Title of Invention

A PROCESS FOR PRODUCING A POLYAMIDE

Abstract The present invention relates to a process for producing a polyamide by reaction of at least one aminonitrile with water, comprising the following steps: of reacting at least one aminonitrile with water at a temperature from 90 to 400oC and a pressure from 0.1 to 35 x 106 Pa. The reaction can be carried out in the presence of a Bronsted acid catalyst selected from a beta-zeolite catalyst, a sheet-silicate catalyst or a titanium dioxide catalyst consisting of from 70 to 100% by weight of anatase and from 0 to 30% by weight of rutile and in which up to 40% by weight of the titanium dioxide may be replaced by tungsten oxide, to obtain a reaction mixture. The reaction mixture is further reacted at a temperature from 150 to 400oC and a pressure which is lower than the pressure in step 1, in the presence of a Bronsted acid catalyst selected from a beta-zeolite catalyst, a sheet-silicate catalyst or a titanium dioxide catalyst consisting of from 70 to 100% by weight of anatase and from 0 to 30% by weight of rutile and in which up to 40% by weight of the titanium dioxide may be replaced by tungsten oxide. The temperature and pressure is selected so as to obtain a first gas phase and a first liquid or a first solid phase or a mixture of first solid and first liquid phase, and the first gas phase is separated from the first liquid or the first solid phase or from the mixture of first liquid and first solid phase. The first liquid or the first solid phase or the mixture of first liquid and first solid phase is admixed with a gaseous or liquid phase comprising water at a temperature from 150 to 370oC and a pressure from 0.1 to 30x106 Pa, optionally in the presence of the above catalyst, to obtain a product mixture. wherein the reaction is carried out in the presence of lactams, amino carboxylic acids or mixtures thereof in an amount of from 0.3 to 10% by weight, based on the amount of aminonitrile used.
Full Text

AS ORIGINALLY FILED
ACCELERATANT FOR PRODUCING POLYAMIDES FROM
AMINONITRILES
The present invention relates to accelerants and processes for producing polyamides from aminonitriles and water, in particular at elevated temperature and elevated pressure.
US 4,629,776 describes a catalytic process for producing polyamides from ω-aminonitriles such as ω-amino-capronitrile (ACN). ACN is reacted with water in the presence of a catalytic amount of an oxidized sulfur compound as catalyst. Sulfuric acid is an example of the catalyst used.
US 4,568,736 describes a similar catalytic process for producing polyamides. The catalyst used in this case is an oxygen-containing phosphorus compound, phosphoric acid or a phosphonic acid.
Complete removal of catalyst is practically not possible m either process. The presence of catalyst in the polymer can hinder the building of high molecular weight polymers and compromise later processing operations, for example spinning. Moreover, the level of volatiles in the polymers obtained is high, so that the polyamides are difficult to process.
EP-A-0 479 306 describes the production of polyamides from ω-aminonitriles. The oaminonitriles are reacted with water in the presence of an oxygen-containing phosphorus compound as catalyst. Once a reaction temperature from 200 to 260°C has been obtained, ammonia and water are continuously removed by decompressing and at the same time water is continuously added, the pressure being selected within the range from 14 to 24 x 105 Pa (14-24 bar).

DE-A-43 39 648 relates to a process for producing caprolactam by reacting aminocarbonitriles with water in the liquid phase using heterogeneous catalysts. Suitable heterogeneous catalysts include acidic, basic or amphoteric oxides of the elements of main groups 2, 3 and 4 of the Periodic Table. Titanium dioxide can be used, for example. The catalyst is used in the form of extrudates, for example.
Existing processes provide inadequate space-time yields in some instances and a molecular weight buildup which could do with improvement. In addition, the product is not always obtained in the requisite purity.
DE-A-197 09 390 and DE-A-198 04 023, both unpublished at the priority date of the present invention, describe the use of heterogeneous metal oxide catalysts in the reaction of aminonitriles with water to form polyamide. The advantage is that the fixed bed catalyst used is completely removable from the reaction mixture or the end product and the product properties are not adversely affected. However, the use of the fixed bed catalyst is subject to constraints if pigmented reaction mixtures are used, since the catalyst solids may blind and hence may lose their catalytic effect.
It is an object of the present invention to provide an accelerant for producing polyamides from aminonitriles and water and an improved process which leads to products which are not impaired by the accelerant. More particularly, the product and processing properties and the purity of the end product shall not be reduced.
We have found that this object is achieved according to the invention by using lactams, aminocarboxylic acids or their mixtures as accelerants or cocatalysts in the production of polyamides from aminonitriles and water.
The lactams, aminocarboxylic acids or mixtures thereof are preferably used in an amount of from 0.1 to 20% by weight, based on the aminonitrile quantity. They may be used together with metal oxide fixed bed catalysts as described hereinbelow.
We have found that this object is additionally achieved according to the invention by a process for producing a polyamide by reaction of at least one aminonitrile with water, which comprises the following steps:

(1) reacting at least one aminonitrile with water at a temperature from 90
to 400oC and a pressure from 0.1 to 35 x 106 Pa, which reaction can be carried out in the presence of a Bronsted acid catalyst selected from a beta-zeolite catalyst, a sheet-silicate catalyst or a titanium dioxide catalyst consisting of from 70 to 100% by weight of anatase and from 0 to 30% by weight of rutile and in which up to 40% by weight of the titanium dioxide may be replaced by tungsten oxide, to obtain a reaction mixture,
(2) further reacting the reaction mixture at a temperature from 150 to
400°C and a pressure which is lower than the pressure in step 1, which reaction can be carried out in the presence of a Bronsted acid catalyst selected from a beta-zeolite catalyst, a sheet-silicate catalyst or a titanium dioxide catalyst consisting of from 70 to 100% by weight of anatase and from 0 to 30% by weight of rutile and in which up to 40% by weight of the titanium dioxide may be replaced by tungsten oxide, the temperature and pressure being selected so as to obtain a first gas phase and a first liquid or a first solid phase or a mixture of first solid and first liquid phase, and the first gas phase is separated from the first liquid or the first solid phase or from the mixture of first liquid and first solid phase, and
(3) admixing the first liquid or the first solid phase or the mixture of first
liquid and first solid phase with a gaseous or liquid phase comprising water at a temperature from 150 to 370°C and a pressure from 0.1 to 30 x 106 Pa, optionally in the presence of the above catalyst, to obtain a product mixture, wherein the reaction is carried out in at least one of steps (1) and (2) in the presence of lactams, aminocarboxylic acids or mixtures thereof in an amount of from 0.1 to 20% by weight, based on the amount of aminonitrile used.
Preferably, the above process additionally comprises the following step:
(4) postcondensing the product mixture at a temperature from 200 to
350°C and a pressure which is lower than the pressure of step 3, the temperature and pressure being selected so as to obtain a second, water- and ammonia-comprising gas phase and a second liquid or second solid phase or a mixture of second liquid and second solid phase, which each comprise the polyamide.

The present invention further provides a continuous process for producing a polyamide by reaction of at least one aminonitrile with water, which comprises the following steps:
(1) reacting at least one aminonitrile with water at a temperature from 90
to 400°C and a pressure from 0.1 to 35 x 106 Pa, which reaction can be carried out in the presence of a Bronsted acid catalyst selected from a beta-zeolite catalyst, a sheet-silicate catalyst or a titanium dioxide catalyst consisting of from 70 to 100% by weight of anatase and from 0 to 30% by weight of rutile and in which up to 40% by weight of the titanium dioxide may be replaced by tungsten oxide, to obtain a reaction mixture.
(2) further reacting the reaction mixture at a temperature from 150 to
400°C and a pressure which is lower than the pressure in step 1, which reaction can be carried out in the presence of a Bronsted acid catalyst selected from a beta-zeolite catalyst, a sheet-silicate catalyst or a titanium dioxide catalyst consisting of from 70 to 100% by weight of anatase and from 0 to 30% by weight of rutile and in which up to 40% by weight of the titanium dioxide may be replaced by tungsten oxide, the temperature and pressure being selected so as to obtain a first gas phase and a first liquid or a first solid phase or a mixture of first solid and first liquid phase, and the first gas phase is separated from the first liquid or the first solid phase or from the mixture of first liquid and first solid phase, and
(4) postcondensing the first liquid or the first solid phase or the mixture of
first liquid and first solid phase at a temperature from 200 to 350°C and a pressure which is lower than the pressure of step 3, the temperature and pressure being selected so as to obtain a second, water- and ammonia-comprising gas phase and a second liquid or second solid phase or a mixture of second liquid and second solid phase, which each comprise the polyamide, wherein the reaction is carried out in at least one of steps (1) and (2) in the presence of lactams, aminocarboxylic acids or mixtures thereof in an amount of from 0.1 to 20% by weight, based on the amount of aminonitrile used.
The principle of the process of the invention is described in DE-A-197 09 390, unpublished at the priority date of the present invention.
The aminonitrile in the mixture can be in principle any aminonitrile, i.e., any compound having both at least one amino group and at least one nitrile group, ω-

"T VU 1^
Aminonitriles are preterred, especially ω-aminoalkyl futures having from
carbon atoms, more preferably 4 to 9 carbon atoms, in the alkylene moiety, or an aminoalkylaryl nitrile having from 8 to 13 carbon atoms, preferred aminoalkylaryl nitriles being aminoalkylaryl nitriles which have an alkylene group of at least one carbon atom between the aromatic unit and the amino and nitrile group. Especially preferred ammoalkylaryl nitriles are those which have the amino group and nitrile group in the 1,4 position relative to each other.
The ω-aminoalkyl nitrile used is preferably a linear ω-aminoalkyl nitrile in which the alkylene moiety (-CH2-) preferably contains from 4 to 12 carbon atoms, more preferably from 4 to 9 carbon atoms, such as 6-amino-l-cyanopentane (6-aminocapronitrile), 7-amino-l-cyanohexane, 8-amino-l-cyanoheptane, 9-amino-l-cyanooctane, 10-amino-l-cyanononane, particularly preferably 6-aminocapronitrile.
6-Ammocapronitrile is customarily obtained by hydrogenation of adiponitrile according to known methods, described for example in DE-A 836,938, DE-A 848,654 or US-A 5,151,543.
Preferably, the lactam used is caprolactam and the aminocarboxylic acid, aminocaproic acid. The lactams and/or aminocarboxylic acids are preferably mixed into the feed mixture upstream of the first reaction step. They can also be added in subsequent reaction steps.
Preferably, both the lactam and the aminocarboxylic acid or their mixture are added as a constituent of an aqueous phase to the reaction mixture. The addition can also take place in highly concentrated form in the solid or liquid state. To this end, the lactam and/or the aminocarboxylic acid may be heated, for example, in a stirred tank to above the melting point and pumped into the respective reaction step.
The addition of lactam and/or aminocarboxylic acid to the reaction mixture preferably takes place in the first, second and/or third step, particularly preferably in the first and third steps.
The lactams, aminocarboxylic acids or mixtures thereof are used in an amount of from 0.01 to 20% by weight, preferably from 0.3 to 10% by weight, particularly preferably from 1.0 to 7.0% by weight, based on the amount of aminonitriles. The addition leads to a considerable acceleration of the hydrolytic polymerization. In the process, the reaction product is not changed or contaminated, since, if the lactams or aminocarboxylic acids are incorporated into the polymer chain, no new polymer constituents are included. More particularly, the lactam and the

aminocarboxylic acid should produce the same polymers; i.e., aminocapronitrile should be used with caprolactam and/or aminocaproic acid as accelerant. The use of these compounds leads to a considerable acceleration in the reaction of the aminonitriles with water.
In what follows, the different steps are described, the lactams and/or aminocarboxylic acids being added at the points indicated hereinabove.
The process can be operated continuously or batchwise.
According to the invention, the first step (step 1) involves heating an aminonitrile with water at a temperature from 90 to 400°C, preferably 180 to 310°C, especially at 220 to 270°C, a pressure from 0.1 to about 15 x 106 Pa, preferably 1 to 10 x 106 Pa, especially 4 to 9 x 106 Pa, being set. hi this step, the pressure and the temperature can be adjusted relative to each other in such a way as to obtain a liquid or a solid phase and a mixture of liquid or solid phase and a gaseous phase.
According to the invention, water is used in a molar ratio of aminoalkyl nitriie to water within the range from 1:1 to 1:10, particularly preferably within the range from 1:2 to 1:8, very particularly preferably within the range from 1:2 to 1:6, preference being given to the use of water in excess, based on the aminoalkyl nitriie used.
In this embodiment, the liquid or solid phase or the mixture of liquid and solid phase corresponds to the reaction mixture, whereas the gaseous phase is separated off. As part of this step, the gaseous phase can be separated from the liquid or solid phase or from the mixture of solid or liquid phase at once, or the synthesis mixture forming within this step can be present in two-phase form: liquid/gaseous, solid/gaseous or liquid-solid/gaseous. It will be appreciated that the pressure and temperature can also be adjusted relative to each other in such a way that the synthesis mixture is present as a single solid or liquid phase.
The removal of the gas phase can be effected by the use of stirred or unstirred separating tanks or tank batteries and by the use of evaporator apparatus, for example by means of circulatory evaporators or thin-film evaporators, as, for example, by film extruders, or by means of annular disk reactors, which ensure an enlarged phase Interface. In certain cases, recirculation of the synthesis mixture or the use of a loop reactor may be necessary to increase the phase interface. Furthermore, the removal of the gas phase can be furthered by the addition of water vapor or inert gas into the liquid phase.

Preferably, the pressure is adjusted at a preselected temperature so that the pressure is smaller than the equilibrium vapor pressure of ammonia, but greater than the equilibrium vapor pressure of the other components in the synthesis mixture at the given temperature. This way, it is possible to favor especially the removal of ammonia and thus speed up the hydrolysis of the acid amide groups.
The two-phase procedure is preferably carried out at a pressure which is above the vapor pressure of pure water associated with the bulk temperature of the reaction mixture, but below the equilibrium vapor pressure of ammonia.
A particularly preferred embodiment of the two-phase procedure utilizes an upright flow tube which is operated under upward flow and optionally has above the product outlet a further opening for gas phase removal. This tubular reactor can be completely or partially packed with catalyst pellets. In a preferred embodiment, the upright reactor utilized in the two-phase procedure is maximally packed with catalyst material up to the phase boundary.
In another, particularly preferred embodiment of the first step, the pressure is selected in such a way that the reaction mixture is present as a single liquid phase, i.e., no gas phase is present in the reactor. For this single-phase procedure, the preferred embodiment is a flow tube packed exclusively with catalyst material.
According to the invention, the aminonitrile/water mixture is heated with a heat exchanger before being introduced into the first step. It will be appreciated that the aminonitrile and the water can also be heated separately from each other and be mixed in the first step by the use of mixing elements.
As regards the residence time of the synthesis mixture in the first step, there are no restrictions whatsoever; however, it is generally selected within the range from about 10 minutes to about 10 hours, preferably within the range from about 30 minutes to about 6 hours.
Although there are no restrictions whatsoever concerning the degree of conversion of nitrile groups in step 1 either, economic reasons especially dictate that the conversion of nitrile groups in step 1 be generally not less than about 70 mol%, preferably not less than about 95 mol%, and especially within the range fi-om about 97 to 99 mol%, each based on the moles of aminonitrile used.
The nitrile group conversion is customarily determined by means of IR spectroscopy (CN stretching vibration at 2247 wavenumbers), NMR or HPLC, preferably by IR spectroscopy.

Nor does the invention rule out conducting the reaction in step 1 additionally in the presence of oxygen-containing phosphorus compounds, especially pho3phoric acid, phosphorous acid and hypophosphorous acid and their alkali metal and alkaline earth metal salts and ammonium salts such as Na3PO4, NaH2PO4, Na2HPO4, NaH2PO3, Na2HPO3, NaH2PO2, K3PO4, KH2PO4, K2HPO4, KH2PO3, K2HPO3, KH2PO2, in which case the molar ratio of co-aminonitrile to phosphorus compounds is selected within the range from 0.01:1 to 1:1, preferably within the range from 0.01:1 to 0.1:1.
The reaction in step 1 is preferably carried out in a flow tube containing a Bronsted acid catalyst selected from a beta-zeolite catalyst, a sheet-silicate catalyst or a titanium dioxide catalyst comprising from 70 to 100% by weight of anatase and from 0 to 30% by weight of rutile and in which up to 40% by weight of the titanium dioxide may be replaced by tungsten oxide. If a very pure aminonitrile is used, the proportion of anatase in the titanium dioxide catalyst should be as high as possible. Preferably, a pure anatase catalyst is used. If the aminonitrile used contains impurities, for example 1 to 3% by weight of impurities, preference is given to using a titanium dioxide catalyst comprising a mixture of anatase and rutile. Preferably, the anatase fraction is from 70 to 80% by weight and the rutile fraction from 20 to 30% by weight. In this case, it is particularly preferable to use a titanium dioxide catalyst comprising about 70% by weight of anatase and about 30% by weight of rutile. The catalyst preferably has a pore volume of from 0.1 to 5 ml/g, particularly preferably from 0.2 to 0.5 ml/g. The average pore diameter is preferably within the range from 0.005 to 0.1 |im, particularly preferably within the range from 0.01 to 0.06 μm. If highly viscous products are used, the average pore diameter should be large. The cutting hardness is preferably greater than 20 N, particularly preferably > 25 N. The BET surface area is preferably more than 40 m /g, particularly preferably more than 100 m^/g. If the BET surface area is smaller, the bed volume should be appropriately higher to ensure adequate catalyst activity. Particularly preferred catalysts have the following properties: 100% of anatase; 0.3 ml/g pore volume; 0.02 μm average pore diameter; 32 N cutting hardness; 116 m /g BET surface area or 84% by weight of anatase; 16% by weight of rutile; 0.3 ml/g pore volume; 0.03 μm average pore diameter; 26 N cutting hardness; 46 m /g BET surface area. The catalysts may be prepared from commercial powders as available for example from Degussa, Finnti or Kemira. When tungsten oxide is used, up to 40% by weight, preferably up to 30% by weight, particularly preferably from 15 to 25% by weight of the titanium dioxide is replaced by tungsten oxide. The catalysts can be prepared as described in Ertl, Knozinger, Weitkamp: "Handbook of heterogeneous catalysis", VCH Weinheim, 1997, pages 98ff. The catalyst can be used in any desired suitable form. It is preferably used in the form of shaped articles, extrudates or pellets, especially in the form of pellets. The pellets are preferably sufficiently large to be readily separable from the product mixture and not to impair the flowability of the product during the reaction.

The pellet form of the catalyst makes it possible to remove the catalyst mechanically at the point of exit from the first step. For example, mechanical filters or sieves are provided at the point of exit from the first step. If the catalyst is additionally used in the second and/or third step, it is preferably present in the same form.
According to the invention, the reaction mixture obtained in the first step is further reacted in step 2 at a temperature from about 200 (150) to about 350 (400)'C, preferably at a temperature within the range from about 210 (200) to about 330 (330)°C, especially within the range from about 230 (230) to about 270 (290)°C, and a pressure which is lower than the pressure in step 1. The pressure in the second step is preferably at least about 0.5 x 10^ Pa lower than the pressure in step 1, and generally the pressure will be within the range fi'om about 0.1 to about 45 x 10^ Pa, preferably within the range from about 0.5 to about 15 x 106 Pa, especially within the range from about 2 to about 6 x 10 Pa (values in brackets: without catalyst).
In step 2, the temperature and the pressure are chosen so as to obtain a first gas phase and a first liquid or first solid phase or a mixture of first liquid and first solid phase and the first gas phase is separated from the first liquid or first solid phase or from the mixture of first liquid and first solid phase.
The first gaseous phase, which consists essentially of ammonia and water vapor, is generally removed continuously by means of a distillation apparatus, such as a distillation column. Any organic constituents of the distillate coremoved in the course of this distillation, predominantly unconverted aminonitrile, can be wholly or partly recycled into step 1 and/or step 2.
The residence time of the reaction mixture in step 2 is not subject to any restrictions whatsoever, but is generally within the range fi'om about 10 minutes to about 5 hours, preferably within the range from about 30 minutes to about 3 hours.
The product line between the first and second steps optionally contains packing elements, for example Raschig rings or Suizer mixing elements, which facilitate a controlled expansion of the reaction mixture into the gas phase. This relates in particular to the single-phase procedure.
Preferably, the reactor of the second step likewise contains the catalyst material of the invention, especially in pellet form. It was found that the reactor provides a further improvement in the product properties compared with a catalyst-free reactor, especially at higher pressures and/or in the presence of a large amount of excess water in the reaction mixture. Temperature and pressure should be selected

in such a way that the viscosity of the reaction mixture remains sufficiently low to prevent any blinding of the catalyst surface. According to the invention, the point of exit from the second process step too is equipped with sieves or filters which guarantee the purity of the reaction mixture and separate the catalyst from the reaction mixture.
hi step 3, the first liquid or the first solid phase or the mixture of first liquid and first solid phase is admixed with a gaseous or liquid phase comprising an aqueous medium, preferably water or water vapor. This is done continuously. The amount of water added (as liquid) is preferably within the range from about 50 to about 1500 ml, more preferably within the range from about 100 to about 500 ml, based in each case on 1 kg of the first liquid or first solid phase or of the mixture of first liquid and first solid phase. This addition of water primarily compensates the water losses incurred in step 2 and furthers the hydrolysis of acid amide groups in the synthesis mixture. This results in a further advantage of this invention, that the mixture of the starting materials as used in step 1 can be used with a small excess of water only.
The gaseous or liquid phase comprising water is preferably preheated in a heat exchanger before being introduced into step 3 and then mixed with the first liquid or the first solid phase or the mixture of first solid and first liquid phase. The reactor may optionally be fitted with mixing elements which further the mixing of the components.
Step 3 may be operated at a temperature from 150 to 370°C and a pressure from 0.1 to 30 X 106 Pa, if a catalyst bed is present, the conditions applicable for step 1 may be employed. Otherwise, the temperature is preferably within the range from 180 to 300°C, particularly preferably within the range from 220 to 280°C. The pressure is preferably within the range from 1 to 10 x 106 Pa, particularly preferably within the range from 2 x 106 Pa to 7 x 106 Pa.
The pressure and temperature can be adjusted to each other in such a way that the synthesis mixture is present as a single liquid or solid phase. In another embodiment, the pressure and temperature are selected so that a liquid or a solid phase or a mixture of solid and liquid phase and also a gaseous phase are obtained. In this embodiment, the liquid or solid phase or the mixture of liquid and solid phase corresponds to the product mixture, whereas the gaseous phase is separated off. As part of this step, the gaseous phase can be separated from the liquid or solid phase or from the mixture of solid or liquid phase at once, or the synthesis mixture forming within this step can be present in two-phase form: liquid/gaseous, solid/gaseous or liquid-solid/gaseous.
The pressure can be adjusted at a preselected temperature so that the pressure is smaller than the equilibrium vapor pressure of ammonia, but greater than the equili-

brium vapor pressure of the other components in the synthesis mixture at the given temperature. This way, it is possible to favor especially the removal of ammonia and thus further speed up the hydrolysis of the acid amide groups.
The apparatus/reactors usable in this step can be identical with those of step 1, as discussed above.
The residence time of this step is likewise not subject to any restrictions, but economic reasons generally dictate a range from 10 minutes to 10 hours, preferably from 60 minutes to 8 hours, particularly preferably from 60 minutes to 6 hours.
The product mixture obtained in step 3 can be further processed as described below.
In a preferred embodiment, the product mixture of step 3 is subjected to a postcondensation in a fourth step at a temperature from 200 to 350°C, preferably at a temperature from 220 to 300°C, especially from 240 to 270°C. Step 4 is carried out at a pressure which is below the pressure of step 3 and is preferably within the range from 5 to 1000 x 106 Pa, more preferably within the range from 10 to 300 x 106 Pa.In the context of this step, the temperature and pressure are selected so as to obtain a second gas phase and a second liquid or solid phase or a mixture of second liquid and second solid phase which each comprise the polyamide.
The postcondensation of step 4 is preferably carried out in such a way that the relative viscosity (measured at a temperature of 25°C and a concentration of 1 g of polymer per 100 ml in 96% strength by weight of sulfuric acid) of the polyamide assumes a value within the range from about 1.6 to about 3.5.
In a preferred embodiment, any water present in the liquid phase can be expelled by means of an inert gas such as nitrogen.
The residence time of the reaction mixture in step 4 depends especially on the desired relative viscosity, the temperature, the pressure and the amount of water added in step
3.
If step 3 is operated as a single-phase regime, the product line between step 3 and step 4 may optionally contain packing elements, for example, Raschig rings or Sulzer mixing elements, which allow a controlled expansion of the synthesis mixture in the gas phase.

The fourth step too can be operated using the catalyst. It was found that the use of the catalyst in step 4 improves the molecular weight buildup in particular when the relative viscosity of the effluent from the third or - in the case of the three-step procedure - the second step is less than RV =1.6 - and/or the molar nitrile group and acid amide content in the polymer is greater than 1%, each based on the moles of aminonitrile used.
In a further embodiment of the invention, step 3 may be dispensed with and the polyamide produced by carrying out steps (1), (2) and (4).
This variant is preferably carried out as follows:
In step 1, the reaction is carried out as described above.
The reaction mixture is treated in step 2 as described above or at a temperature within the range fi'om about 220 to about 300°C and a pressure within the range from about 1 to about 7x106 Pa, the pressure in the second step being at least 0.5 x 106 Pa lower than in step 1. At the same time, the resulting first gas phase is separated fi'om the first liquid phase.
The first liquid phase obtained in step 2 is treated in step 4 as in step 1 or at a temperature within the range fi'om about 220 to 300°C and a pressure within the range fi'om about 10 to about 300 x 106 Pa, the resulting second, water- and ammonia-comprising gas phase being separated from the second liquid phase. Within this step, the relative viscosity (measured as defined above) of the resulting polyamide is adjusted to a desired value within the range from about 1.6 to about 3.5 through choice of temperature and residence time.
The resulting second liquid phase is then conventionally discharged and, if desired, worked up.
In a fiirther preferred embodiment of the present invention, at least one of the gas phases obtained in the respective steps can be recycled into at least one of the preceding steps.
It is further preferable to select the temperature and pressure in step 1 or in step 3 or in both step 1 and step 3 so as to obtain a liquid or a solid phase or a mixture of liquid and solid phase and a gaseous phase and to separate off the gaseous phase.

Furthermore, in the context of the process of the invention, it is also possible to carry out a chain lengthening or branching or a combination thereof For this purpose, polymer branching or chain-extending substances known to a person skilled in the art are added in the individual steps. These substances are preferably added in step 3 or
4.
Usable substances are:
Trifimctional amines or carboxylic acids as branching agents or crosslinkers. Examples of suitable at least trifimctional amines or carboxylic acids are described in EP-A-0 345 648. The at least trifimctional amines have at least three amino groups which are capable of reaction with carboxylic acid groups. They preferably do not have any carboxylic acid groups. The at least trifimctional carboxylic acids have at least three carboxylic acid groups which are capable of reaction with amines and which can also be present, for example, in the form of their derivatives, such as esters. The carboxylic acids preferably do not contain any amino groups capable of reaction with carboxylic acid groups. Examples of suitable carboxylic acids are trimesic acid, trimerized fatty acids, prepared for example from oleic acid and having from 50 to 60 carbon atoms, naphthalenepolycarboxylic acids, such as naphthalene-1,3,5,7-tetracarboxylic acid. The carboxylic acids are preferably defined organic compounds and not polymeric compounds.
Examples of amines having at least 3 amino groups are nitrilotrialkylamine, especially nitrilotriethaneamine, dialkylenetriamines, especially diethylenetriamine, trialkylenetetramines and tetraalkylenepentamines, the alkylene moieties preferably being ethylene moieties. Furthermore, dendrimers can be used as amines. Dendrimers preferably have the general formula I


n is an integer from 2 to 6, and
X is an integer from 2 to 14.
Preferably, n is 3 or 4, especially 3, and x is an integer from 2 to 6, preferably from 2 to 4, especially 2. The radicals R can also have the stated meanings independently of one another. Preferably, R is a hydrogen atom or a -(CH2)NH2 radical.
Suitable carboxylic acids are those having from 3 to 10 carboxylic acid groups, preferably 3 or 4 carboxylic acid groups. Preferred carboxylic acids are those having aromatic and/or heterocyclic nuclei. Examples are benzyl, naphthyl, anthracene, biphenyl, triphenyl radicals or heterocycles such as pyridine, bipyridine, pyrrole, indole, furan, thiophene, purine, quinoline, phenanthrene, porphyrin, phthalocyanine, naphthalocyanine. Preference is given to 3,5,3',5'-biphenyltetracarboxylic acid-phthalocyanine, naphthalocyanine, 3,5,5',5'-biphenyltetracarboxylic acid, 1,3,5,7-naphthalenetetracarboxylic acid, 2,4,6-pyridinetricarboxylic acid, 3,5,3',5'-bipyrid-yltetracarboxylic acid, 3,5,3',5'-ben2ophenonetetracarboxylic acid, 1,3,6,8-acridinetetracarboxylic acid, particularly preferably 1,3,5-benzenetricarboxylic acid (trimesic acid) and 1,2,4,5-benzenetetracarboxyUc acid. Such compounds are commercially available or can be prepared by the process described in DE-A-43 12 182. If ortho-substituted aromatic compounds are used, imide formation is preferably prevented through the choice of suitable reaction temperatures.
These substances are at least trifunctional, preferably at least tetrafunctional. The number of functional groups can be from 3 to 16, preferably from 4 to 10, particularly preferably from 4 to 8. The processes of the invention are carried out using either at least trifunctional amines or at least trifunctional carboxylic acids, but not mixtures of such amines or carboxylic acids. However, small amounts of at least trifimctional amines may be present in the trifimctional carboxylic acids, and vice versa.
The substances are present in an amount from 1 to 50 μmol/g of polyamide, preferably from 1 to 35, particularly preferably 1 to 20, μmol/g of polyamide. The substances are preferably present in an amount from 3 to 150, particularly preferably from 5 to 100, especially from 10 to 70, μmol of equivalents/g of polyamide. The equivalents are based on the number of functional amino groups or carboxylic acid groups.
Difunctional carboxylic acids or difimctional amines are used as chain lengtheners. These have 2 carboxylic acid groups which can be reacted with amino groups, or 2 amino groups which can be reacted with carboxylic acids. The difimctional

carboxylic acids or amines, as well as the carboxylic acid groups or amino groups, do not contain any further functional groups capable of reaction with amino groups or carboxylic acid groups. Preferably, they do not contain any further functional groups. Examples of suitable difunctional amines are those which form salts with difunctional carboxylic acids. They can be linear aliphatic, such as C1-14-alkylenediamine, preferably C2-6-alkylenediamine, for example hexylenediamine. They can also be cycloaliphatic. Examples are isophoronediamine, dicycycan, laromine. Branched aliphatic diamines are likewise usable, an example being Vestamin TMD (trimethylhexamethylenediamine, from Hiils AG). In addition, the diamines can also be aromatic-aliphatic, it being possible to use n-xylylenediamine, for example. Entire amines can each be substituted by C1-12-alkyl, preferably C1-14-alkyl, radicals on the carbon skeleton.
Difunctional carboxylic acids are, for example, those which form salts with difunctional diamines. They can be linear aliphatic dicarboxylic acids, which are preferably C4-2o-dicarboxylic acids. Examples are adipic acid, azelaic acid, sebacic acid, suberic acid. They can also be aromatic. Examples are isophthalic acid, terephthalic acid, naphthalenedicarboxylic acid, as well as dimerized fatty acids.
The difunctional basic building blocks (c) are preferably used in amounts from 1 to 55, particularly preferably from 1 to 30, especially from 1 to 15, μm/g of polyamide.
According to the invention, the product mixture obtained in step 3, or the second liquid or second solid phase or the mixture of second liquid and second solid phase (from step 4) which each comprise the polyamide, preferably a polymer melt, is discharged from the reaction vessel in a conventional manner, for example by means of a pump. Subsequently, the polyamide obtained can be worked up according to conventional methods, as described for example in DE-A 43 21 683 (page 3 line 54 to page 4 line 3) at length.
In a preferred embodiment, the level of cyclic dimer in the nylon-6 obtained according to the invention can be further reduced by extracting the polyamide first with an aqueous solution of caprolactam and then with water and/or subjecting it to a gas phase extraction (described in EP-A-0 284 968, for example). The low molecular weight constituents obtained in this aftertreatment, such as caprolactam, linear caprolactam oligomer and cyclic caprolactam oligomer, can be recycled into the first and/or second and/or third step.
The starting mixture and the synthesis mixture can be admixed in all steps with chain regulators such as aliphatic and aromatic carboxylic and dicarboxylic acids and catalysts such as oxygen-containing phosphorus compounds in amounts within the range from 0.01 to 5% by weight, preferably within the range from 0.2 to 3% by

weight, based on the amount of polyamide-forming monomers and aminonitriles used. Suitable chain regulators include for example propionic acid, acetic acid, benzoic acid, terephthalic acid and triacetonediamine.
Additives and fillers such as pigments, dyes and stabilizers are generally added to the synthesis mixture prior to pelletization, preferably in the second, third and fourth steps. Particular preference is given to using fillers and additives whenever the synthesis or polymer mixture will not encounter fixed bed catalysts in the rest of the processing. One or more impact-modified rubbers may be present m the compositions as additives in amounts from 0 to 40% by weight, preferably fi'om 1 to 30% by weight, based on the entire composition.
It is possible to use, for example, customary impact modifiers which are suitable for polyamides and/or polyaiylene ethers.
Rubbers which enhance the toughness of polyamides generally have two essential features: they have an elastomeric portion which has a glass transition temperature of less than -10°C, preferably less than -30°C, and they contain at least one fimctional group which is capable of interaction with the polyamide. Suitable fimctional groups include for example carboxylic acid, carboxylic anhydride, carboxylic ester, carboxylic amide, carboxylic imide, amino, hydroxyl, epoxide, urethane and oxazoline groups.
Examples of rubbers which enhance the toughness of the blends include for example:
EP and EPDM rubbers grafted with the above fimctional groups. Suitable grafting reagents include for example maleic anhydride, itaconic acid, acrylic acid, glycidyl acrylate and glycidyl methacrylate.
These monomers can be grafted onto the polymer in the melt or in solution, in the presence or absence of a free-radical initiator such as cumene hydroperoxide.
The copolymers of a-olefins described under the polymers A, including especially the ethylene copolymers, may also be used as rubbers instead of polymers A and be mixed as such into the compositions of the invention.
A further group of suitable elastomers are core-shell graft rubbers. These are graft rubbers which are produced in emulsion and which have at least one hard and one soft constituent. A hard component is customarily a polymer having a glass transition

temperature of at least 25°C, while a soft constituent is a polymer having a glass transition temperature of not more than 0°C. These products have a structure made up of a core and at least one shell, the structure being the result of the order in which the monomers are added. The soft constituents are generally derived from butadiene, isoprene, alkyl acrylates, alkyl methacrylates or siloxanes and optionally further comonomers. Suitable siloxane cores can be prepared for example starting from cyclic oligomeric octamethyltetrasiloxane or tetravinyltetramethyltetrasiloxane. These can be for example reacted with y-mercaptopropylmethyldimethoxysilane in a ring-opening cationic polymerization, preferably in the presence of sulfonic acids, to form the soft siloxane cores. The siloxanes can also be crosslinked by, for example, conducting the polymerization reaction in the presence of silanes having hydrolyzable groups such as halogen or alkoxy groups such as tetraethoxysilane, methyltri-methoxysilane or phenyltrimethoxysilane. Suitable comonomers here include for example styrene, acrylonitrile and crosslinking or grafting monomers having more than one polymerizable double bond such as diallyl phthalate, divinylbenzene, butanediol diacrylate or triallyl (iso)cyanurate. The hard constituents are generally derived from styrene, a-methylstyrene and copolymers thereof, preferred comonomers being acrylonitrile, methacrylonitrile and methyl methacrylate.
Preferred core-shell graft rubbers have a soft core and a hard shell or a hard core, a first soft shell and at least one further hard shell. The incorporation of functional groups such as carbonyl, carboxylic acid, acid anhydride, acid amide, acid imide, carboxylic esters, amino, hydroxyl, epoxy, oxazoline, urethane, urea, lactam or halobenzyl groups is here preferably effected by the addition of suitably functionalized monomers during the polymerization of the last shell. Suitable functionalized monomers include for example maleic acid, maleic anhydride, mono-or diesters of maleic acid, tert-butyl (meth)acrylate, acrylic acid, glycidyl (meth)acrylate and vinyloxazoline. The proportion of monomers having fimctional groups is generally within the range from 0.1 to 25% by weight, preferably within the range from 0.25 to 15% by weight, based on the total weight of the core-shell graft rubber. The weight ratio of soft to hard constituents is generally within the range from 1:9 to 9:1, preferably within the range from 3:7 to 8:2.
Such rubbers, which enhance the toughness of polyamides, are known per se and described in EP-A-0 208 187 for example.
A fiirther group of suitable impact modifiers are thermoplastic polyester elastomers. Polyester elastomers are segmented copolyetheresters containing long-chain segments, generally derived from poly(alkylene) ether glycols, and short-chain segments, derived from low molecular weight diols and dicarboxylic acids. Such products are known per se and are described in the literature, for example in US 3,651,014. Corresponding products are also commercially available under the names of Hytrel® (Du Pont), Amitel® (Akzo) and Pelprene® (Toyobo Co. Ltd.).

It will be appreciated that it is also possible to use mixtures of different rubbers.
As further additives there may be mentioned for example processing aids, stabilizers and oxidation retardants, agents against thermal decomposition and decomposition by ultraviolet light, lubricating and demolding agents, flame retardants, dyes and pigments and plasticizers. The proportion thereof is generally up to 40%, preferably up to 15%, by weight, based on the total weight of the composition.
Pigments and dyes are generally present in amounts of up to 4%, preferably from 0.5 to 3.5%, especially from 0.5 to 3%, by weight.
The pigments for coloring thermoplastics are commonly known, see for example R. Gachter and H. Miiller, Taschenbuch der Kunststoffadditive, Carl Hanser Verlag, 1983, pages 494 to 510. The first preferred group of pigments to be mentioned are white pigments such as zinc oxide, zinc sulfide, lead white (2 PbCOa, Pb(OH)2), lithopone, antimony white and titanium dioxide. Of the two most common crystal polymorphs (rutile and anatase) of titanium dioxide, the rutile form is preferred for use as white pigment for the molding compositions of the invention.
Black pigments which can be used according to the invention are iron oxide black (Fe3O4), spinel black (Cu(Cr,Fe)2O4), manganese black (mixture of manganese dioxide, silicon dioxide and iron oxide), cobalt black and antunony black and also, particularly preferably, carbon black, which is usually used in the form of furnace or gas black (see G. Benzing, Pigmente flir Anstrichmittel, Expert-Verlag (1988), p. 78ff).
It will be appreciated that inorganic color pigments such as chromium oxide green or organic color pigments such as azo pigments and phthalocyanines can be used according to the invention to obtain certain hues. Such pigments are generally commercially available.
It can further be of advantage to use the abovementioned pigments or dyes in a mixture, for example carbon black with copper phthalocyanines, since this generally facilitates the dispersion of color in the thermoplastic.
Oxidation retardants and thermal stabilizers which can be added to the thermoplastic compositions of the invention include for example halides of metals of group I of the periodic table, e.g., sodium halides, potassium halides, lithium halides, optionally in conjunction with copper(I) halides, for example chlorides, bromides or iodides. The halides, especially of copper, may also contain electron-rich p-ligands. Examples of

such copper complexes are copper halide complexes with triphenylphosphine, for example. It is further possible to use zinc fluoride and zinc chloride. Other possibilities are sterically hindered phenols, hydroquinones, substituted representatives of this group, secondary aromatic amines, optionally in conjunction with phosphorus-containing acids and salts thereof, and mixtures of these compounds, preferably in a concentration up to 1% by weight, based on the weight of the mixture.
Examples of UV stabilizers are various substituted resorcinols, salicylates, benzotriazoles and benzophenones, which are generally used in amounts of up to 2% by weight.
Lubricating and demolding agents, which are generally included in the thermoplastic material in amounts of up to 1% by weight, are stearic acid, stearyl alcohol, alkyl stearates and N-alkylstearamides and also esters of pentaerythritol with long-chain fatty acids. It is also possible to use salts of calcium, of zinc or of aluminum of stearic acid and also dialkyl ketones, for example distearyl ketone.
The present invention further provides a polyamide producible by one of the processes.
The examples which follow illustrate the invention.

Examples
The time-resolved measurements of production Examples 1-6 and the products of a continuous production of nylon-6 from ACN in a Miniplant (Examples 7-8) show that caprolactam and aminocaproic acid accelerate the reaction of aminocapronitrile.
Comparative Example 1:
In a 2 liter pressure vessel equipped with a heating jacket and an anchor stirrer, 1400 g of a reaction mixture of aminocapronitrile and water in a molar ratio of 1:4 were stirred at 250°C in the sealed reactor. The autogenous pressure was 48 bar. The hydrolysis of the aminocapronitrile (conversion) as a function of the reaction time is reported in Table 1.
Examples 2-4 with caprolactam as catalytically active additive
In a 2 liter pressure vessel equipped with a heating jacket and an anchor stirrer, 1400 g of a reaction mixture of aminocapronitrile and water in a molar ratio of 1:4 and an addition of 1% by weight, 5% by weight and 10% by weight of caprolactam (each based on the ACN fraction) were stirred at 250°C in the sealed reactor. The autogenous pressure was 48 bar. The hydrolysis of the aminocapronitrile (conversion) as a function of the reaction time is reported in Table 1.
Examples 5-6 with aminocaproic acid as catalytically active additive
In a 2 liter pressure vessel equipped with a heating jacket and an anchor stirrer, 1400 g of a reaction mixture of aminocapronitrile and water in a molar ratio of 1:4 and an addition of 5% by weight and 10% by weight of aminocaproic acid (each based on the ACN fraction) were stirred at 250°C in the sealed reactor. The autogenous pressure was 48 bar. The hydrolysis of the aminocapronitrile (conversion) as a function of the reaction time is reported in Table 1.
Examples 7-8: Continuous production of polyamide from ACN in the presence of caprolactam in a Miniplant apparatus.

Polyamide was produced continuously according to the invention in a multistep Miniplant. The aminocapronitrile/caprolactam/water reaction mixture contained 50% by weight of aminocapronitriie, 8% by weight of caprolactam and 42% by weight of water. The comparative runs were carried out using an aminocapronitrile/water mixture containing 50% by weight of ACN and 50% by weight of water. The purity of the aminocapronitrile used was 99.5%.
An HPLC pump fed the preheated reaction mixture at a rate of 150 or 600 g/h into a tubular reactor having an empty volume of 1 liter and an intemal length of 1000 mm. It was completely packed with catalyst pellets which were 100% TiO2 from Finnti, type SI50 in the anatase form, and had a strand length within the range from 2 to 14 mm, a strand thickness of about 4 mm and a specific surface area of more than 100m2/g. The reaction mixture in the tubular reactor had a temperature of 250°C. The pressure in the reactor was 60 bar. The reaction mixture obtained was subsequently transferred into a 2 liter separating vessel and after the reaction at 250°C and 4 bar discharged with the aid of a gear pump.
The product properties of the polyamides produced and the corresponding residence times are listed hereinbelow in Table II.
The purity of the aminocapronitrile used was 99.5%.
The comparative products or examples were prepared by reacting ACN with water without caprolactam under identical process conditions or at the same process parameters. The process parameters and the product properties are tabulated hereinbelow. Throughput is the mass flow of reaction mixture through the first process step.
CL: caprolactam
ACS: aminocaproic acid







AS ENCLOSED TO IPER
We claim:
1. The use of lactams, aminocarboxylic acids or mixtures thereof as accelerant or cocatalyst in the production of polyamides from aminonitriles and water.
2. A use as claimed in claim 1, wherefor the lactams, aminocarboxylic acids or mixtures thereof are used in an amount of from 0.3 to 10% by weight, based on the aminonitrile quantity.
3. A use as claimed in claim 1 or 2, wherefor the lactams, aminocarboxylic acids or mixtures thereof are used together with metal oxide fixed bed catalysts.
4. A process for producing a polyamide by reaction of at least one aminonitrile with water, which comprises the following steps:
(1) reactmg at least one aminonitrile with water at a temperature from 90 to 400°C and a pressure from 0.1 to 35 x 106 Pa, which reaction can be carried out in the presence of a Bronsted acid catalyst selected from a beta-zeolite catalyst, a sheet-silicate catalyst or a titanium dioxide catalyst consisting of from 70 to 100% by weight of anatase and from 0 to 30% by weight of rutile and in which up to 40% by weight of the titanium dioxide may be replaced by tungsten oxide, to obtain a reaction mixture,
(2) further reacting the reaction mixture at a temperature from 150 to 400°C and a pressure which is lower than the pressure in step 1, which reaction can be carried out in the presence of a Bronsted acid catalyst selected from a beta-zeolite catalyst, a sheet-silicate catalyst or a titanium dioxide catalyst consisting of from 70 to 100% by weight of anatase and from 0 to 30% by weight of rutile and in which up to 40% by weight of the titanium dioxide may be replaced by tungsten oxide, the temperature and pressure being selected so as to obtain a first gas phase and a first liquid or a first solid phase or a mixture of first solid and first liquid phase, and the first gas phase is separated from the first liquid or the first solid phase or from the mixture of first liquid and first solid phase, and

(3) admixing the first liquid or the first solid phase or the mixture of first liquid and first solid phase with a gaseous or liquid phase comprising water at a temperature from 150 to 370oC and a pressure from 0.1 to 30x10oCPa, optionally in the presence of the above catalyst, to obtain a product mixture,
wherein the reaction is carried out m at least one of steps (1) and (2) in the presence of lactams, aminocarboxylic acids or mixutres thereof in an amount of from 0.3 to 10% by weight, based on the amount of aminonitrile used.
5. A process as claimed in claim 4, which additionally comprises the following step:
(4) postcondensing the product mixture at a temperature from 200 to 350°C and a pressure which is lower than the pressure of step 3, the temperature and pressure being selected so as to obtain a second, water- and ammonia-comprising gas phase and a second liquid or second solid phase or a mixture of second liquid and second solid phase, which each comprise the polyamide.
6. A process for producing a polyamide by reaction of at least one aminonitrile with
water, which comprises the following steps:
(1) reacting at least one aminonitrile with water at a temperature from 90 to 400°C and a pressure from 0.1 to 35 x 106 Pa, which reaction can be carried out in the presence of a Bronsted acid catalyst selected from a beta-zeolite catalyst, a sheet-silicate catalyst or a titanium dioxide catalyst consisting of from 70 to 100% by weight of anatase and from 0 to 30% by weight of rutile and in which up to 40% by weight of the titanium dioxide may be replaced by tungsten oxide, to obtain a reaction mixture,
(2) further reacting the reaction mixture at a temperature from 150 to 400°C and a pressure which is lower than the pressure in step 1, which reaction can be carried out in the presence of a Bronsted acid catalyst selected from a beta-zeolite catalyst, a sheet-silicate catalyst or a titanium dioxide catalyst consisting of from 70 to 100% by weight of anatase and from 0 to 30% by weight of rutile and in which up to 40% by weight of the titanium dioxide may be replaced by tungsten oxide, the temperature and pressure being selected so as to obtain a first gas phase and a first liquid or a first solid phase or a mixture of first solid and first liquid phase, and the first gas phase is separated from the first liquid or the first solid phase or from the mixture of first liquid and first solid phase, and

(4) postcondensing the first liquid or the first solid phase or the mixture of first liquid and first solid phase at a temperature from 200 to 350°C and a pressure which is lower than the pressure of step 3, the temperature and pressure being selected so as to obtain a second, water- and ammonia-comprising gas phase and a second liquid or second solid phase or a mixture of second liquid and second solid phase, which each comprise the polyamide,
wherein the reaction is carried out in at least one of steps (1) and (2) in the presence of lactams, aminocarboxylic acids or mixtures thereof in an amount of fi:om 0.3 to 10% by weight, based on the amount of aminonitrile used,
7. A process as claimed in any of claims 4 to 6, wherein the temperature and pressure in
step 1 or in step 3 or in both step .1 and step 3 are selected so as to obtain a liquid or a
solid phase or a mixture of liquid and solid phase and a gaseous phase, and the
gaseous phase is separated off.
8. A process as claimed in any of claims 4 to 7, wherein the reaction of step 1 is carried
out with a molar ratio of aminonitrile to water of from 1:1 to 1:30.
9. A process as claimed in any of claims 4 to 8, wherein 6-aminocapronitrile and
caprolactam, aminocapronic acid or mixtures thereof are used.
10. A process as claimed in any of claims 4 to 9, wherein the lactams, aminocarboxylic
acids or mixtures thereof are used in an amount of from 1.0 to 7.0 % by weight,
based on the amount of aminonitrile used.
11. A process for producing a polyamide, substantially as herein described, and
exemplified.


Documents:

in-pct-2001-481-che- abstract.pdf

in-pct-2001-481-che- claims duplicate.pdf

in-pct-2001-481-che- claims original.pdf

in-pct-2001-481-che- correspondence others.pdf

in-pct-2001-481-che- correspondence po.pdf

in-pct-2001-481-che- descripition complete duplicate.pdf

in-pct-2001-481-che- descripition complete original.pdf

in-pct-2001-481-che- form 1.pdf

in-pct-2001-481-che- form 19.pdf

in-pct-2001-481-che- form 26.pdf

in-pct-2001-481-che- form 3.pdf

in-pct-2001-481-che- form 5.pdf

in-pct-2001-481-che- pct.pdf


Patent Number 207420
Indian Patent Application Number IN/PCT/2001/481/CHE
PG Journal Number 26/2007
Publication Date 29-Jun-2007
Grant Date 13-Jun-2007
Date of Filing 03-Apr-2001
Name of Patentee BASF AKTIENGESELLSCHAFT
Applicant Address D-67056 Ludwigshafen
Inventors:
# Inventor's Name Inventor's Address
1 MOHRSCHLADT Ralf Sternallee 5 D-68723 Schwetzingen
2 HILDEBRANDT Volker Am Brunnengarten 23 D-68169 Mannheim
PCT International Classification Number C08G69/00
PCT International Application Number PCT/EP1999/007382
PCT International Filing date 1999-10-05
PCT Conventions:
# PCT Application Number Date of Convention Priority Country
1 198 46 014.7 1998-10-06 Germany