Title of Invention

LUBRICANT COMBINATION AND PROCESS FOR THE PREPARATION THEREOF

Abstract The present invention relates to a process for the preparation of a lubricant combination comprising the step of; selecting a first lubricant powder selected from the group consisting of fatty acid bis-amides and fatty acid monoamides and a second lubricant powder selected from the group consisting of metal soaps, mixing the lubricant powders, and adhering the particles of the second lubricant to the particles of the first lubricant in order to form a lubricant combination of aggregate particles having a core of the first lubricant with the surface of the core being coated with particles of the second lubricant.
Full Text LUBRICANT COMBINATION AND PROCESS FOR THE PREPARATION
THEREOF
This invention relates to a lubricant combination for powder metallurgy and to the manufacture and use of this lubricant combination. More particularly the invention concerns a lubricant combination including at least two lubricants.
Powdered metals, for example, powdered iron, are used to make small, fairly intricate parts, for example, gears. The fabrication of such metallic parts by powdered metal technology involves the following steps:
the powdered metal is blended with a lubricant and other additives to form a mixture,
the obtained mixture is poured into a mould and compacted to form a part using a high pressure, usually of the order of 200 to 1000 MPa,
the part is ejected from the mould,
the part is subjected to a high temperature to decompose and remove the lubricant and to cause all the particles of metal in the part to sinter together
and the part is cooled, after which it is ready for use.
Lubricants are added to metal powders for several reasons. One reason is that they facilitate the production of compacts for sintering by lubricating the interior of the powder during the compaction process. Through selection of proper lubricants higher densities, which is often required, can be obtained. Furthermore, the lubricants provide the necessary lubricating action that is needed to eject the compacted part out of the die. Insufficient lubrication will result in wear and scuffing at the die surface through the excessive friction during the ejection, resulting in premature die

failure. The problems with insufficient lubrication can be solved in two ways; either by increasing the amount of the lubricant or by selecting more efficient lubricants. By increasing the amount of lubricant, an undesired side effect is however encountered in that the gain in density through better "internal lubrication" is reversed by the increasing volume of the lubricant. The better choice would then be to select more efficient lubricants. This has however been found to be a difficult task as efficient lubricants tend to have negative effects on the powder properties of the mixture.
Another possibility would be to look for new ways to combine or use presently used lubricants in order to make them more efficient. The present invention concerns such a new combination of presently used lubricants. The concept of the invention is of course not limited to presently used and known lubricant but is applicable also to future lubricants.
According to the invention the method of making the new lubricants more efficient involves the steps of
selecting a first and a second lubricant powder
mixing the lubricant powders and
subjecting the mixture to conditions for adhering the particles of the second lubricant to the particles of the first lubricant in order to form a lubricant combination of aggregate particles having a core of the first lubricant, the surface of the core being coated with particles of the second lubricant.
The main objective of the first lubricant is to impart good lubricating properties to the powder, which will give higher densities and low ejection forces, whereas the main objective of the second lubricant is to provide a metal powder mixture having good powder properties, such as high flow rates and uniform filling of the die, which in turn gives high productivity and even density distribution in a compacted part.

Examples of lubricants within the first group are fatty acid bis-amides, such as ethylene-bis-palmitinamide, ethylene-bis-stearamide, ethylene-bis-arachinamide, ethylene-bis-behenamide, hexylene-bis-palmitinamide, hexylene-bis-stearamide, hexylene-bis-arachinamide, hexylene-bis-behenamide, ethylene-bis-12-hydroxystearamide, distearyladipamide etc. and fatty acid monoamides, such as palmitinamide, stearamide, arachinamide, behenamide, oleiamide. Additionally the first lubricant may include a solid mixture of two or more lubricants.
The second lubricant may be selected from the group consisting of metal soaps, such as zinc stearate, lithium stearate.
It is preferred that the particles of the lubricant(s) are as close to spherical shape as possible as the spherical shape leads to the highest flow rate and apparent density.
It is furthermore preferred that the first lubricant has an average particle size which is larger than that of the second lubricant. More particularly it is preferred that the average particle size of the first lubricant is 2-3 times larger than that of the second lubricant and most particularly the average particle size of the first lubricant is at least 15μm and the second lubricant has an average particle size of at most 6μm. Additionally it has been found that the amount of the first lubricant preferably should be between 60 and 90% by weight of the total lubricant combination.
One way of providing conditions for adhering the lubricant particles involves heating the particles of the first and/or the second lubricant at a temperature and for a period of time sufficient for achieving a physical bonding between the particles of the first and the second lubricant.
When mixed with metal powders, the concentration of

the lubricant combination plus optional conventional solid lubricants, is suitably in the range of 0.1 to 5% Dy weight, preferably from 0.3 to 1% by weight.
Metal powders of interest is preferably an iron based powder. Examples of iron based powders are alloyed iron based powder, such as a prealloyed iron powder or an iron powder having the alloying elements diffusion-bonded to the iron particles. The iron based powder may also be a mixture of an essentially pure iron powder and the alloying elements, which are eg selected from the group consisting of Ni, Cu, Cr, Mo, Mn, P, Si, V and W. The various amounts of the different alloying elements are between 0 and 10, preferably between 1 and 6 % by weight of Ni, between 0 and 8, preferably between 1 and 5 % by weight of Cu, between 0 and 25, preferably between 0 and 12 % by weight of Cr, between 0 and 5, preferably between 0 and 3 % by weight of Mo, between 0 and 1, preferably between 0 and 0.6 % by weight of P, between 0 and 5, preferably between 0 and 2 % by weight of Si, between 0 and 3, preferably between 0 and 1 % by weight of V and between 0 and 10, preferably between 0 and 4 % by weight of W.
The iron based powder may be an atomised powder or a sponge iron powder.
The particle size of the iron based powder is selected depending on the final use of the sintered product .
The lubricant combination according to the invention is thus a surface modified lubricant having a core of one first lubricant wherein the core surface is coated of particles of second lubricant. A comparison between this lubricant combination and a physical mixture of the same lubricants shows that the properties of the lubricant combination are superior. The same is true also for a molten and subsequently solidified mixture of the same lubricants.

The following non limiting example illustrates the invention. Example
Iron powder compositions were prepared by using lubricant compositions prepared by different methods. The lubricants were composed of the common recipe of 80 % ethylene-bis-stearamide (EBS available as Hoechst Wachs from Clariant AG, Germany) having a melting point of about 145°C, and 20% zinc stearate (available from Megret, UK) having a melting point of about 130°C. The total lubricant content was 0,8% by weight in all cases. The iron powder was ASC 100.29 (available from Hoganas AB, Sweden) and 0,5% by weight of graphite was mixed with the iron powder and lubricant.
The first lubricant composition was prepared by micronizing the two ingredients separately down to average particle sizes below 3 0;xm and subsequently admixing to the iron powder mixture.
The second lubricant composition was prepared by first melting together and solidifying the lubricants, followed by micronization and admixing to the iron powder mixture as described above.
The third lubricant was prepared by adhering the zinc stearate particles to the surface of the EBS through heating of EBS particles to temperatures where partial melting of added zinc stearate particles occurs. A stable mechanical bond between the particles was thus achieved, with the larger EBS particles essentially covered by smaller zinc stearate particles. Also in this case the particle size was below about 30μm.
After mixing, the powder properties of the iron powder compositions were characterised, including the Hall Flow, Apparent density and the Filling index. The Filling index is a measure of the relative difference in filling density (FD) between two cavities of different geometry; While the length and the depth of the cavities are the same (30 mm and 3 0 mm respectively), one cavity

has a width of 13 mm and the other a width of 2 mm. The wider cavity gives larger filling density, and the filling index is defined as;
Filling Index (%) = (FDmax-FDmin)/Fdmax
Theoretically, the Filling index is approximately the same as the relative difference in green density obtained when a powder is pressed in a cavity having cavities of the same geometry as described above, i.e. with sections of different slit widths, e.g. 13 and 2 mm.

From the results presented in Table 1, it is evident that the modification of the BBS lubricant with zinc stearate according to the present invention gives valuable advantages in powder properties compared with conventional methods of physical mixing of the separate components into a powder mixture, or by adding a melted

together and micronized lubricant composition. The flow rate is increased and the apparent density is raised. Furthermore, a more even filling is experienced, which is expected to give a more even density distribution in a complex pressed part compared with mixture made with conventional lubricants containing EBS or some other cohesive lubricants as a main constituent.

WE CLAIM:
1. A process for the preparation of a lubricant combination comprising the step of; selecting a first lubricant powder selected from the group consisting of fatty acid bis-amides and fatty acid monoamides and a second lubricant powder selected from the group consisting of metal soaps, mixing the lubricant powders, and adhering the particles of the second lubricant to the particles of the first lubricant in order to form a lubricant combination of aggregate particles having a core of the first lubricant with the surface of the core being coated with particles of the second lubricant.
2. The process as claimed in claim 1, wherein the conditions for adhering the lubricant particles to each other involves heating the particles of the first and/or the second lubricant at a temperature and a period of time sufficient for achieving a physical bonding between the particles of the first and the second lubricant.
3. The process as claimed in claim 1 or 2, wherein the particles of the first and second lubricants are essenfially spherical.
4. The process as claimed in any one of the claims 1 to 3, wherein the first lubricant has an average particle size of at least 15μm and the second lubricant has an average particle size of at most 6 μm.
5. The process as claimed in claim 1, wherein the first lubricant constitutes about 60 to 90% by weight of the lubricant combination.

6. The process as claimed in any one of claims 1 to 5, wherein the first
lubricant has a solid mixture of two or more lubricants.
7. The process as claimed in claim 1, wherein the first lubricating agent is
selected from the group consisting of fatty acid bis-amides and fatty acid
monoamides and the second lubricating agent is selected from the group consisting
of metal soaps.
8. The process as claimed in claim 7, wherein the first lubricating agent is
ethylene-bis-palmitinamide, ethylene-bis-stearamide, ethylene-bis- arachinamide,
ethylene-bis-behenamide,hexylene-bis-palmirinamide, hexylene-bis-stearamide,
hexylene-bis- arachinamide, hexylene-bis-behenamide, ethylene-bis-12-
hydroxystearamide, distearyladipamide, palmitinamide, stearamide, arachinamide,
behenamide, oleiamide or a combination thereof.
9. The process as claimed in claim 7, wherein the second lubricating agent is
zinc stearate or lithium stearate.
10. A lubricant combination of aggregate lubricant particles wherein the
combination has a core of a first lubricant selected from the group consisting of
fatty acid bis-amides and fatty acid monoamides and a coating of a second
lubricant selected from the group consisting of metal soaps.

Documents:

in-pct-2002-0806-che-abstract-duplicate.pdf

in-pct-2002-0806-che-abstract.pdf

in-pct-2002-0806-che-claims-duplicate.pdf

in-pct-2002-0806-che-claims.pdf

in-pct-2002-0806-che-correspondence-others.pdf

in-pct-2002-0806-che-correspondence-po.pdf

in-pct-2002-0806-che-desceiption(complete)-duplicate.pdf

in-pct-2002-0806-che-description(complete).pdf

in-pct-2002-0806-che-form-1.pdf

in-pct-2002-0806-che-form-19.pdf

in-pct-2002-0806-che-form-26.pdf

in-pct-2002-0806-che-form-3.pdf

in-pct-2002-0806-che-form-5.pdf

in-pct-2002-0806-che-others.pdf

in-pct-2002-0806-che-pct.pdf


Patent Number 214432
Indian Patent Application Number IN/PCT/2002/806/CHE
PG Journal Number 13/2008
Publication Date 31-Mar-2008
Grant Date 12-Feb-2008
Date of Filing 29-May-2002
Name of Patentee HOGANAS AB
Applicant Address S-263 83 Hoganas,
Inventors:
# Inventor's Name Inventor's Address
1 VIDARSSON, Hilmar Troskvagen 15, S-263 53 Hoganas,
PCT International Classification Number C10M 105/00
PCT International Application Number PCT/SE00/02397
PCT International Filing date 2000-12-01
PCT Conventions:
# PCT Application Number Date of Convention Priority Country
1 9904367-1 1999-12-02 Sweden