2.
The effluent from the reactor 10 is cooled in the boiler 1 and the boiler feed water-preheater 2 (BFW-preheater) for recovery of the heat of reaction. Hereafter the effluent is further cooled in the feed/effluent heat exchanger 3 by heat exchange with the converter feed stream 18. The effluent then passes through the water cooler 4 in which a significant part of the product ammonia is condensed. Downstream of the water cooler 4, the reactor effluent is further cooled to about 0®C in a refrigeration arrangement, which consists of two chillers 6 and 7 and a gas/gas heat exchanger 5 for recovery of refrigeration energy. To prevent accumulation of inert gases in the loop, a small purge gas stream is rejected at position 12 downstream of the first chiller 6. After compression in the make-up gas compressor 11, the make-up gas 17 from the gas preparation train is introduced into the loop at position 13 at the entrance to the last chiller 7. By introducing the make-up

gas at this position, its content of moisture and the last traces of CO2 are removed by co-condensation in the chiller 7. The effluent from said chiller flows to the separator 8 for separation of the product ammonia. The gaseous effluent from said separator flows to the gas/gas heat exchanger 5 for recovery of refrigeration energy by heat exchange with the effluent from the water cooler 4. Hereafter the gas is transferred to the recirculation compressor 9 in which the pressure is raised to overcome the pressure drop in the loop. Finally the gas passes the feed/effluent heat exchanger 3 for preheating to the required reactor inlet temperature by heat exchange with the effluent from the BFW-preheater 2, before it is introduced into the reactor 10.

Example 3
Ammonia preparation - process of the invention.
Fig. 7 depicts a process representing an embodiment of the invention. In this process synthesis gas made up of hydro-

gen and nitrogen is converted to ammonia and the 2 050 MTPD ammonia synthesis loop depicted in Fig. 6 has been revamped to a capacity of 2 650 MTPD. Compared to the conventional plant shown in the process flow diagram of Fig. 6, the following new equipment has been added:
• an additional reactor 22 downstream of the original reactor 10, and
• cooling means 21 for the effluent from the reactor 10 before it is introduced into reactor 22.
The ammonia synthesis loop is similar to that depicted in Fig. 6 and the various units are numbered as in Fig. 6. The reactor 22 is loaded with a ruthenium catalyst supported on boron or silicon nitride on a secondary support. The reactor can be either a simple one bed reactor or a reactor with two or more catalyst beds. In the case where two or more beds are present, the inter-bed cooling can be accomplished either in gas/gas heat exchangers or by direct injection of cool quench gas. The flow pattern in the catalyst beds can be either radial or axial.
Application of the catalyst is not limited to the reactor types mentioned, and the catalyst can therefore also be applied in other types of reactors.
The operating conditions of the two converters are shown in Table 3. The operating conditions of reactor 10 alone corresponding to Fig. 6 are as shown in Table 2,
In the case where a single bed reactor is used the required volume of ruthenium catalyst supported on boron or silicon nitride on a secondary support is about 25 m^. In contrast

to this the necessary volume of a similar reactor based on a conventional iron based catalyst is approximately 165 m^. Consequently, the ruthenium catalyst yields both significant savings in the costs of equipment manufacture and handling and appreciable reductions of the space and foundation requirements.






CLAIMS
1. Process for the preparation of ammonia comprising contacting ammonia synthesis gas with one or more catalysts, at least one catalyst having supported ruthenium as the active catalytic material supported on a nitride on a secondary support.
2. Process for the-preparation of ammonia according to claim 1, wherein the secondary support comprises alumina, silica, magnesium oxide or magnesium aluminium spinel.
3- Process for the preparation of ammonia according to claims 1-2, wherein the catalyst having ruthenium as the active catalytic material is supported on boron nitride on a secondary support.
4. Process for the preparation of ammonia according to claims 1-2, wherein the catalyst having ruthenium as the active catalytic material is supported on silicon nitride on a secondary support.
5. Catalyst active in the preparation of ammonia from ammonia synthesis gas according to the process of claim 1 comprising ruthenium as the active catalytic material supported on a nitride on a secondary support.
6. Catalyst according to claim 5, wherein the secondary support comprises alumina, silica, magnesium oxide or magnesium aluminium spinel•

7. Catalyst according to claims 5 and 6, wherein ruthenium as the active catalytic material is supported on boron nitride on a secondary support.
8. Catalyst according to claims 5 and 6, wherein ruthenium as the active catalytic material is supported on sili-con nitride on a secondary support,

9. A process for the preparation of ammonia substantially as herein described with reference to the accompanying drawings.
10. A catalyst substantially as herein described with reference to the accompanying drawings.


Documents:

566-CHE-2003 AMENDED CLAIMS 07-07-2010.pdf

566-CHE-2003 AMENDED PAGES OF SPECIFICATION 07-07-2010.pdf

566-CHE-2003 EXAMINATION REPORT REPLY RECEIVED 07-07-2010.pdf

566-CHE-2003 FORM-3 07-07-2010.pdf

566-CHE-2003 OTHER PATENT DOCUMENT 07-07-2010.pdf

566-CHE-2003 POWER OF ATTORNEY 07-07-2010.pdf

566-CHE-2003 POWER OF ATTRONEY 07-07-2010.pdf

566-che-2003-abstract.pdf

566-che-2003-claims.pdf

566-che-2003-correspondnece-others.pdf

566-che-2003-description(complete).pdf

566-che-2003-drawings.pdf

566-che-2003-form 1.pdf

566-che-2003-form 26.pdf

566-che-2003-form 3.pdf

566-che-2003-form 5.pdf


Patent Number 243022
Indian Patent Application Number 566/CHE/2003
PG Journal Number 40/2010
Publication Date 01-Oct-2010
Grant Date 24-Sep-2010
Date of Filing 09-Jul-2003
Name of Patentee HALDOR TOPSOE A/S
Applicant Address NYMOLLEVEJ 55, DK-2800 DENMARK
Inventors:
# Inventor's Name Inventor's Address
1 SVEND ERIEK NIELSEN BOGELYVEJ 25, DK-3480 FREDENSBORG
2 CLAUS J.H JACOBSEN RUNESTIEN 9, DK-3630 JAEGERSPRIS,
3 HENRIK UDESEN RUDE VANG 16, DK-2840 HOLTE
4 TINE SHIM HESTKOB VAENGE 31, DK-3460 BRIKEROD
5 NIELS KEGEL SORENSEN HYLDEBAKKEN 6, DK-3070 SNEKKERSTEN
PCT International Classification Number B01J23/00
PCT International Application Number N/A
PCT International Filing date
PCT Conventions:
# PCT Application Number Date of Convention Priority Country
1 2002 01088 2002-07-11 Denmark