Title of Invention

"A PROCESS FOR MANUFACTURING GLASS"

Abstract The present invention relates to the production of glass. In particular, the present invention relates to a method for the production of glass utilizing processes of reacting materials in a glass furnace in either a batch mode or a continuous process. These reactions affect the thermodynamics and other characteristics of the glass-forming reaction. The present invention additionally relates to compositions which are useful in such reactions.
Full Text FIELD OF THE INVENTION
The present invention relates to a process of manufacturing glass.
The present invention relates to a product, a process for its preparation, and the use of such product in glass. More particularly, the present invention relates to a process that produces a solid state particle that is particularly useful in the production of glass products, such as flat glass, fiberglass, container glass, lighting glass, tableware, and the like.
BACKGROUND OF THE INVENTION
Processes, and materials for such processes, for the manufacture of glass have millenniums of development. In particular, glass manufacturers have been, and continue to be, concerned with the components, thermodynamics and other characteristics of the glass-making reactions in glass furnaces. The glass reaction generally involves the reaction of materials to produce a composition containing the reacted and/or dispersed components of silica (silicon dioxide from sand, quartz and the like), soda ash (sodium carbonate), and lime (calcium oxide from quicklime, hydrated lime and the like) with other optional components, generally metal oxides of lead, lithium, cerium, iron, magnesium, potassium, barium, borax and the like.
Various considerations have addressed such processes by varying the feed materials and the process schemes for the reaction of such compositions. Such considerations include, for
example, reaction of a portion of the materials before creating a total glass batch. For example, one scheme is pretreatment of the batch constituents by calcining the limestone and/or dolomite constituents so as to decompose the carbonates to oxides. This calcining releases carbon dioxide from the material added to make the total glass batch. This elimination of carbon dioxide before melting begins is advantageous since it reduces the entrapping of gaseous inclusions in the glass. Other schemes involve using various components to attempt to effect the reaction"s thermodynamics or quality or yield results. While advances have been made, there still exists the need for developing processes and feed materials to improve the glass-making processes.
RELATED ART
In U.S. Pat. No. 3,082,102, heating of the batch mixture is performed prior to melting to effect reaction between silica and soda ash to produce sodium metasilicate. The temperature is limited to 820.degrees Centigrade for soda-lime-silica glass to avoid producing a molten phase that would lead to clogging of the preliminary heating apparatus.
In U.S. Pat. No. 3,682,666, a similar process of reacting the whole batch mixture to produce silicates prior to melting is disclosed in which a lowered reaction temperature between 600.degrees Centigrade and 787.degrees Centigrade. Such is made possible by the inclusion of a small amount of halide.
In U.S. Pat. No. 3,817,776, a process is disclosed to partially react preheated sand grains to sodium silicate by contact with molten caustic soda. The remainder of the batch ingredients are added subsequently. This process has the disadvantage of requiring the use of caustic soda, which is more costly than soda ash as a source of sodium for making glass. Also, the process of contacting solids with molten material is more difficult to control and more prone to plugging than a solid state reaction.
In U.S. Pat. No. 3,883,364, glass furnace dusting problems are reduced by providing a process for sintering alkaline earth carbonate to be charged to a glass furnace.
In U.S. Pat. No. 4,248,615, an energy conserving glass manufacturing process is provided in which agglomerants are preconditioned prior to supplying them to a verticle bed for glass manufacturing.
In U.S. Pat. No. 4,539,030, an example of a calcining pretreatment is disclosed. Calcining requires temperatures in excess of 1600 degrees Fahrenheit (870 degrees Centigrade), which precludes treatment of the whole batch mixture because such temperatures would cause fusion of other constituents of the batch, particularly the soda ash or other soda source.
In U.S. Pat No. 4,920,080, silica is reacted with sodium carbonate to form sodium silicate in as a
preliminary step in a glass melting process. The method preferably calcines calcium carbonate-
containing batch materials separately before combining with sodium silicate as liquefying is
DN 01-036
TnTtiated. The process materials are preheated and pre-reacted in two separate portions to optimize prior to initiation of melting.
In U.S. Pat. No. 5,004,706, a process is provided to address problems of stickiness of glass batches by pre-reaction of a portion of the glass batch.
SUMMARY OF THE INVENTION
The present invention discloses a process that includes preferentially reacting a portion of a glass batch within the total glass batch. This preferential reaction is accomplished by reacting a solid state particle containing a portion of the total glass batch thus effectively creating an in-homogeneity in the total glass batch. The components reacted in this preferential reaction are exothermic in nature and effectively lower the eutectic character of the total glass batch.
The present invention further discloses a solid state particle comprising silicon, calcium and magnesium that creates an inhomogeneity within the total glass batch. The solid state particle produced according to the process of the present invention is useful in the production of glass products, such as flat glass.
The present invention further discloses a glass composition comprising silica, soda ash, lime or
limestone, a solid state particle containing silicon dioxide, calcium hydroxide, magnesium oxide,
and magnesium hydroxide, and other optional metal oxides.
DN 01-036
The solid state particle of the present invention is particularly useful in production of glass product sucrrrte flat glass, fiberglass, container glass, lighting glass, tableware, and the like.
STATEMENT OF INVENTION
The present invention relates to a process for manufacturing glass from a glass batch comprising: (a) admixing calcium hydroxide, magnesium oxide, magnesium hydroxide, silicon dioxide, and water to produce an agglomerate; (b) admixing the agglomerate and a second source of silicon dioxide and a source of sodium oxide to produce a glass batch admixture in the glass furnace under temperature conditions such that an exothermic reaction of the agglomerate produces a solid state particle of calcium magnesium silicate composition in the glass batch admixture; (c) subsequently maintaining the temperature of the glass batch admixture to produce a final glass batch; and (d) producing a molten glass product from the glass furnace.
The present invention also relates to solid state particle agglomerate used in manufacturing glass comprising admixing calcium oxide, magnesium oxide, silicon dioxide, and water. The present invention also relates to a glass composition comprising silica, soda ash, lime or limestone, a solid state particle containing silicon dioxide, calcium hydroxide, magnesium oxide, and magnesium hydroxide, and other optional metal oxides.
DESCRIPTION OF THE FIGURES
Figure 1-Solid State Particle in Float Glass Figure 1 shows the reacted silica (stones) per pound of glass as a function of dwell time at a hold temperature of 1400 Centigrade. The black line, representing the control glass without the invention, requires a longer dwell time to reach a point without significant stones compared to the red line representing the invention (glass batch with the solid state particle). The dwell time relates to the melting rate of the glass, which in turn effects the throughput of the glass furnace. Therefore, the glass batch using the invention will melt faster allowing for more throughput on the furnace.
Figure 2-Differential Thermal Analysis
Figure 2 shows the energy evolved or absorbed as a function of temperature for a control glass (in red) and a glass using the solid state particle (in green). The temperatures between 900 Centigrade and 1100 Centigrade show the calcium magnesium silicate reaction in the experimental glass (in green). This reaction is clearly exothermic in nature (compared to the baseline). The control glass without agglomeration of the solid state particle shows an endothermic reaction, typical of most glass reactions in this regime. In total, the graph shows the evidence of a calcium magnesium silicate phase that would not exist in the glass if not for the
present invention. This calcium magnesium silicate not only helps the melting rate as in Figure 1, but also imbues energy into the total glass batch due to the exothermic nature of the reaction.
DETAILED DESCRIPTION OF THE INVENTION
One embodiment of the present invention is a process that includes preferentially reacting a portion of a glass batch within the total glass batch. This preferential reaction is accomplished by reacting a solid state particle containing a portion of the total glass batch thus effectively creating an inhomogeniety in the total glass batch. The components reacted in this preferential reaction are exothermic in nature and effectively lower the eutectic character of the glass batch compared to that eutectic character present without such selection. "Eutectic character" of a glass batch is defined as the temperature needed by two or more batch components in physical contact with each other to drive the glass-forming reactions as well as the path of the reaction and the impact of such on the reaction kinetics and speed. "Solid state particle" refers to a mixture of compounds such as silicon dioxide, calcium hydroxide, magnesium oxide, and magnesium hydroxide that, when heated, will initiate a solid state reaction within the particle that concludes with the production of a new compound such as calcium magnesium silicate.
In a preferred embodiment of the present invention, the solid state particle, comprising
components of silicon dioxide, calcium oxide and magnesium oxide materials, creates an
inhomogeniety and is located within the glass batch. The relative amount of these three
components is effective to produce an exothermic reaction when heated to a reaction initiation
DN 01-036
temperature. This solid state particle is admixed with a mass containing a balance of other glass-forming materials prior to the exothermic reaction. Such other glass-forming materials may contain sodium materials and additional silicon materials as well as various other materials needed to produce the desired glass composition.
The silicon material of the solid state particle is silicon dioxide, and, more preferably, a silica flour. Preferred sources of such include sand, silica flour, nepheline syenite, and spodumene. Preferably the silicon material particle size is 90% less than 0.0075 Centimeters to promote a thermodynamic advantage towards the solid state reaction versus the standard glass reaction.
The calcium material of the solid state particle is calcium oxide and, more preferably, a calcium hydroxide. Preferred sources of such include dolomite lime, dolomitic limestone, calcite, lime, colemanite, natural diopside and wollastonite, ulexite, gypsum, fluorspar, aragonite, and feldspar. Preferably the calcium material particle size is 90% less than 0.0075 Centimeters to promote a thermodynamic advantage towards the solid state reaction versus the standard glass reaction.
The magnesium material of the solid state particle is magnesium oxide and, more preferably, a magnesium hydroxide. Preferred sources of such include dolomitic lime, dolomitic limestone, natural diopside, brucite, periclase, and epsom salt. Preferably the magnesium material particle size is 90% less than 0.0075 Centimeters to promote a thermodynamic advantage towards the solid state reaction versus the standard glass reaction.
The components of the solid state particle, the silicon material, calcium material and magnesium material are in the respective molar ratios of from about zero (0) part to about one (1) part calcium oxide and from about zero (0) part to about one (1) part magnesium oxide with respect to one (1) part silicon dioxide.
More preferably, the components of the solid state particle, the silicon material, the calcium material and the magnesium material are in the respective weight ratios of from about 0.4 parts to about 0.6 parts calcium oxide and from about 0.3 parts to about 0.4 parts magnesium oxide to one (1) part silicon dioxide.
The solid state particle size should be of a magnitude that promotes the attainment and retention of a homogenous distribution of material in the glass batch during the glass reaction. Accordingly, the solid state particle size should be of a similar magnitude of the other glass batch components, more preferably of the silicon source material, e. g. sand, used in the total glass batch. Particularly, the median size of the solid state particle material should be from about 75 percent to about 500 percent of the median size of the balancing silicon dioxide material used to produce the glass batch, even more particularly from about 85 percent to about 115 percent of the median size of the balancing silicon dioxide material.
A preferred solid state particle material is an agglomerate of minerals produced by the admixture
of calcium oxide material, magnesium oxide material, silicon dioxide and water. The
agglomerate is formed to a particle size which approximates the sand balance to be used in the
DN 01-036
glass batch, preferably from about 0.018 centimeters to about 0.14 centimeters, more preferably, from about 0.025 centimeters to about 0.085 centimeters.
The product of the reacted solid state particle, that occurs within the total glass batch, can be a calcium magnesium silicate having an empirical formula of (CaO)x(MgO)y(Si02)z, wherein the weight values of x and y relative to the amount of silica is sufficient to produce an exothermic reaction. Preferably, x, y, and z have the respective ranges from about zero (0) to about three (3), from about zero (0) to about one (1), and from about one (1) to about two (2). The formed calcium magnesium silicate product and the other material in the glass batch react as a total glass batch system to produce the desired glass product. Additional energy to drive the glass-forming reaction to completion is provided to the glass batch system. Preferably, the exothermic reaction provides from about 5 percent to about 20 percent of the total energy needed to perform the total glass batch reactions to produce the desired glass product.
The following examples are intended to illustrate the present invention, but not to limit the scope of protection afforded by the claims hereafter:
EXAMPLE 1
A glass product is to have components of silicon, sodium, calcium, magnesium, measurable in
equivalents as silica dioxide (Si02), sodium oxide (Na20), calcium oxide (CaO), and magnesium
oxide (MgO). To supply the silicon component of the glass, a sand material is selected as a feed
DN 01-036
material. The sand has a size measurement of 30 mesh to 140 mesh. To supply the calcium and magnesium components to the glass batch, the solid state particle containing the magnesium, silica, and calcium components, agglomerated with water, dried, and screened, is added to the total glass batch. The agglomerated (solid state) particles contain silicon dioxide (Si02), hydrated calcium oxide (Ca(OH),), hydrated magnesium oxide (Mg(OH)2), periclase (MgO), and water. This agglomerated particle material is combined with the sand to be used in an amount to complete the total silicon value of the glass batch. Soda ash is added to supply the sodium value for the glass. Since the agglomerated particle does not contain sufficient calcium value for the glass formula, limestone will be used. The total glass batch is heated to a temperature below the glass reaction temperature but sufficient to initiate an exothermic reaction in the agglomerated particles.
The exothermic reaction begins the production of calcium magnesium silicate material in the total glass batch. The temperature of the total glass batch continues to rise due to the supplied heat and the exothermic reaction heat to produce a glass reaction involving the calcium magnesium silicate material, sand, limestone, and soda ash. The exothermic reaction and glass reaction occur simultaneously for a period within the glass batch vessel until all reactions are completed producing a glass.




We Claim:
1. A process for producing a glass, the process comprising:
(a) admixing a calcium material, a magnesium material, and a silicon material with water, producing a solid state particle agglomerate thereby;
(b) admixing the solid state particle agglomerate with at least one glass-forming material comprising a source of silicon dioxide in a glass furnace producing a total glass batch thereby;
(c) heating the total glass batch to a reaction initiation temperature such that the heating initiates an exothermic solid state reaction in the solid state particle agglomerate and the solid state reaction concludes with the production of a calcium magnesium silicate material; and
providing continued heating of the total glass batch to provide additional energy that, with energy supplied by the exothermic solid state reaction, raises the temperature of the total glass batch to produce a glass thereby.
2. The process as claimed in claim 1, wherein the silicon dioxide material, the calcium oxide material and the magnesium oxide material are in the respective weight portions of from zero (0) parts to one (1) part calcium oxide and from zero (0) parts to about one (1) part magnesium oxide to one (1) part silicon dioxide and preferably from 0.4 parts to 0.6 parts calcium oxide and from 0. 3 parts to one 0.4 parts magnesium oxide to one (1) part silicon dioxide.
3. A solid state particle agglomerate produced in the process as claimed in claim 1, comprising admixing calcium oxide, magnesium oxide, silicon dioxide, and water.
4. The solid state particle agglomerate as claimed in claim 3, wherein the said solid state particle reactant is calcium magnesium silicate, having the empirical formula of (CaO)x (MgO)y(Si02)z.
5. The solid state particle agglomerate as claimed in claim 4, wherein the said weight values of x and y relative to the amount of silica is sufficient to produce an exothermic reaction, wherein x, y, and z have the respective ranges of from zero (0) to three (3), from zero (0) to one (1), and from one (1) to two (2).
6. The solid state particle agglomerate as claimed in claim 5, wherein the said particle size is from 0.018 centimeters to 0.14 centimeters and from 0.025 centimeters to 0.085 centimeters.
7. The solid state particle agglomerate as claimed in claim 6, having from 75 percent to 500 percent of the median size of the balancing silicon dioxide and preferably from 85 percent to 115 percent of the median size of the balancing silicon dioxide.
8. The solid state particle agglomerate as claimed in any one of the preceding claims 1 to7, wherein the exothermic reaction provides from 5 percent to 20 percent of the total energy needed to produce the desired glass product.
9. A glass composition produced by the process as claimed in claims 1 to 8, comprising silica, soda ash, lime or limestone, a solid state particle containing silicon dioxide, calcium hydroxide, magnesium oxide, and magnesium hydroxide, and other optional metal oxides.
10. A process for manufacturing glass, a solid state particle agglomerate, a glass composition substantially as herein described with reference to the accompanying drawings and foregoing examples.

Documents:

1038-delnp-2004-abstract.pdf

1038-delnp-2004-assignment.pdf

1038-delnp-2004-claims.pdf

1038-delnp-2004-complete specification (as files).pdf

1038-delnp-2004-complete specification (granted).pdf

1038-delnp-2004-correspondence-others.pdf

1038-delnp-2004-correspondence-po.pdf

1038-delnp-2004-description (complete).pdf

1038-delnp-2004-drawings.pdf

1038-delnp-2004-form-1.pdf

1038-delnp-2004-form-18.pdf

1038-delnp-2004-form-2.pdf

1038-delnp-2004-form-26.pdf

1038-delnp-2004-form-3.pdf

1038-delnp-2004-form-5.pdf

1038-delnp-2004-pct-101.pdf

1038-delnp-2004-pct-210.pdf

1038-delnp-2004-pct-409.pdf

1038-delnp-2004-petition-137.pdf


Patent Number 220908
Indian Patent Application Number 1038/DELNP/2004
PG Journal Number 31/2008
Publication Date 01-Aug-2008
Grant Date 10-Jun-2008
Date of Filing 19-Apr-2004
Name of Patentee SPECIALTY MINERALS (MICHIGAN) INC.
Applicant Address
Inventors:
# Inventor's Name Inventor's Address
1 JOHN ALBERT HOCKMAN
PCT International Classification Number C03C 1/02
PCT International Application Number PCT/US01/49926
PCT International Filing date 2001-12-27
PCT Conventions:
# PCT Application Number Date of Convention Priority Country
1 PCT/US01/49926 1900-01-01 U.S.A.