Title of Invention	A PROCESS FOR PREPARING A POLYAMIDE
Abstract	The invention relates to a process for preparing a polyamide by reaction of at least one arninonitrile with water, which comprises: (1) preparing a reaction mixture by reacting at least one aminonitrile with water in a molar ratio of from 1: 1 to 1 :30 at a temperature of from 100 to 360°C and a pressure of from 4 to 30xi06 Fa, (2) subsequently reacting the reaction mixture obtained in step (1) at a temperature of from 150 to 400°C and a pressure which is lower than the pressure in step (1), whereby the temperature and the pressure are adapted so that a2) a fIrst gas phase, and b2) a fIrst liquid or a fIrst solid phase or a mixture of fIrst solid and fIrst liquid phase is formed, and separating the fIrst gas phase (av from the fIrst liquid and/or solid phase (bV, and (3) preparing the polyamide by reacting the separated fIrst liquid and/or solid phase (b2) with a gaseous or liquid phase comprising water at a temperature of from 150 to 360°C and a pressure of from 0.1 to 30xl06 Fa.

Title of Invention

A PROCESS FOR PREPARING A POLYAMIDE

Abstract

The invention relates to a process for preparing a polyamide by reaction of at least one arninonitrile with water, which comprises: (1) preparing a reaction mixture by reacting at least one aminonitrile with water in a molar ratio of from 1: 1 to 1 :30 at a temperature of from 100 to 360°C and a pressure of from 4 to 30xi06 Fa, (2) subsequently reacting the reaction mixture obtained in step (1) at a temperature of from 150 to 400°C and a pressure which is lower than the pressure in step (1), whereby the temperature and the pressure are adapted so that a2) a fIrst gas phase, and b2) a fIrst liquid or a fIrst solid phase or a mixture of fIrst solid and fIrst liquid phase is formed, and separating the fIrst gas phase (av from the fIrst liquid and/or solid phase (bV, and (3) preparing the polyamide by reacting the separated fIrst liquid and/or solid phase (b2) with a gaseous or liquid phase comprising water at a temperature of from 150 to 360°C and a pressure of from 0.1 to 30xl06 Fa.

Full Text	The present invention relates to a novel process for preparing polyamides from aminonitriles and water at elevated temperature and elevated pressure. US 2 245 129 describes a batchwise two-step preparation of polycaprolactam from ω-aminocapronitrile ("ACN") and water at a temperature within the range from 150 to 300°C, governed by a specific temperature program as a function of the amount of water added, and a pressure of not more than 30 bar. The disadvantages of this process are the long reaction times (20 h in step 1), the low viscosity of the resulting polycaproplactam and the high level of volatile bases (essentially primary acid amides) compared with a polycaprolactam j prepared from caprolactam. DE-C 35 34 817, US 4 568 736 and US 4 629 776 partly solve the problems j described in US 2 245 129 by the use of phosphorus- and sulfur-containing catalysts. The use of the catalysts mentioned improves the low space-time yield of the process described in US 2 245 129. However, the level of volatile bases in all the products prepared by the abovementioned processes is still too high, so that the polyamides are difficult to process and have a reduced carboxyl end group number. The stoichiometric discrepancy between the amino and carboxyl end groups in the products of the abovementioned processes is responsible for their showing an insufficient degree of polymerization and a slow increase in molecular weight during tempering. Furthermore, complete removal of the catalysts is virtually impossible, so that the chemical and physical behavior of the polymers prepared using the catalysts, such as type and quantity of end groups or snap-off behavior during spinning, is adversely affected. EP-A 0 479 306 proposes, in relation to the reaction of ACN with water to give polycaproiactam, to remove ammonia and water continuously, by decompressing, once a reaction temperature from 200. to 260°C has been attained and at the same time to add water continuously while selecting a pressure within the range from 14 to 24 x 106 Pa (14 to 24 bar). EP-A 65 291 describes a continuous process for preparing nylon 66 from dinitriles and diamines. The molecular weight builds up via polycondensation. Caprolactam does not occur as an intermediate, which it does, however, in the polymerization of ACN. Thus, because of the different reaction mechanisms, it was not possible to apply the process mentioned in EP-A 65 291 to the present problem. It is an object of the present invention to provide a process for preparing polyamides from aminonitriles with improved hydrolysis of the reactants, especially of the acid amide groups, and thus a higher carboxyl end group content. The molecular weight increase during the polymerization and the temperability of the product are improved in this way, compared with prior art processes. We have found that this object is achieved by a process for preparing a polyamide by reaction of at least one aminonitrile with water, which comprises the following steps: (1) reacting at least one aminonitrile with water at a temperature from 100 to 360°C and a pressure from 0.1 to 35 x 106 Pa to obtain a reaction mixture, (2) further reacting the reaction mixture at a temperature from 150 to 400°C and a pressure which is lower than the pressure in step 1, the temperature and the pressure being selected so as to obtaih a first gas phase and a first liquid or a first solid phase or a mixture of first solid and first liquid phase, and separating the first gas phase from the first liquid or the first solid phase or from the mixture of first liquid and first solid phase, and (3) admixing the first liquid or the first solid phase or the mixture of first liquid and first solid phase with a gaseous or liquid phase comprising water at a temperature from 150 to 360°C and a pressure from 0.1 to 30 x 106 Pa to obtain a product mixture. The present invention further provides a process for preparing a polyamide by reaction of at least one aminonitrile with water, which comprises the following steps: (1) reacting at least one aminonitrile with water at a temperature from 100 to 360°C and a pressure from 0.1 to 35 x 106 Pa to obtain a reaction mixture, (2) further reacting the reaction mixture at a temperature from 150 to 400°C and a pressure which is lower than the pressure in step 1, the temperature and the pressure being selected so as to obtain a first gas phase and a first liquid or a first solid phase or a mixture of first solid and first liquid phase, and separating the first gas phase from the first liquid or the first solid phase or from the mixture of first liquid and first solid phase, and (3) admixing the first liquid or the first solid phase or the mixture of first liquid and first solid phase with a gaseous or liquid phase comprising water at a temperature from 150 to 360°C and a pressure from 0.1 to 30 x 106 Pa to obtain a product mixture, (4) postcondensing the product mixture at a temperature from 200 to 350 °C and a pressure which is lower than the pressure of step 3, the temperature and pressure being selected so as to obtain a second, water- and ammonia-comprising gas phase and a second liquid or second solid phase or a mixture of second liquid and second solid phase, which each comprise the polyamide. The present invention further provides a process for preparing a polyamide by reaction of at least one aminonitrile with water, which comprises the following steps: (1) reacting at least one aminonitrile with water at a tempeiature from 100 to 360°C and a pressure from 0.1 to 35 x 106 Pa to obtain a reaction mixture, (2) further reacting the reaction mixture at a temperature from 150 to 400 °C and a pressure which is lower than the pressure in step 1, the temperature and the pressure being selected so as to obtain a first gas phase and a first liquid or a first solid phase or a mixture of first solid and first liquid phase, and separating the first gas phase from the first liquid or the first solid phase or from the mixture of first liquid and first solid phase, and (4) postcondensing the first liquid or first solid phase or the mixture of first liquid and first solid phase at a temperature from 200 to 350° C and a pressure which is lower than the pressure of step 3, the temperature and pressure being selected so as to obtain a second, water- and ammonia-comprising gas phase and a second liquid or second solid phase or a mixture of second liquid and second solid phase, which each comprise the polyamide. The aminonitrile can be in principle any aminonitrile, ie., any compound having both at least one amino group and at least one nitrile group. W-Aminonitriles are preferred, especially co-aminoalkyl nitriles having from 4 to 12 carbon atoms, more preferably 4 to 9 carbon atoms, in the alkylene moiety, or aminoalkylaryl nitriles having from 8 to 13 carbon atoms, preferred aminoalkylaryl nitriles being aminoalkylaryl nitriles which have an alkyl spater of at least one carbon atom between the aromatic unit and the amino and nitrile group. Especially preferred aminoalkylaryl nitriles are those which have the amino group and nitrile group in the 1,4 position relative to each other. The w-aminoalkyl nitrile used is preferably a linear w-aminoalkyl nitrile in which the alkylene moiety (-CH2-) preferably contains from 4 to 12 carbon atoms, more preferably from 4 to 9 carbon atoms, such as 6-amino-l-cyanopentane (6-aminocapronitrile), 7-amino-l-cyanohexane, 8-amino- 1-cyanoheptane, 9-amino- 1-cyanooctane, 10-amino- 1-cyanononane, particularly preferably 6-aminocapronitrile. 6-Aminocapronitrile is customarily obtained by hydrogenation of adiponitrile according to known methods, described for example in DE-A 836,938, DE-A 848,654 or US-A 5,151,543. Of course, it is also possible to use mixtures of a plurality of aminonitriles or mixtures of an aminonitrile with further comonomers, for example caprolactam or the below-defined mixture. In a particular embodiment, especially if copolyamides are to be prepared, the following mixture is used instead of pure 6-aminocapronitrile: from 50 to 99.9, preferably from 80 to 90, % by weight of 6-aminocapronitrile, from 0.01 to 50, preferably from 1 to 30, % by weight of at least one dicarboxylic acid selected from the group consisting of aliphatic C4-C10-a-ω-dicarboxylic acids, aromatic C8-C12-dicarboxylic acids and C5-Cs-cycloalkanedicarboxylic acids, from 0 to 50, preferably from 0.1 to 30, % by weight of an a,ω-diamine having from 4 to 10 carbon atoms, from 0 to 50, preferably from 0 to 30, % by weight of an α,ω;-C2-C12-dinitrile, and from 0 to 50, preferably from 0 to 30, % by weight of an α,ω-C5-C12-amino acid or of the corresponding lactam, the individual weight percentages adding up to 100%. Suitable dicarboxylic acids include aliphatic C4-C10-a,o)-dicarboxylic acids such as succinic acid, glutaric acid, adipic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid, preferably adipic acid and sebacic acid, particularly preferably adipic acid, and aromatic C8-C12-dicarboxylic acids such as terephthalic acid and also C5-Cg-cycloalkanedicarboxylic acids such as cyclo-hexanedicarboxylic acid. Suitable a,w-diamines having from 4 to 10 carbon atoms include tetramethylenediamine, pentamethylenediamine, hexamethylenediamine, heptamethylenediamine, octamethylenediamine, nonamethylenediamine and decamethylenediamine, preferably hexamethylenediamine. It is further also possible to use salts of the aforementioned dicarboxylic acids and diamines, especially the salt of adipic acid and hexamethylenediamine, which is known as 6,6 salt. The α ωC2-C12-dinitrile used is preferably an aliphatic dinitrile such as 1,4-dicyanobutane (adiponitrile), 1,5-dicyanopentane, 1,6-dicyanohexane, i ,7-dicyanoheptane, 1,8-dicyanooctane, 1,9-dicyanononane, 1,10-dicyanodecane, particularly preferably adiponitrile. If desired, it is also possible to use diamines, dinitriles and aminonitriles derived from branched alkyls or aryls or alkylaryls. The a,o;-C5-C12-amino acid used can be 5-aminopentanoic acid, 6-aminohexanoic acid, 7-aminoheptanoic acid, 8-aminooctanoic acid, 9-aminononanoic acid, 10-aminodecanoic acid, 11-arainoundecanoic acid or 12-aminododecanoic acid, preferably 6-aminohexanoic acid. According to the invention, the first step (step 1) involves heating an aminonitrile with water at a temperature from about 100 to about 360°C, preferably about 200 to about 350°C, especially about 250 to about 300°C, to which a pressure from about 0.1 to about 35 x 106 Pa, preferably about 4 to about 30 x 106 Pa, especially about 6 to about 12 x 106 Pa, is set. In this step, the pressure and the temperature can be adjusted relative to each other in such a way as to obtain a liquid or a solid phase and a mixture of liquid or solid phase and a gaseous phase. According to the invention, water is used in a molar ratio of aminoalkyl nitrile to water within the range 1:1 to 1:30, particularly preferably within the range 1:2 to 1:10, very particularly preferably within the range from 1:2 to 1:4, preference being given to the use of water in excess, based on the aminoalkyl nitrile used. In this embodiment, the liquid or solid phase or the mixture of liquid and solid phase corresponds to the reaction mixture, whereas the gaseous phase is separated off. As part of this step, the gaseous phase can be separated from the liquid or solid phase or from the mixture of solid or liquid phase at once, or the synthesis mixture forming within this step can be present in two-phase form: liquid/gaseous, solid/gaseous or liquid-solid/gaseous. Of course, the pressure and temperature can also be adjusted relative to each other in such a way that the synthesis mixture is present as a single solid or liquid phase. The removal of the gas phase can be effected by the use of stirred or unstirred separating vessels or vessel batteries and by the use of evaporator apparatus, for example by means of circulatory evaporators or thin-film evaporators, e.g., filmtruders, or by means of annular disk reactors, which ensure an enlarged phase interface. In certain cases, recirculation of the synthesis mixture or the i use of a loop reactor may be necessary to increase the phase interface.1 Furthermore, the removal of the gas phase can be furthered by the addition of water vapor or inert gas into the liquid phase. Preferably, the pressure is adjusted at a preselected temperature so that the pressure is smaller than the equilibrium vapor pressure of ammonia, but greater than the equilibrium vapor pressure of the other components in the synthesis mixture at the given temperature. This way, it is possible to favor especially the removal of ammonia and thus speed up the hydrolysis of the acid amide groups. Step 1 can be carried out using stirred vessels, flow pipes or vessel batteries, A two-phase procedure is preferably carried out using vessels or a reaction column, whereas a procedure involving a single liquid phase is preferably carried out using a packed flow pipe. The use of a tube bundle reactor, facultatively packed, in the first process step is likewise possible and advantageous for a two-phase procedure especially, to improve the heat transfer and to further reduce the axial back-mixing of the reactants. Usable packing elements include, for example, Raschig rings or Sulzer mixing elements in order that a narrow residence time distribution may be ensured and in order that back-mixing may be limited. In a further embodiment, the reactor of the first step is subjected to a downward flow regime, in which case it is again preferably equipped with packing elements which limit any axial back-mixing of the reactants. As a result, the ammonia gas liberated in the reactor, predominantly directly after entry into the reactor, reaches the gas phase at the top of the reactor by the most direct route. Interference caused to the flow profile in the further course of the reactor by ascending gas bubbles or convection is therefore minimal. As regards the residence time of the synthesis mixture in the first step, there are no restrictions whatsoever; however, it is generally set within the range from about 10 minutes to about 10 hours, preferably within the range from about 30 minutes to about 6 hours. i Although there are no restrictions whatsoever concerning the degree of conversion of nitrile groups in step 1 either, economic reasons especially dictate that the conversion of nitrile groups in step 1 be generally not less than about 70 mol%, preferably at least about 95 mol%, and especially within the range from about 97 to about 99 mol%, based on the moles of aminonitrile used. The nitrile group conversion is customarily determined by means of IR spectroscopy (CN stretching vibration at 2247 wavenumbers), NMR or HPLC, preferably by IR spectroscopy. In a further preferred embodiment, the aminonitrile/water mixture is continuously heated with the aid of a heat exchanger and the mixture thus heated is introduced into a reaction vessel heated to the same temperature, preferably into a tube which, if desired, may include internals such as Sulzer mixing elements to avoid back-mixing. Of course, the aminonitrile and the water can also be heated up separately. Nor does the invention rule out conducting the reaction in step I in the presence of oxygen-containing phosphorus compounds, especially phosphoric acid, phosphorous acid and hypophosphorous acid and alkali metal and alkaline earth metal salts and ammonium salts such as Na3P04, NaH2P04, Na2HP04, NaH2P03, Na2HP03, NaH2P02, K3P04, KH2P04, K2HP04, KH2P03, K2HP03, KH2P02, in which case the molar ratio of oj-aminonitrile to phosphorus compounds is selected within the range from 0.01:1 to 1:1, preferably within the range from 0.01:1 to 0.1:1. Nor does it rule out using known metal oxides, for example titanium dioxides, zirconium oxide, aluminum oxide, lanthanum oxide, magnesium oxide, etc., preferably titanium dioxides, for heterogeneous catalysis in the individual process steps in order that the conversion, especially of the nitrile groups, may be furthered. The abovementioned metal oxides are not used in step 4, but they can be used in steps 1 to 3, in which case the use in step 1 is preferred. According to the invention, the reaction mixture obtained in the first step is further reacted in step 2 at a temperature from about 150 to about 400°C, preferably at a temperature within the range from about 220 to about 350°C, especially within the range from about 250 to about 290°C, and a pressure which is lower than the pressure in step 1. The pressure in step 2 is preferably at least about 0.5 x 106 Pa lower than the pressure in step 1, and generally the pressure will be within the range from about 0.05 to about 45 x 106 Pa, preferably within the range from about 0.5 to about 15 x 106 Pa, especially within the range from about 0.5 to about 5 x 106 Pa. In step 2, the temperature and the pressure are chosen so as to obtain a first gas phase and a first liquid or first solid phase or a mixture of first liquid and first solid phase and the first gas phase is separated from the first liquid or first solid phase or from the mixture of first liquid and first solid phase. The first gaseous phase, which consists essentially of ammonia and water vapor, is generally removed continuously by means of a distillation apparatus, for example a distillation column. Any organic constituents of the distillate coremoved in the course of this distillation, predominantly unconverted aminonitrile, can be wholly or partly recycled into step 1 and/or step 2. The residence time of the reaction mixture in step 2 is not subject to any restrictions whatsoever, but is generally within the range from about 10 minutes to about 5 hours, preferably within the range from about 15 minutes to about 4 hours. The product line between the first and second steps optionally contains packing elements, for example Raschig rings or Sulzer mixing elements, which facilitate a controlled expansion of the reaction mixture into the gas phase. In step 3, the first liquid or the first solid phase or the mixture of first liquid and first solid phase is admixed with a gaseous or liquid phase comprising water, preferably with water or water vapor. This is preferably done continuously. The amount of water added (as liquid) is preferably within the range from about 50 to about 1500 ml, more preferably within the range from about 100 to about 500 ml, based on 1 kg of the first liquid or first solid phase or of the mixture of first liquid and first solid phase. This addition of water primarily compensates the water losses incurred in step 2 and furthers the hydrolysis of acid amide groups in the synthesis mixture. This results in a further advantage of this invention, that the mixture of the starting materials as used in step 1 can be used with a small excess of water only. The water-comprising gaseous or liquid phase is preferably preheated in a heat exchanger before being introduced into step 3 and then mixed with the first liquid or the first solid phase or the mixture of first solid and first liquid phase. The reactor may optionally be fitted with mixing elements which further the mixing of the components. Step 3 is operated at a temperature from 150 to 400°C and a pressure from 0.1 to 30 x 106 Pa. The pressure and temperature can be adjusted to each other in such a way that the synthesis mixture is present as a single liquid or solid phase. In another embodiment, the pressure and temperature are selected so that a liquid or solid phase or a mixture of solid and liquid phase and also a gaseous phase are obtained. In this embodiment, the liquid or solid phase or the mixture of liquid and solid phase corresponds to the product mixture, whereas the gaseous phase is separated off. As part of this step, the gaseous phase can be separated from the liquid or solid phase or from the mixture of solid and liquid phase at once, or the synthesis mixture forming within this step can be present in two-phase form: liquid/gaseous, solid/gaseous or liquid-solid/gaseous. ' The pressure can be adjusted at a preselected temperature so that the pressure is smaller than the equilibrium vapor pressure of ammonia, but greater than the equilibrium vapor pressure of the other components in the synthesis mixture at the given temperature. This way, it is possible to favor especially the removal of ammonia and thus speed up the hydrolysis of the acid amide groups. The apparatus/reactors usable in this step are identical with those of step 1, discussed above. In a preferred embodiment, the two-phase procedure is carried out by subjecting the reactor of step 1 to downward flow, in which case this reactor is preferably again equipped with packing elements which limit any axial back-mixing of the reactants. As a result, the ammonia gas liberated in the reactor, predominantly directly after entry into the reactor, reaches the gas phase at the top of the reactor by the most direct route. Interference caused to the flow profile in the further course of the reactor by ascending gas bubbles or convection is therefore minimal. The residence time of this step is likewise not subject to any restrictions, but economic reasons generally dictate a range from about 10 minutes to about 3 hours, preferably about 20 to about 90 minutes. The product mixture obtained in step 3 can be further processed as described below. In a preferred embodiment, the product mixture of step 3 is subjected to a postcondensation in step 4 at temperatures from about 200 to about 350°C, preferably at temperatures of about 220 to 300°C, especially from about 250 to 270°C. Step 4 is carried out at a pressure which is below the pressure of step 3 and would preferably be within the range from about 5 to 1000 x 103 Pa, more preferably within the range from about 10 to about 300 x 103 Pa. In the context of this step, the temperature and pressure are selected so as to obtain a second gas.phase and a second liquid or solid phase or a mixture of second liquid and second solid phase which each comprise the polyamide. ; The postcondensation of step 4 is preferably carried out in such a way that the relative viscosity (measured at a temperature of 25°C and a concentration of 1 g of polymer per 100 ml in 96% strength by weight of sulfuric acid) of the polyamide assume a value within the range of about 1.6 to about 3.5, In a preferred embodiment, any water present in the liquid phase can be expelled by means of an inert gas such as nitrogen. The residence time of the reaction mixture in step 4 depends especially on the desired relative viscosity, the temperature, the pressure and the amount of water added in step 3. If step 3 is operated as a single-phase regime, the product line between step 3 and step 4 may optionally contain packing elements, for example Raschig rings or Sulzer mixing elements, which allow a controlled expansion of the reaction mixture in the gas phase. In a further embodiment of the invention, step 3 may be dispensed with and the polyamide is prepared by carrying out steps (1), (2) and (4). This variant is preferably carried out as follows: In step 1, at least one aminoalkyl nitrile is heated with an excess of water at a temperature within the range from about 250 to about 350°C, more preferably from about 270 to about 300°C and a pressure of from about 4 to 30 x ltf5 Pa, more preferably from about 6 to 30 x 106 Pa, particularly from about 7 to 13 x 106 Pa, and even more preferably from about 8 to 12 x 106 Pa, the pressure and temperature being adjusted to each other in such a way that the synthesis mixture is present as a single liquid phase and the nitrile group conversion being not less than 95 mol%, more preferably in the range of about 97 to 99 moI%, based on the moles of aminoalkyl nitrile used, to obtain a reaction mixture. The reaction mixture is treated in step 2 at a temperature within the range from about 220 to about 300°C, and more preferably about 250 to 270°C, and a pressure within the range from about 1 to about 7 x 106 Pa, more preferably from about 1 to 4 x 106 Pa, the pressure in step 2 being at least 0.5 x 106 Pa lower than in step 1. At the same time, the resulting first gas phase is separated from the first liquid phase. The first liquid phase obtained in step 2 is treated in step 3 at a temperature within the range from about 220 to 300°C, more preferably from about 250 to 270°C, and a pressure within the range from about 10 to about 300 x 103 Pa, more preferably at about atmospheric pressure, the resulting second, water-and ammonia-comprising gas phase being separated from the second liquid phase. Within this step, the relative viscosity (measured as defined above) of the resulting polyamide is adjusted to a desired value within the range from about 1.6 to about 3.5 through choice of temperature and residence time. The resulting second liquid phase is then conventionally discharged and, if desired, worked up. The above-described processes, i.e., the sequence according to the invention of steps (I) to (3) or (1), (2) and (4) or (I) to (4), can be carried out batchwise, i.e., in succession in a single reactor, or continuously, i.e., simultaneously in successive reactors. It is also possible, of course, to carry out some of these steps, for example steps (1) and (2), continuously and the remaining step(s) batchwise. In a further preferred embodiment of the present invention, at least one of the gas phases obtained in the respective steps can be recycled into at least one of the preceding steps. It is further preferable to select the temperature and the pressure in step 1 or in step 3 or in both step 1 and step 3 so as to obtain a liquid or a solid phase or a mixture of liquid and solid phase and a gaseous phase and to separate off the gaseous phase. Furthermore, in the context of the process of the invention, it is also possible to carry out a chain lengthening or branching or a combination thereof. For this purpose, polymer branching or chain-lengthening substances known to a person skilled in the art are added in the individual steps. These substances are preferably added in step 3 or 4. Usable substances are: Trifunctional amines or carboxylic acids as crosslinkers. Examples of suitable at least trifunctional amines or carboxylic acids are described in EP-A-0 345 648. The at least trifunctional amines have at least three amino groups which are capable of reaction with carboxylic acid groups. They preferably do not have any carboxylic acid groups. The at least trifunctional carboxylic acids have at least three carboxylic acid groups which are capable of reaction with amines and which can also be present, for example, in the form of their derivatives, such as esters. The carboxylic acids preferably do not contain any amino groups capable of reaction with carboxylic acid groups. Examples of suitable carboxylic acids are trimesic acid, trimerized fatty acids, prepared for example from oleic acid and having from 50 to 60 carbon atoms, naphthalenepolycarboxylic acids, such as naphthalene-1,3,5,7-tetracarboxyIic acid. The carboxylic acids are preferably defined organic compounds and not polymeric compounds. Examples of amines having at least 3 amino groups are nitrilotrialkylamine, especially nitrilotriethaneamine, dialkylenetriamines, especially diethylenetriamine, trialkylenetetramines and tetraalkylenepentamines, the alkylene moieties preferably being ethylene moieties. Furthermore, dendrimers can be used as amines. Dendrimers preferably have the general formula I (R2N-(CH2)n)2N-(CH2)x-N((Ch2)n.NR2)2 (I) where R is H or -(CH2)n-NRl2, where Rl is H or -(CH2)n-NR22, where R2 is H or -(CH2)n-NR3 2where R3 is H or -(CH2)n-NH2, n is an integer from 2 to 6, and x is an integer from 2 to 14. Preferably, n is 3 or 4, especially 3, and x is an integer from 2 to 6, preferably from 2 to 4, especially 2. The radicals R can also have the stated meanings independently of one another. Preferably, R is a hydrogen atom or a -(CH2)n-NH2 radical. Suitable carboxylic acids are those having from 3 to 10 carboxylic acid groups, preferably 3 or 4 carboxylic acid groups. Preferred carboxylic acids are those having aromatic and/or heterocyclic nuclei. Examples are benzyl, naphthyl, anthracene, biphenyl, triphenyl radicals or heterocycles such as pyridine, bipyridine, pyrrole, indole, furan, thiophene, purine, quinoline, phenanthrene, porphyrin, phthalocyanin, naphthalocyanin. Preference is given to 3,5,3\5'-biphenyltetracarboxylic acid, phthalocyanin, naphthalocyanin, 3,5,3\5'-biphenyltetracarboxyiic acid, 1,3,5,7-naphthaienetetracarboxylic acid, 2,4,6-pyridinetricarboxylic acid, 3,5,3'5'-bipyridyltetracarboxylicacid3,5,3,'.5'-benzophenonetetracarboxylic acid, 1,3,6,8-acridinetetracarboxylic acid, particularly preferably 1,3,5-benzenetricarboxylic acid (trimesic acid) and 1,2,4,5-benzenetetracarboxylic acid. Such compounds are commercially available or can be prepared by the process described in DE-A-4 312 182. If ortho-substituted aromatic compounds are used, imide formation is preferably prevented through the choice of suitable reaction temperatures. These substances are at least trifiinctional, preferably at least tetrafunctional. The number of functional groups can be from 3 to 16, preferably from 4 to 10, particularly preferably from 4 to 8. The processes of the invention are carried out using either at least trifiinctional amines or at least Afunctional carboxylic acids, but not mixtures of such amines or carboxylic acids. However, small amounts of at least trifiinctional amines may be present in the Afunctional carboxylic acids, and vice versa. The substances are present in an amount from 1 to 50 /xmol/g of polyamide, preferably from 1 to 35, particularly preferably 1 to 20, μ mol/g of polyamide. The substances are preferably present in an amount from 3 to 150, particularly preferably from 5 to 100, especially from 10 to 70, μ mol of equivalents/g of polyamide. The equivalents are based on the number of functional amino groups or carboxylic acid groups. Difiinctional carboxylic acids or difunctional amines as chain lengtheners. These have 2 carboxylic acid groups which can be reacted with amino groups, or 2 amino groups which can be reacted with carboxylic acids. The difunctional carboxylic acids or amines, as well as the carboxylic acid groups or amino groups, do not contain any further functional groups capable of reaction with amino groups or carboxylic acid groups. Preferably, they do not contain any further functional groups. Examples of suitable difunctional amines are those which form salts with difunctional carboxylic acids. They can be linear aliphatic, such as CM4-alkylenediamine, preferably C2_6-alkylenediamine, for example hexylenediamine. They can also be cycloaliphatic. Examples are; isophoronediamine, dicycycan, laromine. Branched aliphatic diamines are likewise usable, an example being Vestamin TMD (trimethylhexamethylenediamine, from Hiils AG). In addition, the diamines can also be aromatic-aliphatic, it being possible to use n-xylylenediamine for example. Entire amines can each be substituted by CM2-alkyl, preferably C1-14-alkyl, radicals on the carbon skeleton. Difunctional carboxylic acids are for example those which form salts with difunctional diamines. They can be linear aliphatic dicarboxylic acids, which are preferably C4_20-dicarboxylic acids. Examples are adipic acid, azelaic acid, sebacic acid, suberic acid. They can also be aromatic. Examples are isophthalic acid, terephthalic acid, naphthalenedicarboxylic acid, as well as dimerized fatty acids. The difunctional basic building blocks (c) are preferably used in amounts from 1 to 55, particularly preferably from 1 to 30, especially from 1 to 15, μm/g of polyamide. According to the invention, the product mixture obtained in step 3, or the second liquid or second solid phase or the mixture of second liquid and second solid phase (from step 4) which each comprise the polyamide, preferably a polymer melt, is discharged from the reaction vessel in a conventional manner, for example by means of a pump. Subsequently, the polyamide obtained can be worked up according to conventional methods, as described for example in DE-A 43 21 683 (page 3 line 54 to page 4 line 3) at length. In a preferred embodiment, the level of cyclic dimer in the nylon-6 obtained according to the invention can be further reduced by extracting the polyamide first with an aqueous solution of caprolactam and then with water and/or subjecting it to a gas phase extraction (described in EPrA 28 49 68, for example). The low molecular weight constituents obtained in this aftertreatment, such as caprolactam, linear caprolactam oligomer and cyclic caprolactam oligomer, can be recycled into the first and/or second and/or third step. The starting monomer or monomer mixture can be admixed in all steps, preferably in the fourth step, with customary additives and fillers such as pigments, especially titanium dioxide (anatase and/or rutile), silicon dioxide and talcum, chain regulators such as aliphatic and aromatic carboxylic and dicarboxylic acids such as propionic acid, acetic acid, benzoic acid, terephthalic acid and also triacetonediamine, stabilizers such as copper(I) halides and alkali metal halides, nucleating agents such as magnesium silicate or boron nitride, catalysts such as phosphorous acid and also antioxidants in amounts within the range from 0.01 to 5, preferably within the range from 0.2 to 2, % by weight, based on the amount of monomers used. The present invention further relates to a polyamide preparable by (1) reacting at least one aminonitrile with water at a temperature from 100 to 360°C and a pressure from 0.1 to 35 x 106 Pa to obtain a reaction mixture, (2) further reacting the reaction mixture at a temperature from 150 to 400°C and a pressure which is lower than the pressure in step 1, the temperature and the pressure being selected so as to obtain a first gas phase and a first liquid or a first solid phase or a mixture of first solid and first liquid phase, and separating the first gas phase from the first liquid or the first solid phase or from the mixture of first liquid and first solid phase, and admixing the first liquid or the first solid phase or the mixture of first liquid and first solid phase with a gaseous or liquid phase comprising water at a temperature from 150 to 360°C and a pressure from 0.1 to 30 x 106 Pa to obtain a product mixture, i a polyamide preparable by j reacting at least one aminonitrile with water at a temperature from 100 to 360°C and a pressure from 0.1 to 35 x 106 Pa to obtain a reaction mixture, further reacting the reaction mixture at a temperature from 150 to 400°C and a pressure which is lower than the pressure in step 1, the temperature and the pressure being selected so as to obtain a first gas phase and a first liquid or a first solid phase or a mixture of first solid and first liquid phase, and separating the first gas phase from the first liquid or the first solid phase or from the mixture of first liquid and first solid phase, and admixing the first liquid or the first solid phase or the mixture of first liquid and first solid phase with a gaseous or liquid phase comprising water at a temperature from 150 to 360°C and a pressure from 0.1 to 30 x 106 Pa to obtain a product mixture, postcondensing the product mixture at a temperature from 200 to 350°C and a pressure which is lower than the pressure of step 3, the temperature and pressure being selected so as to obtain a second, water- and ammonia-comprising gas phase and a second liquid or second solid phase or a mixture of second liquid and second solid phase, which each comprise the polyamide, and a polyamide preparable by reacting at least one aminonitrile with water at a temperature from 100 to 360°C and a pressure from 0.1 to 35 x 106 Pa to obtain a reaction mixture, further reacting the reaction mixture at a temperature from 150 to 400 °C and a pressure which is lower than the pressure in step 1, the temperature and the pressure being selected so as to obtain a first gas phase and a first liquid or a first solid phase or a mixture of first solid and first liquid phase, and separating the first gas phase from the first liquid or the first solid phase or from the mixture of first liquid and first solid phase, and postcondensing the first liquid or first solid phase or the mixture of first liquid and first solid phase at a temperature from 200 to 350°C and a pressure which is lower than the pressure of step 3, the temperature and pressure being selected so as to obtain a second, water- and ammonia-comprising gas phase and a second liquid or second solid phase or a mixture of second liquid and second solid phase, which each comprise the polyamide. The polyamides of or obtained according to this invention, especially nylon-6 and its copolymers, can be used for manufacturing fibers and materials of construction. EXAMPLES Example 1 i This example explains the present invention by the reaction of ACN. The AEG (amino end group) and CEG (carboxyl end group) arb determined by the method described in WO 95/01389 (page 6 line 35 to page 7 line 40). The volatile bases are determined by the method of Parnas-Wagner by hydrolyzing the polyamide with HC1, liberating the bases with NaOH, then steam distilling the liberated bases by the method of Parnas into a flask containing HC1 and finally back-titrating the excess HC1 with NaOH. The difference between HC1 used in the receiving flask and back-titrated HC1 can be used to calculate the level of volatile bases (in mg of NH3/kg). The nitrile group conversion was determined by FTIR spectroscopy by means of the characteristic CN group band at 2247 cm"1. The relative viscosity (RV) was determined at 25°C and a concentration of 1 g of polymer per 100 ml in 96 % strength by weight sulfuric acid. In all the runs listed, the step 4 postcondensation was carried out batchwise in a laboratory autoclave: 3 h, 250°C, 105 Pa (1 bar). The results are shown in Table 1. Example 2 The table below shows the experimental conditions in steps 1 and 2. The temperature in step 4 was 270°C, the pressure was 105 Pa (1 bar) and the residence time was 1.5 h. RT = residence time WA = water add in %, based on feed stream of ACN/water mixture in step 1 Comparative examples The table below shows the parameters of products prepared according to the prior art - Example 1 of US 5 109 104 and Example 1 of US 2 245 129. We claim: 1. A process for preparing a polyamide by reaction of at least one aminonitrile with water, which comprises the following steps: (1) reacting at least one aminonitrile with water at a temperature from 100 to 360°C and a pressure from 0.1 to 35 x 106 Pa to obtain a reaction mixture, (2) further reacting the reaction mixture at a temperature from 150 to 400 °C and a pressure which is lower than the pressure in : step 1, the temperature and the pressure being selected so as to obtain a first gas phase and a first liquid or a first solid phase or a mixture of first solid and first liquid phase, and separating the first gas phase from the first liquid or the first solid phase or from the mixture of first liquid and first solid phase, and (3) admixing the first liquid or the first solid phase or the mixture of first liquid and first solid phase with a gaseous or liquid phase comprising water at a temperature from 150 to 360 °C and a pressure from 0.1 to 30 x 106 Pa to obtain a product mixture. 2, A process for preparing a polyamide by reaction of at least one aminonitrile with water, which comprises the following steps: (1) reacting at least one aminonitrile with water at a temperature from 100 to 360°C and a pressure from 0.1 to 35 x 106 Pa to obtain a reaction mixture, uv to 400°C and a pressure which is lower than the pressure in step 1, the temperature and the pressure being selected so as to obtain a first gas phase and a first liquid or a first solid phase or a mixture of first solid and first liquid phase, and separating the first gas phase from the first liquid or the first solid phase or from the mixture of first liquid and first solid phase, and (3) admixing the first liquid or the first solid phase or the mixture of first liquid and first solid phase with a gaseous or liquid phase comprising water at a temperature from 150 to 360°C and a pressure from 0.1 to 30 x 106 Pa to obtain a product mixture, (4) postcondensing the product mixture at a temperature from 200 to 350°C and a pressure which is lower than the pressure of step 3, the temperature and pressure being selected so as to obtain a second, water- and ammonia-comprising gas phase and a second liquid or second solid phase or a mixture of second liquid and second solid phase, which each comprise the polyamide. 3. A process for preparing a polyamide by reaction of at least one aminonitrile with water, which comprises the following steps: (1) reacting at least one aminonitrile with water at a temperature from 100 to 360°C and a pressure from 0.1 to 35 x 106 Pa to obtain a reaction mixture, (2) further reacting the reaction mixture at a temperature from 150 ; to 400°C and a pressure which is lower than the pressure in step 1, the temperature and the pressure being selected so as to obtain a first gas phase and a first liquid or a first solid phase or a mixture of first solid and first liquid phase, and separating the first gas phase from the first liquid or the first solid phase or from the mixture of first liquid and first solid phase, and (4) postcondensing the first liquid or the first solid phase or the mixture of first liquid and first solid phase at a temperature from 200 to 350°C and a pressure which is lower than the pressure of step 3, the temperature and pressure being selected i so as to obtain a second, water- and ammonia-comprising gas phase and a second liquid or second solid phase or a mixture of second liquid and second solid phase, which each comprise the polyamide. 4. A process as claimed in claim 1 or 2, wherein the temperature and pressure in step 1 or in step 3 or in both step 1 and step 3 are selected so as to obtain a liquid or a solid phase or a mixture of liquid and solid phase and a gaseous phase, and die gaseous phase is separated off. 5. A process as claimed in any of the preceding claims, wherein the reaction of step 1 is carried on to a nitrile group conversion of at least 95 mol%, based on the moles of aminonitrile used. 6. A process as claimed in any of claims 1, 2, 4 and 5, wherein, in step 3, the gaseous or liquid phase comprising water is added in an amount from 50 to 1500 ml of water per 1 kg of first liquid or first solid phase or mixture of first liquid and first solid phase. A process as claimed in any of the preceding claims, wherein steps 1 to 3, 1, 2 and 4 or 1 to 4 are carried out continuously. A process as claimed in any of the preceding claims, wherein at least one of the gas phases obtained in the respective steps is recycled into at least one of the preceding steps. A process as claimed in any of the preceding claims, wherein the aminonitrile used is an ca-aminoalkyl nitrile having an alkylene moiety (-CH2-) of from 4 to 12 carbon atoms or an aminoalkylaryl nitrile having 8 to 13 carbon atoms. A process as claimed in any of the preceding claims, wherein the following mixture is used as aminonitrile: from 50 to 99.99% by weight of 6-aminocapronitrile, from 0.01 to 50% by weight of at least one dicarboxylic acid selected from the group consisting of aliphatic C4-C10-a,o;-dicarboxylic acids, aromatic C8-CI2-dicarboxylic acids and C5-Cg-cycloalkanedicarboxylic acids, from 0 to 50% by weight of an α,ω-diamine having 4-10 carbon atoms, from 0 to 50% by weight of an α,ω-C2-C12-dinitrile, and from 0 to 50% by weight of an α,ω-C5-C12-aniino acid or the corresponding lactam, the individual weight percentages adding up to 100%. A process as claimed in any of the preceding claims, wherein a chain lengthening or a chain branching or a combination thereof is carried out. A polyamide preparable by (1) reacting at least one aminonitrile with water at a temperature from 100 to 360°C and a pressure from 0.1 to 35 x 106 Pa to obtain a reaction mixture, (2) further reacting the reaction mbcture at a temperature from 150 to 400 °C and a pressure which is lower than the pressure in step 1, the temperature and the pressure being selected so as to obtain a first gas phase and a first liquid or a first solid phase or a mixture of first solid and first liquid phase, and separating the first gas phase from the first liquid or the first solid phase or from the mixture of first liquid and first solid phase, and (3) admixing the first liquid or the first solid phase or the mixture of first liquid and first solid phase with a gaseous or liquid i i phase comprising water at a temperature from 150 to 360°C and a pressure from 0.1 to 30 x 106 Pa to obtain a product mixture. A polyamide preparable by (1) reacting at least one aminonitrile with water at a temperature from 100 to 360°C and a pressure from 0.1 to 35 x 106 Pa to obtain a reaction mixture, (2) further reacting the reaction mixture at a temperature from 150 to 400°C and a pressure which is lower than the pressure in step 1, the temperature and the pressure being selected so as to obtain a first gas phase and a first liquid or a first solid phase or a mixture of first solid and first liquid phase, and separating the first gas phase from the first liquid or the first solid phase or from the mixture of first liquid and first solid phase, and (3) admixing the first liquid or the first solid phase or the mixture of first liquid and first solid phase with a gaseous or liquid phase comprising water at a temperature from 150 to 360°C and a pressure from 0.1 to 30 x 106 Pa to obtain a product mixture, (4) postcondensing the product mixture at a temperature from 200 to 350 °C and a pressure which is lower than the pressure of step 3, the temperature and pressure being selected so as to obtain a second, water- and ammonia-comprising gas phase and a second liquid or second solid phase or a mixture of second liquid and second solid phase, which each comprise the poly amide. A polyamide preparable by (1) reacting at least one aminonitrile with water at a temperature from 100 to 360°C and a pressure from 0.1 to 35 x 106 Pa to obtain a reaction mixture, (2) further reacting the reaction mixture at a temperature from 150 to 400°C and a pressure which is lower than the pressure in step 1, the temperature and the pressure being selected so as to obtain a first gas phase and a first liquid or a first solid phase or a mixture of first solid and first liquid phase, and separating the first gas phase from the first liquid or the first ! solid phase or from the mixture of first liquid and first solid phase, and (4) postcondensing the first liquid or first solid phase or the mixture of first liquid and first solid phase at a temperature from 200 to 350°C and a pressure which is lower than the pressure of step 3, the temperature and pressure being selected so as to obtain a second, water- and ammonia-comprising gas phase and a second liquid or second solid phase or a mixture of second liquid and second solid phase, which each comprise the polyamide. 15. A process for preparing a polyamide by reaction i of at least one aminonitrile with water, substantially as herein described and exemplified.

Full Text

The present invention relates to a novel process for preparing polyamides from aminonitriles and water at elevated temperature and elevated pressure. US 2 245 129 describes a batchwise two-step preparation of polycaprolactam from ω-aminocapronitrile ("ACN") and water at a temperature within the range from 150 to 300°C, governed by a specific temperature program as a function of the amount of water added, and a pressure of not more than 30 bar. The disadvantages of this process are the long reaction times (20 h in step 1), the low viscosity of the resulting polycaproplactam and the high level of volatile bases (essentially primary acid amides) compared with a polycaprolactam j prepared from caprolactam.
DE-C 35 34 817, US 4 568 736 and US 4 629 776 partly solve the problems j described in US 2 245 129 by the use of phosphorus- and sulfur-containing catalysts. The use of the catalysts mentioned improves the low space-time yield of the process described in US 2 245 129. However, the level of volatile bases in all the products prepared by the abovementioned processes is still too high, so that the polyamides are difficult to process and have a reduced carboxyl end group number. The stoichiometric discrepancy between the amino and carboxyl end groups in the products of the abovementioned processes is responsible for

their showing an insufficient degree of polymerization and a slow increase in molecular weight during tempering. Furthermore, complete removal of the catalysts is virtually impossible, so that the chemical and physical behavior of the polymers prepared using the catalysts, such as type and quantity of end groups or snap-off behavior during spinning, is adversely affected. EP-A 0 479 306 proposes, in relation to the reaction of ACN with water to give polycaproiactam, to remove ammonia and water continuously, by decompressing, once a reaction temperature from 200. to 260°C has been attained and at the same time to add water continuously while selecting a pressure within the range from 14 to 24 x 106 Pa (14 to 24 bar). EP-A 65 291 describes a continuous process for preparing nylon 66 from dinitriles and diamines. The molecular weight builds up via polycondensation. Caprolactam does not occur as an intermediate, which it does, however, in the polymerization of ACN. Thus, because of the different reaction mechanisms, it was not possible to apply the process mentioned in EP-A 65 291 to the present problem.
It is an object of the present invention to provide a process for preparing polyamides from aminonitriles with improved hydrolysis of the reactants, especially of the acid amide groups, and thus a higher carboxyl end group content. The molecular weight increase during the polymerization and the temperability of the product are improved in this way, compared with prior art
processes.
We have found that this object is achieved by a process for preparing a polyamide by reaction of at least one aminonitrile with water, which comprises the following steps:
(1) reacting at least one aminonitrile with water at a temperature

from 100 to 360°C and a pressure from 0.1 to 35 x 106 Pa to obtain a reaction mixture,
(2) further reacting the reaction mixture at a temperature from 150 to 400°C and a pressure which is lower than the pressure in step 1, the temperature and the pressure being selected so as to obtaih a first gas phase and a first liquid or a first solid phase or a mixture of first solid and first liquid phase, and separating the first gas phase from the first liquid or the first solid phase or from the mixture of first liquid and first solid phase, and
(3) admixing the first liquid or the first solid phase or the mixture of first liquid and first solid phase with a gaseous or liquid phase comprising water at a temperature from 150 to 360°C and a pressure from 0.1 to 30 x 106 Pa to obtain a product mixture.
The present invention further provides a process for preparing a polyamide by reaction of at least one aminonitrile with water, which comprises the following steps:
(1) reacting at least one aminonitrile with water at a temperature from 100 to 360°C and a pressure from 0.1 to 35 x 106 Pa to obtain a reaction mixture,
(2) further reacting the reaction mixture at a temperature from 150 to 400°C and a pressure which is lower than the pressure in step 1, the temperature and the pressure being selected so as to obtain a first gas phase and a first liquid or a first solid phase or a

mixture of first solid and first liquid phase, and separating the first gas phase from the first liquid or the first solid phase or from the mixture of first liquid and first solid phase, and
(3) admixing the first liquid or the first solid phase or the mixture of first liquid and first solid phase with a gaseous or liquid phase comprising water at a temperature from 150 to 360°C and a pressure from 0.1 to 30 x 106 Pa to obtain a product mixture,
(4) postcondensing the product mixture at a temperature from 200 to 350 °C and a pressure which is lower than the pressure of step 3, the temperature and pressure being selected so as to obtain a second, water- and ammonia-comprising gas phase and a second liquid or second solid phase or a mixture of second liquid and second solid phase, which each comprise the polyamide.
The present invention further provides a process for preparing a polyamide by reaction of at least one aminonitrile with water, which comprises the following steps:
(1) reacting at least one aminonitrile with water at a tempeiature from 100 to 360°C and a pressure from 0.1 to 35 x 106 Pa to obtain a reaction mixture,
(2) further reacting the reaction mixture at a temperature from 150 to 400 °C and a pressure which is lower than the pressure in step 1, the temperature and the pressure being selected so as to obtain a first gas phase and a first liquid or a first solid phase or a

mixture of first solid and first liquid phase, and separating the first gas phase from the first liquid or the first solid phase or from the mixture of first liquid and first solid phase, and
(4) postcondensing the first liquid or first solid phase or the mixture
of first liquid and first solid phase at a temperature from 200 to 350° C and a pressure which is lower than the pressure of step 3, the temperature and pressure being selected so as to obtain a second, water- and ammonia-comprising gas phase and a second liquid or second solid phase or a mixture of second liquid and second solid phase, which each comprise the polyamide.
The aminonitrile can be in principle any aminonitrile, ie., any compound having both at least one amino group and at least one nitrile group. W-Aminonitriles are preferred, especially co-aminoalkyl nitriles having from 4 to 12 carbon atoms, more preferably 4 to 9 carbon atoms, in the alkylene moiety, or aminoalkylaryl nitriles having from 8 to 13 carbon atoms, preferred aminoalkylaryl nitriles being aminoalkylaryl nitriles which have an alkyl spater of at least one carbon atom between the aromatic unit and the amino and nitrile group. Especially preferred aminoalkylaryl nitriles are those which have the amino group and nitrile group in the 1,4 position relative to each other. The w-aminoalkyl nitrile used is preferably a linear w-aminoalkyl nitrile in which the alkylene moiety (-CH2-) preferably contains from 4 to 12 carbon atoms, more preferably from 4 to 9 carbon atoms, such as 6-amino-l-cyanopentane (6-aminocapronitrile), 7-amino-l-cyanohexane, 8-amino- 1-cyanoheptane, 9-amino- 1-cyanooctane, 10-amino- 1-cyanononane, particularly preferably 6-aminocapronitrile. 6-Aminocapronitrile is customarily obtained by hydrogenation of adiponitrile

according to known methods, described for example in DE-A 836,938, DE-A
848,654 or US-A 5,151,543.
Of course, it is also possible to use mixtures of a plurality of aminonitriles or
mixtures of an aminonitrile with further comonomers, for example caprolactam
or the below-defined mixture.
In a particular embodiment, especially if copolyamides are to be prepared, the
following mixture is used instead of pure 6-aminocapronitrile:
from 50 to 99.9, preferably from 80 to 90, % by weight of
6-aminocapronitrile,
from 0.01 to 50, preferably from 1 to 30, % by weight of at least one
dicarboxylic acid selected from the group consisting of aliphatic
C4-C10-a-ω-dicarboxylic acids, aromatic C8-C12-dicarboxylic acids and
C5-Cs-cycloalkanedicarboxylic acids,
from 0 to 50, preferably from 0.1 to 30, % by weight of an a,ω-diamine
having from 4 to 10 carbon atoms,
from 0 to 50, preferably from 0 to 30, % by weight of an
α,ω;-C2-C12-dinitrile, and
from 0 to 50, preferably from 0 to 30, % by weight of an α,ω-C5-C12-amino
acid or of the corresponding lactam,
the individual weight percentages adding up to 100%.
Suitable dicarboxylic acids include aliphatic C4-C10-a,o)-dicarboxylic acids such
as succinic acid, glutaric acid, adipic acid, pimelic acid, suberic acid, azelaic
acid, sebacic acid, preferably adipic acid and sebacic acid, particularly
preferably adipic acid, and aromatic C8-C12-dicarboxylic acids such as
terephthalic acid and also C5-Cg-cycloalkanedicarboxylic acids such as
cyclo-hexanedicarboxylic acid.
Suitable a,w-diamines having from 4 to 10 carbon atoms include
tetramethylenediamine, pentamethylenediamine, hexamethylenediamine,

heptamethylenediamine, octamethylenediamine, nonamethylenediamine and
decamethylenediamine, preferably hexamethylenediamine.
It is further also possible to use salts of the aforementioned dicarboxylic acids
and diamines, especially the salt of adipic acid and hexamethylenediamine,
which is known as 6,6 salt.
The α ωC2-C12-dinitrile used is preferably an aliphatic dinitrile such as
1,4-dicyanobutane (adiponitrile), 1,5-dicyanopentane, 1,6-dicyanohexane,
i ,7-dicyanoheptane, 1,8-dicyanooctane, 1,9-dicyanononane, 1,10-dicyanodecane,
particularly preferably adiponitrile.
If desired, it is also possible to use diamines, dinitriles and aminonitriles
derived from branched alkyls or aryls or alkylaryls.
The a,o;-C5-C12-amino acid used can be 5-aminopentanoic acid, 6-aminohexanoic
acid, 7-aminoheptanoic acid, 8-aminooctanoic acid, 9-aminononanoic acid,
10-aminodecanoic acid, 11-arainoundecanoic acid or 12-aminododecanoic acid,
preferably 6-aminohexanoic acid.
According to the invention, the first step (step 1) involves heating an
aminonitrile with water at a temperature from about 100 to about 360°C,
preferably about 200 to about 350°C, especially about 250 to about 300°C, to
which a pressure from about 0.1 to about 35 x 106 Pa, preferably about 4 to
about 30 x 106 Pa, especially about 6 to about 12 x 106 Pa, is set. In this
step, the pressure and the temperature can be adjusted relative to each other
in such a way as to obtain a liquid or a solid phase and a mixture of liquid
or solid phase and a gaseous phase.
According to the invention, water is used in a molar ratio of aminoalkyl nitrile
to water within the range 1:1 to 1:30, particularly preferably within the range
1:2 to 1:10, very particularly preferably within the range from 1:2 to 1:4,
preference being given to the use of water in excess, based on the aminoalkyl
nitrile used.

In this embodiment, the liquid or solid phase or the mixture of liquid and solid phase corresponds to the reaction mixture, whereas the gaseous phase is separated off. As part of this step, the gaseous phase can be separated from the liquid or solid phase or from the mixture of solid or liquid phase at once, or the synthesis mixture forming within this step can be present in two-phase form: liquid/gaseous, solid/gaseous or liquid-solid/gaseous. Of course, the pressure and temperature can also be adjusted relative to each other in such a way that the synthesis mixture is present as a single solid or liquid phase. The removal of the gas phase can be effected by the use of stirred or unstirred separating vessels or vessel batteries and by the use of evaporator apparatus, for example by means of circulatory evaporators or thin-film evaporators, e.g., filmtruders, or by means of annular disk reactors, which ensure an enlarged phase interface. In certain cases, recirculation of the synthesis mixture or the
i
use of a loop reactor may be necessary to increase the phase interface.1 Furthermore, the removal of the gas phase can be furthered by the addition of water vapor or inert gas into the liquid phase.
Preferably, the pressure is adjusted at a preselected temperature so that the pressure is smaller than the equilibrium vapor pressure of ammonia, but greater than the equilibrium vapor pressure of the other components in the synthesis mixture at the given temperature. This way, it is possible to favor especially the removal of ammonia and thus speed up the hydrolysis of the acid amide
groups.
Step 1 can be carried out using stirred vessels, flow pipes or vessel batteries, A two-phase procedure is preferably carried out using vessels or a reaction column, whereas a procedure involving a single liquid phase is preferably carried out using a packed flow pipe. The use of a tube bundle reactor, facultatively packed, in the first process step is likewise possible and advantageous for a two-phase procedure especially, to improve the heat transfer

and to further reduce the axial back-mixing of the reactants. Usable packing elements include, for example, Raschig rings or Sulzer mixing elements in order that a narrow residence time distribution may be ensured and in order that back-mixing may be limited.
In a further embodiment, the reactor of the first step is subjected to a downward flow regime, in which case it is again preferably equipped with packing elements which limit any axial back-mixing of the reactants. As a result, the ammonia gas liberated in the reactor, predominantly directly after entry into the reactor, reaches the gas phase at the top of the reactor by the most direct route. Interference caused to the flow profile in the further course of the reactor by ascending gas bubbles or convection is therefore minimal. As regards the residence time of the synthesis mixture in the first step, there are no restrictions whatsoever; however, it is generally set within the range from about 10 minutes to about 10 hours, preferably within the range from
about 30 minutes to about 6 hours.
i
Although there are no restrictions whatsoever concerning the degree of conversion of nitrile groups in step 1 either, economic reasons especially dictate that the conversion of nitrile groups in step 1 be generally not less than about 70 mol%, preferably at least about 95 mol%, and especially within the range from about 97 to about 99 mol%, based on the moles of aminonitrile used. The nitrile group conversion is customarily determined by means of IR spectroscopy (CN stretching vibration at 2247 wavenumbers), NMR or HPLC, preferably by IR spectroscopy.
In a further preferred embodiment, the aminonitrile/water mixture is continuously heated with the aid of a heat exchanger and the mixture thus heated is introduced into a reaction vessel heated to the same temperature, preferably into a tube which, if desired, may include internals such as Sulzer mixing elements to avoid back-mixing. Of course, the aminonitrile and the water can also be

heated up separately.
Nor does the invention rule out conducting the reaction in step I in the presence of oxygen-containing phosphorus compounds, especially phosphoric acid, phosphorous acid and hypophosphorous acid and alkali metal and alkaline earth metal salts and ammonium salts such as Na3P04, NaH2P04, Na2HP04, NaH2P03, Na2HP03, NaH2P02, K3P04, KH2P04, K2HP04, KH2P03, K2HP03, KH2P02, in which case the molar ratio of oj-aminonitrile to phosphorus compounds is selected within the range from 0.01:1 to 1:1, preferably within the range from 0.01:1 to 0.1:1.
Nor does it rule out using known metal oxides, for example titanium dioxides, zirconium oxide, aluminum oxide, lanthanum oxide, magnesium oxide, etc., preferably titanium dioxides, for heterogeneous catalysis in the individual process steps in order that the conversion, especially of the nitrile groups, may be furthered. The abovementioned metal oxides are not used in step 4, but they can be used in steps 1 to 3, in which case the use in step 1 is preferred. According to the invention, the reaction mixture obtained in the first step is further reacted in step 2 at a temperature from about 150 to about 400°C, preferably at a temperature within the range from about 220 to about 350°C, especially within the range from about 250 to about 290°C, and a pressure which is lower than the pressure in step 1. The pressure in step 2 is preferably at least about 0.5 x 106 Pa lower than the pressure in step 1, and generally the pressure will be within the range from about 0.05 to about 45 x 106 Pa, preferably within the range from about 0.5 to about 15 x 106 Pa, especially within the range from about 0.5 to about 5 x 106 Pa. In step 2, the temperature and the pressure are chosen so as to obtain a first gas phase and a first liquid or first solid phase or a mixture of first liquid and first solid phase and the first gas phase is separated from the first liquid or first solid phase or from the mixture of first liquid and first solid phase.

The first gaseous phase, which consists essentially of ammonia and water vapor, is generally removed continuously by means of a distillation apparatus, for example a distillation column. Any organic constituents of the distillate coremoved in the course of this distillation, predominantly unconverted aminonitrile, can be wholly or partly recycled into step 1 and/or step 2. The residence time of the reaction mixture in step 2 is not subject to any restrictions whatsoever, but is generally within the range from about 10 minutes to about 5 hours, preferably within the range from about 15 minutes to about 4 hours.
The product line between the first and second steps optionally contains packing elements, for example Raschig rings or Sulzer mixing elements, which facilitate a controlled expansion of the reaction mixture into the gas phase. In step 3, the first liquid or the first solid phase or the mixture of first liquid and first solid phase is admixed with a gaseous or liquid phase comprising water, preferably with water or water vapor. This is preferably done continuously. The amount of water added (as liquid) is preferably within the range from about 50 to about 1500 ml, more preferably within the range from about 100 to about 500 ml, based on 1 kg of the first liquid or first solid phase or of the mixture of first liquid and first solid phase. This addition of water primarily compensates the water losses incurred in step 2 and furthers the hydrolysis of acid amide groups in the synthesis mixture. This results in a further advantage of this invention, that the mixture of the starting materials as used in step 1 can be used with a small excess of water only. The water-comprising gaseous or liquid phase is preferably preheated in a heat exchanger before being introduced into step 3 and then mixed with the first liquid or the first solid phase or the mixture of first solid and first liquid phase. The reactor may optionally be fitted with mixing elements which further the mixing of the components.

Step 3 is operated at a temperature from 150 to 400°C and a pressure from 0.1 to 30 x 106 Pa.
The pressure and temperature can be adjusted to each other in such a way that
the synthesis mixture is present as a single liquid or solid phase. In another
embodiment, the pressure and temperature are selected so that a liquid or solid
phase or a mixture of solid and liquid phase and also a gaseous phase are
obtained. In this embodiment, the liquid or solid phase or the mixture of liquid
and solid phase corresponds to the product mixture, whereas the gaseous phase
is separated off. As part of this step, the gaseous phase can be separated from
the liquid or solid phase or from the mixture of solid and liquid phase at once,
or the synthesis mixture forming within this step can be present in two-phase
form: liquid/gaseous, solid/gaseous or liquid-solid/gaseous. '
The pressure can be adjusted at a preselected temperature so that the pressure is smaller than the equilibrium vapor pressure of ammonia, but greater than the equilibrium vapor pressure of the other components in the synthesis mixture at the given temperature. This way, it is possible to favor especially the removal of ammonia and thus speed up the hydrolysis of the acid amide groups. The apparatus/reactors usable in this step are identical with those of step 1, discussed above.
In a preferred embodiment, the two-phase procedure is carried out by subjecting the reactor of step 1 to downward flow, in which case this reactor is preferably again equipped with packing elements which limit any axial back-mixing of the reactants. As a result, the ammonia gas liberated in the reactor, predominantly directly after entry into the reactor, reaches the gas phase at the top of the reactor by the most direct route. Interference caused to the flow profile in the further course of the reactor by ascending gas bubbles or convection is therefore minimal. The residence time of this step is likewise not subject to any restrictions, but

economic reasons generally dictate a range from about 10 minutes to about 3
hours, preferably about 20 to about 90 minutes.
The product mixture obtained in step 3 can be further processed as described
below.
In a preferred embodiment, the product mixture of step 3 is subjected to a postcondensation in step 4 at temperatures from about 200 to about 350°C, preferably at temperatures of about 220 to 300°C, especially from about 250 to 270°C. Step 4 is carried out at a pressure which is below the pressure of step 3 and would preferably be within the range from about 5 to 1000 x 103 Pa, more preferably within the range from about 10 to about 300 x 103 Pa. In the context of this step, the temperature and pressure are selected so as to obtain a second gas.phase and a second liquid or solid phase or a mixture of second liquid and second solid phase which each comprise the polyamide. ; The postcondensation of step 4 is preferably carried out in such a way that the relative viscosity (measured at a temperature of 25°C and a concentration of 1 g of polymer per 100 ml in 96% strength by weight of sulfuric acid) of the polyamide assume a value within the range of about 1.6 to about 3.5, In a preferred embodiment, any water present in the liquid phase can be expelled by means of an inert gas such as nitrogen.
The residence time of the reaction mixture in step 4 depends especially on the desired relative viscosity, the temperature, the pressure and the amount of water
added in step 3.
If step 3 is operated as a single-phase regime, the product line between step
3 and step 4 may optionally contain packing elements, for example Raschig
rings or Sulzer mixing elements, which allow a controlled expansion of the
reaction mixture in the gas phase.
In a further embodiment of the invention, step 3 may be dispensed with and
the polyamide is prepared by carrying out steps (1), (2) and (4).

This variant is preferably carried out as follows:
In step 1, at least one aminoalkyl nitrile is heated with an excess of water at a temperature within the range from about 250 to about 350°C, more preferably from about 270 to about 300°C and a pressure of from about 4 to 30 x ltf5 Pa, more preferably from about 6 to 30 x 106 Pa, particularly from about 7 to 13 x 106 Pa, and even more preferably from about 8 to 12 x 106 Pa, the pressure and temperature being adjusted to each other in such a way that the synthesis mixture is present as a single liquid phase and the nitrile group conversion being not less than 95 mol%, more preferably in the range of about 97 to 99 moI%, based on the moles of aminoalkyl nitrile used, to obtain a reaction mixture.
The reaction mixture is treated in step 2 at a temperature within the range from about 220 to about 300°C, and more preferably about 250 to 270°C, and a pressure within the range from about 1 to about 7 x 106 Pa, more preferably from about 1 to 4 x 106 Pa, the pressure in step 2 being at least 0.5 x 106 Pa lower than in step 1. At the same time, the resulting first gas phase is separated from the first liquid phase.
The first liquid phase obtained in step 2 is treated in step 3 at a temperature within the range from about 220 to 300°C, more preferably from about 250 to 270°C, and a pressure within the range from about 10 to about 300 x 103 Pa, more preferably at about atmospheric pressure, the resulting second, water-and ammonia-comprising gas phase being separated from the second liquid phase. Within this step, the relative viscosity (measured as defined above) of the resulting polyamide is adjusted to a desired value within the range from about 1.6 to about 3.5 through choice of temperature and residence time. The resulting second liquid phase is then conventionally discharged and, if
desired, worked up.
The above-described processes, i.e., the sequence according to the invention of

steps (I) to (3) or (1), (2) and (4) or (I) to (4), can be carried out batchwise, i.e., in succession in a single reactor, or continuously, i.e., simultaneously in successive reactors. It is also possible, of course, to carry out some of these steps, for example steps (1) and (2), continuously and the remaining step(s) batchwise.
In a further preferred embodiment of the present invention, at least one of the gas phases obtained in the respective steps can be recycled into at least one of the preceding steps.
It is further preferable to select the temperature and the pressure in step 1 or in step 3 or in both step 1 and step 3 so as to obtain a liquid or a solid phase or a mixture of liquid and solid phase and a gaseous phase and to separate off the gaseous phase.
Furthermore, in the context of the process of the invention, it is also possible to carry out a chain lengthening or branching or a combination thereof. For this purpose, polymer branching or chain-lengthening substances known to a person skilled in the art are added in the individual steps. These substances are preferably added in step 3 or 4. Usable substances are:
Trifunctional amines or carboxylic acids as crosslinkers. Examples of suitable at least trifunctional amines or carboxylic acids are described in EP-A-0 345 648. The at least trifunctional amines have at least three amino groups which are capable of reaction with carboxylic acid groups. They preferably do not have any carboxylic acid groups. The at least trifunctional carboxylic acids have at least three carboxylic acid groups which are capable of reaction with amines and which can also be present, for example, in the form of their derivatives, such as esters. The carboxylic acids preferably do not contain any amino groups capable of reaction with carboxylic acid groups. Examples of suitable carboxylic acids are trimesic acid, trimerized fatty acids, prepared for example from oleic

acid and having from 50 to 60 carbon atoms, naphthalenepolycarboxylic acids, such as naphthalene-1,3,5,7-tetracarboxyIic acid. The carboxylic acids are preferably defined organic compounds and not polymeric compounds. Examples of amines having at least 3 amino groups are nitrilotrialkylamine, especially nitrilotriethaneamine, dialkylenetriamines, especially diethylenetriamine, trialkylenetetramines and tetraalkylenepentamines, the alkylene moieties preferably being ethylene moieties. Furthermore, dendrimers can be used as amines. Dendrimers preferably have the general formula I
(R2N-(CH2)n)2N-(CH2)x-N((Ch2)n.NR2)2 (I)
where
R is H or -(CH2)n-NRl2, where Rl is H or -(CH2)n-NR22, where R2 is H or -(CH2)n-NR3 2where R3 is H or -(CH2)n-NH2, n is an integer from 2 to 6, and x is an integer from 2 to 14.
Preferably, n is 3 or 4, especially 3, and x is an integer from 2 to 6, preferably from 2 to 4, especially 2. The radicals R can also have the stated meanings independently of one another. Preferably, R is a hydrogen atom or a -(CH2)n-NH2 radical.
Suitable carboxylic acids are those having from 3 to 10 carboxylic acid groups, preferably 3 or 4 carboxylic acid groups. Preferred carboxylic acids are those having aromatic and/or heterocyclic nuclei. Examples are benzyl, naphthyl, anthracene, biphenyl, triphenyl radicals or heterocycles such as pyridine, bipyridine, pyrrole, indole, furan, thiophene, purine, quinoline, phenanthrene, porphyrin, phthalocyanin, naphthalocyanin. Preference is given to 3,5,3\5'-biphenyltetracarboxylic acid, phthalocyanin, naphthalocyanin, 3,5,3\5'-biphenyltetracarboxyiic acid,

1,3,5,7-naphthaienetetracarboxylic acid, 2,4,6-pyridinetricarboxylic acid,
3,5,3'5'-bipyridyltetracarboxylicacid3,5,3,'.5'-benzophenonetetracarboxylic acid, 1,3,6,8-acridinetetracarboxylic acid, particularly preferably 1,3,5-benzenetricarboxylic acid (trimesic acid) and 1,2,4,5-benzenetetracarboxylic acid. Such compounds are commercially available or can be prepared by the process described in DE-A-4 312 182. If ortho-substituted aromatic compounds are used, imide formation is preferably prevented through the choice of suitable reaction temperatures.
These substances are at least trifiinctional, preferably at least tetrafunctional. The number of functional groups can be from 3 to 16, preferably from 4 to 10, particularly preferably from 4 to 8. The processes of the invention are carried out using either at least trifiinctional amines or at least Afunctional carboxylic acids, but not mixtures of such amines or carboxylic acids. However, small amounts of at least trifiinctional amines may be present in the Afunctional carboxylic acids, and vice versa.
The substances are present in an amount from 1 to 50 /xmol/g of polyamide, preferably from 1 to 35, particularly preferably 1 to 20, μ mol/g of polyamide. The substances are preferably present in an amount from 3 to 150, particularly preferably from 5 to 100, especially from 10 to 70, μ mol of equivalents/g of polyamide. The equivalents are based on the number of functional amino groups or carboxylic acid groups.
Difiinctional carboxylic acids or difunctional amines as chain lengtheners. These have 2 carboxylic acid groups which can be reacted with amino groups, or 2 amino groups which can be reacted with carboxylic acids. The difunctional carboxylic acids or amines, as well as the carboxylic

acid groups or amino groups, do not contain any further functional groups capable of reaction with amino groups or carboxylic acid groups. Preferably, they do not contain any further functional groups. Examples of suitable difunctional amines are those which form salts with difunctional carboxylic acids. They can be linear aliphatic, such as CM4-alkylenediamine, preferably C2_6-alkylenediamine, for example hexylenediamine. They can also be cycloaliphatic. Examples are; isophoronediamine, dicycycan, laromine. Branched aliphatic diamines are likewise usable, an example being Vestamin TMD (trimethylhexamethylenediamine, from Hiils AG). In addition, the diamines can also be aromatic-aliphatic, it being possible to use n-xylylenediamine for example. Entire amines can each be substituted by CM2-alkyl, preferably C1-14-alkyl, radicals on the carbon skeleton. Difunctional carboxylic acids are for example those which form salts with difunctional diamines. They can be linear aliphatic dicarboxylic acids, which are preferably C4_20-dicarboxylic acids. Examples are adipic acid, azelaic acid, sebacic acid, suberic acid. They can also be aromatic. Examples are isophthalic acid, terephthalic acid, naphthalenedicarboxylic acid, as well as dimerized fatty acids.
The difunctional basic building blocks (c) are preferably used in amounts from 1 to 55, particularly preferably from 1 to 30, especially from 1 to 15, μm/g of polyamide.
According to the invention, the product mixture obtained in step 3, or the second liquid or second solid phase or the mixture of second liquid and second solid phase (from step 4) which each comprise the polyamide, preferably a polymer melt, is discharged from the reaction vessel in a conventional manner, for example by means of a pump. Subsequently, the polyamide obtained can be worked up according to conventional methods,

as described for example in DE-A 43 21 683 (page 3 line 54 to page 4 line 3) at length.
In a preferred embodiment, the level of cyclic dimer in the nylon-6 obtained according to the invention can be further reduced by extracting the polyamide first with an aqueous solution of caprolactam and then with water and/or subjecting it to a gas phase extraction (described in EPrA 28 49 68, for example). The low molecular weight constituents obtained in this aftertreatment, such as caprolactam, linear caprolactam oligomer and cyclic caprolactam oligomer, can be recycled into the first and/or second and/or third step.
The starting monomer or monomer mixture can be admixed in all steps, preferably in the fourth step, with customary additives and fillers such as pigments, especially titanium dioxide (anatase and/or rutile), silicon dioxide and talcum, chain regulators such as aliphatic and aromatic carboxylic and dicarboxylic acids such as propionic acid, acetic acid, benzoic acid, terephthalic acid and also triacetonediamine, stabilizers such as copper(I) halides and alkali metal halides, nucleating agents such as magnesium silicate or boron nitride, catalysts such as phosphorous acid and also antioxidants in amounts within the range from 0.01 to 5, preferably within the range from 0.2 to 2, % by weight, based on the amount of monomers used. The present invention further relates to a polyamide preparable by
(1) reacting at least one aminonitrile with water at a temperature from 100 to 360°C and a pressure from 0.1 to 35 x 106 Pa to obtain a reaction mixture,
(2) further reacting the reaction mixture at a temperature from 150

to 400°C and a pressure which is lower than the pressure in step 1, the temperature and the pressure being selected so as to obtain a first gas phase and a first liquid or a first solid phase or a mixture of first solid and first liquid phase, and separating the first gas phase from the first liquid or the first solid phase or from the mixture of first liquid and first solid phase, and
admixing the first liquid or the first solid phase or the mixture of first liquid and first solid phase with a gaseous or liquid phase comprising water at a temperature from 150 to 360°C and a pressure from 0.1 to 30 x 106 Pa to obtain a product mixture,
i
a polyamide preparable by j
reacting at least one aminonitrile with water at a temperature from 100 to 360°C and a pressure from 0.1 to 35 x 106 Pa to obtain a reaction mixture,
further reacting the reaction mixture at a temperature from 150 to 400°C and a pressure which is lower than the pressure in step 1, the temperature and the pressure being selected so as to obtain a first gas phase and a first liquid or a first solid phase or a mixture of first solid and first liquid phase, and separating the first gas phase from the first liquid or the first solid phase or from the mixture of first liquid and first solid phase, and
admixing the first liquid or the first solid phase or the mixture

of first liquid and first solid phase with a gaseous or liquid
phase comprising water at a temperature from 150 to 360°C and
a pressure from 0.1 to 30 x 106 Pa to obtain a product
mixture,
postcondensing the product mixture at a temperature from 200 to 350°C and a pressure which is lower than the pressure of step 3, the temperature and pressure being selected so as to obtain a second, water- and ammonia-comprising gas phase and a second liquid or second solid phase or a mixture of second liquid and second solid phase, which each comprise the polyamide, and
a polyamide preparable by
reacting at least one aminonitrile with water at a temperature from 100 to 360°C and a pressure from 0.1 to 35 x 106 Pa to obtain a reaction mixture,
further reacting the reaction mixture at a temperature from 150 to 400 °C and a pressure which is lower than the pressure in step 1, the temperature and the pressure being selected so as to obtain a first gas phase and a first liquid or a first solid phase or a mixture of first solid and first liquid phase, and separating the first gas phase from the first liquid or the first solid phase or from the mixture of first liquid and first solid phase, and
postcondensing the first liquid or first solid phase or the mixture of first liquid and first solid phase at a temperature from 200

to 350°C and a pressure which is lower than the pressure of step 3, the temperature and pressure being selected so as to obtain a second, water- and ammonia-comprising gas phase and a second liquid or second solid phase or a mixture of second liquid and second solid phase, which each comprise the polyamide.
The polyamides of or obtained according to this invention, especially nylon-6 and its copolymers, can be used for manufacturing fibers and materials of construction.

EXAMPLES
Example 1
i
This example explains the present invention by the reaction of ACN. The AEG (amino end group) and CEG (carboxyl end group) arb determined by the method described in WO 95/01389 (page 6 line 35 to page 7 line 40).
The volatile bases are determined by the method of Parnas-Wagner by hydrolyzing the polyamide with HC1, liberating the bases with NaOH, then steam distilling the liberated bases by the method of Parnas into a flask containing HC1 and finally back-titrating the excess HC1 with NaOH. The difference between HC1 used in the receiving flask and back-titrated HC1 can be used to calculate the level of volatile bases (in mg of NH3/kg).
The nitrile group conversion was determined by FTIR spectroscopy by means of the characteristic CN group band at 2247 cm"1. The relative viscosity (RV) was determined at 25°C and a concentration of 1 g of polymer per 100 ml in 96 % strength by weight sulfuric acid. In all the runs listed, the step 4 postcondensation was carried out batchwise in a laboratory autoclave: 3 h, 250°C, 105 Pa (1 bar). The results are shown in Table 1.
Example 2
The table below shows the experimental conditions in steps 1 and 2. The temperature in step 4 was 270°C, the pressure was 105 Pa (1 bar) and the residence time was 1.5 h.

RT = residence time
WA = water add in %, based on feed stream of ACN/water mixture
in step 1
Comparative examples
The table below shows the parameters of products prepared according to the prior art - Example 1 of US 5 109 104 and Example 1 of US 2 245 129.

We claim:
1. A process for preparing a polyamide by reaction of at least one
aminonitrile with water, which comprises the following steps:
(1) reacting at least one aminonitrile with water at a temperature from 100 to 360°C and a pressure from 0.1 to 35 x 106 Pa to obtain a reaction mixture,
(2) further reacting the reaction mixture at a temperature from 150
to 400 °C and a pressure which is lower than the pressure in : step 1, the temperature and the pressure being selected so as to obtain a first gas phase and a first liquid or a first solid phase or a mixture of first solid and first liquid phase, and separating the first gas phase from the first liquid or the first solid phase or from the mixture of first liquid and first solid phase, and
(3) admixing the first liquid or the first solid phase or the mixture
of first liquid and first solid phase with a gaseous or liquid
phase comprising water at a temperature from 150 to 360 °C
and a pressure from 0.1 to 30 x 106 Pa to obtain a product
mixture.
2, A process for preparing a polyamide by reaction of at least one
aminonitrile with water, which comprises the following steps: (1) reacting at least one aminonitrile with water at a temperature
from 100 to 360°C and a pressure from 0.1 to 35 x 106 Pa
to obtain a reaction mixture,

uv to 400°C and a pressure which is lower than the pressure in step 1, the temperature and the pressure being selected so as to obtain a first gas phase and a first liquid or a first solid phase or a mixture of first solid and first liquid phase, and separating the first gas phase from the first liquid or the first solid phase or from the mixture of first liquid and first solid phase, and
(3) admixing the first liquid or the first solid phase or the mixture of first liquid and first solid phase with a gaseous or liquid phase comprising water at a temperature from 150 to 360°C and a pressure from 0.1 to 30 x 106 Pa to obtain a product mixture,
(4) postcondensing the product mixture at a temperature from 200 to 350°C and a pressure which is lower than the pressure of step 3, the temperature and pressure being selected so as to obtain a second, water- and ammonia-comprising gas phase and a second liquid or second solid phase or a mixture of second liquid and second solid phase, which each comprise the polyamide.
3. A process for preparing a polyamide by reaction of at least one
aminonitrile with water, which comprises the following steps:
(1) reacting at least one aminonitrile with water at a temperature
from 100 to 360°C and a pressure from 0.1 to 35 x 106 Pa
to obtain a reaction mixture,

(2) further reacting the reaction mixture at a temperature from 150 ;
to 400°C and a pressure which is lower than the pressure in step 1, the temperature and the pressure being selected so as to obtain a first gas phase and a first liquid or a first solid phase or a mixture of first solid and first liquid phase, and separating the first gas phase from the first liquid or the first solid phase or from the mixture of first liquid and first solid phase, and
(4) postcondensing the first liquid or the first solid phase or the mixture of first liquid and first solid phase at a temperature from 200 to 350°C and a pressure which is lower than the
pressure of step 3, the temperature and pressure being selected
i
so as to obtain a second, water- and ammonia-comprising gas phase and a second liquid or second solid phase or a mixture of second liquid and second solid phase, which each comprise the polyamide.
4. A process as claimed in claim 1 or 2, wherein the temperature and pressure in step 1 or in step 3 or in both step 1 and step 3 are selected so as to obtain a liquid or a solid phase or a mixture of liquid and solid phase and a gaseous phase, and die gaseous phase is separated off.
5. A process as claimed in any of the preceding claims, wherein the reaction of step 1 is carried on to a nitrile group conversion of at least 95 mol%, based on the moles of aminonitrile used.
6. A process as claimed in any of claims 1, 2, 4 and 5, wherein, in step 3, the gaseous or liquid phase comprising water is added in

an amount from 50 to 1500 ml of water per 1 kg of first liquid or first solid phase or mixture of first liquid and first solid phase.
A process as claimed in any of the preceding claims, wherein steps 1 to 3, 1, 2 and 4 or 1 to 4 are carried out continuously.
A process as claimed in any of the preceding claims, wherein at least one of the gas phases obtained in the respective steps is recycled into at least one of the preceding steps.
A process as claimed in any of the preceding claims, wherein the aminonitrile used is an ca-aminoalkyl nitrile having an alkylene moiety (-CH2-) of from 4 to 12 carbon atoms or an aminoalkylaryl nitrile having 8 to 13 carbon atoms.
A process as claimed in any of the preceding claims, wherein the
following mixture is used as aminonitrile:
from 50 to 99.99% by weight of 6-aminocapronitrile,
from 0.01 to 50% by weight of at least one dicarboxylic acid
selected from the group consisting of aliphatic
C4-C10-a,o;-dicarboxylic acids, aromatic C8-CI2-dicarboxylic acids
and C5-Cg-cycloalkanedicarboxylic acids,
from 0 to 50% by weight of an α,ω-diamine having 4-10 carbon
atoms,
from 0 to 50% by weight of an α,ω-C2-C12-dinitrile, and
from 0 to 50% by weight of an α,ω-C5-C12-aniino acid or the
corresponding lactam,
the individual weight percentages adding up to 100%.

A process as claimed in any of the preceding claims, wherein a chain lengthening or a chain branching or a combination thereof is carried out.
A polyamide preparable by
(1) reacting at least one aminonitrile with water at a temperature from 100 to 360°C and a pressure from 0.1 to 35 x 106 Pa to obtain a reaction mixture,
(2) further reacting the reaction mbcture at a temperature from 150 to 400 °C and a pressure which is lower than the pressure in step 1, the temperature and the pressure being selected so as to obtain a first gas phase and a first liquid or a first solid phase or a mixture of first solid and first liquid phase, and separating the first gas phase from the first liquid or the first solid phase or from the mixture of first liquid and first solid phase, and
(3) admixing the first liquid or the first solid phase or the mixture
of first liquid and first solid phase with a gaseous or liquid
i i
phase comprising water at a temperature from 150 to 360°C and a pressure from 0.1 to 30 x 106 Pa to obtain a product mixture.
A polyamide preparable by
(1) reacting at least one aminonitrile with water at a temperature from 100 to 360°C and a pressure from 0.1 to 35 x 106 Pa to obtain a reaction mixture,
(2) further reacting the reaction mixture at a temperature from 150 to 400°C and a pressure which is lower than the pressure in step 1, the temperature and the pressure being selected so as to obtain a first gas phase and a first liquid or a first solid

phase or a mixture of first solid and first liquid phase, and separating the first gas phase from the first liquid or the first solid phase or from the mixture of first liquid and first solid phase, and
(3) admixing the first liquid or the first solid phase or the mixture of first liquid and first solid phase with a gaseous or liquid phase comprising water at a temperature from 150 to 360°C and a pressure from 0.1 to 30 x 106 Pa to obtain a product mixture,
(4) postcondensing the product mixture at a temperature from 200 to 350 °C and a pressure which is lower than the pressure of step 3, the temperature and pressure being selected so as to obtain a second, water- and ammonia-comprising gas phase and a second liquid or second solid phase or a mixture of second liquid and second solid phase, which each comprise the poly amide.
A polyamide preparable by
(1) reacting at least one aminonitrile with water at a temperature from 100 to 360°C and a pressure from 0.1 to 35 x 106 Pa to obtain a reaction mixture,
(2) further reacting the reaction mixture at a temperature from 150 to 400°C and a pressure which is lower than the pressure in step 1, the temperature and the pressure being selected so as to obtain a first gas phase and a first liquid or a first solid phase or a mixture of first solid and first liquid phase, and separating the first gas phase from the first liquid or the first ! solid phase or from the mixture of first liquid and first solid phase, and
(4) postcondensing the first liquid or first solid phase or the

mixture of first liquid and first solid phase at a temperature from 200 to 350°C and a pressure which is lower than the pressure of step 3, the temperature and pressure being selected so as to obtain a second, water- and ammonia-comprising gas phase and a second liquid or second solid phase or a mixture of second liquid and second solid phase, which each comprise the polyamide.
15. A process for preparing a polyamide by reaction
i
of at least one aminonitrile with water, substantially as herein described and exemplified.

Documents:

mas-1997-1915-abstract.pdf

mas-1997-1915-claims duplicate.pdf

mas-1997-1915-claims original.pdf

mas-1997-1915-correspondance others.pdf

mas-1997-1915-correspondance po.pdf

mas-1997-1915-descripton complete duplicate.pdf

mas-1997-1915-descripton complete original.pdf

mas-1997-1915-form 1.pdf

mas-1997-1915-form 26.pdf

mas-1997-1915-form 3.pdf

mas-1997-1915-other document.pdf

mas-1997-1915-pct.pdf

« Previous Patent

Next Patent »

Patent Number

204465

Indian Patent Application Number

1915/MAS/1997

PG Journal Number

26/2007

Publication Date

29-Jun-2007

Grant Date

22-Feb-2007

Date of Filing

29-Aug-1997

Name of Patentee

BASF AKTIENGESELLSCHAFT

Applicant Address

67056 LUDWIGSHAFEN, FEDERAL REPUBLIC OF GERMANY.

Inventors:

#	Inventor's Name	Inventor's Address
1	ROBERT WEIB	TRIFTWEG 25, 67281 KIRCHHEIM
2	DIETER KRAUB	LANGGASSE 38, 67269 GRUNSTADT
3	DIETER KELLER	BERLINER STR.3, 67269 GRUNSTADT
4	GUNTER PIPER	SCHLANGENTHALER WEG 10, 67098 BAD DURKHEIM
5	WOLFGANG HARDER	SCHLANGENTHALER WEG 10, 67098 BAD DURKHEIM.
6	ALFONS LUDWING	WEINTALSTR.28, 37271 HOXTER
7	RALF MOHRSCHLADT,	STERNALLEE 5, 68723 SCHWETZINGEN

PCT International Classification Number

C08G69/00

PCT International Application Number

N/A

PCT International Filing date

PCT Conventions:

#	PCT Application Number	Date of Convention	Priority Country
1	197 09 360.6	1997-03-07	Germany
2	196 35 077.8	1996-08-30	Germany