Title of Invention

INK COMPOSITION COMPRISING FIRST AND SECOND OPTICALLY VARIABLE PIGMENTS

Abstract The present invention relates to an ink composition comprising a polymer resin binder and first optically variable dichroic pigment flakes consisting of a comminuted multi-layered thin film interference structure comprising a stack of entirely parallel and plane layers in which at least one of the layers is totally reflecting, having first and second plane surfaces parallel to each other, and deposited on at least one of the plane surfaces at least one transparent dielectric layer, wherein the ink composition further comprising second optically variable multi-layered thin film dichroic pigments comprising a reflecting plate-like core layer in which the reflecting core layer is completely enclosed by at least one transparent dielectric layer and/or semi-opaque metal or metal-oxide layer and the first and the second optically dichroic pigment are selected such that they are not antagonistic to each other. The present invention also relates a blend of fIrst optically variable dichroic pigment flakes.
Full Text

Ink composition comprising first and second optically variable pigments
This invention relates to a printing ink composition comprising first and second multi-layered thin-film interference pigments showing a colour shift which depends on the viewing angle.
Pigments consisting of thin multi-layered film interference structures which show a viewing-angle dependent shift of colour llave been described in various publications as, for example, L. Schmid, M. Mronga, V. Radtke, 0. Seeger "Luster pigments with optically variable properties", European Coatings Journal, 7-8/1997, and patents, e.g. US 4,434,010, US 5,059,245, US 5,084,351, US 5,281,480.
The general principle of these types of interference pigments is basically a sequence of alternate thin layers parallel to each other consisting of partially and/or totally reflecting materials and low refractive index material. The hue, the colour-shift and chroma of these multi-layered interference pigments, which will be abbreviated hereinafter as OVP (Optically variable Pigments), depend on the material of the layers, the sequence of the layers, the number of layers and the layer thicknesses but also on the production process. OVP may be produced by two different categories of processes:
1. Physical vapour deposition (PVD) technologies:
Summarized, the method consists in forming a multi-layered, thin film coating by advanced PVD techniques such as roll coaters, sputtering techniques, etc. on a flexible web of a material, which is preferably soluble in a predetermined solvent. The web is typically a polymer material, such as polyvinyl alcohol or polyethyleneterephthalate. After separating the web from

the multi-layered, thin film coating, flakes are produced therefrom by shredding or grinding them down to the desired flake size. The separation can be accomplished by stripping the multi-layered coating from the web. - For this, preferably a stripping layer is deposited onto the web prior to the other layers. Heat and/or solvent may be used to facilitate the stripping process. Alternatively, instead of stripping, the web may be dissolved in a suitable solvent to accomplish the separation. The coated web may optionally be cut or shredded prior to the dissolution step. As the multi-layered thin film coating is separated from the web, it typically breaks into pieces of irregular shapes and sizes. These pieces usually require further processing to achieve the desired flake size which is suitable for use as pigment flakes in coating compositions and particularly ink compositions. The flakes can be ground down to a size ranging from 2-5 microns without destroying their colour characteristics. Preferably the average particle size is between 5 and 40 microns, but not greater than 120 microns. The flakes are produced to have an aspect ratio of at least 2:1. The aspect ratio is ascertained by taking the ratio of the largest dimension of a surface of the flake parallel to the planes of the layers to the thickness dimension to the flake (perpendicular to the plane) * The flakes can be achieved by all major categories of processing known in the art such as milling, grinding or ultrasonic agitation, optionally in the presence of solvents and/or further auxiliary materials.
OVP produced by this production process are characterized in that the pigment flakes consist of a stack of plane layers lying parallel to each other with outer pigment flake surfaces parallel to each plane layer. Due to the shredding and grinding process, the surfaces of the pigment flake

perpendicular to the plane of the layers are irregularly formed with the inner layers not covered by the outer layers.
OVP having these characteristics will be referred to hereinafter as OVP A,
2. By wet chemical type reactions or Chemical Vapour
Deposition (CVD) - US 4,328,042:
The principle of the chemical synthesis of OVP is to coat commercially available plate-like reflecting pigments with a predetermined number of weakly refracting and semi-opaque thin films. A typical process of this kind may be described more exactly by means of a specific production process run;
In a first step the plate-like pigments are suspended in an alcohol with dispersion aids. Tetraethoxysilane and an aqueous solution of ammonia is continuously added to this solution. Under these conditions, tetraethoxysilane is hydrolysed and the resulting hydrolysis product, the hypothetical silicic acid Si(0H)4/ condenses and forms Si02 as a smooth film on the surfaces of the plate-like pigments. The Si02-coating can also be carried out in a fluidized-bed reactor. In this case, vapours of tetraethoxysilane must react with water vapour. However, at the preferred temperatures of the gas-phase deposition
(100-300°C), tetraethoxysilane does not react in satisfactory yields. Special precursors, which are more reactive have to be used. Suitable precursors
are of Si(0R)2 (00CR)2-type. They vaporize at 150°C and
decompose easily with water at 200°C.
Subsequently in a chemical vapour deposition process, the silicon oxide-coated pigments are coated with metal

oxides or metal films. The coating takes place in a fluidized-bed reactor. The Si02 coated pigments are fluidized with inert gases, which are charged with
gaseous metal carbonyls. At 200°C the carbonyls decompose. If iron carbonyl is used, it can be oxidized to Fe203, which forms smooth thin films on the pigment surfaces. As an alternative method, the iron oxide coating can be carried out in a sol-gel technique known from conventional micas.
When the carbonyls of chromium, molybdenum or tungsten are decomposed under inert conditions, metallic films can be obtain. Since Mo films are not stable against water attack, they are therefore converted to molybdenum sulphide.
OVP produced by this process possess just one coherent surface. The outer coatings surround and encompass inner coatings and/or the reflective core flake. Because of this, the outer layers are not planes, but are substantially parallel to each other. The outer pigment surface is not continuously parallel to the first and second surface of the plate-like reflecting pigment. OVP showing these shape characteristics will be referred to hereinafter as OVP B.
Irrespective of whether type OVP A or OVP B, OVP includes a totally reflecting layer of a material which in the majority of cases is a metal such as aluminium, gold, copper or silver or a metal-oxide or even non-metallic materials. The first reflecting layer has a suitable thickness in the range of 50-150nm but can be up to 3 00 nm. Deposited onto the totally reflecting material is a material with a low-refractive index; such material is often called dielectric material. This layer of a dielectric material must be transparent, with a refraction index not higher than 1.65. Si02 or MgF2 are the preferred dielectric materials. The subsequent semi-

opaque layer or layers are of a metal, metal pxides or sulphids as, for example, aluminium, chromium, MoS2 or Fe203,
Opaqueness of metal is a function of the layer thickness. Aluminium, for example, becomes opaque at approximately 35 to 40 nanometers. Typically the thickness of the semi-opaque layer is between 5 to 10 nanometers. The thickness of the dielectric layer depends on the colour desired. It is thicker if longer wave-lengths are required. OVPA can be of a symmetrical or asymmetrical multilayered structure with regard to the totally reflecting layer.
A quantification of colorimetric properties is possible through the CIELAB color space diagram. In the CIELAB color space, L* indicates lightness, and a* and b* are the chromaticity coordinates. In the diagram, +a* is the red direction, -a* is green, +b* is yellow, and'-b* is blue. Chroma C* » sqrt(a*2 + b*2) increases from the center of the circle outward. Hue angle h = arctg(a*/b*) is 0° along the +a*-axis, 90° along the +b*-axis, 180° along the -a*-axis, 270° along the -b*-axis and 360° (same as 0°) along the +a*-axis(see Rompp Chemie Lexikon, wLacke und Druckfarben", Ed. U. Zorll, Georg Thieme Verlag Stuttgart, New York 1998) .
The flatness of the OVP A flakes allow a parallel orientation both to the underlying substrate and to each other when incorporated in an ink composition and printed. The therewith coated surface presents in consequence almost ideal reflecting conditions at the characteristic wavelengths of the OVP. In combination with flake characteristics which are the result of the PVD production process (plane-parallel layers, absolutely plane and smooth surfaces of the individual layers, minimal deviation of layer thicknesses compared to the predetermined and desired value) a high degree of color saturation (chroma) and the largest amount of color shift possible with OVP of such construction is attained.

Due to large amount of colour shift OVP A has found wide application in copy-preventing applications for security documents such as banknotes, checks, credit cards, passports, identity cards, driving licenses, postage stamps etc.
Inspite of the favourable properties with respect to anti-counterfeiting applications coating composition having comprised OVP A show disadvantages.
As OVP A is obtained by comminuting larger areas of a multilayer interference film, the resulting flakes have open edges, where the inner layers are accessible to chemical attack by the environment. This results in a somewhat lower chemical stability of OVP-A even when the flakes are incorporated in a cured ink layer. This is particularly a mayor drawback for the application on currency such as bank notes. The requirements for chemical resistance of the printing was established by Interpol at the 5th International Conference on Currency and Counterfeiting in 1969 or the Bureau of Engraving and Printing test methods as stated in BEP-88-214 (TH) section M5.
Bright shades, intensive hues and high chroma, are very often incompatible with the artistic aspects of currency design; strong color shifting properties, on the other hand, are the principal (copy preventing) feature justifying the use of OVP. Attempts to reduce the dramatic visual appearance of coatings comprising OVP-A have therefore already been made. OVP-A can be blended with conventional colored or black pigments to attain this and other, related goals (cf. Counterfeit deterrent features for the next-generation currency design", Publication NMAB-472, National Academy Press, Washington, 1993, pp 55-58, and references cited herein). However the mixture with black result in a dull and covered colour. Another method, according to the teaching of

EP 07,36,073, consists in blending OVP-A with suitable mica pigments, whereby the shade of the mica pigment is chosen to be similar to either the normal view color or the grazing view color of the OVP-A in question. However it results that the second color of the OVP is strongly perturbed in such mixtures, leading to an unsatisfactorily small color shift which is sometimes not even perceptible for the human eye. Therefore the mixture is unsuitable for anti-counterfeiting applications.
Moreoveir OVP A is expensive due to the costly production machines and process.
OVP B is cheaper, however the colour shift of coating composition comprising OVP B is weak, sometimes not even perceptible to the human eye, e.g. when shifting within one shade, eg. red. Therefore printing inks comprising OVP B are not suitable for copying preventing applications on security documents.
It is the object of the present invention to overcome the drawbacks of the prior art.
Particularly it is an object of the invention to lessen the chroma of an ink layer comprising OVP A while preserving a colour shift which is sufficient for applications on security documents.
It is a further object to increase the chemical resistance of cured layers comprising OVP A.
The object was solved by an ink composition comprising a polymer resin binder and first optically variable dichroic pigment flakes consisting of a comminuted multi-layered thin film interference structure comprising a stack of entirely parallel and plane layers in which at least one of the layers

is totally reflecting, having first and second plane surfaces parallel to each other, and deposited on at least one of the plane surfaces at least one transparent dielectric layer, the ink composition further comprises second optically variable multi-layered thin film dichroic pigments comprising a reflecting plate-like core layer in which the reflecting core layer is completely enclosed by at least one transparent dielectric layer and/or semi-opaque metal or metal-oxide layer. The first and second optically variable dichroic pigments are selected such that they are not antagonistic to each othe£\ u Antagonistic" in the CIELAB colour-measuring system means that the shades (chroma + hue) of both of the orthogonal and of the grazing view of the first and the second optically variable dichroic pigment are related by a center of inversion.
OVP-blending follows the rules for additive color mixing, i.e. blending red and green OVP yields yellow. Subtractive color mixing, using red and green conventional pigments, would yield black. For this reason, mixing OVP pairs with partly * antagonistic" properties (i.e. having either complementary colors, or counter-acting color shifts) can yield very interesting results.
By blending OVP A and OVP B a reduction of chroma of OVP A is achieved. Beside the reduction of the chroma of OVP A, it has unexpectedly been found that a blend of these two types of OVP maintains a clear colour shift between two distinct shades (perceivable by the human eye), e.g. green to blue, margenta to green even when OVP B quantitatively dominates in the blend. This makes the OVP-blend suited for security applications.
Preferably the chroma C* (orthogonal view) of the first optically variable dichroic pigment is equal or above 50, more preferably equal or above 55 and even more preferably :

equal or above 60, whereas the chroma C* (orthogonal view) of the second optically variable pigment is below 50 preferably below 40 and even more preferably below 30.
An unexpected synergistic effect is the improvement of the chemical resistance of the cured ink layer even if the amount of pigments of OVP A exceed the amount of OVP B. The chemical resistance of cured ink layers comprising blends of OVP A and OVP B instead of just OVP A is particularly strengthened against 2% caustic soda solution, sodium sulphide and industrial laundry.
A preferred embodiment of the present invention is an ink composition comprising a polymer resin binder and first optically variable thin film dichroic pigment flakes consisting of a comminuted multi-layered thin film interference structure comprising a stack of parallel and plane layers in which at least one of the layers is of a reflecting material having first and second plane surfaces parallel to each other and disposed on at least one of the plane surfaces at least one transparent dielectric layer, the ink composition further comprising second optically variable thin film dichroic pigments comprising a reflecting platelike core layer which is completely enclosed by at least one transparent dielectric layer and/or a semi-transparent metal or metal-oxide layer whereby the two dichroic hues of the first and second optically variable, thin film, dichroic pigment flakes are substantially the same. The first thin film multi-layered interference structure corresponds to OVP A and the second multi-layered interference structure corresponds to OVP B.
The perception of colour is very subjective, and what one observer would call "red11 another might call "orange-red" . However, as used throughout this specification and appended claims, the colour names are defined as follows: red is any

transmitted or reflected colour of a wavelength of between about 610 and about 700 nm; orange is any transmitted and reflected colour of between about 590 and 610 nm; yellow is any transmitted or reflected colour of between about 570 and 590 nm; green is any transmitted and reflected colour between about 500 and about 570 nm; blue is any transmitted or reflected colour of between about 460 and about 500 nm; and violet or purple is any transmitted colour of between about 400 and about 460 nm. In another definition, the expression "substantially the same hues" means that the hues designated by values of a* and b* are not differing more than 60 degrees from each other on the CIELAB colour-measuring system.
Preferably good results are obtained when the hue values at the midpoint between orthogonal and grazing view were approximately equal for both, the OVP A and'*the OVP B.
"Approximately equal" means that the difference between the midpoints is not more than 30°.
Particularly good results are obtained when the first multi-layered thin film interference structure (OVP A) has a symmetric construction in respect to the first reflecting layer. In this case on both of said first and second surfaces of the reflecting layer, at least one transparent dielectric layer with an index of refraction not higher than 1,65 is deposited in such a way that the resulting dielectric layers are plane and parallel to the surface of the reflecting layer.
The visual effects of the first multi-layered thin film interference structure, OVP A, is enhanced when a semi-opaque metal or metal-oxide layer is deposited on at least one of the dielectric layers. The same is true for the second multi-layered thin film interference structure, OVP B, in case the dielectric layer is surrounded by a semi-opaque

metal or metal-oxide layer.
Preferred materials for both multi-layered interference structures are chromium for the semi-opaque layer and aluminium for the reflecting layer.
In an ink composition of the present invention, the blend ratio of the first and second multi-layered thin film interference structure (OVP A to OVP B) should be in a ratio of 1:10 to 10:1, preferably in a ratio of 1:1.5 to 1:0,6.
The ink composition of the present invention may further comprise additional non-interference pigments.
Blends of OVP A and OVP B can be incorporated in any suitable ink vehicle as long as the ink vehicle is not detrimental to the visual appearance of the OVP. Particularly it must not cover the optical effects of the pigment and must not be aggressive to the layer materials. Generally ink vehicles comprise at least one film-forming polymeric binder, solvents, optionally water, extenders and auxiliary agents such as non-foaming-, wetting-, rheology-control agents, antioxidants, etc..
The ink layer can be applied to the underlying substrate by any of the known printing techniques, in particular by intaglio, flexographic, gravure and silk-screen printing.
An ink composition comprising first and second multi-layered interference structures is preferably used for printing security documents such as bank notes, cheques, credit cards, etc. The colour shifting properties of an image printed by using such an ink composition are not reproducible by photocopying and as such impart to the document a strong security feature. Besides the application in security documents, an ink of the kind described by the present


The indicated colors and color shifts refer to approximately 50:50 blends* Corresponding diagrams in the CIELAB color space for the nine series of blends are given in Figures 3a to 3i.
As shown in the table, useful colour shifting properties of the blend were obtained with OVP-A and OVP-B having comparable hues (h values) at both relevant viewing angles. In these cases (i.e. the blends of ED 1819 with G/B, of ED 1820 with M/G and of ED 1821 with M/G) the colour shift is very satisfactory in respect to photocopying prevention. Very good results were obtained when hue values at the midpoint between orthogonal and grazing view were approximately equal for both, the OVP-A and the OVP-B. This is the case e.g. in the blend of ED 1821 with M/G) .
Some OVP blends with partially antagonistic behavior of the constituents showed, surprisingly, striking color shifts,

too, as the blend of ED 1821 with G/B (changing from green to almost black) or the blend of ED 1821 with B/R (changing from violet to brown).
A silk screen printing ink was produced by incorporating various percentages of OVP-A and/or OVP-B into a suitable ink matrix. The corresponding chroma and colour (hue) values h, according to the CIELAB color system, were measured on a printed and cured ink patch (silk screen prints made with a Hand Coater no.3/ measurements performed on a PHYMA Penta Gonio.P













The chemical resistance with respect to caustic soda, (2%
solution in water, 30 minutes, 25°C), to saturated solution
of sodiumsulphate in water, (30 minutes, 25°C) and to
industrial laundry (30 minutes 95*c) was dramatically increased for the blends. Whereas an ink layer with an ink according to 100% OVP A simply becomes black and loses the colour shift entirely, an ink layer with an ink according to the blends only becomes a bit darker in colour but keeps colour and colour-shift.





CLAIMS
l. An ink composition comprising a polymer resin binder and first optically variable dichroic pigment flakes consisting of a comminuted multi-layered thin film interference structure comprising a stack of entirely parallel and plane layers in which at least one of the layers is totally reflecting, having first and second plane surfaces parallel to each other, and deposited on at. least one of the plane surfaces at least one transparent dielectric layer, wherein the ink composition further comprising second optically variable multi-layered thin film dichroic pigments comprising a reflecting plate-like core layer in which the reflecting core layer is completely enclosed by at least one transparent dielectric layer and/or semi-opaque metal or metal-oxide layer and the first and the second optically dichroic pigment are selected such that they are not antagonistic to each other.
2. An ink composition according to claim l, characterized in that the chroma C* of the first variable dichroic pigment in orthogonal view is equal or above 50 and the chroma C* of the second optically variable dichroic variable pigment in orthogonal view is below 50.
3. An ink composition according to claims 1 to*2 characterized in that the midpoint of the hues between orthogonal and grazing view of said first and said second optically variable pigment are not differing from each other more than 30°.
4. An ink composition comprising a polymer resin binder and first optically variable dichroic pigment flakes consisting of a comminuted multi-layered thin film

interference structure comprising a stack of entirely-parallel and plane layers in which at least one of the layers is totally reflecting, having first and second plane surfaces parallel to each other, and deposited on at least one of the plane surfaces at least one transparent dielectric layer, the ink composition further comprising second optically variable multi-layered thin film dichroic pigments comprising a reflecting plate-like core layer in which the reflecting core layer is completely enclosed by at least one transparent dielectric layer and/or semi-opaque metal or metal-oxide layer whereby the two dichroic hues of the first optically variable dichroic pigment and the second optically variable dichroic pigment are substantially the same.
5* An ink composition according to one of the claims 1 to 4, wherein the first multi-layered thin film interference structure is symmetric having on both of said surfaces of the reflecting layer at least one transparent dielectric layer having an index of refraction not higher than 1.65 with surfaces parallel and plane to the surface of the reflecting layer.
6. An ink composition according to one of the claims 1 to 5, wherein the first multi-layered thin film interference structure further comprises, disposed on at least one of said dielectric layers, a semi-opaque metal* or metal-oxide layer.
7. An ink composition according to any of the claims 1 to 6 wherein the second multi-layered thin-film interference structure further comprises, disposed on the dielectric layer, a semi-opaque metal or metal-oxide layer.
8. An ink composition according to one of the claims l to 7

wherein the reflecting layer of the first and/or the second multi-layered thin film interference structure is a metal or metal-oxide.
9. An ink composition according to one of the claims 1 to 8 wherein at least one layer of the second multi-layered interference structure is produced by chemical vapour deposition.
10. An ink composition according to one of the claims 1 to 9, characterized in that the ratio between said first and said second optically variable dichroic pigment is in a range of between 1:10 to 10:1, preferably in a range of between 1:1.5 to 1:0.6.
11.An ink composition according to one of the preceding claims, wherein the colour shift of the second multi-layered structure with the viewing angle is less and the chroma is weaker compared with the first interference structure.
12.Blend of first optically variable dichroic pigment flakes consisting of a comminuted multi-layered thin film interference structure comprising a stack of entirely parallel and plane layers in which at least one of the layers is totally reflecting, having first and second plane surfaces parallel to each other, and deposited on at least one of the plane surfaces at least*one transparent dielectric layer, characterized in that the blend comprises second optically variable multi-layered thin film dichroic pigments comprising a reflecting plate-like core layer in which the reflecting core layer is completely enclosed by at least one transparent dielectric layer and/or semi-opaque metal or metal-oxide layer whereby the first and the second optically dichroic pigment are selected such that the color effect is not

12. An ink composition substantially as hereinbefore described with
reference to the accompanying drawings.
13. Blend of first optically variable dichroic pigment flakes substantially
as hereinbefore described with reference to the accompanying
drawings.


Documents:

in-pct-2000-138-che-abstract.pdf

in-pct-2000-138-che-claims filed.pdf

in-pct-2000-138-che-claims granted.pdf

in-pct-2000-138-che-correspondnece-others.pdf

in-pct-2000-138-che-correspondnece-po.pdf

in-pct-2000-138-che-description(complete)filed.pdf

in-pct-2000-138-che-description(complete)granted.pdf

in-pct-2000-138-che-drawings.pdf

in-pct-2000-138-che-form 1.pdf

in-pct-2000-138-che-form 26.pdf

in-pct-2000-138-che-form 3.pdf

in-pct-2000-138-che-form 5.pdf

in-pct-2000-138-che-pct.pdf

in-pct-2000-138-che-priority document.pdf


Patent Number 211033
Indian Patent Application Number IN/PCT/2000/138/CHE
PG Journal Number 50/2007
Publication Date 14-Dec-2007
Grant Date 16-Oct-2007
Date of Filing 22-Jun-2000
Name of Patentee M/S. SICPA HOLDING S.A
Applicant Address Avenue de Florissant 41, 1008 Prilly
Inventors:
# Inventor's Name Inventor's Address
1 BLEIKOLM, Anton Chemin de la Crausaz 12 CH-1024 Ecublens
2 ROZUMEK, Olivier Champ-Riond CH-1609 St. Martin
3 MÜLLER, Edgar Avenue de Florimont 28 CH-1006 Lausanne
PCT International Classification Number C09C 1/00
PCT International Application Number PCT/EP99/07572
PCT International Filing date 1999-10-08
PCT Conventions:
# PCT Application Number Date of Convention Priority Country
1 98118992.1 1998-10-08 EUROPEAN UNION