Title of Invention

METHOD AND APPARATUS FOR PRODUCING POLYCONDENSATION POLYMER AND MOLDED ARICLE THEREOF

Abstract A method for producing a polycondensation polymer, which comprises: introducing a prepolymer of a polycondensation polymer into a polymerization reactor through a feed opening in a molten state; discharging the introduced prepolymer through holes of a perforated plate; and then polycondensing the prepolymer under reduced pressure, while allowing the prepolymer to fall along a support, wherein the perforated plate has two or more areas and polycondensation is performed by introducing a prepolymer and/or a polymer modifier into each of the areas and discharging the introduced prepolymer and/or polymer modifier through holes of each of the areas.
Full Text -1-
Description
METHOD AND APPARATUS FOR PRODUCING POLYCONDENSATION
POLYMER AND MOLDED ARTICLE THEREOF
5 Technical Field
[0001]
The present invention relates a method and an apparatus for producing a
polycondensation polymer and a molded article thereof.
10 Background Art
[0002]
Polycondensation polymers, which typically include polyester resins such as
polyethylene terephthalate (hereinafter abbreviated as "PET"), have excellent heat
resistance and mechanical properties. These polymers have recently been attracting
15 attention as a recyclable and environmentally suitable material, and have been used
in a wide range of applications such as fibers, magnetic tapes, wrapping films, sheets,
injection molded articles for various purposes and preforms for producing beverage
containers.
[0003]
20 Not only having heat resistance and mechanical properties, containers made
of a polycondensation polymer should not affect the taste of the contents. Thus,
polycondensation polymers used for containers need to be of high quality, have a
high polymerization degree, not colored and contain a very small amount of
impurities such as acetaldehyde.
25 [0004]
Further, in recent years, to meet higher demand due to diversification of uses
in addition to demand of high quality, it is attempted to modify properties by


-2-
compensating for defects of a polymer by adding a different polymer,
copolymerizing a different monomer or adding a modifier.
[0005]
For example, in the case of PET containers, a method in which a
5 poly(ethylene terephthalate/ethylene terephthalamide) copolymer is added in order to
increase the crystallization rate to perform high cycle molding or to effectively
crystallize the mouth of a molded bottle (see Patent Document 1), a method of
adding polyolefin (see Patent Document 2), and a method of melt kneading
polyethylene naphthalate to improve the transparency, moldability and heat press
10 resistance of PET (see Patent Document 3) are disclosed.
[0006]
However, when a different polymer and/or various modifiers are melt
kneaded with a polycondensation polymer, thermal decomposition of the polymer
occurs, and quality deterioration such as decrease in molecular weight, coloring and
15 accumulation of decomposition products is unavoidable. To omit the melt kneading
step, a method of polymerization in which a modifier is previously added to the
reaction system for producing a polycondensation polymer is also possible. In most
cases, however, when a modifier is present, thermal degradation of the
polycondensation polymer occurs at the polymerization temperature, and so it
20 becomes difficult to produce a polymer having a polymerization degree as high as
that of a polymer to which no modifier is added. In addition, coloring and
accumulation of decomposition products become noticeable, deteriorating the quality
of the polymer. Likewise, in the method of copolymerizing a different monomer,
since each monomer has a different thermal decomposition temperature, a
25 component having low heat resistance tends to suffer from thermal degradation due
to polymerization conditions, and so it becomes difficult to produce a polymer
having a polymerization degree as high as that of a polymer to which different

-3-
monomer is not copolymerized. This method also has a problem that coloring and
accumulation of decomposition products become noticeable, deteriorating the quality
of the polymer.
[0007]
5 As described above, when it is attempted to improve the properties of a
polymer by adding a different polymer or a modifier, or by copolymerizing a
different monomer, quality of the produced polymer is significantly reduced
compared to that of the initial polymer. Thus, improvement in manufacturing
technique has been desired.
10 [0008]
Further, it is necessary that the method of producing a polymer having
improved properties as described above is applicable to production of a wide variety
of products in small quantities in order to respond flexibly to diversification of uses.
Although batch polymerization is generally used for producing a wide variety of
15 products in small quantities, this method has low productivity and inevitably
increases the production cost. On the other hand, continuous polymerization
basically enables inexpensive production making use of its merit of the scale.
However, when the kind and the amount of modifier or different monomer are
changed, operationability becomes low and great loss is generated, which rather
20 increases the production cost. Thus, continuous polymerization is not suitable for
producing a wide variety of products in small quantities.
As a technique of continuous melt polymerization, methods of polymerization
in which prepolymer is allowed to fall under gravity from the top of a polymerization
reactor have been conventionally proposed. For example, as a method of producing
25 polyester, there is a technique in which a PET oligomer having an average
polymerization degree of 8 to 12 (corresponding to intrinsic viscosity of 0.1 dl/g or
lower) is introduced at 285°C and allowed to fall under gravity along a

-4-
cylindrically-shaped wire gauze vertically disposed in a reactor to perform
polymerization under reduced pressure in the reactor (see Patent Document 4). As
a method of producing polyamide or polyester, there is a technique in which
polymerization is preformed with allowing polymer to fall under gravity along a
5 linear support vertically disposed in a reactor (see Patent Document 5). However,
the studies of the present inventors have revealed that a polymer having a high
polymerization degree cannot be prepared by the above-described method alone.
And what is worse, oligomer discharged through a perforated plate is expanded too
much, polluting the surface of the perforated plate or the wall of the reactor, and
10 these contaminants are modified by decomposition and mixed to the polymer in the
course of long time operation, deteriorating the quality of the product. Moreover,
even if it is attempted to improve the properties of a polymer by simultaneous
polymerization of a different polymer or various modifiers based on the above
polymerization methods, a uniform composition or a uniform copolymer cannot be
15 produced because components are easily separated from each other.
[0009]
[Patent Document 1] JP-A-2003-327812
[Patent Document 2] JP-A-2004-263195
[Patent Document 3] JP-A-2000-17162
20 [Patent Document 4] JP-B-48-8355
[Patent Document 5] JP-A-53-17569
Disclosure of the Invention
Problems to be Solved by the Invention
25 [0010]
An object of the present invention is to produce various high quality
polycondensation polymers having a high polymerization degree, not colored and in

-5-
which the content of impurities generated by thermal decomposition is small, and a
molded article thereof by melt polycondensation at low cost, and to provide a method
of production applicable to producing a polymer whose properties are improved by
copolymerizing a different monomer or adding a different polymer or various
5 modifiers and suitable for producing a wide variety of products in small quantities.
Means for Solving the Problems
[0011]
The present inventors have conducted intensive studies to solve the
10 aforementioned problems and as a result have developed a method of producing a
polycondensation polymer based on a novel principle in which a prepolymer in a
molten state is introduced into a polymerization reactor through a feed opening,
discharged through holes of a perforated plate and allowed to fall along a support to
polymerize under reduced pressure, and have found that melt polymerization at low
15 temperatures which was impossible by conventional known polymerization methods
becomes possible.
[0012]
It has been found that, according to polymerization method in which the
perforated plate is designed to have two or more areas and a prepolymer and/or a
20 polymer modifier are introduced to each area, a polymer whose properties are
improved by copolymerizing a different monomer or adding a different polymer or
various modifiers can be produced, and a high quality polymer having a high
polymerization degree, not colored and in which the content of impurities is small
and a molded article thereof can be produced at low cost.
25 [0013]
It has also been found that all of the above problems can be solved by a
method in which the perforated plate is designed to have two or more areas and a

-6-
polymer polymerized by supplying a prepolymer and/or a polymer modifier to each
area is discharged from one or more outlets of the polymerization reactor. In other
words, it has been found that regarding a polymer whose problems are improved by
copolymerizing a different monomer or adding a different polymer or various
5 modifiers, a high quality polymer having a high polymerization degree, not colored
and in which the content of impurities is small and a molded article thereof can be
produced at low cost. It has also been found that the method has little loss when
product types are changed and is thus suitable for producing a wide variety of
products in small quantities, and the present invention has been completed.
10 [0014]
Accordingly, the present invention is as follows.
(1) A method for producing a polycondensation polymer, which comprises:
introducing a prepolymer of a polycondensation polymer into a polymerization
reactor through a feed opening in a molten state; discharging the introduced
15 prepolymer through holes of a perforated plate; and then polycondensing the
prepolymer under reduced pressure, while allowing the prepolymer to fall along a
support, wherein the perforated plate has two or more areas and polycondensation is
performed by introducing a prepolymer and/or a polymer modifier into each of the
areas and discharging the introduced prepolymer and/or polymer modifier through
20 holes of each of the areas;
(2) The method for producing a polycondensation polymer according (1),
wherein the polymerization reactor has two or more outlets for delivering a produced
polymer;
(3) The method for producing a polycondensation polymer according to (1) or (2),
25 wherein the support has two or more areas corresponding to each area of the
perforated plate of the polymerization reactor, or/and a polymer is delivered through

-7-
an outlet divided into two or more areas corresponding to each area of the perforated
plate or the support;
(4) The method for producing a polycondensation polymer according to any one
of (1) to (3), wherein the prepolymer and/or the polymer modifier are reacted with a
5 molecular weight modifier at a step prior to introducing the prepolymer and/or the
polymer modifier into the polymerization reactor;
(5) The method for producing a polycondensation polymer according to any one
of (1) to (4), wherein the polycondensation polymer is a polyester resin;
(6) A polycondensation polymer produced by the method for producing a
10 polycondensation polymer according to any one of (1) to (5), having a molecular
weight distribution represented by Mw/Mn of 2.0 or higher;
(7) A polycondensation polymer produced by the method for producing a
polycondensation polymer according to any one of (1) to (5), which is a polymer
alloy;
15 (8) A polycondensation polymer produced by the method for producing a
polycondensation polymer according to any one of (1) to (5), which is a polyester
elastomer;
(9) A method for producing a molded article which comprises: transferring a
polymer produced by the method for producing a polycondensation polymer
20 according to any one of (1) to (5) in a molten state to a molding machine and
molding the same;
(10) An apparatus for producing a polycondensation polymer comprising a
polymerization reactor having at least a feed opening, a perforated plate, a support
and an outlet as constituents, wherein the perforated plate has two or more areas, and
25 a prepolymer and/or a polymer modifier is introduced into each of the areas, the
introduced prepolymer and/or polymer modifier is discharged through holes of each

-8-
of the areas, and polycondensation is performed under reduced pressure while
allowing the prepolymer and/or polymer modifier to fall along the support;
(11) The apparatus for producing a polycondensation polymer according to (10),
wherein the polymerization reactor has two or more outlets; and
5 (12) The apparatus for producing a polycondensation polymer according to (10) or
(11), wherein the support of the polymerization reactor has two or more areas
corresponding to each area of the perforated plate, or/and the outlet is divided into
two or more areas corresponding to each area of the perforated plate or the support.
10 Advantages of the Invention
[0015]
When the method of production of the present invention is employed, a high
quality polymer having a high polymerization degree, not colored and in which the
content of impurities generated by thermal decomposition is small and a molded
15 article thereof can be produced by melt polycondensation at low cost. In particular,
when producing a polymer whose properties are improved by copolymerizing a
different monomer or adding a different polymer or various modifiers, a high quality
polymer and a molded article thereof can be produced. In addition, the present
invention is suitable for producing a wide variety of products in small quantities.
20
Best Mode for Carrying Out the Invention
[0016]
The present invention is described in detail below in the order of (A)
principles of polymerization method, (B) description of polycondensation polymer,
25 (C) description of polymer modifier, (D) description of polymerization reactor, (E)
description of polymerization method, (F) description of molding method and (G)
description of produced polymer.

-9-
(A) Principles of polymerization method:
The polymerization method of the present invention comprises introducing a
prepolymer polymerizable by thermal melt polycondensation in a molten state into a
polymerization reactor through a feed opening, discharging the prepolymer through
5 holes of a perforated plate and polymerizing the prepolymer by allowing it to fall
along a support under gravity under reduced pressure.
[0017]
As described later, properties of prepolymer, the construction of the
polymerization reactor and the polymerization method are designed so as to meet
10 appropriate conditions. Such settings produce a great amount of bubbles in the
prepolymer falling along a support, and the polymer rolls down in the form of bubble
balls or agglomerates, rapidly moving to the lower area of the polymerization reactor
in the course of polymerization.
[0018]
15 As a result, the contact area between the polymer and the gas phase is
significantly increased and the action of mixing the polymer is greatly enhanced.
Consequently, by-products of polycondensation (ethylene glycol in the case of PET)
or impurities generated by thermal decomposition in polymerization (acetaldehyde in
the case of PET) can be effectively removed from the prepolymer. Further, in
20 addition to significant increase in the polymerization velocity, a high quality polymer
containing a very small amount of impurities can be produced.
[0019]
In consequence, not only the polymerization velocity is greatly improved
compared to that in the conventional melt polymerization techniques but also a high
25 quality polymer containing a very small amount of remaining impurities can be
produced at low polymerization temperatures, which was impossible by conventional
known polymerization reactors.

-10-
[0020]
The present inventors have conducted further studies and designed a
mechanism of polymerization in which a perforated plate of the polymerization
reactor is separated into two or more areas and a prepolymer and/or a polymer
5 modifier is introduced into each area; or alternatively/further, a prepolymer and/or a
polymer modifier is introduced to each area with changing the supply amount over
time.
[0021]
As a result of their studies, it has been found that when streams of prepolymer
10 introduced through'each area of the perforated plate are combined on the support and
polymerization is performed with allowing the prepolymer to fall, a polymer
homogeneously mixed and uniform in quality can be produced at low temperatures,
which was impossible by conventionally known polymerization reactors or kneaders,
despite the absence of a power driven stirring mechanism such as stirring blade.
15 This has made it possible to produce a high quality polymer at low cost, whose
properties are improved by copolymerizing a different monomer or adding a different
polymer or various modifiers.
[0022]
It is of course possible to introduce the same kind of prepolymer through each
20 area of the perforated plate. Applications are also available such as adjusting the
polymerization velocity or the polymerization degree of the polymer by setting the
supply amount per area as desired, and making molecular weight distribution broader
to produce a polymer having improved melt flowability.
[0023]
25 The present inventors have conducted further studies and designed a
technique in which a perforated plate of the polymerization reactor is separated into
two or more areas, a prepolymer and/or a polymer modifier is introduced into each

-11 -
area, and two or more outlets are formed in the polymerization reactor to discharge
the polymer.
[0024]
As a result of their studies, it has been found that when polymerization is
5 performed with allowing a prepolymer to fall without combining the streams of the
prepolymer introduced through each area of a perforated plate based on the structure
and the position of the support, a plurality of polycondensation polymers can be
simultaneously produced in one polymerization reactor. It has also been found that
when streams of prepolymer introduced through each area of a perforated plate are
10 combined and polymerization is performed with allowing the prepolymer to fall, a
polymer homogeneously mixed and uniform in quality can be obtained.
[0025]
As a result, it has become possible to produce a high quality polymer whose
properties are improved by copolymerizing a different monomer or adding a different
15 polymer or various modifiers at low cost, and to produce a wide variety of polymers
in small quantities with reduced loss by controlling the streams of the prepolymer
falling through the polymerization reactor.
[0026]
It is of curse possible to introduce the same kind of prepolymer through each
20 area of the perforated plate. The production amount in each area can be adjusted by
setting the supply amount per area as desired. A plurality of polymers having a
different polymerization degree can be simultaneously produced. A wide range of
applications such as simultaneous production of a plurality of polymers having a
different polymerization degree by supplying prepolymers which are the same except
25 for the polymerization degree through each area.
[0027]

-12-
(B) Description of polycondensation polymer:
The polycondensation polymer in the present invention means a polymer
having a structure in which at least one kind of monomer containing two or more
functional groups capable of condensing is polymerized by bonding of the functional
5 group. The above monomer may be those in which such functional group is
directly bonded to an aliphatic hydrocarbon group or those in which such functional
group is directly bonded to an aromatic hydrocarbon group.
[0028]
Specific examples of polycondensation polymer include polymers having a
10 structure in which aliphatic hydrocarbon groups are polymerized via the fictional
group, such as aliphatic polyester, aliphatic polyamide and aliphatic polycarbonate;
polymers having a structure in which aliphatic hydrocarbon groups and aromatic
hydrocarbon groups are polymerized via the fictional group, such as aliphatic
aromatic polyester, aliphatic aromatic polyamide and aliphatic aromatic
15 polycarbonate; and polymers having a structure in which aromatic hydrocarbon
groups are polymerized via the fictional group, such as aromatic polyester and
aromatic polyamide.
[0029]
The above-described polycondensation polymer may be a homopolymer or a
20 copolymer. The polycondensation polymer may also be a copolymer in which
different bonds such as an ester bond, an amide bond and a carbonate bond are
present randomly or in blocks. Specific examples of such copolymers include
polyester carbonate and polyester amide.
[0030]
25 The prepolymer refers to a polymer at an initial stage of polymerization
having polymerization degree lower than the produced polymer product. The
prepolymer may contain an oligomer or a monomer, and is prepolymerized to the

-13-
desired polymerization degree using a conventionally known apparatus such as a
vertical agitating polymerization reactor, a horizontal agitating polymerization
reactor having a uniaxial or biaxial agitation blade, a natural falling thin-film
polymerization reactor having trays, a thin-film polymerization reactor involving
5 natural falling on a sloped plane and a wetted-wall column.
[0031]
For example, a prepolymer of polyester is produced by polycondensation of a
compound containing a hydroxyl group and a compound containing a carboxyl group
or a compound having lower alcohol ester of a carboxyl group. A prepolymer of
10 polyamide is produced by polycondensation of a compound containing an amino
group and a compound containing a carboxyl group. A prepolymer of
polycarbonate is produced by polycondensation of a compound having an aryloxy
group or an alkoxy group on both sides of a carbonyl group and a compound having
a hydroxyl group.
15 [0032]
More specifically, a prepolymer of aliphatic polyester is produced by
polycondensation of a monomer in which a hydroxyl group is directly bonded to an
aliphatic hydrocarbon group having 1 to 30 carbon atoms, such as ethylene glycol,
and a monomer in which a carboxyl group is directly bonded to an aliphatic
20 hydrocarbon group having 1 to 30 carbon atoms, such as adipic acid, or a monomer
in which a hydroxyl group and a carboxyl group are directly bonded to an aliphatic
hydrocarbon group having 1 to 30 carbon atoms, such as glycolic acid.
[0033]
A prepolymer of aliphatic aromatic polyester is produced by
25 polycondensation of a monomer in which a hydroxyl group is directly bonded to an
aliphatic hydrocarbon group having 1 to 30 carbon groups, such as ethylene glycol,
1,3-propanediol, 1,3-butanediol, 1,4-butanediol, neopentyl glycol,

-14-
1,6-hexamethylene gloycol, 1,4-cyclohexanediol or 1,4-cyclohexanedimethanol and
a monomer in which a carboxyl group is directly bonded to an aromatic hydrocarbon
group having 6 to 30 carbon atoms, such as terephthalic acid, isophthalic acid, oxalic
acid, succinic acid, adipic acid, dodecane diacid, fumaric acid, maleic acid,
5 1,4-cyclohexanedicarboxylic acid, 5-sodium sulfoisophthalic acid, 3,5-dicarboxylic
acid benzenesulfonic acid tetramethylphosphonium salt,
1,4-cyclohexanedicarboxylic acid or 2,6-naphthalenedicarboxylic acid, or with these
monomers in which the carboxyl group is esterified by lower alcohol.
[0034]
10 A prepolymer of aromatic polyester is produced by polycondensation of a
monomer in which a hydroxyl group is directly bonded to an aromatic hydrocarbon
group having 6 to 30 carbon atoms, such as bisphenol A and a monomer in which a
carboxyl group is directly bonded to an aromatic hydrocarbon group having 6 to 30
carbon atoms such as terephthalic acid.
15 [0035]
A prepolymer of aliphatic polyamide is produced by polycondensation of a
monomer in which an amino group is directly bonded to an aliphatic hydrocarbon
group having 2 to 30 carbon atoms such as hexamethylenediamine and a monomer in
which a carboxyl group is directly bonded to a aliphatic hydrocarbon group having 1
20 to 30 carbon atoms such as adipic acid.
[0036]
A prepolymer of aliphatic aromatic polyamide is produced by
polycondensation of a monomer in which an amino group is directly bonded to an
aliphatic hydrocarbon group having 2 to 30 carbon atoms such as
25 hexamethylenediamine and a monomer in which a carboxyl group is directly bonded
to an aromatic hydrocarbon group having 6 to 30 carbon atoms such as terephthalic
acid.

-15-
[0037]
A prepolymer of aromatic polyamide is produced by polycondensation of a
monomer in which an amino group is directly bonded to an aromatic hydrocarbon
group having 6 to 30 carbon atoms such as paraphenylenediamine and a monomer in
5 which a carboxyl group is directly bonded to an aromatic hydrocarbon group having
6 to 30 carbon atoms such as terephthalic acid.
[0038]
A prepolymer of aliphatic polycarbonate is produced by polycondensation of
a monomer in which a hydroxyl group is directly bonded to an aliphatic hydrocarbon
10 group having 2 to 30 carbon atoms such as 1,6-hexanediol and a monomer in which a
phenoxy group is bonded to both sides of a carboxyl group such as diphenyl
carbonate.
[0039]
A prepolymer of an aliphatic aromatic polycarbonate is produced by
15 polycondensation of a monomer in which a hydroxyl group is directly bonded to an
aliphatic hydrocarbon group having 2 to 30 carbon atoms such as 1,6-hexanediol, a
monomer in which a hydroxyl group is directly bonded to an aromatic hydrocarbon
group having 6 to 30 carbon atoms such as bisphenol A and a monomer in which a
phenoxy group is bonded to both sides of a carboxyl group such as diphenyl
20 carbonate.
[0040]
Referring to all of the above prepolymers, examples of prepolymers also
include those obtained by previously copolymerizing the prepolymer with
polyalkylene glycol such as polyethylene glycol, polypropylene glycol or
25 polytetramethylene glycol.
[0041]

-16-
For details of the method of producing the above-described prepolymers,
"Polymer Synthesis, vol. 1, second edition", 1992 (Academic Press, Inc.), for
example, can be referred to.
[0042]
5 The polymerization degree of the prepolymer suitable for the present
invention can be defined based on the melt viscosity obtained in evaluation under a
condition of a shear rate of 1000 (sec"1) at a temperature at which polymerization is
performed in the polymerization reactor of the present invention, and is preferably in
the range of 60 to 100000 (poise). When the melt viscosity is set to 60 (poise) or
10 higher, intensive foaming and scattering of prepolymer discharged through holes of
the perforated plate of the polymerization reactor can be prevented. On the other
hand, when the melt viscosity is set to 100000 (poise) or lower, polymerization
proceeds rapidly because reaction by-products can be effectively removed from the
system. The melt viscosity is in the range of preferably 100 to 50000 (poise), more
15 preferably 200 to 10000 (poise), particularly preferably 300 to 5000 (poise). A
prepolymer having such a relatively high polymerization degree is preferred in the
present invention because polymerization can be performed with a great amount of
bubbles in the polymer and as a result, the polymerization velocity can be greatly
improved.
20 (C) Description of polymer modifier:
The kind of polymer modifier is not particularly limited, and the polymer
modifier may be liquid at a temperature below the polymerization temperature of the
polymer or may include solid fine particles at a temperature below the
polymerization temperature of the polymer. The polymer modifier may be reactive
25 with a polymer to form a chemical bond, or may not be reactive with the polymer.
The modifier may have catalytic action to promote the polycondensation reaction or

- 17-
have action to inhibit the activity of a polymerization catalyst contained in the
prepolymer.
[0043]
Specific examples thereof include polyalkylene glycols such as polyethylene
5 glycol, polypropylene glycol and polytetramethylene glycol which are bondable to
polycondensation polymer and offer easiness in dyeing, flexibility, sound controlling
properties and antistatic properties; polyolefins such as polyethylene and
polypropylene which offer a crystallization promoting effect, sliding properties and
high melt flowability and these polyolefins whose terminal group is modified so as to
10 be bondable to polycondensation polymer; fine particles of inorganic or organic
substances such as fine particles of talc, silica or metal oxide or powder of multilayer
organic compound which offer mechanical properties, improvement in the gloss of
molded articles, gas barrier properties, oxygen absorption, antibacterial activity and
flame retardance and these particles into which a functional group bondable to
15 polycondensation polymer is introduced; metal compounds containing titanium,
germanium, antimony, tin, aluminum or cobalt which offer polymerization catalytic
action and hue improvement action; compounds containing phosphor, sulfur or
halogen which inhibit the activity of a polymerization catalyst contained in the
prepolymer to suppress thermal decomposition or generation of oligomers; and other
20 known additives such as delustering agents, heat stabilizers, flame retardants,
antistatic agents, dyes, pigments, antifoaming agents, orthochromatic agents,
antioxidants, ultraviolet absorbers, crystal nucleators, brightening agents and
scavengers for impurities and residual monomers.
[0044]
25 These modifiers may be introduced as is or after mixing with a prepolymer or
with oil or polyethylene which facilitate dispersion through any area of the

-18-
perforated plate. They may be individually introduced through each area or in
combination through an identical area.
(D) Description of polymerization reactor:
Referring now to the polymerization reactor of the present invention, the
5 above-described prepolymer is introduced in a molten state into the polymerization
reactor, discharged through holes of a perforated plate and then melt
polycondensation is performed under reduced pressure while allowing the
prepolymer to fall along a support.
(D-l) perforated plate:
10 The perforated plate means a plate having multiple holes. Use of a
perforated plate prevents uneven flow and local residence of a prepolymer in a
reactor, yielding a high quality, homogeneous polymer. The perforated plate has
two or more areas and any prepolymer and/or polymer modifier may be introduced in
any amount through each area to perform polymerization.
15 [0045]
Referring to the structure of the perforated plate, the thickness of the plate is
not particularly limited, but is usually 0.1 to 300 mm, preferably 1 to 200 mm, more
preferably 5 to 150 mm. The perforated plate should bear the pressure in the
molten prepolymer supply chamber. And in the case that the support in the
20 polymerization chamber is fixed to the perforated plate, the plate should have
strength sufficient for supporting the weight of the support and the falling molten
prepolymer. A preferred mode may be a perforated plate reinforced by ribs or the
like.
[0046]
25 The shape of holes on the perforated plate is usually selected from a circle, an
ellipse, a triangle, a slit, a polygon and a star. The hole has a cross section area of
usually 0.01 to 100 cm2, preferably 0.05 to 10 cm2, and particularly preferably 0.1 to

-19-
5 cm2. The shape and the cross section may be changed in each area depending on
the kind of supplied materials. In addition, a nozzle or the like may be connected to
the hole.
[0047]
5 The distance between holes, which is the distance between the centers of
holes, is usually 1 to 500 mm, preferably 10 to 100 mm. The hole on the perforated
plate may be a through hole or a hole with a tube. The hole may also be a tapered
hole. It is preferred that the size and the shape of the hole is determined so that the
pressure loss when the prepolymer passes through the perforated plate is 0.1 to 50
10 kg/cm2. Referring to the position of holes belonging to each area, they may be
randomly positioned, alternately or periodically positioned in the radius or
circumferential direction of concentric circles, alternately or periodically positioned
in a lattice pattern, collectively positioned in each area, or positioned in plural groups
in each area, depending on the purpose.
15 [0048]
The number of holes on a perforated plate is not particularly limited, and is
different depending on conditions such as reaction temperature or pressure, the
amount of catalyst and the range of molecular weight of materials to be polymerized.
Typically, when a polymer is produced at a rate of 100 kg/hr, for example, the
20 necessary number of holes is 10 to 105, more preferably 50 to 104, further preferably
102 to 103. The number of areas is not particularly limited and is usually 2 to 100,
more preferably 2 to 50, further preferably 2 to 10 in view of the equipment cost.
The number of holes belonging to each area is not particularly limited and is usually
1 to 104, more preferably 1 to 103, further preferably 1 to 102 in view of the
25 equipment cost. The number of holes belonging to each area may be the same or
different.
[0049]

-20-
Typically, the material of the perforated plate is preferably metal such as
stainless steel, carbon steel, hastelloy, nickel, titanium, chrome and other types of
alloys.
[0050]
5 Examples of methods of discharging a prepolymer through the above
perforated plate include a method of allowing a prepolymer to fall through a liquid
head or by its own weight and a method of applying pressure and extruding using a
pump or the like. To suppress fluctuation in the amount of falling prepolymer, a
method of extruding prepolymer using a pump having measuring ability such as a
10 gear pump, is preferred.
[0051]
A filter is preferably provided in a channel in the upstream of the perforated
plate. Such filter can eliminate foreign substances, which block hole on the
perforated plate. A filter which can eliminate a foreign substance greater than the
15 diameter of holes on the perforated plate and which is not broken by passing of
prepolymer is appropriately selected.
(D-2) support:
The prepolymer discharged through holes of the perforated plate falls down
along a support. Examples of specific structures of a support include a "wire form",
20 a "chain form" or a "lattice (wire gauze) form" in which wire form materials are
combined, a "space lattice form" in which wire form materials are connected in a
shape like a jungle gym, a flat or curved "thin plate form" and a "perforated plate"
form. In addition, in order to efficiently remove reaction by-product or impurities
generated by thermal decomposition during polymerization, it is preferred that the
25 surface area of falling resin is increased and agitation and surface renewal are
actively induced by allowing a prepolymer to fall along a support having asperities in
the direction where the prepolymer falls. A support having a structure that impedes

-21-
the falling of resin, e.g., a "wire form having asperities in the direction where the
resin falls" is also preferred. These supports may be used in combination or
appropriately positioned depending on the kind of materials supplied from each area
of the perforated plate. The support may be positioned so that streams of materials
5 supplied from each area of the perforated plate are not combined on the support,
streams of materials supplied from each area of the perforated plate are combined on
the support, or part of the streams of materials supplied from each area of the
perforated plate is combined on the support depending on the purpose.
[0052]
10 The term "wire form" means a material having an extremely great ratio of the
mean length of the outer circumferences of cross sections to the length in the
direction vertical to the cross sections. The area of the cross section is not
particularly limited, but it is usually 10-3 to 102 cm2, preferably 10-3 to 101 cm2, and
particularly preferably 10-2 to 1 cm2. The shape of the cross section is not
15 particularly limited, but it is usually selected from a circle, an ellipse, a triangle, a
quadrangle, a polygon and a star. The cross sectional shape may be the same or
different in the length direction. The wire may also be a hollow wire. The wires
include a single wire and a combined wire obtained by twisting multiple wires. The
surface of the wire may be smooth, uneven or may have projections in some part.
20 [0053]
The term "chain form" means a material obtained by connecting rings made
of the above-described wire form material. The shape of the ring may be a circle,
an ellipse, a rectangle or a square. The rings may be connected one-dimensionally,
two-dimensionally or three-dimensionally.
25 [0054]
The term "lattice form (wire gauze form)" means a material formed by
combining the above-described wire form material in a lattice form. Wires to be

-22-
combined may include both a linear wire and a curved wire. The combination angle
may be selected as desired. When a lattice-form (wire gauze form) is projected
from a vertical direction against the plane, the area ratio of the material to the space
is not particularly limited. However, the area ratio is usually between 1:0.5 to
5 1:1000, preferably between 1:1 to 1:500, particularly preferably between 1:5 to 1:100.
The area ratio is preferably equal in the horizontal direction. The area ratio is
preferably equal or the proportion of the space may be increased in the lower part in
the vertical direction.
[0055]
10 The term "space lattice form" means a material obtained by
three-dimensionally combining wire-form materials in a space lattice form like a
so-called jungle gym. Wires to be combined may be both a linear wire and a curved
wire. The combination angle may be selected as desired.
[0056]
15 The term "wire form having asperities in the direction where a polymer falls"
means a material obtained by attaching bars having a circular or polygonal
cross-section perpendicularly to a wire, or a material obtained by attaching disks or
cylinders to a wire. The step between the resulting recess and protrusion is
preferably 5 mm or greater. Specific examples thereof may be a disk-attached wire
20 in which a wire pierces through the center of disks having a diameter 5 mm or more
greater and 100 mm or smaller than the diameter of the wire, having a thickness of 1
to 50 mm with an interval of the disks of 1 to 500 mm.
[0057]
The ratio of the volume of the support installed in the reactor to the internal
25 volume of the reactor is not particularly limited. The ratio is usually 1:0.5 to 1:107,
preferably 1:10 to l:105, particularly preferably 1:50 to l:105. The ratio of the
volume of the support to the internal volume of the reactor is preferably equal in the

-23-
horizontal direction. The ratio is preferably equal or the proportion of the internal
volume of the reactor may be increased in the lower part in the vertical direction.
[0058]
A single support or multiple supports may be provided, and they may be
5 appropriately selected depending on the shape. In the case of a "wire form" support
or a "chain form" support, the number of supports is usually 1 to 105, preferably 3 to
104. In the case of a "lattice form", "two dimensionally-connected chain-form",
"thin plate form" or "perforated plate form" support, the number of supports is
usually 1 to 104, preferably 2 to 103. In the case of a "three-dimensionally
10 connected chain-form" support or a "space lattice form" support, whether a single
support is used or a support is divided to form multiple supports may be
appropriately selected depending on the size of the apparatus, the space where the
support is installed, and the like.
[0059]
15 When multiple supports are used, it is preferable that a spacer or the like be
appropriately used so that the supports do not come into contact with one another.
[0060]
The material of the support is not particularly limited, and usually selected
from stainless steel, carbon steel, hastelloy and titanium. The wire may be
20 subjected to surface treatment such as plating, lining, passivation or acid cleaning if
necessary.
[0061]
In the present invention, a prepolymer is usually supplied to a single support
through one or more holes of a perforated plate, and the number of holes can be
25 appropriately selected depending on the shape of the support. Further, a
prepolymer that has passed through a hole may be allowed to fall along a plurality of
supports. A prepolymer may be supplied \o a support through holes of plural areas


-24-
of a perforated plate, or may be supplied to two or more supports through holes of
one area of the perforated plate depending on the purpose.
[0062]
The position of the support is not particularly limited as long as the
5 prepolymer can fall along the support. The method of attaching the support to the
perforated plate may be accordingly selected from the case in which the support is
disposed so as to pierce through holes of the perforated plate and the case in which
the support is disposed below holes of the perforated plate so as not to pierce through
the holes.
10 [0063]
The falling length along the support of the prepolymer that has passed through
holes is preferably 0.5 to 50 m, more preferably 1 to 20 m, further preferably 2 to 10
m.
(D-3) outlet:
15 The polymerization reactor may have one outlet or two or more outlets.
When two or more outlets are provided, a polymer falling along two or more
supports may be discharged from one outlet, a polymer falling along one support
may be discharged from two or more outlets or a polymer falling along two or more
supports may be discharged from two or more outlets.
20 (D-4) heating apparatus:
The polymerization temperature may be appropriately adjusted by controlling
the temperature of a heater or a heating jacket covering the support disposed along
the wall of the polymerization reactor, or by putting a heater or a heating medium
inside the support and controlling their temperature.
25 (D-5) decompressor:
The degree of reduced pressure in the polymerization reactor may be
appropriately set by controlling the degree of decompression by connecting a vent

-25-
port provided at any position of the polymerization reactor to a vacuum line.
Polymerization by-products, impurities generated by thermal decomposition in
polymerization and inert gas introduced into the polymerization reactor in small
amounts as needed are discharged from the vent port.
5 (D-6) inert gas feeding apparatus:
When inert gas is directly introduced into the polymerization reactor, the gas
may be introduced from a introducing port provided at any position of the
polymerization reactor. It is desired that the inert gas introducing port is positioned
away from the perforated plate but close to the discharge port of the polymer. It is
10 also desired that the feed port is positioned away from the vent port.
[0064]
Alternatively, a method of allowing inert gas to be absorbed to and/or
contained in a prepolymer in advance is also available. In that case, an inert gas
feeding apparatus is provided at the upstream of the polymerization reactor of the
15 present invention.
[0065]
For example, a method using a known absorption device as an inert gas
supply apparatus such as a packed tower-type absorption device, a plate-type
absorption device or a spray tower-type absorption device described in Kagaku Sochi
20 Sekkei/Sosa Series No. 2, Kaitei Gasu Kyushu, pp. 49 to 54 (March 15, 1981,
published by Kagaku Kogyo Co., Ltd.), and a method of pressing inert gas into a
tube transferring a prepolymer may be employed. Most preferred is a method of
using an apparatus for absorption of inert gas while allowing a prepolymer to fall
along a support in an inert gas atmosphere. In this method, inert gas having a
25 pressure higher than that in a polymerization reactor is introduced into the apparatus
for absorption of inert gas. The pressure in this case is preferably between 0.01 to 1

-26-
MPa, more preferably between 0.05 to 0.5 MPa, further preferably between 0.1 to 0.2
MPa.
(E) Description of polymerization method:
The present inventors have found that by polymerizing a prepolymer having a
5 melt viscosity that is within the aforementioned range using the aforementioned
polymerization reactor at a polymerization temperature and a degree of reduce
pressure described below, scattering of prepolymer due to intensive foaming which
occurs immediately below the perforated plate can be prevented, and deterioration of
the quality of the polymer due to contamination of the nozzle surface and walls of the
10 polymerization reactor can be prevented, and in addition, the polymer falling along
the support contains a large amount of bubbles and the surface area of the polymer
increases and the polymer rolls down along the support in the form of bubbles. At
the same time, a significant increase in the polymerization velocity and improvement
of the hue of the polymer have been confirmed.
15 [0066]
It is considered that such significant increase in the polymerization velocity is
caused by combined actions of a surface area expansion effect due to a large amount
of bubbles contained and a surface renewal effect due to plasticizing action of
bubbles. Furthermore, the plasticizing action of bubbles has also made it possible
20 to improve the polymer hue due to a shortened residence time of the polymer in the
polymerization reactor and to easily discharge a polymer having a high
polymerization degree and a high viscosity from the polymerization reactor.
[0067]
In order to obtain a high quality, high polymerization degree polymer,
25 conventional gravity drop type thin-film melt polymerization reactors such as a
wetted-wall column are designed to polymerize a prepolymer in an initial stage of a
reaction having a polymerization degree extremely lower than that of the prepolymer

-27-
used in the method of the present invention at a higher temperature in a shorter
residence time compared to the method of the present invention. In conventional
technical knowledge, when melt polymerization of a prepolymer having a high
polymerization degree as in the method of the present invention is continuously
5 performed, coloring of the prepolymer progresses and the residence time of fall
through the polymerization reactor is increased. Thus, production of high quality
polymer was inconceivable.
[0068]
In this situation, the range of the melt viscosity of the prepolymer is set
10 relatively high in the present invention contrary to conventional technical knowledge
as described above. Further, as described later, the polymerization temperature is
set relatively low contrary to conventional technical knowledge. The present
inventors have found that the above settings enable control of the foaming condition
of a polymer, and found a surprising effect that the polymerization velocity can be
15 significantly increased and a polymer having a high polymerization degree can be
easily discharged at low temperatures.
(E-l) polymerization temperature:
The reaction temperature of polycondensation is preferably (crystalline
melting point -10°C) or higher and (crystalline melting point +60°C) or lower of the
20 polycondensation polymer. By setting the reaction temperature to (crystalline
melting point -10°C) or higher, solidification of the reactant and extension of
reaction time can be prevented. By setting the reaction temperature to (crystalline
melting point +60°C) or lower, thermal decomposition can be prevented and a
polymer having excellent hue can be produced. The reaction temperature is more
25 preferably (crystalline melting point -5°C) or higher and (crystalline melting point
+40°C) or lower, further preferably crystalline melting point or higher and
(crystalline melting point +30°C) or lower. Such relatively low reaction

-28-
temperature is preferred in the present invention because the polymer tends to
contain a large amount of bubbles and as a result, the polymerization velocity can be
greatly improved.
[0069]
5 Herein, the crystalline melting point means a peak temperature at an
endothermic peak derived from melting of crystal measured using Pyris 1 DSC
(input-compensating differential scanning calorimeter) manufactured by Perkin
Elmer, Inc. under the conditions described below. The peak temperature is
determined using attached analysis software.
10 [0070]
Measurement temperature: 0 to 300°C
Temperature rising rate: 10°C/min
(E-2) polymerization pressure:
It is necessary to perform the melt polycondensation reaction of the present
15 invention under reduced pressure so that the polymer contains a large amount of
bubbles. The degree of reduced pressure is accordingly adjusted based on the
sublimation state of prepolymer or products of the polycondensation reaction or the
reaction rate. The degree of reduced pressure is preferably 50000 Pa or lower, more
preferably 10000 Pa or lower, further preferably 1000 Pa or lower, and particularly
20 preferably 500 Pa or lower. The lower limit is not particularly determined, but in
view of scale of equipment for reducing pressure in the polymerization reactor, the
pressure is preferably 0.1 Pa or higher.
[0071]
Moreover, it is also preferable to introduce a small amount of inert gas which
25 does not affect the polycondensation reaction into the polymerization reactor under
reduced pressure to remove by-products generated as a result of polymerization or

-29-
impurities generated by thermal decomposition in polymerization together with theinert gas.
[0072]
It has been understood that inert gas is introduced into a polymerization
5 reactor to decrease the partial pressure of by-products generated as a result of
polymerization and to shift equilibrium so as to promote the reaction effectively. In
the present invention, however, the amount of inert gas to be introduced is extremely
small, and thus, the effect of increasing the polymerization velocity by the decreased
partial pressure can hardly be expected. Thus, the above role of inert gas cannot be
10 explained based on conventional knowledge.
[0073]
The studies of the present inventors have revealed that introduction of inert
gas into a polymerization reactor causes intensive foaming of prepolymer falling
along a support in a molten state, and the surface area of the prepolymer is
15 significantly increased and the surface renewal state is greatly improved. Although
the principle is unknown, it is assumed that the change in the inside and the surface
state of the prepolymer causes a significant increase in the polymerization velocity.
[0074]
Gas that does not have adverse effects such as coloring, denaturation and
20 decomposition on resin is suitable as inert gas to be introduced, and examples of such
gas include nitrogen, argon, helium, carbon dioxide, lower hydrocarbon gas and a
mixed gas thereof. More preferred inert gas is nitrogen, argon, helium or carbon
dioxide, and of these, nitrogen is particularly preferred because it is readily available.
[0075]
25 In the present invention, the amount of inert gas introduced may be extremely
small, and is preferably 0.05 to 100 mg per 1 g of polymer discharged from the
polymerization reactor. When the amount of inert gas is 0.05 mg or more per 1 g of

-30-
polymer discharged from the polymerization reactor, foaming of resin is sufficient
and the effect of improving the polymerization degree increases. On the other hand,
when the amount of inert gas is 100 mg or less, the degree of reduced pressure can be
easily increased. The amount of inert gas is more preferably 0.1 to 50 mg,
5 particularly preferably 0.2 to 10 mg per 1 g of polymer discharged from the
polymerization reactor.
[0076]
Examples of methods of introducing inert gas include a method of directly
introducing inert gas into a polymerization reactor, a method of previously allowing
10 inert gas to be absorbed to and/or contained in a prepolymer and releasing the
absorbed and/or contained gas from the prepolymer under reduced pressure so as to
introduce it into a polymerization reactor, and a method of using these methods in
combination. The term "absorb" used herein means that inert gas is dissolved in a
polymer and not in the form of air bubbles, and the term "contain" means that inert
15 gas is present in the form of air bubbles. When the inert gas is present in the form
of air bubbles, the smaller the size of the air bubble, the better. The average bubble
diameter is preferably 5 mm or less, and more preferably 2 mm or less.
(E-3) polymerization time:
The polymerization time means the total of the time for falling of a polymer
20 along the support and the time of residence of the polymer at the bottom of the
polymerization reactor. The polymerization time is preferably 10 seconds to 100
hours, more preferably 1 minute to 10 hours, further preferably 5 minutes to 5 hours,
particularly preferably 20 minutes to 3 hours.
[0077]
25 In the present invention, a method of discharging all the polymer polymerized
from a prepolymer from the polymerization reactor in a single pass, or a method in
which part of the produced polymer is circulated and reintroduced into the

-31-
polymerization reactor may be employed, and the method of discharging all the
polymer in a single pass is preferred. In the case of circulation, it is preferred that
the temperature is lowered and the residence time is shortened at the bottom or in the
circulation line of the polymerization reactor in order to suppress thermal
5 decomposition in these areas.
(E-4) polymerization velocity:
The polymerization reactor of the present invention has a characteristic that
the polymerization ability can be increased in proportion to the number of supports
disposed in the polymerization reactor in the case of a wire form support and thus
10 scale up can be easily designed.
[0078]
In the case of a wire form support, the flow rate of prepolymer per support is
preferably 10"2 to 1021/hr. When the flow rate is within this range, sufficient
production capacity is assured and the polymerization velocity can be significantly
15 increased. The flow rate is more preferably in the range of 0.1 to 501/hr.
[0079]
In the case of a support in which wires are combined such as a lattice form
(wire gauze form) support, the flow rate of prepolymer is in the range of preferably
10 2 to 1021/hr, more preferably 0.1 to 501/hr per wire structure in the vertical
20 direction constituting the support.
[0080]
In the case of a thin plate form support which does not have a wire combined
structure, the flow rate of prepolymer is in the range of preferably 10 2 to 102 1/hr,
more preferably 0.1 to 50 1/hr per hole of a perforated plate through which a
25 prepolymer is supplied to the support.

-32-
(E-5) molecular weight modifier:
In the present invention, a prepolymer may be reacted with any amount of a
molecular weight modifier according to need in any step prior to introducing the
prepolymer into the polymerization reactor of the present invention. The present
5 inventors have found that the falling speed of the prepolymer along the support can
be drastically changed by changing the molecular weight of the prepolymer
introduced into the polymerization reactor of the present invention and that due to
such change, the residence time in the polymerization reactor can be controlled, and
qualities such as polymerization degree of the produced resin and production
10 quantities thereof can be easily and extensively controlled.
[0081]
In addition, when, for example, a prepolymer is transferred to the
polymerization reactor of the present invention from the prepolymer preparation
process, by making the transfer pipe branched so that the prepolymer can be
15 introduced into each area of the perforated plate of the polymerization reactor of the
present invention and introducing a molecular weight modifier into the branched pipe
leading to an area of the perforated plate, a plurality of polymers having a different
polymerization degree can be produced simultaneously and a polymer having a large
molecular weight distribution can be produced as described later.
20 [0082]
As a molecular weight modifier, a molecular weight reducing agent or a
molecular weight increasing agent may be used. In the present invention, use of the
molecular weight modifier enables extensive control of qualities such as
polymerization degree and production quantities of polycondensation polymer,
25 which was impossible in the conventional polymerization process.
[0083]

-33-
For example, when a molecular weight reducing agent is used, the
polymerization degree of the polycondensation polymer produced in the
polymerization reactor of the present invention can be significantly reduced only by
adding a relatively small amount of a molecular weight reducing agent. This is
5 because increase in the falling speed of the prepolymer along the support produces an
effect of shortening of the reaction time, in addition to the effect by the molecular
weight reducing agent itself, The fact that the polymerization degree of the
produced polycondensation polymer can be significantly reduced means that the
production quantities can be significantly reduced.
10 [0084]
On the contrary, because only the effect by the molecular weight reducing
agent is available in conventional polymerization methods, the polymerization
degree of the polycondensation polymer is reduced only to an extent corresponding
to the amount added of the molecular weight reducing agent. For this reason, a
15 large amount of molecular weight reducing agent must be added to extensively adjust
the molecular weight, and this involves problems of operation, costs and the quality
of products. On the other hand, when a molecular weight increasing agent is used,
the polymerization degree of the polycondensation polymer produced in the
polymerization reactor of the present invention can be significantly increased only by
20 adding a relatively small amount of molecular weight increasing agent. This is
because lowering of the falling speed of the prepolymer along the support produces
an effect of extension of the reaction time, in addition to the effect by the molecular
weight increasing agent itself. The fact that the polymerization degree of the
produced polycondensation polymer can be significantly increased means that the
25 production quantities can be significantly increased. On the contrary, because only
the effect by the molecular weight increasing agent is available in conventional
polymerization methods, the polymerization degree of the polycondensation polymer

-34-
is increased only to an extent corresponding to the amount added of the molecular
weight increasing agent. For this reason, a large amount of molecular weight
increasing agent must be added to extensively adjust the molecular weight, and this
involves problems of operation, costs and the quality of products.
5 [0085]
In addition, when the molecular weight of the prepolymer supplied from the
prepolymer preparation process fluctuates, the fluctuation is to be detected, and
based on the detection result, a molecular weight modifier may be added to the
prepolymer at a stage before introducing the prepolymer into the polymerization
10 reactor. By this, fluctuation in the molecular weight is diminished and a
prepolymer with little fluctuation in the molecular weight can be introduced into the
polymerization reactor.
[0086]
The molecular weight modifier may be allowed to react with the prepolymer
15 in any step before introducing the prepolymer into the polymerization reactor. The
reaction may be performed in a separate reactor. Alternatively, a molecular weight
modifier may be introduced into a prepolymer transfer pipe to induce a reaction in
the pipe. A method of facilitating mixing and reaction of a molecular weight
modifier using a kneader having a driving member such as extruder or a static mixer
20 is also preferred.
[0087]
As a molecular weight reducing agent, a known agent used for
depolymerization or for reducing molecular weight of polymer may be appropriately
used depending on the kind of polymer. Starting monomers described in the above
25 (B), prepolymers having a lower molecular weight or compounds simultaneously
produced in the polycondensation reaction may also be used as a molecular weight
reducing agent.

-35-
[0088]
For example, when the polycondensation polymer is polyester resin, useful is
a compound or a mixture of two or more compounds selected from compounds in
which 2 or less hydroxyl groups are directly bonded to an aliphatic hydrocarbon
5 group having 1 to 30 carbon atoms, such as ethylene glycol, 1,3-propanediol,
1,4-butanediol, neopentyl glycol, 1,6-hexamethylene glycol, 1,4-cyclohexanediol,
methanol, ethanol, propanol, butanol and benzyl alcohol; alkylene glycols such as
diethylene glycol, triethylene glycol, tetraethylene glycol, dipropylene glycol and
tripropylene glycol; water; compounds in which 2 or less carboxyl groups are
10 directly bonded to an aromatic hydrocarbon group having 6 to 30 carbon atoms such
as terephthalic acid, isophthalic acid, naphthalenedicarboxylic acid, 5-sodium
sulfoisophthalic acid and 3,5-dicarboxylic acid benzenesulfonic acid
tetramethylphosphonium salt; compounds in which 2 or less carboxyl groups are
directly bonded to an aliphatic hydrocarbon group having 1 to 30 carbon atoms, such
15 as formic acid, acetic acid, propionic acid, butanoic acid, oxalic acid, succinic acid,
adipic acid, dodecane diacid, fumaric acid, maleic acid and
1,4-cyclohexanedicarboxylic acid; compounds in which a hydroxyl group and a
carboxyl group are directly bonded to an aliphatic hydrocarbon group having 1 to 30
carbon atoms, such as lactic acid and glycolic acid, and these compounds in which
20 the carboxyl group is esterified by lower alcohol.
[0089]
When the polycondensation polymer is polyamide resin or polycarbonate
resin, a starting monomer described in the above (B), a prepolymer having a lower
molecular weight or a compound simultaneously produced in the polycondensation
25 reaction may be used as a molecular weight reducing agent. In addition, the
aforementioned molecular weight reducing agents for polyester resin may be used as
a molecular weight reducing agent for polyamide resin or polycarbonate resin, or the

-36-
aforementioned molecular weight reducing agents for polyamide resin or
polycarbonate resin may be used as a molecular weight reducing agent for polyester
resin. Further, a method of suppressing increase in the molecular weight by
inhibiting the polycondensation reaction by adding a compound which inhibits the
5 action of polymerization catalyst such as water or trimethyl phosphate, a method of
not only decreasing the molecular weight but also suppressing the increase in the
molecular weight by adding a mono-functional or low reactive compound which can
serve as a reaction terminal blocking agent, or a method of inhibiting the
polycondensation reaction by lowering the temperature of a prepolymer by adding a
10 lower temperature prepolymer or mixing part of a prepolymer adjusted to a lower
temperature in some portion with the rest of the prepolymer.
[0090]
The molecular weight increasing agent is not particularly limited as long as it
has action of increasing the molecular weight of a prepolymer upon addition. For
15 example, molecular weight can be increased by adding a higher molecular weight
prepolymer collected from the step closer to the final product, a commercially
available high molecular weight polymer or a high molecular weight polymer
produced by another polymerization method such as solid-state polymerization and
by carrying out an exchange reaction. More specifically, useful is a method or a
20 combination of two or more methods selected from a method of increasing molecular
weight by a partial cross-linking reaction by adding a compound having 3 or more
functional groups capable of inducing a condensation reaction, such as glycerin,
pentaerythritol, sorbitol, 1,2,4-benzenetricarboxylic acid or citric acid; a method of
increasing molecular weight by promoting a polycondensation reaction by adding, or
25 adding in an amount greater than usual amount, a compound having action of a
polymerization catalyst containing titanium, germanium, antimony, tin, aluminum or
cobalt, such as hydrolysates obtained by hydrolysis of titanium oxide, titanium

-37-
tetrabutoxide, titanium tetraisopropoxide, a halogenated titanium compound or
titanium alkoxide, hydrolysates obtained by hydrolysis of germanium oxide,
germanium isopropoxide or germanium alkoxide, antimony oxide, tin acetate, tin
2-ethylhexanoate, aluminum acetate, aluminum propionate, aluminum lactate,
5 aluminum chloride, aluminum hydroxide, aluminum carbonate, aluminum phosphate,
aluminum ethoxide, aluminum isopropoxide, aluminum acetylacetonate and cobalt
acetate; and a method of increasing molecular weight by facilitating a
polycondensation reaction by increasing the temperature of a prepolymer with the
addition of a prepolymer heated to a higher temperature or by mixing part of a
10 prepolymer adjusted to a higher temperature in some portion with the rest of the
prepolymer.
(E-6) others:
In the present invention, other than supplying an additive such as a stabilizer,
a nucleating agent or a pigment through the above-described perforated plate of the
15 polymerization reactor according to need, they may be added to the resin using a
single or twin screw kneader or a static mixer positioned between the polymerization
reactor and the molding machine.
[0091]
In the present invention, various additives, e.g., delustering agents, heat
20 stabilizers, flame retardants, antistatic agent, antifoaming agents, orthochromatic
agents, antioxidants, ultraviolet absorbers, crystal nucleators, brightening agents and
scavengers for impurities may be copolymerized or mixed according to need.
These additives can be added at any stage.
[0092]
25 In particular, an appropriate stabilizer is preferably added depending on
polymers to be polymerized in the present invention. In the case of polyester resin,
for example, pentavalent and/or trivalent phosphorus compounds or hindered phenol

-38-
compounds are preferred. The phosphorus compound is added so that the weight
ratio of phosphorus in the polymer is preferably 2 to 500 ppm, more preferably 10 to
200 ppm. Examples of specific compounds preferred include trimethyl phosphite,
phosphoric acid and phosphorous acid. Phosphorus compounds are preferred
5 because they can suppress coloring of a polymer and serve as a crystal nucleator.
[0093]
A hindered phenol compound means a phenol derivative having a substituent
with steric hindrance at a position adjacent to a phenol hydroxyl group and
containing one or more ester bond in a molecule. The hindered phenol compound is
10 added in a proportion of preferably 0.001 to 1% by weight, more preferably 0.01 to
0.2% by weight based on the weight ratio the obtained polymer.
[0094]
Specific examples of such compounds include pentaerythritol
tetrakis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate],
15 1,1,3-tris(2-methyl-4-hydroxy-5-tert-butylphenyl)butane,
octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate and N,N'-hexamethylene
bis(3,5-di-tert-butyl-4-hydroxyhydrocirmainide). Using these stabilizers together is
one of the preferred methods.
[0095]
20 , Although these stabilizers can be added at any stage before molding, it is
preferred that a phosphorus compound is added at an initial stage of the
polycondensation reaction, and a hindered phenol compound is added at an initial
stage of the polycondensation reaction or after discharging the produced polymer
from the polymerization reactor.
25 [0096]
Further, a crystal nucleator may be added in the present invention. In the
case of polyester resin, for example, a phosphorus compound, an organic acid metal

-39-
salt and powder of polyolefin or other resin are preferable. The crystal nucleator
may be added in a proportion of preferably 2 to 1000 ppm, more preferably 10 to 500
ppm in the polymer.
[0097]
5 Specific examples thereof include phosphates such as 2,2'-methylene
bis(4,6-di-t-butylphenyl)sodium phosphate and bis(4-t-butylphenyl)sodium
phosphate, sorbitols such as bis(p-methylbenzylidene)sorbitol, and metal
element-containing compounds such as bis(4-t-butylbenzoic acid)hydroxyaluminum.
In particular, a crystal nucleator is preferably used for preforms of PET bottles whose
10 mouth part is crystallized by heating, in order to promote the crystallization and
lower the thermal crystallization temperature.
[0098]
Further, in the present invention, addition of a scavenger for low molecular
weight volatile impurities is one of the preferred methods. In the case of PET, for
15 example, acetaldehyde is generated as impurities, and examples of scavengers for
acetaldehyde include polymers or oligomers of polyamide or polyesteramide, and
low molecular weight compounds having an amide group or an amine group such as
2-aminobenzamide. Specific examples thereof include polymers such as polyamide
including nylon 6.6, nylon 6 and nylon 4.6 and polyethyleneimine, and a reaction
20 product of N-phenylbenzeneamine and 2,4,4-trimethylpentene, and Irganox 1098®
and Irganox 565® available from Ciba Specialty Chemicals. These scavengers are
preferably added after the produced polymer is discharged from the polymerization
reactor and before it is fed into the molding machine.
(F) Description of molding method:
25 The produced polymer is once pelletized, then melted again and subjected to
molding, or by a method in which the polymer is transferred to a molding machine in

-40-
a molten state and molded, higher quality molded articles can be produced at low
cost.
[0099]
In the case of pelletization, it is desired that the pelletized polymer is
5 uniformly extruded using an extruder with reduced loss. To obtain such pellet, it is
preferred that molten polymer is extruded in the form of a strand or a sheet,
immediately put in a coolant such as water to be cooled and cut. The temperature
of the coolant is preferably 60°C or lower, more preferably 50°C or lower and further
preferably 40°C or lower. Water is preferable as a coolant in view of economical
10 efficiency and handling properties, and so the temperature of the coolant is
preferably 0°C or higher. Cutting for pelletization is preferably performed after
cooling the resin to 100°C or lower within 120 seconds from extrusion.
[0100]
When the produced polymer is transferred to a molding machine in a molten
15 state and molded, it is important that the polymer discharged from the polymerization
reactor is transferred to the molding machine and molded while maintaining the
quality by suppressing lowering of polymerization degree, coloring and generation of
impurities due to thermal decomposition.
[0101]
20 A polymer once pelletized requires high temperature heating in melt
processing particularly in the case of a highly crystalline polymer, and conditions
become severe as heat tends to be generated by shearing, resulting in the problem of
deterioration of the quality. On the contrary, molded articles produced by the
polymerization method and the molding method of the present invention hardly
25 suffer from deterioration in quality before and after the melt processing. This
seems to be because entry of leak air, breakage of molecular chain due to shearing or
deterioration of resin due to residence in a molten state hardly occurs since

-41 -
polymerization is completed at a low polymerization temperature in a short period in
the polymerization method of the present invention and the polymerization apparatus
has no rotary driving unit or no resin pool in the main body, and because the polymer
is not affected by moisture absorption or oxidation deterioration when supplied to a
5 melt processing apparatus. Further, compared to a molding method after
pelletization, extra steps and energy for transport and storage of pellets and drying of
pellets before molding can be omitted.
[0102]
To transfer the polymer polymerized by the polymerization method of the
10 present invention to a molding machine in a molten state and mold the polymer, it is
necessary to transfer the polymer discharged from the polymerization reactor to the
molding machine and perform melt molding in a short period at the lowest possible
temperature without solidifying the polymer. Herein, the molten state means that a
polymer is melted by heating and in a flowing state, with a viscosity of about
15 500,000 Pa-s or lower.
[0103]
When the temperature for transferring a produced polymer to a molding
machine and molding is (crystalline melting point -10°C) or higher, stable operation
is possible without remarkable increase in viscosity or solidification. When the
20 temperature is set to (crystalline melting point +60°C) or lower, a high quality
molded article with little coloring or generation of volatile impurities due to thermal
decomposition can be produced. The temperature is preferably in the range of
(crystalline melting point +0 to 40°C), more preferably (crystalline melting point +0
to 30°C), further preferably (crystalline melting point +0 to 20°C), and particularly
25 preferably (crystalline melting point +1 to 15°C). The temperature can be set to
such ranges by appropriately controlling the temperature of a transfer pipe, a transfer
pump and a heater or a jacket covering the molding machine.

-42-
[0104]
The time taken before molding is preferably within 40 minutes, more
preferably within 20 minutes and particularly preferably within 10 minutes.
Obviously, the shorter the time, the better. Herein, the time taken before molding
5 means a period of time in which a molten polymer is discharged from a drainage
pump of the polymerization reactor and cooled to not higher than a temperature at
which the polymer crystallizes in a molding machine or after being discharged from
the molding machine. In the case of continuously transferring through a pipe, the
average time calculated from the volume of the pipe or the like and the flow rate can
10 be employed. When this time varies, it is necessary to adjust the time to be within
the above-described time range.
[0105]
Referring to the molding machine, a commercially available pellet molding
machine may be used as is or after modification. Since molten polymer is directly
15 supplied to the molding machine from the polymerization reactor in the present
invention, it is possible to simplify or omit a pellet plasticizing mechanism such as a
melt plasticizing screw which is essential in a conventional pellet molding machine.
As a result, molding can be performed under conditions in which heat generation by
shearing caused by the plasticizing mechanism is low and thus high quality molded
20 articles can be produced.
[0106]
Examples of molded articles produced by the above-described method include
preforms for molding hollow articles, films, sheets and pellets. These articles may
be produced using one molding machine, or the same kind of articles may be
25 simultaneously produced using two or more molding machines, or multiple kinds of
articles may be simultaneously produced using two or more molding machines.
[0107]

-43-
Since an injection molding machine is intermittently operated, when a
plurality of injection molding machines are used, molding cycles of the molding
machines may be delayed at a constant interval to average the flow rate in order to
keep a constant flow rate without allowing the polymer discharged from the
5 polymerization reactor to stay in a pipe connecting the polymerization reactor and
the molding machine for a long time.
[0108]
Further, in the case that a polymer continuously discharged from a
polymerization reactor is introduced into an intermittently operating molding
10 machine, an accumulator for accumulating a molten polymer is preferably installed
along the path. It is more preferable that the molding machine is synchronized with
the accumulator so as to reduce accumulation of molten polymer.
[0109]
Furthermore, an extruder is preferably provided separately from a molding
15 machine so as to perform pelletization simultaneously with molding.
[0110]
When the polymerization reactor of the present invention has two or more
outlets, plural kinds of polymers or compositions can be simultaneously produced.
Accordingly, composite molded articles such as multilayer bottles, multilayer films
20 and conjugated fibers in which polymers or compositions are combined at any
proportions can be produced, or different molded articles may be simultaneously
produced without combining those plural kinds of polymers or compositions. In
particular, in the case of producing composite molded articles, since plural kinds of
polymers or compositions can be prepared in one polymerization reactor, the pipe
25 transferring polymers or compositions to a composite molding machine can be
shortened, and thus deterioration of quality of the polymer in the pipe (in the case of
PET resin, increase of acetaldehyde content) can be prevented. This method is thus

-44-
preferred and also applicable to production of PET/PEN composite bottles having
low acetaldehyde content and excellent gas barrier properties.
[0111]
A single kind of polymer or composition and a molded article thereof may be
5 produced as well. For example, possible applications include simultaneous
production of PET resin preforms having a high polymerization degree suitable for
bottles of carbonated beverages, PET resin preforms having a middle polymerization
degree suitable for bottles of non-carbonated beverages and PET resin pellets having
a relatively low polymerization degree suitable for uses as fiber, using one
10 polymerization reactor having three outlets, two molding machines and a pelletizer.
A plurality of molding machines or pelletizers may be connected to an outlet of a
polymerization reactor, or a molding machine or a pelletizer may be connected to a
plurality of outlets of a polymerization reactor, or they may be connected so that the
combination of the outlet of the polymerization reactor and the molding machine or
15 the pelletizer can be changed.
(G) Description of produced polymer:
According to the production method of the present invention, any kind of
prepolymer and/or polymer modifier can be introduced into each area of a perforated
plate to perform polymerization. Such a prepolymer and/or a polymer modifier
20 introduced from each area of a perforated plate can be polymerized while falling
along a support in a polymerization reactor without being combined, can be
polymerized while falling along a support so as to be combined, or polymerized
while falling along a support so as to be partially combined. In addition, according
to the polymerization method of the present invention, a polymer homogeneously
25 mixed and uniform in quality can be produced at low temperatures despite the
absence of a power driven stirring mechanism such as stirring blade, which was
impossible by conventionally known polymerization reactors and kneaders, and so a

-45-
high quality polymer can be produced. For example, in the case of PET/PBT
polymer alloy, because the melting point of PET and the thermal decomposition
temperature of PBT are close and the alloy could only be produced at a temperature
20°C or more higher than the melting point of PET by conventional technique,
5 deterioration of PBT tends to occur and so it was difficult to produce a high quality
PET/PBT polymer alloy; however, according to the present invention, production at
a polymerization temperature equal to or lower than the melting point of PET is
possible, and therefore a high quality polymer alloy can be produced. Moreover, by
polymerizing while entirely combining prepolymers on a support, a randomly
10 transesterified PET/PBT alloy can be produced, or by polymerizing while combining
part of prepolymers on a support, a PET/PBT alloy having a high blocking properties
can be produced.
[0112]
Examples of polymer alloys produced by the above method include
15 polyester/polyester alloys, polyester/PC alloys and polyester/polyolefin alloys.
Examples of polyester/polyester alloys include polymer alloys obtained by
mixing two or more conventionally known polyester polymers such as PET, PBT,
PTT, polyester elastomer, polyester ether elastomer, polyallylate, liquid crystalline
polyester and aliphatic polyester in any proportion according to any method of
20 combining on the support.
Examples of polyester/PC alloys include polymer alloys obtained by mixing
one or more conventionally known polyester polymers such as PET, PBT, PTT,
polyester elastomer, polyester ether elastomer, polyallylate, liquid crystalline
polyester and aliphatic polyester with a conventionally known polycarbonate
25 polymer in any proportion according to any method of combining on the support.
Examples of polyester/polyolefin alloys include polymer alloys obtained by
mixing one or more conventionally known polyester polymers such as PET, PBT,

-46-
PTT, polyester elastomer, polyester ether elastomer, polyallylate, liquid crystalline
polyester and aliphatic polyester with a conventionally known polyolefin polymer
such as polyethylene or polypropylene in any proportion according to any method of
combining on the support. Herein, using a polyolefin polymer containing a
5 hydroxyl group, a carboxyl group, an epoxy group, an amino group, an ester group or
an amide group bondable to a polyester polymer is also preferred.
Examples of polymer alloys also include polyester/vinyl polymer alloys,
polyester/nylon alloys, polyester/polysulfone alloys, polyester/silicon polymer alloys,
and polymer alloys obtained by mixing two or more conventionally known polymers
10 such as polyester polymer, polycarbonate polymer, polyolefin polymer, vinyl
polymer, nylon polymer, polysulfone polymer and silicon polymer in any proportion
according to any method of combining on the support. Herein, using a polymer
containing a hydroxyl group, a carboxyl group, an epoxy group, an amino group, an
ester group or an amide group chemically bondable to the above component is also
15 preferred. The components may have a linear, branched or grafted skeleton.
[0113]
Referring now to another application of the present invention, a polymer
excellent in melt flowability having a molecular weight distribution represented by
Mw/Mn of 2.0 or higher can also be produced by simultaneous polymerization of
20 polymers having a different polymerization degree at two or more areas of the
support in the polymerization reactor. The molecular weight distribution can be
adjusted as desired based on the kind, the polymerization degree and the amount of
prepolymers introduced into each area of the perforated plate. The molecular
weight distribution is more preferably 2.5 or higher, further preferably 3.0 or higher,
25 particularly preferably 3.5 or higher, and most preferably 4.0 or higher in order to
improve the melt flowability. A higher molecular weight distribution not only
improves melt flowability but also facilitates crystallization of polymer, for example,

-47-
and so producing a polymer having a higher molecular weight distribution by
combining a component having a branched or grafted skeleton in addition to a linear
skeleton is also preferred.
(typical embodiment of production method and apparatus of the present invention)
5 Preferred embodiments of the present invention will now be described taking
polymerization of PET as an example with reference to the figures.
[0114]
Figure 1 and the figures that follow illustrate embodiments of preferred
combination for accomplishing the method of the present invention, but the present
10 invention is not limited to these.
[0115]
Referring to Figure 1, a prepolymer of a polycondensation polymer such as
PET is fed to the polymerization reactor 10 through a feed opening 2 by a transfer
pump (A) and/or a transfer pump (B) 1, passes through holes in area A and/or area B
15 of a perforated plate 3, introduced into the polymerization reactor and falls along a
support 5. At this stage, a prepolymer of a different polymer and/or a polymer
modifier may be fed instead of the prepolymer of PET by the transfer pump (A) or
transfer pump (B) 1.
[0116]
20 The inside of the polymerization reactor is controlled to a pre-determined
reduced pressure and by-product ethylene glycol or inert gas such as nitrogen fed
through an inert gas feed opening 6 as required is discharged from an evacuation port
7. The produced polymer is discharged from an outlet 9 using a discharge pump 8.
[0117]
25 Upon polymerization with allowing a prepolymer to fall along a support,
streams of prepolymer supplied from each area may or may not be combined on the

-48-
support by changing the position of the areas of the perforated plate and the support,
and whether combined or not is selected depending on the purpose.
[0118]
After falling down to the bottom of the polymerization reactor, the produced
5 polymer is discharged from an outlet using a discharge pump. Upon this, it is
preferred that the amount of the produced polymer accumulated at the bottom of the
polymerization reactor is kept as small and constant as possible. Referring to a
method of controlling the accumulated amount, the amount can be controlled by
adjusting the flow rate of the transfer pump and the discharge pump while observing
10 the accumulated amount through an observation hole 4 or monitoring the
accumulated amount using an electrostatic type level meter.
[0119]
The transfer pump, the polymerization reactor main body, the discharge pump
and the transfer pipe are heated and kept warm by a heater or a jacket.
15 [0120]
The polymerization reactor used in the present invention may also have an
agitator or the like at the bottom of the polymerization reactor, but such agitator is
not always required. It is therefore possible to omit the rotary driving part of the
main body of the polymerization reactor and polymerization can be performed under
20 an excellent sealed condition even in a high vacuum. Because the rotary driving
part of the discharge pump is covered with the resin discharged, the polymerization
reactor of the present invention has much better sealing properties than a
polymerization reactor with a rotary driving part attached to the main body.
[0121]
25 The method of the present invention may be carried out with one
polymerization reactor, or with two or more reactors.
[0122]

-49-
In the present invention, the process for increasing the molecular weight of a
prepolymer of a polycondensation polymer such as PET to the intended molecular
weight of the high polymerization degree polycondensation polymer such as PET
may be performed according to a method of polymerization in which whole
5 prepolymer is allowed to fall along a support through holes of a perforated plate.
The process can be performed in combination with another polymerization method,
e.g., an agitation vessel polymerization reactor or a horizontal agitating
polymerization reactor.
[0123]
10 Examples of horizontal agitating polymerization reactors include a screw type,
an independent blade type, an uniaxial type or a biaxial type polymerization reactor
described, for example, in Chapter 4, "Research Report of Research Group on
Reaction Engineering: Reactive Processing Part 2" (Society of Polymer Science,
1992).
15 [0124]
As the agitation vessel polymerization reactor, any agitating vessels described
in Chapter 11 of Handbook of Chemical Equipment (edited by Society of Chemical
Engineers, Japan; 1989) can be used, for example.
[0125]
20 The shape of the vessel is not particularly limited and a vertical or horizontal
cylinder is usually used. The shape of the agitation blade is not particularly limited
either, and a paddle type blade, an anchor type blade, a turbine type blade, a screw
type blade, a ribbon type blade or a double blade may be used.
[0126]
25 The process of producing a prepolymer from starting materials may be
batchwise or continuous. When the process is performed batchwise, all the starting
materials and the reactants are fed to the reactor and allowed to react for a

-50-
pre-determined time, and all the reactants are transferred to the subsequent reactor.
On the other hand, when the process is continuously performed, starting materials
and reactants are continuously fed to each reactor and the reactants are continuously
discharged. In the case of mass production of polycondensation prepolymer of PET
5 and molded articles thereof having uniform quality, the process is preferably
performed batchwise.
[0127]
Figure 2-1 and Figure 2-2 illustrate a specific example of a method of
supplying various prepolymers and polymer modifiers to each area of the perforated
10 plate 3.
"[0128]
Figure 2-1 shows an example of supplying one prepolymer through each area
of a perforated plate. By individually setting the supply amount of prepolymer per
area (A to D) of the perforated plate 3 with respective transfer pumps (A to D) 1, the
15 polymerization velocity and the polymerization degree of the polymer can be
accurately controlled and a broader molecular weight distribution can be obtained,
whereby the melt flowability is further improved. In addition, by supplying the
prepolymer from a certain area alone, the polymerization velocity can be changed
without greatly changing the polymerization condition of the polymerization reactor
20 of the present invention.
[0129]
Figure 2-2 shows an example of supplying one or plural kinds of prepolymers
and/or polymer modifiers through each area of a perforated plate. By individually
setting the supply amount of prepolymer per area (A to D) of the perforated plate 3
25 with the respective transfer pumps (A to D) 1 as shown in the figure, a copolymer
having any composition or a polymer whose properties are improved by adding a
modifier in any composition can be produced.

-51-
[0130]
In both examples, the supply amount in each area (A to D) of the perforated
plate 3 can be changed as desired during polymerization, and thus various high
quality polymers can be produced in small quantities at low cost.
5 [0131]
Figure 3 shows a specific example of a polymerization reactor for
accomplishing the method of the present invention using an inert gas absorption
apparatus. A prepolymer of PET is fed to an inert gas absorption apparatus N10
through a feed opening N2 via a transfer pump Nl, passes through a perforated plate
10 N3 to be introduced into the inert gas absorption apparatus and falls along a support
N5. The inside of the inert gas absorption apparatus is controlled to a
pre-determined reduced pressure by evacuation port N7, and the prepolymer absorbs
inert gas such as nitrogen introduced from an inert gas introducing port N6 while
falling. The prepolymer is then fed to a polymerization reactor 10 through a feed
15 opening 2 via a drainage/transfer pump N8, introduced into the polymerization
reactor through area A of a perforated plate 3 and allowed to fall along a support 5.
[0132]
In these steps, a prepolymer of the same or a different polymer and/or a
polymer modifier may be simultaneously fed through area B of the perforated plate 3
20 via a transfer pump (B) 1. Alternatively, the transfer pump (B) 1 may be installed
to the inert gas feeding apparatus N10, and an area A and an area B may be provided
in the perforated plate N3 of the inert gas supply apparatus N10, not in the perforated
plate 3 of the polymerization reactor 10, so as to supply the prepolymer of the same
or a different polymer and/or a polymer modifier to the area B of the perforated plate
25 N3.
[0133]

-52-
The inside of the polymerization reactor is controlled to a pre-determined
reduced pressure and by-product ethylene glycol is discharged from an evacuation
port 7. The produced polymer is discharged from an outlet 9 using a discharge
pump 8. The transfer pump, the inert gas absorption apparatus main body, the
5 polymerization reactor main body, the discharge pump, the transfer pipe, the
diversion switching valve, the pressure control valve, the back pressure control valve,
the molding machine and the pelletizer are heated and kept warm by a heater or a
jacket.
[0134]
10 Figure 4 is a schematic view illustrating a specific example of an apparatus
for accomplishing the polymerization method and the molding method employed in
the present invention.
[0135]
As described in Figure 1, a prepolymer of a polycondensation polymer such
15 as PET is fed to a polymerization reactor through a feed opening 2 by a transfer
pump (A) and/or a transfer pump (B) 1, introduced into the polymerization reactor
through holes in area A and/or area B of a perforated plate 3, and falls along a
support 5. At this stage, a prepolymer of a different polymer and/or a polymer
modifier may be fed instead of the prepolymer of PET by the transfer pump (A) or
20 transfer pump (B) 1.
[0136]
The inside of the polymerization reactor is controlled to a pre-determined
reduced pressure and by-product ethylene glycol or inert gas such as nitrogen fed
through an inert gas feed opening 6 as required is discharged from an evacuation port
25 7. The produced polymer is continuously discharged using a discharge pump 8 and
supplied to molding machines A to C (12 to 14) through a transfer pipe and
distributor II. Herein, the distributor is a unit for distributing molten polymer to a

-53-
plurality of pipes, which may be equipped with a switching valve so as to control the
flow of the molten polymer more accurately. One or more molding machines may
be connected (3 machines in this figure). The transfer pump, the polymerization
reactor main body, the discharge pump, the transfer pipe, the distributor and the
5 molding machine are heated and kept warm by a heater or a jacket.
[0137]
The molding machine in the present invention refers to an apparatus for
forming molten resin into a specific shape, and examples thereof include extrusion
molding machines, injection molding machines and blow, molding machines.
10 Molded articles molded using a molding machine include bottles, preforms of bottles,
films, sheets, tubes, bars, fibers and injection molded articles of various shapes. Of
these articles, the present invention is suitable for producing preforms of beverage
bottles. It is strongly desired that beverage bottles have excellent strength and
transparency, contain a reduced amount of low molecular weight volatile impurities
15 which affect the taste and the odor of the content, typically aldehyde in the case of
PET, and can be produced at low cost with high productivity.
[0138]
Figure 5 is a schematic view illustrating a specific example of a
polymerization reactor of the present invention having two or more outlets for
20 discharging a produced polymer.
[0139]
As described in Figure 1, a prepolymer of a polycondensation polymer such
as PET is fed to a polymerization reactor through a feed opening 2 by a transfer
pump (A) and/or a transfer pump (B) 1, introduced into the polymerization reactor
25 through holes in area A and/or area B of a perforated plate 3, and falls along a
support 5. At this stage, a prepolymer of a different polymer and/or a polymer

-54-
modifier may be fed instead of the prepolymer of PET by the transfer pump (A) or
transfer pump (B) 1.
[0140]
The inside of the polymerization reactor is controlled to a pre-determined
5 reduced pressure and by-product ethylene glycol or inert gas such as nitrogen fed
through an inert gas feed opening 6 as required is discharged from an evacuation port
7. The produced polymer is discharged through two separated areas from outlets (I
and II) 9 using discharge pumps (I and II) 8.
[0141]
10 Upon polymerization with allowing a prepolymer to fall along a support,
streams of prepolymer supplied from each area of the perforated plate may or may
not be combined on the support by changing the position of the areas of the
perforated plate and the support, and whether combined or not is selected depending
on the purpose. Further, polymers produced by allowing prepolymers to fall so as
15 not to be combined may be discharged from different outlet areas or the same outlet
area, or polymers produced by allowing prepolymers to fall so as to be combined
may be discharged from an identical outlet area or plural outlet areas, and how to
discharge is selected depending on the purpose.
[0142]
20 After falling down to the bottom of the polymerization reactor, the produced
polymer is discharged from an outlet using a discharge pump. Upon this, it is
preferred that the amount of the produced polymer accumulated at the bottom of the
polymerization reactor is kept as small and constant as possible. Referring to a
method of controlling the accumulated amount, the amount can be controlled by
25 adjusting the flow rate of the transfer pump and the discharge pump while observing
the accumulated amount through an observation hole 4 or monitoring the
accumulated amount using an electrostatic type level meter.

-55-
[0143]
The transfer pump, the polymerization reactor main body, the discharge pump
and the transfer pipe are heated and kept warm by a heater or a jacket.
[0144]
5 The polymerization reactor used in the present invention may also have an
agitator or the like at the bottom of the polymerization reactor, but such agitator is
not always required. It is therefore possible to omit the rotary driving part of the
main body of the polymerization reactor and polymerization can be performed under
an excellent sealed condition even in a high vacuum. Because the rotary driving
10 part of the discharge pump is covered with the resin discharged, the polymerization
reactor of the present invention has much better sealing properties than a
polymerization reactor with a rotary driving part attached to the main body. The
method of the present invention may be carried out with one polymerization reactor,
or with two or more reactors.
15 [0145]
In the present invention, the process for increasing the molecular weight of a
prepolymer of a polycondensation polymer such as PET to the intended molecular
weight of the high polymerization degree polycondensation polymer such as PET
may be performed according to a method of polymerization in which whole
20 prepolymer is allowed to fall along a support through holes of a perforated plate.
The process is preferably performed in combination with another polymerization
method, e.g., an agitation vessel polymerization reactor or a horizontal agitating
polymerization reactor.
[1046]
25 Figure 6-1 and Figure 6-2 show examples of a method of supplying various
prepolymers and polymer modifiers to each area of perforated plate 3 and a method

-56-
of discharging a polymer produced by allowing prepolymers to fall along the support
from two or more outlets.
[0147]
Figure 6-1 shows an example of supplying one prepolymer through each area
5 of a perforated plate. By individually setting the supply amount of prepolymer per
area (A to D) of the perforated plate 3 with respective transfer pumps (A to D) 1, the
polymerization velocity and the polymerization degree of the polymer can be
accurately controlled and a broader molecular weight distribution can be obtained,
whereby the melt flowability is further improved. In addition, by supplying the
10 prepolymer from a certain area alone, the polymerization velocity can be changed
without greatly changing the polymerization condition of the polymerization reactor
of the present invention.
[0148]
Prepolymers supplied from each area of the perforated plate 3 falling along
15 the support may or may not be combined with each other depending on the position
of the support. For example, prepolymers supplied from area A and area B of the
perforated plate fall along a support a and a support b without being combined with
each other, and individually discharged from outlet area I and area n. Prepolymers
supplied from area C and area D of the perforated plate are combined on the support
20 c, homogeneously mixed and polymerized while falling along the support c, and
distributed at outlet area HI and area IV and discharged.
[0149]
Figure 6-2 shows an example of supplying one or plural kinds of prepolymers
and/or polymer modifiers through each area of a perforated plate. By individually
25 setting the supply amount of prepolymer per area (A to D) of the perforated plate 3
with the respective transfer pumps (A to D) 1 as shown in the figure, a copolymer

-57-
having any composition or a polymer whose properties are improved by adding a
modifier in any composition can be produced.
[0150]
Prepolymers supplied from each area of the perforated plate falling along the
5 support may or may not be combined with each other depending on the position of
the support. For example, prepolymer A supplied from area A of the perforated
plate falls along a support a without being combined with other prepolymers and
discharged from outlet area I. On the other hand, part of prepolymer A is also
supplied from area B of the perforated plate, combined with prepolymer B or
10 polymer modifier supplied from area C of the perforated plate on the support b,
homogeneously mixed and polymerized while falling along the support b, and
discharged from outlet area II. Also, prepolymer C supplied from area D is not
combined with other prepolymers, polymerized while falling along the support c and
discharged from outlet area HI.
15 [0151]
In addition to the configurations shown in the figures, areas of the perforated
plate, supports and areas of the outlets may be positioned as desired according to the
purpose, and the apparatus can be designed so as to discharge the desired polymer
from each outlet in the desired production amount.
20 [0152]
In both examples, the supply amount in each area (A to D) of the perforated
plate can be changed as desired during polymerization, and thus various high quality
polymers can be produced in small quantities at low cost.
[0153]
25 Figure 7 shows a specific example of a polymerization reactor for practicing
the method of the present invention using an inert gas absorption apparatus. A
prepolymer of a polycondensation polymer such as PET is fed to an inert gas

-58-
absorption apparatus N10 through a feed opening N2 via a transfer pump Nl, passes
through the perforated plate N3 to be introduced into the inert gas absorption
apparatus N10 and falls along a support N5. The inside of the inert gas absorption
apparatus is controlled to a pre-determined reduced pressure by evacuation port N7,
5 and the prepolymer absorbs inert gas such as nitrogen introduced from an inert gas
introducing port N6 while falling. The prepolymer is then fed to a polymerization
reactor 10 through a feed opening 2 via a drainage/transfer pump N8, introduced into
the polymerization reactor through area A of a perforated plate 3 and allowed to fall
along a support 5.
10 [0154]
In these steps, a prepolymer of the same or a different polymer and/or a
polymer modifier may be simultaneously fed through area B of the perforated plate 3
via the transfer pump (B) 1. Alternatively, the transfer pump (B) 1 may be installed
to the inert gas absorption apparatus N10, and an area A and an area B may be
15 provided in the perforated plate N3 of the inert gas supply apparatus N10, not in the
perforated plate 3 of the polymerization reactor 10, so as to supply the prepolymer of
the same or a different polymer and/or a polymer modifier to the area B of the
perforated plate-N3.
[0155]
20 The inside of the polymerization reactor is controlled to a pre-determined
reduced pressure and by-product ethylene glycol or the like is discharged from an
evacuation port 7. The produced polymer is discharged through two separated areas
from outlets (I and II) 9 using discharge pumps (I and IT) 8. The transfer pump, the
inert gas absorption apparatus main body, the polymerization reactor main body, the
25 discharge pump, the transfer pipe, the diversion switching valve, the pressure control
valve, the back pressure control valve, the molding machine and the pelletizer are
heated and kept warm by a heater or a jacket.

-59-
[0156]
Figure 8 is a schematic view illustrating an example of an apparatus for
practicing the polymerization method and the molding method employed in the
present invention. As described in Figure 1, a prepolymer of a polycondensation
5 polymer such as PET is fed to a polymerization reactor through a feed opening 2 by a
transfer pump (A) and/or a transfer pump (B) 1, introduced into the polymerization
reactor through holes in area A and/or area B of a perforated plate 3, and falls along a
support 5. At this stage, a prepolymer of a different polymer and/or a polymer
modifier may be fed instead of the prepolymer of PET by the transfer pump (A) or
10 transfer pump (B) 1.
[0157]
The inside of the polymerization reactor is controlled to a pre-determined
reduced pressure and by-product ethylene glycol or inert gas such as nitrogen fed
through an inert gas feed opening 6 as required is discharged from an evacuation port
15 7. The produced polymer is continuously discharged through two separated areas
from outlets (I and II) 9 using discharge pumps (I and II) 8 and supplied to molding
machines A to C (I and II) (12 to 14) through transfer pipes II and distributors (I and
II). One or more molding machines may be connected (3 machines in this figure).
The transfer pump, the polymerization reactor main body, the discharge pump, the
20 transfer pipe, the distributor and the molding machine are heated and kept warm by a
heater or a jacket.
Examples
[0158]
25 The present invention is described by means of Examples.
[0159]

-60-
The following methods were used for measuring main measurement values in
Examples.
(1) intrinsic viscosity [η]
The intrinsic viscosity [Η] was calculated by extrapolating the ratio r|sp/C of a
5 specific viscosity r|sp measured in o-chlorophenol at 35°C by an Ostwald viscometer
to a concentration C (g/100 ml) to zero concentration, based on the following
formula.
[0160]
[Equation 1]

In the case of PET resin, the polymerization degree of the prepolymer can
also be evaluated based on the above-described commonly used intrinsic viscosity
[rj] instead of melt viscosity.
[0161]
15 For example, a prepolymer of PET resin having an intrinsic viscosity [η] of
0.15 dl/g has a melt viscosity at 260°C of about 60 poise, and a prepolymer of PET
resin having an intrinsic viscosity [r|] of 1.2 dl/g has a melt viscosity at 260°C of
about 100000 poise.
(2) crystalline melting point
20 The crystalline melting point was measured using Pyris 1 DSC
(input-compensating differential scanning calorimeter) manufactured by Perkin
Elmer, Inc. under the following conditions. The peak value at an endothermic peak
derived from melting of crystal was defined as a crystalline melting point. The
peak value was determined using attached analysis software.
25 Measurement temperature: 0 to 300°C
Temperature rising rate: 10°C/min

-61-
[0162]
(3) carboxyl group content at polymer terminal
1 g of sample was dissolved in 25 ml of benzyl alcohol and 25 ml of
chloroform was then added thereto. The resulting solution was subjected to titration
5 using a 1/50N potassium hydroxide benzyl alcohol solution. The carboxyl group
content at polymer terminal was calculated from the obtained titration value VA (ml)
and a blank value V0 obtained in the absence of PET, according to the following
formula.
carboxyl group content at polymer terminal (meq/kg)=(VA-V0)x20
10 [0163]
(4) hue of resin (L value, b value)
1.5 g of a sample was dissolved in 10 g of l,l,l,3,3,3-hexafluoro-2-propanol,
analyzed by an optical transmission method using UV-2500PC (ultraviolet-visible
spectrophotometer) manufactured by Shimadzu Corporation, and evaluated by the
15 method in accordance with JIS Z8730 using attached analysis software.
(5) content of impurities
A sample was finely cut and subjected to freeze pulverization using Freezer
mill 6700 (freeze pulverization machine) manufactured by SPEX Industries Inc.
under cooling with liquid nitrogen for 3 to 10 minutes to give powder having a
20 particle size of 850 to 1000 μm. 1 g of the powder and 2 ml of water were put in a
• glass ampoule, the inside air was replaced by nitrogen, and the ampoule was sealed
and heated at 130°C for 90 minutes to extract impurities such as acetaldehyde.
After cooling, the ampoule was opened and the content of impurities was analyzed
using GC-14B (gas chromatograph) manufactured by Shimadzu Corporation under
25 the following conditions.
column: VOCOL (60 m x 0.25 mm) x film thickness 1.5 μm)

-62-
temperature: maintained at 35°C for 10 minutes, then heated to 100°C at 5°C/minute,
then heated from 100 to 220°C at 20°C/minute
temperature of injection port: 220°C
injection method: split method (split ratio=l:30), injected in an amount of 1.5 pi
5 measurement method: FID method
[0164]
(6) molecular weight distribution
A sample was dissolved in an eluant, i.e., l,l,l,3,3,3-hexafluoro-2-propanol
(in which 5 mmol of trifluoroacetic acid sodium salt was dissolved) at a
10 concentration of 1.0 mg/ml. The resulting solution was analyzed using HLC-8020
GPC (gel permeation chromatograph) manufactured by TOSOH CORPORATION
under the following conditions and evaluated using attached analysis software.
column: HFIP-606M+HFIP-603 manufactured by Showa Denko K.K.
column temperature: 40°C
15 injection amount: 30 μl
measurement method: RI detector, converted to PMMA
Example 1
Using the apparatus shown in Figure 4, a prepolymer of PET resin having an
intrinsic viscosity [η] of 0.46 dl/g, a carboxyl group content at polymer terminal of
20 32 meq/kg and a crystalline melting point of 260°C was supplied to a polymerization
reactor 10 through a feed opening 2 by a transfer pump (A) 1, and the prepolymer
was discharged through holes in area A of a perforated plate 3 in a molten state at
265°C at a rate of 10 g/minute per hole. At the same time, a prepolymer obtained
by copolymerizing 4% by mole of cyclohexane dimethanol with PET having an
25 intrinsic viscosity [η] of 0.28 dl/g, a carboxyl group content at polymer terminal of
30 meq/kg and a crystalline melting point of 240°C was supplied to the
polymerization reactor 10 through the feed opening 2 by a transfer pump (B) 1, and

-63-
the prepolymer was discharged through holes in area B of the perforated plate 3 in a
molten state at 265°C at a rate of 10 g/minute per hole.
[0165]
These supplied prepolymers were polymerized under a reduced pressure of 65
5 Pa while being allowed to fall along the support at an ambient temperature the same
as the discharge temperature, and discharged from the polymerization reactor using a
discharge pump 8. The produced polymer was then transferred through a transfer
pipe and distributor II, and preform molding and molding of hollow articles were
continuously performed at a molding temperature of 280°C using a twin-screw
10 stretch-blow molding machine (SBIII-100H-15 manufacture by Aoki Technical
Laboratory Inc.) as a molding machine A (12). Using an injection molding machine
(MJEC-10 manufactured by MODERN MACHINERY CO. LTD.) as a molding
machine B (13), molding was performed at 280°C to prepare a dumbbell specimen.
As a molding machine C (14), a pelletizer C was set.
15 [0166]
Referring to the perforated plate, one having a thickness of 50 mm and 14
holes 1 mm in diameter linearly aligned in two parallel rows in a distance of 70 mm,
with 7 holes in each row at an interval of 10 mm was used. The holes belonging to
area A and the holes belonging to area B were alternately aligned. As the support, a
20 lattice form support composed of a wire 2 mm in diameter and 8 m in length each
attached immediately below the holes hanging vertically therefrom and wires 2 mm
in diameter and 100 mm in length attached perpendicularly to the above wire at an
interval of 100 mm was used. The material of the support was stainless steel.
[0167]
25 Referring to prepolymers, those produced by adding 0.04% by weight of
diantimony trioxide and trimethyl phosphate in a proportion of 100 ppm based on the
weight ratio of phosphorus were used. The residence time in the polymerization

-64-
reactor was 70 minutes. The residence time means a value obtained by dividing the
amount of polymer present in the polymerization reactor by the amount supplied.
During the polymerization, intensive foaming of prepolymer discharged through the
perforated plate and the consequent contamination of the nozzle surface and walls
5 hardly occurred, while the falling resin contained a large amount of bubbles and
rolled down along the support in the form of bubble balls.
[0168]
As described above, both prepolymers were first discharged at a rate of 10
g/minute per hole and polymerized, and the polymerized resins were fed to molding
10 machines A to C to produce molded articles. Then, polymerization was performed
by discharging prepolymers at a supply rate in area A of 15 g/minute per hole and at
a supply rate in area B of 5 g/minute per hole, and the polymerized resins were fed to
molding machines A to C to produce molded articles. Further, polymerization was
performed by discharging prepolymers at a supply rate in area A of 5 g/minute per
15 hole and at a supply rate in area B of 15 g/minute per hole, and the polymerized
resins were fed to molding machines A to C to produce molded articles. The
molded articles produced under these three conditions were subjected to evaluation
of the crystalline melting point, and as a result, each article had a single melting peak,
meaning that uniform and high quality copolymers were obtained. Properties of the
20 obtained molded articles and the resin pellets are shown in Table 1.
Example 2
Using the apparatus shown in Figure 1, a prepolymer of PET resin having an
intrinsic viscosity [r)] of 0.30 dl/g, a carboxyl group content at polymer terminal of
28 meq/kg and a crystalline melting point of 255°C was supplied to a polymerization
25 reactor 10 through a feed opening 2 by a transfer pump (A) 1, and the prepolymer
was discharged through holes in area A of a perforated plate 3 in a molten state at
255°C at a rate of 10 g/minute per hole. At the same time, polytetramethylene

-65-
glycol having an average molecular weight of 2000 was supplied to the
polymerization reactor 10 through the feed opening 2 by a transfer pump (B) 1 and
discharged through holes in area B of the perforated plate 3 in a molten state at
255°C at a rate of 10 g/minute per hole.
5 [0169]
These supplied materials were polymerized under a reduced pressure of 65 Pa
while being allowed to fall along the support at an ambient temperature the same as
the discharge temperature and discharged from an outlet 9 via a discharge pump 8.
Then, using a pelletizer, pellets of PET resin copolymerized with polytetramethylene
10 glycol were obtained.
[0170]
Referring to the perforated plate, one having a thickness of 50 mm and 14
holes 1 mm in diameter linearly aligned in two parallel rows in a distance of 70 mm,
with 7 holes in each row at an interval of 10 mm was used. The holes belonging to
15 ' area A and the holes belonging to area B were alternately aligned. As the support, a
lattice form support composed of a wire 2 mm in diameter and 8 m in length each
attached immediately below the holes hanging vertically therefrom and wires 2 mm
in diameter and 100 mm in length attached perpendicularly to the above wire at an
interval of 100 mm was used. The material of the support was stainless steel.
20 [0171]
Referring to prepolymers, those produced by adding 0.04% by weight of
diantimony trioxide and trimethyl phosphate in a proportion of 100 ppm based on the
weight ratio of phosphorus were used. The residence time in the polymerization
reactor was 60 minutes. The residence time means a value obtained by dividing the
25 amount of polymer present in the polymerization reactor by the amount supplied.
During the polymerization, intensive foaming of prepolymer discharged through the
perforated plate and the consequent contamination of the nozzle surface and walls

-66-
hardly occurred, while the falling resin contained a large amount of bubbles and
rolled down along the support in the form of bubble balls.
The obtained polymer was uniform and high quality copolymerized PET resin
pellet having rubber elasticity. Properties of the obtained resin are shown in Table
5 2.
Comparative Example 1
Using a conventional agitation vessel type melt polymerization reactor for
PET resin, polymerization of PET resin was performed batchwise at a
polymerization temperature of 285°C in a vacuum of 100 Pa. When the intrinsic
10 viscosity [r|] reached 0.30 dl/g, polytetramethylene glycol was added thereto in the
same amount as PET resin, and polymerization was continued under conditions of a
polymerization temperature of 285°C and a vacuum of 100 Pa for 60 minutes to
produce copolymerized PET resin having an intrinsic viscosity [n] of 0.65 dl/g.
The obtained polymer was yellow and smelled like decomposed polytetramethylene
15 glycol. Properties of the obtained resin are shown in Table 2.
Example 3
Using the apparatus shown in Figure 8, a prepolymer of PET resin having an
intrinsic viscosity [r|] of 0.43 dl/g, a carboxyl group content at polymer terminal of
33 meq/kg and a crystalline melting point of 260°C was supplied to a polymerization
20 reactor 10 through a feed opening 2 by a transfer pump (A) 1, and the prepolymer
was discharged through holes in area A of a perforated plate 3 in a molten state at
265°C at a rate of 10 g/minute per hole. Further, the same prepolymer of PET resin
was supplied to the polymerization reactor 10 through the feed opening 2 by a
transfer pump (B) 1 and discharged through holes in area B of the perforated plate 3
25 in a molten state at 265°C at a rate of 10 g/minute per hole.
[0172]

-67-
Referring to the perforated plate 3, one having a thickness of 50 mm and 20
holes 1 mm in diameter linearly aligned in two parallel rows in a distance of 70 mm,
with 10 holes in each row at an interval of 10 mm was used. The holes belonging to
area A and the holes belonging to area B each correspond to the row of 10 holes
5 linearly aligned at an interval of 10 mm. As the support 5, two lattice form supports
(supports a and b) composed of a wire 2 mm in diameter and 8 m in length each
attached immediately below the holes hanging vertically therefrom and wires 2 mm
in diameter and 120 mm in length attached perpendicularly to the above wire at an
interval of 100 mm were used. The prepolymer supplied from area A of the
10 perforated plate 3 was allowed to fall along the support a and the prepolymer
supplied from area B of the perforated plate 3 was allowed to fall along the support b.
The supports a and b were positioned so that streams of the prepolymers were not
combined. The material of the supports was stainless steel.
[0173]
15 Two outlets 9 were provided and the polymer that has fallen along the support
a was discharged from area I of the outlets, and the polymer that has fallen along the
support b was discharged from area II of the outlets so as not to be combined with
each other.
[0174]
20 Polymerization was performed under a reduced pressure of 65 Pa while
allowing the prepolymer to fall along the support at an ambient temperature the same
as the discharge temperature, and the resultant was discharged from the
polymerization reactor 10 using discharge pumps (I and II) 8. The produced
polymers were then transferred through transfer pipes and distributors (I and II) II,
25 and preform molding and molding of hollow articles were continuously performed at
a molding temperature of 280°C using a twin-screw stretch-blow molding machine
(SBDI-100H-15 manufacture by Aoki Technical Laboratory Inc.) as a molding

-68-
machine A (I). Using an injection molding machine (MJEC-10 manufactured by
MODERN MACHINERY CO., LTD.) as a molding machine A (II), molding was
performed at 280°C to prepare a dumbbell specimen. As molding machines B (I
and II), pelletizers (I and II) of the same type were set. Molding machines C (I and
5 II) were not connected.
[0175]
Referring to prepolymer, one produced by adding 0.04% by weight of
diantimony trioxide and trimethyl phosphate in a proportion of 100 ppm based on the
weight ratio of phosphorus was used. The residence time in the polymerization
10 reactor was 70 minutes. The residence time means a value obtained by dividing the
amount of polymer present in the polymerization reactor by the amount supplied.
During the polymerization, intensive foaming of prepolymer discharged through the
perforated plate and the consequent contamination of the nozzle surface and walls
hardly occurred, while the falling resin contained a large amount of bubbles and
15 rolled down along the support in the form of bubble balls.
[0176]
As described above, the prepolymer was first supplied from areas A and B of
the perforated plate at 10 g/minute per hole, and polymerization and molding were
performed to produce molded articles and pellets. Their properties were evaluated
20 and it has been found that pellets produced using pelletizers I and II had the same
quality.
Then, the prepolymer was supplied from area A of the perforated plate at 10
g/minute per hole and from area B of the perforated plate at 8 g/minute per hole, and
polymerization and molding were performed to produce molded articles and pellets.
25 Their properties were evaluated and it has been found that molded articles and pellets
having a different polymerization degree based on the supply rate of the prepolymer

-69-
were simultaneously but separately obtained. Properties of the obtained molded
articles and resin pellets are shown in Table 3.
Example 4
Using the apparatus shown in Figure 8, which is the same as the apparatus
5 used in Example 3, a prepolymer of PET resin having an intrinsic viscosity [r|] of
0.43 dl/g, a carboxyl group content at polymer terminal of 33 meq/kg and a
crystalline melting point of 260°C was supplied to a polymerization reactor 10
through a feed opening 2 by a transfer pump (A) 1, and the prepolymer was
discharged through holes in area A of a perforated plate 3 in a molten state at 265 °C
10 at a rate of 10 g/minute per hole. At the same time, a prepolymer obtained by
copolymerizing 2% by mole of cyclohexane dimethanol with PET having an intrinsic
viscosity [η] of 0.45 dl/g, a carboxyl group content at polymer terminal of 30 meq/kg
and a crystalline melting point of 248 °C was supplied to the polymerization reactor
10 through the feed opening 2 via a transfer pump (B) 1 and discharged through
15 holes in area B of the perforated plate 3 in a molten state at 265 °C at a rate of 10
g/minute per hole.
[0177]
Polymerization was performed under a reduced pressure of 65 Pa while
allowing the prepolymers to fall along the support at an ambient temperature the
20 same as the discharge temperature. Referring to prepolymers, those produced by
adding 0.04% by weight of diantimony trioxide and trimethyl phosphate in a
proportion of 100 ppm based on the weight ratio of phosphorus were used. The
residence time in the polymerization reactor was 65 minutes. The residence time
means a value obtained by dividing the amount of polymer present in the
25 polymerization reactor by the amount supplied. During the polymerization,
intensive foaming of prepolymer discharged through the perforated plate and the
consequent contamination of the nozzle surface and walls hardly occurred, while the

-70-
falling resin contained a large amount of bubbles and rolled down along the support
in the form of bubble balls.
[0178]
As described above, each prepolymer was supplied from area A or B of the
5 perforated plate at 10 g/minute per hole, and polymerization and molding were
performed to produce molded articles and pellets. Their properties were evaluated
and it has been found that the polymer obtained from the discharge pump I side was
PET having a crystalline melting point of 260°C and the polymer obtained from the
discharge pump II side was a copolymer in which 2% by mole of cyclohexane
10 dimethanol was copolymerized with PET having a crystalline melting point of 248 °C.
As herein described, different molded articles and pellets were obtained
simultaneously but separately. Properties of the obtained molded articles and resin
pellets are shown in Table 4.
Example 5
15 Using the apparatus shown in Figure 5, a prepolymer of PET resin having an
intrinsic viscosity [rj] of 0.32 dl/g, a carboxyl group content at polymer terminal of
29 meq/kg and a crystalline melting point of 255°C was supplied to a polymerization
reactor 10 through a feed opening 2 by a transfer pump (A) 1, and the prepolymer
was discharged through holes in area A of a perforated plate 3 in a molten state at
20 255 °C at a rate of 10 g/minute per hole. At the same time, polytetramethylene
glycol having an average molecular weight of 2000 was supplied to the
polymerization reactor 10 through the feed opening 2 via a transfer pump (B) 1 and
discharged through holes in area B of the perforated plate 3 in a molten state at
255°C at a rate of 10 g/minute per hole.
25 [0179]
Referring to the perforated plate, one having a thickness of 50 mm and 14
holes 1 mm in diameter linearly aligned in two parallel rows in a distance of 70 mm,

-71-
with 7 holes in each row at an interval of 10 mm was used. The holes belonging to
area A and the holes belonging to area B were alternately aligned. Specifically, one
row has a line of (ABABABA), which is referred to as row a, and the other row has a
line of (BABABAB), which is referred to as row b.
5 [0180]
As the support, two lattice form supports (supports a and b) composed of a
wire 2 mm in diameter and 8 m in length each attached immediately below the holes
hanging vertically therefrom and wires 2 mm in diameter and 100 mm in length
attached perpendicularly to the above wire at an interval of 100 mm were used. The
10 prepolymer and the polytetramethylene glycol supplied through the row a of the
perforated plate was allowed to fall along the support a and the prepolymer and the
polytetramethylene glycol supplied through the row b of the perforated plate was
allowed to fall along the support b. The supports a and b were positioned so that
streams of the prepolymers were not combined. The material of the supports was
15 stainless steel.
[0181]
Two outlets 9 were provided and the polymer that has fallen along the support
a was discharged from area I of the outlets, and the polymer that has fallen along the
support b was discharged from area II of the outlets so as not to be combined with
20 each other.
[0182]
Polymerization was performed under a reduced pressure of 65 Pa while
allowing the prepolymer to fall along the support at an ambient temperature the same
as the discharge temperature, and the produced polymers were discharged from the
25 polymerization reactor by discharge pumps (I and II) 8 and pelletized using
pelletizers I and II of the same type.
[0183]

-72-
Referring to prepolymer, one produced by adding 0.04% by weight of
diantimony trioxide and dimethyl phosphate in a proportion of 100 ppm based on the
weight ratio of phosphorus was used. The residence time in the polymerization
reactor was 60 minutes. The residence time means a value obtained by dividing the
5 amount of polymer present in the polymerization reactor by the amount supplied.
During the polymerization, intensive foaming of prepolymer discharged through the
perforated plate and the consequent contamination of the nozzle surface and walls
hardly occurred, while the falling resin contained a large amount of bubbles and
rolled down along the support in the form of bubble balls.
10 The polymers discharged from the discharge pumps I and II were uniform and
high quality copolymerized PET resin pellets having rubber elasticity and each
having a polytetramethylene glycol content of 42.9% by weight and 57.1% by weight.
Properties of the obtained resins are shown in Table 5.

-73-
[0184]
[Table 1]

Polymerization condition Molded article Shape Intrinsicviscosity Crystallinemelting point Molecular weightdistribution Hue Acetaldehydecontent
(amount dischargedthrough perforated plate) (dl/g) (°C) (Mw/Mn) (L value, b value) (ppm)
Area A =10 g/minute-hole Molded article A Hollowbody 0.76 248.0 2.0 99.6,0.16 6.3
Area B =10 g/minute-hole Molded article B Dumbbell 0.74 248.1 1.9 97.5, 0.21 9.4
Molded article C Pellet 0.76 248.0 2.0 99.7,0.13 5.3
Area A =15 g/minute-hole Molded article A Hollowbody 0.76 252.2 2.0 99.1,0.16 6.4
Area B =5 g/minute-hole Molded article B Dumbbell 0.74 252.2 2.0 96.6, 0.29 10.1
Molded article C Pellet 0.76 252.1 2.0 99.5,0.17 5.5
Area A =5 g/minute-hole Molded article A Hollowbody 0.77 243.4 1.9 99.4,0.15 5.3
Area B =15 g/minute-hole Molded article B Dumbbell 0.74 243.3 2.0 97.6, 0.26 9.1
Molded article C Pellet 0.76 243.3 2.0 99.1,0.18 4.5

-74-
[0185]
[Table 2]

Polymerizationcondition Intrinsic viscosity Crystallinemelting point Molecular weightdistribution Hue Acetaldehydecontent
(dl/g) (°C) (Mw/Mn) (L value, b value) (ppm)
Example 2 0.82 258.3 2.1 99.1,0.21 7.1
ComparativeExample 1 0.65 255.9 2.3 94.3,1.71 174

-75-
[0186]
[Table 3]

Polymerization condition Molded article Shape Intrinsicviscosity Crystallinemelting point Molecular weightdistribution Hue Acetaldehydecontent
(amount dischargedthrough perforated plate) (dl/g) (°C) (Mw/Mn) (L value, b value) (ppm)
Area A =10 g/minute-hole Molded article A(I) Hollowbody 0.74 260.1 2.0 99.6,0.16 7.7
Area B =10 g/minute-hole Pelletizer(I) Pellet 0.76 260.0 2.0 99.7,0.13 4.5
Molded article A(II) Dumbbell 0.72 260.0 2.0 99.5, 0.15 9.5
Pelletizer(H) Pellet 0.76 260.0 2.0 99.7,0.13 4.5
Area A =10 g/minute-hole Molded article A(I) Hollowbody 0.74 260.1 2.0 99.6,0.16 7.7
Area B =8 g/minute-hole Pelletizer(I) Pellet 0.76 260.0 2.0 99.7,0.13 4.5
Molded article A(II) Dumbbell 0.82 260.0 2.0 98.5,0.19 11.4
Pelletizer(H) Pellet 0.84 260.0 2.0 99.2,0.16 5.7

-76-
[0187]
[Table 4]

Polymerization condition Molded article Shape Intrinsicviscosity Crystallinemelting point Molecular weightdistribution Hue Acetaldehydecontent
(amount dischargedthrough perforated plate) (dl/g) (°C) (Mw/Mn) (L value, b value) (ppm)
Area A =10 g/minute-hole Molded article A(I) Hollowbody 0.75 260.1 2.0 99.6,0.16 7.4
Area B =10 g/minute-hole Pelletizer(I) Pellet 0.76 260.0 2.0 99.7,0.13 4.6
Molded article A(H) Dumbbell 0.79 248.1 1.9 99.5,0.15 8.3
Pelletizer(II) Pellet 0.80 248.0 2.0 99.7.0.13 4.4

-77-
[0188]
[Table 5]

Polymerization condition PTMGcontent Intrinsicviscosity Crystallinemelting point Molecular weightdistribution Hue Acetaldehydecontent
(wt%) (dl/g) (°C) (Mw/Mn) (L value, b value) (ppm)
Example 5 Pelletizer I 42.9 0.82 258.3 2.1 99.0, 0.19 6.9
Pelletizer II 57.1 0.93 258.1 2.1 99.2,0.15 7.1

-78-
Industrial Applicability
[0189]
The present invention aims at producing various high quality
polycondensation polymers having a high polymerization degree, not colored and in
5 which the content of impurities generated by thermal decomposition is small and
molded articles thereof by melt polycondensation at low cost. This technique is
applicable to production of a polymer whose properties are improved by
copolymerizing a different monomer or adding a different polymer or various
modifiers and suitable for producing a wide variety of products in small quantities.
10
Brief Description of the Drawings
[0190]
[Figure 1] A schematic view illustrating an example of a polymerization reactor used
in the present invention;
15 [Figure 2-1] A schematic view illustrating an example of a method of supplying a
prepolymer to a perforated plate employed in the present invention: (1) an example
of supplying one prepolymer through each area of a perforated plate;
[Figure 2-2] A schematic view illustrating an example of a method of supplying a
prepolymer to a perforated plate employed in the present invention: (2) an example
20 of supplying one or a plurality of prepolymers and/or polymer modifiers through
each area of a perforated plate;
[Figure 3] A schematic view of an inert gas absorption apparatus and a
polymerization reactor used in the present invention;
[Figure 4] A schematic view illustrating an example of a polymerization reactor and
25 a molding machine used in the present invention;
[Figure 5] A schematic view illustrating an example of a polymerization reactor used
in the present invention;

-79-
[Figure 6-1] A schematic view illustrating an example of a method of supplying a
prepolymer to a perforated plate, a method of polymerization and a method of
discharging a polymer employed in the present invention: (1) an example of
supplying one prepolymer through each area of a perforated plate;
5 [Figure 6-2] A schematic view illustrating an example of a method of supplying a
prepolymer to a perforated plate, a method of polymerization and a method of
discharging a polymer employed in the present invention: (2) an example of
supplying one or a plurality of prepolymers and/or polymer modifiers through each
area of a perforated plate;
10 [Figure 7] A schematic view of an inert gas absorption apparatus and a
polymerization reactor used in the present invention; and
[Figure 8] A schematic view illustrating an example of a polymerization reactor and
a molding machine used in the present invention.

15 Description of symbols
[0191]
1 transfer pump
2 feed opening
3 perforated plate
20 4 observation hole
5 support and falling polymer
6 inert gas introducing port
7 evacuation port
8 drainage pump
15 9 outlet
10 polymerization reactor
N1 transfer pump

N2 feed opening
N3 perforated plate
N5 support and falling polymer
N6 inert gas introducing port
5 N7 evacuation port
N8 drainage/transfer pump
N10 inert gas absorption apparatus
11 transfer pipe and distributor
12 molding machine A
10 13 molding machine B
14 molding machine C

-80-

-81-
CLAMS
1. A method for producing a polycondensation polymer, which comprises:
introducing a prepolymer of a polycondensation polymer into a polymerization
reactor through a feed opening in a molten state; discharging the introduced
5 prepolymer through holes of a perforated plate; and then polycondensing the
prepolymer under reduced pressure, while allowing the prepolymer to fall along a
support, wherein the perforated plate has two or more areas and polycondensation is
performed by introducing a prepolymer and/or a polymer modifier into each of the
areas and discharging the introduced prepolymer and/or polymer modifier through
10 holes of each of the areas.
2. The method for producing a polycondensation polymer according to claim 1,
wherein the polymerization reactor has two or more outlets for delivering a produced
polymer.
3. The method for producing a polycondensation polymer according to claim 1
15 or 2, wherein the support has two or more areas corresponding to each area of the
perforated plate of the polymerization reactor, or/and a polymer is delivered through
an outlet divided into two or more areas corresponding to each area of the perforated
plate or the support.
4. The method for producing a polycondensation polymer according to any one
20 of claims 1 to 3, wherein the prepolymer and/or the polymer modifier are reacted
with a molecular weight modifier at a step prior to introducing the prepolymer and/or
the polymer modifier into the polymerization reactor.
5. The method for producing a polycondensation polymer according to any one
of claims 1 to 4, wherein the polycondensation polymer is a polyester resin.
25 6. A polycondensation polymer produced by the method for producing a
polycondensation polymer according to any one of claims 1 to 5, having a molecular
weight distribution represented by Mw/Mn of 2.0 or higher.

-82-
7. A polycondensation polymer produced by the method for producing a
polycondensation polymer according to any one of claims 1 to 5, which is a polymer
alloy.
8. A polycondensation polymer produced by the method for producing a
5 polycondensation polymer according to any one of claims 1 to 5, which is a polyester
elastomer.
9. A method for producing a molded article which comprises: transferring a
polymer produced by the method for producing a polycondensation polymer
according to any one of claims 1 to 5 in a molten state to a molding machine and
10 molding the same.
10. An apparatus for producing a polycondensation polymer comprising a
polymerization reactor having at least a feed opening, a perforated plate, a support
and an outlet as constituents, wherein the perforated plate has two or more areas, and
a prepolymer and/or a polymer modifier is introduced into each of the areas, the
15 introduced prepolymer and/or polymer modifier is discharged through holes of each
of the areas, and polycondensation is performed under reduced pressure while
allowing the prepolymer and/or polymer modifier to fall along the support.
11. The apparatus for producing a polycondensation polymer according to claim
10, wherein the polymerization reactor has two or more outlets.
20 12. The apparatus for producing a polycondensation polymer according to claim
10 or 11, wherein the support of the polymerization reactor has two or more areas
corresponding to each area of the perforated plate, or/and the outlet is divided into
two or more areas corresponding to each area of the perforated plate or the support.

A method for producing a polycondensation polymer, which comprises:
introducing a prepolymer of a polycondensation polymer into a polymerization
reactor through a feed opening in a molten state; discharging the introduced
prepolymer through holes of a perforated plate; and then polycondensing the
prepolymer under reduced pressure, while allowing the prepolymer to fall along a
support, wherein the perforated plate has two or more areas and polycondensation is
performed by introducing a prepolymer and/or a polymer modifier into each of the
areas and discharging the introduced prepolymer and/or polymer modifier through
holes of each of the areas.

Documents:

01201-kolnp-2007-abstract.pdf

01201-kolnp-2007-claims.pdf

01201-kolnp-2007-correspondence others 1.1.pdf

01201-kolnp-2007-correspondence others 1.2.pdf

01201-kolnp-2007-correspondence others 1.3.pdf

01201-kolnp-2007-correspondence others.pdf

01201-kolnp-2007-description complete.pdf

01201-kolnp-2007-drawings.pdf

01201-kolnp-2007-form 1.pdf

01201-kolnp-2007-form 18.pdf

01201-kolnp-2007-form 2.pdf

01201-kolnp-2007-form 3.pdf

01201-kolnp-2007-form 5.pdf

01201-kolnp-2007-gpa.pdf

01201-kolnp-2007-priority document.pdf

1201-KOLNP-2007-ABSTRACT.pdf

1201-KOLNP-2007-CANCELLED PAGES.pdf

1201-KOLNP-2007-CLAIMS.pdf

1201-KOLNP-2007-DESCRIPTION (COMPLETE).pdf

1201-KOLNP-2007-DRAWINGS.pdf

1201-KOLNP-2007-FORM 1.pdf

1201-KOLNP-2007-FORM 2.pdf

1201-KOLNP-2007-FORM 3.pdf

1201-KOLNP-2007-FORM-27.pdf

1201-KOLNP-2007-PA.pdf

1201-KOLNP-2007-PCT SEARCH REPORT.pdf

1201-KOLNP-2007-PETITION UNDER RULE 137.pdf

1201-KOLNP-2007-REPLY TO EXAMINATION REPORT.pdf


Patent Number 242556
Indian Patent Application Number 1201/KOLNP/2007
PG Journal Number 36/2010
Publication Date 03-Sep-2010
Grant Date 01-Sep-2010
Date of Filing 05-Apr-2007
Name of Patentee ASAHI KASEI CHEMICALS CORPORATION
Applicant Address 1-2, YURAKU-CHO, CHIYODA-KU, TOKYO
Inventors:
# Inventor's Name Inventor's Address
1 YOKOYAMA, HIROSHI 1-2, YURAKU-CHO, CHIYODA-KU, TOKYO 100-8440
2 AMINAKA, MUNEAKI 1-2, YURAKU-CHO, CHIYODA-KU, TOKYO 100-8440
PCT International Classification Number C08G 85/00
PCT International Application Number PCT/JP2005/021643
PCT International Filing date 2005-11-25
PCT Conventions:
# PCT Application Number Date of Convention Priority Country
1 2004-345241 2004-11-30 Japan
2 2004-345246 2004-11-30 Japan
3 2005-235816 2005-08-16 Japan