Title of Invention

"A METHOD OF MAKING A BLEEDING INK COMPOSITION"

Abstract A method of making a bleeding ink composition for use in printing security documents by providing at least one compound of the kind such as herein described capable of forming a binder matrix by polymerization and/or crosslinking and mixing said compound substantially homogeneously with dyestuff of the kind such as herein described substantially inert to said compound and sensible to organic solvents and/or other chemical reagents wherein the compound forming a binder matrix makes up about 40 to 85 % of the total ink weight and the dye stuff comprises about 5 to 20 % by weight of the total ink.
Full Text The present invention relates to a method of making a bleeding ink composition.
The present invention belongs to the field of the art of printing and describes a new and useful ink, a method of manufacturing an ink and the use of a composition as an ink which can be printed particularly by dry or wet offset by screen-, flexo- and gravure-printing as well as letterpress printing methods such as used mainly on security documents. Such inks are also named "fugitive inks"
A great number of security documents are presently knov/n; examples of such documents are bank cheques, money transfer orders, identity cards, other identity documents such as passports and driver's licences, postal stamps, lottery tickets , airline transportation tickets, shares, certificates, affidavits and others.
All security documents should be protected against forgery or counterfeiting. The main threats are:
Total counterfeit where, a document is reproduced in its entirety; or
Forgery where a document is altered by deleting artd/or repla-cing information, for example the amount of money on a cheque, a' signature on a driver's licence, or information, on a passport
In each case, a well selected security printing ink can. contribute considerably to the security of the document.
Solvent bleeding pointing inks are already known and have been used for a rather long time in the field of security inks. The protection conferred to the security document is
established bya fading by a fading or even disappearance of the colour,
by a change in colour or by a bleeding off when the document is contacted with an organic solvent or any other chemical substance used as a falsifying reagent.
The application methods and the principles of the function of the bleeding or fugitive printing inks in contact with solvents and other chemical agents, are the following:
The inks can be printed specifically by dry or wet offset by screen-, flexo- and gravure-printing or by letterpress. They are composed of a vehicle or binder whose components are mineral oils and alkyd resins, one or more dyestuffs that are soluble in organic solvents and are the substances sensitive to said chemical agents, and different additives. The dye-stuffs are mostly chromium completes, cobalt complexes or copper phthalocyanine blue. The drying mechanism is a purely physical one and acts principally by penetration into an absorbing solid fibrous substrate. In fact, if drying is defined as a conversion of the liquid printing ink into a solid and stationary film on the substrate, these printing inks do not dry but remain "liquid"; however, they are sufficiently permanently entrapped within the interstices of the fibres of the substrate for their mobility to be drastically reduced. The absorption of such printing inks is partial and progressive, and several days after the printing ere necessary for the printed document to show an apparently dry condition, typically 5 to 7 days. Only after that time can the printed substrate be further processed, for example in order to apply personalised information, i.e. by laser printer or ion deposition printer. Furthermore, the absorption capacity of the substrate determines the quality and the drying time.
Thus, the working principle of bleeding printing inks known to date is based on the fact that the matrix of the ink remains soluble in organic solvents and other chemical agents.
Now, the objective of the present invention is to provide printing inks for the above mentioned printing processes that can be effectively dried to form a solid matrix but which also form a print that remains sensitive to solvents and other chemical reagents. Another objective of this invention is to provide bleeding security documents that will be at least in part printed with such inks.
The present invention relates to a method of making a bleeding ink composition by providing at least one compound of the kind such as herein described capable of forming a binder matrix by polymerization and/or crosslinking and mixing said compound substantially homogeneously with dyestuff of the kind such as herein described substantially inert to said compound and sensible to organic solvents and/or other chemical reagents.
The bleeding printing inks, printed layers, printed substrates, methods of making an ink composition of this invention which meet the objectives mentioned above are defined in the independent claims. The new use of an ink composition is also the subject matter of this invention. Special embodiments of the ink and the security documents are defined in the dependent claims.
The invention is based on the highly unexpected finding that it is possible to obtain a printing ink which bleeds in contact with organic solvents and other chemical reagents, this even if the formulation of the ink is based on a solid matrix which is formed when the liquid ink is transformed into a solid film on the substrate and wherein this solid film itself is resistant to said solvents and chemical reagents after drying. The condition necessary to obtain the required sensitivity to bleeding is the use of dyestuffs and colouring agents which are sensitive to said solvents and chemical reagents. That is, the soluble dyestuff is attacked by the said solvents and/or reagents whereas the said matrix remains unaltered.
Manufacturing of the links of the present invention rely on the dispersion of the dyestuffs in the binder matrix which results in an ink product wherein substantially homogeneously distributed dye molecules, dye molecule aggregates and substantially undissolved and also substantially homogeneously distributed dye particles may coexist. The extent to which the dye particles are dissolved depends mainly on the dye/-
binder system. Complete dye solution will strongly and positively impact on colour development and therefore on the tinctorial strength of the prints whereas undissolved dye particles will adversely affect these characteristics.
When brought ir.to contact with a dried print performed with. an ink of the invention, solvents and/or reagents will diffuse through the binder matrix and reach dye molecules and particles causing them respectively to be washed-off or dissolved, leading to the so-called "bleeding effect". It is the surprising experience of the inventors that, provided the dyestuff is sensitive to the solvent or reagent, bleeding is necessarily observed.
The presence of porosities and defects in the dried ink film accounts probably much more for the penetration oil the solvents or reagents than pure diffusion of molecules-, of the bleeding agent through the polymeric network formed upon curing of the binder matrix. A dried ink film whatever the printing technique used inevitably presents micro-defects and porosities of all kinds such as micro-voids, micro-cracks,
bubbles and others which are so many penetration paths for the bleeding agent.
Moreover, the roughnesss of the substrate may indirectly impact on the bleeding effect by disturbing the ink film structure and in situations where the ink film is very thin it will actually consist of discontinuous and unconnected areas more easily accessible to the solvents and the reagents than large and solid ink spots. This; undoubtedly applies to an offset print on a standard cheque or bond paper where the 1 to 4 µm thick offset ink film is unable to compensate for the roughness of the substrate, the amplitude of which is at least 10 µm.
The binder matrix may also be made specifically porous. Porosity may be achieved by a variety of known techniques,
such as using a solvent which evaporates and leaves micropo-res, by mixing incompatible compounds, by adding additives creating micropores and by other techniques.
The substantially homogeneous distribution of the dyestuff (molecules and/or aggregates and/or particles) in the binder matrix results in an ink layer containing substantially homogenepously distributed dyestuff. This results in dye molecules and/cr aggregates and/or particles being distributed also on the surface or with very little coverage by the binder matrix which allows solvent to diffuse/reach the dye rather aasily.
It is worthwhile to note that a poor colour development, may favour a strong bleeding effect by reinforcing the contrast between untouched areas and those tested for bleeding.
Also of interest are all combinations between dyestuffs exhibiting a sensitivity toward different solvents or reagents. This will provide tamper evidence againet attempts made by using various chemicals and therefore reinforce the protection of the document against falsification.
Combinations of such dyestuffs and conventional pigments offer interesting possibilities as well, A violet obtained by combining a blue fugitive dye and a red resistant one will turn to red upon contact with a solvent or reagent. able; to dissolve and extract the blue dye thus making the fraud obvious.
This new type of bleeding inks brings about the same or better protective effects on security documents than known bleeding inks which, however, have the serious drawbacks described above. In addition, the compounds forming a solid matrix have been found to have better abrasion resistance.
The bleeding printing ink of the present invention can be
printed on absorbing substrates but also on non-absorbing ones since it does not need to penetrate into the substrate in order to be dried or to acquire an apparently dry condition. This advantageous property allows the user to get. a much broader choice of substrates to print upon than with known bleeding inks.
A further, most advantageous property which has already been mentioned before is the considerable diminution of time necessary from the moment of printing until the drying and any post-treatments to which the printed substrates are typically subjected. The existing bleeding inks need several days for drying, 5 to 7 on average, whereas the printing inks of this invention can be processed immediately after printing when they are formulated to dry by radiation energy such as UV light or electron beam, or after approximately 24 hours when they are dried by oxypolymerisation.
As it has already been mentioned above, the known bleeding printing inks contain a matrix or binder system which remains liquid and soluble in organic solvents and other chemical agents even after drying. In contrast thereto, the bleeding printing ink of the present invention forms a matrix on drying which becomes solid and resistant to chemical agents. In the cases where the printings are dried, i.e. cured or crosslinked under UV radiation or electron beam, the matrix is composed of a binder system containing one or more radiation curing compounds. These compounds form a matrix which is solid and resists to chemical products after a chemical. polymerisation reaction initiated by said radiation.
Compounds which are cured or crosslinked by radiation are known to the specialised ink manufacturer. Mainly, these compounds are oligomers of high or low viscosity. In the case where they are highly viscous substances, they are blended with liquid radiation curable monomers acting as viscosity regulators. These monomers are non-volatile and take part in
the polymerisation reaction wherein they become solids.
The mechanism of polymerisation can be free radical, cationic or both, called hybrid.
If the bleeding printing ink is to be dried by UV radiation, it should contain a photoinitiation system in order to start the polymerisation reaction. Such systems are widely known to the specialist ink manufacturer.
In a free radical induced polymerisation, photoinitiators can undergo photocleavage (Norrish type I photoinitiators) or proceed by the abe tract ion of hydrogon from a suitable donor (Norrish type II photoinitiators), in order to generate free radicals. The chemical reactive free radical species thus created transfer their energy to the carbon-carbon double bonds provided by the unsaturated ink binder constituents, and then the chain propagation and chain termination steps occur. It is understood that the ink binder should contain unsaturated acrylic monomers and/or oligomers which may also be modified ones.
In a cationically induced polymerisation, the photoinitiators generate ionic species initiating the polymerisation. Materials that cure by cationic mechanism include, for example, epoxides and vinyl ethers* The propagation is achieved by the attack of heterocycles under ring opening and/or vinylic carbon-carbon double bonds.
It is possible to provide a hybrid curing system, that is, curing is achieved by both free radicals and cationic mechanisms .
If the bleeding ink is to be dried by electron beam radiation, the addition of a photoinitiation system is generally not necessary.
In the bleeding printing ink of the present invention which, is dried by oxypolymerisation, the solid matrix that resists chemical products is obtained from a binder system similar to that of an ink drying by oxidation. The drying mechanism is an oxidation which implies a radical induced polymerisation of unsaturated fatty chains, brought about by atmospheric oxygen. This is a chemical reaction which may bs catalysed or accelerated by siccatives or dryers which should be incorporated into the printing ink formulation.
The bleeding or fugitive printing ink of thie invention contains one ore more dyestuffs as agents which are sensitive to organic solvents and other chemical agents. These dye-stuffs are typically the same ones as those which are normally used in known bleeding inks.
As a general rule, the binder system of the bleeding printing ink according to the present invention makes up about 40 to about 85 % by weight of the total ink weight. The dye-stuff (s), as agents that are sensible to chemical reagents, comprise typically from about 5 to about 20 % by weight of the total ink.
If the printing,ink is designed to dry under UV radiation, the photoinitiator system contains an initiator and, optionally, a co-initiator These compounds represent about 2 to about 15 % by weight of the ink.
The amount of further components of the ink, for example extenders, pigments such as Ti02 or CaCO3, stabilisers, viscosity regulators, etc., is comprised between 0 and about 15 % by weight of the printing ink.
The bleeding ink of the present invention affords the same or better level of protection on security documents than the inks already known, but comprises a binder matrix which resists the attack of organic solvents and other chemical
reagents and which is obtained in a drying time duration much shorter than the known inks. Furthermore, the known bleeding inks produce printings which are not really dry and wherein the ink continues to migrate within the interstices of the fibres of the substrate. In contrast thereto, the printings obtained in using the inks, of the present invention are stable, really dry and unable to migrate in or on the sub-strate still further, the present inks can be printed with excellent results on non-absorbing substrates such as plastic films.
The following Examples are given by way of explanation only
and can by no means be interpreted as a limitation of the
invention. In the Examples, all percentages are given by
weight.
Example 1:
A bleeding ink that dries on ultraviolet (UV) radiation was prepared for wet offset printing, and the following products were blended on a three-roller mill:
Product amount, parts
by weight
Aliphatic urethane triacrylate 43.0
Polyester acrylate {fatty acid modified) 10.0
Glycerol propoxytriagrylate (monomer) 12.5
Hydroquinone (stabiliser) 0.5
Ti02 (pigment) 1.0
CaC03 (pigment) 8.0
Dyestuff C.I, Solvent; Blue 67 (Ciba-Geigy) 15.0
Benzophsnone 7.0
Isopropyl thiosanthone 3.0
Paper was printed continuously with this printing ink at a
speed of 150 m/min and dried under 3 uV lamps having a total power of 240 w/cm lin.
The printed paper was tested using organic solvents and other chemical products (such as acetone and/or ethanol) immediately after printing and then 4 weeks later. The sensitivity of the dried, printed ink to bleeding and to colour fading, was perfect. The tests were made as follows:
Samples having a size of 20x30 mm were cut from the printed sheets after drying. These samples were immersed during 5 minutes with intermittent stirring in different organic solvents, for example acetone, ethanol, higher boiling alcohols, trichloroethylene, etc. The samples were removed after 5 minutss and dried, and their colour was compared with the untreatsd paper sheet.
If a "drop text" (deposition of a drop of solvent/reagent on the print) is performed using the same solvents, bleeding is observed with a staining of the non-printed areas surrounding the printed pattern.
Example 2:
A bleeding ink that dries by oxypolymerisation was prepared for dry and wet offset printing, and the following products were blanded on a three-roller mills
Product amount, parts
by weight
Varnish 40 to 60
Alkyd resin (Alsynol PN 66 from DMS) 15 to 25
DyestufE (Neopen Yellow from BASF) 15 to 20
Wax (Polytron 90 from Lawter) 4 to 5
Siccative (cobalt naphthenate) 1 to 2
Oxidation inhibitor (hydroquinone) 0.3 to 0.5
Silica (Aerosil 200 from Degussa) 1 to 3
The varnish is composed of a phenolic resin (Albertol KP 648, Hoechst), a bleached linseed oilr and a mineral oil (PKWF . 28/31, Haltermann).
The ink was printed on paper sheets by the offset printing process, and the printed paper was dried in open air. The drying was complete after about 24 hours. Tests with organic solvents and other chemical products were conducted on samples of the printed sheets after 24 hours and 4 weeks later. The sensitivity of the dried ink to bleeding and colour fading was excellent. The tests were made according to the method described in Example 1.
Example 3:
A UV-drying bleeding ink for screen printing was prepared
according to the following formulation:
Amounts,
Product Parts by weight
epoxy acrylate 15.0
oligoamine 25.0
glycerol propoxytriacrylate
{monomer) 30.0
dianol-diacrylate (monomer) 15.0
hydroquinone (stabiliser) 0,5
dyestuff C.I solvent blue 67 10.0
isopropyl thioxanthone 1.0
2-methy1-1 [4-(methylthio)pheny1]
-2-morpholino-propanone-l 3.5
anti-foaming agent 3,0
The ink was printed using a flat-bed screen machine. The drop test, using acetone and ethanol gave clearly visible bleeding
and staining.
The security dccuments to be printed with the bleeding inks of the present invention can be printed, entirely with prints from the new bleeding inks of the present invention, but it is also possible to print only those locations or regions . where forgery is to be expected.


We claim:
1. A method of making a bleeding ink composition for use in printing security documents by providing at least one compound of the kind such as herein described capable of forming a binder matrix by polymerization and/or crosslinking and mixing said compound substantially homogeneously with dyestuff of the kind such as herein described substantially inert to said compound and sensible to organic solvents and/or other chemical reagents wherein the compound forming a binder matrix makes up about 40 to 85 % of the total ink weight and the dye stuff comprises about 5 to 20 % by weight of the total ink.
2. A method as claimed in claim 1, wherein the said compound used
for forming a binder matrix is selected from epoxy acrylates, polyester
acrylates and polyurethane acrylates, these acrylates being optionally
modified, epoxides and vinyle ethers, and mixtures thereof.
3. A method of making a bleeding ink composition substantially as
herein described with reference to the foregoing examples.


Documents:

1086-del-1997-abstract.pdf

1086-del-1997-claims.pdf

1086-DEL-1997-Correspondence Others-(05-10-2011).pdf

1086-DEL-1997-Correspondence Others-(16-08-2011).pdf

1086-del-1997-correspondence-others.pdf

1086-del-1997-correspondence-po.pdf

1086-del-1997-description (complete).pdf

1086-del-1997-form-1.pdf

1086-del-1997-form-13.pdf

1086-DEL-1997-Form-16-(16-08-2011)-1.pdf

1086-DEL-1997-Form-16-(16-08-2011).pdf

1086-del-1997-form-19.pdf

1086-del-1997-form-2.pdf

1086-del-1997-form-3.pdf

1086-del-1997-form-4.pdf

1086-DEL-1997-GPA-(05-10-2011).pdf

1086-DEL-1997-GPA-(16-08-2011).pdf

1086-del-1997-gpa.pdf

1086-del-1997-petition-137.pdf

Patent no.-214829-Correspondence Others-(30-11-2012).pdf

Patent no.-214829-GPA-(30-11-2012).pdf


Patent Number 214829
Indian Patent Application Number 1086/DEL/1997
PG Journal Number 10/2008
Publication Date 07-Mar-2008
Grant Date 18-Feb-2008
Date of Filing 28-Apr-1997
Name of Patentee SICPA HOLDING S.A.
Applicant Address AVENUE DE FLORISSANT 41, 1008 PRILLY, SWITZERLAND
Inventors:
# Inventor's Name Inventor's Address
1 PANDELIS PAPADIMITRIOU DE LA COTE 50, 1110 MORGES, SWITZERLAND
2 OLIVIER ROZUMEK CHAMP-RIOND, 1609 ST. MARTIN, SWITZERLAND
3 ANTON BLEIKOLM CHEMIN DE LA CRAUSAZ, 1024 ECUBLENS, SWITZERLAND
4 PHILIPPE AMON AVENUE SECRETAN 26, 1005 LAUSANNE, SWITZERLAND
PCT International Classification Number C09D 11/10
PCT International Application Number N/A
PCT International Filing date
PCT Conventions:
# PCT Application Number Date of Convention Priority Country
1 NA