Title of Invention

"METHOD FOR OBTAINING POLYMERIZABLE VINYL CHLORIDE FROM A RAW PRODUCT DERIVED FROM THE PYROLYSIS OF 1,2-DICHLOROETHANE"

Abstract The invention concerns a method for obtaining directly polymerisable vinyl chloride which consists in subjecting a cooled raw product derived from of pyrolysis of 1,2-dichloroethane, to a another cooling process at a temperature not more than 40°C, under pressure ranging between 10 to 15 bars then in leaving it at substantially identical temperature and pressure levels for a duration not more than 20 minutes. The invention also concerns a device for implementing the method.
Full Text The invention relates to a method for obtaining vinyl chloride capable of polymerization, from a raw product derived from the pyrolysis of 1,2-dichloroethane.
The invention also relates to an apparatus for implementing the method.
The products obtained from pyrolyzing 1,2-dichloroethane, hereafter denoted by DCE, contain in particular small quantities of 1,3-butadiene, of the order of 10 to 100 parts per million (ppm), relative to vinyl chloride. These contents ' of 1,3-butadiene, denoted hereafter by BD, which are found in the final vinyl chloride are sufficient to inhibit its polymerization and it is necessary to reduce the BD contents to less than 8 ppm in order to make the vinyl chloride polymerizable under industrial conditions.
It has often been found that the content of 3D formed during pyrolysis of DCE is lower the purer said DCE used, but it is always necessary to limit the BD content in the vinyl chloride obtained by pyrolysis of DCE in order for vinyl chloride polymerization to be able to proceed normally.
To do this, many methods have been -proposed. In the majority of cases, these methods involve, in order to remove the BD, chlorination, hydrochlorination or hydrogenation reactions with or without the presence of catalysts.
Thus, patent FR 1 216 030 proposes to purify the vinyl chloride obtained by pyrolysis of DCE by making the vinyl chloride pass as a mixture with hydrochloric acid, in the vapor phase, over a hydrochlorination catalyst such as HgCl2 or FeCl3. However, this method requires the inclusion of an additional catalytic treatment plant, thereby possibly considerably increasing the production costs, and requires least


some of the unconverted DCE to be separated from the pyrolysis products.
In Patent US 3 125 607, anhydrous chlorine is added to the vinyl chloride at a temperature between -20°C and 0°C in a ratio of chlorine to BD to be removed of about 5/1. The BD content passes from 200 ppm to almost 0 ppm after 30 minutes of chlorinatien.
However, this method has the drawback of including an additional distillation for removing the chlorinated products from the BD, the excess chlorine and various impurities liable to be formed during BD chlorination.
Patent US 3 125 608 discloses a method of purifying gaseous vinyl chloride containing BD, by heating said vinyl chloride with hydrogen to a temperature ranging from 60 °C to 250°C in the presence of a catalyst consisting of Pd supported by activated alumina.
This method has the drawback of including an additional hydrogenation plant.
According to the method described in Patent US 3 142 709, the vinyl chloride is purified of BD by bringing liquid vinyl chloride into contact with an amount of. anhydrous hydrochloric acid representing from 0.5 to 5% by weight of the vinyl chloride for a period ranging from 2 minutes to 5 hours. However, this method applies only to the vinyl chloride already separated from the other pyrolysis products and involves an additional distillation.
Patent FR 1 602 522 discloses a method for obtaining vinyl chloride immediately capable of polymerization, which consists, starting from the raw product derived from the pyrolysis of DCE, in condensing, under a pressure greater than atmospheric pressure, said raw product in order to obtain a liquid phase that is left to mature for at least two hours at a temperature between 0°C and 100°C before separating the constituents thereof.
According to that method, the liquid phase after such a treatment contains practically no BD. In practice, this liquid phase remains in tanks.
This method applies most particularly to pyrolysis products containing at most 10 ppm BD relative to vinyl chloride.
When the pyrolysis products contain larger amounts of BD, such as for example at most 20 ppm, the process is carried out in the following manner.
After .the prior condensation step, which is carried out by suitably cooling the gaseous pyrolysis products maintained at a pressure above atmospheric pressure, a gas phase is obtained which is in equilibrium with the liquid phase and contains a certain amount of BD. The matured liquid phase is used as liquid for scrubbing said gas phase, so as to absorb the residual BD. It then undergoes further maturing for at least two hours. Thus, by repeating this operation, in one or more columns, depending on the BD content in the raw pyrolysis product, it is possible to completely purify vinyl chloride of BD.
Although giving satisfactory results, these various methods of operation have many drawbacks.
For low BD contents, this method applies only to the liquid phase obtained after condensation of the raw product derived from the pyrolysis of DCE and does not take account of the BD contents of the gas phase that may fluctuate and consequently be found in the final vinyl chloride.
When the amounts of BD are higher, at least one operation of scrubbing the gas phase with the liquid phase matured for at least two hours is carried out, which liquid scrubbing phase is again matured for at least two hours.
This process involves many additional items of equipment and the long residence times result in large volumes of inflammable and toxic products under pressure.
The Applicant has found that it is possible to obtain a vinyl chloride capable of polymerization without the drawbacks of the aforementioned methods, by using simple and effective means for reducing the 1,3-butadiene (BD) content of the entire stream coming from the pyrolysis of DCE.
The subject of the invention is therefore a method for obtaining vinyl chloride immediately capable of polymerization from all of the raw product derived from the pyrolysis of DCE having undergone a cooling operation, said method being characterized in that all of the cooled raw product, consisting of a liquid phase and a gas phase, is cooled further down to a temperature of at most 40°C under a pressure ranging from 10 to 15 bar, and then recovered from a tank at substantially identical temperatures and pressures, in which tank the liquid phase remains for a time of at most 20 minutes, and preferably for a time ranging from 5 to 15 minutes, before separation of the constituents.
According to the present invention, the expression "vinyl chloride capable of polymerization" denotes a vinyl chloride having a BD weight content of at most 8 ppm and preferably between 2 and 7 ppm.
According to the present invention, the gas stream coming from the pyrolysis furnace(s) undergoes suitable cooling, which consists of a succession of quenching and condensation operations, which results in a mixture in which the gas phase is in equilibrium with the liquid phase. This mixture - the cooled raw product -comprises vinyl chloride, hydrochloric acid, unconverted DCE, BD and various byproducts. The amounts of BD may vary widely and depend in particular on the purity of the DCE used and on the conditions under which said DCE is pyrolyzed. They are generally between 10 ppm and 100 ppm in current methods.
According to the present invention, all of the cooled raw ^product is subjected to a further cooling operation under a pressure of greater than atmospheric pressure in a heat exchanger of the falling-film
exchanger type from which it leaves at a temperature of at most 40°C. The pressure within said exchanger is at most 15 bar, and preferably between 10 and 15 bar.
All of the cooled raw product thus treated is immediately collected in a tank under pressure and temperature conditions almost identical to those under which it was cooled in the falling-film exchanger, in which tank the liquid phase remains for a time of at most 20 minutes and preferably for a time ranging from 5 to 15 minutes.
Next, the constituents of the mixture are separated using means known per se. According to the present invention, it is preferred however to separate? the hydrochloric acid from the DCE/vinyl chloride mixture in a first distillation column, then the vinyl chloride from the DCE in a second column and, finally, the. last traces of HC1 are removed in a suitable apparatus.
The vinyl chloride coming from the third column advantageously has a BD content of less than 8 ppm and is then immediately capable of polymerization.
The invention also relates to an apparatus for implementing the method.
This apparatus (1) , placed in a vinyl chloride production plant as shown schematically in Figure 1 (the dotted area), inserted between a cooling zone (7), for cooling the gas stream (GS) coming from the pyrolysis zone (8), and the HCl distillation column (9), consists of a falling-film heat exchanger (2) placed on top of a receiving pot (3), this being a horizontal cylindrical tank. The exchanger (2) is fed with the entire cooled raw product (at 7) via a line (4). The HCl distillation column is fed with raw product treated in the apparatus (1) with, on the one hand, liquid product via the line (5) and, on the other hand, gaseous product via the line (6). Withdrawn from the column (9) as tops product is HCl and as bottoms product a mixture comprising vinyl chloride, unconverted DCE and various byproducts, which mixture
feeds the vinyl chloride distillation column (10) via a line (12), from which column is withdrawn, as tops product, vinyl chloride (14) that is purified in a suitable apparatus (11), from which apparatus it is withdrawn at (16) and that is capable of industrial polymerization.
The unconverted DCE and various byproducts are removed at (13).
The residual HC1 is withdrawn at (15).
The apparatus according to the invention is designed in such a way that the exchanger is placed on the receiving pot in such a way that the products from the exchanger flow directly into said pot.
The falling-film exchanger consists of vertical tubes enclosed in a calender, through which tubes the liquid and gas streams flow, the liquid trickling down the walls of said tubes. Cooling is provided by cooling water flowing on the calender side. A person skilled in the art will determine the necessary number of tubes suitable for the streams to be treated and for the cooling.
The method and the apparatus for implementing the method according to the invention allow the BD content in vinyl chloride to be lowered, making it immediately polymerizable. They also have the advantage of relieving the refrigeration demand at the top of the HCl distillation column. The example that follows illustrates the invention.
EXAMPLE
The example is carried out in an industrial plant as shown schematically in Figure 1 and designed in such a way that it can produce 50 metric tons of immediately polymerizable vinyl chloride per hour.
The pyrolysis zone (8), consisting of three furnaces, is fed with DCE having a purity of 99.7%.
This zone is maintained at a mean temperature of about 480°C and at a pressure of 30 bar.
The stream coming from this pyrolysis zone, which comprises vinyl chloride (VC), HC1, unconverted DCE (about 50%), BD and other byproducts, leaves at a temperature close to 480°C and at a pressure of 30 bar and passes into a cooling zone (7), consisting of quenching columns, which lowers its temperature to around 180°C and into various exchangers with various cold levels, which lower its temperature from 180°C to about 60°C.
All of the raw product thus cooled that leaves (7), consisting of a gas phase comprising vinyl chloride, HC1, and small amounts of DCE, and of a liquid phase, comprising DCE, vinyl chloride and small amounts of HC1, is introduced into the top of the falling-film exchanger (2) at a temperature of about 56°C. This exchanger consists of 1652 tubes and is cooled with 28°C water flowing countercurrently through the calender. The pressure inside the falling-film exchanger (2) is 14 bar.
The stream leaves (2) at a temperature of 37°C and a pressure of 14 bar and falls directly into the pot (3), which is a simple horizontal cylindrical tank, in which the liquid phase remains for 15 minutes at approximately 37°C and a pressure of 14 bar. The gas and liquid streams are then directed to the distillation column (9) via the lines (6) and (5) respectively. In this column, HC1 is separated at the top at about 25°C and a pressure of 13 bar.
The liquid phase, comprising VC, DCE and various byproducts is withdrawn from the boiler maintained at about 110°C. and sent into the distillation column (10) via the line (12).
In this column, the VC is separated at the top at 30°C and a pressure of 4 bar.
The bottom of the column (10) maintained at 150°C, essentially contains DCE and various byproducts that are withdrawn at (13). The VC is then sent via the line (14) into the column (11) where the residual HC1 is removed, said HC1 being withdrawn as top product (15).
The VC withdrawn from this column at (16) has a mean BD
weight content ranging from 3 to 6 ppm and, as a
consequence, is immediately polymerizable on am
industrial scale.




We claim:
1. A method for obtaining vinyl chloride immediately capable of polymerization from all of the raw product derived from the pyrolysis of 1,2-dichloroethane having undergone a cooling operation, said method being characterized in that the cooled raw product, consisting of a liquid phase and a gas phase, is cooled further down to a temperature of at more 40°C under a pressure ranging from 10 to 15 bar, and then recovered from a tank at substantially identical temperature for a pressures, in which tank the liquid phase remains for a time of at most 20 minutes before separation of the constituents.
2. The method as claimed in claim 1, wherein the liquid phase remains in the tank for a time ranging from 5 to 15 minutes.
3. The method as claimed in claims 1 or 2, wherein the constituents are separated by distillation under pressures greater than atmospheric pressure.
4. An apparatus for implementing the method as claimed in any one of claims 1 to 3, wherein it consists of a falling-film exchanger (2) placed on top of a receiving pot (3), these items of equipment being inserted between a cooling zone (7), for cooling the gas stream coming from the pyrolsis zone (8), and a distillation zone comprising an HC1 distillation column (9), a vinyl chloride distillation column (10) and a suitable device (11) for eliminating traces of HC1.

Documents:

1026-DELNP-2004-Abstract-(04-09-2009).pdf

1026-delnp-2004-abstract.pdf

1026-DELNP-2004-Claims-(04-09-2009).pdf

1026-delnp-2004-claims.pdf

1026-DELNP-2004-Correspondence-Others-(04-09-2009).pdf

1026-DELNP-2004-Correspondence-Others-(08-04-2009).pdf

1026-delnp-2004-Correspondence-Others-(16-03-2010).pdf

1026-delnp-2004-correspondence-others.pdf

1026-delnp-2004-correspondence.pdf

1026-DELNP-2004-Description (Complete)-(04-09-2009).pdf

1026-delnp-2004-description (complete).pdf

1026-delnp-2004-description.pdf

1026-DELNP-2004-Drawings-(04-09-2009).pdf

1026-delnp-2004-drawings.pdf

1026-DELNP-2004-Form-1-(04-09-2009).pdf

1026-DELNP-2004-Form-1-(08-04-2009).pdf

1026-delnp-2004-form-1.pdf

1026-delnp-2004-form-13-(08-04-2009).pdf

1026-delnp-2004-form-18.pdf

1026-DELNP-2004-Form-2-(04-09-2009).pdf

1026-DELNP-2004-Form-2-(08-04-2009).pdf

1026-delnp-2004-form-2.pdf

1026-DELNP-2004-Form-3-(04-09-2009).pdf

1026-delnp-2004-form-3.pdf

1026-delnp-2004-form-5.pdf

1026-delnp-2004-form1.pdf

1026-delnp-2004-form2.pdf

1026-delnp-2004-form26.pdf

1026-delnp-2004-form3.pdf

1026-delnp-2004-form5.pdf

1026-DELNP-2004-GPA-(04-09-2009).pdf

1026-delnp-2004-gpa.pdf

1026-DELNP-2004-Others-Document-(08-04-2009).pdf

1026-delnp-2004-pct-pamphlate.pdf

1026-DELNP-2004-Petition-137-(04-09-2009).pdf

1026-DELNP-2004-Petition-138-(04-09-2009).pdf


Patent Number 238964
Indian Patent Application Number 1026/DELNP/2004
PG Journal Number 5/2010
Publication Date 05-Mar-2010
Grant Date 02-Mar-2010
Date of Filing 19-Apr-2004
Name of Patentee ARKEMA FRANCE
Applicant Address 4/8, COURS MICHELET, 92800 PUTEAUX, FRANCE
Inventors:
# Inventor's Name Inventor's Address
1 BEATRICE RONDOT RUE DU PUECH DE LA CABANE, F-30640 BEAUVOISION, FRANCE
2 FRANCOIS VANNEY 54 AVENUE FOCH, F-69006 LYON, FRANCE
PCT International Classification Number C07C 17/38
PCT International Application Number PCT/FR02/03518
PCT International Filing date 2002-10-15
PCT Conventions:
# PCT Application Number Date of Convention Priority Country
1 01/13364 2001-10-17 France