Title of Invention

A SOLAR CELL AND A METHOD OF FABRICATING THE SAME

Abstract

ABSTRACT 1764/MAS/96 A SOLAR CELL AND A METHOD OF FABRICATING THE SAME The present invention relates to a solar cell comprising: an n-type semi conductive substrate having a front surface and a back surface; a first plurality of emitter regions formed in said front surface to a relatively shallow depth with a relatively lightly doped p-type concentration; a second plurality of emitter regions formed in said front surface to a substantially greater depth than said first plurality of regions with a an at least moderately doped p-type concentration, said first and second plurality of regions being interspersed; a dopant region formed in said back surface for providing a back surface field; an ohmic contact formed over said dopant region; and a first patterned ohmic electrode layer containing aluminum formed over said second plurality of emitter regions; wherein said second plurality of emitter regions is formed from a p+-type dopant of aluminum.

Full Text

This invention relates to the field of solar cells for converting solar energy into electrical energy. More particularly, this invention relates to solar cells having front and back electrodes. CROSS-REFERENCE TO PROVISIONAL APPUCATION This application claims priority based on Provisional Application Serial No. 60/004,833 filed October 5, 1995, for STRUCTURE AND FABRICATION PROCESS FOR SELF-ALIGNED LOCALLY DEEP-DIFFUSED EMITTER (SALDE) SOLAR CELL. Solar cells comprising semiconductor devices employing the photovoltaic effect for converting solar energy into electric energy have long been known. A typical solar cell comprises a semiconductive substrate provided with metal electrodes on one or more surfaces of the substrate, the electrodes being electrically cormected to the substrate at the surface. The vast majority of solar cell designs incorporate a p-n junction within the semiconductive substrate for separating the electrons and holes generated within the body of the semiconductive substrate in response to the incidence of solar radiation. The metal electrodes are characterized as either the p-type electrode, used to collect the holes or the n-type electrode, used to collect electrons. In a single-sided solar cell, both types of electrodes are located on a single major surface of the substrate. In a double-sided solar cell, the electrodes of one type are located on one major surface of the substrate, while the electrodes of the other type are located on the other major surface of the substrate. A common double-sided cell configuration provides a single common electrode on the back surface of the cell and a plurality of electrodes on the front surface of the cell. This plurality of electrodes is made up of a plurality of essentially metal stripes ohmically interconnected by means of a bus bar stripe. Known techniques for forming the metal stripes include evaporating aluminum onto the cell surface using a patterned mask, applying liquid aluminum to the cell surface and screen printing a mixture of aluminum and glass frit onto the cell surface in the stripe pattern. This last technique (screen printing), while convenient, suffers from the disadvantage of introducing high electrical resistance within the electrodes, since glass frit is a good electrical insulator. This disadvantage is particularly severe when the glass frit accumulates at the interface between the substrate material (typically silicon) and the aluminum alloy contact electrode. The actual location of the glass frit after formation of the electrode is dependent upon the details of the processing employed, and the process typically requires a temperature-time spike to achieve effective alloying without excessively segregating the glass frit at the interface. This requirement adds complexity to the electrode formation process, which is undesirable. Typically, the non-contacted surfaces between the metal stripes on the cell are passivated using some type of thermal oxide, such as one of the oxides of silicon. Electrons and holes can recombine at the illuminated surface of the semiconductive substrate or within the bulk of the material. Any such recombination of electrons and holes results in a reduction in solar cell conversion efficiency, and is thus highly undesirable. Recombination at the illumination surface of the semiconductor substrate can occur in both the metal-electrode contacted region and the region not covered by the metal electrode. Techniques have been explored for reducing the occurrence of electron-hole recombination at the illuminated semiconductor surface. For the metal-contacted region, the emitter of the p-n junction underlying the metal electrodes should be heavily doped (e.g. at a concentration of ~ 1x10^° cm"^ or moderately doped (~ 1x10^^ cm-3) and the junction should be relatively deep (e.g. > 2 µm) within the substrate. In contrast, for the non-contacted regions between the metal electrodes and under the passivated surface, the emitter portion of the p-n junction should be lightly doped (e.g. ~ 5x10" cm"^ and the junction should be relatively shallow (for example, about 0.2 /xm) within the substrate. Unfortunately, these two techniques pose conflicting requirements for doping the region adjacent the illumination surface of a solar cell. Although these opposing requirements can be implemented, the required processing is costly and complex, which results in a relatively high cost per cell fabricated and relatively low yield of acceptable functioning solar cells. For example, for high efficiency solar cells, the conflicting requirements of the two recombination techniques have been addressed by providing a second doped region under the electrode contact area. While this solution is effective, it requires two photolithography processing steps, two separate diffusion conditions for the emitter region, and an additional photolithography step in order to align the electrode grid pattern to the deeply diffused junction, all of which add substantial cost to the manufacturing process. Consequently, this solution is not consistent with the requirement of low cost for the fabrication of silicon solar cells for many applications. In addition to the problems imposed by the electron-hole recombination phenomenon, another problem affecting the doping process involves silicon surface passivation. In particular, an effective silicon surface passivation requires a lightly-doped p-n junction since the observed surface recombination velocity increases vAth the surface doping concentration. Efforts to date to provide a low cost solar cell with effective reduction of electron-hole recombination have not met with success. SUMMARY OF THE INVENTION The invention comprises a solar cell with reduced electron-hole recombination performance, relatively high efficiency including relatively low electrode resistance, which can be fabricated at relatively low cost using simplified fabrication techniques resulting in relatively high yield. ^/ From an apparatus standpoint, the invention comprises a solar cell comprising a semiconductive substrate having first and second surfaces, a first plurality of emitter regions formed in one of the first and second surfaces to a relatively shallow depth with a relatively low dopant concentration, a second plurality of emitter regions formed in said one of the first and second surfaces to a substantially greater depth than the first plurality of regions with a relatively higher dopant concentration than the first plurality of regions, the first and second plurality of regions being interspersed, a dopant region formed in the second one of the first and second surfaces for providing a surface field, an ohmic contact formed over the dopant region, and a first patterned ohmic electrode layer containing aluminum formed over the second plurality of emitter regions. The semiconductor substrate preferably comprises n-type doped silicon, and the first plurality of emitter regions are preferably formed using a p+ type dopant material, such as boron. The second plurality of emitter regions is preferably formed from a p+ type dopant material comprising either pure aluminum or an alloy of aluminum and silicon. The dopant region is preferably formed using an n+ type dopant material, such as phosphorus. The depth of the shallow emitter regions is preferably no greater than about 0.2 /im, and the dopant concentration is preferably no greater than about 5x10^° cm"\ The minimum depth of the second plurality of deep emitter regions is about 2 /xm, and the dopant concentration is preferably no less than about 1x10^^ cm" Accordingly the present invention relates to a solar cell comprising: an n-type semi conductive substrate having a front surface and a back surface; a first plurality of emitter regions formed in said front surface to a relatively shallow depth with a relatively lightly doped p-type concentration; a second plurality of emitter regions formed in said front surface to a substantially greater depth than said first plurality of regions with a an at least moderately doped p-type * concentration, said first and second plurality of regions being interspersed; a dopant region formed in said back surface for providing a back surface field; an ohmic contact formed over said dopant region; and a first patterned ohmic electrode layer containing aluminum formed over said second plurality of emitter regions; wherein said second plurality of emitter regions is formed from a p+-type dopant of aluminum. The present invention also provides a a method of fabricating a solar cell having self- aligned locally deep-diffused emitters, said method comprising the steps of: (a) providing an n-type semiconductive substrate having a front surface and a back surface; (b) forming a relatively shallow p-type emitter region in said front surface; (c) forming a relatively n-type field region in said back surface; (d) providing a patterned layer containing aluminum on said front surface; (e) heating said substrate to form a plurality of relatively deep p-type emitter regions in said substrate in regions underlying said patterned layer; and (f) providing an ohmic contact to said back surface. The invention will now be described more in detail with reference to the accompanying drawings, in which; FIG. 1 is a perspective view of a preferred embodiment of the invention; FIG. 2 is a bottom plan view of the Fig. 1 embodiment; FIG. 3 is an enlarged sectional view of the Fig. 1 embodiment illustrating the junctions; and FIGS. 4A-4F are schematic sectional views illustrating the fabrication of the Fig. 1 embodiment. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Turning now to the drawings, Fig. 1 is a perspective view of a single solar cell 10 incorporating the invention. As seen in this figure, the solar cell comprises a substrate 12 of a suitable semiconductive material, such as Sb-doped n-type silicon. Deployed on the upper, front illumination surface of substrate 12 is an electrode structure comprising a plurality of individual stripes or fingers 14 ohmically interconnected along one end by means of a bus bar 15. Stripes 14 and bus bar 15 are preferably fabricated from aluminum with an overcoat of a solderable ohmic material, such as silver. Located along the lower, back surface of substrate 12 is a single back electrode 17 (shown in full in Fig. 2), which is preferably composed of silver. Electrical connection to the cell 10 is made via bus bar 15 and back electrode 17. A passivation layer 18 of a suitable oxide material, such as SiOj, is formed in the areas between stripes 14 along the top surface of substrate 12. The passivation layer also extends about the circumference of substrate 12 in the region between the top and bottom surfaces thereof. Positioned on top of the passivation layer 18 is a coating 19 of a suitable antireflective material, such as titanium oxide. A silver layer 20 is located or positioned on top of the metal stripes 14 and the bus bar 15 in order to provide better ohmic contact with external circuitry. With reference to Fig. 3, the emitter structure of the solar cell comprises relatively deep emitter regions 21 underlying the metal electrode stripes 14 and relatively shallow emitter regions 22 underlying the regions of the substrate 12 surface not covered by the electrode stripes 14 and underlying the passivation layer 18. In the preferred embodiment, the emitter regions 21, 22 are p+ regions formed in the n-type substrate 12, thereby forming p-n junctions along the boundaries between the emitter regions 21, 22 and the substrate 12. The relatively deep regions 21 are at least moderately doped (~ 10^* cm'^) p-type using aluminum as the dopant material and preferably extend to a depth from the top surface in the range from about 2 to about 10 /xm. The relatively shallow emitter regions 22 are relatively Ughtly doped (~ 5x10'* cm"^) and extend to a depth from the top surface of substrate 12 no more than about 0.2 /xm. Figs. 4A-4F illustrate the process for fabricating the solar cell shown in Figs. 1-3. With reference to Fig. 4A, an n-type silicon substrate 12, preferably dendritic web silicon doped n-type with antimony, is first provided. Next, as shown in Fig. 4B, p4- and n+ layers are diffused into the upper and lower surfaces, respectively, of substrate 12. The p+ and n+ diffused layers are formed using any one of several known techniques, such as simultaneous front and back diffusion from a liquid dopant source using rapid thermal processing. The p+ dopant is preferably boron, while the n+ dopant is preferably phosphorus. The p+ layer creates the emitter for the cell and the n+ layer creates a back-surface field to repel holes from the ohmic contact to the base. The back n+ layer also promotes ohmic contact to the negative contact metal electrode 17. Next, fritless aluminum is screen printed over the front surface area in the Fig. 1 pattern, forming stripes 14 which are nominally 100 µm wide and spaced apart by approximately 1000 µm and bus bar 15. The fritless aluminum may comprise pure aluminum as well as an aluminum/silicon alloy in which the silicon concentration is less than that required to form a eutectic composition. The result of this screen printing step is illustrated in Fig. 4C. Next, the developing cell is heat treated at a temperature in the range from approximately 750°C to about lOOO^C. During this critical heat treat step, the aluminum alloys with the silicon (liquid phase) to a depth determined by the thickness of the aluminum originally deposited and in accordance with the known aluminum/silicon phase diagram. Next, the temperature is lowered and the silicon regrows by liquid phase epitaxy until the eutectic temperature (577°C) is reached. The regrown silicon is doped p-type with the aluminum in a concentration of about 10^* cm"^ The required p-n junction is formed as the aluminum concentration exceeds the donor concentration in the starting silicon, and the eutectic alloy (88.7% aluminum and 11.3% silicon, by weight) remains on the surface to serve as a contact to the p-type silicon. If the heat treatment is done in an oxygen ambient, a thin layer 18 of silicon dioxide is grown to a thickness of about 100 A on the front surface of the substrate 12 to passivate the surface and thereby reduce surface recombination. In the absence of an oxygen ambient, a passivation layer can be separately provided. The result of the heat treat processing is illustrated in Fig. 4D. It is important to note that this one process step creates a deep emitter under the grid, a contact to the deep diffused emitter, and oxide passivation of the exposed emitter surface and the sides of the cell. Next, a suitable antireflective (AR) coating 19, such as titanium oxide, is applied on the front surface of the developing ceU using a technique such as atmospheric pressure chemical vapor deposition. The result of this process step is shown in Fig. 4E. Next, an ohmic conductive metal layer 17 is screen printed and fired onto the entire back surface to form the bottom electrode and an overlayer 20 of solderable material such as silver is screen printed and fired on top of the aluminum electrode pattern 14, 15 on the front surface. The finally finished cell is illustrated in section in Fig. 4F. Solar cells fabricated according to the teachings of the invention afford a number of advantages. Firstly, the combination of deep moderately doped emitter regions under the electrodes and shallow lightly doped emitter regions under the exposed non-contacted regions acts to minimize recombination of holes and electrons in a functioning solar cell. In addition, the use of fritless aluminum enables the formation of the relatively deep emitter regions, provides a positive contact ohmic electrode material and supplies a gettering agent to remove impurities and enhance the bulk lifetime, all in a single process step. Importantly, the ohmic metal contacts to the deep diffused emitter regions are self-aligned during the heat treat process step, thereby eliminating any need for additional photolithography steps to perform the electrode alignment required in prior art processing. Further, by using fritless aluminum, the problem of lower resistance encountered in prior art processes employing a mixture of aluminum and glass frit is completely eliminated, thereby simplifying the heat treat process step. Further, the application of the solderable metal (e.g. silver layer 20) over the aluminum alloy contact electrodes 14, 15 facilitates the interconnection of many cells together in order to achieve a higher power generation capability. Lastly, the invention is tolerant of a non-uniform emitter, since the aluminum electrodes dope the underlying silicon p-type. It is even possible for the emitter to have n-type islands within the p-type region without deleterious effects. Although the p-n junction at the boundary of deep emitter regions 21 may be quite deep (i.e., in the range from about 2 to about 10 µm), since this junction is under the electrodes 14 only, it screens the base of the solar cell from the contact metal and is therefore beneficial. The depth of the alloy junction can be controlled by using an aluminum/silicon alloy as the screen printed material instead of pure aluminum. In general, as the silicon concentration in such an alloy is increased toward the eutectic composition, the amount of silicon that the printed aluminum can dissolve decreases. As a consequence, the depth of the finished junction also decreases. In addition, the minority carrier lifetime will increase in web silicon as the point defects that are quenched in during crystal growth are annealed during the heat treating step of the process. The minority carrier lifetime will also increase in other forms of silicon than dendritic web silicon because of the phenomenon of impurity gettering associated with the aluminum-silicon alloying process. Having the relatively deep p+ region 21 immediately adjacent the relatively shallow p+ region 22 provides the benefit of having a deep and moderately doped emitter under the grid and a shallow and lightly doped emitter under the passivation layer 18. The following is a specific example of solar cells fabricated according to the teachings of the invention. Dendritic web silicon strips 10 cm long and 2 1/2 cm wide by 100 µm thick were simultaneously diffused after dopant application (phosphorus and boron on opposite sides of the web strips) in a rapid thermal processing system. Aluminum paste with no glass frit was printed on the emitter side of the web strips to a thickness of 15 µm and fired at 800°C for 60 seconds in a belt furnace with an air ambient. SEM pictures of the p + diffused layer under the aluminum paste showed a junction depth of 2.4-5 µm. The fabricated solar cell had a single layer titanium oxide antireflective coating. Measured parameters for the best cell (25 cm squared area) indicated a short circuit current of 27.46 mA/cm squared and open circuit voltage of .586 V, a fill factor of .756, and an energy conversion efficiency of 12.17%. Although this process was not optimized to obtain high efficiency, the fill factor of 0.756 is considered respectable for screen printed solar cells. While the above provides a full and complete disclosure of the preferred embodiments of the invention, various modifications, alternate constructions and equivalents may be employed, as desired. For example, while the invention has been described with reference to rectangular geometry, other geometries such as circular may be employed, as desired. In addition, while specific oxide and antireflective coatings have been indicated, other oxides and other antireflective substances may also be employed. Therefore, the above description and illustrations should not be construed as limiting the scope of the invention, which is defined by the appended claims. WE CLAIM: 1. A solar cell comprising: an n-type semi conductive substrate having a front surface and a back surface; a first plurality of emitter regions formed in said front' surface to a relatively shallow depth with a relatively lightly doped p-type concentration; a second plurality of emitter regions formed in said front surface to a substantially greater depth than said first plurality of regions with an at least moderately doped p-type concentration, said first and second plurality of regions being interspersed; a dopant region formed in said back surface for providing a back surface field; an ohmic contact formed over said dopant region; and a first patterned ohmic electrode layer containing aluminum formed over said second plurality of emitter regions; wherein said second plurality of emitter regions is formed from a p+- type dopant of aluminum. 2. The solar cell as claimed in claim 1, wherein said first plurality of emitter regions are formed using a p + -type dopant of boron. 3. The solar cell as claimed in claim 1, wherein said dopant region is formed using an n + -type dopant material. 4. The solar cell as claimed in claim 3, wherein said dopant material is phosphorus. 5. The solar cell as claimed in claim 1, wherein said first plurality of emitter regions has a depth no greater than about 0.2 urn. 6. The solar cell as claimed in claim 1, wherein said first plurality of emitter i o T regions has a concentration not greater than about 5x10 cm" . 7. The solar cell as claimed in claim 1, wherein said second plurality of emitter regions has a minimum depth of about 2 um. 8. The solar cell as claimed in claim 1, wherein said ohmic contact is formed from silver. 9. The solar cell as claimed in claim I, wherein a second patterned layer of a solderable ohmic material is provided over said first patterned ohmic electrode layer. 10. The solar cell as claimed in claim 9, wherein said solderable material is silver. 11. The solar cell as claimed in claim 15 wherein a passivation layer is provided on said one of said first and second surfaces in regions between said first patterned ohmic contact layer. 12. The solar cell as claimed in claim 11, wherein an antireflective layer is provided over said passivation layer. 13. The solar cell comprising an n-type semiconductive substrate having a front surface and a back surface; a first plurality of emitter regions formed in said front surface to a relatively shallow depth with a relatively lightly doped p-type concentration; a second plurality of emitter regions formed in said front surface to a substantially greater depth than said first plurality of regions with an at least moderately doped p-type concentration, said first and second plurality of regions being interspersed; a dopant region formed in said back surface for providing back surface field; an ohmic contact formed over said dopant region; and a first patterned ohmic electrode layer containing aluminum formed over said second plurality of emitter regions; wherein said second plurality of emitter regions is formed form a p +-type dopant of an alloy of aluminum and silicon. 14. A method of fabricating a solar cell having self- aligned locally deep-diffused emitters, said method comprising the steps of: (a) providing an n-type . semiconductive substrate having a front surface and a back surface; (b) forming a . relatively shallow p-type emitter region in said front surface; (c) forming a relatively n-type field region in said back surface; (d) providing a patterned layer containing aluminum on said front surface; (e) heating said substrate to form a plurality of relatively deep p-type emitter regions in said substrate in regions underlying said patterned layer; and (f) providing an ohmic contact to said back surface. 15. The method as claimed in claim 14, wherein said relatively shallow n-type field region is formed using an n +-type dopant material. 16. The method as claimed in claim 14, wherein the step of applying an ohmic patterned layer is applied over said patterned layer containing aluminum. 17. The method as claimed in claim 14, wherein a passivation layer is formed over said one of said first and second surfaces in regions not covered by said patterned layer. 18. The method as claimed in claim 14, wherein a layer of antireflective material is formed over said passivation layer. 19. The method as claimed in claim 14, wherein said step (b) of forming is conducted to provide emitter regions having a depth no greater than about 0.2 µ.m. 20. The method as claimed in claim 14, wherein said step (b) of forming is conducted to provide emitter regions having a dopant concentration not greater than 5x1018 cm"3. 21. The method as claimed in claim 14, wherein said step (e) of heating is conducted to provide emitter regions having a minimum depth of 2 ji.m. 22. The method as claimed in claim 14, wherein said step (e) of heating is conducted to provide relatively deep emitter regions having a dopant concentration no less than lxl019 cm"3. 23. The method as claimed in claim 14, wherein said step (d) of providing is conducted with pure aluminum. 24. The method as claimed in claim 14 wherein said step (d) of providing is conducted using a mixture of aluminum and silicon. 25. A solar cell substantially as herein described with reference to the accompanying drawings. 26. A method of fabricating a solar cell substantially as herein described with reference to the accompanying drawings.

Documents:

1764-mas-96 abstract-duplicate.pdf

1764-mas-96 abstract.pdf

1764-mas-96 assignment.pdf

1764-mas-96 claims-duplicate.pdf

1764-mas-96 claims.pdf

1764-mas-96 correspondence-others.pdf

1764-mas-96 correspondence-po.pdf

1764-mas-96 description (complete)-duplicate.pdf

1764-mas-96 description (complete).pdf

1764-mas-96 drawings-duplicate.pdf

1764-mas-96 drawings.pdf

1764-mas-96 form-1.pdf

1764-mas-96 form-26.pdf

1764-mas-96 form-4.pdf

1764-mas-96 form-6.pdf

1764-mas-96 others.pdf

1764-mas-96 petition.pdf