Abstract The present invention relates to a process for the preparation of a precalcined vanadiumlphosphorus mixed oxide catalyst precursor, comprising the steps of reacting vanadium pentoxide in an organic medium in the presence of a phosphorus source to obtain a catalyst precursor comprising vanadyl acid orthophosphate hemihydrate of the formula (VO)HPO4.0,5H20 as main component, and a heat treatment of said catalyst precursor to obtain a precalcined catalyst precursor, characterized in that the organic medium comprises (a) isobutyl alcohol or a mixture of isobutyl alcohol and benzyl alcohol and (b) a polyol the weight ratio (a) to (b) of 99:1 to 5:95, the vanadium pentoxide together with the phosphorus source is suspended in the organic medium and the mixture is kept under agitation at a temperature of 90 to 200°C over a period of 1 h to 24 h, and the heat treatment is conducted in air or oxygen-depleted air at about 300°C for about 3 hours, to obtain a precalcined catalyst precursor having a residual carbon content of 0.8 to 1.5 wt.%.
Full Text The invention relates to a process for the production of a vanadium/phosphorus mixed oxide catalyst precursor, its transformation into the active catalyst and a process for the production of maleic anhydride using this catalyst.
Maleic anhydride is a well known and versatile intermediate for manufacturing unsaturated polyester resins, pharmaceuticals or agrochemicals. It is usually produced by catalytic partial oxidation of aromatic (e. g., benzene) or non-aromatic (e. g., n-butane) hydrocarbons.
The main component of the active catalyst in the oxidation of non-aromatic hydrocarbons like «-butane to maleic anhydride is vanadyl pyrophosphate, (yO)■lP20^, which as a rule is obtained by thermal treatment of vanadyl acid orthophosphate hemi hydrate of the formula (VO)HPO4-0.5HjO, acting as catalyst precursor. Both vanadyl pyrophosphate and vanadyl acid orthophosphate hemihydrate may, if desired, be accompanied by a promoter element selected from the groups lA, IB, IIA, IIB, IIIA, IIIIB, IVA, IVB, VA, VB, VIA, VIB and VIIIA of the periodic table of elements, or mixtures of such elements. Methods for preparing the precursor compound conventionally involve reducing a heptavalent vanadium compound under conditions which will provide vanadium in a tetravalent state (average oxidation number +IV).
Prior art knows a great many different procedures, which however in general involve the use
of vanadium pentoxide (V2O5) as a source of pentavaleit vanadium and orthophosphoric acid
(H3PO4) as the phosphorus source (see e.g. US-A-5 137 860 or EP-A-0 804 963).
As a reducing agent in principle any inorganic or organic compound containing elements
which are able to act as a redox couple possessing an oxidation potential suitable for this kind
of reaction may be suitably applied.
The most common reducing agent is hydrogen chloride in aqueous solution.
Also favorably applied are organic media like primary or secondary aliphatic alcohols or
aromatic alcohols such as benzyl alcohol as these compounds seem to at least in part dissolve
the reactants and thereby facilitate the redox reaction.

The most preferred organic reducing agent is isobutyl alcohol as isobutyl alcohol combines optimal characteristics such as (i) a boiling point of 108 °C at atmospheric pressure, (ii) dissolution of the vanadium alcoholates formed from V2O5, thus favoring a complete redox reaction in the liquid phase and (iii) achieving a redox potential for the couples isobutyl alcohol/isobutyraldehyde and isobutyl alcohol/is butyric acid suitable to let the alcohol act as reducing agent. The tetravalent vanadium reacts with phosphoric acid (H3PO4) and leads to precipitation of the precursor vanadyl acid orthophosphate hemihydrate of the formula (VO)HPO4-0.5H2O. The precipitate is usually washed with isobutyl alcohol and subsequently dried.
A major disadvantage of the conventional method as described above is that even after drying the precursor contains some percent of organic compounds from the organic reaction medium, compounds which are supposedly either (i) strongly adsorbed at the solid surface, and therefore not easily removable by the washing and drying treatment, or (ii) physically trapped in between the crystals of the precursor, or (iii) physically or chemically trapped ("intercalated") in the crystalline structure of the precursor.
It has been found that this percentage of organic compound which remains trapped in the precursor is a fundamental parameter which can adversely affect the performance characteristics of the active catalyst obtained after the thermal treatment.
The object of the present invention therefore was to pro\ide a method for controlling the carbon content in a vanadium/phosphorus mixed oxide catalyst precursor and accordingly to provide a superior catalyst precursor which, when activated, leads to superior results in the conversion of a non-aromatic hydrocarbon to maleic anhydride.
It was found that the objectives could be achieved with a new process for the preparation of a vanadium/phosphorus mixed oxide catalyst precursor ao:ording0 to claim I.
The invention comprises reducing a source of vanadium in the presence of a phosphorus source in an organic medium which comprises
(a) isobutyl alcohol or a mixture of isobutyl alcohol and benzyl alcohol and
(b) a polyol
in the weight ratio of 99:1 to 5:95.

In a mixture of isobutyl alcohol and benzyl alcohol the benzyll alcohol content is as a rule between 5 and 50 wt.%.
As a source of vanadium a tetravalent or pentavalent vanadium compound may be applied. Representative examples, although not limiting, are vanadium tetrachloride (VCI4), vanadium •oxytribromide (VOBr,), vanadium pentoxide (VjOj), vanadyl phosphate (VOPO^-n H2O) and vanadium tetraoxide (V2O4). Vanadium pentoxide is the f )referred vanadium source. As mentioned above, the vanadium source may, if desired, be accompanied by promoter elements selected from the groups lA, IB, IIA, IIB, IIIA, HUB, IVA, IVB, VA, VB, VIA, VIB and VIIIA of the periodic table of elements, or mixtures thereof.
Preferred promoter elements are selected from the group consisting of zirconium, bismuth, lithium, molybdenum, boron, zinc, titanium, iron and nickel.
Orthophosphoric acid (H3PO4) is the preferred phosphorus source.
Isobutyl alcohol is the preferred component (a).
Polyols which can be used as the component (b) are expediently C2 aliphatic polyols, preferably C2-alkanediols such as 1,2-ethanediol, l,2-pP3panediol, 1,3-propanediol, 1,2-butanediol, 1,3-butanediol, 1,4-butanediol, 2,3-butanediol, 1,2-pentanediol, 1,3-pentane-diol, 1,4-pentanediol, 1,5-pentanediol, 2,3-pentanediol,2,4-pentanediol, 1,2-hexanediol, 1,3-hexanediol, 1,4-hexanediol, 1,5-hexanediol, 1,6-hexanediol, 2,3-hexanediol, 2,4-hexanediol, 2,5-hexanediol and 3,4-hexanediol.
Most preferred polyols are the C2-4-alkanediols 1,2-ethanediol, 1,3-propanediol and 1,4-butanediol.
The preferred mixture of alcohols contains 5 to 30 mol% of polyol with repect to isobutyl alcohol.
As a rule the vanadium source together with the phosphorus source is suspended in the organic medium and the mixture is kept under agitation at a temperature of expediently 90 °C: to 200 °C, preferably 100 °C to 150 °C over a period of 1 h to 24 h.

The ratio of vanadium source to phosphorus source is conveniently such that the P/V atomic ratio is inthe range of 1:1 to 1.3:1, preferably 1.1:1 to 1.2:1.
As a rule after the reduction the precursor vanadyl acid orthophosphate hemihydrate of the formula (VO)HPO40.5H2O is formed which is filtered, washed and subsequently dried at a temperature of expediently 120 °C to 200 °C.
Due to the reduction treatment according to the invention the carbon content of the precursor can be controlled in the range of 0.7 wt.% to 15.0 wt.%, preferably in the range of 0.7 wt.% to 4 wt.%.
It has been found that best results are obtained with catalyst precursors which, after an additional thermal treatment at about 300 "C for about 3 hours in air have a residual carbon content of 0.7 wt.% to 3 wt.%, most preferably 0.8 wt.% to 1.5 wt.%.
Once prepared the precursor can in view of its further activation treatment be formed into
defined structures with defined properties. Such procedures may include wet grinding to a
specific particle size, the addition of additives to improve attrition resistance, and the
formation of a convenient shape.
A spherical shape for instance is most suitable for the application of the catalyst in a fluidized
bed.
The further transformation of the so formed precursor into the active catalyst can be performed following a great number of activation processes known in the art, but in general include a heat treatment applying temperatures of up to 600 °C. More in detail, these processes may involve:
(a) an initial heating of the precursor to a temperature not to exceed 250 °C
(b) a further heat treatment from about 200 °C to at least 380 °C to 600 °C at the maximum
(c) maintaining the temperature of stage (b) over a certain time and
(d) cooling the activated catalyst, thereby maintaining an individually controlled atmosphere in all steps.

In a prefeired embodiment, the activation of the precursor is accomplished using the procedure described in EP-A-0 804 963.
In a more preferred embodiment, the activation comprises the steps of
(a) heating the catalyst precursor iron room temperature to a recalculation temperature of about 300 °C in air or oxygen-depleted air
(b) keeping at said precalcination temperature,
(c) further heating the precalcined catalyst precursor in nitrogen up to a calcinations temperature of about 550 °C and
(d) keeping at said calcinations temperature.
After the transformation into the active catalyst the catalyst is ready to be applied for the conversion of non-aromatic hydrocarbons to maleic anhydride.
Such processes are well known in the art, e. g. from US-A-4 594 433, US-A-5 137 860 or US-A-4 668 652.
In general the non-aromatic hydrocarbon is converted with oxygen or an oxygen containing gas at a temperature from about 320 °C to 500 °C to maleic anhydride. The non-aromatic hydrocarbon is expediently selected from aliphatic C4.10 hydrocarbons, preferably n-butane. The conversion can take place in a fixed bed or a fluidized bed reactor but preferably in a fluidized bed reactor. The following examples are given by way of illustration only and are not construed as to in any way limit the invention.
Examples:
In the following examples, the carbon content was determined by combustion in pure oxygen at high temperature using the apparatus and procedure described below and detection of the carbon dioxide formed by infrared analysis.
Apparatus: ELTRA 900CS
Measuring range: 0.001-100 wt.% C

Sensitivity: 0.0001 wt.% C
Time per sample: 90 s
Sample size: 0.1-0.5 g
Oven temperature: 400-1500 °C
Oxygen purity: 99.5 % min.
Oxygen flow rate: 4 1/min
Procedure:
The furnace was heated up to 1330 °C and oxygen flow was opened 10 minutes before
starting the analysis. High carbon content detector was selected and calibrated with standard
samples having known carbon content. The sample size used was 150 ± 10 mg.
Comparative Example 1 (following example 1 (comparison) of EP-A 0 804 963)
Into a three-necked 1-1 flask fitted with thermometer, mechanical stirrer and packed glass distillation column with reflux condenser and water separator (cf example 5), were introduced 8.20 g of V2O5 and 10.1 g of HjP04 (100%). suspended in 75 ml of isobutyl alcohol (99%+). The mixture was then kept under agitation and heated u]) to reflux and left at these conditions for 6 h. The colour of the mixture changed from red-brown to dark green and then finally to bright blue.
The mixture was cooled to room temperature, then filtered and washed with a large excess of isobutyl alcohol. The solid was then dried in air at 125 °C for 5 h. The carbon content of the dried precipitate was 0.6 wt.%.
The solid was then treated in air by heating from room temperature to 300 °C (heating rate 1 K/min), then left at 300 °C for 6 h, heated in Nj up to :550 °C (heating rate 1 K/min) and finally left at 550 °C for 6 h. After the precalcination step (in air at 300 °C), the residual carbon content was 0.5 wt.%.

The preparation of the precursor was done as described in comparative example 1, but the thermal treatment was done according to the procedure of example 4 of EP-A-0 804 963:
(a) heating in air from 25 °C to 180 °C at a.heating rate of 4 K/min
(b) further heating from 180 °C to 425 °C in a mixture of air (70% vol) and steam (30% vol) at a heating rate of 1.5 K/min
(c) isothermal step at 425 °C in the same atmosphere as in step (b), for 2 h
(d) isothermal step at 425 °C in an atmosphere of nitrogeri (70% vol) and steam (30% vol) for 3 h
(e) cooling in a mixture of nitrogen and steam at a rate of-2 K/min.
Comparative Example 3
The preparation of the precursor was done as described in comparative example 1, but the
isobutyi alcohol was replaced by 35.5g of 1,3-propanediol.
The dried catalyst precursor had a carbon content of 11 .(> wt.%.
The activation was performed according to the procedure of comparative example 1.
Example 1
4.11 g of V2O5 and 5.11 g of H3PO4 (100%) were suspended in 37.5 ml of a mixture of 1,2-ethanediol/isobutyl alcohol (20/80 v/v). The mixture was kept under agitation and heated up to reflux, and left at these conditions for 6 h. The color of the mixture changed from red-brown to dark green and then finally to bright blue.
The mixture was cooled to room temperature, then filtered and washed with a large excess of isobutyl alcohol. The solid was then dried in air at 125 °C for 5 h.
The dried catalyst precursor had a carbon content of 2.3 wt.%, while after the precalcination treatment in air at 300 °C the amount of residual carbon was 1.2 wt.%. The activation was performed according to comparative example 1.

The same procedure as in example 1 was carried out, with the exception of 1,2-ethanediol
being replaced with benzyl alcohol.
The dried catalyst precursor hat a carbon content of 1.6 wt.% while after precalcination the
residual amount of carbon was 0.4 wt.%.
The activation was performed according to the procedure]-e of comparative example 1.
Example 2
8.20 g of V2O5 and 10.07 g of H3PO4 (100%) were susp(;nded in 75 ml of a mixture of 1,3-propanediol/isobutyl alcohol (20/80 v/v). The mixture was kept under agitation and heated up to reflux, and left at these conditions for 6 h. The color of the mixture changed from red-brown to dark green and then finally to bright blue.
The mixture was cooled to room temperature, then filleted and washed with a large excess of isobutyl alcohol. The solid was then dried in air at 125 "C for 5 h.
The dried catalyst precursor had a carbon content of 2.8 wt,% while after precalcination the residual amount of carbon was 1.8 wt.%. The activation was performed according to the procediu-e of comparative example 1.
Example 3
The procedure of example 1 was repeated, but as reducing agent 37.5 ml of a mixture of
1,4-butanediol/isobutyl alcohol (20/80 v/v) was chosen.
The dried catalyst precursor had a carbon content of 1.6 wt.% while after precalcination the
residual amount of carbon was 1.1 wt.%.
The activation was performed according to the procedure of comparative example 1.

The procedure of example 1 was repeated, but as reducing agent 37.5 ml of a mixture of
1,3-butanediol/isobutyl alcohol (20/80 v/v) was chosen.
The dried catalyst precursor had a carbon content of 1.6 wt.% while after precalcination the
residual amount was 1.4 wt.%.
The activation was performed according to comparative example 1.
Example 5
The procedure of example 3 was repeated (using the apparatus described in comparative
example 1), but the water generated during the reaction was partially removed by isentropic
destination.
The dried catalyst precursor had a carbon content of 2.3 wt.% while after precalcination the
residual amount was 1.5 wt.%.
The activation was performed according to comparative example 2.
Catalytic tests
The catalytic tests were performed at atmospheric pressure in a fixed-bed stainless steel laboratory reactor (length 25.4 cm, diameter 1.27 cm) loaded with 3 g of catalyst. The products were collected and absorbed in anhydrous acetone and analyzed by gas chromatography. The performance of the catalyst was determined on the basis of the percent conversion of n-butane fed to the reactor (together with oxygen and helium), the yield of maleic anhydride recovered in the absorber (MA yield) in % and the selectivity of the conversion towards maleic anhydride (MA selectivity) in %. The following conditions were maintained during the tests: W/F (weight of catalystotal volumetric’ flow rate): 1.3 g-s/ml
feed composition: 1.7 % n-butane, 17.2% O2, rest He
measurement: after 200-300 h time-on-stream (stable
catalytic performance).




From the examples reported above it is clear that the best performance (i. e., the highest yield is obtained for those catalysts (Ex. 3 and 4) which fulfill both the requirements of having a carbon content in the precursor of 1 to 2 wt.%, and a residual carbon content after pre-calcinations at 300 °C in air of 0.8 to 1.5 wt.%.


WE CLAIM:
1. A process for the preparation of a precalcined vanadiumlphosphorus mixed oxide catalyst precursor, comprising the steps of reacting vanadium pent oxide in an organic medium in the presence of a phosphorus source to obtain a catalyst precursor comprising vanadyl acid orthophosphate hemihydrates of the formula (VO)HPO4.0,5H2O as main component, and a heat treatment of said catalyst precursor to obtain a precalcined catalyst precursor, characterized in that the organic medium comprises (a) isobutyl alcohol or a mixture of isobutyl alcohol and benzyl alcohol and (b) a polyol the weight ratio (a) to (b) of 99:1 to 5:95, the vanadium pent oxide together with the phosphorus source is suspended in the organic medium and the mixture is kept under agitation at a temperature of 90 to 200°C over a period of 1 h to 24 h, and the heat treatment is conducted in air or oxygen-depleted air at about 300°C for about 3 hours, to obtain a precalcined catalyst precursor having a residual carbon content of 0.8 to 1.5 wt.%.
2. The process as claimed in claim 1, wherein the phosphorus source is phosphoric acid.
3. The process as claimed in claims 1 or 2, wherein the component (a) of the organic medium is isobutyl alcohol.
4. The process as claimed in any one of claims 1 to 3, wherein the polyol is a C2-6 aliphatic polyol.

5. The process as claimed in claim 4, wherein the C2-6 aliphatic polyol is a C2-6-
alkanediol, preferably a C2-4-alkanediol.
6. A precalcines vanadium/phosphorus mixed oxide catalyst precursor,
obtainable by a process as claimed in any one of claims 1 to 5.
7. A process for the transformation of the catalyst precursor as claimed in
claim 6, into an active catalyst for the production of maleic anhydride, which
process comprises heating the proclaimed catalyst precursor in nitrogen up to a
calcinations temperature of about 500°C and keeping it at said calcinations
temperature.
8. An active catalyst for the production of maleic anhydride, obtainable by the
process of claim 7.
9. "The process for the production of maleic anhydride, which comprises
converting a feed gas comprising a non-aromatic hydrocarbon having at least 4
carbon atoms and oxygen in the presence of the active catalyst as claimed in claim
8. at a temperature from 320°C to SOO"^C.
10. The process as claimed in claim 9, wherein the non-aromatic hydrocarbon is
w-butane.

Documents:

in-pct-2001-1688-che abstract-duplicate.pdf

in-pct-2001-1688-che abstract.pdf

in-pct-2001-1688-che claims-duplicate.pdf

in-pct-2001-1688-che claims.pdf

in-pct-2001-1688-che correspondence-others.pdf

in-pct-2001-1688-che correspondence-po.pdf

in-pct-2001-1688-che description(complete)-duplicate.pdf

in-pct-2001-1688-che description(complete).pdf

in-pct-2001-1688-che form-1.pdf

in-pct-2001-1688-che form-19.pdf

in-pct-2001-1688-che form-26.pdf

in-pct-2001-1688-che form-3.pdf

in-pct-2001-1688-che form-5.pdf

in-pct-2001-1688-che others.pdf

in-pct-2001-1688-che pct.pdf

in-pct-2001-1688-che petition.pdf


Patent Number 215968
Indian Patent Application Number IN/PCT/2001/1688/CHE
PG Journal Number 13/2008
Publication Date 31-Mar-2008
Grant Date 05-Mar-2008
Date of Filing 29-Nov-2001
Name of Patentee LONZA S.P.A
Applicant Address Via Vittor Pisani, 31, I-20124 Milano,
Inventors:
# Inventor's Name Inventor's Address
1 ALBONETTI, Stefania Via Selice, 213, I-40026 Imola,
2 CAVANI, Fabrizio Via San Giovanni Bosco, 78, I-41100 Modena,
3 LIGI, Simone Via Bramante, 17, I-61030 Montefelcino,
4 MAZZONI, Gianluca Via Marzanica, 1, I-24020 Torre Boldone,
PCT International Classification Number B01J 27/198
PCT International Application Number PCT/EP2000/004939
PCT International Filing date 2000-05-30
PCT Conventions:
# PCT Application Number Date of Convention Priority Country
1 MI99 A001233 1999-06-01 Italy