Title of Invention | "A BIMETALLIC CATALYST COMPOSITION" |
---|---|
Abstract | A bimetallic catalyst composition comprising a fluorided metallocene catalyst component, a non-metallocene catalyst component, and an activator, the catalyst components and activator supported on an inorganic oxide dehydrated at a temperature between 870°C and 1500°C. |
Full Text | The present invention relates to a bimetallic catalyst composition [0001] The present invention relates to bimodal polyolefin production, and more particularly, to bimodal polyolefins in producing films, wherein the bimodal polyolefin is produced in a single reactor using a bimetallic catalyst in a desirable embodiment BACKGROUND [0002] Bimodal polymers produced using two 01 more different catalyst types— bimetallic catalysts—are of increasing interest, especially in producing polyethylene and other polyolefins See, for example, US 5,525,678 However, problems exist in using these bimetallic catalysts, especially m the gas phase One problem is catalyst activity, which should be as high as possible in order to economize the process, as catalysts costs are significant [0003] One method of improving catalyst efficiency m gas phase processes is to improve upon the catalyst used in the process A promising class of single-site catalysts for commercial use includes those wherem the metal center has at least one extractable fluorine (or fluorine "leaving group") Disclosures of such catalysts include US 20020032287, WO 97/07141, DE 43 32 009 Al, EP-A2 0 200 351, EP-A1 0 705 849, EF Murphy, et al, Synthesis and spectroscopic characterization of a series of substituted cyclopentadienyl Group 4 fluorides, crystal structure of the acetylacetonato complex [(acac)2(r| -C5Me5)Zr(p-F)SnMe3Cl], DALTON, 1983 (1996), A Heizog, et al, Reactions of (qs-C5Me5)ZrF3, (rf-C5Me4Et)ZtF3, (-C5M45)2ZrF2l (5-C5Me5)HfF3, and (5-C5Me5)TaF4 with AlMe3, Structure of the First Hafnium-Aluminum-Carbon Cluster, 15 ORGANOMETALLICS 909-917 (1996), F Garbassi, et al, JOURNAL OF MOLECULAR CATALYSIS A CHEMICAL 101 199-209 (1995), and W Kammsky, et al , Fluorinated Half-Sandwich Complexes as Catalysts in Syndwspecific Styrene Polymerization, 30(25) MACROMOLECULES 7647-7650 (1997) Use of such single site catalyst components m a olefin polymerization system is desirable, especially in gas-phase polyethylene polymenzation It would be desirable to further improve upon this system, especially for bimodal gas phase polymenzation processes The present invention is directed towards solving this and other problems SUMMARY [0004] The present invention provides a method for bimodal polyolefin production, preferably using bimetallic catalysts, and polyolefins films made from bimodal polyolefin compositions At least one embodiment of the invention is directed to a process of producing a bimodal polyolefin composition that includes contacting monomers with a supported bimetallic catalyst composition for a time sufficient to form a bimodal polyolefin composition, wherein the supported bimetallic catalyst includes a first catalyst component and a second catalyst component that includes a metallocene catalyst compound having at least one fluoride or fluorine containing leaving group [0005] Another specific embodiment of the invention is directed to a process of producing a bimodal polyolefin composition comprising contacting monomers with a supported bimetallic catalyst composition for a time sufficient to form the bimodal polyolefin composition that includes a high molecular weight polyolefin component and a low molecular weight polyolefin component, wherein the supported bimetallic catalyst includes a first catalyst component that includes a fluonnated metallocene represented by the formula Cp2MF2 wherein Cp is a substituted or unsubstituted cyclopentadienyl nng or derivative thereof, M is a Group 4, 5, or 6 transition metal and a support material comprising silica dehydrated at a temperature of 800 °C or more [0006] Yet another specific embodiment of the invention is directed to a process of producing a bimodal polyolefin composition, including providing a particulate support material comprising silica, heating the particulate support material to a temperature of 800 °C or more for a time sufficient to form a dehydrated support material including dehydrated silica, combining the dehydrated support material with a non-polar hydrocarbon to provide a support slurry, providing a first catalyst component that is a non-metallocene catalyst, providing a second catalyst component that includes a metallocene catalyst compound having at least one fluoride or fluorine containing leaving group, combining the support slurry with the first and second catalyst components to form a supported bimetallic catalyst composition, and contacting monomers with the bimetallic catalyst composition for a time sufficient to form a bimodal polyolefin composition having a density of from 0 86 g/cm3 to 0 97 g/ cm3, a molecular weight distnbution of from 5 to 80, a I2 of from 0 01 dg/min to 50 dg/mm, and a melt index ratio of from 40 to 500 [0007] In certain aspects, a film made from one or more of the bimodal polyolefin compositions disclosed herein has a Dart Drop Impact F50 Value of at least 100 [g] on 25 4 micron film and 75 [g] on 12 5 micron film [0008] In certain aspects, a film made from one or more of the bimodal polyolefin compositions disclosed herein has an MD Tear value of at least 0 4 g/micron on 25 4 micron film and at least 0 2 g/micron on 12 5 micron film [0009] In certain aspects, a film made from one or more of the bimodal polyolefin compositions disclosed herein has a TD Tear value of at least 1 5 g/micron on 24 5 micron film and 1 0 g/micron on 12 5 micron film [0010] In particular embodiments, the support material useful in the process of the invention has been enhanced, in that it includes silica dehydrated at a temperature of 800°C or more In a more particular embodiment, the support material includes silica dehydrated at a temperature of 830 °C or more In yet a more particular embodiment, the support material includes silica dehydrated at a temperature of 875 °C oi more DETAILED DESCRIPTION General Definitions [0011] As used herein, in reference to Periodic Table "Groups" of Elements, the "new" numbenng scheme for the Periodic Table Groups are used as in the CRC HANDBOOK OF CHEMISTRY AND PHYSICS (David R Lide ed , CRC Press 81st ed 2000) [0012] As used herein, the phrase "catalyst system" includes at least one "catalyst component" and at least one "activator", both of which are descnbed further herein The catalyst system may also include other components, such as supports, etc , and is not limited to the catalyst component and/or activator alone or in combination The catalyst system may include any number of catalyst components in any combination as described herein, as well as any activator in any combination as described herein [0013] As used herein, the phrase "catalyst compound" includes any compound that, once appropnately activated, is capable of catalyzing the polymerization or oligomenzation of olefins, the catalyst compound compnsing at least one Group 3 to Group 12 atom, and optionally at least one leaving group bound thereto [0014] As used herein, the phrase "leaving group" refers to one or more chemical moieties bound to the metal center of the catalyst component that can be abstracted from the catalyst component by an activator, thus producing the species active towards olefin polymerization or oligomenzation The activator is descnbed further below [0015] As used herein, the term "fluonnated catalyst component" or "fluonded catalyst component" means a catalyst compound having at least one fluonde or fluonne containing leaving group, preferably a metallocene or metallocene-type catalyst compound having at least one fluoride or fluonne containing leaving group [0016] As used herein, a "hydrocarbyl" includes aliphatic, cyclic, olefmic, acetylenic and aromatic radicals (i e, hydrocarbon radicals) comprising hydrogen and carbon that are deficient by one hydrogen A "hydrocarbylene" is deficient by two hydrogens [0017] As used herein, an "alkyl" includes linear, branched and cyclic paraffin radicals that are deficient by one hydrogen Thus, for example, a -CH3 group ("methyl") and a CH3CH2- group ("ethyl") are examples of alkyls [0018] As used herein, an "alkenyl" includes linear, branched and cyclic olefin radicals that are deficient by one hydrogen, alkynyl radicals include linear, branched and cyclic acetylene radicals deficient by one hydrogen radical [0019] As used herein, "aryl" groups includes phenyl, naphthyl, pyndyl and other radicals whose molecules have the ring structure characteristic of benzene, naphthylene, phenanthrene, anthracene, etc For example, a C6H5- aromatic structure is an "phenyl", a C6H42- aromatic structure is an "phenylene" An "arylalkyl" group is an alkyl group having an aryl group pendant therefrom, an "alkylaryl" is an aryl group having one or more alkyl groups pendant therefrom [0020] As used herein, an "alkylene" includes linear, branched and cyclic hydrocarbon radicals deficient by two hydrogens Thus, -CH2- ("methylene") and -CH2CH2- ("ethylene") are examples of alkylene groups Other groups deficient by two hydrogen radicals include "arylene" and "alkenylene" [0021] As used herein, the phrase "heteroatom" includes any atom other than carbon and hydrogen that can be bound to carbon, and in one embodiment is selected from the group consisting of B, Al, S1, Ge, N, P, O, and S A "heteroatom-containmg group" is a hydrocarbon radical that contains a heteroatom and may contain one or more of the same or different heteioatoms, and from 1 to 3 heteroatoms in a particular embodiment Non-limiting examples of heteroatom-contammg groups include udicals of lmines, amines, oxides, phosphmes, ethers, ketones, oxoazolines heterocyclics, oxazolmes, thioetheis, and the like [0022] As used herein, an "alkylcarboxylate", "arylcarboxylate", and "alkylarylcarboxylate" is an alkyl, aryl, and alkylaryl, respectively, that possesses a carboxyl group in any position Examples include C6H5CH2C(O)O-, CH3C(O)O-, etc [0023] As used herein, the term "substituted" means that the group following that term possesses at least one moiety in place of one or more hydrogens in any position, the moieties selected from such groups as halogen radicals (esp, Cl, F, Br), hydroxyl groups, carbonyl groups, carboxyl groups, amine groups, phosphine groups, alkoxy groups, phenyl groups, naphthyl groups, C1 to C10 alkyl groups, C2 to C10 alkenyl groups, and combinations thereof Examples of substituted alkyls and aryls includes, but are not limited to, acyl radicals, alkylamino radicals, alkoxy radicals, aryloxy radicals, alkylthio radicals, dialkylamino radicals, alkoxycarbonyl radicals, aryloxycarbonyl radicals, carbomoyl radicals, alkyl- and dialkyl-carbamoyl radicals, acyloxy radicals, acylamino radicals, arylamino radicals, and combinations thereof [0024J As used herein, structural formulas are employed as is commonly understood in the chemical arts, lines ("----") used to represent associations between a metal atom ("M", Group 3 to Group 12 atoms) and a hgand or hgand atom (eg, cyclopentadienyl, nitrogen, oxygen, halogen ions, alkyl, etc), as well as the phrases "associated with", "bonded to" and "bonding", are not limited to representing a certain type of chemical bond, as these lines and phrases are meant to represent a "chemical bond", a "chemical bond" defined as an attractive force between atoms that is strong enough to permit the combined aggregate to function as a unit, or "compound" [0025] A certain stereochemistry for a given structure or part of a structure should not be implied unless so stated for a given structure or apparent by use of commonly used bonding symbols such as by dashed lines and/or heavy lines [0026] Unless stated otherwise, no embodiment of the present invention is herein limited to the oxidation state of the metal atom "M" as defined below in the individual descriptions and examples that follow The ligation of the metal atom "M" is such that the compounds described herein are neutral, unless otherwise indicated [0027] As used herein, the term "bimodal," when used to describe a polymer or polymer composition (eg, polyolefins such as polypropylene or polyethylene, or other homopolymers, copolymers or terpolymers) means "bimodal molecular weight distribution," which is understood as having the broadest definition persons m the pertinent art have given that term as reflected in printed publications and issued patents For example, a single composition that includes polyolefins with at least one identifiable high molecular weight distribution and polyolefins with at least one identifiable low molecular weight distribution is considered to be a "bimodal" polyolefin, as that term is used herein In a particular embodiment, other than having different molecular weights, the high molecular weight polyolefin and the low molecular weight polyolefin are essentially the same type of polymer, for example, polypropylene or polyethylene [0028] As used herein, the term "productivity" means the weight of polymer produced per weight of the catalyst used in the polymenzation process (e g, grams polymer/gram catalyst) [0029] As used herein, the term "dehydrated" is understood as having the broadest definition persons in the pertinent art have given that term in describing catalyst support materials, for example, silica, as reflected in printed publications and issued patents, and includes any material, for example, a support particle, from which a majority of the contained/adsorbed water has been removed Gas-phase polymerization using bimetallic catalysts comprising a fluonded metallocene catalyst component [0030] The present invention provides a process for producing a bimodal polyolefin composition comprising contacting olefin monomers with a bimetallic catalyst composition to form a bimodal polyolefin composition, wherein the bimetallic catalyst composition comprises a first catalyst component, and metallocene catalyst compound having at least one fluoride or fluorine containing leaving group In a particular embodiment, the bimetallic catalyst is supported The bimetallic catalyst, each of its components, and the method of polymenzation are set out in greater detail below [0031] In one aspect of the invention, the method of making bimodal polymers is characterized in that the monomers are contacted with the bimetallic catalyst in a single reactor vessel and form the bimodal polyolefin composition in the same reactor vessel [0032] The present invention also provides a bimodal film composition comprising a polyolefin having a density of from 0 86 g/cm3 to 0 97 g/cm3, a molecular weight distnbution of from 5 to 80, a melt index of from 0 01 dg/min to 50 dg/min, and a melt index ratio of from 40 to 500 The film composition, or film, is formed from the bimetallic catalyst of the invention, and has certain desirable features as set out further below Bimetallic Catalyst [0033] As used herein, the term "bimetallic catalyst" or "bimetallic catalyst system" refers to two or more catalyst components used in combination with at least one activator, and optionally a support material, that is useful m polymerizing olefins The "supported bimetallic catalyst" or "supported bimetallic catalyst composition" refers the bimetallic catalyst system as used in combination with a support material, wherein one or more of the components that make up the bimetallic catalyst system may be bound to the support In a particular embodiment, the bimetallic catalyst of the invention includes two catalyst components In a more particular embodiment, the bimetallic catalyst component includes a "first catalyst component" and a "second catalyst component" 10034] As used herein, the term "first catalyst component" refers to any catalyst component other than the second catalyst component Preferably, the first catalyst component is a non-metallocene catalyst component, examples of which include titamum or vanadium based Ziegler-Natta catalysts compounds as described further herein [0035] As used herein, the term "non-metallocene compound" refers any catalyst that is neither a metallocene nor one of the metallocene-type catalyst compounds identified below ] 003 6] As used herein, the term "second catalyst component" refers to any catalyst that is different from a first catalyst component, a metallocene catalyst component in a particular embodiment In a particular embodiment, the second catalyst component includes a fluonded metallocene component which comprises at least one fluoride ion leaving group or fluorine containing group [0037] Certain embodiments of the present invention involve contacting monomers with the bimetallic catalyst component In a particular embodiment, each different catalyst compound that comprises the bimetallic catalyst resides, or is supported on a single type of support such that, on average, each particle of support material includes both the first and second catalyst components In another embodiment, the first catalyst component is supported separately from the second catalyst component such that on average any given particle of support material composes only the first or the second catalyst component In this later embodiment, each supported catalyst may be introduced into the polymerization reactor sequentially in any order, alternately in parts, or simultaneously [0038] In a particular embodiment, the first catalyst component includes a titanium non-metallocene catalyst component, from which a higher molecular weight resm (eg, > ca 100,000 amu) can be produced In a particular embodiment, the second catalyst component includes a metallocene component, from which a lower molecular weight resin (eg, [0039] In one embodiment, an "enhanced silica" is prepared as described herein and constitutes the support, the £ st catalyst component is a non nietallocene compound that is first combined with the enhanced silica, to provide a supported non-metallocene composition, the supported non-metallocene composition is combined with the second catalyst component, for example, a fluonded metallocene (a metallocene having at least one fluorine ion leaving group), resulting m a fluormated bimetallic catalyst composition having enhanced productivity when used in production of a bimodal polyolefin composition [0040] Various methods of affixing two different catalyst components (albeit a different combination of catalysts) to a support can be used In general, one procedure for prepanng a supported bimetallic catalyst can include providing a supported first catalyst component, contacting a slurry that includes the first catalyst component in a non-polar hydrocarbon with a solution that includes the second catalyst component, which may also include an activator, and drying the resulting product that includes the first and second catalyst components and recovering a bimetallic catalyst composition First Catalyst Component [0041] As noted above, the bimetallic catalyst composition includes a first catalyst component, which is (or includes) a non-metallocene compound However, it is contemplated that for certain applications the first catalyst component may alternatively be a metallocene compound, or even one of the metallocene-type catalyst compounds identified below that is different in structure from the second catalyst component as described herein In a particular embodiment, the first catalyst component is a Ziegler-Natta catalyst compound Ziegler-Natta catalyst components are well known in the art and described by, for example, m ZIEGLER CATALYSTS 363-386 (G Fink, R Mulhaupt and H H Bnntzinger, eds , Springer-Verlag 1995) Examples of such catalysts include those comprising T1CI4 and other such transition metal oxides and chlondes [0042] The first catalyst component is combined with a support material in one embodiment, either with or without the second catalyst component The first catalyst component can be combined with, placed on or otherwise affixed to a support in a vanety of ways In one of those ways, a slurry of the support in a suitable non-polar hydrocarbon diluent is contacted with an organomagnesium compound, which then dissolves in the non-polar hydrocarbon diluent of the slurry to form a solution from which the organomagnesium compound is then deposited onto the carrier The organomagnesium compound can be represented by the formula RMgR', where R' and R are the same or different C2-C12 alkyl gioups, or C4-C10 alkyl groups, or C4-C8 alkyl groups In at least one specific embodiment, the organomagnesium compound is dibutyl magnesium In one embodiment, the amount of organomagnesium compound included in the silica slurry is only that which will be deposited, physically or chemically, onto the support, for example, being bound to the hydoxyl groups on the support, and no more than that amount, since any excess organomagnesium compound may cause undesirable side reactions Routine experimentation can be used to determine the optimum amount of organomagnesium compound For example, the organomagnesium compound can be added to the slurry while stirnng the slurry, until the organomagnesium compound is detected m the support solvent Alternatively, the organomagnesium compound can be added in excess of the amount that is deposited onto the support, in which case any undeposited excess amount can be removed by filtration and washing The amount of organomagnesium compound (moles) based on the amount of dehydrated silica (grams) generally range from 0 2 mmol/g to 2 mmol/g in one embodiment [0043] Optionally, the organomagnesmm compound-treated slurry is contacted with an electron donor, such as tetraethylorthosiloxane (TEOS) or an organic alcohol R"OH, where R" is a C1-C12 alkyl group, or a C1 to C8 alkyl group, or a C2 to C4 alkyl group In a particular embodiment, R"OH is n-butanol The amount of alcohol used in an amount effective to provide an R"OH Mg mol/mol ratio of from 0 2 to 1 5, or from 0 4 to 1 2, or from 0 6 to 1 1, or from 0 9 to 1 0 [0044J The organomagnesium and alcohol-treated slurry is contacted with a non- metallocene transition metal compound Suitable non-metallocene transition metal compounds are compounds of Group 4 and 5 metals that are soluble in the non-polar hydrocarbon used to form the silica slurry Suitable non-metallocene transition metal compounds include, for example, titanium and vanadium hahdes, oxyhahdes or alkoxyhahdes, such as titanium tetrachloride (T1Cl4), vanadium tetrachloride (VCU) and vanadium oxytnchlonde (VOCl3), and titanium and vanadium alkoxides, wherein the alkoxide moiety has a branched or unbranched alkyl group of 1 to 20 caibon atoms, preferably 1 to 6 carbon atoms Mixtures of such transition metal compounds may also be used The amount of non-metallocene transition metal compound used is sufficient to give a transition metal to magnesium mol/mol ratio of from 0 3 to 1 5, or from 0 5 to 0 8 The diluent can then be removed in a conventional manner, such as by evaporation or filtering, to obtain the dry, supported first catalyst component [0045] The first and second catalyst components may be contacted with the support in any order In a particular embodiment of the invention, the first catalyst component is reacted first with the support as described above, followed by contacting this supported first catalyst component with a second catalyst component Process for Making a Fluorinated Catalyst Compound [0046] Embodiments of the invention include a process of producing a fluorinated catalyst compound, and m particular, a fluonded metallocene catalyst component The fluonded metallocene itself is described m more detail below The fluonded metallocene catalyst component can be (or include) any fluonded metallocene catalyst component, but is preferably a fluonded metallocene catalyst component The fluonded metallocene catalyst component can be, for example, any one of the catalysts descnbed in greater detail below, or the "second catalyst component" of the bimodal catalyst The fluonded catalyst compound is preferably a metallocene type compound having the general formula (Cp(R)p)mMXnFr (which can include, for example, a partially fluonnated metallocene), wherein Cp is a cyclopentadienyl hgand or ligand isolobal to cyclopentadienyl (as described further below) that can be substituted in any position by a group R as set out below, M is a Group 4, 5, or 6 transition metal in a particular embodiment, X is an anionic ligand such as a halogen, carboxylate, acetylacetonate, alkoxide, hydroxide, or oxide, p is an integer from 0 to 10, m is an integer from 1 to 3, n is an integer from 0 to 3, and r is an integer from 1 to 3 [0047] The process includes contacting a metallocene catalyst compound with a fluonding agent, and more particularly, a fluonnated inorganic salt, for a time sufficient to form the fluonded metallocene catalyst compound The metallocene catalyst compound preferably has the same genera) formula as the desired fluonnated metallocene compound, with the exception that the one or more leaving groups X are an anionic ligand (e g, chlonne or bromine) rather than fluorine The metallocene compound that is contacted with the fluonding agent may be commercially available, or may be prepared by methods known to one skilled in the art [0048] The metallocene compound may include a cyclopentadienyl ligand or ligand isolobal to Cp, either substituted or unsubstituted The amount of substitution on Cp may affect the yield of the fluonnated metallocene compound Therefore, at least one Cp of the metallocene is substituted in one embodiment, and two Cps are substituted in another embodiment, wherein the metallocene is a sandwich metallocene as set out below In a particular embodiment, the substituent group (R) is not an aryl group such as phenyl, indenyl or fluorenyl In at least certain embodiments, it has been discovered that benzene substituent groups correspond to reduced product yields For example, when R is indenyl, the product yield may be as low as zero Preferably, the substituent groups include hydrocarbyl groups In a preferred embodiment, alky] substitution results in surprisingly high yields, for example, 95% or more [0049] In one embodiment, the fluonding agent is a fluonnated inorganic salt or combination of salts descnbed by the general formula (a) (Formula Removed) wherein α is a cationic species selected from the group consisting of Group 1 and 2 cations, anihnium and substituted versions thereof, and NH4+, NH3R, NH2R2, and NHR3+ wherein R is selected from the group consisting of hydride, chlonde, C1 to C10 alkyl and C6 to C12 aryls, ß is an anionic species selected from the group consisting of fluorine ions and compounds comprising fluorine and one or more elements selected from the group consisting of hydrogen, silicon, carbon, phosphorous, oxygen, aluminum and boron, and a and b are integers from 1 to 10 [0050] In a particular embodiment, the fluonnated inorganic salt is a compound charactenzed in that it is capable of generating fluoride ions when contacted with water or other protic diluent Non-limiting examples of the fluonnated inorganic salt include (NH4)3AlF6,NH4HF2, NaF, KF, NH4F, (NH4)2 S1F6 and combinations thereof [0051] The fluonnated inorganic salt compound may include a fluonnated inorganic salt mixture The fluonnated inorganic salt compound is preferably soluble or partially soluble in a diluent Therefore, the mixture may include the fluonnated inorganic salt and a diluent, that is, the fluonnated inorganic salt may be dissolved in a diluent pnor to contacting the metallocene catalyst compound The diluent may include an organic diluent In a particular embodiment, the diluent is water or water in combination with some other polar diluent that is miscible with water (e g , ethers, ketones, aldehydes, etc) In another embodiment, the diluent is any desirable protic medium In a particular embodiment, the fluonnated inorganic salt is combined with a diluent that is at least 50 wt% water, and at least 60 wt% water in another embodiment, and at least 70 wt% water in yet another embodiment, and at least 80 wt% water in yet another embodiment, and at least 90 wt% in a particular embodiment, and at least 99 wt% water in a more particular embodiment [0052] The metallocene compound that is contacted with the fluondmg agent may be initially charged m an inert or non-protic diluent The inert diluent may include one of, or a mixture of, aliphatic and aromatic hydrocarbons or a halogenated solvent Suitable hydrocarbons include substituted and unsubstituted aliphatic hydrocarbons and substituted and unsubstituted aromatic hydrocarbons In a particular embodiment, the inert diluent is selected from the group consisting of C3 to C30 hydrocarbons and C1 to C10 halogenated hydrocarbons and mixtures thereof in a particular embodiment Non-limiting examples of suitable inert diluents include hexane, heptane, octane, decane, toluene, xylene, dichloromethane, dichloroethane, chloroform and 1-chlorobutane [0053] In a particular embodiment of the method of fluonding metallocenes described herein, the fluonnated inorganic salt combined with a protic diluent is reacted with the metallocene combined with an inert diluent In a more particular embodiment, the fluonnated inorganic salt in at least 50% water is combined with the metallocene to be fluonded dissolved/suspended in a hydrocarbon or halogenated hydrocarbon diluent The combined reactants may form two or more phases in contact with one another The fluonding reaction then takes place under desirable mixing and temperature conditions [0054] In embodiments of the fluonding step wherein the fluonding agent is immiscible or only partially miscible with the diluent, it is within the scope of the invention to use a reagent that will assist the transport of the fluonding agent to the alkylated catalyst component or the diluent phase in which the alkylated catalyst component exists, or assist in the reaction between the fluonding agent and alkylated catalyst component Such reagents— phase-transfer catalysts—are known in the art and are used in reactions wherein, for example, an aqueous or polar diluent phase is in contact with a non-polar or hydrocarbon diluent phase, and the reactants are separated as such Non-limiting examples of such phase-transfer catalysts include quaternary ammonium salts (e g, quaternary ammonium bisulfate), crown ethers, and others common in the art [0055] Depending on the desired degree of substitution, the ratio of fluonne (of the fluonding agent) to metallocene combined to react is from 1 equivalent to 20 equivalents in one embodiment, and from 2 to 10 equivalents in another embodiment, and from 2 to 8 equivalents in yet another embodiment, and from 2 to 5 equivalents in yet another embodiment, wherein a desirable range comprises any combination of any upper limit with any lower limit While excess fluonnated inorganic salt may not be detrimental, the molar ratio of the reactants is preferably determined by the number of anionic hgands to be substituted in the metallocene compound, that is, the number of anionic hgands to be replace by fluorine or fluoride atoms In a particular embodiment, the number of anionic hgands to be substituted is 2 [0056] Stated another way, the desired amount of fluonding agent, based on the equivalents of fluorine in the fluondmg agent, that is combined with the metallocene catalyst compound ranges from 1, or 2, or 3, oi 4, or 5 to 6, or 7, or 8, or 10, or 12, or 14 or 15 or 18 or 20, wherein a desnable range comprises any combination of any upper limit with any lower limit described herein In another embodiment, the desired amount of fluondmg agent, based on the equivalents of fluondmg agent as a whole, ranges from 1, or 2, or 3, or 4 to 5 or 6, or 7, or 8, or 9, or 10, wherein a desirable range comprises any combination of any upper limit with any lower limit described herein [0057J The fluonnated inorganic salt may be reacted with the metallocene compound by vigorously strring the compounds The reaction may occur at any temperature that affords the desired mono-, di- or tnfluonded metallocene, including temperatures of from -80 °C to 120 °C in one embodiment, and from 0 to 100 °C in a more particular embodiment, and from 10 to 60°C in yet a more particular embodiment, and from 15 to 40°C in yet a more particular embodiment At those temperatures, reaction times of 0 05 hour to 8 hours are sufficient to form a fluonnated metallocene compound, but routine experimentation may be desirable to amve at an optimum temperature Generally, the reaction time is dependent upon the amount of reactants reacted In one embodiment, the reaction time is from 0 1 hour to 3 hours [0058] The diluent, along with reaction by-products, can be removed from the mixture in a conventional manner, such as by evaporation or filtering, to obtain the dry, fluonnated metallocene compound For example, the fluonded metallocene may be dned in the presence of magnesium sulfate The filtrate, which contains the fluonnated metallocene compound in high punty and yield, can without further processing be directly used in the polymenzation of olefins if the solvent is a hydrocarbon [0059] Contacting the metallocene compound with the fluonnated inorganic salt, an aqueous fluonnated inorganic salt, results in a product yield of 50% or more in a particular embodiment The product yield is 80% or more in yet a more particular embodiment The product yield is 90%o or more in yet a more particular embodiment Unexpectedly, contacting the metallocene compound with the aqueous solution of fluonnated inorganic salt results in a fluonded metallocene compound having high productivities Fluonded Metallocene Catalyst Component [0060] The bimetallic catalyst system useful in the present invention includes a second catalyst component that composes at least one fluonded metallocene catalyst component as descnbed herein Metallocene catalyst compounds are generally descnbed throughout in, for example, 1 & 2 METALLOCENE-BASED POLYOLEF[NS (John Scheirs & W Kaminsky eds , John Wiley & Sons, Ltd 2000), G G Hlatky in 181 COORDINATION CHEM REV 243-296 (1999) and in particular, for use in the synthesis of polyethylene in 1 METALLOCENE-BASED POLYOLEFTNS 261-377 (2000) The metallocene catalyst compounds as described herein include "half sandwich" and "full sandwich" compounds having one or more Cp ligands (cyclopentadienyl and ligands isolobal to cyclopentadienyl) bound to at least one Group 3 to Group 12 metal atom, and one or more leaving group(s) bound to the at least one metal atom Hereinafter, these compounds will be referred to as "metallocenes" or "metallocene catalyst components" The fluonded metallocene components are those wherein at least one leaving group bound to M is a fluoride ion or a fluonne-containing group The metallocene catalyst component is supported on a support matenal in a particular embodiment as descnbed further below, and may be supported with or without the first catalyst component, with the first catalyst component in a particular embodiment [0061] The Cp ligands are typically -bonded and/or fused nng(s) or nng systems The nng(s) or nng system(s) typically compnse atoms selected from the group consisting of Groups 13 to 16 atoms, and more particularly, the atoms that make up the Cp ligands are selected from the group consisting of carbon, nitrogen, oxygen, silicon, sulfur, phosphorous, germanium, boron and aluminum and combinations thereof, wherein carbon makes up at least 50% of the nng members Even more particularly, the Cp hgand(s) are selected from the group consisting of substituted and unsubstituted cyclopentadienyl hgands and hgands isolobal to cyclopentadienyl, non-limiting examples of which include cyclopentadienyl, indenyl, fluorenyl and other structures Further non-limiting examples of such hgands include cyclopentadienyl, cyclopentaphenanthreneyl, indenyl, benzmdenyl, fluorenyl, octahydrofluorenyl, cyclooctatetraenyl, cyclopentacyclododecene, phenanthnndenyl, 3,4-benzofluorenyl, 9-phenylfluorenyl, 8-H-cyclopent[a]acenaphthylenyl, 7H-dibenzo fluorenyl, indeno[l,2-9]anthrene, thiophenoindenyl, thiophenofluorenyl, hydrogenated versions thereof (eg-, 4,5,6,7-tetrahydroindenyl, or "H4Ind"), substituted versions thereof, and heterocyclic versions thereof In a particular embodiment, the metallocenes useful in the present invention are selected from those including one or two, two in a more particular embodiment, of the same or different Cp nngs selected from the group consisting of cyclopentadienyl, indenyl, fluorenyl, tetrahydroindenyl, and substituted versions thereof [0062J The metal atom "M" of the metallocene catalyst compound, as described throughout the specification and claims, may be selected from the group consisting of Groups 3 through 12 atoms and lanthanide Group atoms in one embodiment, and selected from the group consisting of Groups 3 through 10 atoms in a more particular embodiment, and selected from the group consisting of Sc, T1, Zr, Hf, V, Nb, Ta, Mn, Re, Fe, Ru, Os, Co, Rh, Ir, and Ni in yet a more particular embodiment, and selected from the group consisting of Groups 4, 5 and 6 atoms in yet a more particular embodiment, and a Ti, Zr, Hf atoms in yet a more particular embodiment, and Zr in yet a more particular embodiment The oxidation state of the metal atom "M" may range from 0 to +7 in one embodiment, and in a more particular embodiment, is +1, +2, +3, +4 or +5, and in yet a more particular embodiment is +2, +3 or +4 The groups bound the metal atom "M" are such that the compounds described below in the formulas and structures are electrically neutral, unless otherwise indicated The Cp hgand(s) form at least one chemical bond with the metal atom M to form the "metallocene catalyst compound" The Cp hgands are distinct from the leaving groups bound to the catalyst compound in that they are not highly susceptible to substitution/abstraction reactions [0063] In one aspect of the invention, the one or more metallocene catalyst components of the invention are represented by the formula (I) (Formula Removed) wherein M is as described above, each X is chemically bonded to M, each Cp group is chemically bonded to M, and n is an integer from 0 to 4, and either 1 or 2 in a particular embodiment [0064] The ligands represented by CpA and CpB in formula (I) may be the same or different cyclopentadienyl ligands or ligands isolobal to cyclopentadienyl, either or both of which may contain heteroatoms and either or both of which may be substituted by a group R In one embodiment, CpA and CpB are independently selected from the group consisting of the group consisting of cyclopentadienyl, indenyl, tetrahydroindenyl, fluorenyl, and substituted derivatives of each [0065J Independently, each CpA and CpB of formula (I) may be unsubstituted or substituted with any one or combination of substitucnt groups R Non-limiting examples of substituent groups R as used m structure (I) as well as nng substituents in structures (Va-d) include groups selected from the group consisting of hydiogen radicals, alkyls, alkenyls, alkynyls, cycloalkyls, aryls, acyls, aroyls, alkoxys, aryloxys, alkylthiols, dialkylamines, alkylamidos, alkoxycarbonyls, aryloxycarbonyls, carbomoyls, alkyl- and dialkyl-carbamoyls, acyloxys, acylaminos, aroylammos, and combinations thereof [0066] More particular non-limiting examples of alkyl substituents R associated with formula (I) through (V) include methyl, ethyl, propyl, butyl, pentyl, hexyl, cyclopentyl, cyclohexyl, benzyl, phenyl, methylphenyl, and tert-butylphenyl groups and the like, including all their isomers, for example tertiary-butyl, isopropyl, and the like Other possible radicals include substituted alkyls and aryls such as, for example, fluoromethyl, fluroethyl, difluroethyl, lodopropyl, bromohexyl, chlorobenzyl and hydrocarbyl substituted organometalloid radicals including tnmethylsilyl, tnmethylgermyl, methyldiethylsilyl and the like, and halocarbyl- substituted organometalloid radicals including tns(tnfluoromethyl)silyl, methylbis(difluoiomethyl)silyl, bromomethyldimethylgermyl and the like, and disubstituted boron radicals including dimethylboron for example, and disubstituted Group 15 radicals including dimethyl amine, dimethylphosphine, diphenyl amine, methylphenylphosphme, Group 16 radicals including/- methoxy, ethoxy, propoxy, phenoxy, methylsulfide and ethylsulfide Other substituents R include olefins such as but not limited to olefinically unsaturated substituents including vinyl-term mated hgands, for example 3-butenyl, 2-propenyl, 5-hexenyl and the like In one embodiment, at least two R groups, two adjacent R groups in one embodiment, are joined to form a nng structure having from 3 to 30 atoms selected from the group consisting of carbon, nitrogen, oxygen, phosphorous, silicon, germanium, aluminum, boron and combinations thereof Also, a substituent group R group such as 1-butanyl may form a bonding association to the element M [0067] At least one X m the formula (1) above and for the formulas/structures (II) through (V) below is independently selected from the group consisting of fluoride ions, fluonnated C6 to C24 aryls, C7 to C25 alkylaryls and ftuonnated C| to C12 alkyls, wherein "fluonnated" means at least one, and up to 100% of the hydrogen atoms of the group are replaced by fluorine atoms, and from 50 to 100% of the hydrogen atoms in a particular embodiment, selected independently from fluoride ions, methyl, ethyl, propyl, phenyl, methylphenyl, dimethylphenyl, tnmethylphenyl, fluoromethyls (mono-, di- and tnfiuoromethyls) and fluorophenyls (mono-, di-, tn-, tetra- and pentafluorophenyls) in yet a more particular embodiment, and are fluoride ions in yet a more particular embodiment In a particular embodiment, all X groups on the metallocene are fluonne or fluonne containing groups as described, and in yet a more paiticular embodiment, all of the X groups on the metallocene useful in the invention are fluonne ions [0068] Non-limiting examples of other X groups include alkyls, amines, phosphmes, ethers, carboxylates, dienes, hydrocarbon radicals having from 1 to 20 carbon atoms, fluonnated hydrocarbon radicals (e g, -C6F5 (pentafluorophenyl)), fluonnated alkylcarboxylates (eg, CF3C(O)O-), hydndes and halogen ions and combinations thereof Other examples of X hgands include alkyl groups such as cyclobutyl, cyclohexyl, methyl, heptyl, tolyl, tnfluoromethyl, tetramethylene, pentamethylene, methyhdene, methyoxy, ethyoxy, propoxy, phenoxy, bis(N-methylamhde), dimethylamide, dimethylphosphide radicals and the like In one embodiment, two or more X's fomi a part of a fused nng or nng system [0069] In another aspect of the invention, the metallocene catalyst component includes those of formula (I) where CpA and CpB are bndged to each other by at least one bndging group, (A), such that the structure is represented by formula (II) (Formula Removed) [0070J These bndged compounds represented by formula (II) are known as "bndged metallocenes". CpA, CpB, M, X and n in structure (II) are as defined above for formula (I), and wherein each Cp hgand is chemically bonded to M, and (A) is chemically bonded to each Cp Non-limiting examples of bndging group (A) include divalent hydrocarbon groups containing at least one Group 13 to 16 atom, such as but not limited to at least one of a carbon, oxygen, nitrogen, silicon, aluminum, boron, germanium and tin atom and combinations thereof, wherein the heteroatom may also be C1 to C12 alkyl or aryl substituted to satisfy neutral valency The bndging group (A) may also contain substituent groups R as defined above (for formula (I)) includmg halogen radicals and iron More particular non-limiting examples of bridging group (A) are represented by C1 to C6 alkylenes, substituted C1 to C6 alkylenes, oxygen, sulfur, R'2C= R'2Si=, —S1(R,)2Si(R2)-, R2Ge=, R'P= (wherein "=" represents two chemical bonds), where R' is independently selected from the group consisting of hydnde, hydrocarbyl, substituted hydrocarbyl, halocarbyl, substituted halocarbyl, hydrocarbyl-substituted organometalloid, halocaibyl-substituted organometalloid, disubstituted boron, disubstituted Group 15 atoms, substituted Group 16 atoms, and halogen radical, and wherein two or more R' may be joined to form a nng or ring system In one embodiment, the bndged metallocene catalyst component of formula (II) has two or more bndging groups (A) [0071] Other non-limiting examples of bridging group (A) include methylene, ethylene, ethylidene, propyhdene, isopropylidene, diphenylmethylene, 1,2-dimethyl ethylene, 1,2-diphenylethylene, 1,1,2,2-tetramethylethylene, dimethylsilyl, diethylsilyl, methyl-ethylsilyl, tnfluoromethylbutylsilyl, bis(tnfiuoromethyl)silyl, di(n-butyl)silyl, di(n-propyl)silyl, di(i-propyl)silyl, di(n-hexyl)silyl, dicyclohexylsilyl, diphenylsilyl, cyclohexylphenylsilyl, t-butylcyclohexylsilyl, di(t-butylphenyl)silyl, di(p-tolyl)silyl and the corresponding moieties wherein the S1 atom is replaced by a Ge or a C atom, dimethylsilyl, diethylsilyl, dimethylgermyl and diethylgermyl [0072] In another embodiment, bridging group (A) may also be cyclic, comprising, for example 4 to 10, 5 to 7 nng members in a more particular embodiment The nng members may be selected from the elements mentioned above, from one or more of B, C, S1, Ge, N and O m a particular embodiment Non-limiting examples of nng structures which may be present as or part of the bridging moiety are cyclobutyhdene, cyclopentyhdene, cyclohexylidene, cycloheptylidene, cyclooctylidene and the corresponding nngs where one or two carbon atoms are replaced by at least one of S1, Ge, N and O, in particular, S1 and Ge The bonding arrangement between the nng and the Cp groups may be either cis-, trans-, or a combination [0073] The cyclic bndgmg groups (A) may be saturated or unsaturated and/or carry one or more substituents and/or be fused to one or more other nng structures If present, the one or more substituents are selected from the group consisting of hydrocarbyl (e g, alkyl such as methyl) and halogen (eg, F, CI) in one embodiment The one or more Cp groups which the above cyclic bridging moieties may optionally be fused to may be saturated or unsaturated and are selected from the group consisting of those having 4 to 10, more particularly 5, 6 or 7 nng members (selected from the group consisting of C, N, O and S in a particular embodiment) such as, for example, cyclopentyl, cyclohexyl and phenyl Moreover, these nng structures may themselves be fused such as, for example, in the case of a naphthyl group Moreover, these (optionally fused) nng structures may carry one or more substituents Illustrative, non-hmiting examples of these substituents are hydrocarbyl (particularly alkyl) groups and halogen atoms [0074] The hgands CpA and Cp8 of formulae (I) and (II) are different from each other in one embodiment, and the same in another embodiment [0075] In yet another aspect of the invention, the metallocene catalyst components include bridged mono-ligand metallocene compounds (eg, mono cyclopentadienyl catalyst components) In this embodiment, the at least one metallocene catalyst component is a bndged "half-sandwich" metallocene represented by the formula (III) (Formula Removed) wherein CpA is defined above and is bound to M, (A) is a bridging group bonded to Q and CpA, and wherein an atom from the Q group is bonded to M, and n is an integer 0, 1 or 2 In formula (III) above, CpA, (A) and Q may form a fused ring system The X groups and n of formula (III) are as defined above in formula (I) and (II) In one embodiment, CpA is selected from the group consisting of cyclopentadienyl, indenyl, tetrahydroindenyl, fluorenyl, substituted versions thereof, and combinations thereof [0076] In formula (III), Q is a heteroatom-contammg ligand in which the bonding atom (the atom that is bonded with the metal M) is selected from the group consisting of Group 15 atoms and Group 16 atoms in one embodiment, and selected from the group consisting of nitrogen, phosphorus, oxygen or sulfur atom in a more particular embodiment, and nitrogen and oxygen m yet a more particular embodiment Non-limiting examples of Q groups include alkylammes, arylamines, mercapto compounds, ethoxy compounds, carboxylates (e g, pivalate), carbamates, azenyl, azulene, pentalene, phosphoyl, phosphinimine, pyrrolyl, pyrozolyl, carbazolyl, borabenzene other compounds comprising Group 15 and Group 16 atoms capable of bonding with M [0077] In yet another aspect of the invention, the at least one metallocene catalyst component is an unbndged "half sandwich" metallocene represented by the formula (IVa) (Formula Removed) wherein CpA is defined as for the Cp groups in (I) and is a ligand that is bonded to M, each Q is independently bonded to M, X is a leaving group as described above in (I), n ranges from 0 to 3, and is 0 or 3 in one embodiment, q ranges from 0 to 3, and is 0 or 3 in one embodiment In one embodiment, CpA is selected from the group consisting of cyclopentadienyl, indenyl, tetrahydroindenyl, fluorenyl, substituted version thereof, and combinations thereof [0078] In formula (IVa), Q is selected from the group consisting of ROO", RO-, R(O)-, -NR-, -CR2-, -S-, -NR2, -CR3, -SR, -S1R3, -PR2, -H, and substituted and unsubstituted aryl groups, wherein R is selected from the group consisting of C1 to C6 alkyls, C6 to C12 aryls, Ci to C like Non-hmiting examples of Q include C1 to C12 carbamates, C1 to C12 carboxylates (eg, pivalate), C2 to C20 allyls, and C2 to C20 heteroallyl moieties [0079] Described another way, the "half sandwich" metallocenes above can be described as in formula (IVb), such as described in, for example, US 6,069,213 (Formula Removed) wherein M, CpA, X and n are as defined above, Q2GZ forms a polydentate ligand unit (e g , pivalate), wherein at least one of the Q groups form a bond with M, and is defined such that each Q is independently selected from the group consisting of -O-, —NR-, -CR2— and -S-, G is either carbon or silicon, and Z is selected from the group consisting of R, -OR, -NR2, -CR3, -SR, -S1R3, -PR2, and hydride, providing that when Q is -NR-, then Z is selected from the group consisting of -OR, -NR2, -SR, -S1R3, -PR2, and provided that neutral valency for Q is satisfied by Z, and wherein each R is independently selected from the group consisting of C1 to C10 heteroatom containing groups, C1 to C10 alkyls, C6 to C12 aryls, C6 to C12 alkylaryls, C1 to C10 alkoxys, and C6 to C12 aryloxys, n is 1 or 2 in a particular embodiment, and T is a bndging group selected from the group consisting of C1 to C10 alkylenes, C6 to C12 arylenes and C1 to C10 heteroatom containing groups, and C6 to C12 heterocyclic groups, wherein each T group bridges adjacent "CpAM(Q2GZ)Xn" groups, and is chemically bonded to the CpA groups m is an integer from 1 to 7, m is an integer from 2 to 6 in a more particular embodiment [0080] In another aspect of the invention, the at least one fluonded metallocene catalyst component can be described more particularly in structures (Va), (Vb), (Vc) and (Vd) (Formula Removed) wherem in structures (Va) to (Vd) M is selected from the group consisting of Group 3 to Group 12 atoms, and selected from the group consisting of Group 3 to Group 10 atoms m a more particular embodiment, and selected from the group consisting of Group 3 to Group 6 atoms in yet a more particular embodiment, and selected from the group consisting of Group 4 atoms in yet a more particular embodiment, and selected from the group consisting of Zr and Hf in yet a more particular embodiment, and is Zr in yet a more particular embodiment, wherein Q in (Va-i) and (Va-ii) is selected from the group consisting of halogen ions, alkyls, alkylenes, aryls, arylenes, alkoxys, aryloxys, amines, alkylammes, phosphines, alkylphosphines, substituted alkyls, substituted aryls, substituted alkoxys, substituted aryloxys, substituted amines, substituted alkylammes, substituted phosphines, substituted alkylphosphines, carbamates, heteroallyls, carboxylates (non-limiting examples of suitable carbamates and carboxylates include trimethylacetate, trimethylacetate, methylacetate, p-toluate, benzoate, diethylcarbamate, and dimethylcarbamate), fluonnated alkyls, fluonnated aryls, and fluonnated alkylcarboxylates, q is an integer ranging from 1 to 3, wherein each R is independently selected from the group consisting of hydrocarbyls and heteroatom-contaming hydrocarbyls in one embodiment, and selected from the group consisting of alkylenes, substituted alkylenes and heteroatom-containmg hydrocarbyls in another embodiment, and selected from the group consisting of C1 to C12 alkylenes, C1 to C12 substituted alkylenes, and C1 to C12 heteroatom-containmg hydrocarbons in a more particular embodiment, and selected from the group consisting of C1 to C4 alkylenes in yet a more particular embodiment, and wherein both R* groups are identical in another embodiment in structures (Vb-d), A is as descnbed above for (A) in structure (II), and more particularly, selected from the group consisting of -0-, -S-, -SO2-, -NR-, =S1R2, =GeR2, =SnR2, -R2S1S1R2- RP=, C1 to C12 alkylenes, substituted C1 to C12 alkylenes, divalent C4 to Ci2 cyclic hydrocarbons and substituted and unsubstituted aryl groups in one embodiment, and selected from the group consisting of C5 to C8 cyclic hydrocarbons, -CH2CH2-, =CR2 and =S1R2 in a more particular embodiment, wherein and R is selected from the group consisting of alkyls, cycloalkyls, aryls, alkoxys, fluoroalkyls and heteroatom-contaimng hydrocarbons in one embodiment, and R is selected from the group consisting of C1 to C6 alkyls, substituted phenyls, phenyl, and C1 to C6 alkoxys in a more particular embodiment, and R is selected from the group consisting of methoxy, methyl, phenoxy, and phenyl in yet a more particular embodiment, wherein A may be absent in yet another embodiment, in which case each R* is defined as for R'-R12, each X is as described above in (I), n is an integer from 0 to 4, and from 1 to 3 in another embodiment, and 1 or 2 in yet another embodiment, and R1 through R12 are independently selected from the group consisting of hydrogen radical, halogen radicals, C1 to C12 alkyls, C2 to C12 alkenyls, C6 to C12 aryls, C7 to C20 alkylaryls, C1 to C12 alkoxys, d to C12 fluoroalkyls, C6 to C12 fluoroaryls, and C1 to C12 heteroatom-contammg hydrocarbons and substituted derivatives thereof m one embodiment, selected from the group consisting of hydrogen radical, fluorine radical, chlonne radical, bromine radical, Q to Co alkyls, C2 to C(, alkenyls, C7 to C18 alkylaryls, C1 to C6 fluoroalkyls, C2 to C6 fluoroalkenyls, C7 to Cis fluoroalkylaryls m a more particular embodiment, and hydrogen radical, fluorine radical, chlonne radical, methyl, ethyl, propyl, isopropyl, butyl, isobutyl, tertiary butyl, hexyl, phenyl, 2,6-di-methylpheyl, and 4-tertiarybutylpheyl groups in yet a more particular embodiment, wherein adjacent R groups may form a ring, either saturated, partially saturated, or completely saturated [0081] The structuie of the metallocene catalyst component represented by (Va) may take on many forms such as disclosed in, for example, US 5,026,798, US 5,703,187, and US 5,747,406, including a dimer or oligomenc structure, such as disclosed in, for example, US 5,026,798 and US 6,069,213 [0082] In a particular embodiment of the metallocene represented in (Vd), R1 and R2 forin a conjugated 6-membered carbon ring systein that may or may not be substituted [0083] Non-limiting examples of metallocene catalyst components consistent with the description herein include cyclopentadienylzirconiuin Xn, indenylzirconiuin Xn, (l-methylindenyl)zirconiuin Xn, (2-methyhndenyl)zircomuin Xn, (l-propyhndenyl)zircomuin Xn, (2-propyhndenyl)zirconiuin Xn, (l-butyhndenyl)zircomuin Xn, (2-butyhndenyl)zirconiuin Xn, (methylcyclopentadienyl)zirconiumXn, tetrahydromdenylzirconiuin Xn, (pentamethylcyclopentadienyl)zirconmin Xn, cyclopentadienylzirconiuin Xn, pentamethylcyclopentadienyltitaniuin Xn, tetramethylcyclopentyltitaniuin Xn, 1,2,4-tnmethylcyclopentadienylzirconiuin X„, dimethylsilyl(l,2,3,4-tetramethylcyclopentadienyl)(cyclopentadienyl)zircomuin Xn, dimethylsilyl(l,2,3,4-tetramethylcyclopentadienyl)(l,2,3-mmethyl-cyclopentadienyl)zircomum Xn, dimethylsilyl(l,2,3,4-tetramethylcyclopentadienyl)(l,2-dimethyl-cyclopentadienyl)zirconmm Xn, dimethylsilyl(lJ2,3,4-tetramethyl-cyclopentadienyl)(2-methylcyclopentadienyl)zirconiumXn, dimethylsilyl(cyclopentadienyl)(indenyl)zircomuin Xn, dimethylsilyl(2-methyhndenyl)(fluorenyl)zirconiuin Xn, diphenylsilyl(l,2,3,4-tetramethyl-cyclopentadienyl)(3-propylcyclopentadienyl)zirconiuin Xn, dimethylsilyl (1,2,3,4-tetramethylcyC10pentadienyl) (3-t-butylcyclopentadienyl)zircomuin Xn, dimethylgermyl(l52-dimethylcyclopentadienyl)(3-isopropylcyclopentadienyl)zircomumXn, dimethylsilyl (1,2,3,4-tetramethyl-cyclopentadienyl)(3-methylcyclopentadienyl) zirconiuin Xn, diphenylmethyhdene(cyclopentadienyl)(9-fluorenyl)zirconiuin Xn, diphenylmethyhdene(cyclopentadienyl)(indenyl)zirconiuin Xn, ]so-propyhdenebis(cyclopentadienyl)zn coniuin Xn, iso-propyhdene(cyclopentadienyl)(9-fluorenyl)zirconiuin Xn, iso-propyhdene(3-methylcyclopentadienyl)(9-fluorenyl)zirconiumXn, ethylenebis(9-fluorenyl)zirconiuin Xn, meso-ethylenebis(l-indenyl)zirconiuin Xn, ethylenebis( 1 -indenyl)zirconiuin Xn, ethylenebis(2-methyl-1 -indenyl)zircoin urn Xn, ethylenebis(2-methyl-4,5,6,7-tetrahydro-l-indenyl)zirconmin Xn, ethylenebis(2-propyl-4,5,6,7-tetrahydro-l-indenyl)zircomuin Xn, ethylenebis(2-isopropyl-4,5,6,7-tetrahydro-l-indenyl)zirconiumXn, ethylenebis(2-butyl-4,5,6,7-tetrahydro-l -indenyl)zirconmin Xn, ethylenebis(2-isobutyl-4,5,6,7-tetrahydro-l-indenyl)zirconiumXn, dimethylsilyl(4,5,6,7-tetrahydro-l-indenyl)zircomumXn, diphenyl(4,5,6,7-tetrahydro-l-mdenyl)zirconiuin Xn, ethylenebis(4,5,6,7-tetrahydro-l -mdenyl)zirconiuin Xn, dimethylsilylbis(cyclopentadienyl)zircoruumXn, dimethyIsilyIbis(9-fluorenyl)zircomuin Xn, dimethylsilylbis(l -mdenyl)zirconiuin Xn, dimethylsilylbis(2-methyhndenyl)zirconiuin Xn, dimethylsilylbis(2-propylmdenyl)zirconmin Xn, dimethylsilylbis(2-butylindenyl)zircomuin Xn, diphenylsilylbis(2-methylindenyl)zircomumXn, diphenylsilylbis(2-propylindenyl)zircomuin Xn, diphenylsilylbis(2-butyhndenyl)zirconiumXn, dimethylgermylbis(2-methylindenyI)zircoiuuin Xn dimethylsilylbis(tetrahydroindenyl)zircoruuin X,„ dmiethylsilylbis(tetramethylcyC10pentadienyl)zircomurn Xn, dimethylsilyl(cyclopentadienyl)(9-fluorenyl)zirconiuin Xn, diphenylsdyl(cyclopentadienyl)(9-fluorenyl)zirconmmXn, diphenyIsilylbis(indenyl)zirconiuin Xn, cyclotnmethylenesilyl(tetramethylcyclopentadienyl)(cyclopentadienyl)zircoiuumXn, cyclotetramethylenesilyl(tetramethylcyclopentadienyl)(cyclopentadienyl) zircomuin Xn, cyclotnmethylenesilyl(tetramethylcyclopentadienyl)(2-methylindenyl)zircomumXn, cyclotnmethylenesilyl(tetiamethylcyclopentadienyl)(3-methylcyclopentadienyl)zircoruuin X, cyclotnmethylenesilylbis(2-methyhndenyl)zircomuin Xn, cyclotnmethylenesilyl(tetramethylcyclopentadienyl)(2,3,5- tnmethylcyclopentadienyl)zircomuin Xn, cyclotnmethylenesilylbis(tetiamethylcyclopentadienyl)zircomuin Xn, dimethylsilyl(tetramethylcyclopentadieneyl)(N-tert-butylamido)titaniuin Xn, bis(cyclopentadienyi)chiomiumXn, bis(cyclopentadienyl)zirconiuin Xn, bis(n-butylcyclopentadienyl)zirconiumXn, bis(n-dodecyclcyclopentadienyl)zirconiuin Xn, bis(ethylcyclopentadienyl)zircomumXn, bis(iso-butylcyclopentadienyl)zirconiuin Xn, bis(iso-propylcyclopentadienyl)zirconiuin Xn, bis(methylcyclopentadienyl)zircomumXn, bis(n-oxtylcyclopentadienyl)zirconiumXn, bis(n-pentylcyclopentadienyl)zirconiumXn, bis(n-propylcyclopentadienyl)zircomuin Xn, bis(tnmethylsilylcyclopentadienyl)zirconiuin Xn, bis(l,3-bis(tnmethy]silyl)cyclopentad]enyl)zirconiuin Xn, bis(l-ethyl-2-methylcyclopentadienyl)zirconiumXn, bis(l-ethyl-3-methylcyC10pentadienyl)zircomumXn, bis(pentamethylcyclopentadienyl)zircomuin Xn, bis(pentamethylcyclopentadienyl)zircomuin Xn, bis(l -propyl-3-methylcyclopentadienyl)zirconmin Xn, bis(l -n-butyl-3-methylcyclopentadienyl)zirconmin Xn, bis(l-isobutyl-3-methylcyclopentadienyl)zirconiumXn, bis(l -propyl-3-butylcyclopentadienyl)zircomuin Xn, bis( 1,3-n-butylcyclopentadienyl)zirconiura Xn, bis(4,7-dimethyhndenyl)zircomuin Xn, bis(indenyl)zircomuin Xn, bis(2-methyhndenyl)zirconiuin Xn, cyclopentadienylmdenylzirconiumXn, bis(n-propylcyclopentadienyl)hafruuin Xn, bis(n-butylcyclopentadienyl)hafhiumXn, bis(n-pentylcyclopentadienyl)hafniumXn, (n-propyl cyclopentadienyl)(n-butyl cyclopentadienyl)hafaiuin Xn, bis[(2-tnmethylsilylethyl)cyclopentadienyl]hafiiiuin Xn, bis(tnmethylsilyl cyclopentadienyl)hdfhiuin Xn, bis(2-n-propyhndenyl)hafniuin Xn, bis(2-n-butylindenyl)hafniuin Xn, dimethylsilylbis(n-propylcyc]opentadienyl)hafhiuin Xn, dimethylsilylbis(n-butylcyclopentadienyl)hafoiumXn, bis(9-n-propylfluorenyl)hafmuin Xn, bis(9-n-butylfluorenyl)hafmumXn, (9-n-propylfluorenyl)(2-n-propyhndenyl)hafhiumXn, bis(l-n-propyl-2-methylcyclopentadienyl)haftiiumXn, (n-propylcyclopentadienyl)(l-n-propyl-3-n-butylcyclopentadienyl)hafhmin Xn, dimethylsilyl(tetramethylcyclopentadienyl)(cyclopropylamido)titaniuin Xn, dimethylsilyl(tetramethyleyclopentadienyl)(cyclobutylamido)titaniumXn, dimethylsi]yl(tetramethyleyclopentadienyl)(cyclopentylamido)titanmin Xn, dimethylsilyl(tetramethylcyclopentadienyl)(cyclohexylamido)titaniuin Xn, dimethylsilyl(tetramethylcyclopentadienyl)(cycloheptylamido)titaniuin Xn, dimethylsilyl(tetramethylcyc!opentadienyI)(cyclooctylamido)titaniuin Xn, dimethylsilyI(tetramethylcyclopentadienyl)(cyclononylamido)titanmmXn, dimethylsilyl(tetramethylcyclopentadienyl)(cyclodecylamido)titaniuin Xn, dimethylsilyl(tetramethylcyclopentadienyl)(cycloundecylamido)titaniuin Xn, dimethylsilyl(tetramethylcyclopentadienyl)(cyc]ododecylamido)titanjuin Xn, dimethylsilyl(tetramethylcyclopentadienyl)(sec-butylamido)titamuin Xn, dimethylsilyl(tetramethylcyclopentadienyl)(n-octylamido)titaniuin Xn, dimethylsilyl(tetramethylcyclopentadienyl)(n-decylarrndo)titamuin Xn, dimethylsilyl(tetramethyIcyclopentadienyl)(n-octadecylamido)titaniuin Xn, methylphenylsilyl(tetramethylcyclopentadienyl)(cyclopropylamido)titaniumXn, methylphenylsilyl(tetramethylcyclopentadienyl)(cyclobutylamido)titamuin Xn, methylphenylsilyl(tetramethylcyclopentadienyl)(cyclopentylamido)titaniuin Xn, methylphenylsilyl(tetramethylcyclopentad]enyl)(cyclohexylamido)titaniuin Xn, methylphenylsilyl(tetramethylcyclopentadienyl)(cyclohepty]am3do)titamuin Xn, methylphenylsilyl(tetramethylcyclopentadienyl)(cyclooctylamido)titamumXn, methylphenylsilyl(tetramethylcyclopentadienyl)(cyC10nonylanndo)titaruuin Xn, methylphenylsilyl(tetramethylcyC10pentadienyl)(cyC10decylamido)titanium, Xn, methylphenylsilyl(tetramethylcyclopentadienyl)(cycloundecylamido)titaniumXn, methylphenylsilyl(tetramethylcyclopentadienyl)(cyclododecylamido)titaniumXn, methylphenylsilyl(tetramethylcyclopentadienyl)(sec-butylamido)titaniumXn, methylphenylsilyl(tetramethylcyclopentadieny])(n-octylaniido)titaniumXn, methylphenylsilyl(tetramethylcyclopentadienyl)(n-decylamido)titamumXn, methylphenylsilyl(tetramethylcyclopentadienyl)(n-octadecylamido)titaniumXn, diphenylsilyl(tetramethylcyclopentadienyl)(cyclopropylamido)titaniumXn, diphenylsilyl(tetramethylcyclopentadienyl)(cyclobutyIamido)titamuin Xn, diphenylsilyl(tetramethylcyclopentadienyl)(cyclopentylamido)titaniumXn, diphenylsilyl(tetramethylcyclopentadienyl)(cyclohexylamido)titamuin Xn, diphenylsilyl(tetramethylcyclopentadienyl)(cycloheptylamido)titaniuin Xn, diphenylsilyl(tetramethylcyclopentadienyl)(cyclooctylamido)titaniumXn, diphenylsilyl(tetramethylcyclopentadienyl)(cyclononylamido)titaniuin Xn, diphenylsilyl(tetramethylcyclopentadienyl)(cyclodecylamido)titamuin Xn, diphenylsilyl(tetramethylcyclopentadienyl)(cycloundecylamido)titanmin Xn, diphenylsilyl(tetramethylcyclopentadienyl)(cyclododecylamido)titanmin Xn, diphenylsilyl(tetramethylcyclopentadienyl)(sec-butylamido)titarnuin Xn, diphenylsilyl(tetramethyleyclopentadienyl)(n-octylamido)titanmmXn, diphenylsilyl(tetramethyleyclopentadienyl)(n-decylamido)titanmin Xn, diphenylsilyl(tetramethylcyclopentadienyl)(n-octadecylamido)titaniuin Xn, and denvatives thereof [0084] Wherein the value of n is 1, 2 or 3, and at least one X is a fluoride ion By "derivatives thereof, it is meant any substitution or ring formation as described above foi structures (Va-d) in one embodiment, and in particular, replacement of the metal "M" (Cr, Zr, Ti or Hf) with an atoin selected fi-oin the group consisting of Cr, Zr, Hf and T1, and replacement of the "X" group with any of C1 to C5 alkyls, C6 aryls, C6 to C10 alkylaryls, fluonne, chlorine, or bromine In a particular embodiment, each of the above metallocenes is a fluonded metallocene wherein one or more of the X groups is a fluoride, and all X gioups aie fluorides in yet a more particular embodiment [0085] More particularly, non-limiting examples of the fluonded catalyst components useful in the method of the invention are as follows Bis(methylcyclopentadienyl)zirconiuin difluonde, Bis(ethylcyclopentadienyl)zirconiumdifluonde, Bis(propylcyclopentadienyl)zirconiuin difluonde, Bis(isopropylcyclopentadienyl)zircomuin difluonde, Bis(butylcyclopentadienyl)zircomuin difluonde, Bis(isobutylcyclopentadienyl)zircoruuin difluonde, Bis(neopentylcyclopentadienyl)zirconiuin difluonde, Bis(cyclopentylcyclopentadienyl)zirconiuin difluonde, Bis(cyclohexylmethylcyclopentadienyl)zirconiuin difluonde, Bis(allylcyclopentadienyl)zirconiuin difluonde, Bis((3-butenyl)cyclopentadienyl)zircomuin difluonde, Bis(tnmethylsilylcyclopentadienyl)zircomuin difluonde, Bis(tnmethy]germylcyclopentadienyl)z]rconiuin difluonde, Bis(tnmethylsilylmethylcyclopentadienyl)zirconiuin difluonde, Bis(l,2-dimethylcyclopentadienyl)zircomuin difluonde, Bis(l,3-dimethylcyclopentadienyl)zirconiuin difluonde, Bis(l,2,3-tnmethylcyclopentadienyI)zircoruuin difluonde, Bis(l,2,4-tnmethylcyclopentadienyl)zircomuin difluonde, Bis(tetramethylcyclopentadienyl)zirconiuin difluonde, Bis( 1,3-methylethylcyclopentadienyl)zirconiuin difluonde, Bis(l,3-methylpropylcyclopentadienyl)zirconiuin difluonde, Bis(l ,3-methylbutylcyclopentadienyl)zirconiura difluonde, Bis(phenylcyclopentadienyl)zircoruuin difluonde, Bis(l,3-methyIphenyIcyC10pentadienyI)zircomuin difluonde, Bis(benzylcyclopentadienyl)zircoruuin difluonde, Bis(l,3-methylbenzylcyclopentadienyl)zirconiuin difluonde, Bis(phenethylcyclopentadienyl)zircoruuin difluonde, Bis((3-phenylpropyl)cyclopentadienyl)zircoruuin difluonde, (Tetramethylcylopentadienyl)(propylcyclopentadienyl)zirconiuin difluonde, (Pentamethylcylopentadienyl)(propylcyclopentadienyl)zirconiuin difluonde, CyclopentadienyI(propylcyC10pentadienyl)zircomuin difluonde, Cyclopentadienyl(butylcyclopentadienyl)zirconiuin difluonde, Cyclopentadienyl(cyclopentylcyclopentadienyl)zircomuin difluonde, Cyclopentadienyl (tetrahydroindenyl)zircomuin difluonde, Cyclopentadienyl(l,3-methylbutylcyclopentadienyl)zircomuin difluonde, Cyclopentadienyl(tetramethylcyclopentadienyl)zircomuin difluonde, Cyclopentadienyl(propyltetramethylcyclopentadienyl)zircotuuin difluonde, Cyclopentadienyl(butyItetramethylcyclopentadienyI)zircomuin difluonde, Cyclopentadienyl(cyclopentyltetramethylcyclopentadienyl)zircoinuin difluonde, Cyclopentadienyl(indenyl)zircomuin difluonde, Cyclopentadienyl(l-methyhndenyl)zirconiuin difluonde, Cyclopentadienyl(fluorenyl)zirconiuin difluonde, Cyclopentadienyl(tetrahydrofluorenyl)zircomuin difluonde, Cyclopentadienyl(octahydrofluorenyl)zirconiuin difluoi ide, Bis(tetrahydroindenyI)zirconmin difluonde, Bis(trihydropentalenyl)zircomuin difluonde, Bis(pentahydroazulenyl)zirconiuin difluonde, Dimethylsilylbis(tetrahydroindenyl)zircomuin difluonde, Ethylenebis(tetrahydromdenyl)zirconiuin difluonde, Bis(indenyl)zircomuin difluonde, Bis(l-methyhndenyl)zirconiuin difluonde, Bis(2-methyhndenyl)zirconiuin difluonde, Bis(4,7-dimethylindenyl)zirconiuin difluonde, Bis(5,6-dimethylmdenyl)zirconiuin difluonde, Bis(l-phenyhndenyl)zirconiuin difluonde, Bis(2-phenylindenyl)zircomuin difluonde, Bis(fluorenyl)zircomuin difluonde, Bis(l-methylfluorenyl)zirconiuin difluonde, Bis(2,7-di-t-butylfluorenyl)zirconiuin difluonde, Dimethylsilylbis(3-methylcyclopentadienyl)zircoruuin difluonde, Dimethylsilylbis(3-propylcyclopentadienyl)zirconmin difluonde, Dimethylsilylbis(2,4-dimethylcyclopentadienyl)zirconiuin difluonde, Dimethylsilylbis(2,3,5-tnmethylcyclopentadienyl)zirconmin difluonde, Dimethylsilylbis(tetramethylcyclopentadienyl)zirconiuin difluonde, Dimethylsilylbis(indenyl)zirconmin difluonde, Dimethylsilylbis(2-methylmdenyI)zirconiuin difluonde, Dimethylsilylbis(2-methyl-4-phenylindenyl)zirconiuin difluonde, Dimethylsilylbis(2-methyl-4-(3,5-di-t-butyl)phenylmdenyl)zirconiuin difluonde, Dimethylsilylbis(2-methyl-4-naphthyhndenyl)zirconiuin difluonde, Dimethylsilyl(cyclopentadienyl)(indenyl)zirconiuin difluonde, Dimethylsilyl(tetramethylcyclopentadienyl)(indenyl)zirconiuin difluonde, Silacyclobutyl(tetramethylcyclopentadienyl)(indenyl)zirconiuin difluonde, SiIacyclopentyl(tetramethylcyclopentadienyl)(indenyl)zirconiuin difluonde, Ethylenebis(mdenyl)zircoruuin difluonde, Ethylenebis(2-methyhndenyI)zirconiuin difluonde, Isopropyhdene(cyclopentadienyl)(fluorenyl)zircomuin difluonde, Diphenylmethyhdene(cyclopentadienyl)(fluoienyl)zirconiuin difluonde, Dimethylsilyl(cyclopentadienyl)(fluorenyl)zirconiuin difluonde, Diphenylsilyl(cyclopentadienyl)(fluorenyl)zirconiuin difluonde, Dimethylsilylbis(fluorenyl)zircomuin difluonde, Ethylenebis(fluorenyl)zircoruuin difluonde, Bis(methyIcyclopentadienyl)hafhiuin difluonde, Bis(ethylcyclopentadienyl)hafhiuin difluonde, Bis(propylcyclopentadienyl)hafruuin difluonde, Bis(butylcyclopentadienyl)hafniuin difluonde, Bis(isobutylcyclopentadienyl)hafhiuin difluonde, Bis(neopentylcyclopentadienyl)hafhiuin difluonde, Bis(cyclopentylcyclopentadienyl)hafniuin difluonde, Bis(ally]cyclopentadienyl)hafmuin difluonde, Bis((3-butenyl)cyclopentadienyl)hafhiuin difluonde, Bis(cyclohexylmethylcyclopentadienyl)hafhiuin difluonde, Bis(tnmethylsilylmethylcyclopentadienyl)hafruuin difluonde, Bis((3-phenylpropyl)cyclopentadienyl)hafhiuin difluonde, Bis( 1,3-methylbutylcyclopentadienyl)hafhiuin difluonde, Bis(l,3-methylpropylcyclopentadienyl)hafhiuin difluonde, Ethylenebis(indenyl)hafniuin difluonde, Dimethylsilylbis(3-propylcyclopentadienyl)hafhiuin difluonde, Dimethylsilylbis(2,4-methylpropylcyclopentadienyl)hafniuin difluonde, Dimethylsilylbis(tetramethylcyclopentadienyl)hafmuin difluonde, Dimethylsilylbis(indenyl)hafhiuin difluonde, Diphenylsilylbis(indenyl)hafmuin difluonde, Bis(cyclopentadienyl)titamuin difluonde, Bis(methylcyclopentadienyl)titaniuin difluonde, Bis(ethylcyclopentadienyl)titaniuin difluonde, Bis(propylcyclopentadienyl)titamuin difluonde, Bis(butylcyclopentadienyl)titanmin difluonde, Bis(isobutylcyclopentadienyl)titaniuin difluonde, Bis(neopentylcyclopentadienyl)titaniuin difluonde, Bis(cyclopentylcyclopentadienyl)titaniuin difluonde, Ethylenebis(mdenyl)titamumdifluonde, Dimethylsilylbis(mdenyl)titanmin difluonde, Diphenylsilyl(cyclopentadienyl)(fiuorenyl)titaniuin difluonde, (cyclopentadienyl)zirconium tnfiuonde, (lndenyl)zirconmin tnfiuonde, (1 -methyhndenyI)zirconiuin tnfiuonde, (2-methylindenyl)zircomuin tnfiuonde, (l-propylmdenyl)zirconiuin tnfiuonde, (2-propyhndenyl)zirconiuin tnfiuonde, (1 -butyhndenyl)zirconiuin tnfiuonde, (2-butyhndenyl)zirconiuin tnfiuonde, (methylcyclopentadienyJ)zircomuin tnfiuonde, (tetrahydroindenyl)zircomuin tnfiuonde, (pentamethylcyclopentadienyl)zircoruuin tnfiuonde, (cyclopentadienyl)zirconiuin tnfiuonde, pentamethylcyclopentadienyltitamuin tnfiuonde, tetramethylcyclopentyldienyltitaniuin tnfiuonde, 1,2,4-tnmethylcyclopentadienylzirconmin tnfiuonde, and mixtures thereof [0086] It is contemplated that the metallocene catalysts components described above include their structural or optical or enantiomenc isomers (racemic mixture), and may be a pure enantiomer in one embodiment [0087] As used herein, a single, bndged, asymmetncally substituted metallocene catalyst component having a racemic and/or meso isomer does not, itself, constitute at least two different bndged, metallocene catalyst components [0088] The "metallocene catalyst component" useful in the present invention may comprise any combination of any "embodiment" described herein [0089] When combined to forin the bimetallic catalyst component, the molar ratio of ' metal froin the first catalyst component to the second catalyst component (e g, molar ratio of Ti Zr) is a value of froin 0 1 to 20 in one embodiment, and froin 1 to 18 in another embodiment, and froin 2 to 15 in yet another embodiment, and froin 3 to 12 in yet another embodiment, and froin 4 to 10 in yet another embodiment, and froin 4 to 8 in yet another embodiment, wherein a desirable molar ratio of first catalyst component metal second catalyst component metal is any combination of any upper limit with any lower limit descnbed herein Activator [0090] As used herein, the terin "activator" is defined to be any compound or combination of compounds, supported or unsupported, which can activate a catalyst compound (eg, Ziegler-Natta, metallocenes, Group 15-containing catalysts, etc), such as by creating a cationic species froin the catalyst component Typically, this involves the abstraction of at least one leaving group (X group in the formulas/structures above) froin the metal center of the catalyst component The catalyst components of the present invention are thus activated towards olefin polymerization using such activators Embodiments of such activators include Lewis acids such as cyclic or ohgomenc poly(hydrocarbylalummuin oxides), alkylaluminuin compounds and so called non-coordinating ionic activators ("NCA") (alternately, "ionizing activators" or "stoichiometric activators"), or any other compound that can convert a neutral metallocene catalyst component to a metallocene cation that is active with respect to olefin polymerization [0091J More particularly, it is within the scope of this invention to use Lewis acids such as alumoxane (eg, "MAO"), modified alumoxane (eg, "TfBAO"), and alkylaluminuin compounds as activators, and/or ionizing activators (neutral or ionic) such as tn (n-butyl)ammomuin tetrakis(pcntafluorophenyl)boron and/or a tnsperfluorophenyl boron metalloid precursors to activate desirable metallocenes described herein MAO and other aluminum-based activators are well known in the art Ionizing activators are well known in the art and are descnbed by, for example, Eugene You-Xian Chen & Tobin J Marks, Cocatalysts for Metal-Catalyzed Olefin Polymerization Activators, Activation Processes, and Structure-Activity Relationships 100(4) CHEMICAL REVIEWS 1391-1434 (2000) The activators may be associated with or bound to a support, either in association with the catalyst component (eg, metallocene) or separate froin the catalyst component, such as descnbed by Gregory G Hlatky, Heterogeneous Single-Site Catalysts for Olefin Polymerization 100(4) CHEMICAL REVIEWS 1347-1374(2000) [0092] Non-limiting examples of aluminuin alkyl compounds which may be utilized as activators for the catalyst precursor compounds for use in the methods of the present invention include tnmethylalummum, tnethylalummum, trnsobutylaluminum, tn-n-hexylalummum, tn-n-octylalummuin and the like [0093] Examples of neutral ionizing activators include Group 13 tn-substituted compounds, in particular, tn-substituted boron, tellurium, aluminum, galliuin and indiuin compounds, and mixtures thereof The three substituent groups are each independently selected froin the group consisting of alkyls, alkenyls, halogen, substituted alkyls, aryls, arylhahdes, alkoxy and halides In one embodiment, the three groups are independently selected froin the group consisting of halogen, mono or multicyclic (including halosubstituted) aryls, alkyls, and alkenyl compounds and mixtures thereof In another embodiment, the three groups are selected froin the group consisting of alkenyl groups having 1 to 20 carbon atoms, alkyl groups having 1 to 20 carbon atoms, alkoxy groups having 1 to 20 carbon atoms and aryl groups having 3 to 20 carbon atoms (including substituted aryls), and combinations thereof In yet another embodiment, the three groups are selected froin the group consisting of alkyls having 1 to 4 carbon groups, phenyl, naphthyl and mixtures thereof In yet another embodiment, the three groups are selected froin the group consisting of highly halogenated alkyls having 1 to 4 carbon groups, highly halogenated phenyls, and highly halogenated naphthyls and mixtures thereof By "highly halogenated", it is meant that at least 50% of the hydrogens are replaced by a halogen group selected froin the group consisting of fluorine, chlorine and bromine In yet another embodiment, the neutral stoichiometric activator is a tn-substituted Group 13 compound comprising highly fluonded aryl groups, the groups being highly fluonded phenyl and highly fluonded naphthyl groups [0094] In another embodiment, the neutral tn-substituted Group 13 compounds are boron compounds such as a tnsperfluorophenyl boron, tnsperfluoronaphthyl boron, tns(3,5-di(tnfluorornethyl)phenyi)boron, tns(di-t-butylmethylsilyl)perfluorophenylboron, and other highly fluonnated trisarylboron compounds and combinations thereof, and their aluminuin equivalents Other suitable neutral ionizing activators are described in US 6,399,532 Bl, US 6,268,445 Bl, and in 19 ORGANOMETALLICS 3332-3337 (2000), and in 17 ORGANOMETALLICS 3996-4003 (1998) [0095] Illustrative, not limiting examples of ionic ionizing activators include tnalkyl- substituted ammoniuin salts such as tnethylammoniuin tetra(phenyl)boron, tnpropylammoniuin tetra(phenyl)boron, tn(n-butyl)amrnomuin tetra(phenyl)boron, tnmethylammoniuin tetra(p- tolyI)boron, tnmethylammomum tetra(o-tolyl)boron, tnbutylammonium tetra(pentafluorophenyl)boron, tnpropylammonium tetra(o,p-dimethyIphenyl)boron, tnbutylammoniuin tetra(m,m-dimethylphenyl)boron, tnbutylammoniuin tetra(p-tn- fluoromethylphenyl)boron, tnbutylammomuin tetra(pentafluorophenyl)boron, tn(n- butyl)ammoniuin tetra(o-tolyl)boron and the hke, N,N-dialkyl arulimuin salts such as N,N- dimethylanihniuin tetra(phenyl)boron, N,N-diethylamhniuin tetra(phenyl)boron, N,N-2,4,6- pentamethylanihruuin tetra(phenyl)boron and the like, dialkyl ammoniuin salts such as di- (isopropyl)ammonium tetra(pentafluorophenyl)boron, dicyclohexylammonium tetra(phenyl)boron and the like, and tnaryl phosphoniuin salts such as tnphenylphosphoniuin tetra(phenyl)boron, tn(methylphenyl)phosphomum tetra(phenyl)boron, tn(dimethylphenyl)phosphonmin tetra(phenyl)boron and the hke, and their aluminuin equivalents [0096] In yet another embodiment of the activator of the invention, an alkylaluminum can be used in conjunction with a heterocyclic compound The nng of the heterocyclic compound may includes at least one nitrogen, oxygen, and/or sulfur atom, and includes at least one nitrogen atoin in one embodiment The heterocyclic compound includes 4 or more nng members in one embodiment, and 5 or more ring members in another embodiment [0097] The heterocyclic compound for use as an activator with an alkylaluminuin may be unsubstituted or substituted with one or a combination of substituent groups Examples of suitable substituents include halogen, alkyl, alkenyl or alkynyl radicals, cycloalkyl radicals, aryl radicals, aryl substituted alkyl radicals, acyl radicals, aroyl radicals, alkoxy radicals, aryloxy radicals, alkylthio radicals, dialkylamino radicals, alkoxycarbonyl radicals, aryloxycarbonyl radicals, carbomoyl radicals, alkyl- or dialkyl- carbamoyl radicals, acyloxy radicals, acylamino radicals, aroylamino radicals, straight, branched or cyclic, alkylene radicals, or any combination thereof The substituents groups may also be substituted with halogens, particularly fluorine or bromine, or heteroatoms or the like [0098] Non-limiting examples of hydrocarbon substituents include methyl, ethyl, propyl, butyl, pentyl, hexyl, cyclopentyl, cyclohexyl, benzyl or phenyl groups and the like, including all their isomers, for example tertiary butyl, isopropyl, and the like Other examples of substituents include fluoromethyl, fluoroethyl, difluoroethyl, lodopropyl, bromohexyl or chlorobenzyl [0100] In one embodiment, the heterocyclic compound is unsubstituted In another embodiment one or more positions on the heterocyclic compound are substituted with a halogen atoin or a halogen atoin containing group, for example a halogenated aryl group In one embodiment the halogen is selected froin the group consisting of chlorine, bromine and fluorine, and selected froin the group consisting of fluorine and bromine in another embodiment, and the halogen is fluorine in yet another embodiment [0101] Non-limiting examples of heterocyclic compounds utilized in the activator of the invention include substituted and unsubstituted pyrroles, imidazoles, pyrazoles, pyrrolines, pyrrolidines, punnes, carbazoles, and indoles, phenyl indoles, 2,5,-dimethylpyrroles, 3-pentafluorophenylpyrrole, 4,5,6,7-tetrafluoromdole or 3,4-difluoropyrroles [0102] In one embodiment, the heterocyclic compound described above is combined with an alkyl aluminuin or an alumoxane to yield an activator compound which, upon reaction with a catalyst component, for example a metallocene, produces an active polymerization catalyst Non-limiting examples of alkylaluminums include tnmethylaluminum, tnethylaluminum, tnisobutylaluminum, tn-n-hexylaluminum, tn-n-octylalummum, tn-iso-octylalummum, tnphenylaluminum, and combinations thereof [0103] Other activators include those described in WO 98/07515 such as tns (2, 2', 2"- nonafluorobiphenyl) fluoroalummate Combinations of activators are also contemplated by the invention, for example, alumoxanes and ionizing activators in combinations Other activators include aluminum/boron complexes, perchlorates, penodates and lodates including their hydrates, lithiuin (2,2'-bisphenyl-ditnmethylsihcate) 4THF, silyhuin salts in combination with a non-coordinating compatible anion Also, methods of activation such as using radiation, electro-chemical oxidation, and the like are also contemplated as activating methods for the purposes of rendenng the neutral metallocene-type catalyst compound or precursor to a metallocene-type cation capable of polymenzmg olefins Other activators or methods for activating a metallocene-type catalyst compound are described in for example, US 5,849,852, 5,859,653 and 5,869,723 and WO 98/32775 [0104] In general, the activator and catalyst component(s) are combined in mole ratios of activator to catalyst component froin 1000 1 to 0 1 1 in one embodiment, and froin 300 1 to 1 1 in a more particular embodiment, and froin 150 1 to 11 in yet a more particular embodiment, and froin 50 1 to 1 1 in yet a more particular embodiment, and froin 10 1 to 0 5 1 in yet a more particular embodiment, and froin 3 1 to 0 3 1 in yet a more particular embodiment, wherein a desirable range may include any combination of any upper mole ratio limit with any lower mole ratio limit descnbed herein When the activator is a cyclic or oligomenc poly(hydrocarbylalummuin oxide) {e g, "MAO"), the mole ratio of activator to catalyst component ranges froin 2 1 to 100,000 1 in one embodiment, and froin 10 1 to 10,000 1 in another embodiment, and froin 50 1 to 2,000 I in a more particular embodiment When the activator is a neutral or ionic ionizing activator such as a boion alkyl and the ionic salt of a boron alkyl, the mole ratio of activator to catalyst component ianges froin 0 5 1 to 10 1 in one embodiment, and froin 1 1 to 5 1 in yet a more particular embodiment [0105] More particularly, the molar ratio of Al/metallocene-metal (Al froin MAO) ranges froin 40 to 500 in one embodiment, and ranges froin 50 to 400 in another embodiment, and ranges froin 60 to 300 in yet another embodiment, and ranges froin 70 to 200 in yet another embodiment, and ranges froin 80 to 175 in yet another embodiment, and ranges froin 90 to 125 in yet another embodiment, wherein a desirable molar ratio of Al(MAO) to metallocene-metal "M" can be any combination of any upper limit with any lower limit descnbed herein Supports [0106] A support may also be present as part of the bimetallic catalyst systein of the invention Supports, methods of supporting, modifying, and activating supports for single-site catalyst such as metallocenes is discussed in, for example, 1 METALLOCENE-BASED POLYOLEFINS 173-218 (J Scheirs & W Kaminsky eds , John Wiley & Sons, Ltd 2000) The terms "support" or "earner", as used herein, are used interchangeably and refer to any support matenal, a porous support matenal in one embodiment, including inorganic or organic support materials Non-limiting examples of support materials include inorganic oxides and inorganic chlorides, and in particular such materials as talc, clay, silica, alumina, magnesia, zircoma, iron oxides, bona, calciuin oxide, zinc oxide, banuin oxide, thoria, aluminuin phosphate gel, glass beads, and polymers such as polyvinylchlonde and substituted polystyrene, functionalized or crosshnked organic supports such as polystyrene divmyl benzene polyolefins or polymenc compounds, and mixtures thereof, and graphite, in any of its various forms {0107] The support may be contacted with the other components of the catalyst system in any number of ways In one embodiment, the support is contacted with the activator to form an association between the activator and support, or a "bound activator" In another embodiment, the catalyst component may be contacted with the support to forin a "bound catalyst component" In yet another embodiment, the support may be contacted with the activator and catalyst component together, or with each partially in any order The components may be contacted by any suitable means as in a solution, slurry, or solid form, or some combination thereof, and may be heated to any desuable temperature to effectuate a desirable chemical/physical transformation [0108] Desirable earners are inorganic oxides that include Group 2, 3, 4, 5, 13 and 14 oxides and chlondes in one embodiment, and more particularly, inoiganic oxides and chlorides of Group 13 and 14 atoms Yet more particularly, support materials include silica, alumina, silica-alumina, magnesiuin chlonde, graphite, and mixtures thereof Other useful supports include magnesia, titania, zircoma, montmonllonite (EP 0 511 665 Bl), phyllosilicate, and the like Also, combinations of these support matenals may be used, for example, sihca-chromium, silica-alumina, silica-titania and the like Additional support matenals may include those porous acrylic polymers desenbed in EP 0 767 184 B1 [0109] In one aspect of the support useful in the invention, the support possess a surface area in the range of froin 10 to 700 m2/g, pore volume in the range of froin 0 1 to 4 0 cm3/g and average particle size in the range of froin 5 to 500 urn In another embodiment, the surface area of the earner is in the range of froin 50 to 500 m2/g, pore volume of froin 0 5 to 3 5 cm3/g and average particle size of froin 10 to 200 uin In yet another embodiment, the surface area of the earner is in the range is froin 100 to 400 m2/g, pore volume froin 0 8 to 3 0 cin /g and average particle size is froin 5 to 100 uin The average pore size of the earner of the invention typically has pore size in the range of froin 10 to 1000A, froin 50 to 500A in another embodiment, and froin 75 to 350A in yet another embodiment [0110] In one embodiment of the support, graphite is used as the support The graphite is a powder in one embodiment In another embodiment, the graphite is flake graphite In another embodiment, the graphite and has a particle size of froin 1 to 500 microns, froin 1 to 400 microns in another embodiment, and froin 1 to 200 in yet another embodiment, and froin 1 to 100 microns in yet another embodiment [0111] Dehydration or calcining of the support may or may also be earned out In one embodiment, the support is calcined pnor to reaction with the fluonne or other support-modifying compound In another embodiment, the support is calcined and used without further modification, or calcined, followed by contacting with one or more activators and/or catalyst components Suitable calcining temperatures range froin 100°C to 1500°C in one embodiment, and froin 200°C to 1200°C in another embodiment, and froin 300°C to 1000°C in another embodiment, and froin 350°C to 900°C in yet another embodiment, and froin 400°C to 850°C in yet a more particular embodiment, and froin 800°C to 900°C in yet a more particular embodiment, and froin 810°C to 890°C in yet a more particular embodiment, wherein a desirable range compnses any combination of any upper temperature limit with any lower temperature limit Calcining may take place in the absence of oxygen and moisture by using, for example, an atmosphere of dry nitrogen [0112] The support, especially an inorganic support or graphite support, may be pretreated such as by a halogenation process or other suitable process that, for example, associates a chemical species with the support either through chemical bonding, ionic interactions, or other physical or chemical interaction In one embodiment, the support is fluonded The fluonne compounds suitable for providing fluorine for the support are desirably inorganic fluonne containing compounds Such inorganic fluorine containing compounds may be any compound containing a fluonne atoin as long as it does not contain a carbon atoin Particularly desirable are inorganic fluonne containing compounds selected froin the group consistmg of NH4BF4, (NH4)2S1F6, NH+PFo, NH4F, (NH4)2TaF7, NH4NbF4, (NH4)2GeF6, (NH4)2SmF6, (NH4)2T1F6, (NH4)2ZrF6, MoF6, ReF6, GaF3, S02C1F, F2, SiF4, SF6, C1F3, C1F5, BrF5, IF7, NF3, HF, BF3, NHF2 and NH4HF2 [0113] A desirable method of treating the support with the fluorine compound is to dry mix the two components by blending at a concentration of froin 0 01 to 10 0 millimole F/g of support in one embodiment, and in the range of froin 0 05 to 6 0 millimole F/g of support in another embodiment, and in the range of froin 0 1 to 3 0 millimole F/g of support in yet another embodiment The fluonne compound can be dry mixed with the support either before or after charging to the vessel for dehydration or calcining the support Accordingly, the fluonne concentration present on the support is in the range of froin 0 2 to 5 wt% in one embodiment, and froin 0 6 to 3 5 wt% of support in another embodiment [0114] Another method of treating the support with the fluonne compound is to dissolve the fluonne in a solvent, such as water, and then contact the support with the fluonne containing solution When water is used and silica is the support, it is desirable to use a quantity of water that is less than the total pore volume of the support Desirably, the support and, for example, fluonne compounds are contacted by any suitable means such as by dry mixing or slurry mixing at a temperature of froin 100°C to 1000°C in one embodiment, and froin 200°C to 800°C in another embodiment, and froin 300°C to 600°C in yet another embodiment, the contacting in any case taking place for between two to eight hours [0115] It is within the scope of the present invention to co-contact (or "co-immobilize") more than one catalyst component with a support Non-limiting examples of co-lmmobihzation of catalyst components include two or more of the same or different metallocene catalyst components, one or more metallocene with a Ziegler-Natta type catalyst, one or more metallocene with a chromiuin or "Phillips" type catalyst, one or more metallocenes with a Group 15 containing catalyst, and any of these combinations with one or more activators More particularly, co-supported combinations include metallocene A/metallocene A, metallocene A/metallocene B, metallocene/Ziegler Natta, metallocene/Group 15 containing catalyst, metallocene/chromiuin catalyst, metallocene/Ziegler Natta/Group 15- containing catalyst, metallocene/chromiuin catalyst/Group 15 containing catalyst, any of the these with an activator, and combinations thereof [0116] Further, the catalyst systein of the present invention can include any combination of activators and catalyst components, either supported or not supported, in any number of ways For example, the catalyst component may include any one or both of metallocenes and/or Group 15-containing catalysts components (eg, US 6,265,505, US 5,707,913, EP 0 893 454, and WO 99/01460), and may mclude any combination of activators, any of which may be supported by any number of supports as described herein Non-limiting examples of catalyst systein combinations useful in the present invention include MN + NCA, MN S + NCA, NCA S + MN, MN NCA S, MN + A1A, MN S + A1A, ALVS + MN, MN A1A S, A1A S + NCA + MN, NCA S + MN + A1A, G15 + NCA, G15 S + NCA, NCA S + G15, G15 NCA S, G15 + A1A, G15 S + A1A, A1A S + G15, G15 A1A S, A1A S + NCA + G15, NCA S + G15 + A1A, MN + NCA + G15, MN S + NCA + G15, NCA S + MN + G15, MN NCA S + G15, MN + G15 + A1A, MN S + A1A + G15, A1A S + MN + G15, MN A1A S + G15, A1A S + NCA + MN + G15, NCA S + MN + A1A + G15, MN + NCA, G15 MN S + NCA, G15NCAS + MN, G15MNNCAS, G15 MN S + A1A, G15A1AS + MN, G15 MN A1A S, G15 A1A S + NCA + MN, G15 NCA S + MN + A1A, MN + ZN + NCA, MN S + ZN + NCA, NCA S + ZN + MN, ZN MN NCA S, MN + ZN + A1A, MN ZN S + A1A, A1A S + ZN + MN, MN A1A ZN S, A1A ZN S + NCA + MN, MN A1A S + ZN, wherein "MN" is metallocene component, "ZN" is a Ziegler-Natta catalyst component, such as described above for the first catalyst component, "NCA" is a non-coordinating activator including ionic and neutral boron and aluminuin based compounds as described above, "A1A" is an aluminuin alkyl and/or alumoxane based activator, "G15" is a Group 15-containing catalyst component as described above, and "S" is a support, and wherein the use of " " with "S" means that that those groups next to the colon are associated with ("supported by") the support as by pretreatment and other techniques known in the art, and the "+" sign means that the additional component is not directly bound to the support but present with the support and species bound to the support, such as present in a slurry, solution, gas phase, or another way, but is not meant to be limited to species that have no physico-chemical interaction with the support and/or supported species Thus, for example, the embodiment "MNNCA S + G15" means that a metallocene and NCA activator are bound to a support, and present m, for example, a gas phase polymerization with a Group 15 containing catalyst component [0117] In a particular embodiment, the catalyst systein is selected froin the group consisting of MNZNNCAS, MNZNA1AS, MN AlA S + ZN, ZN AlA S + MN, MN NCA S + ZN, and ZN MN AlA NCA S The components may be combined in any order desirable to achieve the highest polymerization activity In one embodiment, the ZN catalyst is immobilized prior to immobilizing the metallocene, in another embodiment, the metallocene is first immobilized, and in yet another embodiment, an activator is first immobilized, followed by either the metallocene and/or the ZN catalyst In yet another embodiment, both the MN and ZN catalyst components are immobilized simultaneously on the support, the support being pretreated with activator in one embodiment, and treated after catalyst component treatment in yet another embodiment [0118] One embodiment of the support useful in the present invention is a so called "enhanced support", prepared by heating support particles at a dehydration temperature of at least 800°C or more, and between 800°C and 1000°C in another embodiment, resulting in an enhanced support having a modified chemical structure In a particular embodiment, the heating of the support takes place in an inert (e g, N2 or Ar) atmosphere, and in the absence of water In preferred embodiments, increased productivity is achieved when the enhanced support is combined with the other parts of the bimetallic catalyst discussed herein, to forin a supported bimetallic catalyst, which is then contacted with monomers during polymerization to produce a bimodal polyolefin compositions [0119] In one or more specific embodiments, an enhanced support is first prepared, preferably in the manner described below, then that enhanced support is treated (e g, combined with ingredients that forin the first catalyst) to provide a supported catalyst that includes the first catalyst component In specific embodiments, that supported first catalyst is then treated in the presence of the second catalyst component to provide a supported bimetallic catalyst [0120] The enhanced support is prepared by any suitable means, and more particularly, by any means wherein water is removed froin the support, such as by heating, exposure to low pressure, chemical treatment, or combinations thereof Heating the support at a dehydration temperature of at least 800°C, and between 800°C and 1000°C in a particular embodiment, provides an enhanced support, for example, enhanced silica, which provides surpnsmgly improved results over support that is dehydrated at lower temperatures, that is, below 800°C, even slightly lower temperatures, for example, 760°C While not immediately apparent from the enhancement procedure itself, it is contemplated that the heat treatment results in an actual chemical and/or physical change in the support structure itself, which only reveals its beneficial structure when combined with a first and second catalyst components described herein, and placed in the context of an actual polymerization For example, when the enhanced silica is combined with both the first catalyst component and the second catalyst component to forin a supported bimetallic catalyst composition, that supported bimetallic catalyst composition, including the enhanced silica, has been discovered as having desirably high productivity when used in a polymerization process for making bimodal polyolefin in a single reactor For example, a productivity of at least 3000 grams polymer/grain catalyst can be achieved More preferably, the bimetallic catalyst that includes the enhanced support has a productivity of at least 3500 grams polymer/grain catalyst Even more preferably yet, a bimetallic catalyst having the enhanced support has a productivity of at least 4000 grams polymer/grain catalyst Other specific embodiments of the invention include bimetallic catalysts with productivities of 4500 grams polymer/grain catalyst and above, 5000 grams polymer/grain catalyst and above, or even 6000 grams polymer/grain catalyst and above [0121] In a particular embodiment, the support useful in the present invention is a Group 13 or 14 inorganic oxide support having a pore volume ranging froin 0 8 to 3 cm3/g and a surface area of froin 100 to 500 m2/g This support is desirably dehydrated as desenbed herein in one embodiment A preferred support is an amorphous high surface area silica, such as Davison 952 or Sylopol® 955, sold by Davison Chemical Division of W R Grace and Company Those silicas are in spherical form, prepared by the spray drying process, with a surface area of 300 m2/g and a pore volume of 1 65 cm3/g A procedure for dehydrating the silica at 600 °C is set forth in US 5,525,678 [0122] The enhanced support is then combined with a non-polar hydrocarbon diluent to forin a support slurry, which can be stirred and optionally heated during mixing [0123J A variety of non-polar hydrocarbon diluents can be used to forin the support slurry, but any non-polar hydrocarbon selected should remain in liquid forin at all relevant reaction temperatures, and the ingredients used to forin the first catalyst component should be at least partially soluble in the non-polar hydrocarbon Accordingly, the non-polar hydrocarbon diluent is considered to be a "solvent" herein, even though in certain embodiments the ingredients are only partially soluble in the hydrocarbon [0124] Examples of suitable non-polar hydrocarbons include C4-C10 linear or branched alkanes, cycloalkanes and aromatics More specifically, a non-polar alkane can be isopentane, hexane, isohexane, n-heptane, octane, nonane, or decane, a non-polar cycloalkane such as cyclohexane, or an aromatic such as benzene, toluene, or ethylbenzene Mixtures of different non-polar hydrocarbons can also be used [0125] The support slurry can be heated both during and after mixing of the support particles with the non-polar hydrocarbon solvent, but at the point when either or both of the catalysts are combined with the support slurry, the temperature of the slurry should be sufficiently low so that neither of the catalysts are inadvertently deactivated Thus, the temperature of the support slurry (eg, silica slurry) is preferably maintained at a temperature below 90°C, for example, froin 25 to 70°C, or froin 40 to 60°C in another embodiment Gas Phase Polymerization Process [0126] The bimetallic catalysts, and more particularly, the supported bimetallic catalyst composition, described herein are preferably used to make bimodal polyolefin compositions, that is, compositions having a bimodal molecular weight distribution, in a particular embodiment, the bimetallic catalysts described herein are used in a single polymerization reactor to make the bimodal polyolefin composition Once the supported bimetallic catalyst composition is prepared, as described above, a variety of processes can be earned out using that composition Among the varying approaches that can be used include procedures set forth in US 5,525,678 in which those processes are modified in accordance with the mventions claimed herein, for example, involving the high fluidized bulk density as described herein The equipment, process conditions, reactants, additives and other materials will of course vary in a given process, depending on the desired composition and properties of the polymer being formed For example, the processes discussed in any of the following patents can be used US 6,420,580, 6,388,115, 6,380,328, 6,359,072, 6,346,586, 6,340,730, 6,339,134, 6,300,436, 6,274,684, 6,271,323, 6,248,845, 6,245,868, 6,245,705, 6,242,545, 6,211,105, 6,207,606, 6,180,735, and 6,147,173 [0127] More particularly, the process of the present invention is directed toward a gas phase polymerization process of one or more olefin monomers having froin 2 to 30 carbon atoms, froin 2 to 12 carbon atoms in a more particular embodiment, and froin 2 to 8 carbon atoms in yet a more particular embodiment The invention is particularly well suited to the polymerization of two or more olefin monomers of ethylene, propylene, l-butene, 1-pentene, 1-hexene, 1-heptene, 1-octene, 1-nonene, 4-methyl- 1-pentene, 1-isobutene, 1-isobutene and 1-decene [0128] Other monomers useful in the piocess of the invention include ethylenically unsaturated monomers, dtolefins having 4 to 18 carbon atoms, conjugated or nonconjugated dienes, polyenes, vinyl monomers and cyclic olefins Non-limiting monomers useful in the invention may include norbornene, norbomadiene, isobutylene, isoprene, vinylbenzocyclobutane, styrenes, alkyl substituted styrene, ethyhdene norbornene, dicyclopentadiene and cyclopentene [0129] In the most preferred embodiment of the process of the invention, a copolymer of ethylene is produced, where with ethylene, a comonomer having at least one a-olefin having froin 4 to 15 carbon atoms, froin 4 to 12 carbon atoms in yet a more particular embodiment, and froin 4 to 8 carbon atoms in yet a more particular embodiment, is polymerized in a gas phase process [0130] In another embodiment of the process of the invention, ethylene or propylene is polymerized with at least two different comonomers, optionally one of which may be a diene, to forin a terpolymer [0131] Typically in a gas phase polymerization process a continuous cycle is employed where in one part of the cycle of a reactor system, a cycling gas stream, otherwise known as a recycle streain or fluidizmg medium, is heated in the reactor by the heat of polymenzation This heat is removed froin the recycle composition in another part of the cycle by a cooling systein external to the reactor Generally, in a gas fluidized bed process for producing polymers, a gaseous streain containing one or more monomers is continuously cycled through a fluidized bed in the presence of a catalyst under reactive conditions The gaseous streain is withdrawn froin the fluidized bed and recycled back into the reactor Simultaneously, polymer product is withdrawn froin the reactor and fresh monomer is added to replace the polymerized monomer (See for example US 4,543,399, 4,588,790, 5,028,670, 5,317,036, 5,352,749, 5,405,922, 5,436,304, 5,453,471, 5,462,999, 5,616,661 and 5,668,228 ) [0132] The reactor pressure in a gas phase process may vary froin 100 psig (690 kPa) to 500 psig (3448 kPa) in one embodiment, froin 200 psig (1379 kPa) to 400 psig (2759 kPa) in a more particular embodiment, and froin 250 psig (1724 kPa) to 350 psig (2414 kPa) in yet a more particular embodiment [0133] The reactor temperature in a gas phase process may vary froin 30°C to 120°C in one embodiment, froin 60°C to 115°C in a more particular embodiment, froin 70°C to 110°C in yet a more particular embodiment, and froin 70°C to 95°C in yet a more particular embodiment, or as set out further below [0134] In an embodiment of the invention, the process is operated by introducing a carboxylate metal salt such as aluminuin stearate or other metal-fatty acid compound into the reactor and/or contacting a carboxylate metal salt with the catalyst systein of the invention pnor to its introduction into the reactor [0135] The "catalyst system" useful in the gas phase polymenzation process of the invention includes the first and second catalyst components, making up a bimetallic catalyst, and one or more activators The bimetallic catalyst is activated by any suitable means known in the art, either before introduction into the polymenzation reactor or in situ The supported bimetallic catalyst is fed to the reactor in a dry (no diluent) state in a particular embodiment In another embodiment, the bimetallic catalyst is suspended in a diluent (eg, C5 to C15 hydrocarbon) comprising froin 5 wt% to 100 wt% mineral oil or silicon oil and fed into the reactor [0136] The gas-phase process of the present invention includes contacting the catalyst systein (including catalyst components and activators, and optionally, a support) with monomers in a reactor vessel of desirable configuration to forin a polyolefin In one embodiment, the contacting may take place in a first reactor vessel, followed by transfer of the formed polymer into another second, third etc reactor vessel to allow further polymerization, optionally by adding the same or different monomers and optionally by adding the same or different catalyst components, activators, etc In a particular embodiment of the present invention, the bimetallic catalyst systein is contacted with monomers in a single reactor vessel (or "reactor"), followed by isolation of a finished polyolefin resin [0137J For example, a gas phase polymerization process claimed herein may include use of a continuous cycle in which a cvchng gas streain (z e, a recycle streain or fluidizmg medium) is heated in the reactor by the heat of polymerization This heat can be removed from the recycle streain in another part of the cycle by a cooling systein that is external to the reactor In a gas fluidized bed process for producing polymers, a gaseous streain containing one or more monomers can be continuously cycled through a fluidized bed in the presence of a catalyst under reactive conditions The gaseous streain is preferably withdrawn froin the fluidized bed and then recycled back into the reactor Polymer product can be withdrawn froin the reactor and fresh monomer added to replace the polymerized monomer (See for example US 4,543,399, 4,588,790, 5,028,670, 5,317,036, 5,352,749, 5,405,922, 5,436,304, 5,453,471, 5,462,999, 5,616,661 and 5,668,228) [0138] The reactor pressure in a gas phase process may vary froin 100 psig (690 kPa) to 500 psig (3448 kPa) in one embodiment, froin 200 psig (1379 kPa) to 400 psig (2759 kPa) in a particular embodiment, and froin 250 psig (1724 kPa) to 350 psig (2414 kPa) in yet a more particular embodiment [0139] In one aspect of the invention, the voidage of the gas phase reactor is desirably controlled In one embodiment, the polymerization process of the invention is characterized as a process of polymenzation using a bimetallic catalyst wherein the voidage of the flmdized bed gas phase reactor is maintained at less than 40% This can be accomplished by any suitable means such as by, for example, adjusting the hydrogen level in the reactor or reactors The voidage of the reactor can be described in the equation below (A) (Formula Removed) wherein SBD is the "settled bulk density" of the formed resin granules in the reactor, FBD is the "fluidized bulk density", which is the density of the resin granules in the reactor, and "gas density" is simply the density of the gas in the reactor The FBD is the ratio of the measured pressure drop upward across a centrally fixed portion of the reactor to the height of the fixed portion As noted therein, the FBD is a mean value, which may be gi eater or less than the localized bulk density at any point in the fixed reactor portion Since the gas density is diminishingly small, the equation describing voidage can be simplified to the following (B) (Formula Removed) [0140] Certain specific embodiments of the invention are advantageously directed to a process having fluidized bulk density (FBD) that is higher than other bimodal polyolefin polymenzation processes A high FBD (or low voidage) can have benefits in a gas phase polymenzation process, since higher FBD generally means higher catalyst productivity due to the higher residence times allowable in such a reactor A high FBD also provides for advantages for restarting a commercial-scale reactor when a gas phase polymenzation cycle is interrupted by extraneous factors For example, a low FBD corresponds to excessive bed expansion during the restarting process, and can sometimes even make the restart process unsuccessful [0141] As used herein, the terin "fluidized bulk density" (FBD) has the same meaning given that same terin in US 5,436,304, in which the terin is defined as the ratio of the measured pressure drop upward across a centrally fixed portion of the reactor to the height of the fixed portion, for example, a "pressure tap vertical separation " As noted therein, the FBD is a mean value, which may be greater or less than the localized bulk density at any point in the fixed reactor portion [0142] All FBD values that are absolute values of fluidized bulk density are expressed in units of lbs/ft The values of FBD of the present invention range froin 5 to 50 lbs/ft3 in one embodiment, froin 7 to 40 lbs/ft3 in a more particular embodiment, and froin 8 to 30 lbs/ft3 in yet a more particular embodiment, and froin 10 to 25 lbs/ft in yet another embodiment, wherein a desirable range for FBD may be any combination of any upper limit with any lower limit [0143] All SBD values are expressed in units of lbs/ft3 The values of SBD of the present invention range froin 10 to 60 lbs/ft in one embodiment, and froin 12 to 50 lbs/ft in a more particular embodiment, and froin 14 to 40 lbs/ft in yet another embodiment, and froin 15 to 35 lbs/ft3 in yet another embodiment, wherein a desirable lange for SBD may be any combination of any upper limit with any lower limit [0144] In one embodiment, the voidage of the reactor is less than 50% (expressing the values above as percentages), and less than 45% in a more particular embodiment, and less than 40% in yet a more particular embodiment, and less than 35% in a particular embodiment, and less than 30% in a more particular embodiment, and less than 20% in a more particular embodiment, and at least 5% in one embodiment, and at least 10% in a more particular embodiment, wherein a desirable range of voidage values may include any combination of any upper voidage limit with any lower voidage limit described herein Stated another way, the FBD/SBD ratio may have a value of froin greater than 0 40 (or 40% when multiplied by 100 as in the data tables) in one embodiment, and greater than 45% in a more particular embodiment, and greater than 50% in yet a more particular embodiment, and greater than 60% in yet a more particular embodiment, and greater than 65% in yet a more particular embodiment, and less than 95%o in one embodiment, and less than 90%) in yet another embodiment, and less than 85% in yet a more particular embodiment, wherein a desirable range of FBD/SBD values may include any combination of any upper FBD/SBD limit with any lower FBD/SBD limit described herein [0145] It has been found that the voidage can be adjusted to a desirable level when usmg bimetallic catalyst systems composing at least one metallocene by adjusting the level of hydrogen in the polymerization reactor The level of hydrogen in the reactor can be adjusted by adjusting the level of hydrogen in the gas streain that is introduced into the reactor, or stated alternately, adjusting the ratio of hydrogen and ethylene [0146] In certain specific embodiments, the polymerization reactor temperature is maintained at a certain level to further optimize the voidage at a desuable level As used herein, the terin "reactor temperature" can refer to an actual measured temperature (i e , at a point in time) of a fluidized bed in a reaction zone of a fluidized bed reactor used to carry out a gas phase polymerization, and can also refer to a calculated number that equals an average of a plurality of actual measured temperatures, measured intermittently over a period of time, for example, an average of ten measured temperatures over a four-hour period In a particular embodiment, the polymerization reactor temperature langes froin 100°C, or 99°C, or 98°C, or 97°C, or 96°C, or 95°C, or 94°C, or 93°C, or 92°C, or 91 °C, or 90°C, to 40°C, 50°C, 60°C, 70°C, or 80°C, or 82°C, or 84°C, or 86°C, or 88°C, or 90°C, wherein the reactor temperature may be in a range froin any combination of any upper temperature limit with any lower temperature limit described herein Thus, for example, a reactor temperature that averages 97°C for at least a one, two, three, four or more-hour period may be utilized dunng a continuous gas phase polymenzation cycle of the invention in one embodiment [0147] The voidage (or FBD) may be controlled in one embodiment by adjusting the hydrogen level in the polymenzation process The hydrogen levels (also referred to as hydrogen amounts) are sometimes expressed herein in terms of the molar ratio of H2 to C2 (also H2/C2 or H2 C2), wherein H2 refers to molecular hydrogen, and C2 refers to ethylene Alternatively, the hydrogen levels discussed herein can refer to the ratio of moles H2 to moles of monomers used in the polymenzation reaction, for example, ethylene, propylene and/or butene Preferably, however, the hydrogen level referenced herein is the molar ratio of hydrogen gas to ethylene monomers As with reactor temperature, the hydrogen levels referenced herein and in the claims include actual instantaneous measured hydrogen levels, for example, a molar ratio of hydrogen gas to ethylene, or an average hydrogen level, based on measured hydrogen levels taken intermittently over a period of time [0148] The ratio of hydrogen to ethylene has an upper limit of 0 015 in one embodiment, and an upper limit of 0 01 in another embodiment, 0 009 in yet another embodiment, and 0 008 in a more particular embodiment, and 0 007 in yet a more particular embodiment, and 0 006 in yet a more particular embodiment, and 0 005 in yet a more particular embodiment, and 0 004 in yet a more particular embodiment Thus, for example, the average ratio of a molecular hydrogen to ethylene over a four-hour period is 0 009 or below during a continuous gas phase polymerization cycle in one embodiment The ratio of hydrogen to ethylene may have a lower limit of 0 0005 in another embodiment, and 0 001 in a more particular embodiment, and 0 002 in yet a more particular embodiment, and 0 003 in yet a more particular embodiment, and 0 004 in yet a more particular embodiment, and 0 005 in yet a more particular embodiment The range of hydrogen levels (molar ratios of H2/C2) may have comprise any combination of any upper ratio limit with any lower ratio limit described herein For example, in a specific embodiment, the molar ratio of the hydrogen gas in the gaseous streain to ethylene in the gaseous streain is froin 0 003 to 0 009 [0149] An alkylaluminuin compound, or mixture of compounds, such as tnmethylaluminuin or triethylalummuin is feed into the reactor in one embodiment at a rate of froin 10 wt ppin to 500 wt ppin (weight parts per million alkylaluminuin feedrate compared to ethylene feed rate), and froin 50 wt ppin to 400 wt ppin in a more particular embodiment, and froin 60 wt ppin to 300 wt ppin in yet a more particular embodiment, and froin 80 wt ppin to 250 wt ppin in yet a more particular embodiment, and froin 75 wt ppin to 150 wt ppin in yet another embodiment, wherein a desirable range may comprise any combination of any upper limit with any lower limit The alkylaluminuin can be represented by the general formula AIR3, wherein each R is the same or different and independently selected froin C1 to C10 alkyls and alkoxys [0150] Also, water may also be fed mto the reactor in another embodiment at a rate of froin 0 01 wt ppin to 200 wt ppin (weight parts per million water feedrate compared to ethylene feed rate), and froin 0 1 wt ppin to 150 wt ppin in another embodiment, and froin 0 5 wt ppin to 100 wt ppin in yet another embodiment, and froin 1 wt ppin to 60 wt ppin in yet another embodiment, and froin 5 wt ppin to 40 wt ppin in yet a more particular embodiment, wherein a desirable range may comprise any combination of any upper limit with any lower limit described herein Bimodal Polymer Product and Films Made Therefrom [0151] The polymers produced by the processes described herein, utilizing the bimetallic catalysts described herein, which are preferably bimodal, can be used in a wide variety of products and end-use applications such as films, pipes and tubing, wire coating, and other applications The polymers produced by the process of the invention include linear low density polyethylene, elastomers, plastomers, high density polyethylenes, mediuin density polyethylenes, low density polyethylenes, polypropylene and polypropylene copolymers [0152] Polymers that can be made using the described processes can have a variety of compositions, charactenstics and properties At least one of the advantages of the bimetallic catalysts is that the process utilized can be tailored to forin a polymer composition with a desired set of properties For example, it is contemplated that the polymers having the same properties as the bimodal polymer compositions in US 5,525,678 can be formed Accordingly, US 5,525,678 Also, the bimetallic catalysts described herein can be used in polymerization processes to forin polymers having the same properties as the polymers in the following patents US 6,420,580, 6,388,115, 6,380,328, 6,359,072, 6,346,586, 6,340,730, 6,339,134, 6,300,436, 6,274,684, 6,271,323, 6,248,845, 6,245,868, 6,245,705, 6,242,545, 6,211,105, 6,207,606, 6,180,735, and 6,147,173 [0153] The polymers, typically ethylene based polymers, have a density in the range of froin 0 860 g/cm3 to 0 970 g/cm3 in one embodiment, froin 0 880 g/cm3 to 0 965 g/cm3 in a more particular embodiment, froin 0 900 g/cm3 to 0 960 g/cm3 in yet a more particular embodiment, froin 0 905 g/cm3 to 0 955 g/cm3 in yet a more particular embodiment, froin 0 910 g/cin to 0 955 g/cin in yet a more particular embodiment, greater than 0 915 g/cin in yet a more particular embodiment, greater than 0 920 g/cm3 in yet a more particular embodiment, and greater than 0 925 g/cm3 in yet a more particular embodiment [0154] The polymers denved froin the bimodal catalyst and process of the invention have a bulk density of froin 0 400 to 0 900 g/cm3 in one embodiment, and froin 0 420 to 0 800 g/cm3 in another embodiment, and froin 0 430 to 0 500 g/cm3 in yet another embodiment, and froin 0 440 to 0 60 g/cm3 in yet another embodiment, wherein a desirable range may comprise any upper bulk density limit with any lower bulk density limit described herein [0155] The polymers have a molecular weight distribution, a weight average molecular weight to number average molecular weight (Mw/Mn) of froin 5 to 80 in one embodiment, of froin 10 to 60 in a more particular embodiment, of froin 15 to 55 in yet a more particular embodiment, and of froin 20 to 50 in yet a more particular embodiment [0156] The polymers made by the described processes have a melt index (MI) (I2, as measured by ASTin D-1238, 190/2 16) in the range froin 0 01 dg/min to 100 dg/min in one embodiment, froin 0 01 dg/min to 50 dg/min in a moie particular embodiment, froin 0 02 dg/min to 20 dg/min in yet a more particular embodiment, and froin 0 03 dg/min to 2 dg/min in yet a more particular embodiment, and froin 0 002 dg/min to 1 dg/min in yet a more particular embodiment, wherein a desirable range may comprise any combination of any upper I2 limit with any lower I2 limit [0157] Polymers made by the method of the invention have an HLMI (I21, I21 is measured by as measured by ASTM-D-1238, 190/21 6) value that ranges froin 0 01 to 50 dg/min in one embodiment, and froin 0 1 to 30 in another embodiment, and froin 0 5 to 20 in yet a more particular embodiment, and froin 1 to 10 in yet a more particular embodiment wherein a desirable range is any combination of any upper l21 limit with any lower I21 limit [0158] Polymers made by the described processes have a melt index ratio (MIR, or I21/I2) of froin 20 to 500 in one embodiment, froin 30 to 300 in a more particular embodiment, and froin 60 to 200 in yet a more particular embodiment Expressed differently, polymers made by the described processes have a melt index ratio of froin greater than 40 in one embodiment, greater than 50 in a more particular embodiment, greater that 60 in yet a more particular embodiment, greater than 65 in yet a more particular embodiment, and greater than 70 in yet a more particular embodiment [0159] The bimodal polymers produced by the present invention may have a certain average particle size, or APS, ranging froin greater than 150 microns in one embodiment, and froin 150 to 2000 microns in a more particular embodiment, and froin 150 to 1000 microns in yet another embodiment, and froin 300 to 800 microns in yet a more particular embodiment This was determined by using standard sieves Fines (particles of less than 125 urn) are typically present to less than 5 wt%, or less than 4 wt%, or less than 3 wt% [0160] In certain embodiments, propylene based polymers can be produced using the processes descnbed herein These polymers include atactic polypropylene, isotactic polypropylene, hemi-isotactic and syndiotactic polypropylene Other piopylene polymers include propylene block or impact copolymers Propylene polymers of these types are well known in the art see for example US 4,794,096, 3,248,455, 4,376,851, 5,036,034 and 5,459,117 [0161] The polymers of the invention may be blended and/or coextruded with any other polymer Non-limiting examples of other polymers include linear low density polyethylenes produced via conventional Ziegler-Natta and/or metallocene-type catalysis, elastomers, plastomers, high pressure low density polyethylene, high density polyethylenes, polypropylenes and the like [0162] Polymers produced by the process of the invention and blends thereof are useful in such forming operations as film, sheet, pipe and fiber extrusion and co-extrusion as well as blow molding, injection molding and rotary molding Films include blown or cast films formed by coextrusion or by lamination useful as shrink film, cling film, stretch film, sealing films, oriented films, snack packaging, heavy duty bags, grocery sacks, baked and frozen food packaging, cable and wire sheathing, medical packaging, industrial liners, membranes, etc in food-contact and non-food contact applications Fibers include melt spinning, solution spinning and melt blown fiber operations for use in woven or non-woven forin to make filters, diaper fabnes, medical garments, geotextiles, etc Extruded articles include medical tubing, wire and cable coatings, geomembranes, and pond liners Molded articles include single and multi-layered constructions in the forin of bottles, tanks, large hollow articles, rigid food containers and toys, etc [0163] More particularly, the polymers made by the method of the invention are useful in making films The films may be of any desirable thickness or composition, in one embodiment froin 1 to 100 microns, and froin 2 to 50 microns in a more particular embodiment, and froin 10 to 30 microns in yet a more particular embodiment, and compnse copolymers of ethylene with a C3 to C10 olefin in one embodiment, ethylene with C3 to C8 a-olefins in a particular embodiment, and ethylene with C4 to C6 α-olefins in yet a more particular embodiment The resins used to make the films may be blended with other additives such as pigments, antioxidants, fillers, etc, as is known in the art, as long as they do not interfere with the desired filin properties [0164] In one embodiment, a filin made froin one or more of the bimodal polyolefin compositions disclosed herein has a Dart Drop Impact F50 Value of at least 100 [g] on 25 4 micron filin and 50 [g] on 12 5 micron film, and in a more particular embodiment, the bimodal compositions have a Dart Drop Impact of at least 100 [g] on 25 4 micron filin and 75 [g] on 12 5 micron film, and in yet a more particular embodiment, the bimodal compositions have a Dart Drop Impact of at least 200 [g] on 25 4 micron filin and 100 [g] on 12 5 micron film [0165] In one embodiment, a filin made froin one or more of the bimodal polyolefin compositions disclosed herein has an MD Tear value of at least 0 8 g/micron on a 25 4 micron filin in one embodiment, of at least 0 6 g/micron on a 25 4 micron filin in a more particular embodiment, and of at least 0 4 g/micron on a 25 4 micron filin in yet a more particular embodiment, and less than 5 g/micrograin on a 25 4 micron filin in yet a more particular embodiment, and less than 5 g/micron on a 25 4 micron filin in yet a more particular embodiment, and at least 0 2 g/micron on 12 5 micron filin in one embodiment, at least 0 4 g/micron on 12 5 micron filin in a more particular embodiment, and at least 0 8 g/micron on 12 5 micron filin in yet a more particular embodiment, and less than 10 g/micron on 12 5 micron filin in one embodiment, and less than 5 g/micron on 12 5 micron filin a more particular embodiment, wherein a desirable range of MD Tear values may compnse any upper limit (corresponding to a given gauge) with any lower limit descnbed herein [0166] In one embodiment, a filin made froin one or more of the bimodal polyolefincompositions disclosed herein has a TD Tear value of at least 1 5 g/micron on 24 5 micron filin in one embodiment, at least 3 g/micron on 24 5 micron filin in a more particular embodiment, and at least 5 g/micron on 24 5 micron filin in yet a more particular embodiment, and at least 9 g/micron on 24 5 micron filin in one embodiment, and less than 40 g/micron on a 24 5 micron filin in yet a more particular embodiment, and less than 20 g/micron on a 24 5 micron filin in yet a more particular embodiment, and 1 0 g/micron on 12 5 micron filin in yet another embodiment, 2 0 g/micron on 12 5 micron filin in yet a more particular embodiment, 3 0 g/micron on 12 5 micron filin in yet a more particular embodiment, and less than 20 g/micron on a 12 5 micron filin in yet a more particular embodiment, and less than 15 g/micron on a 12 5 micron filin in yet a more particular embodiment, wherein a desirable range of TD Tear values may comprise any upper limit (corresponding to a given gauge) with any lower limit described herein [0167] The invention can thus be described by any combination of the various embodiments descnbed above For example, the method of producing a fluonded metallocene catalyst component can be descnbed by the reaction scheme (VI) (Formula Removed) wherein in is a Group 4, 5 or 6 metal in one embodiment, and zirconiuin or hafniuin in a particular embodiment, each X is independently selected froin the group consisting of chloride, bromide, C1 to C20 carboxylates, C2 to C20 acetylacetonates, hydroxide and C1 to C10 alkoxides in one embodiment, and more particularly selected froin the group consisting of chloride, bromide, C1 to C20 carboxylates, C2 to C20 acetylacetonates, R are groups that may replace hydndes on the Cp nngs and are independently selected froin groups as defined above, and in a particular embodiment, selected froin the group consisting of C1 to C6 alkyls, p is an integer froin 0 to 5 in one embodiment, and froin 1 to 5 in a particular embodiment, wherein when p is 2 on any given Cp nng, adjacent R gioups may forin ring systems, [a]a[C]b is as defined above, and the reaction conditions are as defined above in one embodiment, and more particularly, compnse a two phase system, wherein one phase is an aqueous phase compnsing at least 50 wt% water, at least 80% water in a particular embodiment, and the other phase comprising a hydrocarbon or halogenated hydrocarbon diluent [0168] The present invention also includes a bimetallic catalyst composition compnsing at least one fluonded metallocene catalyst component as described herein, a non-metallocene catalyst component, and an activator, the catalyst components and activator supported on an inorganic oxide dehydrated at a temperature of greater than 800°C The non-metallocene component, or "first catalyst component" is desirably a Ziegler-Natta catalyst component The composition is formed in one embodiment by first synthesizing the fluonded metallocene as desenbed above, followed by combimng with the non-metallocene catalyst component, activator and support in any order In one embodiment, the non-metallocene component is first combined with the support followed by an activator, followed then by combining with the fluonded metallocene catalyst produced by the method desenbed herein [0169] The present invention also includes a process for producing a bimodal polyolefin composition compnsing the steps of (a) contacting a metallocene catalyst compound with an fluonnated inorganic salt for a time sufficient to forin a fluonnated metallocene catalyst compound, next, (b) isolating the fluonded metallocene catalyst compound, followed by (c) combimng the fluonded metallocene catalyst compound with an activator and ethylene monomers and optionally a support at froin 50°C to 120°C, and (d) isolating polyethylene The catalyst may be combined with other monomer such as 1-butene, 1-hexene, etc [0170] In one embodiment, the fluonded metallocene, activator and support are also combined with a Ziegler-Natta catalyst compnsing titaniuin hahde This can be done in any desirable order to produce a bimetallic catalyst In a particular embodiment, the fluonded metallocene, activator and support are combined and isolated prior to combining with ethylene monomers In another embodiment, the combined fluonded metallocene, activator and support are suspended in a diluent compnsing fioin 5 wt% to 100 wt% mineral oil oi silicon oil In a particular embodiment, the fluonnated inorganic salt is charactenzed in that it generates fluoride ions when contacted with a diluent that is at least 50 wt% watei [0171] These embodiments of the present invention arc exemplified by the following examples EXAMPLES Example 1 [0172] In the following example, five samples of supported bimetallic catalysts were prepared Each sample differed pnmanly in whether a fluonnated or chlorinated metallocene was used and the dehydration temperature for the silica support Specifically, Samples 1 and 4 had the same dehydration temperature (760 °C), but differed in whether fluonnated or chlonnated metallocene was used, demonstrating a slight increase in polymer productivity at that temperature (760°C) due to use of a fluonde leaving group rather than a chlonde leaving group Samples 3 and 5 demonstrate that the fluonnated metallocene samples that included silica dehydrated at temperatures above 800°C provided surpnsmgly higher catalyst productivity than either chlonnated metallocene samples having silica dehydrated at similar temperatures (Sample 3) or fluonnated metallocene samples having silica dehydrated at lower temperatures Specific properties of the samples are displayed in Table 1 [0173] Catalyst Preparation In all the samples, Davidson Sylopol® 955 Silica was used Samples 1 and 4 were dehydrated at a temperature of 760°C, Sample 2 was dehydrated at 830°C, and Samples 3 and 5 were dehydrated at 875°C Then, for each sample, a non-metallocene catalyst was combined with the dehydrated silica That is, for each sample, 500 grams of the respective dehydrated silica was added into a 5-hter, 3-neck round bottoin flask enclosed in an N2 glove box Anhydrous hexane (2500 ml) was then added into the flask, making a sihca/hexane slurry The slurry was heated to a temperature of 54°C while under constant stirring, and 380 grams of a 15 wt % solution of dibutyl magnesiuin was added to the slurry over a period of 20 minutes The slurry was then allowed to stand for an additional 30 minutes Butanol (27 4 grams) was diluted to volume with hexane in a 125 ml volumetric flask The entire 125 ml of diluted butanol solution was added dropwise into the flask containing the slurry, and then the slurry was held at a temperature of 54°C for 30 minutes while under constant agitation Titaniuin tetrachloride (41 0 grams) was diluted to volume with hexane in a 125 ml volumetric flask The entire 125 ml of diluted titaniuin tetrachloride solution was then added dropwise mto the flask containing the slurry Following the addition of the solution, the slurry was allowed to stand for 30 minutes at a temperature of 54°C The slurry was then allowed to cool to ambient temperature to forin the "ZN" supported catalyst [0174] The respective metallocene catalyst compound was then added to each sample froin the above slurry First, 673 grams of a 30 wt % solution of methylaluminoxane (MAO) in toluene was added to a new flask in an N2 glove box For Samples 1, 2, and the metallocene bis-n-butyl-cyclopentadienyl zirconiuin dichlonde (13 72 grams) was added into the MAO solution and the mixture was stirred until all of the solids had been dissolved For Samples 4 and 5, 13 72 grams of the metallocene bis-n-butyl-cyclopentadienyl zirconiuin difluonde was added into the MAO solution, and the mixture was stirred until all of the solids had been dissolved Next, the MAO/Metallocene mixture was slowly added into the flask containing the previously prepared titaniuin reaction sluny over a penod of one hour Toluene (50 ml) was used to wash the residual MAO/Metallocene mixture remaining in the flask into the flask containing the reaction slurry Each resulting mixture that included the respective bimetallic catalyst sample was then held at ambient temperature for a period of one hour Afterward, each mixture was dried using a rotary vaporizer, followed by removing most of the hexanes using a vacuuin pressure of 21 mmHg at a temperature of 52°C The high boiling point toluene was subsequently removed using a vacuuin pressure of 28 mmHg at a temperature of 70°C The final dned bimetallic catalyst appeared brown in color as a free flowing solid Each sample of "ZN/MN" supported catalyst was used in a separate polymerization run in a gas phase reactor, under the conditions identified in Table 1 to forin a polyethylene polymer composition [0175] Fluid-Bed Polymerization The polymerizations were conducted in a continuous gas phase fluidized bed reactor The fluidized bed is made up of polymer granules The gaseous feed streams of ethylene and hydrogen together with liquid comonomer were mixed together in a mixing tee arrangement and introduced below the reactor bed into the recycle gas line Monomers of 1-hexene were used as the comonomer The individual flow rates of ethylene, hydrogen and comonomer were controlled to maintain fixed composition targets The ethylene concentration was controlled to maintain a constant ethylene partial pressure The hydrogen was controlled to maintain a constant hydrogen to ethylene mole ratio The concentration of all the gases were measured by an on-line gas chromatograph to ensure relatively constant composition in the recycle gas stream [0176] The solid catalyst was injected directly into the fluidized bed using purified nitrogen as a earner Trimethylalummuin (TMA) was added as a cocatalyst for the ZN catalyst Its rate was adjusted to maintain a constant production rate The reacting bed of growing polymer particles is maintained in a fluidized state by the continuous flow of the make up feed and recycle gas through the reaction zone A superficial gas velocity of 1-3 ft/sec was used to achieve this The reactor was operated at a total pressure of 300 psig To maintain a constant reactor temperature, the temperature of the recycle gas is continuously adjusted up or down to accommodate any changes in the rate of heat generation due to the polymenzation [0177] The fluidized bed was maintained at a constant height by withdrawing a portion of the bed at a rate equal to the rate of formation of particulate product The product is removed semi-contmuously via a senes of valves into a fixed volume chamber, which is simultaneously vented back to the reactor This allows for highly efficient removal of the product, while at the same time recycling a large portion of the unreacted gases back to the reactor This product is purged to remove entrained hydrocarbons and treated with a small steain of humidified nitrogen to deactivate any trace quantities of residual catalyst [0178] Resin Properties The properties of the polymer was determined by the following test methods 1 Melt Index ASTMD-1238-Condition E, 2 Density ASTMD-105, 3 Bulk Density The resin is poured via a 7/8 inch diameter funnel into a fixed volume cylinder of 400 cc The bulk density is measured as the weight of resin divided by 400 cc to give a value in g/cc, 4 Particle Size The particle size is measured by determining the weight of material collected on a series of U S Standard sieves and determining the weight average particle size based on the sieve senes used The fines are defined as the percentage of the total distribution passing through a 120 mesh standard sieve This has a particle size equivalent of 120 microns Fines are important since high levels can lead to sheeting and fouling of the reaction cycle gas systein This results in heat exchanger distnbutor plate fouling requiring a reactor shut down to clean out [0179] Each run was operated over a period of 24 hours, as indicated in Tables 1 and 3 Each run was conducted using the same continuous gas phase fluidized bed reactor The fluidized bed of that reactor was made up of polymer granules During each run, the gaseous feed streams of ethylene and hydrogen were introduced below the reactor bed into a recycle gas line Hexene comonomer was introduced below the reactor bed The individual flows of ethylene, hydrogen and hexene comonomer were controlled to maintain fixed composition targets, identified in Tables 1 and 3 The concentrations of gases were measured by an on-line chromatograph Example 2 [0180] Resins produced froin the catalysts in Example 1 were compounded on a ZSK- 30 compounder with an additive package of 1500 ppin Irganox 1010, 1500 ppin Irgafos 168 and 1500 ppin zinc stearate The compounding operation was conducted under a nitrogen blanket, and conditions were adjusted to maintain the melt temperature below 230°C Films made froin the polymers were formed for purposes of assessing polymer properties The following example describes the fabricating conditions for the filin fabrication process Films were fabncated on an Alpine blown filin line with a single 50 min grooved extruder The die was 100 min in diameter and had a 1 min die gap Extrusion was conducted at a rate of 45 4 kg/hr, while maintaining a temperature profile of 201/204°C on the extruder and a flat temperature profile of 210°C on the die The filin was blown at a 4 1 blow up ratio (BUR), with an initial gauge of 25 microns and a frost line height of 90 cin using chilled air without using an internal bubble stabilizer bar or an internal bubble cooling The take-up speed was gradually increased until either the maximuin take-up speed of the winder was reached or the onset of the bubble instability was noted Physical properties, reported in Table 2 were measured on stable bubbles of gauges 25 and 12 microns using standard ASTin techniques Elmendorf Tear Strength values were measured in the MD and TD direction in accordance with ASTin D1922-00 Dart Drop Impact F50 values were measured using the procedures in ASTin D1709-00 [0181] The present invention offers many advantages over the prior art One advantage is that the catalyst systein offers improved catalyst productivity in polyethylene production More particularly, the silica supported titanium-based Ziegler Natta/fluonded metallocene catalyst has an activity of froin greater than 4500 g/g in one embodiment, and greater than 5000 g/g in a more particular embodiment, and greater than 5400 g/g in yet a more particular embodiment at a polymenzation temperature of froin 90 to 100°C in one embodiment, and froin 93 to 98°C in a more particular embodiment This is a higher activity than for the corresponding chlonded metallocene (Samples 1-3) and even the chlonded metallocenes with the enhanced silica support (Samples 2-3) [0182] The catalyst and method of the present invention also offers the advantage of producing polyethylene polymers having bulk densities ranging froin 0 420 to 0 500 g/ml in one embodiment, and ranging froin 0 440 to 0 490 g/ml in another embodiment, and ranging froin 0 450 to 0 480 g/ml in yet a more particular embodiment, and particularly when an silica support is used that has been dehydrated at froin 830°C or more in particular embodiments [0183] These results are accomplished using a molar ratio of hydrogen to ethylene as descnbed herein, and more particularly of froin 0 001 to 0 015 in one embodiment, and from 0 002 to 0 010 in another embodiment, and froin 0 003 to 0 009 in yet another embodiment, and froin 0 004 to 0 008 in yet another embodiment, wherein a desirable range may compnse any combination of any upper mole ratio limit with any lower mole ratio limit described herein [0184] While the present invention has been described and illustrated by reference to particular embodiments, those of ordinary skill in the art will appreciate that the invention lends itself to many different variations not illustrated herein For these reasons, then, reference should be made solely to the appended claims for purposes of determining the scope of the present invention Further, certain features of the present invention are described in terms of a set of numerical upper limits and a set of numerical lower limits It should be appreciated that ranges formed by any combination of these limits are within the scope of the invention unless otherwise indicated [0185] Unless otherwise indicated, all numbers expressing quantities of ingredients, properties, reaction conditions, and so forth, used in the specification and claims are to be understood as approximations based on the desired properties sought to be obtained by the present invention, and the error of measurement, etc , and should at least be construed in light of the number of reported significant digits and by applying ordinary rounding techniques Notwithstanding that the numerical ranges and values setting forth the broad scope of the invention are approximations, the numerical values set forth are leported as precisely as possible All priority documents are herein fully incorporated by reference for all jurisdictions in which such incorporation is permitted Further, all documents cited herein, including testing procedures, are herein fully incorporated by reference for all jurisdictions in which such incorporation is permitted TABLE 1. Reaction Conditions and Resin Properties (Table Removed) TABLE2. Filin Properties (Table Removed) WE CLAIM: 1. A bimetallic catalyst composition comprising a fluorided metallocene catalyst component, a non-metallocene catalyst component of the kind such as herein described, and an activator of the kinds such as herein described, the catalyst components and activator supported on an inorganic oxide of the kind such as herein described dehydrated at a temperature between 870°C and 1500°C, wherein the fluorided metallocene compound is described by the formulae: (Formula Removed) wherein M is a Group 4, 5 or 6 atoms and more particularly Ti, Zr and Hf, CpA and CpB are each bound to M and are independently selected from the group consisting of cyclopentadienyl ligands, substituted cyclopentadienyl ligands, ligands isolobal to cyclopentadienyl and substituted ligands isolobal to cyclopentadienyl; (A) is a divalent bridging group bound to both CpA and CpB selected from the group consisting of divalent C1 to C20 hydrocarbyls and C1 to C20 heteroatom containing hydrocarbonyls; wherein the heteroatom containing hydrocarbonyls comprise from one to three heteroatoms; at least one X is a fluoride ion; and n is an integer from 1 to 3, said composition comprises inorganic oxide support from 50 to 80 wt %, activator from 10-40 wt %, non-metallocene component from 0.1-15 wt % and fluorided metallocene component from 0.1 to 15 wt %. 2. The bimetallic catalyst composition as claimed in claim 1, wherein the metallocene compound is described by the formulas: (Formula Removed) wherein M is zirconium or hafnium; CpA and CpB are each bound to M and are independently selected from the group consisting of substituted cyclopentadienyl ligands, substituted indenyl ligands, substituted tetrahydroindenyl ligands, substituted fluorenyl ligands, and heteroatom derivatives of each; wherein the substituent groups are selected from the group consisting of C1 to C10 alkyls and halogens; (A) is a divalent bridging group bound to both CpA and CpB selected from the group consisting of divalent C1 to C20 hydrocarbyls and C1 to C20 heteroatom containing hydrocarbonyls; wherein the heteroatom containing hydrocarbonyls comprise from one to three heteroatoms; at least one X is a fluoride ion; and n is an integer from 1 to 3. 3. The bimetallic catalyst composition as claimed in claim 1, wherein at least one Cp is substituted. 4. The bimetallic catalyst composition as claimed in claim 1, wherein at least one Cp is disubstituted. 5. The bimetallic catalyst composition as claimed in claim 1, wherein at least one Cp has from 2 to 5 substitutions. 6. The bimetallic catalyst composition as claimed in claims 1, wherein the substituent groups are selected from the group consisting of methyl, ethyl, n-propyl, iso-propyl, n-butyl, iso-butyl, and tert-butyl. 7. The bimetallic catalyst composition as claimed in claim 1, wherein the inorganic oxide of the kind such as herein described is silica. 8.The bimetallic catalyst composition of claim 1, wherein the fluorided metallocene compound is described by the formulae: CpAMXn, wherein M is a Group 4, 5 or 6 atoms and more particularly Ti, Zr and Hf, CpA is bound to M and is independently selected from the group consisting of substituted cyclopentadienyl ligands and substituted ligands isolobal to cyclopentadienyl; at least one X is a fluoride ion; and n is an integer from 1 to 3. 9. A bimetallic catalyst composition as claimed in any of the preceding claims whenever utilized optionally in combination with catalyst system for a process for producing a bimodal polyolefin composition. |
---|
577-delnp-2005-correspondence-others.pdf
577-delnp-2005-correspondence-po.pdf
577-delnp-2005-description (complete).pdf
577-delnp-2005-petition-137.pdf
Patent Number | 241615 | |||||||||||||||||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Indian Patent Application Number | 577/DELNP/2005 | |||||||||||||||||||||||||||
PG Journal Number | 30/2010 | |||||||||||||||||||||||||||
Publication Date | 23-Jul-2010 | |||||||||||||||||||||||||||
Grant Date | 15-Jul-2010 | |||||||||||||||||||||||||||
Date of Filing | 15-Feb-2005 | |||||||||||||||||||||||||||
Name of Patentee | UNIVATION TECHNOLOGIES,LLC., | |||||||||||||||||||||||||||
Applicant Address | 5555 SAN FELIPE, SUITE 1950, HOUSTON,TX 77056,U.S.A | |||||||||||||||||||||||||||
Inventors:
|
||||||||||||||||||||||||||||
PCT International Classification Number | C08F 4/02 | |||||||||||||||||||||||||||
PCT International Application Number | PCT/US2003/025281 | |||||||||||||||||||||||||||
PCT International Filing date | 2003-08-12 | |||||||||||||||||||||||||||
PCT Conventions:
|