Title of Invention

"A POLYMERIC MATERIAL SUITABLE FOR PREAPARING BIAXIBILITY-ORIENTED FILMS AND CONTAINES"

Abstract A polymeric material suitable for preparing biaxially-oriented films and containers having high characteristic of resistance to gas permeability, obtained by mixing a melted material under such conditions that the polymeric components thereof are rheologicaiiy compatible, comprising: an aromatic polyester resin, premixed with a dianhydride of a tetracarboxylic acid, In an amount between 0.01 and 3% by weight; a polyamide derived from m-xylyiene diamine and from a dicarboxyiic acid with 6-22 carbon atoms in an amount equal to 1 to 90% by weight on the sum of a) + b).
Full Text The present invention relates to biaxially-oriented films and containers provided with high resistance to gas permeability, and to the polymeric materials used to prepare said containers and films.
Aromatic polyester resins are used in ever-increasing amounts in the production of beverage containers and films.
The barrier properties of aromatic polyester resins are rather limited. In the case of containers for carbonated beverages prepared from said resins, the possibility to preserve the beverages for a sufficiently long time is uncertain.
Polyamide resins have remarkable mechanical properties, but they have the drawback that they have a high moisture absorption which reduces their properties.
Polyamide resins are normally used mixed with aromatic polyester resins in order to improve the mechanical characteristics of the latter. The presence of polyester resin in the mix reduces the moisture-absorbing tendency of polyamide resins.
Mixing the resins, however, is difficult because of their poor compatibility in the melted state.
In order to obtain better mechanical properties and to avoid peeling in products, it has been suggested to mix the resins in the extruder in the presence of a dianhydride of a tetracarboxylic acid (JP 1-272660 Kokai).
Pyromellitic anhydride is the preferred compound.
The mechanical properties of the resulting mixtures can be improved further by subjecting the mixtures to a solid-state polycondensation treatment (WO 94/09069).
Among polyamides, the most commonly used polyamides, such as nylon 6 and 66, have slightly better gas barrier properties than polyester resins

2
such as polyethylene terephthalate (PET) and copolyethylene terephthalates containing small proportions of units derived from isophthalic acid.
However, a polyamide obtained from m-xylylene diamine and adipic acid (poly-m-xylylene adipamide, poly MXD-6) is known as having considerable gas barrier properties (in relation to oxygen and carbon dioxide) which are distinctly better than those of polyethylene terephthalate.
This polyamide is used in mixture (obtained in an extruder) with PET or COPET in order to improve their barrier properties.
The oxygen permeability of a 1.5-liter PET bottle (produced by injection blow-molding) is reduced by approximately 50% when the bottle is obtained from a mixture which contains 16% by weight of polyamide and by approximately 20% when it contains 7% polyamide by weight.
The barrier properties of the 16% polyamide mixture are similar to those of a bottle formed of a two-layer film, one layer being PET and the other one being polyamide.
It has now been found unexpectedly that it is possible to remarkably improve the barrier properties of biaxially-oriented films and containers which can be obtained from polyester resins used in a mixture with a polyamide such as poly MXD-6 if the polyester resin is first mixed in the melted state with a dianhydride of a tetracarboxylic acid and the resulting mixture is further mixed, again in the melted state, with a polyamide such as poly MXD-6, working under temperature and shear forces conditions and with.viscosities of the melted polymeric components such as to render the polymeric components of the mixture compatible from the Theological viewpoint. The dianhydride is mixed with the polyester resin in an amount from 0.01 to 3% by weight.
Pyromellitic dianhydride is preferred. Other dianhydrides that can be used are dianhydrides of 1, 2, 3, 4-cyclobutane tetracarboxylic acid,

3
3,3':4,4'-benzophenone tetracarboxylic acid, 2,2 bis-(2,4-dicarboxyphenyl)ether. The dianhydrides of aromatic tetracarboxylic acids are preferred.
Preferably, the polyester resin is a copolyethylene terephthalate in which up to 25%, preferably 1 to 15%, of the units derived from terephthalic acid are substituted by units or sequences derived from isophthalic acid or from mixtures thereof with naphthalene dicarboxylic acids.
The polyamide is preferably poly MXD-6. Other polyamides that can be used are those obtainable from an aliphatic dicarboxylic acid other than adipic acid containing 6 to 22 atoms of carbon and an arilene diamine, preferably m-xylylene diamine.
Said dicarboxylic acid is preferably suberic, sebacic and dodecanoic acid.
Polyamides with crystallization rates similar to those of polyester are preferably used.
The numeral molecular weight of the starting polyamide is generally between 8000 and 50000.
The terminal-NH2 groups of the starting polyamide can be reacted with epoxy compounds in order to increase its dispersion in the polyester matrix. Epikote from the Shell Italia is an example of usable epoxi compounds.
Preferably, the polyamide is used in an amount equal to 5 to 30% by weight on the mixture. Larger amounts can be used depending on the final properties of the mixture.
It is in fact possible, and it is another aspect of the invention, to prepare, operating according to the method of the invention, mixtures having a polyamide content of more than 50% by weight and up to 80-90% by weight which can be used as master batch.
A preferred mixing process consists in extruding the polyester resin with the addition of the dianhydride and in subsequently extruding the mixture with the addition of the polyamide.

4
It is possible to work in a single stage by premising in the extruder the
polyester and dianhydride first and then adding the polyamide in the
extruder.
In order to achieve good compatibilization among the polymeric
components, their viscosities in the melted state has to be very similar. Preferably, the ratio between the viscosity of the polyester and the
viscosity of the polyamide is between 0.2:1 and 4:1.
Operating under the above conditions it is possible to obtain
compositions wherein the polyamide is dispersed in the polyester matrix with domains having size of less than 1 micron, preferably in the range from 0.2 to 0.4 micron. The rnicrostructure was obtained by scanning electron microscope (S.E.M.) of the fracture surface of injection molded small bars treated with formic acid to extract the polyamide. The bars obtained according to example 1 have a rnicrostructure wherein the dispersed phase has a size of less than 0.5 micron. The size of the domains in the bars obtained from example 1 but without using PMDA are higher than 1.5 micron as average. The microstructure according to the invention is characteristic in particular of the blends of poly MXD-6 with PET or copolyethylene thereftalates containing up to 25% of units deriving from isophtalic acid.
It is surprising that when working under the mixing conditions according to the invention it is possible to obtain materials having gas barrier properties (relative to O2 and CO2) which are far higher than those obtainable by mixing the polyester resin and the polyamide in the absence of the dianhydride of tetracarboxylic acid or by mixing the three components of the mixture simultaneously or by first mixing the poiyamide with the dianhydride and then adding the polyester resin.
Oxygen permeability in 1.5-liter bottles with an average thickness of 225 microns can be reduced of 4 or more times and CO2 permeability can be reduced by 2 or more times as a function of the content of the polyamide

5
(pMXD-6).
The polyester resin is obtained by polycondensation (according to known methods) of terephthalic acid or lower diesters thereof with a diol with 2-12 carbon atoms, such as for example ethylene glycol, 1,4-butanediol and 1,4-cyclohexane dimethylol. The copolyethylene terephthalate is, as mentioned, the preferred resin for preparing containers.
The polyethylene terephthalate homopolymer can be conveniently used in the preparation of biaxially-oriented films.
The starting polyester resin used in the preparation of the compositions according to the invention has an intrinsic viscosity of 0.3 to 0.8 dl/g. The initial viscosity can be increased by subjecting the resin, premised with the dianhydride of the tetracarboxylic acid or the mixture containing the polyester resin, the polyamide and the dianhydride, to a solid-state polycondensation treatment at temperatures between approximately 150 and 230°C for a time and at temperature conditions sufficient to increase by at least 0.1 units the viscosity of the polyester resin.
Since the polyester resin is difficult to separate by solvent extraction in the mixture, the increase in intrinsic viscosity of the polyester resin in the mixture is considered similar to the increase in the polyester resin when it is treated alone in the same temperature and duration conditions to which the mixture has been subjected.
The solid-state polycondensation treatment, in addition to leading to an increase in the intrinsic viscosity of the polyester resin, allows to improve the mechanical properties of the compositions, particularly impact resistance.
The treatment applied to the polyester resin added of the dianhydride of the tetracarboxylic acid allows to bring the viscosity of the resin in the melted state to values which are similar to those of the polyamide resin, particularly when the initial polyester resin has relatively low intrinsic viscosity values.

6
The mixing of the polyester with the dianhydride and then with the polyamide is performed in a single- or twin-screw extruder. Contrarotating and interroeshing twin-screw extruders are preferred, using residence times . of generally less than 180 seconds and working at temperatures above the melting temperatures of the polymeric components, generally between 200° and300°C,
The biaxially oriented films and containers are prepared according to known methods. For example, bottles for beverages are prepared by injection-stretch blow molding; biaxially oriented films are prepared with the double-bubble method or by cast-extrusion followed by biaxial stretching.
The material according to the invention can also be used to prepare multilayer films comprising, as a core layer, a biaxially oriented film obtained from the material according to the invention.
Another application of the blends according to the invention, wherein the polyester resin is a copolyetliylene therephtfaalate with 10% or more of units from isophthalic acid resides in the preparation by free blowing of preforms of high capacity pouches (5 1. or more) suitable for being filled with liquids such as soft drinks or others.
The pouches have high clarity and good mechanical properties. They can be easily folded without breakage or stress withening problems.
The intrinsic viscosity is measured in solutions of 0.5 g of resin in 100 ml of 60/40 solution by weight of phenol and tetrachloroethane, at 25°C according to ASTM standard D 4603-86.
The measurement of the malt viscosity is performed with a Goettfert rheometer equipped with a 2-mm capillary tube, working at 280°C with a shear rate of 100 sec"1. EXAMPLES
The following examples are given to illustrate but not to limit the invention.

7
EXAMPLE 1
20 kg/h of crystallized granules of copolyethylene terephthalate (COPET) containing 4.5% isophthalic acid (IPA) with IV = 0.6 dl/g (pre-dried at 140°C in vacuum for at least 12 h) are fed together with 20 g/h of pyromellitic dianhydride (PMDA) (0.1% by weight on the COPET) in a twin-screw extruder with contrarotating and intermeshing screws and then pelletized.
The operating conditions are:
Screw rotation rate: 100 rpm
Cylinder temperature: 280°C throughout the cylinder - COPET feed: 20 kg/h
PMDA feed: 20 g/h
Residence time: 1.5 min
The resulting pellets were crystallized at 130°C in a reactor in continuous under nitrogen flow.
IV after extrusion was 0.61 dl/g.
20 kg/h of crystallized COPET containing 0.1% PMDA obtained as mentioned above are fed into a twin-screw extruder provided with contrarotating and intermeshing screws together with 2.2 kg/h of poly-MXD-6 (Mitsubishi Gas Chemical - MGC - Japan) having a viscosity in the molten state at 280°C and 100 sec1 of shear rate of 1000 PAS and pelletized.
The conditions for preparing the mixture are the same used for the treatment of COPET with the addition of PMDA.
EXAMPLE 2
Preparation of the mixture of COPET and PMDA of example 1 is repeated, the only difference being that COPET with 4.5% isophthalic acid is replaced with a mixture containing 92/8 by weight of COPET with 2% isophthalic acid, IV = 0.8 dl/g and 8% polyethylene isophthalate.
The IV of the pellets was 0.81 dl/g. The pellets are crystallized at 130°C

8
in a reactor operating continuously in nitrogen.
The pellets are then extruded together with 10% by weight of poly MXD-6 in the conditions of example 1.
EXAMPLE 3
The preparation of example 1 (premixing of COPET with PMDA and subsequent extrusion with 10% poly MXD-6) was repeated, with the only difference that the COPET used contained 2% isophthalic acid and had an IVof0.6dyg.
EXAMPLE 4
The preparation of example 1 was repeated, with the only difference that the mixture contained 70% by weight of poly-MXD-6.
EXAMPLE 5
A composition, prepared according to example 1, by using in place of COPET containing 45% IPA a mixture containing S6% by weight of COPET with 2% of IPA (IV = 0.8 dl/g) and 14% of polyethylene isophthalate, and in which the percentage of poly-MXD was 7.5% by weight, was used to prepare 40 g preforms.
The preforms were submitted to free blowing using a Sidel machine equipped with an infrared heater to heat the preforms to 110°. The preforms were blown using air at 3 bar pressure. The obtained pouches have a capacity of 5 1. and are highly clear. They can be folded (when empty) ami refilled with liquids.
The pouches filled with 51. water can withstand a drop impact of 1 m. ,
¦ft1*/* A ¦* #TVT yo *o* T
EXAMPLES 6,7
The mixtures obtained according to examples 1-4 were used to produce 36-g preforms using a Husky injection unit.
The preforms were then blown in a 1.5- and 2-liter cavity to produce bottles by stretch-blow molding. The thickness of the 1.5-liter bottles was 225 microns (average value) and the thickness of the 2-liter bottles was 195 microns (average value).

9
The permeability characteristics of the bottles with respect to O2 and C02 are listed in table 1. Gas permeability was measured at 18°C, 40% RH, using Mocon instruments.
COMPARISON EXAMPLE 1
The preparation of example 1 was repeated, the only difference being that a mixture with 90/10 by weight of COPET (containing 2% IP A, with IV = 0.8 dl/g) and of poly MXD-6, not containing PMDA, was extruded.
1.5-liter bottles were prepared by injection-blow molding in the conditions used in examples 6-7.
The permeability to O2 and CO2 of the bottles was much higher than in the bottles of examples 6-7.
COMPARISON EXAMPLE 2
1.5-liter bottles were prepared in the conditions of examples 6-7, using a resin formed by COPET with 2% IPA and IV=0.8 dl/g.
The data on O2 and CO2 permeability are listed in table 1.

10
TABLE i MIXTURES

% weight pMXD-6
%IPA
O2 permeability
1.5-liter bottles ml/bott/d/atm
2-liter bottles
C02 permeability
1.5-liter bottles ml/bott/d/atm
Improvement %
O2 permeability
1.5-liter bottles
2-liter bottles
CO2 permeability
1.5-litcr bottles


Comparison 2 Example 1 Example 2 Example 3 Example 4
0 10 10 10 70
2 4.5 10 2 4.5
0.53 0.13 0.1 0.12
0.62 0.23 0.14 0.14
18.2 7.25 5.31 7.02 2.7
407 550 449
362 578 567
251 343 250 670

11
WE CtAiM
1. A polymeric material suitable for preparing biaxialiy-oriented films and
containers having high characteristic of resistance to gas permeability,
obtained by mixing a melted material under such conditions that the
polymeric components thereof are ideologically compatible, comprising:
a) an aromatic polyester resin, premixed with a dianhydride of a
tetracarboxyllc acid, In an amount between 0.01 and 3% by weight;
b) a polyamide derived from m-xylylene diamine and from a
dicarboxylic acid with 6-22 carbon atoms in an amount equal to 1 to
90% by weight on the sum of a) + b).

2. A material as claimed in claim 1, wherein the polyester resin is
copoiyethylene terephthalate containing up to 25% of units derived from
isophthaiic acid.
3. A material as claimed in claims 1-2, wherein the polyamide is poiym-
xylyfene adipamide.
4. A polymeric material as claimed in claims 1-3, wherein the dianhydride is
pyromellttic dianhydride is pyromellftfc dianhydride.
5. A polymeric material as claimed in claims 1-4, wherein the material
obtained from the metted mixture comprising the components a),b) and c)
is subjected to solid-state polycondensation until the intrinsic viscosity of
the starting polyester is increased of at feast 0.1 units.
6. A polymeric material as claimed in claim 5, wherein the polyester
premixed with the dianhydride is subjected to solid-state polycondensation
until the intrinsic viscosity of the Initial polyester is increased of at least 0.1
units.
7. A polymeric material as claimed in claims 1-6, wherein the polyester and
the polyamide have melt viscosities, at the mixing temperature, in a ratio
from 0.2:1 to 4:1.

-12-
8. A polymeric material as claimed in claims 1-7, capable of providing
containers whose resistance to oxygen permeability is less than 0.065
ml/bottle/day/atm, measured on a 1.5-liter bottle with a thickness of 225
microns prepared by inject ion-blow molding.
9. A polymeric material comprising an aromatic polyester resin and a
poly amide derived from dicarboxyltc acid and an arilene diamine, wherein
the potyamide is dispersed in a polyester resin matrix with average size of
the dispersed domains of less than 1 micron.
10.A polymeric material as claimed in claim 9, wherein the average size of the dispersed domains is from 0.2 to 0.4 micron.
11.A polymeric material as claimed in claims 9-10, wherein the polyester resin is a copolyethylene terephthalate containing up to 25% of units derived from isophthalic acid and the pofyamide is poly-m-xylylene adipamide.
12.A polymeric material as claimed in claim 1, wherein said container is prepared by mixing of the said polyester and polyamide with extruder under temperature, shear force conditions and melt viscosity values of the polymeric components such as to render said components compatible from a rheological viewpoint.
13.A polymeric material as claimed in claim 1, wherein said container is made of said polymeric material which comprises of a polyester resin and a polyamide and they have an oxygen permeability of less than 0.065 mi/bottle/day/atm, measured on a 1.5-liter bottle with a thickness of 225 microns.
14.A polymeric material as claimed in claim 1, wherein said film is obtained by mixing of the said polyester and polyamide with extruder under temperature, shear force conditions and melt viscosity values of the polymeric components such as to render said components compatible from a rheological viewpoint and by biaxial-stretching of films prepared by cast extrusion.

-13
15.A polymeric material as claimed In claim 14, wherein said film is obtained by blow-molding using the double-bubble method.
A polymeric material suitable for preparing biaxially-oriented films and containers having high characteristic of resistance to gas permeability, obtained by mixing a melted material under such conditions that the polymeric components thereof are rheologicaiiy compatible, comprising: an aromatic polyester resin, premixed with a dianhydride of a tetracarboxylic acid, In an amount between 0.01 and 3% by weight; a polyamide derived from m-xylyiene diamine and from a dicarboxyiic acid with 6-22 carbon atoms in an amount equal to 1 to 90% by weight on the sum of a) + b).

Documents:

00514-cal-1999-abstract.pdf

00514-cal-1999-claims.pdf

00514-cal-1999-correspondence.pdf

00514-cal-1999-description(complete).pdf

00514-cal-1999-form-1.pdf

00514-cal-1999-form-18.pdf

00514-cal-1999-form-2.pdf

00514-cal-1999-form-3.pdf

00514-cal-1999-form-5.pdf

00514-cal-1999-letters patent.pdf

00514-cal-1999-p.a.pdf

00514-cal-1999-priority document others.pdf

00514-cal-1999-priority document.pdf

514-CAL-1999-(04-09-2012)-CORRESPONDENCE.pdf

514-CAL-1999-(23-12-2011)-CORRESPONDENCE.pdf

514-CAL-1999-(23-12-2011)-PA.pdf

514-CAL-1999-CERTIFIED COPIES(OTHER COUNTRIES)-1.1.pdf

514-CAL-1999-CERTIFIED COPIES(OTHER COUNTRIES).pdf

514-CAL-1999-CORRESPONDENCE 1.1.pdf

514-CAL-1999-CORRESPONDENCE-1.2.pdf

514-CAL-1999-FORM 13.pdf

514-CAL-1999-FORM 16.pdf

514-CAL-1999-FORM 27.pdf

514-CAL-1999-FORM-27.pdf

514-CAL-1999-OTHERS.pdf


Patent Number 202599
Indian Patent Application Number 514/CAL/1999
PG Journal Number 09/2007
Publication Date 02-Mar-2007
Grant Date 02-Mar-2007
Date of Filing 01-Jun-1999
Name of Patentee SINCO RICERCHE S.P.A
Applicant Address VIALE AZARI 110,28048 VERBANIA PALLANZA(PROV.OF VERBANIA)
Inventors:
# Inventor's Name Inventor's Address
1 HUSSAIN AL GHATA VIA DELLE PIAGGE 12- 03014 FIUGGI (PROVINCE OF FROSINONE),
2 SANDRO COBROR LARGO PALAZZO DELPRETE 3-86077 POZZILLI (PROV.OF ISERNIA)
3 TONINO SEVERINI VIA DELLE SORBE 31-00034 COLLEFERRO (PROV.OF ROMA)
PCT International Classification Number B29D 22/00.
PCT International Application Number N/A
PCT International Filing date
PCT Conventions:
# PCT Application Number Date of Convention Priority Country
1 M198A0001335 1998-06-11 Italy