Title of Invention

A CONTINUOUS PROCESS FOR THE SOLID STATE POLYCONDENSATION OF AROMATIC POLYESTER RESINS

Abstract

57) Abstract:- The present invention relates to a continuous process for the solid state polycondensation of aromatic polyester resins such as herein described, where the resin is fed from the top of a moving bed reactor and discharged from bottom an inert gas is circulated counter-or equicurrent with the resin and the temperature in the reactor is kept between 180° and 230° C, with resin average residence times enough to obtain an increase of polymer intrinsic viscosity of at least 0.1 dl/g, characterized by the fact that the ratio R by weight between the gas rate of flow per hour and the rate of flow per hour of the polymer discharged from reactor is lower than 0.6.

Full Text

continuous The present invention relates to a/process for the solid state polycondensation of polyester resins. The aromatic polyester resins, particularly three of them, the polyethyleneterephthalate (PET) the copolymers of the terephthalic acid with minor proportions of isophthalic acid and polybuthyleneterephthalate find wide application both in the fibres and the films area, or as molding material. While for fibres and films the intrinsic viscosity of the resin is in general between 0.6-0.75 dl/g, for the molding material are necessary higher values, which with difficulty are directly obtainable by the polycondensation process of the resin. The intrinsic viscosity is increased to the required values (in general higher than 0.75 dl/g) by means of SSP processes of the resin, at a temperature in general between 190° and 230°C. The starting resin used for the SSP process is in the amor¬phous state; it is necessary to take it to a sufficient de¬gree of crystallinity before it is submitted to the SSP pro¬cess. The crystallisation is necessary in order to avoid polymer chips stocking in the polycondensation reactor that is in general feigned by a vertical moving bed where the polymer filled from the top is passed through by an inert gas stream which removes the volatile residual products of the polycon¬densation reaction (ethylene glycol and acetaldehyde in the case or poiyetnyienecerepntnaiace; . The products removal of the polycondensation reaction is a fundamental requisite for the development of the same re¬action. Various reactions occur during the polycondensation. The main reaction, that leads to the increase of the PET mole¬cular weight is the removal of ethylene glycol: PET - COO - CH2 - CH2 - OH+HO - CH2 - CH2 - OCO - PET PET - COO - CHj - CH2 - OOC - PET+HO - CHj - CHj - OH Other reactions lead to the esterifications of carboxylic end-groups and to the formation of acetaldehyde. The polycondensation and esterification reactions are rever¬sible while the reactions leading to the acetaldehyde for¬mation are irreversible and of various type. They include the degradation reaction of the polymeric chain with the formation of a vinylester end-group, which reacting with an OH end-group eliminates acetaldehyde; the reaction of the vinylester group with a COOH end group with formation of an anhydride group and acetaldehyde removal; the degrada¬tion reaction of hydroxyethylic end groups with acetaldehyde formation. The acetaldehyde removal from the polymer at levels lower than few ppm is a fundamental requisite in the case of PET for the production of items for food uses, such as mineral water bottles. As already indicated, the residual products of the from the crystallisation stage. The polycondensation reaction is in general carried out in a tubular reactor with moving bed, wherein the polymer enters from the top and comes out from the bottom and an inert gas stream is passed over the polymer. In US patent No. 4 064 122 there are described process of this type, where the granular polymer is crystallized up to a degree of density of at least 1.3 90 g/cm’, operating in crystallizers with forced movement at a temperature between 220° and 260°C and effecting then the polycondensation re¬action in a reactor with moving bed, operating at tempera¬tures equal or lower than those used in the crystallization step. The temperature in the crystallization step is in general between 23 0° and 24 5°C and the process is carried out till to obtain crystallinity values corresponding to 1.403-1.415 g/cm’ density. A temperature between 230° and 245°C is used in the polycondensation step to obtain an optimal value of the reaction speed combined with a low degree of polymer degradation. An inert gas, preferably nitrogen, is used to remove the residual products formed in the polycondensation stage. The gas is recycled after by¬products purification. The polymer undergoes hydrolysis decompositions when the water content exceeds that one above indicated. The reaction speed is influenced negatively, when the glycol content exceeds the above indicated one. High contents of oxygen and acetaldehyde cause discoloring in the shaped article and high contents of acetaldehyde are not allowed in the shaped articles for food use. To limit the purification costs of the gas recycling and the energy costs for the maintenance of the gaseous flow, the ration by weight between the gas rate of flow per hour and the rate of flow per hour of the polymer leaving the reactor has to be maintained between 0.7:1 and 3:1 preferably between 1:1 and 2:1. By using values lower than 0.7 (0.5 and 0.3 in the examples) and operating in the conditions set forth in US patent No. 4 064 112 patent (crystallization temperature 235°C and po¬lycondensation temperature 230°C) the intrinsic viscosity of the polymer does not increase significantly. By using ratios lower than 0.7, there is an increase of the temperature difference through the reactor section. US patent No. 4 161 578, describes a solid state crystalli-zation/polycondensation process where the polymer in chips is crystallized in an equipment with forced movement, acting at temperatures between 180° and 235°C till to obtain a crystallinity degree corresponding to at least 1.385 g/cm’ of density and subsequently fed to a polycondensation moving bed reactor, where the polymer is heated to temperatures higher than those used in the crystallization step. Nitrogen is circulated in the polycondensation reactor in countercurrent with the polymer feed with a ratio by weight between the rates of flow comprised from 0.7 to 3.5 kg Nj/kg PET. It has been unexpectedly found that even using ratios R bet¬ween the rate of flow per hour by weight of inert gas fed to the polycondensation reactor and the rate of flow per hour by weight of the polymer coming out of the reactor lower than those considered till now as limit values, below which interesting results could not be obtained, it is pos¬sible to effectively remove the by-products of the polycon¬densation reaction, thus obtaining high reaction kinetics. It has furthermore been unexpectedly found that the exother¬mic heat of the reaction decreases using low R ratios; this allows to better control the thermal profile in the SSP reactor and to improve also the plant operability. The usable R ratio is lower than 0.6 and preferably com¬prised between 0.2 and 0.5. The use of such low ratios allows considerable energy sav¬ings in the gas blowing operation. In the invention process the polycondensation reaction is carried out at temperatures between about 190° and 23 0°C, preferably between 210° and 220°C. The polymer to subject to the SSP reaction has a crystalli-nity degree comprised in general between 4 0 and 50% by weight and it is fed as chips. Preferably, the crystalline organization of the polymer is such that the pre-melting peak appearing in the DSC curve is shifted toward temperatures higher than those used in the reaction. Results of this type are obtainable by operating, for ex- ample, according to the crystallization process described in the Applicant's Italian application No. MI94A002355 whose description is herewith incorporated by reference. In the process described in the application, the chips of the amorphous polymer are at first submitted to a crystalli¬zation process carried out in a fluidized bed and then to crystallization processes in two mechanical mixers, the first working at a temperature between 10° and 30°C higher than that of the fluidized bed and the second one at a tem¬perature corresponding to that used in the next SSP reactor. The inert gas stream coming out from the SSP reactor is sub¬mitted to purification processes for the removal of the or¬ganic products impurities therein present. The process is described in W095/02446 application whose description is herewith incorporated by reference. The average residence times in the SSP reactor are such as to obtain an increase of the polymer intrinsic viscosity of at least 0.1 dl/g; they are in general comprised between 5 and 20 hours. The kinetics of the intrinsic viscosity increase can be considerably increased if the polymer is blended in the mol¬ten state, in a step previous to that of crystallization, with a polyfunctional compound containing two or more groups capable of reacting with condensation or addition reaction with the OH and COOH end groups of the polyester. The pyromellitic anhydride, and in general the dianhydrides of tetracarboxylic aromatic or aliphatic acids are examples of such compounds. These compounds are used in a quantity comprised in general between 0.1 and 2% by weight on the polymer. The pyromellitic anhydride is the preferred compound. The use of these compounds is described in the European patent 422 282 and in US patents No. 5 243 020, 5 334 669 and 5 338 8 08 whose description is herewith incorporated by reference. The polyester resins used in the crystallization process of the invention comprise the polycondensation products of C1-C20 diols such as ethylene glycol butylene glycol, 1,4 cy-clohexandimethyol with aromatic bicarboxylic acids, such as terephthalic acid, 2,6 naphthalene bicarboxylic acid or their reactive derivatives such as the lower alkyl esters such as for example, diethyl terephthalate. Polyethyleneterephthalate is the preferred resin. Besides the terephthalic units also units deriving from other bicarboxylic acids such as the isophthalic acid and the naphthalendicarboxylic acids can be present in a quan¬tity of about 0.5-20% by weight. Accordingly, the present invention provides a continuous process for the solid state polycondensation of aromatic polyester resins such as herein described, where the resin is fed from the top of a moving bed reactor and discharged from bottom; an inert gas is circulated counter-or equicurrent with the resin and the temperature in the reactor is kept between 180° and 230°C, with resin average residence times enough to obtain an increase of polymer intrinsic viscosity of at least 0.1 dl/g, characterized by the fact that the ratio R by weight between the gas rate of flow per hour and the rate of flow per hour of the polymer discharged from reactor is lower than 0.6. The following examples are given to illustrate but not to limit the invention. Example 1: A polycondensation test in the solid state was carried out in a continuous reactor with moving bed and with a rate of flow of solid of 50 kg/h. The used resin is a copolyethyleneterephthalate containing a percentage by weight of isophthalic acid of 2.2%. The starting intrinsic viscosity was 0.60 dl/g and the ace-taldehyde content of 35 ppm, A polymer with a final intrinsic viscosity of 0.80 dl/g was produced keeping constant the average temperature of the re¬actor and changing only the inert gas quantity fed (nitro¬gen) (changing therefore the R ratio). The average residence time was 12 hours. The fed nitrogen contained less than 10 ppm of organic compounds expressed as methane equivalent. The obtained results are shown in Table 1. Example 2 By using the same reactor, the same polymer and the same inert gas, as in example 1, some tests were carried out using different temperatures of inert gas. The obtained results are shown in Table 2. Comparative Example 1 The test of example 1 was repeated using an R ratio of 1, keeping constant the average chips temperature at 210.1°C and the residence time at 12h. The intrinsic viscosity of the obtained polymer was of 0.80 dl/g. WE CLAIM: 1. A continuous process for the solid state polycondensation of aromatic polyester resins such as herein described, where the resin is fed from the top of a moving bed reactor and discharged from bottom; an inert gas is circulated counter-or equicurrent with the resin and the temperature in the reactor is kept between 180° 230°C, with resin average residence times enough to obtain an increase of polymer intrinsic viscosity of at least 0.1 dl/g, characterized by the fact that the ratio R by weight between the gas rate of flow per hour and the rate of flow per hour of the polymer discharged from reactor is lower than 0.6. 2. The process according to claim 1, w4ierein R ratio is comprised between 0.2 and 0.5. 3. The process according to claims 1 and 2, wherein the temperature in the reactor is comprised between 190° and 210°C. 4. The process according to claims 1, 2 or 3, wherein the inert gas is nitrogen. 5. The process according to claim 4, wherein the nitrogen is circulating in equicurrent with the polymer. 6. The process accord to anyone of the preceding claims, wherein the polyester resin is polyethyleneterephthalate or copolyethyleneterephthalate containing from 1 to 20% of isophthalic acid units. 7. The process according to anyone of the preceding claims, wherein the nitrogen is recycled to the reactor after having been submitted to a purification process of the organic impurities till to obtain values lower than 10 ppm expressed as methane equivalent. 8. A continuous process for the solid state polycondensation of aromatic polyester resins substantially as herein described and exemplified.

Documents:

1592-mas-1995 abstract.pdf

1592-mas-1995 claims.pdf

1592-mas-1995 correspondence-others.pdf

1592-mas-1995 correspondence-po.pdf

1592-mas-1995 description(complete).pdf

1592-mas-1995 form-1.pdf

1592-mas-1995 form-26.pdf

1592-mas-1995 form-4.pdf

1592-mas-1995 others.pdf

1592-mas-1995 petition.pdf