Title of Invention

RESIN MOLDED ARTICLE HAVING A SPRING STRUCTURE AND METHOD OF PRODUCING THE RESIN MOLDED ARTICLE

Abstract A resin molded article having a spring structure, comprising a three-dimensional structure with voids at a predetermined bulk density, said three-dimensional structure being formed by contacting, entwining, and gathering adjacent ones of random loops or curls of solid and/or hollow continuous filaments and/or short filaments made from a mixture of a polyolefin resin and VAC, EVA or SBS, with a weight ratio of 70 to 97 % and 3 to 30 % with respect to said VAC or said EVA wherein said three-dimensional structure is increased in bulk density in a direction of width thereof, at appropriate space intervals in a direction of length thereof.
Full Text FORM 2
THE PATENTS ACT, 1970 (39 of 1970)
COMPLETE SPECIFICATION (See Section 10, rule 13)
RESIN MOLDED ARTICLE HAVING A SPRING STRUCTURE AND METHOD OF PRODUCING THE RESIN MOLDED ARTICLE
EIN KOHSAN CO., LTD. of NO. 32-2, NISHI-GOTANDA, 1-CHOME, SHINAGAWA-KU, TOKYO, JAPAN, JAPANESE Company
The following specification particularly describes the nature of the invention and the manner in which it is, to be performed:-
GRANTED
29-6-2004


BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to a resin molded article with a spring structure and a 'method of producing the same, and more particularly to a resin molded article with a spring structure, which is excellent in shock resistance and load capacity and is also

suitable for use as a

niter medium, and a method of producing The same.

2. Description of the Related Art

At present, a polyurethane foam isa mainstream material of cushions for seats

and beds.
Further, a cushion has been proposed in Japanese Laid-Open Patent Publication (Kokai) No. 2000-51011, which is produced by partially bonding synthetic fibers and natural fibers of 1 to 20 deniers with each other, by a synthetic rubber adhesive.
Still further, a seat cushion pad for an automotive vehicle has been disclosed in Japanese Patent No. 2995325, in which a scat surface part is formed of a high resilience foam having a one layer structure, and the high resilience foam is made of a polyurethane foam which contains 10 wl% or less of tolylene diisocyanate (TD1), and the remainder isocyanate formed by diphenylmethane diisocyanate.
Generally, polyurethane foams sink deeply, and the user gets fatigued if he sits thereon for a long time. Further, it is difficult to recycle the polyurethane foams since they are thermoset resins. Therefore, polyurethane foams can only be recycled

by crushing them into chips by a crusher, and bonding !he chips into a material called chip foam (ribbon dead foam), or just burned for recovery of thermal energy. The method of disposal of polyurethane foams includes landfilling and incineration.
However, stable lands cannot be created by using polyurethane foams since they are
low in bulk density and soft, and hence landfill sites suitable therefor are limited.
Further, incineration of polyurethane foams causes much damage to incinerators, and
generates toxic gases which are required to be eliminated at high costs. However,
i
there has been no alternate material which has a performance as high as a
i polyurethane foam 'when used as a cushioning material for seats, beds, etc. and which
can be manufactured at low costs.
i
Further, polyurethane foams are so flexible that when used for seat cushion pads for an
automotive vehicle, they cause a ,user to have feelings of being heaved
from below and being rocked. Therefore, long hours of driving causes the user to
feel numb at feet and get much fatigued. In addition, polyurethane foams have the

following problems to be solved:
Polyurethane foams are difficult to clean and recycle. An amine catalyst used
in manufacturing the .fame is trapped in the foams thereof, causing bad smell.
A polyurethane, foam has a heat storage property, and is liable to be stuffy,
and there is a fear that if the polyurethane foam is exposed to intensive light for a
long time, it may start to burn. Moreover, when burned, it generates gases of
cyanogen, hydrogen chloride, and ammonia,
Although year 2020 is set to a deadline of abolition of use of CFCs substitute which is used as a foaming agent, there is not yet found an alternate agent that is more excellent in foaming performance than the CFCs substitute.
TDI (Tolylene Diisocyanate) which is an isocyanate normally used for producing soft polyurethane foams is a very harmful materia! and Notification No. 25 of the Ministry of Labor of Japanese Government prescribes that TDI should be used


at a concentration of 0.005 ppm or less. In many actual manufacturing sites,

.thorough control of TDI is not carried out, causing damage to health of workers.
In the above-mentioned seat cushion pad for an automotive vehicle disclosed in Japanese Patent No. 2995325 is improved in the characteristics of the soft polyurethane foam, but has the drawbacks of polyuretharie foams.
Although the cushion proposed in Japanese Laid-Open Patent Publication
(Kokai) No. 2000-51011 offers advantages in that it has excellent air permeability and
is cleanable, it suffers from disadvantages in that it has a low durability, a,
manufacturing method thereof is complicated, and a processing cost is remarkably high. Further, the rubbir adhesive and a crosslinkable polyurethane are thermoset resins which are difficult to recycle, and since the cushion is not of a single composition, it is difficult to recycle the cushion.
A cushion.disclosed in Japanese Patent No. 2548477 is produced by fusion-bonding high-melting polyester fibers with low-melting thermoplastic elastomers, and hence suffers from problems to be solved in that the cushion is difficult to recycle, a manufacturing method thereof is complicated, and a processing cost is remarkably high.
The invention has been made as a solution to the above problems, and an object thereof is to provide a resin cushion element with a spring structure which can be recycled, manufactured at reduced costs, and does not sink deep so that it does not fatigue the user even after it is used for a long time, for being used in place of the polyurethane foam which is difficult to recycle and suffers from the problems described hereinabove even in the disposal thereof.
Further, the invention permits resins, such as PE and the like, which are
regenerated for reusing thermoplastic, resin vessels for packaging edible oil and waste
t
agricultural plastic film's, to be regenerated as articles with high added value. The

resin cushion clement with a spring structure according to the invention can be ,


recycled as many times as required. Further, the cushion structure according to the invention is produced by using, as a material, a mixture of a polyolcfin resin, such as PE and PP, and a vinyl acetate resin (hereinafter referred to as "VAC"), or an ethylene vinyl acetate copolymer (hereinafter referred to as "EVA"), or styrene butadiene styrene (hereinafter referred to as "SBS"), and another object of the invention is to provide a resin molded article with a spring structure, which is excellent in cushioning properties when used for a cushion of a bed or a seat. Further, still another object of the invention is to provide a method which is capable of manufacturing, by easy molding steps, a molded article which is high in the
freedom of shaping thereof, and has desired physical properties, such as load
i i
withstanding strength (load capacity) and shock resistance and the like.



SUMMARY OF THE INVENTION
'
■•l
A resin molded article 30 having a spring structure according to the invention
i comprises a three-dimensional structure at a predetermined bulk density (hereinafter
I simply referred to as the "three-dimensional structure"), the three-dimensional
structure being formed by contacting, entwining, and gathering adjacent ones of
random loops or purls of continuous filaments and/or short filaments made from a
mixture of a pojyblefin resin and VAC, EVA or SBS.
This invention is also characterized in that the three-dimensional structure has voids provid ng low and high densities.
The mixture ratio of the vinyl abctate content of the polyolcfin resin to VAC or EVA,is 70 to 97 wt% to 3 to 30 \vt%, preferably, 80 to 90 wt% to 10 to 20 wl%.
If the VAC content is equal to or lower than 3 wt%, the impact resilience of the three-dimensional structure is low, whereas when the VAC content is equal to or higher than 30 wt%, the thermal characteristics of the structure are degraded.



The mixture ratio of the polyolclin resin to SBS is 50 to 97 wt% to 3 to 50 wt%, preferably, 70 to 90 wt% to 10 to 30 wt%. The polyolefin resin may be a regenerated resin.
The solid continuous filaments and/or short filaments have a diameter e.g. of
0.3 mm to 3.0 mm, preferably 0.7 to 1.0 mm, and the hollow continuous filaments
and/or short filaments have a diameter of 1.0 mm to 3.0 mm, preferably 1.5 to 2.0
mm. Further, the three-dimensional structure has a bulk density e.g. of 0.001 to 0.2
g/cm3, preferably 0.02 to 0.1 g/cm'1. Although it is possible to form the
three-dimensional structure only by solid filaments or hollow filaments, if a mixture
thereof is used, the mixture ratio of solid filaments to hollow filaments is e.g. 0 to 50
to 50 to 100. Further, if hollow filaments are used in a central portion of the
structure, and covered with solid ones, a tactile impression can be increased.
The present invention relates to a cushion material for a seat of an automotive
vehicle or a bed, for instance. When the bulk density of the three-dimensional
structure is equal to or lower than 0.001 g/cm1, strength thereof is decreased. If the
bulk density is equal to or higher than 0.08 g/cm3, it is impossible to reduce a weight
thereof, and elasticity thereof is lost. ,
If the diameter of the filaments is equal to or smaller than 0.3 mm, sturdiness
of the filaments is lost, and increased number of portions of the filaments are
fusion-bonded to thereby reduce the void ratio of the three-dimensional structure.
I Inversely, if the diameter of the filaments is equal to or larger than 3.0 mm, the
filaments are excessively sturdy, and hence loops or curls are not formed, so that
reduced number of potions of the filaments are fusion-bonded to thereby decrease the
strength of the three-dimensional structure. The diameter of hollow filaments is. 1.0
mm to 3.0 mm,| preferably 1.5 rnm to 2.0 mm. If the ratio of hollow filaments is
equal to or smaller than 10 %, it does not contribute to reduction of the weight of the


structure, whereas if the same is equal to or larger than 80 %, cushioning properties

of the slruclure are degraded.
To maintain elasticity and strength of the structure as a cushion as well as reduce the weight thereof, the void ratio of the three-dimensional structure is required to be 91 to 99 %, preferably 93 to 96 %.
[void ratio (%)] = (1 — [bulk density] / [density of resin]) X,'l00

This invention further relates to a method of producing a resin molded article
having a spring structure, by melt-extruding a polyolefin resin or a thermoplastic

elastomer into a plurality of filaments, and Contacting, entwining and gathering
adjacent ones of random loops or curls of continuous filaments, thereby forming a
three-dimensional structure with voids at a predetermined bulk density, wherein a
take-off speed for taking off the extruded continuous filaments is changed to thereby
form high density portions having an increased bulk density which each extend in a
i
direction of width of the three-dimensional structure and are arranged at appropriate
space intervals in a direction of length of the three-dimensional structure
BRIEF DESCRIPTION Of THE DRAWINGS
The object and advantages of the invention will become understood from the following detailed description of preferred embodiments thereof in connection with the accompanying drawings in which like names designate like elements, and in which:
FIG. 1 is a diagram schematically showing processes of manufacturing resin molded articles having a spring structure, according to an embodiment of the invention;
FfG. 2 is a diagram schematically showing an embodiment of an apparatus for


implementing the method according to the invention;
FIG. 3 is a diagram schematically showing another embodiment of the apparatus for implementing the method according to the invention;
FIG. 4 is a diagram schematically showing still another embodiment of the apparatus for implementing the method according to the invention;
FIG. 5 is a graph showing a load-compression deflection ratio according to Example 1;
FIG. 6 is a graph showing a load-compression deflection ratio according to Example 2;
FIG. 7 is a graph showing a load-compression deflection ratio according to Example 3;
FIG. 8 is a graph showing a load-compression deflection ratio according to
Example 4;
FIG. 9 is a graph showing a load-compression deflection ratio according to
i
Example 5; '
FIG. 10 is a graph showing a load-compression deflection ratio according to
Example 6; '
FIG. 11 is a graph showing a load-compression deflection ratio according to
Example 7;
FIG. 12 is a graph showing a load-compression deflection ratio according to

Example 8;

FIG. 13 is a graph showing a load-compression deflection ratio according to
Example 9;

FIG. 14 is a graph showing a load-compression deflection ratio accordihg to Example 10;
FIG. 15 is agExample 11;
aph showing a load-compression deflection ratio according to

FIG. 16 is a graph showing a load-compression deflection ratio according to
Comparative Example 1; '
FIG. 17 is a graph showing a load-compression deflection ratio according to Comparative

Example 2;
FIG. 18 is a graph showing a load-compression deflection ratio according to
i
Comparative Example 3; and
FIG. 19 is a graph showing a load-compression deflection ratio according to

Comparative Example 4;.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT


(Three-dimensional Structure)
A three-dimensional structure employed in the invention has voids and is
formed of continuous filaments and/or e.g. short filaments that are randomly entwined
and gathered. The continuous and/or short filaments form a plurality of loops or
curls. The above three-dimensional structure can be formed as follows: A
thermoplastic resin, such as polyethylene, for instance, and VAC, EVA or SBS are
metered and mixed using a tumbler or a cutting feeder: The mixture is subjected to
melt-extrusion at a predetermined speed through a plurality of nozzles, taken off by a
winder, referred to hereinafter, and formed into solid and/or hollow continuous
filaments of 600 deniers to 90,000 deniers, preferably 3,000 deniers to 30,000 deniers,
more preferably 6,000 deniers to 10,000 deniers. The filaments in a fused state are
caused to form loops having a diameter of 1 mm to 10 mm, preferably 1 mm to 5
mm, and are taken off by the winder within water while bringing adjacent ones of the
filaments into contact with each other within the water to be entwined forming
random loops. In taking off the filaments, the take-off speed of thq winder is





adjusted to a low take-off speed by the winder at intervals of e.g. 3 to 5 m such that
i
there is formed a three-dimensional spring structure with a thickness of 10 mm to 200
mm and a width of 2,000 mm, the three-dimensional spring structure having
i high-density portions having a high bulk density with a length of 30 cm to 50 cm in a
longitudinal direction formed when the extruded materia! is received at the low
take-off speed and low bulk density portions other than the high detisity portions.
The contacted and entwined portions of the filaments are at least partially fused and
bonded to one another.
The continuous and/or short filaments are preferably made of a thermoplastic
elastomer, e.g. an elastomer of polypropylene, polyester, nylon or PVC.
The three-dimensional structure can be formed such that it has low density portions and high density portions in bulk density as required. The bulk density at the low density portions is 0.005 to 0.03 g/cm3, preferably 0.008 to 0.03 g/cm3, particularly preferably 0.01 to 0.03 g/cm3, while the bulk density at the high density portions is 0.03 to 0.08 g/cm1, preferably 0.04 to 0.07 g/cm'1, particularly preferably 0.05 to 0.06 g/cm3.
The void ratio of the three-dimensional structure at the low density portions is
96 to 99 %, preferably 97 to 99 %, and particularly preferably 97 to 98 %, while the
void ratio at the high density portions is 91 to 97 %, Dreferably 92 to 96 %, and
i particularly preferably 93 to 94 %.
(Manufacturing Method)
In the method of producing the resin molded article 30 having a spring
structure, according to the invention, will be described. It is preferable that resin
materials are dry-blended with each other by a tumbler, referred to hereinafter, or a
metering feeder, or mixed or melted and mixed with each other to form pellets,
followed by being fed to a hopper of an extruder.
i Resin materials, e.g. polyethylene and SBS were blended with each othtir by a

I tumbler (KR blender made by Katoriki Seisakmsho) at 40 rpm for 15 minutes (FIG.
i The above mixture was fed into a 11 thereof, and taken off at 60 rpm at a take-off speed of 1.0/min. Resins were
melted and kneaded at a temperature of 200°C for Examples 1 to 6, and at a

temperature of 260°C for Examples 7 to 9, and extruded through a lot of injection
i
ports formed in a molding die 12 and having a predetermined diameter. More
specifically, the mixture is subjected to melt extrusion at a predetermined speed |
i
through a plurality of nozzles, taken off by the winder, referred to hereinafter, and formed into solid or hollow continuous filaments having a predetermined diameter. The filaments in a fused state are caused to form loops, and arc taken off by the winder within water while bringing adjacent ones of the filaments into contact with each other within the, water so as to be entwined forming random loops. When taking off the filaments, the take-off speed of the winder is adjusted to a low speed at predetermined intervals. For instance, iF the take-off speed of the feed rollers 14 and 14 of the winder is adjusted to a low speed for a preset time period from each preset time by using a timer or the like, it is possible to obtain the resin molded article 30 having a spring structure with high and low density portions, which includes high bulk density portions with a predetermined length in the direction of the length thereof at predetermined space intervals. That is, the resin molded article 30 having a spring structure can be manufactured by forming a three-dimensional spring structure, referred to hereinafter, which includes the high bulk density portions (high density portions B) formed when the take-off speed is low, and the other low density portions (low density portions A) (FIG. 2). The taken-off material randomly curled or looped is solidified in the water in a bath 15 and taken up by take-up rollers 16 and 16, to provide the resin molded article 30 having a spring structure. The thickness and bulk density of the extruded material are set between the feed rollers 14


and 14 of the winder 13 in the bath 15. When the material is taken off, it is sometimes difficult to bend it by the feed rollers 14 and 14. To eliminate this inconvenience, by forming still lower density portions than the low density portions, the material is bent at the still lower density portions and drawn out of the water. (FIG. 3).
FIG. 4, shows a cutting device arranged in the bath 15 for cutting the molded form. The cutting device 19 is positioned in the vicinity of the winder 13 at a location downward thereof. Arranged at an inner wall of the bath 15 opposed to the cutting device 19 is a transport device 11 comprised of a conveyer having a lot of engaging projections for insertion into voids of each single molded form cut off at a cutting portion. In the figure, reference numerals 25 and 26 designate a water supply valve and a drainage valve, respectively (FIG. 4). The filaments are randomly curled or looped,, solidified in the water in the bath 15 and taken up by the take-up rollers 16 and 16, as the resin molded article 30 having a spring structure.
As described above, the resin molded article 30 having a spring structure is obtained which has, for instance, a thickness of 30 mm and includes a high density portion with a length of 30 cm after every low density portion having a length of 3
m.

The resin molded larticle 30 having a spring structure can be manufactured by using the abover-mentioned three-dimensional structure which includes one type of
property or a combination of a plurality of types of properties different from each
other.
Examples
Examples of molded products which are different in compounding ratio ,
between resin materials '
Examples of spring structures were produced by using combinations of resin materials PE + VAC, PE + EVA, and PP + SBS, while varying the compounding


ratio of each of the combinations.
The compounding ratios, manufacturilng conditions, and characteristic values,
i such as bulk density, are shown in Table 1, Table 2, and Table 3, respectively.
Examples 1 to 3: PE + VAC
Examples 4 to 6: PE + EVA
Examples 7 to 9: PP + SBS .
Table 1
Compounding ratios in Examples 1 to 9



Table 2
Manufacturing conditions of Examples 1 to 9

Molding die

Discharge rate

Take-off speed



300 mm(W) X 50 rnm(T)

28 kg/h

1.0 m/min


Table 3
Characteristic values of Examples 1 to 9
Bulk density Diameter Area Thickness
0.03 g/cm3 1.5 mm 300 X300 mm 50 mm
(hollow)
Examples of manufactured products-which are different in bulk density
Spring structures changed in bulk density were produced from resin materials
having the same compounding ratio of PE : VAC = 90 : 10. The process of
producing the spring structures will be described. The resin materials were blended
by using a tumbler called KR blender (type: KRT-100) made by Katoriki
Seisakusho, at 40 rpm for 15 minutes. The spring structures were molded by using
the 65, mm uniaxial extruder, and taken off at a screw rotational speed of 60 rpm,
and at take-off speeds of 3.1 m/min. and 0.6 m/min. The temperature of the resins
was 200°C.
The compounding ratios between the resin materials, manufacturing
conditions, and characteristic values, such as bulk density, are shown in Table 4,

Table 5, and Table 6, respectively.
Examples 10 and 11 (PE + VAC)
Table 4

Compounding ratios in Examples 10 and 1

PE(wt%) VAC(wl%)
Example 10 90 10
Example 11 90 10


Table 5
Manufacturing conditions of Examples 10 and 11

Molding die' Discharge rate Take-off speed
Example 10 300 mmCW)X(T) 28kg/h !
3.1m/min
Example 11 300 mm(W) X (T) 28k'g/h , 0.6m/rriin
Table 6
Characteristic values of Example 10 'and 1

Bulk density Diameter Area Thickness
Example 10 0.01 g/cm3 1.5 mm (hollow) 300x300 mm 50 mm
I
Example 11 0.05 g/cm3 1.5 mm (hollow) 300x300 mm 50 ' 50 mm
Comparative Examples
Polyurethane foam
i
A soft polyurethane foam which is a mainstream material for a cushion eicmcnt was prepared as Comparative Example I. The manufacturing conditions and product characteristics of the soft polyurethane are shown in Table 7.

Comparative Example 1 (polymethane foam) fable 7
t
Main raw material and manufacturing conditions of Comparative Example 1

Molding method Cold mold foam
Polyol type Polyether polyol (terminal 1st class-OH)
functional group number 3
molecular weight 4500-6000
Foam stabilizer Low-activity silicon foam stabilizer
Isocyanate TDI-80
Foaming machine Foaming machine for few ingredient (2 to 3)
Die temperature

during injection

50°C



during mold release

50°C



curing time

14 min.

Conventional spring structure
PP (non other composition is added).
Spring structures were produced only from the resin material PP by varying
the bulk density.


The spring structures were molded by using the 65 mm uniaxial extruder, and
taken off at a screw rolalional speed of 60 rpm, and at take-off speeds of 0.6 m/min,

1.0 m/min and 3.1 m/min. The temperature o!f the-resin was 260°C. The compountding ratios, manufacturing conditions, and characteristic values, such as bulk density, are sholwn in Table 8, Table 9, and Table 10, respectively.

Comparative Examples 2, 3, and 4 (only PP)
Table 8
Compounding ratios of Comparative Examples 2 to 4

1 i PP (wt%)
t
Comparative Example 2 100
Comparative Example 3
Comparative Example 4 | i
100
1
Table 9

Manufacturing conditions of Comparative Examples 2 to 4




Table 10

Characteristic values of Comparative Examples 2 to 4


I
Tests
In the tests, the following properties are revealed.
Test I: Compression characteristic
Test 2: Residual distortion after repeated compression
Test 3: Impact resilience ratios
Test 1: Compression characteristics
The test was carried out in conformity with the J1S K 6400 soft polyurethane foam-testing method Appendix (reference) 1. The size of test pieces is 300 (W) X 300 (L) X 50 (T). Diagrammatic views showing load-compression deflection ratios are shown in FIGS. 5 to 19.
Cushion elements having a spring structure, which are all of Examples, and a polyurethane foam, which is Comparative Example, 3 are compared with each other.
None of Examples have a noticeable yield point which is found in Comparative Example 1. This means that the cushion elements have a small quantity of local sinkage, thereby making it possible to uniformly receive load on a whole region in

contact with a cushion structure.
Next, in Comparative Example 1, a rise of load is recognized when the deflection ratio exceeds 50 %, while such a rise is not recognized in any of Examples. Further, in all Examples, the three-dimensional structure can be effectively deformed up to about 90 % of thickness thereof. This shows that the structure does not provide a bottom touching feeling to ,a user, and that it can be quickly restored upon removal of load therefrom, that is, the three-dimensional structure has a high setting resistance.
Next, the cushion elements having a spring structure, which are all of Examples, and Comparative Examples 2 to 4, which are the conventional spring structures, are compared with each other. Comparative Example 2 has a yield point, requires a high load relative to compression deflection, undergoes plastic deformation, and does not exhibit elastic recovery. Although Comparative Examples 3 and 4 do
not have a yield point, a rise of load is recognized when the deflection ratio thereof
exceeds 50 %, which means that they give a bottom touching feeling to a user.

Further, they undergo plastic deformation, and 'does not exhibit elastic recovery.
If the compounding ratios between the resin materials and the bulk density are i
changed, it is possible to produce a cush'ion structure with desired hardness.
Test 2: Residual distortion after repeated compression
The test was carried out in conformity with the JIS K 6400 soft polyurethane
foam-testing method 8.1 A. The size of test pieces is 300(W) X 300(L) X 50(T).
The test was executed on the narrowed range of objects: Example 2 (PE +
i VAC, bulk density 0.03), Comparative Example 1, and Comparative Example 3 (pP,
bulk density 0.03). Results of the tests are shown in Table 11.


Table 11
Results of measurement of residual distortion after repeated compression
Residual distortion after
repeated compression (%)
Example 1 93

Comparative Example 1 ' 95 '
Comparative Example 3 75
i
i
i
Example 1 and Comparative Example 1 show that they have the same level of
performance. Although Example 2 and Comparative Example 3 have the same
structure and are different only in resin, the residual distortion of Comparative
Example 3 which undergoes plastic deformation is sharply reduced to 75 %. The
resin molded article according to the invention has the same level of setting resistance
as that of a polyurethane foam.

Test 3: Impact resilience i '
, The test was carried out in conformity with the JIS K 6400 soft polyurethane
foam-testing method 9.2B. The size of a test piece is 300 (W) x 300'(L) x 50 (T).
Objects of the test are the same as Test 2. Results of the test are shown in Table 12.
Table 12 Measurement results of impact resilience ratios

Impact resilience (%)
Example 1 91 .
Comparative Example 1 65
Comparative Example 3 70

The resin molded article according to the invention has impact resilience 1.4
times as high as that of a polyurelhanc foam.
Although it is difficult to recycle a polyurethane foam, the resin molded article
i
according to the invention can be regenerated into a product after it is used and hence
it is excellent in recyclability. •'
The resin molded article according to the invention can be manufactured at reduced costs since recycled resins can be used for producing the same.
The resin molded article does not give a bottom touching sense, and has a very small quantity of local sinkage, thereby making it possible to uniformly receive load on a whole region in contact with the cushion structure. Hence, the article causes less fatigue of the user than a polyurethane foam.
Since the resin molded article according to the invention has a structure having
\ completely continuous voids, it is more excellent in air permeability than a
polyurethane foam.
Although in manufacturing the polyurethane foam, toxic materials, such as TDI and the like, are used, the resin molded article of the present invention can be produced without generating toxic gases and hence ensures good working conditions.
According to the invention, it is possible to recycle regenerated resins with
high added values.
Thus, the broadest claims that follow are not directed to a machine that is

configuration a specific way. Instead, said broadest claims are intended to protect
the heart or essence of this breakthrough invention. This invention is clearly new

and useful. Moreover, it was not obVious .to those of ordinary skill in the art at the time it was made, in view of the prior art when considered as a whole.
Moreover, in view of the revolutionary nature of this invention, it is clearly a pioneering invention. As such, the claims that follow are entitled to very

broad interpretation as to protect the heart of this invention, as a matter of law.
It will thus be seen that the objects set forth above, and those made apparent from the foregoing description, are efficiently attained. Also, since certain changes may be made in the above construction without departing from the scope of the invention, it is intended that all matters contained in the foregoing description or shown in the accompanying drawings shall be interpreted as illustrative and not in a limiting sense.
It is also to be understood that the following claims are intended to cover
all of the generic and specific features of the invention herein described, and all

statements of the scope of the invention which, as a matter of language, might be
said to fall therebetween. Now that the invention ihas been described;


We Claim:
1. A resin molded article having a spring structure, comprising a three-dimensional structure with voids at a predetermined bulk density, said three-dimensional structure being formed by contacting, entwining, and gathering adjacent ones of random loops or curls of solid and/or hollow continuous filaments and/or short filaments made from a mixture of a polyolefin resin and VAC, EVA or SBS, with a weight ratio of 70 to 97 % and 3 to 30 % with respect to said VAC or said EVA wherein said three-dimensional structure is increased in bulk density in a direction of width thereof, at appropriate space intervals in a direction of length thereof.
2. The resin molded article according to claim 1, wherein said three-dimensional structure has voids providing low and high densities.
3. The resin molded article according to any one of claims 1 to 3, wherein a mixture ratio of said polyolefin resin to said SBS is 50 to 97 wt% to 3 to 50 wt%, preferably, 70 to 90 wt % to l0 to 30 wt % .
4. The resin molded article according to claim 1 or 2, wherein said solid continuous filaments and/or short filaments have a diameter of 0.3 mm to 3.0 mm, preferably 0.7 to 1.0 mm, and said hollow continuous filaments and/or short filaments have a diameter of 1.0 mm to 3.0 mm, preferably 1.5 to 2.0 mm.
5. The resin molded article according to any one of claims 1 to 5, wherein said three-dimensional structure has a bulk density of 0.001 to 0.08 g/cm3, preferably 0.02 to 0.06 g/cm3.
6. The resin molded article according to any one of claims 1 to 6, wherein said three-dimensional structure is a cushion material for seats of an automotive vehicle or a bed.


7. A method of producing a resin molded article as claimed in claim 1 having a spring structure, by melt-extruding a polyolefin resin into a plurality of filaments, and contacting, entwining and gathering adjacent ones of random loops or curls of continuous filaments, thereby forming a three-dimensional structure with voids at a predetermined bulk density, wherein a take-off speed for taking off the extruded continuous filaments is changed to thereby form high density portions having an increased bulk density which each extend in a direction of width of said three-dimensional structure and are arranged at appropriate space intervals in a direction of length of said three-dimensional structure.
8. The resin molded article according to any one of claims 1 to 5, wherein said three-dimensional structure has a bulk density of 0.005 to 0.03 g/cm3, preferably 0.008 to 0.03 g/cm3 , particularly preferably 0.01 to 0.03 g/cm3 at low density portions, and a bulk density of 0.03 to 0.08 g/cm3, preferably 0.04 to 0.07 g/cm3, particularly preferably 0.05 to 0.06 g/cm3 at high density portions.
9. The resin molded article according to claim 9, wherein said three-dimensional structure has a void ratio of 96 to 99 %, preferably 97 to 99 %, and particularly preferably 97 to 98 % at said low density portions, and a void ratio of 91 to 97 %, preferably 92 to 96 %, and particularly preferably 93 to 94 % at said high density portions.
10. The resin molded article according to any one of claims 1 to 5, wherein a mixture ratio of solid filaments to hollow filaments is 0 to 50 to 50 to 100.
11. The resin molded article according to any one of claims 1 to 5, wherein outer surfaces of said hollow filaments are covered with solid filaments.
Dated this 24th day of April, 2001
HIRAL CHANDRAKANT JOSHI AGENT FOR EIN KOHSAN CO., LTD.


Documents:

376-mum-2001-cancelled pages(29-6-2004).pdf

376-mum-2001-claims(granted)-(29-6-2004).doc

376-mum-2001-claims(granted)-(29-6-2004).pdf

376-mum-2001-correspondence(22-2-2005).pdf

376-mum-2001-correspondence(ipo)-(25-5-2005).pdf

376-mum-2001-drawing(29-6-2004).pdf

376-mum-2001-form 1(24-4-2001).pdf

376-mum-2001-form 1(29-6-2004).pdf

376-mum-2001-form 19(17-2-2004).pdf

376-mum-2001-form 2(granted)-(29-6-2004).doc

376-mum-2001-form 2(granted)-(29-6-2004).pdf

376-mum-2001-form 3(17-2-2004).pdf

376-mum-2001-form 3(24-4-2001).pdf

376-mum-2001-form 5(24-4-2001).pdf

376-mum-2001-power of authority(26-4-2001).pdf

abstract1.jpg


Patent Number 197791
Indian Patent Application Number 376/MUM/2001
PG Journal Number 41/2007
Publication Date 12-Oct-2007
Grant Date 03-Jan-2006
Date of Filing 24-Apr-2001
Name of Patentee EIN KOHSAN CO LTD
Applicant Address 32-2, NISHI-GOTANDA, 1-CHOME SHINAGAWA - KU, TOKYO, JAPAN.
Inventors:
# Inventor's Name Inventor's Address
1 SADAO NISHIBORI NO. 1-9-206, HIGASHI-SHINAGAWA 1-CHOME, SHINAGAWA-KU, TOKYO, JAPAN.
2 YUICHIRO NAKAMURA NO. 859, BEPPU, HOZUMI-CHO, MOTOSU-GUN, GIFU, JAPAN.
PCT International Classification Number N/A
PCT International Application Number N/A
PCT International Filing date
PCT Conventions:
# PCT Application Number Date of Convention Priority Country
1 2000-246907 2000-08-16 Japan