Title of Invention

METHOD FOR CONTINUOUS CASTING FOR PRODUCTION OF STRANDS AND CONTINUOUS CASTING PLANT FOR CARRYING OUT THE METHOD

Abstract Method for continuous casting for production of strands, the cross-section of which is reduced during solidification in the manner that the casting is, in particular, in an oscillating chill mould and the strand cross-section is linearly reduced over a minimum length of the strand guiding means directly below the chill mould, i.e. direct strand reduction, and a non-linear strand cross-sectional reduction, for example in accordance with the square root function, i.e. soft reduction, is carried out subsequently over the remaining strand guidance at most up to directly before the liquid phase point and continuous casting plant for carrying out the method.
Full Text Field of the Invention
The present invention relates to a method for continuous casting for production of strands and continuous casting plant for carrying out the method.
Description of the Related Art
It is known in the art that strands are manufactured in such high-speed plants generally with a solidification thickness of between 18 and 450 mm and casting speeds of up to at most 15 m/min., for example, in plants for casting slabs, blooms and billets with quadratic or round profiles, wherein a reduction of the strand cross-section is preferably carried out during the solidification after the strand emerges from the mold.
This technology of casting and rolling of thin slabs or round billets is known from German patents 44 03 048, 44 03 049 and 41 39 242; in the case of thin slabs, this technology is used daily in production plants.
For example, a thin slab having a thickness of, for example, 65 mm is reduced to 40 mm in segment 0 which is arranged directly underneath the mold. This strand thickness reduction of 25 mm or 38.5% may be a disadvantage with respect to the quality of certain steels which are sensitive to intemal ruptures. Thus, the internal deformation of the strand, due to the strand thickness reduction or also called casting and rolling, may trigger intemal ruptures because the critical deformation of the material is exceeded at the inner strand shell liquid/solid, but also at the outer strand shell.
The above example is based on a circular arc segment 0 which has a length of 2 m and which does not introduce bending work or bending deformation into the strand shell. In this case, the deformation speed of the strand shell during casting and during solidification, which represents a measure for the strand deformation, is 1.25 mm/s at a casting speed of 6 m/min. When the casting speed is increased to, for example, 10 m/min., this value of the deformation speed increases to 2.08 mm/s and becomes very

critical. Such internal deformations caused by casting and rolling are not only critical for deep drawing steel qualities which are relatively insensitive to internal deformations, but primarily for sensitive steels, such as microalloyed APX-80 qualities.
In addition, in vertical bending units in which usually bending of the strand occurs in the segment underneath the mold simultaneously with the deformation caused by casting and rolling, the bending deformation introduced into the strand is significantly increased, so that the danger of exceeding the critical deformation and, thus, the formation of cracks is even further increased.
SUMMARY OF THE INVENTION
Therefore, in view of the findings and relationships describes above, it is the primary object of the present invention to provide technical method measures and simple apparatus features for predetermining the deformation density of the strand cross-section reduction in such a way that the critical deformation of the strand is not exceeded while taking into consideration the casting speed and also the steel quality.
In accordance with the present invention, the continuous casting method for producing strands, wherein the cross-section of the strands is reduced during the solidification, includes casting into a mold, particularly an oscillating mold, and reducing the strand cross-section linearly over a minimum length of the strand guiding means immediately underneath the mold, i.e., casting and rolling, and subsequently carrying out a further strand cross-section reduction through the remaining strand guiding means, i.e., soft reduction, up to maximum reduction immediately in front of the final solidification or sump tip.
The continuous casting plant according to the present invention for carrying out the above-described method includes the following elements:
an oscillating mold;

a segment 0 which hnearly reduces the strand in its cross-section at most by 40% over a length of at least 1 m;
a remaining strand guiding means which reduces the strand in its cross-section up to at most immediately following the sum tip, i.e., soft reduction; wherein
the total reduction of the strand cross-section in segment 0 and in the remaining strand guiding means is configured to be up to 60%.
The features of the present invention are applicable to all sizes cast in a strand and also for all types of continuous casting plants.
The following unexpected solution according to the present invention for achieving the above-described objects will be explained in more detail in connection with a thin slab, wherein the invention is particularly discussed with respect to casting of thin slabs having a thickness of between 60 and 120 mm after solidification, i.e., the thickness of the slab in the edge areas is, for example, a minimum of 70 mm and a maximum of 160 nmi at the mold exit. In accordance with the prior art, the reduction of the strand thickness, which usually takes place between the upper and the lower side of a strand guiding means, is today under test conditions at most 60%, i.e., a slab having a thickness of 50 mm is reduced to about 20 mm over a roll gap length of about 200 mm, and is under production conditions at most 38.5%, i.e., the strand is reduced fi-om 65 to 40 mm over the length of the segment 0 which is about 2 m, wherein segment 0 is arranged underneath the mold. In both cases, the maximum casting speed is 6 m/min.
The invention will be described on the basis of an example of a thin slab having a thickness of 100 mm at the mold exit and a solidification thickness of 80 mm. The invention proposes a type of distribution and the realization of the slab thickness reduction during the solidification of the thin slab in the strand guiding stand for, for example, casting speeds of 6 and 10 m/min.

In tables 1 and 1.1, the essential process and apparatus data of the invention are compared to those of the prior art. Table 1 shows the data for casting speeds of 6 m/min and table 1.1 shows the data for casting speeds of 10 m/min.
In both tables, the total reduction of the thickness of the strand of 20 mm during the solidification is varied in its distribution between the segment 0 and the remaining strand guiding means, i.e., the segments 1 through at most 13. In the tables, the prior art is illustrated by a total reduction of the strand thickness of 20 mm carried out solely in segment 0 (compare items 19 through 22 in column 1). This clearly shows that the reduction speed of the strand is increased in the segment 0 which has a length of 3 m from 0.67 to 1.11 mm/s, triggered by the strand thickness reduction or the casting and rolling process and, thus, functionally the strand shell deformation, wherein the casting speed increases from 6 m/min to 10 m/min.
Items 19-22 and 23-28, columns 2, 3 and 4 and items 29-34 represent the solution according to the present invention which results in a significant lowering of the deformation density of the strand shell by a redistribution of the total thickness reduction of 20 mm between the segment 0 and the segments 1-n, also called soft reduction. This redistribution will be explained in detail with the aid of the following examples:
15 mm in segment 0 and 5 mm in the segments 1-n, items 19-28, column 2;
10 mm in segment 0 and 10 mm in segments 1-n, items 19-28, column 3;
5 mm in segment 0 and 15 mm in segments 1-n, items 19-28, column 4;
20 mm in segments 0-n, items 29-34.
In this manner, the reduction speed, and, thus the functional deformation density of the strand shell with a 20 mm total thickness reduction and 10 m/min casting speed can be reduced from:
1.11 mm/s, 20 mm in segment 0, according to the prior art, item 21, column 1, to 0.114 mm/s, 20 mm in segments 0-13, item 33.

However, as a result of displacing a portion of the thickness reduction from segment 0 into the segments 1-13 or 1-2, depending on the casting speed, the work to be introduced into the strand increases with increasing strand shell thickness. Therefore, the present invention takes into account that an optimum distribution of the total thickness reduction in the total strand guiding means between the segment 0 and the segment n, which reaches immediately behind the final solidification, also includes the strand shell thickness. This is achieved in an advantageous manner by a square root function over the solidification time either in the areas of the segments 1-n, soft reduction or in the areas of the segments 0-n, soft reduction.
Accordingly the present invention provides a method for continuous casting for production of strands, the cross-section of which is reduced during solidification in the manner that the casting is, in particular, in an oscillating chill mould and the strand cross-section is linearly reduced over a minimum length of the strand guiding means directly below the chill mould, i.e. direct strand reduction, and a non-linear strand cross-sectional reduction, for example in accordance with the square root function, i.e. soft reduction, is carried out subsequently over the remaining strand guidance at most up to directly before the liquid phase point.
The various features of novelty which characterize the invention are pointed out with particularity in the claims annexed to and forming a part of the disclosure. For a better understanding of the invention, its operating advantages, specific objects attained by its use, reference should be had to the drawing and descriptive matter in which there are illustrated and described preferred embodiments of the invention.
BRIEF DESCmPTION OF THE DRAWING
In the drawing:
FIG. 1 is a diagram showing in illustration la a prior art method with a total reduction of the cast strand of 20 mm only in segment 0, and in illustration lb the method according to the invention with a reduction of 10 mm in segment 0 and a soft reduction in segments 1-13;

FIG. 2 is a diagram showing the strand thickness reduction in dependence on the soft reduction in the individual segments 1-n at casting speeds of 6 and 10 m/min;
FIG. 3 is a diagram showing the reduction rate in dependence on the soft reduction in the individual segments 1-n at casting speeds of 6 and 10 m/min;
FIG. 4 is a diagram showing in illustration 4a a reduction of 10 mm in segment 0 and a soft reduction in segments 1-8 at a casting speed of 6 m/min; and in illustration 4b the method of the invention with a reduction of 10 mm in segment 0 and a soft reduction in segments 1-13;
FIG. 5 A shows the internal strand deformation at a reduction of the strand only in segment 0 in accordance with the prior art;
FIG. 5B shows the internal strand deformation at a reduction of the strand in segment 0 and in segments 1-13 according to the invention;
FIG. 6 is a schematic illustration of the continuous casting plant according to the present invention with a vertical bending unit with segment 0 and segments 1-13; and
FIG. 7 is a schematic illustration of the structure of the segments of the strand guiding unit for carrying out the invention.
DESCRIPTION OF THE PREFERRED EMBODIMENTS
FIG. 1 of the drawing schematically shows in partial illustrations la and lb the situation of a strand having a thickness in the mold of 100 mm and a solidification thickness of 80 mm, with a casting speed of 10 m/min. and a total strand thickness reduction of 20 mm only in segment 0, i.e., casting and rolling in illustration la of FIG. 1, or 10 mm in segment 0, casting and rolling, and 10 mm in segments 1-13, i.e., soft reduction in illustration lb of FIG. 1. Moreover, the diagram shows the strand in the machine with its steel phases, such as:

the overheating phase (1), the pure molten steel phase or also called penetration zone with its lowest liquidus point 1.1;
the two-phase area melt/crystal (2) with its lowest solidus point, the sump tip 2.1 after 30 m of strand guidance composed of a mold having a length of about 1.2 m, a segment 0 having a length of 3 m and the segments 1-13 having a total length of 26 m; and
solid phase or strand shell (3).
The pure molten steel phase or also penetration zone is located in the area of segment 0 in which is carried out a strand thickness reduction or the casting and rolling of 2.times. 10 mm or 20 mm and no further reduction in the following segments 1-13, in accordance with the prior art as shown on side l a of FIG. 1, or, in accordance with the present invention, shown on side lb, a reduction of 2.times.5 mm or 10 mm, i.e., casting and rolling, and an additional 10 mm in the following segments 1-13, i.e., soft reduction. The reduction of the strand thickness in segment 0, which is constructed, for example, as a tong-segment with two clamping devices, for example, hydraulic cylinders 14, at the segment exit, it is carried out linearly over a length of 3 m; the reduction in the area of the segments 1-13 can take place partially in each segment, or also linearly over all segments as well as non-linearly, i.e., following the example of a square root. On side lb of FIG. 1, the strand thickness reduction of 10 mm is linearly distributed in segments 1-13, i.e., soft reduction.
When comparing the present invention, i.e., side lb of FIG. 1, with the prior art, i.e., side la of FIG. 1, the reduction speed in mm/s of the strand shell which represents a measure for the strand shell deformation can be significantly reduced, as illustrated by the following values:
prior art, side la:
segment 0, reduction 20 mm, casting and rolling,
reduction speed 1.11 mm/s;

segments 1-13, reauction 0 mm, no solt reduction,
reduction speed 0.
Invention, side lb:
segment 0, reduction 10 mm, casting and rolling,
reduction speed 0.56 mm/s;
segments 1-13, reduction 10 mm, soft reduction,
reduction speed 0.064 mm/s.
The distribution of the strand thickness reductions can now be selected between the segment 0 and the following segments 1-13 in an optimum manner with respect to the possible strand deformation while avoiding internal cracks and surface cracks and with respect to the minimum work to be introduced for strand thickness reduction which increases with the thickness of the strand shell.
This distribution effect on the reduction speed and, thus, on the load acting on the strand shell, is indicated in tables 1 and 1.1 and is shown in FIGS. 2 and 3. FIG. 2 shows the reduction of the strand thickness in mm/m strand guidance for a total thickness reduction of 20 mm in dependence on different reductions in the segment 0 and the corresponding complimentary thickness reduction in the segments 1-13 for the continuous casting speeds of 6 and 10 m/min. In the case of a linear distribution of the total reduction of 20 mm over all segments 0 to 8 or 13, the following values are adjusted with respect to thickness reduction RL-6 and RL-10 and reduction speed RS-6 and RS-10 of:
1.168 mm/m strand guiding means RL-6 and 0.117 mm/s RS-6 at 6 m/min casting speed, or
0.685 mm/m strand guiding means RL-10 and 0.114 mm/s RS-10 at 10/min casting speed.

These values have the lowest deformation density, however, they require a maximum amount of work and result in a soft reduction process over the entire strand guiding means. The claimed invention takes into consideration the gap between the extreme of the total reduction of 20 mm in segment 0 and the uniform reduction distributed over the strand guiding means in segment 0 to shortly behind the final solidification of the strand.
As is the case in FIG. 1, FIG. 4 schematically illustrates the situation of a strand having a thickness in the mold of 100 mm and a solidification thickness of 80 mm for the casting speeds VG of 6 m/min, side 4a of FIG. 4, and 10 m/min, side 4b. In accordance with the present invention, in the case of VG 6 m/min, the strand thickness reduction of, for example, 10 mm is carried out in segment 0 and the remaining reduction of 10 mm is carried out in segments 1-8, corresponding to the shorter solidification distance. Thus, the lowest liquidus point 1.2 is already at about 1.8 m and the sump tip 2.2 is at about 18.12 m. Since the reduction of the strand thickness takes place at most over 18.12 m, and simultaneously is to include the final solidification, the segments 1-8 are utilized for the reduction of the thickness. As is the case in FIG. 1, side lb, side 4b of FIG. 4 shows the situation of the strand in the case of a casting speed of VG 10 m/min.
The comparison of the casting situations according to the present invention shown on sides 4a and 4b of FIG. 4, results in the following values of the reduction speeds, and thus, loads acting on the strand shell:
6 m/min, side 4a of FIG. 4, example of the invenfion, segment 0, reduction 10 mm, reduction speed 0.33 mm/s, casting and rolling;
segments 1-8, reduction 10 mm, reduction speed 0.071 mm/s, soft reduction;
10 m/min, side 4b of FIG. 4, example of the invention, segment 0, reduction 10 mm, reduction speed 0.56 mm/s, casting and rolling;
segments 1-13, reduction 10 mm, reduction speed 0.064 mm/s, soft reduction.

This comparison demonstrates that the distribution of the thickness reduction is also a question of the casting speed and that, in accordance with the location of the sump tip, i.e., the casting speed, the thickness reduction and its distribution in the segments 1-n or 0-n, must be adapted to an optimum casting situation with respect to the casting safety and the strand quality.
The drawing shows the effect of a distribution of the strand thickness reduction in segment 0 and in the segments 1-13 in accordance with the invention, illustrated in FIG. 5b, in the example of a vertical bending machine, as compared to the prior art shown in FIG. 5a, on the internal strand deformation caused by the bending deformation and the strand thickness reduction, in dependence on the strand guidance for the maximum casting speed of, for example 10 m/min.
FIG. 5 a representing the prior art shows the internal strand deformation in dependence on the strand guiding means 4, for example, for a maximum casting speed Vg-10 of 10 m/min as compared to the limit deformation D-Gr. At the exit of the mold, the strand is subjected to a deformation caused by casting and rolling D-Gw in segment 0, as well as to a deformation caused by the bending process D-B. Both deformations are superimposed to the total deformation D-Ge which is greater than the limit deformation D-Gr and, thus, becomes critical. When the limit deformation is exceeded, this leads to internal cracks at the phase boundary solid/liquid, and, thus, to a diminished quality of the strand and to a lowering of the casting safety. The strand is subjected to another increase of the internal deformation D by the deformation D-R occurring during return bending in segment 4 from the inner circular arc into the horizontal which, however, cannot be critical because the number of return bending points is selected when "designing" the plant in such a way that the return bending process cannot trigger at maximum casting speed a critical internal deformation in the strand shell of the steel quality which is most sensitive to cracks.
FIG. 5b shows the technical features of the method according to the present invention in cormection with a vertical bending plant, as schematically illustrated in FIG. 6. The internal deformation D of the strand shell 3 does not become critical at

any moment of solidification, i.e., from the mold exit to the end of the stand 13. In accordance with the invention, this is ensured by the distribution of the total strand thickness reduction of 20 mm to, for example, 10 mm in segment 0 D-Gw and 10 mm in the stands 1-13 D-sr. In addition, the bending process and the attendant deformation D-V has been transferred from segment 0 to segment 1 in order not to additionally increase the deformation density D-Gw in segment 0, which is caused by casting and rolling of, for example, 10 mm and, while lowered, is still relatively high. The deformation D-SR produced in segments 1-13 and caused by soft reduction of a total of, for example, 10 mm, is relatively small and does not result in a practical increase of the deformation D-R when return bending the strand in segment 4, i.e., D-Ge is approximately greater than/equal to D-R.
FIG. 6 shows a vertical bending unit in which the present invention can be used for casting slabs having a thickness of 100 mm at the mold exit with a solidification thickness of 80 mm and a maximum VG 10 m/min. This plant has the technical method features described in connection with FIGS. 1-5. In addition to a distributor V and a submerged pouring pipe Ta, the continuous casting plant includes:
a vertical mold K having a length of about 1.2 m, which is preferably constructed concavely in horizontal direction;
a segment 0 having a length of 3 m, which is equipped for casting and rolling or also for strand thickness reduction preferably as a tong-type segment and with two hydraulic cylinders 14 at its exit;
segment 1 with 5 bending points 23;
segments 2 and 3 with the inner circular arc having a radius of about 4 m;
segment 4 for return bending the strand from the inner circular arc through five return bending points 24 into the horizontal; and
segments 5-13 in the horizontal portion of the machine.

This machine configuration with a maximum casting speed of 10 m/min and a maximum capacity of about 3 million tons per year constitutes an extremely advantageous solution for use of the invention in which a minimum deformation density of the strand occurs during its solidification.
In order to be able to advantageously realize the type of strand thickness reduction according to the present invention in the above-described segments 1-13, the segments should be constructed in principle as illustrated in FIG. 7. A segment should preferable be constructed of an odd number of 3, 5, 7 or 9 pairs of rollers 15, wherein each pair has a lower roller 16 and an upper roller 17. Each segment, in turn, is altematingly composed of a driven pair of rollers 18, controlled with respect to position and force by a hydraulic system 19, and two non-driven pairs of rollers 21 which are connected to a hydraulic system 20 in the area of the upper rollers 17 and are provided with a machine element 22 which makes it possible to allow the pair of rollers of the upper path in castmg direction to swing about an angle of, for example +/-5 degrees in order to be able to guide the strand and ensure its shape in any casting situation with a given strand thickness reduction.
This configuration of the segments 1-13 results in an optimum strand guidance in any type of distribution of the strand thickness reduction, any casting situation, any type of steel quality, with respect to its sensitivity to intemal cracks, i.e., the level of the critical deformation limit and with respect to the use of a minimum of hydraulic systems for each pair of rollers. Thus, 0.66 hydraulic systems are used for each pair of rollers. Also, the use of driven pairs of rollers of 0.33 units per pair of rollers represents a mechanical minimum with a maximum effect with respect to process technology and quality of the strand to be cast and its outer surface quality and its intemal quality, i.e., for example, a minimum structural requirement and a minimum cumulation of tensile stresses in the strand shell between the driven pairs of rollers.
The present invention has been described in connection with a thin slab plant; however, the present invention can also be utilized with respect to the method and the apparatus in other continuous casting plants, such as:

slab plants;
bloom plants; and
billets plants for square and round billets.
While specific embodiments of the invention have been shown and described in detail to illustrate the inventive principles, it will be understood that the invention may be embodied otherwise without departing from such principles.









WE CLAIM :
1. Method for continuous casting for production of strands, the cross-section of
which is reduced during solidification in the manner that the casting is, in particular,
in an oscillating chill mould and the strand cross-section is linearly reduced over a
minimum length of the strand guiding means directly below the chill mould, i.e. direct
strand reduction, and a non-linear strand cross-sectional reduction, for example in
accordance with the square root function, i.e. soft reduction, is carried out
subsequently over the remaining strand guidance at most up to directly before the
liquid phase point.
2. Method as claimed in claim 1, wherein in the case of rectangular strand shapes the cross-section is preferably reduced by a reduction in the thickness direction.
3. Method as claimed in claim 1 or 2, wherein the thickness of the strand is reduced to a maximum of 60% of the strand thickness at the chill mould exit.
4. Method as claimed in any one of claims 1 to 3, wherein preferably thin slabs with a thickness of 120 millimetres are reduced in thickness to 50 millimetres after hardening.
5. Method as claimed in any one of claims 1 to 4, wherein breaking down the overall thickness reduction into direct strand reduction directly below the chill mould and into soft reduction in the remaining strand guidance at a speed of less than 1.25 millimetres per second for maximum casting speed.
6. Method as claimed in any one of claims 1 to 5, wherein casting is at a maximum speed of up to 12 metres per minute.
7. Method as claimed in any one of claims 1 to 6, wherein during the soft reduction the thickness is reduced linearly over the hardening length.

8. Method as claimed in any one of claims 1 to 6, wherein during soft reduction the
strand thickness is reduced in linearly reducing manner over the solidification time.
9. Method as claimed in any one of claims 1 to 7, wherein the entire thickness reduction from the outlet of the chill mould to at most directly before the liquid phase point elapses linearly and constantly.
10. Method as claimed in any one of claims 1 to 9, wherein the bending of a strand from the vertical into the inner circular arc of a vertical bending continuous casting plant is undertaken in the region of the soft reduction.
11. Method as claimed in any one of claims 1 to 10, wherein the direct strand
reduction is carried out exclusively in the vertical strand guidance without the lowest
liquidus point emerging from the strand guidance at maximum casting speed.
12. Continuous casting plant for carrying out the method as claimed in any one of
claims 1 to 11, comprising
an oscillating chill mould (K),
a segment 0, which linearly reduces the strand in its cross-section by a maximum of 40% over a length of at least one metre,
a remaining strand guiding means, which reduces the strand by soft reduction in its cross-section to at most directly ahead of the liquid phase point (2.1), and
in which the entire reduction of the strand cross-section in the segment 0 and in the remaining strand guiding means is designed to be to 60%.
13. Continuous casting plant as claimed in claim 12, wherein for the casting of
rectangular shapes the segment (0) and the following segments (1-n) are designed for
the cross-sectional reduction by reduction in the strand thickness.

14. Continuous casting plant as claimed in claim 12 or 13, wherein the segment (0) for reduction in the strand thickness is equipped at its exit with two position-regulated and force-regulated clamping cylinders.
15. Continuous casting plant as claimed in any one of claims 12 to 14, wherein the segment (0) is designed for reduction of the strand thickness by at most 100 millimetres.
16. Continuous casting plant as claimed in any one of claims 12 to 15, wherein the segments (1 to n) are position-regulated and force-regulated with respect to their strand thickness setting.
17. Continuous casting plant as claimed in any one of claims 12 to 16, wherein the number of roller pairs (15) per segment is uneven and amounts to at least three.
18. Continuous casting plant as claimed in any one of claims 12 to 17, wherein each third roller pair (18) is driven.
19. Continuous casting plant as claimed in any one of claims 12 to 18, wherein the upper rollers of the non-driven roller pairs (21) are provided with a position-regulated and force-regulated clamping cylinder.
20. Continuous casting plant as claimed in any one of claims 12 to 19, wherein the upper rollers of the non-driven roller pairs (21) and their cylinders (20) are provided with a device (22) which permits a pendulation of the rollers by preferably +/- 5° in casting direction.
21. Continuous casting plant as claimed in any one of claims 12 to 20, wherein the segment (0) is arranged vertically and has a maximum length of 5 metres.
22. Continuous casting plant as claimed in claim 21, wherein the first downstream segment (1) has at least one bending point (23) for bending of the strand from the vertical into a circular arc.

23. Continuous casting plant as claimed in any one of claims 12 to 22, wherein at
least one return bending point (24) for straightening the strand from the circular arc
into the horizontal is provided in at least one of the segments (2 to n).
24. Continuous casting plant as claimed in claim 23, wherein the horizontal part of the strand guidance has a length of at least 4 metres.
25. Continuous casting plant as claimed in any one of claims 12 to 24, wherein the chill mould walls are constructed to be concave.
26. Continuous casting plant as claimed in any one of claims 12 to 25, wherein an
immersion outlet (Ta) and casting powder are used for the casting.
27. Continuous casting plant as claimed in any one of claims 13 to 25, wherein the
wide sides of the chill mould are constructed to be concave in horizontal direction and
decrease in their concavity in direction towards the chill mould outlet.
28. Continuous casting plant as claimed in any one of claims 13 to 27, wherein the
narrow sides of the chill mould are constructed to be concave in horizontal direction.
29. Method for continuous casting for production of strands, substantially as
hereinabove described and illustrated with reference to figures lb, 2, 3, 4, 5b, 6 & 7 of
the accompanying drawings.

Documents:

106-mas-1998 abstract duplicate.pdf

106-mas-1998 abstract.jpg

106-mas-1998 abstract.pdf

106-mas-1998 claims duplicate.pdf

106-mas-1998 claims.pdf

106-mas-1998 correspondence others.pdf

106-mas-1998 correspondence po.pdf

106-mas-1998 description (complete) duplicate.pdf

106-mas-1998 description (complete).pdf

106-mas-1998 drawings duplicate.pdf

106-mas-1998 drawings.pdf

106-mas-1998 form-1.pdf

106-mas-1998 form-19.pdf

106-mas-1998 form-26.pdf

106-mas-1998 form-4.pdf

106-mas-1998 others.pdf

106-mas-1998 petition.pdf


Patent Number 217219
Indian Patent Application Number 106/MAS/1998
PG Journal Number 21/2008
Publication Date 23-May-2008
Grant Date 26-Mar-2008
Date of Filing 16-Jan-1998
Name of Patentee SMS SCHLOEMANN-SIEMAG AKTIENGESELLSCHAFT
Applicant Address EDUARD-SCHLOEMANN-STRASSE 4, 40237 DUSSELDORF,
Inventors:
# Inventor's Name Inventor's Address
1 DR. FRITZ-PETER PLESCHIUTSCHNIGG REISERWEG 69, 47269 DUISBURG,
PCT International Classification Number B22D 11/12
PCT International Application Number N/A
PCT International Filing date
PCT Conventions:
# PCT Application Number Date of Convention Priority Country
1 NA