Title of Invention

PHOTOACTIVE POLYMERS

Abstract A photoactive polymer of the general formula I: 5 in which: P is a photoactive group which can photoisomerise and/or photodimerise; B represents an aromatic or alicyclic group which is unsubstituted or substituted by fluorine, chlorine or cyano, or by a cyclic, straight-chain or branched alkyl residue which is unsubstituted, mono-substituted by cyano or halogeno, or poly-substituted by halogeno, having 1 to 18 carbon atoms and wherein one or more CH.2 groups may independently be replaced by -0-, -CO-, -CO-O-, -0-CO-, -Si(CH3)2-0-Si(CH3)2-, -NR2-, -NR2-CO-, -CO-NR2-, -NR2-CO-0-, -O-CO-NR2-, -NR2-CO-NR2-, -CH=CH-, -OC-. -0-CO-0-, with the proviso that oxygen atoms are not directly attached to each other, and wherein R2 represents a hydrogen atom or lower alkyl, or B further repiesents a nitrogen atom or -CR2-; A, C, D each independently of the other represents an aromatic or alicyclic group which is unsubstituted or substituted by fluorine, chlorine, cyano, or by a cyclic, straight-chain or branched alkyl residue which is unsubstituted, mono-substituted by cyano or halogeno, or poly-substituted by halogeno, having 1 to 18 carbon atoms and wherein one or more Chb groups may independently be replaced by -0-, -CO-, -CO-O-, -0-CO-, -Si(CH3)2-0-Si(CH3)2-, -NR2-, NR2-CO-, -CO-NR2-, -NR2-CO-0-, -O-CO-NR2-, -NR2-CO-NR2-, -CH=CH-, -C=C-, -O-CO-O-, with the proviso that oxygen atoms are not directly attached to each other, and wherein R2 represents a hydrogen atom or lower alkyl; M represents a repeating monomer unit in a homo- or copolymer; S1, S2, S3, S4, S5 represent a single covalent bond or a spacer unit, comprising a straight-chain or branched alkylene residue which is unsubstituted, mono-substituted by cyano or halogeno, or poly-substituted by halogeno, having 1 to 24 carbon atoms, wherein one or more CH2 groups may independently be replaced by -0-, -CO-, -CO-O-, -O-CO-, -Si(CH3)2-0-Si(CH3)2-, -NR2-, -NR2-CO-, -CO-NR2-, -NR2-CO-0-, -0-CO-NR2-, -NR2-CO-NR2-, -CH=CH-, -C=C-, -O-CO-O-, with the proviso that oxygen atoms are not directly attached to each other, and wherein R2 represents a hydrogen atom or lower alkyl; n1, n2 are each independently a positive integer up to 2 with the proviso that n1 + n2 ≤ 2; R1 is a hydrogen atom, or a straight-chain or branched alkyl residue which is unsubstituted, mono-substituted by cyano or halogeno, or poly-substituted by halogeno, having 1 to 18 carbon atoms, wherein one or more CH2 groups may independently be replaced by -0-, -CO-, -CO-O-, -O-CO-, -Si(CH3)2-0-Si(CH3)2-, -NR2-, -NR2-CO-, -CO-NR2-, -NR2-CO-0-, -O-CO-NR2-, -NR2-CO-NR2-, -CH=CH-, -C=C-, -O-CO-O-, with the proviso that oxygen atoms are not directly attached to each other, and wherein R2 represents a hydrogen atom or lower alk/1.
Full Text FORM 2
THE PATENTS ACT, 1970
(39 of 1970)
COMPLETE SPECIFICATION
[See section 10; Rule 13]
PHOTOACTIVE POLYMERS;
ROLIC AG, A CORPORATION ORGANIZED AND EXISTING UNDER THE LAWS OF SWITZERLAND, WHOSE ADDRESS IS CHAMERSTRASSE 50, 6301 ZUG, SWITZERLAND.
THE FOLLOWING SPECIFICATION PARTICULARLY DESCRIBES THE NATURE OF THIS INVENTION AND THE MANNER IN WHICH IT IS TO BE PERFOMED. 1

Photoactive polymers
The present invention relates to new photoactive polymers, and their use as orientation layers for liquid crystals and in the construction of unstructured and structured optical elements and multi-layer systems.
Different electro-optical effects used for liquid crystal displays (LCD) require alignment layers with very high pretilt angles. Vertically aligned nematic (VAN) LCDs for instance require pretilt angles between 85° and 90°, measured from the surface plane. In the case of hybrid aligned nematic (HAN)-LCDs, the pretilt angle at one of the substrates has to be in the above range, whereas the tilt angle at the other substrate is low (typically 0-10°). Brushed polyimides which are capable of inducing high pretilt angles suffer from the known drawbacks of the brushing technique. In the case of VAN-LCDs especially scratches caused by brushing and insufficient pretilt angle uniformity are well known problems of the brushing technique. on the other hand, stable ;photoalignable matenals for high pretilt angles,which would solve they
above problems,are not khown so far
Most of the known electro-optic LCD-modes suffer from residual birefringence of the liquid crystal layer which results in reduced contrast, intrinsic colours and/or restricted viewing angles. Optical retarders are applied to the LCD to compensate for the residual birefringence. Tilted LC-configurations which are formed upon applying a voltage to the LCD are used in most of the commercialised LCDs to adjust grey scale. The very asymmetric viewing angle dependence of such tilted LC-configurations is optimally compensated if the optical axis of the compensating retarder is tilted as well. Liquid crystal polymers (LCP) which were photoaligned by LPP-materials prior to polymerisation are ideally suited to such an application, as the tilt of the optical axis can principally be adjusted to any value between 0° and 90° by the adjacent alignment layer. A drawback of known alignment materials inducing very high pretilt angles is their high surface tension which causes wetting problems. Consequently, it is not possible to coat a uniform layer of LCP-prq>olymers on top of such alignment layers.

EP-A-0 611 786 (F. Hoffmann-La Roche AG) discloses polymers having isomerisation / dimerisation units of the general formula:


wherein:
Ma, Mb, Mc
x,yz
Sa, Sb Za,Zb
n m

signify monomer units for homo- or copolymers;
indicate mole fractions of the copolymers, whereby in each
caseO represent spacer units;
represent molecule units which can undergo photochemical
isomerisation / dimerisation;
is from 4-100 000; and
is 0 or 1.

These linear and cyclic polymers or oligomers have a photoreactive ethene group for use as orientating layers for liquid crystals.
WO-A-96/10049 (F. Hof&nann-La Roche AG) discloses polymers of the general formula:


wherein:
M1 and M2 signify monomer units for homo- or copolymers;
x and yindicate mole fractions of the comonomers, with in each
case 0 p signifies 4 to 30 000;
S1 and S2 signify spacer units;
Ql signifies a structural unit of the formula:
-A-(zl-B)z-Z2- IIa;
Q^ signifies a structural unit of the formula:
-A-(Zl-B)z-Rl- IIb;
A and B each independently signify pyridine-2,5-diyl, pyrimidine-
-2,5-diyl, 1,4-cyclohexylene, l,3-dioxane-2,5-diyl or optionally
substituted 1,4-phenylene;
Z1 and Z2 each independently signify a single covalent bond, -CH2-CH2-,
-CH2O-, -OCH2-, -CONR-, -RNCO-, -COO- or -OOC-;
R signifies hydrogen or lower alkyl;
Rl signifies hydrogen, optionally substituted alkyl or alkoxy with
in each case 1 to 12 carbon atoms, cyano, nitro or halogen;
z signifies 0 or 1;
C signifies a photochemically dimerisable coumarin or
quinolinone derivative; and
m and n each independently signify 0 or 1.
These linear and cyclic polymers or oligomers of coumarin and quinolinone derivatives have a photoreactive ethene group and may be used as orieriting layers for ;, liquid crystals:;
EP-A-0763 552 (Rolic AG) discloses polymer compositions in which repeating units of general formula I are present:


wherein
M 1 signifies a repeating monomer unit from the group; acrylate, methacrylate,
2-chloroacrylate, 2-phenylacrylate; optionally N-lower alkyl substituted acrylamide, methacrylamide, 2-chloroacrylamide and 2-phenylacrylamide; vinyl ether, vinyl ester, styrene derivative, siloxane;
S1 signifies spacer units such as, for example, a single covalent bond, a
straight-chain or branched alkylene grouping represented hereinafter by -(CH2)r as well as -(CH2)r-O-, -(CH2)r-0-(CH2)s-, -(CH2)r-0-(CH2)s-0-, -(CH2)rCO-, -(CH2)rCO-0-, -(CH2)r-0-CO-,
-(CH2)rNR2-, -(CH2)r-CO~NR2-, -(CH2)rNR2-CO-,
(CH2)r-NR2-CO-0- or -(CH2)r-NR2-CO-NR3-, which is optionally mono- or multiply-substituted with fluorine, chlorine or cyano and in which r and s are each a whole number of 1 to 20, with the proviso that r +
s≤ 20, and R2 and R3 each independently signify hydrogen or lower alkyl; ring A signifies phenylene which is unsubstituted or optionally substituted with
fluorine, chlorine, - cyano, alkyl or allcoxy, pyridine-2,5-diyl,
pyrimidine-2,5-diyl, l,3-dioxane-275-diyl, cyclohexane-l,4-diyl,
piperidine-l,4-diyl, piperazine-l,4'-diyl; ring B signifies phenylene which is unsubstituted or optionally substituted with
fluorine, chlorine, cyano, alkyl or allcoxy, pyridine-2,5-diyi, pyrimidine-
-2,5-diyl, 1,4- or 2,6-naphthylene, l,3-dioxane-2,5-diyl, cyclohexane-
-1,4-diyl;

Yl, Y2 each independently signify a single covalent bond, -(CH2)t-, -0-, -CO-, -CO-0-, -0-OC-, -NR4-, -CO-NR4-, -R4N-CO-, -(CH2)u-0-, -0-(CH2)u-, -(CH2)u-NR4- or -NR4-(CH2)U-, in which
R4 signifies hydrogen or lower alkyl;
t signifies a whole number of 1 to 4;
u signifies a whole number of 1 to 3;
m, n each independently signify 0 or 1;
ring C signifies phenylene which is unsubstituted or optionally substituted with
fluorine, chlorine, cyano, alkyl or alkoxy, or pyrimidine-2,5-diyl, pyridine-2,5-diyl, 2,5-thiophenylene, 2,5-furanylene, 1,4- or 2,6-naphthylene;
Z signifies -O- or -NR5-, in which R5 signifies hydrogen or lower alkyl, or
a second group of formula D, in which
D signifies a straight-chain or branched alkylene group with 1 to 20 carbon
atoms which is optionally substituted with fluorine or chlorine, a
cycloalkyl residue with 3 to 8 ring atoms which is optionally substituted
with fluorine, chlorine alkyl or alkoxy.
These cross-linkable, photoactive polymer materials with 3-arylacrylic acid esters and amides may be used as orienting'layers'for liquid "Crystals and for the .production of ndh-structured arid structured optical elements and multi-layer systems.
EP-A-0860455 (Rolic AG) discloses polymers of the general formula I:



wherein: Ml, Ml
M2
w, w1, w2

denote a recurring monomer unit from the group:
acrylate, methacrylate, 2-chloroacrylate, 2-phenylacrylate; optionally by lower alkyl N-substituted acrylamide, methacrylamide, 2-chloroacrylamide and 2-phenylacrylamide; vinyl ethers, vinyl esters, styrene derivatives, siloxanes;
denotes a recurring monomer unit from the group:
acrylate, methacrylate, 2-chloroacrylate, 2-phenylacrylate, optionally by lower alkyl N-substituted acrylamide, methacrylamide, 2-chloroacrylamide and 2-phenylacrylamide; vinyl ether, vinyl ester; straight-chain or branched alkyl esters of acrylic or methacrylic acid, allyl esters of acrylic or methacrylic acid, alkyl vinyl ethers or ester, phenoxyalkyl acrylates or phenoxyalkyl methacrylates or hydroxyalkyl acrylates or hydroxyalkyl methacrylates, phenylalkyl acrylates or phenylalkyl methacrylates, in which the alkyl groups have 1 to 20, preferably 5 to 20, but in particular 5 to 18 carbon atoms; acrylonitrile, methacrylonitrile, styrene, 4-methylstyrene or siloxanes;
arc molar fractions of the comonomers with 0
7

S1,.S1 independently of one another a spacer unit, such as an optionally
monosubstituted or polysubstituted by fluorine, chlorine or cyano
straight-chain or branched alkylene group -(CH2)r. or a chain of
formula -(CH2)r-L-(CH2)s in which L denotes a single bond or a
linking functional group such as -0-, -COO-, -OOC-, -NR1-,
-NR1CO-, -CO-NR1-, -NRl-COO-, -OCO-NR1-,
-NR1-CO-NR1-, -CH=CH-, -C=C-;
in which Rl denotes hydrogen or lower alkyl and r and s each represent an integer from 1 to 20, with the proviso that r + s ≤ 24;
D' independently of one another -O- or -NR2_; in which R2 denotes
hydrogen or lower alkyl;
X', Y, Y' independently of one another denote hydrogen, fluorine, chlorine, cyano, alkyl with 1 to 12 carbon atoms which is optionally substituted with fluorine and in which optionally one CH2 group or a plurality of non-neighbouring CH2 groups may be replaced by 0, -COO-, -OOC-, and/or -CH=CH-;
A' independently of one another denote phenylene, pyridine-2,5-diyl,
pyrimidine-2,5-diyI, l,3-dioxane-2,5-diyl, cyclohexane-l,4-diyl, piperidine-l,4-diyl, piperazine-l,4-diyl which is unsubstituted or optionally substituted with fluorine, chlorine, cyano, alkyl, alkoxy or fluoroalkoxy;
B' independently of one another denote phenylene, pyridine-2,5-diyl,
pyrimidine-2,5-diyl, 1,4- or 2,6-naphthylene, l,3-dioxane-2,5-diyl, cyclohexane-l,4-diyl which is unsubstituted or optionally substituted with fluorine, chlorine, cyano, alkyl, alkoxy or fluoroalkoxy;
C independently of one another denote phenylene, or
pyrimidine-2,5-diyl, pyridine-2,5-diyl, 2,5-thiophenylene,


2,5-furanyIene, 1,4- or 2,6-naphthylene which is unsubstituted or optionally substituted with fluorine, chlorine, cyano, alkyl, alkoxy or fluoroalkoxy;
K, K' independently of one another denote hydrogen, fluorine, chlorine,
cyano, nitro or a straight-chain or branched alkyl-, alkoxy-
alkyl-COO-, alkyl-CO-NR3 or alkyl-OCO-group with 1 to 20 carbon atoms optionally substituted with fluorine, chlorine, cyano or nitro in which optionally a CH2 group or a plurality of non-neighbouring CH2 groups may be replaced by -0-, -CH=CH- or -C=C- and in which R3 hydrogen or lower alkyl;
with the proviso that at least one of the rings A, B, C and/or at least one of the rings A', B", C represents a phenylene group, which is substituted with at least one alkoxy group or fluoroalkoxy group, in which, if K denotes alkoxy or fluoroalkoxy, at least one of the rings A, B, C and/or at least one of the rings A', B', C represents a phenylene group, which is substituted with at least one further alkoxy group or fluoroalkoxy group;
Z, Z', Z'.Z1' independently of one another denote a single covalent bond,
-(CH2)t-, -0-, -CO-, -CO-0-, -0-OC-, -NR4-, -CO-NR4-,
-R4N-CO-, -(CH2)u-0-, -0-(CH2)ir, -(CH2)U-NR4- or
-NR4-(CH2)u;
in which R4 denotes hydrogen or lower alkyl,
t denotes an integer from 1 to 4;
u denotes an integer from 1 to 3; and
p, p', n, n' independently of one another denotes 0 or 1.


These crosslinkablc photoactive polymers may be used as orientation layers for liquid crystals and for the production of unstructured or structured optical elements and. multilayer systems'.'
The present invention provides optically active or inactive photoactive polymers of the general formula 1:

in which:
P is a photoactive group which can photoisomerise and/or photo-
dimerise;
B represents an aromatic or alicyclic group which is unsubstituted or
substituted by fluorine, chlorine or cyano, or by a cyclic, straight-chain or branched alkyl residue which is unsubstituted, mono-substituted by cyano or halogeno, or poly-substituted by halogeno, having 1 to 18 carbon atoms and wherein one or more CH2 groups may independently be replaced by -0-, -CO-, -CO-O-, -O-CO-, -Si(CH3)2-0-Si(CH3)2-, -NR2-, -NR2-CO-, -CO-NR2-, -NR2-CO-0-, -OCO-NR2-, -NR2-CO-NR2-, -CH=CH-, -OC-, -O-CO-O-, with the proviso that oxygen atoms are not directly attached to each other, and wherein R2 represents a hydrogen atom or lower alkyl, or B further represents a nitrogen atom or -CR2-;
A, C, D each independently of the other represents an aromatic or alicyclic
group which is unsubstituted or substituted by fluorine, chlorine, cyano, or by a cyclic, straight-chain or branched alkyl residue which is unsubstituted, mono-substituted by cyano or halogeno. or poly-substituted by halogeno, having 1 to 18 carbon atoms and


wherein one or more CH2 groups may independently be replaced
by -0-, -CO-, -CO-O-, -O-CO-, -Si(CH3)2-0-Si(CH3)2-, -NR2-,
-NR2-CO-, -CO-NR2-, -NR2-CO-0-, -O-CO-KR2-,
-NR2-CO-NR2-, -CH=CH-, -OC-, -O-CO-O-, with the proviso that oxygen atoms are not directly attached to each other, and wherein R2 represents a hydrogen atom or lower alkyl;
M represents a repeating monomer unit in a homo- or copolymer;
S1, S2, S3, S4, S5 represent a single covalent bond or a spacer unit, such as a straight-chain or branched alkylene residue which is unsubstituted, mono-substituted by cyano or halogeno, or poly-substituted by halogeno, having 1 to 24 carbon atoms, wherein one or more CH2 groups may independently be replaced by -0-, -CO-, -CO-0-, -O-CO-, -Si(CH3)2-0-Si(CH3)2-, -NR2-, -NR2-CO-, -CO-NR2-, -NR2-CO-0-, -O-CO-NR2-, -NR2-CO-NR2-, -CH-CH-, -C^C-, -O-CO-O-, with the proviso that oxygen atoms are not directly attached to each other, and wherein R2 represents a hydrogen atom or lower alkyl;
nl, n2 are each independently a positive integer up to 2 with the proviso
that n1 + n2 ≤ 2;
R1 is a hydrogen atom, or a straight-chain or branched alkyl residue.
which is unsubstituted, mono-substituted by cyano or halogeno, or poly-substituted by halogeno, having 1 to 18 carbon atoms, wherein one or more CH2 groups may independently be replaced
by -0-, -CO-, -CO-0-, -O-CO-, -Si(CH3)2-0-Si(CH3)2-, -NR2-,
5 -NR2-CO-, -CO-NR2-, -NR2-CO-0-5 -O-CO-NR2-,
-NR2-CO-NR2-, _CH=CH-, -OC-, -O-CO-O-, with the proviso that oxygen atoms are not directly attached to each other, and wherein R2 represents a hydrogen atom or lower alkyl.


The invention also provides the use of the polymers of the general formula I as orientation layers for liquid crystals and in the construction of unstructured and structured optical elements and multi-layer systems.
The new photoreactive materials show excellent alignment and induce very high pretilt angles in the liquid crystal layer in LCDs.
Surprisingly these materials can easily be coated with LCP-prepolymers without wetting problems. For example, in a liquid crystal cell the pretilt angle of the optical axis in an LCP-layer is very high. Tilt domains which are sometimes observed in tilted LCP-layers do not show up.
Preferred photoactive groups P are groups which undergo a photocyclisation and have the general formula II and HI:

wherein the broken line indicates the point of linkage to S1 and wherein:
E represents phenylene which is unsubstituted or substituted by fluorine,
chlorine or cyano, or by a cyclic, straight-chain or branched alkyl residue which is unsubstituted, mono-substituted by cyano or halogeno, or poly-substituted by halogeno, having 1 to 18 carbon atoms and wherein one or more CH2 groups may independently be replaced by -O-, -CO-, -CO-O-, -O-CO-, -Si(CH3)2-0-Si(CH3)2-, -NR2-; -NR2-CO-, -CO-NR2-, -NR2-CO-0-, -O-CO-NR2-, -NR2-CO-NR2-, -CH=CH- -G=C-, -O-CO-O-, with the proviso that oxygen atoms are not directly attached 10 each other, and wherein R2 represents a hydrogen atom or lower alkyl, or E further represents


pyiimidine-2,5-diyl, pyridine-2,5-diyl) 2,5-thiophenylene,
2,5-furanylene, or 1,4- or 2,6-naphthylene;
F represents -OR4, -NR5R6, or an oxygen atom linked to ring E in the
ortho position to form a coumarin unit wherein R , R5 and R are a hydrogen atom or a cyclic, straight-chain or branched alkyl residue which is unsubstituted, mono-substituted by halogeno, or poly--substituted by halogeno, having 1 to 18 carbon atoms and wherein one or more CH2 groups may independently be replaced by -0-, -CO-, -CO-O-, -O-CO-, -CH=CH-, with the proviso mat oxygen atoms are not directly attached to each other, or R5 and R6 are linked together to form an alicyclic ring with 5 to 8 atoms;
X, Y each independently of the other represents hydrogen, fluorine, chlorine,
cyano, alkyl optionally substituted by fluorine having from 1 to 12 carbon atoms in which optionally one or more non-adjacent CH2 groups are replaced by -0-, -CO-O-, -O-CO- and/or -CH=CH-;
R3 is a hydrogen atom, or a straight-chain or branched alkyl residue which
is unsubstituted, mono-substituted by cyano or halogeno, or poly--substituted by halogeno, having 1 to 18 carbon atoms, wherein one or more CH2 groups may independently be replaced by -0-, -CO-,
-C0-0-, -O-CO-, -Si(CH3)2-0-Si(CH3)2-, -NR2-, -NR2-CO-, -CO-NR2-, -NR2-CO-0-, -O-CO-NR2-, -NR2-CO-NR2-, -CH=CH-, -C=C-5 -O-CO-O-, with the proviso that oxygen atoms are not directly attached to each other, and wherein R2 represents a hydrogen atom or lower alkyl.


Special preferred photoactive groups P have the general formula IV and V:

wherein the broken line indicates the point of linkage to S1 and wherein R3 has the
meaning given under formula II and III;
F represents -OR4 or -NR5R6, wherein R and R5 are a cyclic, straight-
chain or branched alkyl residue which unsubstituted, mono-substituted by halogeno, or poly-substituted by halogeno, having 1 to 18 carbon atoms and wherein one or more CH2 groups may independently be replaced by -0- or-CH=CH-, with the proviso that oxygen atoms are not directly attached to each other, and wherein R6 is a hydrogen atom or a cyclic, straight-chain or branched alkyl residue which is unsubstituted, mono-substituted by halogeno, or poly-substituted by halogeno, having 1 to 18 carbon atoms and wherein one or more CH2 groups may independently be replaced by -O- or-CH=CH-, with the proviso that oxygen atoms are not directly attached to each other, or R5 and R6 link together to form an alicyclic ring with 5 to 8 atoms; and
E represents phenylene which is unsubstituted or substituted by a cyclic,
straight-chain or branched alkyl residue which is unsubstituted, mono-substituted by halogeno, or poly-substituted by halogeno, having 1 to 12 carbon atoms and wherein one or more CH2 groups may independently be replaced by -0-, -CO-, -C0-0-, -0-CO, -CH=CH-, -C=C-, with the proviso that oxygen atoms are not directly attached to each other, or E further represents pyrimidine-2,5-diyl, pyridine-2,5-diyJ, 2,5-thiophenylene, 2,5-furanylene, 1,4- or 2,6-naphthylene.
Especially preferred photoactive P groups have the general formula IV wherein:


E represents phenylene which is unsubstituted or substituted by a
straight-chain or branched alkyl residue which is unsubstituted or mono- or polysubstituted by fluorine, having 1 to 6 carbon atoms and wherein one or more CH2 groups may independently be replaced by -0-, -CO-, -CO-O-, -O-CO, -CH=CH-, with the proviso that oxygen atoms are not directly attached to each other, or E further represents pyrimidine-2,5-diyl, pyridine-2,5-diyl, 2,5-furanylene, 1,4- or 2,6-naphthylene;
F represents -OR4 or -NHR5, wherein R4 and R5 are a cyclic,
straight-chain or branched alkyl residue which is unsubstituted or mono- or polysubstituted by fluorine, having 1 to 18 carbon atoms and wherein one or more CH2 groups may independently be replaced by -0-, with the proviso that oxygen atoms are not directly attached to each other.
The preferred polymers of formula I can be further divided into:
a) polymers of formula I in which B represents a aromatic or alicyclic group and where n1 + n2= 1;
b) polymers of formula I in which B represents a aromatic or alicyclic group and where n1 +n2 = 0;
c) polymers of formula I in which B represents a group -CR2- and where 0 d) optically inactive polymers of formula I.
Preferred groups B are aromatic which are unsubstituted or substituted by fluorine, chlorine or cyano, or by a cyclic, straight-chain or branched alkyl residue which is unsubstituted, mono-substiiuted by cyano or halogeno, or poly-substituted by halogeno, having 1 10 18 carbon atoms and wherein one or more CH2 groups may independently be replaced by -O-. -CO-. -CO-O-, -O-C0-, -CH=CH-, with the proviso that oxygen atoms are not directly attached to each other, or B further represents -CR'-. wherein R2 texcaants hydrogen atom or lower alkyl.

Especially preferred groups B are 1,2,5-benzenetriyl and 1,3,5-benzenetriyl groups which are unsubstituted or substituted by fluorine and where the spacer group S5 is in position 1.
Preferred groups A, C and D are phenylene which is unsubstituted or substituted by fluorine, chlorine, cyano, or by a cyclic, straight-chain or branched alkyl residue which is unsubstituted, mono-substituted by cyano or halogeno, or poly-substituted by halogeno, having 1 to 12 carbon atoms, wherein one or more CH2 groups may independently be replaced by -0-, -CO-, -CO-O-, -O-CO-, -CH=CH-, -C=C- or -O-CO-O- with the proviso that oxygen atoms are not directly attached to each other, or A, C and D further represents cyclohexane-l,4-diyl, pyrimidine-2,5-diyl. pyridine-2,5-diyl, 1,4- or 2,6-naphthylene.
Especially preferred groups A, C and D are phenylene, which is unsubstituted or substituted by fluorine, straight-chain or branched alkyl residue which is unsubstituted or mono- or polysubstituted by fluorine, having 1 to 8 carbon atoms, wherein one or more CH2 groups may independently be replaced by -0-, -CO-, -CO-O-, -O-CO- or -CH=CH- with the proviso that oxygen atoms are not directly attached to each other, or A, C and D further represents cyclohexane-l,4-diyl, pyrimidme-2,5-diyl, pyridine-2,5-diyl or 2,6-naphthylene.
Preferred "spacer units" S1, S2, S3, S4 and S5 in the context of the present invention represent a single covalent bond or a spacer unit, such as a straight-chain or branched alkylene grouping represented by -(CH2)r-, optionally mono- or poly-substituted by fluorine, chlorine or cyano, or a chain of the formula -L1-(CH2)r-L2- or -L1-(CH2)r-L2-(CH2)s-L3-, wherein L1, L2 and L3 each independently of the others represent a single bond or linking functional groups such as -0-, -CO-O-, -O-CO-, -NR2-, -NR2-CO-, -CO-NR2-, -NR2-CO-0-, -O-CO-NR2-, -NR2-CO-NR2-, -CH=CH-, -OC-, -O-CO-O-, -Si(CH3)2-0-Si(CH3)2-, wherein R2 represents hydrogen atom or lower alkyl and r and s are each an integer from 1 to 20, with the

proviso that r + s ≤ 24 and with the proviso that in the case where the repeating monomer unit M is linked to S5 via a nitrogen atom or a oxygen atom which is by definition part of M, as for example in acrylate, methacrylale, 2-chloroacrylate, 2-phenylacrylate, optionally N-ower alkyl substituted acrylamide, methacrylamide, 2-chloroacrylamide, 2-phenylacrylamide; or a vinyl ether, vinyl ester, maleic acid derivative or fumaric acid derivative; L1 signifies a single bond.
Especially preferred "spacer units" S1, S2, S3, S4 and S5 in the context of the present
invention are a straight-chain or branched alkylene grouping, represented by -(CH2)r»
and also -(CH2)rO-, -(CH2)rCO-, -(CH2)r-CO-0-, -(CH2)rO-CO-,
-(CH2)r-CO-NR2-, -(CH2)r-NR2-CO-, -(CH2)rNR2-, -0-(CH2)r, -CO-0-(CH2)r,
-0-CO-(CH2)r-, -NR2-CO-(CH2)r, -CO-NR2-(CH2)r, -NR2-(CH2)r,
-0-(CH2)r-CO-0-, -0-(CH2)rO-CO-, -0-(CH2)r-CO-NR2-, -0-(CH2)rNR2-:
-0-(CH2)r-0-, -0-(CH2)rNR2-CO-, -NR2-(CH2)rCO-0-, -NR2-(CB2)r-0-,
-NR2-(CH2)rNR2-, -NR2-(CH2)rO-CO-5 -CO-NR2-(CH2)rO-,
-CO-Ml2.(CH2)r-lSrR.2-, -CO-NR2-(CH2)rO-CO-, -0-CO-(CH2)r-CO-,
-0-C0-(CH2)r-O-, -0-CO-(CH2)rNR2-, -0-CO-(CH2)rCO-O-,
-0-CO-(CH2)rCO-NR2-, -0-CO-(CH2)r-NR2-CO-, -(CH2)rO-(CH2)5-,
-(CH2)r-CO-0-(CH2)5-, -(CH2)r-0-CO-(CH2)5s-, -(CH2)rNR2-CO-(CH2)s5
KCH2)r-NR2-CO-0-(CH2)5, -(CH2)rO-(CH2)5-0-, -(CH2)r-CO-0-(CH2)5-0-,
-(CH2)rO-CO-(CH2)s-0-, -(CH2)r-KR2-CO-(CH2)5-0-,
-(CH2)r-NR2-CO-0-(CH2)5-0-, -0-(CH2)r-0-(CH2)5-, -0-(CH2)rCO-0-(CH2)5-,
-0-(CH2)r-NR2-CO-(CH2)5 -0-(CH2)rNR2-CO-0-(CH2)5-,
-0-(CH2)rCO-0-(CH2)5-0-, -0-(CH2)r-0-(CH2)5-0-,
-0-(CH2)r-NR2-CO-(CH2)5s-0-, -0-(CH2)rNR2-CO-0-(CH2)5-0-,
-CO-0~(CH2)rO
Most preferred "spacer units" S1, S2, S3, S4 and S5 are a straight-chain alkylene
grouping represented by -(CH2)r, and also -(CH2)r-0-, -(CH2)r-CO-0-,
-(CH2)rO-CO-, -(CH2)r-CO-NH-, -(CH2)rNH-CO-, -0-(CH2)r, -CO-0-(CH2)r,
-CO-NB-(CH2)r-, -0-CO-(CH2)r. -0-CO-(CH2)rCO-0-, -0-(CH2)r-0-CO-,
. -0-(CH2)r-CO-NH-, -0-(CH2)rNH-CO-, -CO-0-(CH2)rO-, -CO-NH-(CH2)r-0-,
-0-(CH2)rO-, -(CH2)r-NH-CO-(CH2)5, -(CH2)rNH-CO-0-(CH2)5-,
-(CH2)r-0-(CH2)5-0-, -(CH2)r-NH-CO-(CH2)5-0-, -(CH2)r-MH-CO-0-(CH2)5-0-,
-0-(CH2)rNH-CO-(CH2)5-, -0-(CH2)rO-(CH2)5-0-, -0-CO-(CH2)rO-(CH2)5-0-,
-CO-0-(CH2)r-0-(CH2)5-0-, -0-(CH2)rNH-CO-(CH2)5-O-,
-0"CO-(CH2)r-NH-CO-(CH2)5-0-, wherein r and s are each an integer from 2 to 12 and the sum of r + s ≤ 15.
Examples of preferred "spacer units" S1, S2, S3, S4 and S5 are 1,2-ethylene.
1,3-propylene, 1,4-butylene, 1,5-pentylene, 1,6-hexylene, 1,7-heptylene, 1,8-octylene,
1,9-nonylene, 1,10-decyIene, 1.11-undecylene, 1,12-dodecylene, 3-methyl-
-1,4-butylene, 3-propyleneoxy, 3-propyleneoxycarbonyl, 2-ethylenecarbonyloxy,
4-butyleneoxy, 4-butyleneoxycarbonyl, 3-propylenecarbonyloxy, 5-pentyleneoxy,
5-pentyleneoxycarbonyl, 4-butylenecarbonyloxy, 6-hexyleneoxy, 6-hexyleneoxyc-
arbonyl, 5-pentylenecarbonyloxy, 7-heptyleneoxy, 7-heptyleneoxycarbonyl,
6-hexylenecarbonyloxy, 8-octyleneoxy, 8-octyleneoxycarbonyl, 7-heptylenecarbonyl-
oxy, 9-nonyleneoxy, 9-nonyleneoxycarbonyl, 8-octyIenecarbonyloxy, 10-decylene-
oxy, 10-decyleneoxycarbonyl, 9-nonylenecarbonyloxy, 11-undecyleneoxy,
11-undecyleneoxycarbonyl, 10-decylenecarbonyloxy, 12-dodecyleneoxy,
12-dodecyleneoxycarbonyl, 11-undecylenecarbonyloxy, 3-propylenehninocarbonyl, 4-butyleneiminocarbonyl, 5-pentyleneiminocarbonyl, 6-hexyleneiniinocarbonyl, 7-heptyleneiminocarbonyl, 8-octyleneiminocarbonyl, 9-nonyleneiminocarbonyl, 10-decyleneiminocarbonyl, 11-undecyleneiminocarbonyl, 12-dodecyleneimino-carbonyl, 2-etlylenecarbonylimino, 3-propylenecarbonylimino, 4-butylenecarbonyl-irnino, 5-pentylenecarbonyliminc, 6-hexylenecarbonyltmino. 7-heptylenecarbony!-;) imino, 8-octylenecarbonylimmo. 9-nonylcnccarbonylimino. 10-decylcnecarbonyl-imino, 11-undecylenecarbonylimino. 6-(3-propy1enbiniaocart>otiyioxy)bexylenc,


6-(3-propyl eneoxy)hexylene, 6-(3-propyleneoxy)hexyleneoxy, 6-(3-propyleneimino-carbonyloxy)hexyleneoxy, 6-(3-propyleneiminocarbonyl)hexyl, 6-(3-propyleneimino-carbonyl)hexyloxy, 1,2-ethylenedioxy, 1,3-propylenedioxy, 1,4-butylenedioxy, 1,5-pentylenedioxy, 1,6-hexylenedioxy, 1,7-heptylenedioxy, 1,8-octylenedioxy, 1,9-nonylenedioxy, 1,10-decylenedioxy, 1,11-undecylenedioxy, 1,12-dodecylene-dioxy and the like.
Preferred groups R1 are a hydrogen atom, or a straight-chain or branched alkyl residue which is unsubstituted or halogeno or polyhalogeno-substituted, having 1 to 12 carbon atoms, wherein one or more CH2 groups may independently be replaced by -0-, -CO-, -CO-O-, -O-CO-, -CH=CH- or -C=C-, with the proviso that oxygen atoms are not directly attached to each other.
Especially preferred groups R1 are straight-chain or branched alkyl residue, having 1 to 8 carbon atoms, wherein one or more CH2 groups are each independently replaced by -0-, -CO-, -CO-O- or -O-CO- or -CH=CH-, with the proviso that oxygen atoms are not directly attached to each other. For example, methyl, ethyl, propyl, butyl, isobutyl, pentyl, hexyl, octyl, allyl, but-3-en-l-yl, pent-4-en-l-yl, hex-5-en-l-yl, methoxy, ethoxy, propoxy, butoxy, pentyloxy, hexyloxy, heptyloxy, octyloxy, 3-methylpentyloxy, but-3-enyloxy, pent-4-enyloxy and the like.
Preferred repeating monomer units M are acrylate, methacrylate, 2-chloroacrylate, 2-phenylacrylate, optionally N-lower alkyl substituted acrylamide, methacrylamide, 2-chloroacrylamide, 2-phenylacrylamide, vinyl ether, vinyl ester, styrene derivatives, siloxanes, imides, amic acids and their esters, amidimides, maleic acid derivatives, fumaric acid derivatives.
Especially preferred repeating monomer unit M are acrylate, methacrylate, optionally AMower-alkyl-substituted acrylamide, methacrylamide, vinyl ether, vinyl ester, styrene derivatives, imides, amic acids and there esters, amidimides.

Most preferred repealing monomer units M are acrylate, methacrylate, styrene derivatives, imides, amic acids and their esters, and amidimides.
Preferred imide units M from which the main chains of the side-chain polymers according to the invention are generally synthesised are groups of the general formulae III, V and VII and/or the analogous amic acid groups and amic acid ester groups of the general formulae IV, VI and VIII:




in which the broken line symbolises the linkage to S5 and wherein:

Tl
T2, T3

represents the tetravalent organic radical of a tetracarboxylic acid dianhydride after formal removal of the two -CO-O-CO- groups, the four valencies of which are distributed between four different carbon atoms of the radical;
each independently of the other represents an aromatic or alicyclic trivalent group, the three valencies of which are distributed between three different carbon atoms of the group, the group being unsubstituted or substituted by fluorine, chlorine, cyano, by a cyclic, straight-chain or branched alkyl residue which is unsubstituted, mono-substituted by halogeno, or poly-substituted by halogeno, having 1 to 18 carbon atoms and wherein one or more CH2 groups may independently be replaced by -0-, -CO-, -CO-O-, -O-CO-, -CH=CH-, -OC-, with the proviso that oxygen atoms are not directly attached to each other,



S6, S7, S8, S9, S10 represent a single covalent bond or a spacer unit, such a straight-chain or branched alkylene residue which is unsubstituted, mono-substituted by cyano or halogeno, or poly-substituted by halogeno, having 1 to 24 carbon atoms, wherein one or more CH2 groups may independently be replaced by -0-, -CO-, -CO-O-, -O-CO-, -Si(CH3)2-0-Si(CH3)2-, -NR2-, -NR2-CO-, -CO-NR2-, -NR2-CO-0-, -O-CO-NR2-, -NR2-CO-NR2-, -CH-CH-, -C=C-, -O-CO-O-, with the proviso that oxygen atoms are not directly attached to each other, and wherein R2 represents hydrogen atom or lower alkyl;
J represents an aromatic or alicyclic divalent, trivalent or tetravalent
group, the valencies of which are distributed between different atoms of the group, which is unsubstituted or substituted by fluorine, chlorine, cyano, by a cyclic, straight-chain or branched alkyl residue which is unsubstituted or mono cyano, or halogeno or polyhalogeno-substituted, having 1 to 18 carbon atoms and wherein one or more CH2 groups may independently be replaced by -0-, -CO-, -CO-0-, -O-CO-, -CH=CH-, -C-C-, with the proviso that oxygen atoms are not directly attached to each other, or J further represents a nitrogen atom or -CR2- and wherein R2 represents a hydrogen atom or lower alkyl;
K represents the radical of an aliphatic, alicyclic or aromatic diamine
after formal removal of the two amino groups; and
G represents hydrogen atom or a monovalent organic group, derived
from an alcohol after formal removal of the hydroxy group.
The tetracarboxylic acid dianhydride on which the tetravalent organic radical T1 is based may be aliphatic, alicyclic or aromatic.
Preferred examples of aliphatic or alicyclic tetracarboxylic acid anhydrides are: — butanetctracarboxylic acid dianhydride;


— ethylenemaleic acid dianhydnde;
— 1,2,3,4-cyclobutanetetracarboxylic acid dianhydnde;
— 1,2,3,4-cyclopentanetetracarboxylic acid dianhydnde;
— 2,3,5-tricarboxycyclopentylacetic acid dianhydnde;
— 3,5,6-tricarboxynorbomylacetic acid dianhydnde;
— 2,3,4,5-tetrahydrofurantetracarboxyIic acid dianhydride;
— 4-(2,5-dioxotetrahydrofuran-3-yl)tetrahydronaphthalene-l,2-dicarboxylic acid dianhydride;
— 5-(2,5-dioxotetrahydrofuran-3-yl)-3-methyl-3-cyclohexene-1.2-dicarboxylic acid dianhydride;
— bicyclo[2.2.2]oct-7-ene-2,3,5,6-tetracarboxylic acid dianhydride;
— bicyclo[2.2.2]octane-2,3,5,6-tetracarboxylic acid dianhydride; and
— l,8-dimethylbicyclo[2.2.2]oct-7-ene-2,3,5,6-tetracarboxylic acid dianhydride.
Examples of preferred aromatic tetracarboxylic acid dianhydrides are:
■— pyromellitic acid dianhydride;
— 3,3',4,4'-benzophenonetetracarboxylic acid dianhydride;
— 4,4'-oxydiphthalic acid dianhydride;
— 3,3',4,4'-diphenylsulfonetetracarboxylic acid dianhydride;
— 1,4,5,8-naphthalenetetracarboxylic acid dianhydride;
— 2,3,6,7-naphthalenetetracarboxylic acid dianhydride;
— 3,3',4,4'-dimethyldiphenylsilanetetracarboxylic acid dianhydride;
— 3,3',4,4'-tetraphenylsilanetetracarboxylic acid dianhydride;
— 1,2,3,4-furantetracarboxylic acid dianhydride;
— 4,4'-bis(3,4-dicarboxyphenoxy)diphenyl sulfide dianhydride;
— 4,4'-bis(3,4-dicarboxyphenoxy)diphenyl sulfone dianhydride;
— 4,4'-bis(3,4-dicarboxyphenoxy)diphenylpropane dianhydride;
— 3,3',4,4'-biphenyltetracarboxylic acid dianhydride;
— ethylene glycol bis(trimellitic acid) dianhydride;
— 4,4'-( 1,4-phenylene)bis(phthalic acid) dianhydride;
— 4,4'-(l,3-phenylene)bis(phthalic acid) dianhydride;
— 4,4'-(hexafluoroisopropylidcnc)diphthalic acid dianhydnde;

— 4,4'-oxydi(l,4-phenylene)bis(phthalic acid) dianhydride; and
— 4,4'-methylenedi(l,4-phenylene)bis(phthalic acid) dianhydride.
Especially preferred are:
— 1,2,3,4-cyclobutanetetracarboxylic acid dianhydride;
— 1,2,3,4-cyclopentanetetracarboxylic acid dianhydride;
— 2,3,5-tricarboxycyclopentylacetic acid dianhydride;
— 5-(2,5-dioxotetrahydrofuran-3-yl)-3-methyI-3-cyclohexene-l,2-dicarboxylic acid dianliydride;
— 4-(2,5-dioxotetrahydrofuran-3-yl)tetrahydronaphthalene-l,2-dicarboxylic acid dianhydride;
— 4,4'-(hexafluoroisopropylidene)diphthalic acid dianhydride; and
— bicyclo[2.2.2]oct-7-ene-2,3,5,6-tetracarboxylic acid dianhydride.
The groups T2 and T3 can be derived from aliphatic, alicyclic or aromatic dicarboxylic acid anhydrides.
Preferred groups T2 and T3 are trivalent aromatic or carbocyclic groups, the three valencies of which are so distributed between three different carbon atoms that two of those valencies are located at adjacent carbon atoms.
Especially preferred groups T2 and T3 are trivalent benzene derivatives, the three valencies of which are so distributed between three different carbon atoms that two of those valencies are in the ortho position relative to one another.
Preferred "spacer units" S6 in the context of the present invention are a straight-chain or branched alkylene grouping, represented by -(CH2)r-, and also -(CH2)r-0-, -(CH2VCO-, -(CH2)r-CO-0-, -(CH2)r-0-CO-, -(CH2)rCO-NR2-, -(CH2)r-NR2-CO-, -(CH2)rNR2-, -(CH2)r-CKCH2)s-, -(CH2)rCO-0-(CH2)s-, -(CH2)r-0-CO-(CH2)s-, -(CH2)r-NR2-CO-(CH2)s-, -(CH2)r-NR2-CO-0-(CH2)s-, -(CH2)rO-(CH2)s-0-, -
-CH2)rNR2-CO-0-(CH2)s-0-,-(CH2)rO-(CH2)s-CO-0-,-(CH2)r-0-(CH2)s-0-CO-, wherein r and s are each an integer from 1 to 20, but especially from 2 to 12, with the proviso that r + s Examples of preferred "spacer units" S6 are 1,2-ethylene, 1,3-propylene, 1,4-butylene, 1,5-pentylene, 1,6-hexylene, 1,7-heptylene, 1,8-octylene, 1,9-nonylene, 1,10-decylene, 1,11-undecylene, 1,12-dodecylene, 3-methyl-1,4-butylene, 3-propyleneoxy, 3-propyleneoxycarbonyl, 2-ethylenecarbonyloxy, 4-butyleneoxy,
4-butyleneoxycarbonyl, 3-propylenecarbonyloxy, 5-pentyleneoxy,
5-pentyleneoxycarbonyl, 4-butylenecarbonyloxy, 6-hexyleneoxy,
6-hexyleneoxycarbonyl, 5-pentylenecarbonyloxy, 7-heptyleneoxj', 7-heptyleneoxy-
carbonyl, 6-hexylenecarbonyloxy, 8-octyleneoxy, 8-octyleneoxycarbonyl,
7-heptylenecarbonyloxy, 9-nonyleneoxy, 9-nonyleneoxycarbonyl, 8-octylene-
cafbonyloxy, 10-decyleneoxy, 10-decyleneoxycarbonyl, 9-nonylenecarbonyloxy,
11 -undecyleneoxy, 11 -undecyleneoxycarbonyl, 10-decylenecarbonyloxy,
12-dodecyleneoxy, 12-dodecyleneoxycarbonyl, 11-undecylenecarbonyloxy,
3-propyleneiminocarbonyl, 4-butyleneiminocarbonyl, 5-pentyleneiminocarbonyl, 6-hexyleneiminocarbonyl, 7-heptyleneiminocarbonyl, 8-octyleneiminocarbonyl,
9-nonyleneiminocarbonyl, 10-decyleneiminocarbonyl, 11-undecyleneiminocarbonyl,
12-dodecyleneiminocarbonyl, 2-ethylenecarbonylimino, 3-propylenecarbonylimino,
4-butylenecarbonylimino, 5-pentylenecarbonylimino, 6-hexylenecarbonylimino,
7-heptylenecarbonylimino, 8-octylenecarbonylimino, 9-nonylenecarbonylimino,
10-decylenecarbonylimino, 11-undecylenecarbonylimino, 6-(3-propyleneimino-
carbonyloxy)hexylene, 6-(3-propyleneoxy)hexylene, 6-(3-propyleneoxy)hexyleneoxy,
6-(3-propyleneiminocarbonyloxy)hexyleneoxy5 6-(3-propyleneiminocarbonyl)-
hexylene, 6-(3-propyleneiminocarbonyl)hexyleneoxy and the like.
Preferred "spacer units" S7 and S10 in the context of the present invention are a straight-chain or branched alkylene grouping, represented by -(CH2)r-, and also -0-(CH2)r. -CO(CH2)r, -CO-0-(CH2)r, -0-CO-(CH2)r, -NR2-CO-(CH2)r,

-NR2-(CH2)r, -CO-NR2-(CH2)r, -NR2-CCKCH2)r-, -0-(CH2)rO-(CH2)s-,
-(CH2)r-CO-0-(CH2)s-, -(CH2)r-0-CO-(CH2)s-, -(CH2)r-NR2-CO-(CH2)s-,
-(CH2)r-NR2-CO-0-(CH2)s-, -0-(CH2)rO-(CH2)s-, -0-(CH2)rCO-O-(CH2)s-,
-0-(CH2)r-0-CO-(CH2)5-, -0-(CH2)rNR2-CO-(CH2)s-,
-0-(CH2)rNR2-CO-0-(CH2)5-,-0-CO-(CH2)r(HCH2)s-,-CO-0-(CH2)rO-(CH2)s-, wherein r and s are each an integer from 1 to 20, but especially from 2 to 12, with the proviso that r + s Examples of preferred "spacer units" S7 and S10 are 1,2-ethylene, 1,3-propylene,
1,4-butylene, 1,5-pentylene, 1,6-hexylene, 1,7-heptylene, 1,8-octylene, 1,9-nonylene,
1,10-decylene, 1,11-undecylene, 1,12-dodecylene, 3-methyl-1,4-butylene, 2-oxy-
ethylene, 3-oxypropylene, 4-oxybutylene, 5-oxypentylene, 6-oxyhexylene, 7-oxy-
heptylene, 8-oxyoctylene, 9-oxynonylene, 10-oxydecylene, ll-oxyundecylene,
12-oxydodecylene, 2-(oxycarbonyl)ethylene, 3-(oxycarbonyl)piopylene, 4-(oxy-
carbonyl)butylene, 5-(oxycarbonyl)pentylene, 6-(oxycarbonyl)hexylene,
7-(oxycarbonyl)heptylene, 8-(oxycarbonyl)octylene, 9-(oxycarbonyl)nonylene,
10-(oxycarbonyl)decylene, ll-(oxycarbonyl)undecylene, 12-(oxy-
carbonyl)dodecylene, 2-(carbonyloxy)ethylene, 3-(carbonyloxy)propylene,
4-(carbonyloxy)butylene, 5-(carbonyloxy)pentylene, 6-(carbonyloxy)hexylene,
7-(carbonyloxy)heptylene, S-(carbonyloxy)octylene, 9-(carbonyloxy)nonylene,
10-(carbonyloxy)decylene, 1 l-(carbonyloxy)undecylene, 12-(carbonyl-
oxy)dodecylene, 2~(carbonylimino)ethylene, 3-(carbonylimino)propylene,
4-(carbonylimino)butylene, 5-(carbonylimino)pentylene, 6-(carbonylimino)hexylene,
7-(carbonyhmino)heptylene, 8-(carbonylimino)octylene, 9-(carbonylimino)nonylene,
10-(carbonylimino)decyleue, 11 -(carbonylimino)undecylene, 12-(carbonyl-
imino)dodecylene, 2-iminoethylene, 3-iminopropylene, 4-iminobutylene, 5-imino-
pentylene, 6-iminohexylene, 7-iminoheptylene, 8-iminooctylene, 9-iminononylene,
10-iminodecylene, 11-iminoundecylene, 12-iminododecylene, 2-imino-
carbonylethylene, 3-iminocarbonylpropylene, 4-iminocarbonylbutylene, 5-imino-carbonylpentylene, 6-iminocarbonylhexylenc, 7-iminocarbonylheptyicnc, S-inuno-

carbonyloctylene, 9-iminocarbonylnonylene, 10-iminocarbonyldecylene, 11-imino-carbonylundecylene, 12-iminocarbonyldodecylene, 2-(2-ethyleneoxy)ethylene, 2-(3-propyleneoxy)ethylene, 6-(4-butyleneoxy)hexylene, 2-(2-ethyleneimino-carbonyl)ethylene, 2-(3-propyleneiminocarbonyl)ethylene, 6-(4-butyleneimino-carbonyl)hexylene, 6-(3-propyleneiminocarbonyloxy)hexylene, 6-(3-propyleneimino-carbonyl)hexylene and the like.
Preferred "spacer units" S8 and S9 in the context of the present invention are a straight-chain or branched alkylene grouping, represented by -(CH2)r, and also
, -(CH2)rO-, -(CH2)r-CO-, -(CH2)rCO-0-, -(CH2)rO-CO-, -(CH2)r-CO-NR2-, -(CH2)r-NR2-CO-, -(CH2)rNR2-, -0-(CH2)r, -CO-0-(CH2)r-, -O-C0-(CH2)r, -NR2-CO-(CH2)r, -CO-NR2-(CH2)r, -NR2-(CH2)r-, -0-(CH2)r-CO-0-, -0-(CH2)rO-CO-, -0-(CH2)rCO-NR2-, -0-(CH2)rNR2-, -0-(CH2)rO-7 -0-(CH2)r-NR2-CO-, -NR2-(CH2)r-C0-O, -NR2-(CH2)rO-, -NR2-(CH2)rNR2-,
. -NR2-(CH2)r-0-CO-, -CO-NR2-(CH2)r-0-, -CO-NR2-(CH2)r-NR2-,
-CO-NR2-(CH2)rO-CO-, -0-CO-(CH2)r-CO-, -0-CO-(CH2)rO-,
-0-CO-(CH2)rNR2-, -0-CO-(CH2)rCO-0-, -0-CO-(CH2)rCO-NR2-,
-0-CO-(CH2)rNR2-CO-, -(CH2)rO-(CH2)s-, -(CH2)rCO-0-(CH2)s-,
-(CH2)rO-CO-(CH2)s-, -(CH2)r-NR2-CO-(CH2)s-, -(CH2)rNR2-CO-0-(CH2)s-!
-(CH2)r-0-(CH2)s-0-, -(CH2)r-CO-0-(CH2)s-0-, -(CH2)rQ-CO-(CH2)s-0-,
-(CH2)rNR2-CO-(CH2)s-0-, -(CH2)rNR2-CO-0-(CH2)s-0-, -0-(CH2)rO-(CH2)s-,
-0-(CH2)rCO-O-(CH2)s-, -0-(CH2)rNR2-CO-(CH2)s-,
-0-(CH2)rNR2-CO-0-(CH2)s-, -0-(CH2)r-CO-0-(CH2)s-Ch
-0-(CH2)r-0-(CH2)s-0-, -0-(CH2)r-NR2-CO-(CH2)s-0-!
-0-(CH2)r-NR2-CO-0-(CH2)s-0-, -CO-0-(CH2)rO-(CH2)s-,
-CO-0-(CH2)rO-(CH2)s-0-, wherein r and s are each an integer from 1 to 20, but especially from 2 to 12, with the proviso that r + s
Examples of preferred "spacer units" S8 and S9 are 1,2-ethylene, 1,3-propylene, 1,4-butylene, 1,5-pentylene, 1,6-hexylene, 1,7-heptylene, 1,8-octylene, 1,9-nonylene, 1,10-decylene, 1,11-undecylcne, 1,12-dodecylene, 3-methyl- 1,4-butylene, 3-propyleneoxy, 3-propyleneoxycarbonyl, 2-ethylenecarbonyloxy, 4-butyleneoxy, 4-butyleneoxycarbonyl, 3-propylenecarbonyloxy, 5-pentyleneoxy, 5-penty)ene-oxycarbonyl, 4-butylenecarbonyloxy, 6-hexyleneoxy, 6-hexyleneoxycarbonyl, 5-pentylenecarbonyloxy, 7-heptyleneoxy, 7-heptyleneoxycarbonyl, 6-hexylene-carbonyloxy, 8-octyleneoxy, 8-octyleneoxycarbonyl, 7-heptylenecarbonyloxy, 9-nonyleneoxy, 9-nonyleneoxycarbonyl, 8-octylenecarbonyloxy, 10-decyleneoxy, 10-decyleneoxycarbonyl, 9-nonylenecarbonyloxy, 11-undecyleneoxy, 11-undecylene-oxycarbonyl, 10-decylenecarbonyloxy, 12-dodecyleneoxy, 12-dodecyleneoxy-carbonyl, 11-undecylenecarbonyloxy, 3-propyleneiminocarbonyl, 4-butyleneimino-carbonyl, 5-pentyleneiminocarbonyl, 6-hexyleneiminocarbonyl, 7-heptyleneimino-carbonyl, 8-octyleneiminocarbonyl, 9-nonyIeneiminocarbonyl, 10-decyleneimino-carbonyl, 11-undecyleneiminocarbonyl, 12-dodecyleneiminocarbonyl, 2-ethylene-carbonylimino, 3-propylenecarbonylirnino, 4-butylenecarbonylimino, 5-pentylene-carbonylimino, 6-hexylenecarbonylimino, 7-heptylenecarbonylimino, 8-octylene-carbonylirnino, 9-nonylenecarbonylimino, 10-decylenecarbonylimino, 11-undecylene-carbonylimino, 6-(3-propyleneiminocarbonyloxy)hexylene, 6-(3-propyleneoxy)-hexylene, 6-(3-propyleneoxy)hexyleneoxy, 6-(3-propyleneiminocarbonyloxy)-hexyleneoxy, 6-(3-propyleneiminocarbonyl)hexyl, 6-(3-propyleneiminocarbonyl)-hexyloxy, 1,2-ethylenedioxy, 1,3-propyl enedioxy, 1,4-butylenedioxy, 1,5-pentylene-dioxy, 1,6-hexylenedioxy, 1,7-heptylenedioxy, 1.8-octylenedioxy, 1,9-nonylenedioxy. 1,10-decylenedioxy, 1,11-undecylenedioxy, 1,12-dodecylenedioxy and the like.
The radicals K are divalent groups that can be derived from aliphatic, alicyclic or aromatic diamines by formal removal of the amino groups.
Preferred examples of such aliphatic and alicyclic diamines are: ethylcnediamine, 1.3-propylcncdiaminc, 1,4-butylenediamine. 1,5-pentylenediamine, 1,6-hcxylenediaminc, 1.7-beptylenediamine, 1,8-ocrylenediam.ine, 1,9-nonylene-diaminc, 1.10-dcrylcncdiamine, l.ll-undecylenediamine, 1,12-dodecylenediamine,

ά,ά'-diamino-m-xylene, ά,ά'-diamino-p-xylene, (5-amino-2,2,4-trimethylcyclo-pentyl)methylamine, 1,2-diaminocyclohexane, 4,4'-diaminodicyclohexylmethane, l,3-bis(methylamino)cyclohexane, and 4,9-dioxadodecane-l,12-diamine.
Preferred examples of aromatic diamines are:
3,5-diaminobenzoic acid methyl ester; 3,5-diaminobenzoic acid hexyl ester;
3,5-diaminobenzoic acid dodecyl ester; 3,5-diaminobenzoic acid isopropyl ester;
4,4'-methylenedianiline; 4,4'-ethylenedianiline; 4,4'-diamino-3,3'-dimethyldiphenyl-
methane; 3,3',5,5'-tetramethylbenzidine; 4,4'-diaminodiphenyl sulfone; 4,4'-diamino-'l I diphenyl ether; 1,5-diaminonaphthalene; 3,3'-dimethyl-4,4'-diaminobiphenyl;
3,4'-diaminodiphenyl ether; 3,3'-diammobenzophenone; 4,4'-diaminobenzophenone;
4,4'-diamino-2,2'-dimethylbibenzyl; 2,2-bis[4-(4-aminophenoxy)phenyl] sulfone;
1,4-bis(4-aminophenoxy)benzene; 1,3-bis(4-aminophenoxy)benzene;
1,3-bis(3-aminophenoxy)benzene; 2,7-diaminofluorene; 9,9-bis(4-aminophenyl)- fluorene; 4,4'-memylenebis(2-chloroaniline); 4,4-bis(4-aminophenoxy)biphenyl;
2,2',5,5,-tetrachloro-4,4'-diaminobiphenyl; 2,2'-dichloro-4,4'-diamino-5,5,-dimethoxy-
biphenyl; 3,3'-dimethoxy-4,4'-diaminobiphenyl; 4,4'-(l ,4-phenyleneisopropylidene)-
bisaniline; 4,4'-(l ,3-phenyleneisopropylidene)bisaniline; 2,2-bis[4-(4-arninophenoxy)-
phenyl]propane; 2,2-bis[3-(4-aminophenoxy)phenyl]hexafluoropropane; 2,2-bis- [3-amino-4-methylphenyl]hexafluoropropane; 2,2-bis(4-aminophenyl)hexafluoro-
propane; 2,2,-bis[4-(4-amino-2-trifluoromethylphenoxy)phenyl]hexafluoropropane;
4J4,-diamino-2,2,-bis(trifluoromethyl)biphenyl; and 4J4'-bis[(4-amino-2-trifluoro-
methyl) phenoxy]2',3',5',6',2',3',5',6',-octafluorobiphenyl.
The divalent, trivalent or tetravalent group J serves essentially as a grouping for linking the polymer main chain to the side-chain, which comprises the whole of formula I except M. Two of the valencies in J serve as linkages, indicated in formulae III to VIIII, via S6 to S10 within the main chain. The third and optionally the fourth valency serves as the linkage to one or two side-chain(s) of the formula I (formula 1 except M). The polymer chain may, however, also comprise building blocks of the formulae III to VIII in which the side-chain of formula I is absent, that is to say where the group J is merely divalent. The proportion of building blocks of the formulae in to

VIII in which J is divalent, that is to say in which there is no crosslinkable side-chain of the formula I present, is generally less than 75 %, but preferably less than 50 % and more especially less than 30 %. Of the trivalent and tetravalent groups J that contain one or two crosslinkable side-chains of the formula I, the trivalent groups, that is to say those groups which are linked to only one crosslinkable side-chain of the formula I, are preferred.
The photoactive polymer of formula I may be a homopolymer or a copolymer. However, we prefer it to be a copolymer.
Preferably at least 50% of the monomer building blocks forming the main chain of photoactive polymer of formula I are linked to one or two side-chains, which comprises the whole of formula I except M. Especially preferred is a polymer in which at least 70% of the monomer building blocks forming the main chain are linked to one or two of the side-chains.
Preferably the monomer building blocks carrying a side-chain are each linked to only one side-chain.
The building blocks of the formulae IV, VI and VIII are amic acid groupings or amic acid ester groupings (i.e. carboxamide-carboxylic acid groupings or carboxamide-carboxylic acid ester groupings) which on the one hand may occur as a result of incomplete imidisation in the polyimide chain. On the other hand, polymers mat consist only of building blocks of formulae IV, VI or VIII, that is to say polyamic acids or polyamic acid esters, are important precursors for the preparation of the polyimides according to the invention and are also included in the present invention. Of those polymers which contain groups of formulae IV, VI or VIII, preference is given to those in which G is hydrogen, that is to say those which consist exclusively of, or contain some, polyamic acid groups.


The term "phenylene" includes in the context of the present invention 1,2-, 1,3- or 1,4-phenylene that is unsubstituted or mono- or poly-substiruled. Preference is given to 1,3- or 1,4-phenylene, but especially to 1,4-phenylene.
The expression "cyclic, straight-chain or branched alkyl residue which is unsubstituted or halogeno or polyhalogeno-substituted, having 1 to 12 carbon atoms and wherein one or more CH2 groups may independently be replaced by -0-, -CO-, -CO-O-, -O-CO, -CH=CH-, -0=C-, with the proviso that oxygen atoms are not directly attached to each other" denotes for example, methyl, ethyl, propyl, isopropyl, butyl, isobutyl, sec-butyl, tert-butyl, pentyl, isopentyl, cyclopentyl, hexyl, cyclohexyl, heptyl, octyl, nonyl, decyl, undecyl, dodecyl, 3-methylpentyl, allyl, but-3-en-l-yl, pent-4-en-l-yl, hex-5-en-l-yl, propynyl, butynyl, pentynyl, methoxy, ethoxy, propoxy, isopropoxy, butoxy, isobutox)', sec--butoxy, tert-butoxy, pentyloxy, isopentyloxy, cyclopentyloxy, hexyloxy, cyclohexyloxy, heptyloxy, octyloxy, nonyloxy, decyloxy, undecyloxy, dodecyloxy, 3-methylpentyloxy, allyloxy, but-3-enyloxy, pent-4-enyloxy, cylohexylmethoxy, cyclopentylrnethoxy, methoxy-carbonyl, ethoxycarbonyl, propoxycarbonyl, isopropoxycarbonyl, butoxycarbonyl, isobutoxycarbonyl, sec-butoxycarbonyl, fer/-butoxycarbonyl, pentyloxycarbonyl, isopentyloxycarbonyl, cyclopentyloxycarbonyl, hexyloxycarbonyl, cyclohexyloxy-carbonyl, octyloxycarbonyl, nonyloxycarbonyl, decyloxycarbonyl, undecyloxy-carbonyl, dodecyloxycarbonyl, 3-methylpentyloxycarbonyl, ahyloxycarbonyl, but-3-enyloxycarbonyl, pent-4-enyloxycarbonyl, cylohexylmethoxycarbonyl, cyclo-pentylmethoxycarbonyl, acetoxy, ethylcarbonyloxy, propylcarbonyloxy, isopropyl-carbonyloxy, butylcarbonyloxy, isobutylcarbonyloxy, .sec-butylcarbonyloxy, fe?'/-butylcarbonyloxy, pentylcarbonyloxy, isopentylcarbonyloxy, cyclopentyl-carbonyloxy, hexylcai'bonyloxy, cyclohexylcarbonyloxy, octylcarbonyloxy, nonyl-carbonyloxy, decylcarbonyloxy, undecylcarbonyloxy, dodecylcarbonyloxy. 3-methylpentylcarbonyloxy, but-3-enyloxy, pent-4-enyloxy, acetyl, ethylcarbonyl, propylcarbonyl, isopropylcarbonyl, butylcarbonyl, isobutylcarbonyl, sec-butyl-carbonyl, pentylcarbonyl, isopentylcarbonyl, cyclohexylcarbonyl, octylcarbonyl, nonylcarbonyl, decylcarbonyl, undecylcarbonyl, dodecylcarbonyl, mcthoxvacetoxy, 1-methoxy-2-propoxy, 3-methoxy-l-propoxy. 2-mctboxyeihoxy. 2-isopropoxycthoxy,

l-ethoxy-3-pentyloxy, 3-butyn-l-oxy, 4-pentyn-l-oxy, 5-chloro-l-pentyn, 4-pentynecarbonyloxy, 6-propyloxyhexyl, 6-propyloxyhexyloxy, 2-fluoroethyl, trifluoromethyl, 2,2,2-lrifluoroethyl, IH,1H-pentadecafluorooctyl, 1H,\H,1 7H-dodeca-fluoroheptyl, 2-(perfluorooctyl)ethyl, 2-(perfluorobutyl)ethyl, 2-(perfluorohexyl)-ethyl, 2-(perfluorodecyI)ethyl, perfluoropropyl, perfluorobutyl, perfluoroheptyl, perfluorooctyl, perfluororionyl. 1-fluoropropoxy, 1-fluoropentyloxy, 2-fluoropropoxy, 2,2-difluoropropoxy, 3-fluoropropoxy, 3,3-difluoropropoxy, 3,3,3-trifluoropropoxy, trifluoromethoxy and the like.
The term "aliphatic", unless the context requires otherwise, includes straight-chain and branched alkyl, as well as saturated and unsaturated groups. Possible substituents include alkyl, aryl (thus giving an araliphatic group) and cycloalkyi, as well as amino, cyano, epoxy, halogen, hydroxy, nitro, oxo etc. Possible heteroatoms which may replace carbon atoms include nitrogen, oxygen and sulphur. In the case of nitrogen further substitution is possible with groups such as alkyl, aryl and cycloalkyi.
The term "alkyl" likewise, unless the context requires otherwise, includes straight-chain and branched alkyl, as well as saturated and unsaturated groups.
The term "lower alkyl", denotes straight-chain and branched saturated hydrocarbon radicals having from 1 to 6, preferably from 1 to 3, carbon atoms, such as methyl, ethyl, propyl or isopropyl and the like.
The term "aromatic" includes carbocylic and heterocyclic groups, either unsubstituted or substituted by one or more groups.
The side-chain polymers according to the invention can be present in the form of homopolymers as well as in the form of copolymers. The term "copolymers" is to be understood as meaning especially statistical copolymers.
The polymers of formula I arc characterised by being readily accessible. The methods for the production will be known to a person skilled in the art.

The polymers of formula I, with acrylate, methacrylate and styrene derivative as repeating monomer unit, can be prepared in principle according to two different processes. In addition to the direct polymerisation of pre-finished monomers there
exists the possibility of polymer-analogous reaction of reactive photoactive
derivatives with functional polymers.
For the direct polymerisation, the monomers and the comonomers are firstly prepared separately from the individual components. The formation of the polymers is subsequently effected in a manner known per se under the influence of UV radiation or heat or by the action of radical or ionic catalysts. Potassium peroxodisulfate, dibenzoyl peroxide, azobisisobutyronitrile or di-fert-butyl peroxide are examples of radical initiators. Ionic catalysts are alkali-organic compounds such as phenyllithium or naphthylsodium or Lewis acids such as BF3, A1C13, SnCl3 or TiCl4 The monomers can be polymerised in solution, suspension, emulsion or substance.
In the second process a polymer of formula I can also be produced in a polymer-analogous reaction from a pre-finished functional polymer and a suitable functionalised photoactive derivative. Many known processes such as, for example, esterification, trans-esterification, amidation or the etherification are suitable for polymer-analogous reactions.
This polymers have a molecular weight MW between 1 000 and 5 000 000, preferably however between 5 000 and 2 000 000, especially advantageously however between 10 000 and 1 000 000.
The preparation of the polyamic acids and polyimides according to the invention is generally carried out analogously to the methods frequently described in the polyimide literature, for example Plast. Eng. 36 (1996) (Polyimides, fundamentals and applications).

For example, the polycondensation reaction for the preparation of the polyamic acids is carried out in solution in a polar aprotic organic solvent, such as γ-butyrolactone, N,N-dimethylacetamide, N-methylpyrrolidone or N,N-dimethylformamide. In most cases equimolar amounts of the dianhydride and the diamine are used, that is to say one amino group per anhydride group. If it is desired to stabilise the molecular weight of the polymer, it is possible for that purpose to add an excess or a less-than--stoichiometric amount of one of the two components or to add a monofunctional compound in the form of a dicarboxylic acid monoanhydride or in the form of a monoamine. Examples of such monofunctional compounds are maleic acid anhydride, phthalic acid anhydride, aniline and so on. The reaction is carried out preferably at a temperature of less than 100 °C.
The cyclisation of the polyamic acids to form the polyimides can be carried out by heating, that is to say by condensation with removal of water or by other imidisation reactions with reagents. When carried out purely thermally, the imidisation of the polyamic acids is not always complete, that is to say the resulting polyimides may still contain proportions of polyamic acid. The imidisation reactions are generally carried out at a temperature of from 60 to 250 °C, but preferably at less than 200 °C. In order to achieve imidisation at rather lower temperatures there are additionally mixed into the reaction mixture reagents that facilitate the removal of water. Such reagents are, for example, mixtures consisting of acid anhydrides, such as acetic acid anhydride, propionic acid anhydride, phthalic acid anhydride, trifluoroacetic acid anhydride, and tertiary amines, such as triethylamine, trimethylamine, tributylarnine, pyridine, N,N-dimethylaniline, lutidine, collidine etc.. The amount of reagents used in that case is preferably at least two equivalents of amine and four equivalents of acid anhydride per equivalent of polyamic acid to be condensed.
The imidisation reaction can be carried out before or alternatively only after applica¬tion to a support. The latter variant is preferred especially when the polyimide in question has poor solubility in the customary solvents.

The polyamic acids and the polyimides of the present invention has an intrinsic viscosity preferably in range of 0.05 to lO dL/g, more preferably 0.05 to 5 dL/g. Herein, the intrinsic viscosity (rinh = In ηrel/C) is determined by measuring a solution containing a polymer in a concentration of 0.5g/100ml for its viscosity at 30 °C using N-methyl-2-pyrrolidone as solvent.
The number of monomer building blocks from which the polymer chains according to the invention are synthesised can vary within a wide range. It is generally from 2 to 2000, but especially from 3 to 200.
The polymer according to the invention may contain additives such as silane-containing compounds and epoxy-containing crosslinking agents for further improving the adhesion of the polymer to a substrate. Example for silane adhesion promoters were described in the literature, for example Plast. Eng. 36 (1996) (Polyimides, fundamentals and applications). The above epoxy-containing crosslinking agent preferably includes 4,4'-methylenebis(N,N-diglycidylaniline), trimethylolpropane triglycidyl ether, benzene- 1,2,4,5-tetracarboxylic acid l,2:4,5-N,N'-diglycidyldiimide, polyethylene glycol diglycidyl ether, N,N-diglycidyl-cyclohexylamine and the like.
The polymer according to the invention may contain additives such a photosensitiser, a photoradical generator and/or a cationic photoinitiator. Example for such additives were 2,2-dimethoxyphenylethanone, mixture of diphenylmethanone and N,N-dimethylbenzenamine or ethyl 4-(dimethylarnino)benzoate, xanthone, thioxanthone, lRGACURE™ 184, 369, 500, 651 and 907 (Ciba), Michler's ketone, triaryl sulfonium salt and the like.
The polymers according to the invention may be used as a single polymer or as mixture with other polymers, oligomers, monomers, photoactive polymers, phoioactive oligomers and/or photoactive monomers. Thus the properties of the layer may be modified to give what is sought, lor example, an induced pretilt angles, good


surface wetting, high voltage holding ratio, a specific anchoring energy etc. may be obtained.
The polymers according to the invention can then be applied to a support and, after any imidisation step which may be necessary, crosslinked by irradiation with linearly polarised light, that is to say by cycloaddition of their side-chains containing the photoreactive group, there being obtained, depending upon the direction of polarisation of the light radiated in, a preferred direction of orientation and of the angle of tilt for liquid crystals that are bought into contact with the orientation layer. By spatially selective irradiation of the molecular units according to the invention it is hence possible for very specific regions of a surface to be aligned and provided with a defined angle of tilt. At the same time the orientation layer so produced is also stabilised by the cycloaddition.
The present invention therefore relates also to the use of the polymers according to the invention as orientation layers for liquid crystals, and to their use in optical constructional elements, especially in the production of hybrid layer elements.
Such orientation layers can be produced, for example, by first preparing a solution of the resulting polymer material, which is applied to a support, which is optionally coated with an electrode (for example a glass plate coated with indium-tin oxide (ITO)), in a spin-coating apparatus, so that homogeneous layers of 0.05 to 50 urn thickness are produced. Then, or optionally after prior imidisation, the regions to be oriented can be irradiated, for example, with a high-pressure mercury vapour lamp, a xenon lamp or a pulsed UV laser, using a polariser and optionally a mask for creating images of structures. The irradiation time is dependent upon the output of the individual lamps and can vary from a few seconds to several hours. The dimerisation can also be carried out, however, by irradiation of the homogeneous layer using filters that, for example, allow only the radiation suitable for the crosslinking reaction to pass through.
Further aspects of the present invention are:


a) Optical or electro-optical devices having at least one orientation layer, characterised in that the orientation layer contains polymers according to formula I; and
b) Use of polymer according formula I in the construction of unstructured and structured optical elements and multi-layer systems.
The polymers in accordance with the invention are illustrated in more detail by the following Examples. In the Examples hereinafter Tg signifies the glass temperature, C signifies the crystalline phase, N signifies the nematic phase I signifies the isotropic phase and p signifies the number of repeating units in the polymer. Relative molecular weights were determined by gel permeation chromatography (GPC) at 35 °C using THF as solvent with polystyrene standard.
Example 1
Poly-[l-(ll-[5-[4-[(E)-2-methoxycarbonylvinyl]benzoyloxy]-2-(4-propylbenzoyl-oxy)benzoyloxy]undecyloxycarbonyI]-l-rnethyIethylene]

A mixture of 0.89 g (1.22 mmol) (E)-5-[4-(2-methoxycarbonylvinyl)benzoyloxy]--2-(4-propylbenzoyloxy)benzoic acid ll-(2-methylacryloyloxy)undecyl ester and 2.0 mg (0.012 mmol) a.a'-azoisobutyronitrile (AIBN) in 2.45 ml dry tetrahydrofuran (THF) was degassed in a sealable tube. The rube was then sealed under argon and stirred at 60 °C for 17 h. The polymer was diluted with 2.5 ml THF, precipitated into

500 ml diethyl ether and collected. The polymer was reprecipitated
from THF (7.0 ml) into 750 ml methanol to yield 0.71 g
(80%) poly-f 1 -[ 11 -[5-[4-[(E)-2-melhoxycarbonylvinyl]benzoyloxy]-2-(4-propyl-
benzoyloxy)benzoyloxy]undecyloxycarbonyl]-l-methylethylene] as a hard solid;
Mn=7.4* 104;pdi =-6.59,'Tg; = "493'.°C\cl.p.'(N/I)127.3oC.
The (E)-5-[4-(2-methoxycarbonylvinyl)benzoyloxy]-2-(4-propylbenzoyloxy)benzoic acid 1 l-(2-methylacryloyloxy)undecyl ester used as stalling material was prepared in accordance with the following procedure:
(E)-4-Carboxyl cinnamic acid methyl ester


O
o
o —
10.0 g (66.6 mmol) 4-carboxybenzaldehyde were dissolved in 100 ml toluene and 23.6 g (69.9 mmol) [(methoxycarbonyl)methyl]triphenylphosphorane were added. The reaction was slightly exothermic. The thick suspension was diluted with 50 ml toluene. After 18 h at room temperature the product was collected by filtration and was digest in 100 ml isopropyl alcohol at reflux temperature for 1 hour. The solid was then filtered off at 0 °C, dried overnight at 45 °C under vacuum, resulting in 8.9 g (65%) (E)-4-carboxyl cinnamic acid methyl ester as white powder.
2-Methylacrylic acid 11-bromoundecyl ester

19.2 g (76.4 mmol) 11-bromo-l-undecanol, 7.2 g (S4.i mmol) mcthacryhc acid and 1.03 g (8 4 mmol) 4-dimethylaminopyridine were dissolved in 157 ml dichior-


methane. The solution was subsequently cooled to 0 °C and then a solution of 17.4 g (84.2 mmol) dicyclohexylcarbodiimide in SO ml dichloromethane was added dropwise, in the course of 45 minutes at 0 °C. The reaction was allowed to warm to room temperature, stirred for 19 hours and filtered. The filtrate was concentrated by evaporation. Chromatography of the residue on 170 g silica gel using toluene yielded 19.3 g (98.4%) 2-methylacrylic acid 11-bromoundecyl ester.
2,5-Dihydroxybenzoic acid ll-(2-niethylacryloyIoxy) ester

8.46 g (54.9 mmol) 2,5-dihydroxybenzoic acid was suspended in 55 ml acetonitrile. 8.24 ml (54.9 mmol) l,8-diazabicyclo[5.4.0]undec-7-ene(l,5o) (DBU) were added dropwise in the course of 10 minutes. The reaction temperature rise to 40 °C. 19.3 g (60.4 mmol) 2-methyl-acrylic acid 11 -bromo-undecyl ester were added by room temperature and the mixture was then heated at reflux temperature for 17.5 hours. The reaction mixture was cooled and then partitioned between diethyl ether and water; the organic phase was washed with water, with IN sulfuric acid and again with water, dried over sodium sulfate, filtered and concentrated by rotary evaporation. The residue was recrystallised, first form a mixture of ethyl acetate (17 ml) and hexane (100 ml) and again form a mixture of terr-butyl methyl ether (50 ml) and hexane (100 ml) to yield 17.1 g (79%) 2,5-dihydroxybenzoic acid ll-(2-methylacryloyloxy) ester as white crystals.

(E)-2-Hydro\y-5-l4-(2-inethoxycarboDylvinyl)bcazoyIoxylbenzoic acid 1 l-(2-metliylacryloyloxy)uridecyl ester

4.76 g (12.1 mmol) 2,5-dihydroxybenzoic acid ll-(2-methylacryIoyloxy)ester, 2.50 g (12.1 mmol) (E)-4-carboxyl cinnamic acid methyl ester and 0.37 g (3.0 mmol) 4-dimethylaminopyridme were dissolved in 30 ml of dichloromethane. A suspension of 2.32g (12.1 mmol) N-(3-dimethylaminopropyl)-N-ethylcarbodiimide hydrochloride and 25 ml dichloromethane were added dropwise in the course of 1 hour. After 1.5 hour at room temperature the reaction mixture was partitioned between dichloromethane and water; the organic phase was washed repeatedly with water, dried over sodium sulfate, filtered and concentrated by rotary evaporation. Chromatography of the residue on 240 g silica gel using cyclohexane : ethyl acetate 9:1 yielded 6.1 g (87%) (75)-2-hydroxy-5-[4-(2-methoxycarbonylvinyl)benzoyloxy]-benzoic acid 11 -(2-methylacryloyloxy)-undecyl ester as white powder, m.p. = 51 °C.

(E)-5-(4-(2-Methoxycarbouylvinyl)bcnzoylo\7]-2-(4-propyIbeazoyloxy) benzoic acid ll-(2-methylacryloyloxy)undecyl ester

1.0 g (1.72 mmol) (E)-2-hydioxy-5-[4-(2-methoxycarbonylvinyl)ben2oy]oxy]ben2oic acid ll-(2-methyiacryloyloxy)undecyl ester, 0.37 g (2.24 mmol) 4-propylbenzoic acid and 58 mg (0.47 mmol) 4-dimethylaminopyridirie were dissolved in 20 ml of dichloromethane. A suspension of 0.43g (2.24 mmol) N-(3-dimethylaminopropyl)-N-ethylcarbodiimide hydrochloride and 10 ml dichloromethane were added dropwise in the course of 45 minutes. After 65 hour at room temperature the reaction mixture was partitioned between dichloromethane and water; the organic phase was washed repeatedly with water, dried over sodium sulfate, filtered and concentrated by rotary evaporation. Chromatography of the residue on 120 g silica gel using cyclohexane : ethyl acetate 4:1 and subsequent crystallisation form 50 ml isopropyl alcohol yielded 0.99 g (79%) (£)-5-[4-(2-methoxycarbonylvinyl)benzoyloxy]-2-(4-propylbenzoyl-oxy)benzoic acid 1 l-(2-methyiacryloyloxy)undecyl ester as white powder, m.p.(C/N}
86.8°c.cl.p(N/I),102.8oC.
The following compounds were prepared in an analogous manner:
— Poly[l-[ll-[5-[4-[(E)-2-methoxycarbonylvinyl]benzoyloxy]-2-(4-pentyl-
benzoyloxy)beiizoyloxy]undecyloxycarbonyl]-l-methylethylene], Mn =
6.9 x 104, pdi = 5.08, Tg = 45.9 °C, cl.p.(N/I) 127.30C
— Poly[l -[1 l'[5-[4-[(E)-2-methoxycarbonyl-vinyl]-benzoyloxy]-2-(4-heptyl-
benzoyloxy)benzoyloxy]-undecyloxycarbonyl]-l-memylethylene], Mn =
1.00 x 105, pdi = 7.04, Tg - 41.7 °C, cl.p.(N/I),123.6oC

Poly[ 1 -[ 1 l-[5-[4-[(E)-2-methoxycarbonylvinyl]benzoyloxy]-2-(4-propylcyclo-hexanoyloxy)benzoyloxy]undecyloxycarbonyl]-l-methylethylene], Mn - 7.2 x 104, pdi = 4.29, Tg = 45.4 °C, cl.p..(N/I) 113.6oC Poly-[l-[8-[5-[4-[(E}-2-methoxycarbonylvinyl]benzoyloxy]-2-(4-propyl-benzoyloxy)benzoyloxy]octyloxycarbonyl]-l-methylethylene], Mn 1.68 x 105, pdr-2.96, Tg=62.7°C, cl.p.(N/I) 132.6oC Poly-[l-[6-[5-[4-[(E)-2-methoxycarbonylvinyl]bcnzoyloxy]-2-(4-propyl-benzoyloxy)benzoyloxy]hexyloxycarbonyl]-l-methylethylene], Mn = 1.17 x 105, dpi-2.61, Tg-62.7°C, cl.p.(N/I) 138.8oC Poly-[ 1 -[ 11 -[2-[4-[(E)-2-methoxycarbonylvinyl]benzoyloxy]-5-(4-propyl-benzoyloxy)benzoyloxy]undecyloxycarbonyl]-l-methylethylene], Mn 4.7 x 104, pdi=2.31, Tg=54.8°C, cl.p:(N/I) 124.3oC
Example 2
Poly-[l-[ll-[2-[4-pentylbenzoyloxy]-5-[6-[2-methoxy-4-(methoxycarbonylvinyl)-phenoxy]oxyhexyI]benzoyJoxyjundecyJoxycarbonyI]-l-methylethyIene]

Preparation was carried out analogously to Example 1 using 1.0 g (1.17 nimol) (E)-2-[4-pentylbenzoyloxy]-5-[6-[2-methoxy-4-(methoxycarbonylvinyl)phenoxy]oxy-hexyl]bepzoic acid ll-(2-methylacryloyloxy)undecyl ester yielding 0.84 g (84 %) poly-[l-[l l-[2-[4-pentylbenzoyloxy]-5-[6-[2-methoxy-Hmethox.vcarbonyl-

vinyl)phenoxy]oxyhexyl]benzoyloxy]undecyloxycarbonyl]-l-memylethylene] as hard solid; Mn = 7.3 x 104, pdi = 4.40, Tg = 34.0 °C, cl.p. (N/I) 54.2oC
The (E)-2-[4-pentylbenzoyloxy]-2-[5-[2-methoxy-4-(methoxycarbonylvinyl)-
phenoxy]oxyhexyl]benzoic acid 11 -(2-methylacryloyloxy)undecyl ester used as starting material was prepared in accordance with the following procedure:
(E)-4-Hydroxy-3-methoxycinnamic acid methyl ester

25 g (0.13 mol) of (E)-4-hydroxy-3-methoxycinnamic acid were dissolved in 180 ml of methanol, and 5 ml of concentrated sulfuric acid were added. The solution was heated under reflux for 2 hours. The main amount of the methanol (about 150 ml) was then distilled off and the residue that remained was poured into 500 ml of ice-water. The precipitated ester was filtered off with suction, washed in succession with cold water, with a small amount of a cold saturated sodium bicarbonate solution and again with cold water and dried at 50 °C under a water-jet vacuum. Chromatography on 250 g of silica gel using dichloromethane : diethyl ether (19:1) yielded 21.78 g of (E)-4-hydroxy-3-methoxycinnarnic acid methyl ester in the form of a light-yellow oil.
(E)-4-(6-Hydroxyhexyloxy)-3-methoxycinnamic acid methyl ester


3.92 ml (25.2 mmol) of 1,6-hexanediol vinyl ether were added to a solution of 5.0 g (24.0 mmol) of (E)-4-hydroxy-3-methoxycinnamic acid methyl ester and 6.61 g (25.2 mmol) of triphenylphosphine in 150 ml of tetrahydrofuran. The colourless solution was subsequently cooled to 0 °C and then 11.5 ml (25.3 mmol) of a 40% solution of azodicarboxylic acid diethyl ester in toluene were added dropwise thereto in the course of 30 minutes. The mixture was subsequently allowed to react first for 30 minutes at 0 °C and then for 22.5 hours at room temperature. 150 ml of methanol and 10 drops of concentrated sulfuric acid were then added to the reaction solution and the mixture was stirred for 1.5 hours. The reaction mixture was then partitioned between ethyl acetate and water; the organic phase was washed with a saturated sodium bicarbonate solution and repeatedly with saturated sodium chloride solution, dried over magnesium sulfate, filtered and concentrated by evaporation. Chromato¬graphy of the residue on 470 g of silica gel using toluene : ethyl acetate 1:1 and subsequent crystallisation from ethyl acetate : hexane 3:5 yielded 6.13 g of 4-(6~hydroxyhexyloxy)-3-methoxycinnamic acid methyl ester.
(E)-2-Hydroxy-5-[6-[2-methoxy-4-(methoxycarbonylvinyl)phenoxy]oxyhexyl]ben zoic acid ll-(2-methylacry!oyloxy)undecyl ester

1.27 g (3.24 mmol) 2,5-dihydroxybenzoic acid ll-(2-methylacryloyloxy)ester, 1.0 g (3.24 mmol) 4-(6-hydroxyhexyloxy)-3-methoxycinnamic acid methyl ester and 0.89 g (3.40 rnmol) of triphenylphosphine in 20 ml of tetrahydrofuran. The colourless solution was subsequently cooled to 0 °C and then 1.48 ml (3.40 mmol) of a 40% solution of azodicarboxylic acid diethyl ester in toluene were added dropwise thereto

in the course of 10 minutes. The mixture was subsequently allowed to react for 3 hours at 0 °C. The reaction mixture was then partitioned between ethyl acetate and water; the organic phase was washed with repeatedly with saturated sodium chloride solution, dried over magnesium sulfate, filtered and concentrated by evaporation. The residue was digest in a mixture form methanol and water 3:2. The solid was then filtered off and dried overnight at 45 °C under vacuum. Chromatography of the solid on 150 g of silica gel using toluene : ethyl acetate 1:1 yielded 1.45 g (65 %) of (E}-2-hydroxy-5-[6-[2-methoxy-4-(methoxycarbonylvinyl)phenoxy]oxyhexyl]benzoic acid ll-(2-methylacryloylox'y) undecyl ester as colourless oil.
(E)-2-f4-pentyIbenzoyloxy]-5-[6-[2-methoxy-4-(methoxycarboDylvinyl)-phenoxy]oxyhexyI]benzoic acid ll-(2-methyIacryloyloxy)undecyl ester


— 0

1.43 g (2.09 mmol) (£')-2-hydroxy-5-[6-[2-methoxy-4-(methoxycarbonylvinyl) phenoxy]oxyhexyI]benzoic acid 11 -(2-methylacryloyloxy)undecyl ester, 0.42 g (2.20 mmol) 4-pentylbenzoic acid and 64 mg (0.52 mmol) 4-dimethylaminopyridine were dissolved in 30 ml of dichloromethane. A suspension of 0.42g (2.20 mmol) N-dimethylammopropy-N-ethylcarbodiimide hydrochloride and 3 ml dichloro¬methane were added dropwise in the course of 15 minutes. After 20 hour at room temperature the reaction mixture was partitioned between dichloromethane and water; the organic phase was washed repeatedly with water, dried over sodium sulfate, filtered and concentrated by rotary evaporation. Chromatography of the residue on 150 g silica gel using cyclohexane : ethyl acetate 4:1 and subsequent crystallisation form 20 ml isopropyl alcohol yielded 1.40 g (78%) (E)-2-[4-pentylbcnzoyloxy]-

-5-[6-[2-methoxy-4-(methoxycarbonylvinyl)phenoxy]oxyhexyl] benzoic acid 11 -(2-methy]acry]oyJoxy)undecy] ester as white crystals.
Example 3
Polyimide
96.6 mg (0.493 mmol) of 1,2,3,4-cyclobutantetracarboxylic acid dianhydride was
added to a solution of 0.434 g (0.547 mmol) of 3,5-diaminobenzoic
acid 11 -[2-[4-pentylbenzoyloxy]-5-[4-(2-methoxycarbonyl-vinyl)benzoyloxy]-
benzoyloxyjundecyl ester in 3 ml of tetrahydrofuran. Stirring was then carried out at 0 °C for 2 hours. 10.7 mg (0.055 mmol)) of 1,2,3,4-cyclobutantetracarboxylic acid dianhydride were added. The mixture was subsequently allowed to react for 69 hours at room temperature. The polymer mixture was diluted with 3.0 ml THF, precipitated into 150 ml diethyl ether and collected. The polymer was reprecipitated form THF (10 ml) into 500 ml water to yield, after drying at room temperature under vacuum, 0.51 g of polyamic acid A in the form of a beige powder; [n] = 0.51 dL/g.
The 3,5-diaminobenzoic acid ll-[2-[4-pentylbenzoyloxy]-5-[4-(2-methoxycarbonyl-• vinyl)benzoyloxy]ben2oyloxy]undecyl ester used as starting material was prepared in accordance with the following procedure:

3,5-Dinitrobenzoic acid 11-bromoundecyl ester


11.4 g (45.4 mmol) 11-bromo-l-undecanol, 11.0 g (47.7 mmol) 3,5-dinitrobenzoyl chloride, 54 mg 4-dimethylaminopyridine were dissolved in 94 ml dichloromethane. The solution was subsequently cooled to 0 °C and then 18.3 ml (227 mmol) Pyridine was added dropwise, in the course of 25 minutes. After 4.5 hours at 0 °C the reaction mixture was partitioned between dichloromethane and water; the organic phase was washed repeatedly with water, dried over sodium sulfate, filtered and concentrated by rotary evaporation. Chromatography of the residue on 200 g silica gel using Toluene yielded 18.1 g (90%) 3,5-Dinitrobenzoic acid 11-bromoundecyl ester as yellow powder.

3,5-Dinitrobenzoic acid ll-[2,5-dihydroxybenzoyloxy)undecyI ester P"
o = N+
2.78 g (18.0 mmol) 2,5-dihydroxybenzoic acid were dissolved in 36 ml dimethylformamide. 2.96 ml (19.8 mmol) l,8-diazabicyclo[5.4.0]undec-7-ene( 1,5-5) (DBU) were added dropwise in the course of 15 minutes. The reaction temperature rise to 30 °C, subsequently 8.83 g (19.8 mmol) 3,5-dinitrobenzoic acid 11-bromoundecyl ester were added in one portion. The mixture was then heated at 80 °C for 2 hours. The reaction mixture was cooled and then partitioned between dichloromethane and IN hydrochloric acid, the organic phase was washed twice with water, dried over sodium sulfate, filtered and concentrated by rotary evaporation. Chromatography of the residue on 200 g silica gel using Toluene yielded 5,28 g (57%) 3,5-dinitrobenzoic acid 1 l-[2,5-dihydroxybenzoyloxy]undecyl ester as yellow powder.

3,5-Dinitrobcnzoic acid ll-[2-liydroxy5-[4-(2-methoxycarbonylvinyI)-benzoyloxy]benzoy!oxy]undecyl ester
P" 0 = N+

2.50 g (4.82 mmol) 3,5-Dinitrobenzoic acid ll-[2,5-dihydroxybenzoyloxy] undecyl ester, 0.99 g (4.82 mmol) (E-4-carboxyl cinnamic acid methyl ester and 0.15 g (1.20 mmol) 4-dimeuiylaminopyridine were dissolved in 12 ml of dichloromethane. A suspension of 0.92 g (4.82 mmol) Ndimethylaminopropy-N'-ethylcarbodiirriide hydrochloride and 10 ml dichloromethane were added dropwise in the course of 45 minutes. After 3 hours at room temperature the reaction mixture was partitioned between dichloromethane and water; the organic phase was washed repeatedly with water, dried over sodium sulfate, filtered and concentrated by rotary evaporation. Chromatography of the residue on 100 g silica gel using toluene yielded 2.63 g (77%) 3,5-dinitrobenzoic acid ll-[2-hydroxy 5-[4-(2-methoxycarbonyl-vinyl)benzoyloxy] benzoyloxyjundecyl ester as yellow powder.

3,5-Dinitrobenzoic acid ll-{2-[4-pcntylbcnzoyloxy]-5-[4-(2-methoxycarbonyl-vinyI)benzoyloxy]benzoyloxy]undecyl ester

1.31 g (1.86 mmol) 3,5-dinitrobenzoic acid ll-[2-[4-pentylbenzoyloxy]--5-[4-(2-methoxycarbonylvinyl)benzoyIoxy]benzoyloxy]undecyl ester, 0.34 g (2.05 mmol) 4-propylbenzoic acid and 63 mg (0.51 mmol) 4-dimethylaminopyridine were dissolved in 26 ml of dichloromethane. A suspension of 0.39g (2.05 mmol) N-3-dimemylaminopropyl)-N'-ethylcarbodhmide hydrochloride and 11 ml dichloromethane were added dropwise in the course of 40 minutes. After 27.5 hour at room temperature the reaction mixture was partitioned between dichloromethane and water; the organic phase was washed repeatedly with water, dried over sodium sulfate, filtered and concentrated by rotary evaporation. Chromatography of the residue on 50 g silica gel using first toluene then toluene: ethyl acetate and subsequent crystallisation form 300 ml isopropyl alcohol yielded 1.23 g (77%) 3,5-dinitrobenzoic acid ll-[2-[4-pentylbenzoyloxy]-5-[4-(2-methoxycarbonylvinyl)benzoyloxy]benzoyl-oxyjundecyl ester as white crystals.

3,5-Diaminobenzoic acid ll-[2-[4-pentylbenzoyloxy]-5-(4-(2-methoxycarbonyI-vinyI)benzoyloxy]benzoyloxy]undecyl ester

1.23 g (1.44 mmol) of 3,5-dinitrobenzoic acid ll-[2-[4-pentylbenzoyloxy]--5-[4-(2-methoxycarbonyl-vinyl)benzoyloxy]benzoyloxy]undecyl ester and 0.31 g (5.76 mmol) of ammonium chloride were suspended in 15 ml of a mixture consisting of methanol : water 9:1. 1.88 g (28.8 mmol) of zinc were then added in one portions. After 0.5 hour at room temperature 20 ml of a mixture consisting of methanol : water 9:1 were added to the thick suspension. After a further 21 hours the reaction suspension was partitioned between dichloromethane and water. The resulting suspension was filtered, the organic phase was washed with a saturated sodium bicarbonate solution and repeatedly with water. The organic phase was then dried over sodium sulfate, filtered and concentrated by evaporation. Chromatography of the residue on 25 g of silica gel using toluene, toluene : ethyl acetate 9:1 and toluene : ethyl acetate 1:1 and subsequent twice crystallisation form a mixture of 5 ml ethyl acetate and 3.5 ml hexane yielded 0.434 g (38%) of 3,5-diaminobeiizoic acid 11 -[2-[4-pentylbenzoyloxy]-5-[4-(2-methoxycarbonylvinyl)benzoyloxy]benzoyl-oxy]undecyl ester as yellow crystals.


Example 4
Copolymer example,
Poly-[l-[ll-[5-[4-[(E)-2-inethoxycarbonylviuyl)benzoyloxy]-2-(4-propylbenzoyl-
oxy)benzoyloxy]undecyloxycarbonyl]-l-methylethylene-
-co-l-[ll-[5-[4-[((E)"2-metlioxycarbonylvinyI]benzoyloxy]-2-(4-pentylbeuzoyl-
oxy')benzoyloxy)undecyloxycarbonyl]-l-methylethylene]

Preparation can be carried out analogously to Example 1 using 0.89 g (1.22 mmol) (E)-5-[4-(2-methoxycarbonylvinyl)benzoyloxy]-2-(4-propylbenzoyloxy) benzoic acid ll-(2-methylacryloyloxy)undecyl ester, 0.10 g (0.13 mmol) (E)-5-[4-(2-methoxy-carbonylvinyl)benzoyloxy]-2-(4-pentylbenzoyloxy) benzoic acid 11 -(2-methyl-acryloyloxy)undecyl ester and (0.013 mmol) a,a'-azoisobutyronitrile yield poly--[ 1 -[ 11 -[5-[4-[(E)-2-methoxycarbonylvinyl]benzoyloxy]-2-(4-propylbenzoyloxy)-benzoyloxy]undecyloxycarbonyl]-l-methyl ethylene-co-l-[l l-[5-[4-[((E)-2-methoxy-carbonylvinyl]benzoyloxy]-2-(4-pentyllbenzoyloxy)benzoyloxy]undecyloxy-carbonyl]-1 -methylethylene].

The following copolymers can be synthesis in a analogous manner:
— Poly-[l-[ll-[5-[4-[(E)-2-methoxycarbonylvinyl]benzoyloxy]-2-(4-propyl-
benzoyloxy)benzoyloxy]undecyloxycarbonyl]-l-methylethylene-
-co-1 -[ 11 -[5-[4-[((E)-2-metlioxycarbonylvinyl]benzoyloxy]-2-(4-heptyl-benzoyloxy)benzoyloxy] undecyloxycarbonyl]-1 -melhylethylene]
— Pol y-[ 1 -[ 11 -[5-[4-[(E)-2-methoxycarbonyl vinyl]benzoyloxy]-2-(4-pentyl-benzoyloxy)benzoyloxy]undecyloxycarbonyl]-1 -methylethylene--co-l-[ll-[5-[4-[((E)-2-methoxycarbonylvinyl]benzoyloxy]-2-(4-heptyl-benzoyloxy)benzoyloxy]undecyloxycarbonyl]-1 -methylethylene]
— Poly-[l-[ll-[5-[4-[(E)-2-methoxycarbonylvinyl]benzoyloxy]-2-(4-propyl-benzoyloxy)benzoyloxy]undecyloxycarbonyl]-l-methylethylene--co-l-[ll-[5-[4-[((E)-2-methoxycarbonylvinyl]benzoyloxy]-2-(4-propyl-cyclohexanoyloxy)benzoyloxy]undecyloxycarbonyl]-l -methylethylene]
— Poly-[ 1 -[8-[5-[4-[(E)-2-methoxycarbonylvinyl]benzoyloxy]-2-(4-propyl-benzoyloxy)benzoyloxy]octyloxycarbonyl]-1 -methylethylene-co-l-[8-[5-[4-[((E)-2-methoxycarbonylvinyl]benzoyloxy3-2-(4-heptylbenzoyl-oxy)benzoyloxy]octyloxycarbonyl] -1-methylethylene]
— Poly-[ 1 -[8-[5-[4-[(E}-2-methoxycarbonylvinyl]beiizoyloxy]-2-(4-propylben2o yloxy)benzoyloxy]octyloxycarbonyl]-1-methylethylene-
-co-1 -[11 -[5-[4-[((E}-2-methoxycarbonylvinyl]beii2oyloxy]-2-(4-heptyl-benzoyloxy)benzoyloxy]undecyloxycarbonyl]-l-methylethylene]
Example 5
A two percent by weight solution S1 of the photoreactive polymer A was prepared using cyclopentanone as a solvent. The solution was stirred for 30 minutes at room temperature.

Photopolymer A:

Solution S1 was spin-coated at 2000 rpm onto two ITO (indium-tin oxide) coated glass plates, which were then dried for 10 minutes at 180 °C.
Both substrates were subsequently exposed for six minutes to the polarised ultraviolet light from a 200W high pressure mercury lamp. The intensity of the UV-light, measured in a surface perpendicular to the propagation of the light was 1.6 mW/cm2. A film polariser HNP'B by Polaroid was used to polarise the UV-light. During irradiation the substrates were tilted by 70o respective to the direction of the incoming light.
With the coated sides facing inwards, the two plates were assembled into a parallel cell, using a glass fibre of 20 μm as a spacer. The cell was immediately filled with a nematic liquid crystal mixture MLC 12000-000 (Merck) at a temperature only just above the nematic-isotropic transition temperature of 89 °C. After filling the cell was slowly cooled.
Using the crystal rotation technique, the pretilt angle in the above liquid crystal cell was .determined as 88°.


Example 6
A mixture MLCP was prepared comprising the following liquid crystalline diacrylate monomers:



In addition to the diacrylate monomers, photoinitiator IRGACURE™ 369 from Ciba SC as well as BHT which served as an inhibitor were added to the mixture. Thus the composition of mixture MLCP was as follows:

Monl 77 wt. %
Mon2 14.5 wt. %
Mon3 4.7 wt. %
IRGACURE™ 369 1.9 wt. %
BHT 1.9 wt. %

Finally, the solution S(LCP) resulted from dissolving 20 wt. % of mixture MLCP IN anisole.
Like in example 5, solution S1 was spincoated on a glass plate, dried and subsequently exposed to the polarised UV-light, having an incidence angle of 70°. Then diacrylate solution S(LCP) was spin-coated at 800 rpm for 2 minutes on top of the irradiated LPP-layer. To cross-link the diacrylates the plate was exposed to isotropic UV-light under nitrogen atmosphere for 5 minutes.
Between crossed polarisers it was found that the LCP-layer was well aligned according the direction of the LPP-irradiating polarised UV-light. From the strong asymmetric viewing angle dependence of the LCP-retarder it was concluded that the optical axis of the LCP-layer was highly tilted.
To estimate the mean tilt angle of the optical axis, the effective optical anisotropy An, when looked perpendicularly through the layer was determined from measurements of the layer thickness d and the retardation And as Anefr= 0.033. From the known An - 0.13 of the LCP material the mean tilt angle the opticla axis was calculated as 58o


WE CLAIM:
1. A photoactive polymer of the general formula I:

5
in which:
P is a photoactive group which can photoisomerise and/or
photodimerise;
B represents an aromatic or alicyclic group which is unsubstituted or
substituted by fluorine, chlorine or cyano, or by a cyclic, straight-chain or branched alkyl residue which is unsubstituted, mono-substituted by cyano or halogeno, or poly-substituted by halogeno, having 1 to 18 carbon atoms and wherein one or more CH.2 groups may independently be replaced by -0-, -CO-, -CO-O-,
-0-CO-, -Si(CH3)2-0-Si(CH3)2-, -NR2-, -NR2-CO-, -CO-NR2-,
-NR2-CO-0-, -O-CO-NR2-, -NR2-CO-NR2-, -CH=CH-, -OC-.
-0-CO-0-, with the proviso that oxygen atoms are not directly
attached to each other, and wherein R2 represents a hydrogen atom
or lower alkyl, or B further repiesents a nitrogen atom or -CR2-;
A, C, D each independently of the other represents an aromatic or alicyclic
group which is unsubstituted or substituted by fluorine, chlorine,
cyano, or by a cyclic, straight-chain or branched alkyl residue
which is unsubstituted, mono-substituted by cyano or halogeno, or
poly-substituted by halogeno, having 1 to 18 carbon atoms and
wherein one or more Chb groups may independently be replaced
by -0-, -CO-, -CO-O-, -0-CO-, -Si(CH3)2-0-Si(CH3)2-, -NR2-,
NR2-CO-, -CO-NR2-, -NR2-CO-0-, -O-CO-NR2-,


-NR2-CO-NR2-, -CH=CH-, -C=C-, -O-CO-O-, with the proviso that oxygen atoms are not directly attached to each other, and wherein R2 represents a hydrogen atom or lower alkyl;
M represents a repeating monomer unit in a homo- or copolymer;
S1, S2, S3, S4, S5 represent a single covalent bond or a spacer unit, comprising a straight-chain or branched alkylene residue which is unsubstituted, mono-substituted by cyano or halogeno, or poly-substituted by halogeno, having 1 to 24 carbon atoms, wherein one or more CH2 groups may independently be replaced by -0-, -CO-, -CO-O-, -O-CO-, -Si(CH3)2-0-Si(CH3)2-, -NR2-, -NR2-CO-, -CO-NR2-, -NR2-CO-0-, -0-CO-NR2-, -NR2-CO-NR2-, -CH=CH-, -C=C-, -O-CO-O-, with the proviso that oxygen atoms are not directly attached to each other, and wherein R2 represents a hydrogen atom or lower alkyl;
n1, n2 are each independently a positive integer up to 2 with the proviso
that n1 + n2 ≤ 2;
R1 is a hydrogen atom, or a straight-chain or branched alkyl residue
which is unsubstituted, mono-substituted by cyano or halogeno, or poly-substituted by halogeno, having 1 to 18 carbon atoms, wherein one or more CH2 groups may independently be replaced
by -0-, -CO-, -CO-O-, -O-CO-, -Si(CH3)2-0-Si(CH3)2-, -NR2-,
-NR2-CO-, -CO-NR2-, -NR2-CO-0-, -O-CO-NR2-,
-NR2-CO-NR2-, -CH=CH-, -C=C-, -O-CO-O-, with the proviso that oxygen atoms are not directly attached to each other, and wherein R2 represents a hydrogen atom or lower alk/1.
-

2. A polymer as claimed in claim 1 in which group P is a group which undergoes a photocyclisation and has the general formula 11 and 111:

wherein the broken line indicates the point of linkage to S1 and wherein:
E represents phenylene which is unsubstituted or substituted by fluorine,
chlorine or cyano, or by a cyclic, straight-chain or branched alkyl residue which is unsubstituted, mono-substituted by cyano or halogeno, or poly-substituted by halogeno, having 1 to 18 carbon atoms and wherein one or more CH2 groups may independently be replaced by
-0-, -CO-, -CO-O-, -O-CO-, -Si(CH3)2-0-Si(CH3)2-, -NR2-,
-NR2-CO-, -CO-NR2-, -NR2-CO-0-, -O-CO-NR2-, -NR2-CO-NR2-,
-CH=CH-, -OC-, -O-CO-O-, with the proviso that oxygen atoms are
not directly attached to each other, and wherein R2 represents a
hydrogen atom or lower alkyl, or E further represents
pyrimidine-2,5-diyl, pyridine-2,5-diyl, 2,5-thiophenylene,
2,5-furanylene, or 1,4- or 2,6-naphthylene;
F represents -OR4, -NR5R6, or an oxygen atom linked to ring E in the
ortho position to form a coumarin unit wherein R4, R and R are a hydrogen atom or a cyclic, straight-chain or branched alkyl residue which is unsubstitu.ed, mono-substituted by halogeno, or poly--substituted by halogeno, having 1 to 18 carbon atoms and wherein one or more CH2 groups may independently be replaced by -0-, -CO-, -CO-O-, -O-CO-, -CH=CK-, with the proviso that oxygen atoms are not directly attached to each other, or R"1 and R6 are linked together to form an alicyclic ring with 5 to 8 atoms;


X, Y each independently of the other represents hydrogen, fluorine, chlorine,
cyano, alkyl optionally substituted by fluorine having from 1 to 12 carbon atoms in which optionally one or more non-adjacent CH2 groups are replaced by -0-, -CO-0-, -O-CO- and/or -CH=CH-;
R3 is a hydrogen atom, or a straight-chain or branched alkyl residue which
is unsubstituted, mono-substituted by cyano or halogeno, or poly-substituted by halogeno, having 1 to 18 carbon atoms, wherein one or more CH2 groups may independently be replaced by -0-, -CO-,
-CO-O-, -O-CO-, -Si(CH3)2-0-Si(CH3)2-, -NR2-, -NR2-CO-, -CO-NR2-, -NR2-CO-0-, -O-CO-KR2-, -NR2-CO-NR2-, -CH=CH-, -OC-, -O-CO-O-, with the proviso that oxygen atoms are not directly attached to each other, and wherein R2 represents a hydrogen atom or lower alkyl.
3. A polymer as claimed in claim 2 in which group P has the general formula IV and V:

wherein the broken line indicates the point of linkage to S1 and wherein R3 has the
meaning given under formula II and III in claim 2;
F represents -OR4 or -NR5R6, wherein R4 and R1 are a cyclic, straight-
chain or branched alkyl residue which unsubstituted, mono-substhuted by halogeno, or poly-substituted by halogeno, having 1 to 18 carbon atoms and wherein one or more CH2 groups may independently be replaced by -O- or-CH=CH-, with the proviso that oxygen atoms are not directly attached to each other, and wherein R6 is a hydrogen atom or a cyclic, straight-chain or branched aikyi residue which is


unsubstituted, mono-substituted by halogeno, or poly-substituted by
halogeno, having 1 to 18 carbon atoms and wherein one or more CH2
groups may independently be replaced by -O- or-CH=CH-, with the
proviso that oxygen atoms are not directly attached to each other, or R'"1
and R6 link together to form an alicyclic ring with 5 to 8 atoms; and
E represents phenylene which is unsubstituted or substituted by a cyclic,
straight-chain or branched alkyl residue which is unsubstituted, mono-substituted by halogeno, or poly-substituted by halogeno, having 1 to 12 carbon atoms and wherein one or more CH2 groups may independently be replaced by -0-, -CO-, -CO-O-, -OCO, -CH=CH-, -OC-, with the proviso that oxygen atoms are not directly attached to each other, or E further represents pyrimidine-2,5-diyl, pyridine-2,5-diyl, 2,5-thiophenylene, 2,5-furanylene, 1,4- or 2,6-naphthylene.
4. A polymer as claimed in claim 3 in which group P has the general formula IV
wherein:
E represents phenylene which is unsubstituted or substituted by a
straight-chain or branched alkyl residue which is unsubstituted 01 mono- or polysubstituted by fluorine, having 1 to 6 carbon atoms and wherein one or more CH2 groups may independently be replaced by -0-, -CO-, -CO-O-, -O-CO, -CH=CH-, with the proviso that oxygen atoms are not directly attached to each other, or E further represents pyrimidine-2,5-diyl, pyridine-2,5-diyl, 2,5-furanylene, 1,4- or 2,6-naphthylene;
F represents -OR4 or -NHR5, wherein R4 and R5 are a cyclic,
straight-chain or branched alkyl residue which is unsubstituted or mono- or polysubstituted by fluorine, having 1 to 18 carbon atoms and wherein one or more CH2 groups may independently be replaced by -0-, with the proviso that oxygen atoms are not directly attached to each other.


5. A polymer as claimed in any one of claims 1 to 4 in which B represents a aromatic or alicyclic group and where n1 + n2 = 0 or 1.
6. A polymer as claimed in any one of claims 1 to 4 in which B represents a group -CR2- and where 0 ≤ n1 + n2 ≤ 2.
7. A polymer as claimed in any one of claims 1 to 4 in which the polymer is optically inactive.
8. A polymer as claimed in any one of claims 1 to 5 in which group B is aromatic which is unsubstituted or substituted by fluorine, chlorine or cyano, or by a cyclic, straight-chain or branched alkyl residue which is unsubstituted, mono-substituted by cyano or halogeno, or poly-substituted by halogeno, having 1 to 18 carbon atoms and wherein one or more CH2 groups may independently be replaced by -0-, -CO-, -CO-O-, -O-CO-, -CH-CH-, with the proviso that oxygen atoms are not directly attached to each other, or B further represents -CR2-, wherein R2 represents hydrogen atom or lower alkyl.
9. A polymer as claimed in claim 8 in which group B is a 1,2,5-benzenetriyl or 1,3,5-benzenetriyl group which is unsubstituted or substituted by fluorine and where the spacer group S5 is in position 1.
10. A polymer as claimed in any preceding claim in which groups A, C and D are phenylene which is unsubstituted or substituted by fluorine, chlorine, cyano, or by a cyclic, straight-chain or branched alkyl residue which is unsubstituted, mono-substituted by cyano or halogeno, or poly-substituted by halogeno, having 1 to 12 carbon atoms, wherein one or more CH2 groups may independently be replaced by -0-, -CO-, -CO-O-, -O-CO-, -CH=CH-, -CsC- or -O-CO-O- with the proviso that oxygen atoms are not directly attached to each other, or A, C and D further represents cyclohexane-l,4-diyl, pyrimidine-2,5-diyl, pyridine-2,5-diyl, 1,4- or 2,6-naphthylene.


11. A polymer as claimed in claim 10 in which groups A, C and D are phenylene, which is unsubstituted or substituted by fluorine, straight-chain or branched alkyl residue which is unsubstituted or mono- or polysubstituted by fluorine, having 1 to 8 carbon atoms, wherein one or more CH2 groups may independently be replaced by -0-, -CO-, -C0-0-, -O-CO- or -CH=CH- with the proviso that oxygen atoms are not directly attached to each other, or A, C and D further represents cyclohexane-l,4-diyl, pyrimidine-2,5-diyl, pyridine-2,5-diyl or 2,6-naphthylene.
12. A polymer as claimed in any preceding claim in which S', S2, S3, S4 and S5 represent a single covalent bond or a straight-chain or branched alkylene grouping represented by -(CH2)r,.optionally mono- or poly-substituted by fluorine, chlorine or
cyano, or a chain of the formula -Ll-(CH2)rL2- or -Ll-(CH2)r-L2-(CH2)s-L3-,
wherein L',L2 and L3 each independently of the others represent a single bond or linking functional groups such as -0-, -CO-O-, -O-CO-, -NR2-, -NR2-CO-5 -CO-NR2-,
-NR2-CO-0-, -O-CO-NR2, -NR2-CO-NR2-, -CH=CH-, -CSC-, -O-CO-O-, -Si(CH3)2-0-Si(C})2-, wherein R represents hydrogen atom or lower alkyl and r and s are each an integeHr from 1 to 20, with the proviso that r + s ≤ 24 and with the proviso that in the case where the repeating monomer unit M is linked to Ss via a nitrogen atom or a oxygen atom which is by definition part of M, L1 signifies a single bond.
13. A polymer as claimed in claim 12 in which Sl, S2, S3, S4 and S5 are a
straight-chain or branched alkylene grouping, represented by -(CH2)r, and also
-(CH2)rO-, -(CH2)rCO, -(CH2)rCO-0-, -(CH2)r-0-CO-, (CH^-CO-NR2-,
-(CH2)r-NR2-CO-, -(CH2)rNR2-. -0-(CH2)r, -CO-0-(CH2)r, -0-CO-(CH2)r,
-NR2-CO-(CH2)r, -CO^NR2^CH2)r-J -l\U2-(CH2)r> -0-(CH2)r-CO-0-,
-0-(CH2)rO-CO-, -0-(CH2)rCO-NR2-, -0-(CH2)rNR2-, -0-(CH2)rO-,
-0-(CH2)rNR2-CO-, -NR2-(CH2)r-CO-0-, , -NR2-(CH2)rO-, -NR2-(CH2)rNR2-,
-NR2-(CH2)r-0-CO-, -CO-NR2-(CH2)rO , -CO-NR2-(CH2)rNR2-,
-CO-NR2-(CH2)rO-CO-, -0-CO-(CH2)rCO-, -0-CO-(CH2)rO-,
-0-CO-(CH2)rNR2-, -0-CO-(CH2)r CO-0-, -0-CO-(CH2)rCO-NR2-,
-0-CO-(CH2)r-NR2-CCS -(CH2)rO-(CH2)s-, -(CH2)rCO-0-(CH2)r,


-(CH2)r-0-CO-(CH2)r, -(CH2)rNR2-CO-(CH2)s-, -(CH2)r-NR2-CO-0-(CH2)s-,
-(CH2)r-0-(CH2)s-0-, -(CH2)rCO-0-(CH2)s-0-, -(CH2)r-0-CO-(CH2)s-0-,
-(CH2)rNR2-CO-(CH2)s-0-, -(CH2)rNR2-CO-0-(CH2)s-0-, -0-(CH2)rO-(CH2)s-1
-0-(CH2)r-CO-0-(CH2)s-, -0-(CH2)rNR2-CO-(CH2)s-,
-0-(CH2)r-NR2-CO-0-(CH2)s-, -0-(CH2)r-CO-0-(CH2)s-0-,
-0-(CH2)r-0-(CH2)s-0-, -0-(CH2)rNR2-CO-(CH2)s-0-,
-0-(CH2)r-NR2-CO-0-(CH2)s-0-, -CO-0-(CH2)r-0-(CH2)s-,
-CO-0-(CH2)r-0-(CH2)s-0-, wherein r and s are each an integer from 1 to 20, with the proviso that r + s ≤ 21, and wherein R2 represents hydrogen or lower alkyl.
14. A polymer as claimed in claim 13 in which S1, S2, S3, S4 and S5 are a
straight-chain alkylene grouping represented by -(CH2)r, and also -(CH2)r-0-,
-(CH2)rCO-0-, -(CH2)r-0-CO-, -(CH2)r-CO-NH-, -(CH2)r-NH-CO-, -0-(CH2)r,
-CO-0-(CH2)r, -CO-NH-(CH2)r, -0-CO-(CH2)r-, -0-CO-(CH2)r-CO-0-,
-0-(CH2)r-0-CO-, ~0-(CH2)rCO-NH-, -0-(CH2)r-NH-CO-, -C0-O-(CH2)r-0-,
-CO-NH-(CH2VO-, -Q-(CH2)1-0-, -(CH2)rNH-CO-(CH2)s-,
-(CH2)r-NH-CO-0-(CH2)s-, -(CH2)r-0-(CH2)s-0-, -(CH2)rNH-CO-(CH2)s-0-,
-(CH2)r-NH-CO-0-(CH2)s-0-, -0-(CH2)r-NH-CO-(CH2)s-, -0-(CH2)r-0-(CH2)s-0-,
-0-CO-(CH2)r-0-(CH2)s-0-, -CO-0 ('CH2)r-O-(CH2)s-0 ,
-0-(CH2)rNH-CO-(CH2)s-0-, -0-CO-(CH2)rNH-CO-(CH2)s-0-, wherein r and s are each an integer from 2 to 12 and the sum of r + s ≤15.
15 A polymer as claimed in any preceding claim in which R1 is a hydrogen atom, or a straight-chain or branched alkyl residue which is unsubstitutsd or halogeno or polyhalogeno-substituted, having 1 to 12 carbon atoms, wherein one or more CH2 groups may independently be replaced by -O-, -CO-, -CO-0-, -0-CO-, -CH=CH- or -CsC-, with the proviso that oxygen atoms are not directly attached to each other.
16. A polymer as claimed in claim 15 in which R1 is a straight-chain or branched alkyl residue, having 1 to 8 carbon atoms, wherein one or more CH2 groups are each


independently replaced by -0-, -CO-, -CO-O- or -O-CO- or -CH=CH-, with the proviso that oxygen atoms are not directly attached to each other.

17. A polymer as claimed in any preceding claim in which the repeating monomer unit M is acrylate, methacrylate, a styrene derivative, an imide, am amic acid or an ester thereof or an amidimide.
18. A polymer as claimed in any preceding claim in which the imide unit M from which the main chain is synthesised is one or more groups of the general formulae III, V and VII and/or the analogous amic acid groups and amic acid ester groups of the general formulae IV, VI and VIII:




in which the broken line symbolises the linkage to S5 and wherein:

Tl
T2, T3

represents the tetravalent organic radical of a tetracarboxylic acid dianhydride after formal removal of the two -CO-O-CO- groups, the four valencies of which are distributed between four different carbon atoms of the radical;
each independently of the other represents an aromatic or alicyclic trivalent group, the three valencies of which are distributed between three different carbon atoms of the group, the group being unsubstituted or substituted by fluorine, chlorine, cyano, by a cyclic, straight-chain or branched alkyl residue which is unsubstituted, mono-substituted by halogeno, or poly-substituted



by halogeno, having 1 to 18 carbon atoms and wherein one or more CH2 groups may independently he replaced by -0-, -CO-, -CO-O-, -O-CO-, -CH-CH-, -C=C-, with the proviso that oxygen atoms are not directly attached to each other;
S6, S7, S8, S9, S10 represent a single covalent bond or a spacer unit, comprising a straight-chain or branched alkylene residue which is unsubstituted, mono-substituted by cyano or halogeno, or poly-substituted by halogeno, having 1 to 24 carbon atoms, wherein one or more CH2 groups may independently be replaced by -0-, -CO-, -CO-O-, -O-CO-, -Si(CH3)2-0-Si(CH3)2, -NR2-, -NR2-CO-, -CO-NR2-, -NR2-CO-0-, -O-CO-NR2-, -NR2-CO-NR2-, -CH=CH-, -C=C-, -O-CO-O-, with the proviso that oxygen atoms are not directly attached to each other, and wherein R2 represents hydrogen atom or lower alkyl;
J represents an aromatic or alicyclic divalent, trivalent or tetravalent
group, the valencies of which are distributed between different atoms of the group, which is unsubstituted or substituted by fluorine, chlorine, cyano, by a cyclic, straight-chain or branched alkyl residue which is unsubstituted or mono cyano, or halogeno or polyhalogeno-substituted, having 1 to 18 carbon atoms and wherein one or more CH2 groups may independently be replaced by -0-, -CO-, -CO-O-, -O-CO-, -CH=CH-, -C^C-, with the proviso that oxygen atoms are not directly attached to each other, or J further represents a nitrogen atom or -CR2- and wherein R2 represents a hydrogen atom or lower alkyl;
K represents the radical of an aliphatic, alicyclic or aromatic diamine
after formal removal of the two amino groups; and
G represents hydrogen atom or a monovalent organic group, derived
from an alcohol after formal removal of the hydroxy group.


19. A polymei as claimed in claim 18 in which the groups T2 and T3 are trivalent aromatic or carbocyclic groups, the three valencies of which are so distributed between three different carbon atoms that two of those valencies are located at adjacent carbon atoms.
20. A polymer as claimed in claim 19 in which the groups T2 and T3 are trivalent benzene derivatives, the three valencies of which are so distributed between three different carbon atoms that two of those valencies are in the ortho position relative to one another.
21. A polymer as claimed in any one of claims 18 to 20 in which S6 is a straight-chain or branched alkylene grouping, represented by -(CH2)r> and also -(CH2)r-0-, -(CH2)r-CO-, -(CH2)r-CO-0-, -(CH2)r-0-CO-, -(CH2)r-CO-NR2-, -(CH2)r-NR2-CO-, -(CH2)r-NR2-, -(CH2)rO-(CH2)s-, -(CH2)rCO-0-(CH2)s-, -(CH2)r-0-CO-(CH2)s-, -(CH2)rNR2-CO-(CH2)s-, -(CH2)r-NR2-CO-0-(CH2)s-, -(CH2)rO-(CH2)rO-, -(CH2)r-CO-0-(CH2)s-0-, -(CH2)rO-CO-(CH2)s-CK -(CH2)rNR2-CO-(CH2)s-0-, -(CH2)r-NR2-CO-0-(CH2)s-0-,-(CH2)r-0-(CH2)s-CO-0-,-(CH2)r-0-(CH2)s-0-CO-, wherein r and s are each an integer from 1 to 20, with the proviso that r + s 22. A polymer as claimed in any one of claims 18 to 21 in which S7 and S10 are a straight-chain or branched alkylene grouping, represented by -(CH2)r-, and also -0-(CH2)r-, -CO-(CH2)r-, -CO-0-(CH2)r-. -0-CO-(CH2)r, -NR2-CO-(CH2)r-, -NR2-(CH2)r-, -CO-NR2-(CH2)r-, -NR2-CO-(CH2)r, -0-(CH2)r-0-(CH2)s-, -(CH2)r-CO-0-(CH2)s-, -(CH2)r-0-CO-(CH2)s-, -(CH2)r-NR2-CO-(CH2)s., -(CH2)r-NR2-CO-0-(CH2)s-, -0-(CH2)rO-(CH2)s-, -0-(CH2)rCO-0-(CH2)s-, -0-(CH2)r-0-CO-(CH2)s-, -0-(CH2)rNR2-CO-(CH2)s-, -0-(CH2)rNR2-CO-0-(CH2)s-,-0-CO-(CH2)rO-(CH2),-,-CO-0-(CH2)rO-(CH2)s-, wherein r and s are each an integer from 1 to 20, with the proviso that r + s

19. A polymer as claimed in claim 18 in which the groups T2 and T3 are trivalent aromatic or carbocyclic groups, the three valencies of which arc so distributed between three different carbon atoms that two of those valencies are located at adjacent carbon atoms.
20. A polymer as claimed in claim 19 in which the groups T2 and T3 are trivalent benzene derivatives, the three valencies of which are so distributed between three different carbon atoms that two of those valencies are in the ortho position relative to one another.
21. A polymer as claimed in any one of claims 18 to 20 in which S6 is a straight-chain or branched alkylene grouping, represented by -(CH2)r, and also -(CH2)r-0-, -(CH2)r-CO-, -(CH2)rCO-0-, -(CH2)r-0-CO-, -(CH2)r-CO-NR2-, -(CH2)r-NR2-CO-, -(CH2)r-NR2-, -(CH2)r-0-(CH2)s-, -(CH2)r-CO-0-(CH2)s-, -(CH2)r-0-CO-(CH2)r, -(CH2)r-NR2-CO-(CH2)s-, -(CH2)r-NR2-CO-0-(CH2)s-, -(CH2)r-0-(CH2)s-0-, -(CH2)r-CO-0-(CH2)s-0-, -(CH2)rOCO-(CH2)s-0-, -(CH2)rNR2-CO-(CH2VO-, -(CH2)r-NR2-CC-0-(CH2)s-0-,-(CH2)rO-(CH2)s-CO-0-, -(CH2)rO-(CH2)s-0-CO, wherein r and s are each an integer from 1 to 20, with the proviso that r + s 22. A. polymer as claimed in any one of claims 18 to 21 in which S7 and S10 are a straight-chain or branched alkylene grouping, represented by -(CH2)t-, and also
-0-(CH2)r, -CO(CH2)r-, -CO-0-(CH2)r, -0-CO-(CH2)r, -NR2-CO-(CH2)r,
-NR2-(CH2)r, -CONR2-(CH2)r-, -NR2-CO-(CH2)r, -0-(CH2)r-0-(CH2)5-)
-(CH2)r-CO-0-(CH2)s-, -(CH2)r-0-CO-(CH2)s-, -(CH2)r-NR2-CO-(CH2)s-,
-(CH2)rNR2-CO-0-(CH2)s-, -0-(CH2)rO-(CH2)s-, -0-(CH2)rCO-0-(CH2V,
-0-(CH2)r-0-CO-(CH2)s-, -0-(CH2),-NR2-CO-(CH2)s-,
-0-(CH2)rNR2-CO-0-(CH2)s-,-0-CO-(CH2)rO-(CH2)3-J-CO-0-(CH2)rO-(CH2)s-wherein r and s are each an integer from 1 to 20, with the proviso that r + s ≤ 21 and wherein R2 represents hydrogen or lower alkyl.


WO 00/59966

PCT/I BOO/00349

23. A polymer as claimed in any one of claims 18 to 22 in which" S8 and S9 are a
straight-chain or branched alkylene grouping, represented by -(CH2V, and also
-(CH2)r-0-, -(CH2)r-CO-, -(CH2)r-CO-0-, -(CH2)r-0-CO-, -(CH2)r-CO-NR2-,
-(CH2)rNR2.CO-, -(CH2)rNR2-, -0-(CH2)r, -CO-0-(CH2)r, -O CO-(CH2)r,
-MR2-CO-(CH2)r, -CO-NR2-(CH2)r, -NR2-(CH2)r, -0-(CH2)rCO-0-,
-0-(CH2)r-0-CO-, -0-(CH2)r-CO-NR2-, -0-(CH2)rNR2-, 0-(CH2)rO-,
-0-(CH2)rNR2-CO-) -NR2-(CH2)T-C0-O, -NR2-(CH2)r-0-, -NR2-(CH2)rNR2-,
-NR2-(CH2)r-0-CO-, -CO-NR2-(CH2)rO-, -CO-NR2-(CH2)rNR2-,
-CO-NR2-(CH2)r-0-CO-, -0-CO-(CH2)rCO-, -0-CO-(CH2)r-0-,
-0-CO-(CH2)rNR2-, -0-CO-(CH2)r-CO-0-, -0-CO-(CH2)rCO-NR2-,
-0-CO-(CH2)rNR2-CO-, ~(CH2)r-0-(CH2)s-, -(CH2)r-CO-0-(CH2)s-,
-(CH2)r-0-CO-(CH2)s-, -(CH2)r-NH2-CO-(CH2)s-) -(CH2)r-NR2-CO-0-(CH2)s-,
-(CIl2)r-0-(CH2)s-O-, -(CH2)r-CO-0-(CH2)s-0-, -(CH2)rO-CO-(CH2)s-0-,
-(CH2)rNR2-CO-(CH2)s-0-, -(CH2)r-NR2-CO-0-(CH2)s-0-, -0-(CH2)r-0-(CH2)s-,
-0-(CH2)r-CO-0-(CH2)s-, -0-(CH2)rNR2-CO-(CH2)s-,
-0-(CH2)rNR2-CO-0-(CH2)s-, -0-(CH2)r-C0-0-(CH2)s-O,
-0-(CH2)rO-(CH2)s-0-, -0-(CH2VNR2-CO-(CH2)s-0-,
-0-(CH2)rNR2"CO-0-(CH2)s-0-, -CO-0-(CH2)r-0(CH2)s-,
-CO-0-(CH2)rO-(CH2)s-0-, wherein r and s are each an integer from 1 to 20, with the proviso that r + s ≤ 21, and wherein R2 represents hydrogen or lower alkyl.
24. A polymer according to any one of claims 1 to 23, characterised in that the polymer is a copolymer.
25. A polymer according to any one of claims 18 to 23 characterised in that at least 50% of the monomer building blocks forming the main chain are linked to one or two side-chains, which comprises the whole of formula I except M.


26. A polyines" according to claim 25, characterised in thai al least 70% of ihe monomer building blocks forming ihe main chain arc linked lo one or two of the side-chains.
27. A polymer according lo any one of claims 18 lo 23, characterised in that the monomer building blocks carrying a side-chain are each linked to only one side-chain.
28. A polymer as claimed in any one of claims 18 to 27 which contain one or more groups of formulae IV, VI or VUl, m which G is hydrogen.
29. A polymer as claimed in any preceding claim which contains as an additive a silanc-containing compound and/or an cpoxy-containing crosslinking agent.
30. A polymer as claimed in any preceding claim which contains as an additive a photoscnsiliscr, a photoradical generator and/or a calionic photoinilialor.
31. A polymer as claimed in any preceding claim in mixture with one or more other polymers, oligomers, monomers, photoactive polymers, photoactive oligomers and/or photoactive monomers.
32. A polymer as claimed in any preceding claim applied to a support and, after any imidisation step which may be necessary, crosslinkcd by irradiation with linearly polarised light.
33. An orientation layer for liquid crystals, whinh comprises a polymer as claimed in claim 1 that is crosslinked by irradiation with linearly poia ized light.
Dated this 4th day of September, 2001.
FOR ROLIC AG By their Agent



(MANISH SAURASTRIKRISHNA
KRISHNA & SAURASTR

Documents:

in-pct-2001-01051-mum-cancelled pages(06-02-2006).pdf

in-pct-2001-01051-mum-claims(granted)-(04-09-2001).doc

in-pct-2001-01051-mum-claims(granted)-(06-02-2006).pdf

in-pct-2001-01051-mum-correspondence(06-02-2006).pdf

in-pct-2001-01051-mum-correspondence(ipo)-(29-06-2005).pdf

in-pct-2001-01051-mum-form 1(04-09-2001).pdf

in-pct-2001-01051-mum-form 13(22-02-2005).pdf

in-pct-2001-01051-mum-form 19(27-01-2004).pdf

in-pct-2001-01051-mum-form 1a(22-06-2004).pdf

in-pct-2001-01051-mum-form 2(granted)-(04-09-2001).doc

in-pct-2001-01051-mum-form 2(granted)-(06-02-2006).pdf

in-pct-2001-01051-mum-form 24(02-08-2005).pdf

in-pct-2001-01051-mum-form 3(04-09-2001).pdf

in-pct-2001-01051-mum-form 3(22-06-2004).pdf

in-pct-2001-01051-mum-form 5(04-09-2001).pdf

in-pct-2001-01051-mum-form-pct-ipea-409(06-02-2006).pdf

in-pct-2001-01051-mum-petition under rule 137(22-06-2004).pdf

in-pct-2001-01051-mum-power of attorney(22-11-2000).pdf


Patent Number 207339
Indian Patent Application Number IN/PCT/2001/01051/MUM
PG Journal Number 30/2007
Publication Date 27-Jul-2007
Grant Date 06-Jun-2007
Date of Filing 04-Sep-2001
Name of Patentee ROLIC AG
Applicant Address CHAMERSTRASSE 50, 6301 ZUG, SWITZERLAND
Inventors:
# Inventor's Name Inventor's Address
1 HUBERT SEIBERLE BODENSEESTRASSE 1, 79576 WEIL AM RHEIN, GERMANY
2 GUY MARCK 16A, RUE DU KAEGY, 68440 SCHLIERBACH, FRANCE
3 OLIVIER MULLER 15,RUE PRINCIPALE, 68610, LAUTENBACH, FRANCE.
PCT International Classification Number C08F 246/00
PCT International Application Number N/A
PCT International Filing date 2000-03-27
PCT Conventions:
# PCT Application Number Date of Convention Priority Country
1 99 07 801.6 1999-04-04 GB