Title of Invention

A POLYMER BATTERY COMPRISING NEGATIVE ELECTRODE CONTAINING GRAPHITE PARTICLE HAVING AMORPHOUS CARBON ATTACHED TO THE SURFACE THEREOF

Abstract The invention relates to a polymer battery comprising: a negative electrode comprising, as an active material, a carbon material containing graphite particles having amorphous carbon attached to the surface thereof; an electrolyte layer; and a positive electrode comprising at least a lithium-containing chalcogenide as an active material, wherein the electrolyte layer forms a composite obtained by crosslinking a precursor of an ion-conductive compound contained in the positive electrode and/or the negative electrode together with a precursor of an ion-conductive compound contained in a polymer fiber forming the electrolyte layer, characterized in that the ion-conductive compound is used as a gel containing a Li salt and an organic solvent containing ethylene carbonate, wherein the content of ethylene carbonate in the electrolyte layer is 2 to 55 wt% and the content of the Li salt is 3 to 35 wt% and wherein the polymer fiber is a nonwoven textile having a gas permeability of 1 to 500 sec/cm<SUP>3</SUP>. fig 2
Full Text

Technical Field
The present invention relates to a polymer battery comprising negative electrode containing graphite particle having amorphous carbon attached to the surface thereof, more particularly a polymer battery using an ion-conductive compound which acts reversibly at ambient temperature. Especially, the polymer battery uses the ion-conductive compound and a negative electrode containing, as an active material, a carbon material formed of graphite particles having amorphous carbon attached to the surface thereof.
Background Art
As electrolytes for currently commercially available non-aqueous electrolyte batteries such as lithium primary batteries, lithium secondary batteries and the like, organic electrolytes formed of electrolytic salts dissolved in organic solvents are commonly used. However, the organic electrolytes are liable to leak out of components, generate the elution of electrode materials and volatilize. Therefore, there have been a problem in long-term reliability and a problem of scattering electrolytes during a sealing process.
Recently, instead of using metallic lithium or its alloy for negative electrodes, have been developed carbon materials utilizing absorption-desorption of lithium ions and matrix

materials such as electroconductive polymers. Thereby, it has become possible in principle to avoid generation of dendrite, which takes place with the case where metallic lithium or its alloy is used. Consequently, the incidence of short circuit within batteries has dropped sharply. The carbon materials, especially, are known to have a lithium absorption-desorption potential close to a lithium deposition-dissolution potential. Among the carbon materials, graphite has a large capacity per unit weight and unit volume since it can take lithium atoms within its crystal lattice in a proportion of one lithium atom to six carbon atoms theoretically. Furthermore, graphite provides a flat lithium intercalation-deintercalation potential and is chemically stable. Graphite can contribute greatly to the cycle stability of batteries.
For example, J.Electronchm. Soc, Vol.137, 2009 (1990), Japanese Unexamined Patent Publications Nos. HEI 4(1992)-115457, HEI 4(1992)-115458 and HEI 4(1992)-237971 disclose batteries using graphite type carbon materials as negative electrode active materials, and Japanese Unexamined Patent Publications Nos. HEI 4(1992)-368778, HEI 5(1993)-28996 and HEI 5(1993}-114421 disclose batteries using surface-treated graphite type carbon materials as negative electrode active materials.
As described above, the graphite type carbon materials can provide a discharge capacity almost equal to a theoretical

capacity in organic electrolytes formed mainly of ethylene carbonate (EC). Since the charge-discharge potential thereof is slightly higher than the lithium dissolution-deposition potential and is extremely flat, it is possible to realize high-capacity secondary batteries with flat battery voltage by producing the batteries using graphite type carbon materials as negative electrode active materials.
Thus the capacity of batteries can be raised with the graphite type carbon materials, but there still remains a problem in that the graphite type carbon materials cause decomposition of organic electrolytes due to their high crystallinity. For example, propylene carbonate (PC), which is a solvent for organic electrolytes, is widely used as a solvent for electrolytes of lithium batteries since it has a large potential window, a low coagulation point (-70 *C) and a high chemical stability.
However, it is reported in J, Electrochm. Soc, Vol. 142, 1746 (1995) that, in the case where a graphite type carbon material is used as a negative electrode active material, PC decomposes significantly and the electrode formed of the graphite material cannot be charged or discharged if only 10 % of PC is present in the electrolyte.
In recent years, reports have been made about organic electrolytes of EC mixed with various low-viscosity solvents for improving ion conductivity at low temperatures. However,

there remain problems in volatility and leakage of such organic electrolytes.
For the purpose of improving the leakage-proof property, safety and long-term storability, ion-conductive polymers having a high ion conductivity have been reported, and are extensively studied as one means for solving the above-mentioned problems. As one type of ion-conductive polymers presently under study, homopolymers and copolymers composed of ethylene oxide as a fundamental unit, which are in the form of straight-chain polymers, crosslinked network polymers or comb-form polymers have been proposed and are almost put in practical use. Various batteries using the above-mentioned ion-conductive polymers are described in patent publications and others, which are typified, for example, by U.S. Patent No. 4,303,784 (1981) to Armand et. al., U.S. Patent No. 4,589,197 (1986) to North and U.S. Patent No. 4547440 (1985) to Hooper et. al. These disclosures are characterized by using ion-conductive polymers wherein electrolytic salts are dissolved in polymeric materials having polyether structure. These proposed ion-conductive polymers are under research and development as electrolytes for large-size lithium batteries to be power sources of electric automobiles. However, since the ion-conductive polymers described above have low ion conductivity at temperatures below room temperature, it is difficult to realize small-size,

light-weight batteries with high energy density which are demanded for power sources for driving portable electronic instruments and for memory back-up.
On the other hand, as means for further improving the ion conductivity more than the above-described ion-conductive polymers improve it, are proposed methods of adding organic solvents (especially preferably organic solvents with high dielectric constant such as EC or PC) to ion-conductive polymers while maintaining a solid state, as typified by Japanese Unexamined Patent Publication Nos. SHO 59(1984)-149601 and SHO 58(1983)-75779 and U.S. Patent No.4,792,504. However, in the cases where these proposed methods are used, the ion conductivity is surely improved, but film strength declines significantly. In other words, even in the cases where these proposed methods are used, there is also a possibility that electrolyte layers are deformed and destroyed by compression and slight short circuits take place after batteries or electrochromic devices are actually assembled by inserting thin films of the ion-conductive polymers between electrodes.
Further, in secondary batteries, as the volume of electrode active materials expands and contracts at charging and discharging, the electrolyte layers also receive compression and relaxation stress. Accordingly, it is also necessary to consider not only the improvement of the ion

conductivity but also the improvement of mechanical properties for improving the performance of the ion-conductive polymers.
JP10214615 describes the manufacture of a non-aqueous secondary battery and negative active material, wherein the adhesive strength of amorphous carbon with graphite particles is increased by a method, wherein a negative electrode contains carbon material with amorphous carbon adhered to a surface of the graphite particle oxidized by potassium permanganate as negative active material.
JP10284080 relates to a lithium secondary battery, wherein the surface of a graphitized carbonaceous material is covered with a carbonizable organic material, baked and crushed to form an amorphous carbon-converging graphitized carbonaceous material, which is furthermore treated with an acidic or alkaline solution. This material is used in a negative electrode.
JP11238503 discloses a non aqueous electrolyte secondary battery which is capable of enhancing high rate characteristics and charging/discharging cycle characteristics.
JP1186911 describes a polymer battery in which impedance is low and the change with the lapse of time is small.
JP10302838 describes a solid electrolyte with high ionic conductivity, high uniformity, high ionic conductivity especially at low temperature, using a polymer having solid strength sufficient to use as the solid electrolyte of an electrochemical element as a matrix, and provide an electrochemical element, especially a nonaqueous secondary battery using this solid electrolyte.

JP10208544 describes an ion conductivity and mechanical strengtn, restrain metal corrosion for use in a battery, and obtain superior self-discharge and cyclic characteristics in a given battery by preparing an electrolytic salt constituting a solid electrolyte together with a polymer matrix as a mixture of two or more kinds containing U-sulfonate at a specific ratio.
JP05335005 describes a lithium ion battery which is free from violent spout of the electrolyte decomposition gas out of a battery vessel accompanied with particulates of the active material even in case it is, in charged state, placed on a hot plate or the like which is heated to 250°C approximately.
Disclosure of Invention
After intensive study on the above problems, the inventors of the present invention have found that the use of graphite particles having amorphous carbon attached to the surface thereof for a negative electrode active material suppresses the decomposition of an ion-conductive compound contained in an ion conductor, further reduces the decline of the mechanical strength of an electrolyte with charge-discharge cycles and improves the performance of a battery using the ion-conductive compound.
The present invention provides a polymer battery comprising a negative electrode comprising at least a carbon material as an active material, an electrolyte layer, and a positive electrode comprising at least a lithium-containing chalcogenide as an active material, characterized in that the electrolyte layer contains an ion-conductive compound and a polymer fiber, and the carbon material comprises graphite particles having amorphous carbon attached to the surface thereof.
Brief Description of Accompanying Drawings

Fig. 1 is a schematic view illustrating a basic construction of a polymer battery in accordance with the present invention;
Fig. 2 is a schematic sectional view illustrating the construction of a polymer battery in accordance with Example 1 of the present invention, including an enlarged view of an essential part of the battery;
Fig. 3 is a graphical representation showing charge-discharge cycle characteristics of polymer batteries of Example 1 and Comparative Example 1 in accordance with the present invention;
Fig. 4 is a graphical representation showing dependency (average value) of discharge capacity on discharge current regarding 10 polymer batteries of Example 2 and Comparative Example 2 each; and
Fig. 5 is a graphical representation showing dependency (average value) of discharge capacity on discharge current regarding 10 polymer batteries of Example 3 and Comparative Example 5 each.
Embodiment for Carrying Out the Invention
To sum up, by use of graphite particles to the surfaces of which amorphous carbon is attached for the negative electrode active material and also by use of an ion-conductive compound and a polymer fiber for the electrolyte layer, the

present invention provides a polymer battery more excellent in the following points than the prior-art batteries, especially a polymer battery suitable for a small-size, light-weight battery:
1) Since the negative electrode active material is comprised of the graphite particles having amorphous carbon attached to the surface thereof, the ion-conductive compound can be prevented from decomposing. That means, it is possible to prevent explosion of the battery and leakage to the outside owing to an increase in the inner pressure of the battery caused by the generation of gas such as ethylene gas, carbon dioxide gas and others by the decomposition of the ion-conductive compound. Thus the battery is excellent in long-term reliability and safety.
2) To provide good performance and a high energy density. In the present invention, particularly, by improving the ion conductivity and the mechanical properties of the ion-conductive compound, it is possible to reduce the thickness of the film of the ion-conductive compound, thereby decreasing the inner resistance of the battery and improving the filling factor of the active materials in the battery, which leads to the achievement of the above objectives.
3) To provide extremely high workability. In the present invention, particularly, this objective is achieved by utilizing a method of putting a precursor of the ion conductive compound in the negative and positive electrodes beforehand

and then crosslinking said precursor with a precursor of the ion conductive compound in the electrolyte layer by ultraviolet irradiation or by heat.
In the present invention, since the negative electrode active material is comprised of the graphite particles having amorphous carbon attached to the surface thereof, the electrolyte layer containing the ion-conductive compound can be prevented from decomposing- Thereby the leakage can be eliminated and the long-term reliability can be improved.
The graphite particles having amorphous carbon attached to the surface thereof can be obtained as follows: A particulate carbon material to be a core (referred to as "core carbon material" or "carbon material to be a core" or simply "core" hereinafter) is dipped in a raw material for a coating carbon material (for example, coal or petroleum heavy oil such as tar, pitch or the like; referred to simply as "heavy oil, etc." hereinafter), and then, is separated from the heavy oil, etc. At this time, if a specific means is adapted, a carbon material in which the surface of the core is uniformly covered with pitch can be produced. The obtained carbon material is baked to give the above-mentioned graphite particles. It has been found out that the thus obtained particles of the carbon material of two-layer structure are spherical or ellipsoidal, or in a form approximate thereto, and have a form of carbon crystals whose edges are rounded. Further, measurement by

a BET method has clearly shown that the particles after the above-described treatment have a specific surface area smaller than that of the core carbon material before the treatment and that pores, which are related to the specific surface area by the BET method, are closed in some manner.
In this carbon material, pores related to the specific surface area measured by the BET method are filled by adhesion or coating of carbon of the heavy oil, etc., and the specific surface area is 5 m2/g of smaller (preferably about 1 to 5 m2/g). If the specific surface area is larger than 5 m2/g, it is unpreferable because a contact area with the electrolyte becomes larger and side reaction with the ion-conductive compound takes place more easily.
In the present invention, as the carbon material to be the core, is used a graphite material of high crystallinity whose average interplanar distance (doo2) in plane (002) is 0.335 to 0.340 nm, whose crystalline unit cell thickness (Lc) in a direction of plane (002) is 10 nm or more (more preferably, 40 nm or more) and whose crystalline unit cell thickness (La) in a direction of plane (110) is 10 nm or more (more preferably, 50 nm or more) by X-ray wide-angle diffraction analysis. If (doo2) is larger than 0.340 nm and (Lc) and (La) are smaller than 10 nm, it is unpreferable because the carbon material has low crystallinity and the discharge capacity decreases.
In the carbon material of the present invention, it is

characteristic that the crystallinity of the amorphous carbon adhering to or coating the surface of the core is lower than the above-mentioned crystallinity of the core.
The carbon material of the present invention has an absolute specific gravity within the range of 1.50 to 2.26 g/cm3. If the absolute specific gravity is lower than 1.50 g/cm3, it is not preferable because the filling factor of the negative electrode active material in the battery is low and the energy density is low. If the absolute specific gravity is higher than 2.26 g/cm3, the carbon material forms graphite single crystal and become poor in formability as a battery material.
The electrolyte layer contains an ion-conductive compound, a polymer fiber and optionally a Li salt. Particularly, the ion-conductive compound is preferably comprised of a crosslinked product obtained by crosslinking at least one of precursors of ion-conductive compounds represented by the following formulae:
(wherein Ri is a hydrogen atom or methyl group, Ai, A2 and A3 are bivalent residues having at least three ethylene oxide units (EO) and optionally containing a propylene oxide unit (PO), and the numbers of PO and EO satisfy PO/EO = 0 to 5 and EO + PO ^ 35),


(wherein R2 and R3 are independently a hydrogen atom or methyl group, A4 is a bivalent residue having at least three ethylene oxide units (EO) and optionally containing a propylene oxide unit (PO), and the numbers of PO and EO satisfy PO/EO - 0 to 5 and EO + PO ^ 35), and

(wherein R4 and R5 are independently a hydrogen atom or a methyl group, A5 is a bivalent residue having at least three ethylene oxide units (EO) and optionally containing a propylene oxide unit (PO), and the numbers of PO and EO satisfy PO/EO - 0 to 5 and EO + PO ^ 35).
Acrylates which are the following precursors of ion-conductive compounds are preferred since theircrosslinking reaction degree is high. That is because the reactivity of the acrylates is considered higher in the crosslinking reaction since methyl groups of methacrylates make steric hindrance. In the following formulae, methyl, ethyl, propyl and the like are mentioned as lower alkyl groups having a carbon number of one or more.


(wherein Rx* is a hydrogen atom or a lower alkyl group having a carbon number of one or more, Ai, A2 and A3 are bivalent residues containing three or more ethylene oxide units (EO) or containing ethylene oxide units and (a) propylene oxide unit(s) (PO), and the numbers of PO and EO satisfy PO/EO * 0 to 5 and EO + PO ^ 10),

(wherein R2' and R3* are independently a hydrogen atom or a lower alkyl group having a carbon number of one or more, A4 is a bivalent residue containing at least three ethylene oxide units (EO) or containing ethylene oxide units and (a) propylene oxide unit(s) (PO), and the numbers of PO and EO satisfy PO/EO = 0 to 5 and EO + PO ^ 10),

(wherein R4' and Rs* are independently a hydrogen atom or a lower alkyl group having a carbon number of one or more, As is a bivalent residue containing at least three ethylene oxide units (EO) or containing ethylene oxide units and (a) propylene oxide unit(s) (PO), and the numbers of PO and EO satisfy


The ion-conductive compound is used as a gel which contains an organic solvent containing ethylene carbonate and the Li salt. As the organic solvent, may be mentioned cyclic carbonates such as propylene carbonate, ethylene carbonate, etc.; cyclic esters such as y -butyrolactone, etc.; chain esters such as methyl propionate, ethyl propionate, etc.; chain carbonates such as diethyl carbonate, dimethyl carbonate, methylethyl carbonate, etc.; ethers such as tetrahydrofuran and its derivatives, 1,3-dioxane, 1,2-dimethoxyethane, methyl diglyme, etc.; nitriles such as acetonitrile, benzonitrile, etc.; dioxolan and its derivatives; sulfolan and its derivatives, which may be used singly or as a combination of two or more thereof. However, the organic solvent is not limited to these compounds. The blending ratio and blending method therefor are not limited.
Particularly preferred is a gel containing an organic electrolyte in which the Li salt is dissolved in a mixed organic solvent of ethylene carbonate (EC) with one or more solvents selected from propylene carbonate (PC), y -butyrolactone (GBL), ethylmethyl carbonate (EMC), dimethyl carbonate (DMC) and diethyl carbonate (DEC), since the solvent does not decompose easily in the negative electrode comprised of a graphite type carbon material as an active material.

Here, the weight ratio of the ion-conductive compound to the organic electrolyte is preferably within the range of 30 : 70 to 2 : 98. If the weight ratio of the ion-conductive compound is higher than 30, the ion conductivity is not sufficient, and if the weight ratio of the ion-conductive compound is lower than 2, sufficient mechanical strength is not obtained.
The content of EC in the organic electrolyte is 2 to 55 wt% and the content of the Li salt is 3 to 35 wt% because the ion conductivity is satisfactory enough. Further, if the content of EC is 2 to 35 wt%, the decrease of the ion conductivity at low temperatures is reduced.
The polymer fiber of the electrolyte layer (a fibrous organic compound) has high stability to the organic solvent if it is comprised of at least one of a polypropylene fiber, a polyethylene fiber and a polyester fiber. These polymer fibers may form nonwoven textiles having a gas permeability of 1 to 500 sec/cm3. A gas permeability lower than 1 sec/cm is not preferable because the ion conductivity is not enough, and a gas permeability higher than 500 sec/cm is not preferable because the mechanical strength is not enough and short circuits are liable to occur. Here the gas permeability means a volume of air transmitted per unit time period when air is applied onto 1 cm of nonwoven textile at a pressure of 124.5 Pa in accordance with a Frajour test method described in JIS

L1096 6,27.1.
Further, the weight ratio of the ion-conductive compound to the polymer fiber of the electrolyte layer may suitably be within the range of 91 : 9 to 50 : 50. If the weight ratio of the ion-conductive compound is higher than 91, it is not preferable because the mechanical strength is not enough, and if the ratio is lower than 50, it is not preferable because the ion conductivity is not enough.
The electrolyte layer may be formed by crosslinking the precursor of the ion-conductive compound, which has been put in either the negative electrode or the positive electrode beforehand, with the precursor of the ion-conductive compound, which has been put in the fibrous organic compound beforehand. Thereby, adhesion at the interface between the electrode and the electrolyte layer can be improved, and the cycle characteristics and high-current discharge characteristics of the battery can be improved.
As a crosslinking method, may be used a method using energy of light such as an ultraviolet ray, an electron beam, visible light or the like and a thermal method. It is also important to use a polymerization initiator, if necessary. In the crosslinking method using an ultraviolet ray or heat, especially, it is preferable to add several percent or less of the polymerization initiator. As the polymerization initiators, commercially available products may be used such as

2,2-dimethoxy-2-phenylacetophenone (DMPA), benzoyl peroxide (BPO) and the like. The wavelength of the ultraviolet ray may suitably be 250 to 360 nm.
The positive electrode active material may preferably be a lithium-containing chalcogen compound because it already contains a lithium source for lithium intercalation into the negative electrode of carbon, which is necessary for the first charging. A lithium-containing metal oxide, especially, allows the production of a battery having a high energy density because its charge/discharge potential is high. As examples thereof, may be mentioned LiCo02, L1NIO2, LiMn02, LiMn204 and LiCoxNi(i-xj02 (0 When the above-mentioned positive and negative electrode layers are formed, a binder and/or a conductor may be added as appropriate for the purpose of obtaining a uniformly mixed disperse coating liquid (paste) and/or for the purpose of improving characteristics (discharge characteristics and charge/discharge cycle characteristics) of mixed materials for the positive electrode and for the negative electrode.
In the case where the binder is used, may be mentioned a method using, as a coating liquid, a binder solution of a thermoplastic resin and a polymer having rubber elasticity dissolved in a solvent, in which the electrode active material and, if desired, the above-mentioned ion-conductive

compound are dispersed.
As examples of the above-mentioned binders, the following may be mentioned: polymers of acrylonitrile, methacrylonitrile, vinylidene fluoride, vinyl fluoride, chloroprene, vinyl pyrrolidone, vinyl pyridine, styrene and its derivatives, vinylidene chloride, ethylene, propylene, dienes (e.g., cyclopentadiene, 1,3-cyclohexadiene, butadiene, etc.), and copolymers of these compounds. Particular examples include poly acrylonitrile, polyvinylidene fluoride, polyvinyl pyrrolidone, polyethylene, polypropylene,
ethylene-propylene-diene terpolymer (EPDM), sulfonated EPDM, styrene-butadiene rubber and the like.
The conductor may desirably be an electron conductive material that does not hinder battery reaction by the electrodes and does not undergo chemical reaction. Typically, conductive materials such as artificial graphite, natural graphite (scaly graphite, flaky graphite, etc.), carbon black, acetylene black, Ketchen black, carbon fiber, powdered metals, conductive metal oxides and the like may be mixed in the mixed materials for the positive electrode and for the negative electrode for the purpose of improving the electron conductivity.
The amount of the binder added is not particularly limited, but may preferably be within the range of 1 to 25 wt% in the electrode. The amount of the conductor added is not

particularly limited either, but may preferably be within the range of 2 to 15 wt% in the electrode.
The mixed materials for the positive electrode and for the negative electrode of the present invention may desirably be applied onto a positive electrode collector and a negative electrode collector in a uniform thickness, for example, using means such as roll coating using an applicator roll or the like, a doctor blade method, spin coating, bar coater or the like. However, these means are not limitative ones. In the case where these means are used, it is possible to increase an actual surface area of the electrode active material contacting the electrolyte layer and a current collector. This enables the electrodes to be disposed in a thickness and a shape according to use.
The battery may be produced either after the method of making present the precursor of the ion-conductive compound of the present invention both in the positive or negative electrode layer and in the electrolyte layer or after the method of making present precursors of the ion-conductive compound in the positive electrode, in the negative electrode and in the electrolyte layer. Especially, according to the present invention, the former method enables either one of two interfaces between the positive electrode layer / the electrolyte layer / the negative electrode layer to be eliminated and the ion conductivity of the battery to be raised. Further, by the

former method, it is possible to simultaneously crosslink the precursor of the ion-conductive compound in the polymer fiber and that in one of the mixed materials for the electrodes, and therefore, the production process can be simplified.
For the positive electrode collector, are preferred materials such as aluminum, stainless steel, titanium, copper and the like, and for the negative electrode collector, are preferred materials such as stainless steel, iron, nickel, copper. These materials, however, are not limitative ones. The collectors may be in the form of foil, mesh, expanded metal, lath, porous substance, resin film coated with an electron conductive material, but their form is not limited thereto.
The battery may be in the shape of a cylinder, coin, film, card and the like, but its shape is not limited thereto. As package materials, may be mentioned metals, resins and the like. EXAMPLES
The present invention is now explained in detail with reference to examples, which should not be construed to limit the scope of the invention.
In all the following examples and comparative examples, when used precursors of ion-conductive compounds were crosslinked by ultraviolet rays, an initiator DMPA was used in an amount of 0.1 wt% of the precursors,
Fig.l and Fig. 2 are schematic views illustrating basic

constructions of polymer batteries produced in the present invention.
First, in Figs. 1 and 2, a polymer battery 8 is composed mainly of a positive electrode 5, an electrolyte layer 6, a negative electrode 7 and a package 4. Further, reference numeral 1 denotes a terminal of the negative electrode 7, 2 a terminal of the positive electrode 5 and 3 a sealing member of the package 4. (Example 1)
Polyvinylidene fluoride (PVDF), 9 wt%, was mixed as a
r
binder with carbon material particles having amorphous carbon attached to the surface thereof whose (d002) was 0.336 nm, (Lc) was 100 nm and (La) was 97 nm by X-ray wide-angle diffraction analysis and whose specific surface area was 2 m2/g by the BET method. With the resulting mixture, N-methyl-2-pyrrolidone (NMP) was mixed and dissolved to give a paste. The paste was coated onto a rolled copper foil of 20 u m thickness, dried and pressed to give a negative electrode. The area of this electrode was 9 cm2 and its thickness was 85 urn.
With powdered UC0O2 of 7 a m average particle diameter, were added 7 wt% of PVDF as a binder and 5 wt% of acetylene black of 2 urn average particle diameter as a conductor. With the resulting mixture, NMP was mixed and dissolved to give a paste. The paste was coated onto a rolled

aluminum foil of 20 u m thickness, dried and pressed to give a positive electrode. The area of this electrode was 9 cm2 and its thickness was 80 tt m.
The polymer fiber contained in the electrolyte layer was a nonwoven textile of polyester having a gas permeability of 380 sec/cm3, an area of 10 cm2 and a thickness of 20 //m.
These negative electrode, positive electrode and polymer fiber were immersed in a mixture solution of the following compound Ki with an average molecular weight of 7500 to 9000 which was a precursor of an ion-conductive compound:

(wherein Ai, A2 and A3 are bivalent residues containing at least three ethylene oxide units (EO) and optionally a propylene oxide unit (PO) and the numbers of PO and EO satisfy PO/EO =0.25), the following compound K2 with an average molecular weight of 3500 to 4500 which was a precursor of an ion-conductive compound:

(wherein A4 is a bivalent residue containing at least three ethylene oxide units (EO) and optionally a propylene oxide unit

(PO), and the numbers of PO and EO satisfy PO/EO = 0.25), and the following compound K3 with an average molecular weight of 400 to 550 which was a precursor of an ion-conductive compound:

(wherein A5 is a bivalent residue containing at least three ethylene oxide units (EO) and a propylene oxide unit (PO), and the numbers of PO and EO satisfy PO/EO « 0.25) in equivalent weight ratios, the mixture solution containing 4.5 wt% of UBF4 dissolved therein, and allowed to stand under reduced pressure for 15 minutes in order that the precursors penetrated inside pores.
The polymer fiber which formed a composite with the precursors of the ion-conductive compounds was laminated on the negative electrode which formed a composite with the precursors of the ion-conductive compounds. The resulting laminate was irradiated from above with an ultraviolet ray of 350 nm wavelength at an intensity of 30 mW/cm2 for three minutes. At this time, the weight ratio of the ion-conductive compounds to the polymer fiber was 90 : 10.
The positive electrode which formed a composite with the precursors of the ion-conductive compounds, as it was, was irradiated from above with an ultraviolet ray of 350 nm

wavelength at an intensity of 30 mW/cm2 for three minutes.
The resulting composite of the negative electrode, the polymer fiber and the ion-conductive compounds was bonded to the composite of the positive electrode and the ion-conductive compounds to produce a battery using the ion-conductive compounds. The total thickness of these positive electrode layer/electrolyte layer/negative electrode layer was 190 ttm. (Comparative Example 1)
PVDF as a binder, 9 wt%, was mixed with artificial graphite particles whose (d002) was 0.337 nm, (Lc) was 100 nm and (La) was 100 nm by X-ray wide-angle diffraction analysis and whose specific surface area was 10 m2/g by the BET method. NMP was admixed and dissolved to give a paste. The paste was coated onto a rolled copper foil of 20 nm thickness, dried and pressed to give a negative electrode. The area of this electrode was 9 cm2 and its thickness was 83 a m.
As the positive electrode, was used the same as used in Example 1.
The electrolyte layer and the battery were also made in the same manner as in Example 1, The total thickness of the obtained positive electrode layer/electrolyte layer/negative electrode layer was 188 tt m.
The batteries of Example 1 and Comparative Example 1 were charged at a constant current of 2.3 mA until they

reached a battery voltage of 4.1 V. After they reached 4.1V, the batteries were charged at the constant current for the total charge time of 12 hours. The batteries were discharged at a constant current of 2.3 mA until they reached a battery voltage of 2.75 V. The cycle characteristics of the batteries were evaluated under these charge/discharge conditions. The results are shown in Fig. 3,
From the results and Fig. 3, it is found that the battery using the carbon material having the amorphous carbon attached to the surface thereof is excellent in the cycle characteristics since the decomposition of the ion-conductive compound in the electrolyte layer and the destroy of the negative electrode/electrolyte layer interface is suppressed better. (Example 2)
PVDF as a binder, 7 wt%, was mixed with carbon material particles having amorphous carbon attached to the surface thereof whose (d002) was 0.337 nm, (Lc) was 100 nm and (La) was 95 nm by X-ray wide-angle diffraction analysis and whose specific surface area was 5 m2/g by the BET method. NMP was admixed and dissolved to give a paste. The paste was coated onto an electrolytic copper foil of 18 Mm thickness, dried and pressed to give a negative electrode. The area of this electrode was 9 cm2 and its thickness was 80 /im.
With powdered L1C0O2 of 5 & m average particle

diameter, were added 4 wt% of PVDF as a binder and 9 wt% of acetylene black of 2 u m average particle diameter as a conductor. NMP was admixed and dissolved to give a paste. The paste was coated onto a rolled aluminum foil of 20 ttm thickness, dried and pressed to give a positive electrode. The area of this electrode was 9 cm2 and its thickness was 85 li m.
The polymer fiber contained in the electrolyte layer was a nonwoven textile of polypropylene (PP) having a gas permeability of 250 sec/cm3, an area of 10 cm2 and a thickness of 20 n m.
An electrolyte was prepared in which 13 wt% of LiPFe was dissolved in a mixed solvent of EC and EMC (the EC content : 35 wt%). The electrolyte was mixed with the following compound K4 with an average molecular weight of 7500 to 9000 which was a precursor of an ion-conductive compound:

(wherein Ai, A2 and A3 are bivalent residues containing at least three ethylene oxide units (EO) and optionally a propylene oxide unit (PO) and the numbers of PO and EO satisfy PO/EO =0.25) in a weight ratio of 90 : 10. Thereafter, the negative electrode, the positive electrode and the polymer fiber were allowed to stand under reduced pressure for five minutes.

The above-described mixed solution of the electrolyte and the precursor compound K4 was poured thereon and allowed to stand for another five minutes.
The polymer fiber which formed a composite with the precursor of the ion-conductive compound and the electrolyte was laminated on the negative electrode which formed a composite with the precursor of the ion-conductive compound and the electrolyte. The resulting laminate was irradiated from above with an ultraviolet ray of 350 nm wavelength at an intensity of 40 mW/cm2 for three minutes. At this time, the weight ratio of the ion-conductive compound to the polymer fiber was 85 : 15.
The positive electrode which formed a composite with the precursor of the ion-conductive compound and the electrolyte was irradiated from above with an ultraviolet ray of 350 nm wavelength at an intensity of 40 mW/cm2 for three minutes.
The resulting composite of the negative electrode, the polymer fiber and the ion-conductive gel was bonded to the composite of the positive electrode and the ion-conductive gel to produce a battery using the ion-conductive compound. The total thickness of these positive electrode layer/electrolyte layer/negative electrode layer was 190 Mm. (Comparative Example 2)
For the negative electrode, the polymer fiber contained

in the electrolyte and the positive electrode, the same ones as used in Example 2 were used.
However, the negative electrode, the polymer fiber and the positive electrode were separately formed into composites with an ion-conductive gel whose precursor was the same as the precursor compound K4 in Example 2. The composites were bonded to each other to produce a battery using the ion-conductive compound. The total thickness of these positive electrode layer/ electrolyte layer/negative electrode layer was 195 Mm. (Comparative Example 3)
For the negative electrode and the positive electrode, the same ones as used in Example 2 were used.
However, the polymer fiber was not contained in the electrolyte layer. The negative electrode and the positive electrode were separately formed into composites with an ion-conductive gel whose precursor was the same as the precursor compound K4 in Example 2. The negative electrode and the positive electrode having formed the composites with the ion-conductive gel were bonded to each other to produce a battery using the ion-conductive compound. The total thickness of these positive electrode layer/electrolyte layer/negative electrode layer was 170 Mm.
The batteries of Example 2 and Comparative Examples 2 and 3 were charged at a constant current of 2.3 mA until

they reached a battery voltage of 4.1 V. After they reached 4.1V, the batteries were charged at the constant current for the total charge time of 12 hours. The batteries were discharged at constant currents of 2.3 mA, 5 mA, 10 mA and 20 mA until they reached a battery voltage of 2.75 V. The results of a charge/discharge test under the above conditions are shown in Fig. 4.
The results of this test shows that seven out of ten batteries of Comparative Examples 3 short-circuited during the initial charge, while none of batteries of Example 2 and Comparative Example 2 short-circuited. Regarding the discharge capacity versus discharge currents, the batteries of Example 2 exhibited a higher discharge capacity at a higher discharge current as understood from Fig. 4. Therefore, it has been found that a battery produced by bonding the positive electrode layer to the simultaneously crosslinked negative electrode layer and electrolyte layer containing the polymer fiber has a reduced contact interface, and furthermore allows the thickness of the ion-conductive compound layer to be reduced, and thus the discharge load characteristics are improved. It has also been found that, in the case where the polymer fiber is not formed into a composite with the electrolyte layer, the thickness of the ion-conductive compound layer can be reduced, but the mechanical strength weakens and the battery is liable to short-circuit.

(Example 3)
PVDF as a binder, 7 wt%, was mixed with carbon material particles having amorphous carbon attached to the surface thereof whose (d002) was 0.339 nm, (Lc) was 60 nm and (La) was 40 nm by X-ray wide-angle diffraction analysis and whose specific surface area was 5 m2/g by the BET method. NMP was admixed and dissolved to give a paste. The paste was coated onto an electrolytic copper foil of 18 n m thickness, dried and pressed to give a negative electrode. The area of this electrode was 9 cm2 and its thickness was 85 U m.
With powdered LiCo02 of 7 ii m average particle diameter, were added 4 wt% of PVDF as a binder and 9 wt% of acetylene black of 2 um average particle diameter as a conductor. NMP was admixed and dissolved to give a paste. The paste was coated onto a rolled aluminum foil of 20 lira thickness, dried and pressed to give a positive electrode. The area of this electrode was 9 cm2 and its thickness was 80 u m.
The polymer fiber contained in the electrolyte layer was a nonwoven textile of polyester having a gas permeability of 490 sec/cm3, an area of 10 cm2 and a thickness of 25// m.
An electrolyte was prepared in which 15 wt% of LiN(CF302)2 was dissolved in a mixed solvent of EC and DMC (the EC content : 20 wt%). The electrolyte was mixed with a precursor of an ion-conductive compound with an average molecular weight of 7500 to 9000 which was the same as the

precursor compound K4 in Example 2 in a weight ratio of 95 : 5. Thereafter, the negative electrode, the positive electrode and the polymer fiber were allowed to stand under reduced pressure for two minutes. The above-described mixed solution was poured thereon and allowed to stand for another fifteen minutes.
The polymer fiber which formed a composite with the precursor of the ion-conductive compound and the electrolyte was laminated on the negative electrode which formed a composite with the precursor of the ion-conductive compound and the electrolyte. The resulting laminate was irradiated from above with an ultraviolet ray of 360 nm wavelength at an intensity of 40 mW/cm2 for two minutes. At this time, the weight ratio of the ion-conductive compound to the polymer fiber was 50 ; 50,
The positive electrode which formed a composite with the precursor of the ion-conductive compound and the electrolyte was from above irradiated with an ultraviolet ray of 350 nm wavelength at an intensity of 40 mW/cm2 for two minutes.
The resulting composite of the negative electrode, the polymer fiber and the ion-conductive gel was bonded to the composite of the positive electrode and the ion-conductive gel to produce a battery using the ion-conductive compound. The total thickness of these positive electrode layer/electrolyte

layer/negative electrode layer was 195 ii m. (Comparative Example 4)
A battery was produced in the same manner as in Example 3 except that the gas permeability of a nonwoven textile of polyester in the electrolyte layer was 510 sec/cm3 and the weight ratio of the ion-conductive compound and the polymer fiber was 97 : 3. (Comparative Example 5)
A battery was produced in the same manner as in Example 3 except that the polymer fiber in the electrolyte layer is a nonwoven textile of PP having a gas permeability of 0.5 sec/cm3, an area of 10 cm2 and a thickness of 20 n m and the weight ratio of the ion-conductive compound to the polymer fiber was 40 : 60.
The batteries of Example 3 and Comparative Examples 4 and 5 were charged at a constant current of 2.1 mA until they reached a battery voltage of 4.1 V. After they reached 4.1 V, the batteries were charged at the constant voltage for the total charge time of 12 hours. The batteries were discharged at constant currents of 2.1 mA, 5 mA, 10 mA and 20 mA until they reached a battery voltage of 2.75 V. The results of a charge/discharge test under these conditions are shown in Fig. 5.
In this test, five out of ten batteries of Comparative Example 4 short-circuited during the initial charge, while none

of batteries of Example 3 and Comparative Example 5 short-circuited. Regarding the discharge capacity versus discharge currents, the batteries of Example 3 exhibited a higher discharge capacity at a higher current as understood from Fig. 5. Therefore, it has been found that, if the gas permeability of the polymer fiber in the electrolyte layer exceeds 500 sec/cm3, the mechanical strength of the electrolyte layer declines and short circuit is easily induced, and that, if the gas permeability of the polymer fiber is below 1 sec/cm3, openings in the polymer fiber decreases and the resistance of the electrolyte layer rises, which results in a decline in the discharge load characteristics of the battery. (Example 4)
PVDF as a binder, 7 wt%, was mixed with carbon material particles having amorphous carbon attached to the surface thereof whose (d002) was 0.338 nm, (Lc) was 100 nm and (La) was 100 nm by X-ray wide-angle diffraction analysis and whose specific surface area was 3 m2/g by the BET method. NMP was admixed and dissolved to give a paste. The paste was coated onto an electrolytic copper foil of 18 n m thickness, dried and pressed to give a negative electrode. The area of this electrode was 9 cm2 and its thickness was 83 u m.
With powdered UC0O2 of 10 nm average particle diameter, were added 3 wt% of PVDF as a binder and 6 wt% of acetylene black of 2 fivn average particle diameter as a

conductor. NMP was admixed and dissolved to give a paste. The paste was coated onto a rolled aluminum foil of 20 n m thickness, dried and pressed to give a positive electrode. The area of this electrode was 9 cm2 and its thickness was 80 n m.
The polymer fiber contained in the electrolyte layer was a nonwoven textile of PP having a gas permeability of 350 sec/cm3, an area of 10 cm2 and a thickness of 20 M m.
An electrolyte was prepared in which 12 wt% of LiBF4 was dissolved in a mixed solvent of EC and EMC (the EC content : 55 wt%). The electrolyte was mixed with a precursor of an ion-conductive compound with an average molecular weight of 7500 to 9000 which was the same as the precursor compound K4 in Example 2 in a weight ratio of 95 : 5. Thereafter, the negative electrode, the positive electrode and the polymer fiber were allowed to stand under reduced pressure for two minutes. The above-described mixed solution was poured thereon, and allowed to stand for another fifteen minutes.
The polymer fiber which formed a composite with the precursor of the ion-conductive compound and the electrolyte was laminated on the negative electrode which formed a composite with the precursor of the ion-conductive compound and the electrolyte. The resulting laminate was irradiated from above with an ultraviolet ray of 360 nm wavelength at an intensity of 40 mW/cm2 for two minutes. At this time, the

weight ratio of the ion-conductive compound to the polymer fiber was 75 : 25.
The positive electrode which formed a composite with the precursor of the ion-conductive compound and the above-described electrolyte was irradiated from above with an ultraviolet ray of 355 nm wavelength at an intensity of 40 mW/cm2 for two minutes.
The resulting composite of the negative electrode, the polymer fiber and the ion-conductive gel was bonded to the composite of the positive electrode and the ion-conductive gel to produce a battery using the ion-conductive compound. The total thickness of these positive electrode layer/electrolyte layer/negative electrode layer was 185 u m. (Example 5)
A battery similar to that of Example 4 was produced except that, in the electrolyte, 14 wt% of LiBF* was dissolved in a mixed solvent of EC and GBL (the EC content : 35 wt%). (Example 6)
A battery similar to that of Example 4 was produced except that, in the electrolyte, 13 wt% of LiBF4 was dissolved in a mixed solvent of EC and DEC (the EC content : 30 wt%). (Example 7)
A battery similar to that of Example 4 was produced except that, in the electrolyte, 12 wt% of LiPFe was dissolved in a mixed solvent of EC, PC and EMC (EC : PC : DEC - 3 : 30 ;

67 by weight). (Comparative Example 6)
A battery similar to that of Example 4 was produced except that, in the electrolyte, 12 wt% of LiPF6 was dissolved in a mixed solvent of EC and DMC (the EC content : 60 wt%).
The batteries of Examples 4 to 7 and Comparative Example 6 were charged at a constant current of 2.0 mA until they reached a battery voltage of 4.1 V. After they reached 4.1 V, the batteries were charged at the constant voltage for the total charge time of 12 hours. The batteries were discharged at constant current of 2.0 mA until they reached a battery voltage of 2.75 V. The initial discharge was carried out at a temperature of 25 'C and the second discharge was carried out at a temperature of - 20 t. The following tables show the ratio of the second discharge capacity to the first discharge capacity.



As shown in Table 2 and further as shown in the following table, it has been proved that a battery in which the content of EC exceeds 55 wt% hardly discharge in a low-temperature ambience at - 20 *C. It has also been proved that the use of the carbon material having amorphous carbon attached to the surface thereof can avoid the decomposition of PC almost completely. Therefore, it has been found that the carbon material having amorphous carbon attached to the surface thereof used in the present invention lessens the decomposition of the ion-conductive compound and is a material for negative electrodes of batteries excellent in

reliability and safety. (Example 8)
a) PVDF as a binder, 9 parts by weight, was mixed with 100 parts by weight of carbon material particles comprising graphite particles having amorphous carbon attached to the surface thereof whose (d002) was 0.336 nm, (Lc) was 100 nm and (La) was 97 nm by X-ray wide-angle diffraction analysis and whose specific surface area was 2 m2/g by the BET method. NMP was admixed and dissolved to give a paste. The paste was coated onto a rolled copper foil of 20 Mm thickness, dried and pressed to give a negative electrode. The area of this electrode was 9 cm2 and its thickness was 85 u m.
An electrolyte was prepared in which 1.0 mol/L of LiBF4 was dissolved in a mixed solvent of EC, PC, GBL and EMC (EC : PC : GBL : EMC - 30 : 20 : 20 : 30 (volume %)). The electrolyte was mixed with the following compounds K5 and K6 which were precursors of ion-conductive polymers in a weight ratio of 90 : 5 : 5. To the resulting mixture, DMPA 1000 ppm was added to prepare a polymerization liquid.
The compound Ks has an average molecular weight of 7500 to 9000 and is represented by the following formula:


(wherein Ai, A2 and A3 are bivalent residues containing at least three EO and optionally PO and the numbers of PO and EO satisfy PO/EO =0.25).
The compound K6 has an average molecular weight of 2500 to 3500 and is presented by the following formula:

(wherein A5 is a bivalent residue containing at least three EO and optionally PO, and the numbers of PO and EO satisfy PO/EO = 0.25).
The above-mentioned negative electrode was allowed to stand under reduced pressure for five minutes and the above-described mixed solution was poured onto the negative electrode, which was then allowed to stand for another 15 minutes.
(b) A nonwoven textile of polyester having a gas permeability of 380 sec/cm3, an area of 10 cm2 and a thickness of 20 um was used as a fibrous organic compound of the electrolyte layer.
An electrolyte was prepared in which 1.0 mol/L of LiBF4 was dissolved in a mixed solvent of EC, PC, GBL and EMC (EC : PC : GBL : EMC - 30 : 20 : 20 : 30 (volume %)). The electrolyte was mixed with the compounds Ks and K6 which were precursors of ion-conductive polymers in a weight ratio of

90 : 5 : 5. To the resulting mixture, DMPA 1000 ppm was added to prepare a polymerization liquid.
Thereafter, the fibrous organic compound having formed a composite with the precursors of the ion-conductive polymers was laminated on the negative electrode. The laminated was irradiated from above with an ultraviolet ray of 365 nm wavelength at an intensity of 30 mW/cm2 for three minutes. At this time, the weight ratio of the ion-conductive polymers to the fibrous organic compound was 90 : 10.
By irradiation with the ultraviolet ray for a specific period of time, an ion-conductive polymer was formed in a gel state to be integrated with the negative electrode and the fibrous organic compound. The thus obtained ion-conductive polymer layer was 20 Am thick.
c) With 100 parts by weight of powdered LiCo02 of 7 M m average particle diameter, were mixed 7 parts by weight of PVDF as a binder and 5 parts by weight of acetylene black as a conductor. NMP was admixed and dissolved to give a paste. The paste was coated onto a rolled aluminum foil of 20 urn thickness, dried and pressed to give a positive electrode. The area of this electrode was 9 cm2 and its thickness was 80 tt m.
An electrolyte was prepared in which 1.0 mol/L of LiBF4 was dissolved in a mixed solvent of EC, PC, r BL and EMC (EC : PC : r BL : EMC - 30 : 20 : 20 : 30 (volume %)). The electrolyte was mixed with the compounds Ks and Ke which

were precursors of ion-conductive polymers in a weight ratio of 90 : 5 : 5. To the resulting mixture, DMPA 1000 ppm was added to prepare a polymerization liquid.
Next, the above-described positive electrode was allowed to stand under reduced pressure for five minutes. The above mixed solution was poured onto the positive electrode, cast and allowed to stand for another five minutes.
Thereafter, the positive electrode, with nothing put on, was irradiated with an ultraviolet ray of 365 nm wavelength at an intensity of 30 mW/cm2 for three minutes. Thereby an ion-conductive polymer was formed in a gel state to be integrated with the positive electrode. The thus obtained ion-conductive polymer layer was 10 Mm thick.
d) A battery of Example 8 was produced by bonding the (ion-conductive polymer + fibrous organic compound) layer / the negative electrode / the negative electrode collector obtained in b) to the positive electrode collector / the positive electrode / the ion-conductive polymer layer obtained in a). The total thickness of these positive electrode layer / electrolyte layer / negative electrode layer was 190 um. (Example 9)
A battery of Example 9 was produced in the same manner as in Example 8 except that the compound K6 in Example 8 was replaced with the following compound K7. The total thickness of the positive electrode layer / electrolyte layer

/ negative electrode layer was 190 tim.
The compound K7 has an average molecular weight of 200 to 300 and is presented by the following formula:

(wherein Ae is a bivalent residue containing at least three EO and optionally PO, and the numbers of PO and EO satisfy PO/EO - 0.25). (Example 10)
A battery of Example 10 was produced in the same manner as in Example 8 except that the compound Ke in Example 8 was replaced with the following compound Ks. The total thickness of the positive electrode layer / electrolyte layer / negative electrode layer was 190 um.
The compound Ks has an average molecular weight of 3500 to 4500 and is presented by the following formula:

(wherein A4 is a bivalent residue containing at least three EO and optionally PO, and the numbers of PO and EO satisfy PO/EO - 0.25). (Example 11)
A battery of Example 11 was produced in the same

manner as in Example 8 except that the mixed solvent of EC, PC, GBL and EMC (EC : PC : GBL : EMC = 30 : 20 : 20 ; 30 (volume %)) in Example 8 was replaced with a mixed solvent of EC, PC and EMC (EC : PC : EMC - 35 : 35 : 30 (volume %)). The total thickness of the positive electrode layer / electrolyte layer / negative electrode layer was 190 Mm. (Comparative Example 7)
A battery of Comparative Example 7 was produced in the same manner as in Example 8 except that the negative electrode active material in Example 8 was replaced with an artificial graphite having properties of (d002) = 0.337 nm, (Lc) = 100 nm and (La) =100 nm by X-ray wide-angle diffraction analysis and a specific surface area of 10 m2/g by the BET method. The total thickness of the positive electrode layer / electrolyte layer / negative electrode layer was 190 Mm.
The following table 4 summarizes the constitution of the batteries of Examples 2, 8 to 11 and Comparative Example 7.



The batteries of Examples 2, 8 to 11 and Comparative Example 7 were charged at a constant current of 2.3 mA until they reached a battery voltage of 4.1 V. After they reached 4.1 V, the batteries were charged at the constant voltage for the total charge time of 12 hours. The batteries were discharged at a constant current of 2.3 mA and 10 mA until they reached a battery voltage of 2.75 V. Fig.5 shows the discharge capacity and the charge/discharge efficiency at the first cycle when the discharge was conducted under the above conditions. Table 5

As understood from Table 5, as compared with the battery of Example 2, the batteries of Examples 8 to 11 exhibited equivalent or better discharge capacities at high load. Equivalent results are shown regarding the charge/discharge at the first cycle.
That is, it has been proved that a precursor of an

ion-conductive polymer constituted of acrylate is more preferable than one constituted of methacrylate.
On the other hand, the discharge capacity and charge/discharge efficiency of the battery of Comparative Example 7 were by far lower than those of the batteries of the examples. That shows that, with use of the carbon material of the present invention in which amorphous carbon is attached to the surface of graphite particles, ion-conductive polymers containing PC are sufficiently usable in the present battery system.
More particularly, it has been found that the battery in which the carbon material of the present invention and the ion-conductive polymer are combined solves the problem as reported with conventional graphite type carbon materials that the presence only of 10 % PC in the electrolyte induces the decomposition of PC remarkably and renders charge/discharge operation impossible.
By use of a polymer battery comprising a negative electrode comprising at least a carbon material as an active material, an electrolyte layer and a positive electrode comprising at least a lithium-containing chalcogenide as an active material, wherein the electrolyte layer contains an ion-conductive compound and a polymer fiber, and the carbon material comprises graphite particles having amorphous

carbon attached to the surface thereof, it has become possible to suppress the decomposition of the ion-conductive compound caused by charge and discharge, and as a result, to eliminate the short circuit, expansion and leakage of the battery and improve the reliability of the battery.
Furthermore, by use of the material for positive electrodes of the present invention, it has become possible to reduce the amount of the EC component in the ion-conductive compound and produce a battery which can exhibit excellent charge/discharge characteristics at low temperatures.
Also, when the battery is produced, by including the precursor of the ion-conductive compound beforehand in the above-mentioned negative electrode and positive electrode and crosslinking the precursor with the precursor of the ion-conductive compound in the electrolyte layer, it is possible to reduce the number of interfaces between the electrodes and the electrolyte. Thus the internal resistance of the battery can be reduced, and the battery can be produced to be excellent in high load discharge characteristics and high-speed charge characteristics. Further, the electrode and electrolyte can be integrally formed and the productivity of the battery can be improved.
If the precursor of the ion-conductive compound of the present invention is a mono-functional, di-functional or tri-functional acrylate, the crosslinking reaction shows a high

degree of reaction. Accordingly, the precursor does not remain unreacted within the electrode or at the interface, and consequently, side reaction on the electrodes can be suppressed and the battery can be produced to have good cycle characteristics and high reliability.




WE CLAIM:
1. A polymer battery comprising:
a negative electrode comprising, as an active material, a carbon material containing graphite particles having amorphous carbon attached to the surface thereof;
an electrolyte layer; and
a positive electrode comprising at least a lithium-containing chalcogenide as an active material,
wherein the electrolyte layer forms a composite obtained by crosslinking a precursor of an ion-conductive compound contained in the positive electrode and/or the negative electrode together with a precursor of an ion-conductive compound contained in a polymer fiber forming the electrolyte layer, characterized in that the ion-conductive compound is used as a gel containing a Li salt and an organic solvent containing ethylene carbonate, wherein the content of ethylene carbonate in the electrolyte layer is 2 to 55 wt% and the content of the Li salt is 3 to 35 wt% and wherein the polymer fiber is a nonwoven textile having a gas permeability of 1 to 500 sec/cm .
2. A polymer battery as claimed in claim 1, wherein the negative electrode and
the positive electrode contain the same ion-conductive compound as the electrolyte
layer contains, the ion-conductive compound in the negative electrode, the positive
electrode and the electrolyte layer are formed by crosslinking corresponding
precursors, and the crosslinking of the precursor of the ion-conductive compound in
the electrolyte layer is carried out together with the crosslinking of the precursor of the
ion-conductive compound contained in the negative and/or positive electrode.

3. A polymer battery as claimed in claim 2, wherein the positive electrode, the
negative electrode and the electrolyte layer form a single composite obtained by
including the precursor of the ion-conductive compound beforehand in the polymer
fiber of the electrolyte layer, the positive electrode arid the negative electrode and
crosslinking the precursor by applying an ultraviolet ray onto the polymer fiber, the
positive electrode and the negative electrode.
4, A polymer battery as claimed in any one of claims 1 to 3, wherein the
electrolyte layer comprises a Li salt and the ion-conductive compound is a crosslinked
substance obtained by crosslinking at least one of precursors of ion-conductive
compounds represented by the following formulae:

(wherein Rt is a hydrogen atom or methyl group, A|, A2 and A3 are bivalent residues having at least three ethylene oxide units (EO) or having (an) ethylene oxide unit(s) (EO) and (a) propylene oxide unit(s) (PO), the numbers of PO and EO satisfy PO/EO = 0 to 5, and the average molecular weight is 7500 to 9000),

(wherein R2 and R3 are independently a hydrogen atom or methyl group, A4 is a bivalent residue having at least three ethylene oxide units (EO) or having (an) ethylene oxide unit(s) (EO) and (a) propylene oxide unit(s) (PO), and the numbers of PO and EO satisfy PO/EO = 0 to 5),


(wherein R4 and R5 are independently a hydrogen atom or a methyl group, A5 is a bivalent residue having at least three ethylene oxide units (EO) or having (an) ethylene oxide unit(s) (EO) and (a) propylene oxide unit(s) (PO), and the numbers of PO and EO satisfy PO/EO - 0 to 5).
5. A polymer battery as claimed in any one of claims 1 to 3, wherein the electrolyte layer comprises a Li salt and the ion-conductive compound is a crosslinked substance obtained by crosslinking at least one of precursors of ion-conductive compounds represented by the following formulae:

(wherein Rj is a hydrogen atom or a lower allcyl group having a carbon number of 1 or more, A\ A2 and A3 are bivalent residues having at least three ethylene oxide units (EO) or having (an) ethylene oxide unit(s) (EO) and (a) propylene oxide unit(s) (PO), the numbers of PO and EO satisfy PO/EO = 0 to 5, and EO + PO £10, and the average molecular weight is 7500 to 9000),

(wherein R2 and R3* are independently a hydrogen atom or a lower allcyl group having a carbon number of 1 or more, A4 is a bivalent residue having at least three ethylene oxide units (EO) or having (an) ethylene oxide unit(s) (EO) and (a) propylene oxide unit(s) (PO), and the numbers of PO and EO satisfy PO/EO « 0 to 5 and EO + PO > 10),

(wherein R* and R5 are independently a hydrogen atom or a lower alkyl group having a carbon number of 1 or more, A5 is a bivalent residue having at least three ethylene oxide units (EO) or having (an) ethylene oxide unit(s) (EO) and (a) propylene oxide unit(s) (PO), and the numbers of PO and EO satisfy PO/EO = 0 to 5 and EO + PO > 3).
6. A polymer battery as claimed in claim 4 or 5, wherein the electrolyte layer contains an organic electrolyte in which at least one Li salt selected from LiBF4, LiPFe and LiN(CF3S02)2 is dissolved in a mixed organic solvent composed of ethylene carbonate and at least one solvent selected from propylene carbonate, y-butyrolactone, ethylmethyl carbonate, dimethyl carbonate and diethyl carbonate.
7. A polymer battery as claimed in claim 6, wherein the weight ratio of the ion-conductive compound to the organic electrolyte is within a range from 30 : 70 to 2 : 98.
8. A polymer battery as claimed in any one of claims 1 to 7, wherein the polymer fiber comprises at least one of polypropylene fiber, polyethylene fiber and polyester fiber.
9. A polymer battery as claimed in any one of claims 1 to 8, wherein the weight ratio of the ion-conductive compound to the polymer fiber in the electrolyte layer is within a range from 91 : 9 to 50: 50.
10. A polymer battery as claimed in any one of claims 1 to 9, wherein the graphite particles having amorphous carbon attached to the surface thereof have an average interplanar distance (doo2) in plane (002) of 0.335 to 0.340 nm, a crystalline unit

battery thickness (Lc) in a direction of plane (002) of 10 nm or more (more preferably, 40 nm or more), a crystalline unit battery thickness (La) in a direction of plane (110) is 10 nm or more and a specific surface area of 5 m2/g or less.


Documents:

in-pct-2002-0783-che abstract duplicate.pdf

in-pct-2002-0783-che claims duplicate.pdf

in-pct-2002-0783-che description (complete) duplicate.pdf

in-pct-2002-0783-che drawings duplicate.pdf

in-pct-2002-783-che-abstract.pdf

in-pct-2002-783-che-assignment.pdf

in-pct-2002-783-che-claims .pdf

in-pct-2002-783-che-correspondence others.pdf

in-pct-2002-783-che-correspondence po.pdf

in-pct-2002-783-che-description complete.pdf

in-pct-2002-783-che-drawings.pdf

in-pct-2002-783-che-form 1.pdf

in-pct-2002-783-che-form 26.pdf

in-pct-2002-783-che-form 3.pdf

in-pct-2002-783-che-form 5.pdf

in-pct-2002-783-che-other documents.pdf

in-pct-2002-783-che-pct.pdf


Patent Number 220623
Indian Patent Application Number IN/PCT/2002/783/CHE
PG Journal Number 29/2008
Publication Date 18-Jul-2008
Grant Date 29-May-2008
Date of Filing 27-May-2002
Name of Patentee SHARP KABUSHIKI KAISHA
Applicant Address
Inventors:
# Inventor's Name Inventor's Address
1 MITATE, TAKEHITO
2 SADA, TSUTOMU
3 NISHIMURA, NAOTO
4 NISHIJIMA, MOTOAKI
5 TORATA, NAOTO
6 YAMADA, KAZUO
7 TAKEDA, KAZUNARI
PCT International Classification Number H01M 10/40
PCT International Application Number PCT/JP2000/008142
PCT International Filing date 2000-11-17
PCT Conventions:
# PCT Application Number Date of Convention Priority Country
1 2000-324111 2000-10-24 Japan
2 11-330245 1999-11-19 Japan