Indian Patents. 277978:BONDING LAYER ON FLUOROPOLYMERS

Title of Invention	BONDING LAYER ON FLUOROPOLYMERS
Abstract	The invention relates to a device comprising a layer made from a fluoropolymer, of which at least part of the surface is covered with a composition comprising a polymer having at least one fluorinated function and at least one acid or base function and forming a bonding layer on said fluoropolymer, said bonding layer being fully or partly covered by another layer.

Full Text	FORM 2 THE PATENTS ACT, 1970 (39 of 1970) & THE PATENTS RULES, 2003 COMPLETE SPECIFICATION [See section 10, Rule 13] BONDING LAYER ON FLUOROPOLYMERS; COMMISSARIAT A L'ENERGIE ATOMIQUE, A CORPORATION ORGANIZED AND EXISTING UNDER THE LAWS OF FRANCE, WHOSE ADDRESS IS 25 RUE LEBLANC BATIMENT LE PONANT D", 75015 PARIS, FRANCE AND SOFILETA, A CORPORATION ORGANIZED AND EXISTING UNDER THE LAWS OF FRANCE, WHOSE ADDRESS IS 1 AVENUE DE CHANTEREINE, 38300 BOURGOIN JALLIEU, FRANCE. THE FOLLOWING SPECIFICATION PARTICULARLY DESCRIBES THE INVENTION AND THE MANNER IN WHICH IT IS TO BE PERFORMED. FIELD OF THE INVENTION The present invention relates to devices incorporating fluoropolymer layers. It proposes to at least partially cover the layers with an additional layer called "bonding layer', for facilitating the deposition of subsequent layers. Such a bonding layer is prepared using polymers having at least one fluorinated function and at least one acid or base function. PRIOR ART Fluoropolymers are commonly used in various technical fields today. Thus, fluoropolymers are used in the manufacture of electronic components such as organic transistors, or electrical insulation, and in the fabrication of mechanical parts subject to extreme service conditions (temperature or the presence of aggressive solvents). In the particular case of organic electronics, fluoropolymers, and in particular Cytop® (trade name of poly perfluoro butenyl vinyl ether), have particularly suitable properties for constituting the grid dielectric of a transistor. However, the use of such fluoropolymers raises the following problems, still unsolved today: it is impossible, using a wet method, to deposit other layers on a fluoropolymer previously deposited in a thin film, regardless of the deposition method (spin-coating or various printing methods); it is impossible to bond two fluoropolymer parts together, or to bond a plastic to a fluoropolymer. 2 This makes highly problematic the manufacture of complex devices comprising various elements indispensable for their operation. This is the case for example of a complete transistor, in which the placement of a dielectric requires subsequent manufacturing steps. An obvious need therefore exists to develop technical solutions for facilitating and improving the deposits on fluoropolymer based layers. SUMMARY OF THE INVENTION The present invention is based on the Applicant's finding that certain fluoropolymers develop aptitudes to adhere to materials, and in particular to fluoropolymers. Essentially, these particular fluoropolymers, having adhesive properties, carry at least one acid or base function. According to a first aspect, the present invention therefore relates to a device, in particular a transistor, comprising a layer made from a fluoropolymer, of which at least part of the surface is covered with a composition comprising at least a polymer having at least one fluorinated function and at least one acid or base function. According to the invention, the composition comprising at least the polymer having at least one fluorinated function and at least one acid or base function forms a bonding layer on the fluoropolymer. This bonding layer is itself partly or fully covered by one or more other layers made with materials of interest. By definition, the device therefore partly consists of a first fluoropolymer. This part is called "layer", insofar as it has outer surfaces which are intended to be covered, at least partially or fully, by at least the bonding layer according to the invention. In the context of the present invention, fluoropolymer means a polymer or a copolymer of which at least one of the component monomers contains at least one fluorine (F) atom per monomer. This polymer may be crosslinked or non-crosslinked. Such polymers are, for example, selected from the following list: 3 TeflonR: trade name of polytetrafluoroethylene (PTFE) (sold by DuPont): CytopR: trade name of poly perfluoro butenyl vinyl ether (sold by Ashai Glass); HalarR (sold by Solvay Solexis); Hyflon® (sold by Solvay Solexis); Parylene-F (sold for example by Aldrich). Note that these references are well known to a person skilled in the art in the field of polymers, but of which the exact chemical formula is not always available. Cytop is advantageously selected from this list. It will clearly appear from a reading of the rest of the description that this first fluoropolymer lacks any acid or base function. The second polymer, used for the formation of the bonding layer according to the invention, is a polymer or a copolymer defined as follows: at least one of its component monomers contains at least one fluorine (F) atom per monomer. In this respect, it is therefore a second fluoropolymer; at least one of its component monomers contains an acid or base function. In the context of the present invention, the acid or base functions are defined by Bronsted or Lewis. Polymers answering to this definition are for example: Nafion® (DuPont); Hyfion IonH (Solvay Solexis); FlemionR (Ashai Glass). Here also, these are references well known to a person skilled in the art in the field of polymers, but of which the exact chemical formula is still unavailable. Preferably, the acid function is provided by a carboxylic, phosphonic, sulfonic, sulfone or Si(CH3)3 function. The base function may be an amine. According to an advantageous embodiment, the monomer having at least one fluorinated 4 function is of the same type as the monomer present in the fluoropolymer. This is the case for example of the pair Teflon® (first fluoropolymer)/Nafion® (second fluoropolymer) which both comprise monomers of tetrafluoroethylene. Advantageously, the fluorinated function and the acid or base function are carried by the same monomer. This is the case for example of Nafion , of which the monomers of tetrafluoroethylene incorporate perfluorovinyl ether groups terminating in sulfonic groups. It has been found that such a polymer carrying at least one fluorinated function and at least one acid or base function has aptitudes to adhere both to fluoropolymers. such as Teflon and Cytop (or equivalent materials), and to other materials, for example adhesive. Teflon thus covered permits the adhesion of a conductive ink, of another part made from Teflon® or from another material (for example melamine), etc. The bonding layer thus formed, which advantageously has a thickness of between 20 nm and 2 um, can thus be partly or fully covered by one or more other layers prepared with materials of interest. They may be electrodes, semiconductive materials, dielectrics, layers of ink or adhesive. It should be noted that for applications related to electronics in particular, it is desirable that the acid or base groups present in the fluoropolymer are not oriented under an electric field. To prevent this from occurring, it is recommended, in the composition serving for the formation of the bonding layer, to combine compounds of the molecule or polymer type creating bonds with the acid or base sites of the fluoropolymer. These bonds may be of the low energy interaction type, for example hydrogen bonds. Alternatively, an acid-base reaction may take place in solution between the fluoropolymer and the compound. Furthermore, it is conceivable to mix the fluoropolymer carrying the acid or base functions directly with a material of interest, such as a resin, particularly of photolithography, inks in particular conductive inks, or dielectrics. Such a mixture also has a strong affinity for fluoropolymer based substrates. In this particular case, the layer placed on the bonding layer may for example consist of a metal to constitute electrical contacts. 5 According to a preferred embodiment, the inventive device is a transistor. The present invention therefore serves to modify the surface of a fluoropolymer using a second fluoropolymer, and thereby to make the surface of the first fluoropolymer compatible with processes such as printing, spin-coating or bonding. According to another aspect, the invention therefore relates to a method for fabricating a device as defined above, comprising: in a first step, the deposition, on all or part of the outer surface of the fluoropolymer layer, of a composition comprising a polymer having at least one fluorinated function and at least one acid or base function, in order to form a bonding layer after drying: in a second step, the deposition of a material of interest on this bonding layer, in order to form another layer (functional layer) after drying. The deposition of the second fluoropolymer on the first can be carried out either by dip-coating, or by spin-coating, or by printing (inkjet, flexography, heliography, etc.) These techniques can be implemented for the second deposition. The second polymer, carrying at least one fluorinated function and at least one acid or base function, is generally formulated in a composition suitable for the deposition technique employed. Such a composition may be in the form of a solution comprising from 0.3 to 5% by weight of the polymer having at least one fluorinated function and at least one acid or base function. A solvent suitable for dissolving said polymer is selected and incorporated in the composition. It may for example be isopropanol. Typically, after deposition and drying, the second polymer forms a thin film the thickness of which is between 20 nm and 2 µm. This thickness depends in particular on the fluoropolymer concentration of the layer on which the deposition is made. 6 This composition may also be enriched with one or more polymers or compounds having a chemical structure close to the structure of the layer or of the material that is added on to the second polymer. In fact, in a subsequent step of the fabrication method, a material of interest is advantageously deposited on the layer thus formed. By way of example, such a composition has the following formula (% by weight): -4%Nafion2021; - 90% isopropanol; - 4% polyvinyl phenol; - 2% melamine. The bonding layer obtained with this composition is particularly suitable for receiving (and in particular for being covered fully or partly) a layer based on polyvinylphenol crosslinked by melamine formol. This layer serves to limit the electrical leakage of the complete stack. DETAILED DESCRIPTION OF THE INVENTION The way in which the invention can be implemented and the advantages thereof will appear more clearly from the exemplary embodiments that follow, provided for information and nonlimiting, in conjunction with the appended figures. Figure 1 shows a schematic of the transistor obtained by the prior art methods. Figure 2 shows a schematic of a transistor obtained according to the present invention, comprising a bonding layer. Figure 3 shows a schematic of a transistor obtained according to the present invention, comprising a bonding layer and an additional dielectric layer. Figure 4 shows a cross section of two fluoropolymer parts bonding together by means of bonding layers according to the invention. 7 First application: Organic transistors It is now acknowledged that to obtain organic transistors with low hystereses and high mobilities, it is necessary for the grid dielectric to consist of a polymer having a low K (J.Veres et al. "Gate Insulators in Organic Field-Effect Transistors", Chem. Mater. 2004, 16,4543-4555). Among the low K polymers often used for the manufacture of organic transistors, fluoropolymers are materials of choice. However, the incorporation of such materials in the fabrication of transistors is not an easy matter. The major problem observed is that it is impossible, using wet methods (spin-coating or printing) to deposit on these materials, the other layers making up the stack of a transistor. Figure 1 shows the various steps in the fabrication of an organic transistor according to the prior art. For the top grid, the following are deposited in succession on a substrate (1): two electrodes (2). called source and drain; a semi conductive material (3); a layer of fluoropolymer (4) corresponding to the first fluoropolymer; the second electrode (2) called grid electrode. And for the bottom grid: an electrode (2) called grid; a layer of fluoropolymer (4) corresponding to the first fluoropolymer: the second electrodes (2). called source and drain: a semi conductive material (3). Due to the abovementioned difficulties of deposition on the layer of fluoropolymer (4), an adhesion (5) deficiency exists between this layer and the upper layer, that is the electrode (2) and/or the semiconductive material (3). A lack of uniformity of the layers is also observed. Thanks to the present invention, it is possible to deposit conductive inks by screen printing 8 or by inkjet printing. It is thereby possible, for example, to print the grid or the source and the drain of a transistor. Figure 2 shows the placement of a bonding layer according to the invention (6) between the fluoropolymer (4) layer and the electrodes (2) and/or the semiconductive material (3). On such a bonding layer (6). it is also possible to deposit other dielectrics (7) in a thin film, such as polyimides or silsesquioxanes, or PVP (polyvynilphenol) melamine formol, as shown in Figure 3. Here also, the deposition can be obtained by conventional techniques such as spin-coating or printing methods. Second application: Patterns on water-repellent fabrics or substrates A bonding layer according to the invention can be used for printing patterns on water-repellent fabrics or substrates, in which the water repellency is provided by a conventional fluoropolymer. In this case, the substrate is treated by a polymer having at least one fluorinated function and at least one acid or base function, by dip-coating or by printing methods such as flexography, inkjet heliography. After drying, the surface becomes compatible with conventional printing methods. Third application: Bonding of two fluoropolymer parts A bonding layer according to the invention can be used for bonding a part that is molded or machined in a fluoropolymer, with a second material which may not necessarily be a fluoropolymer. In this case, shown in Figure 4, the fluoropolymer (4) parts are coated with a polymer having at least one fluorinated function and at least one acid or base function (6), by dip-coating. Their interfaces become compatible with adhesives such as cyanoacrylate or epoxy/amine, cationic epoxy, UV acrylic (8). It is thereby possible to obtain a cohesive fracture of the adhesive seal. 9 Fourth application: Combination of the polymer carrying at least one fluorinated function and at least one acid or base function with other compounds Example 1: 5% by weight of a solution of Nafion® 2021 (DuPont) was added to S1818 photolithography resin (Shipley). The mixture was deposited by spin-coating on a polyethylene naphthalene substrate, previously coated with a layer of Cytop® fluoropolymer. The resin was annealed, exposed and developed as recommended by the resin manufacturer. It was then possible to carry out the steps of etching of the Cytop® layer. Example 2: 8% by weight of a solution of Nafion® 2021 (DuPont) was added to 5025 screen printing conductive ink (DuPont). The mixture thus obtained was screen printed on a layer of Cytop fluoropolymer through an appropriate stencil. It was then possible for example to print the grid of the transistor directly on a fluoropolymer based dielectric. Example 3: 0.2% by weight of a solution of Nafion® 2021 (DuPont) was added to TEC-IJ-010 (Inkteck) conductive ink for inkjet printing. The mixture thus obtained was compatible with the 60 micron inkjet printing head sold by MicroFab. After inkjet printing and annealing at 100°C, for 20 minutes, of such a mixture obtained on a layer of CytopR fluoropolymer, a conductive layer was obtained. This mixture made it possible for example to print the grid of the transistor on a fluoropolymer based dielectric. Example 4: An organic transistor having a top grid configuration was fabricated with P3HT (poly 3-n-hexylthiophene-2,5-diyl) as semiconductor, and Cytop® fluoropolymer as dielectric. The source and drain electrodes were gold. 0.05 g of poly 4-vinylpyridine was added to a solution comprising 1 g of Nafion® 2021 (DuPont) and 20 g of isopropanol. The mixture was screen-printed on the surface of the Cytop® fluoropolymer. The grid of the transistor was printed with an ink containing silver nanoparticles, such as Cabot AG-LT-G-100-S ink. This transistor, after application of a constant electric field to the grid, produced electrical aging curves compatible with organic electronic applications. 10 WE CLAIM : 1. A device comprising a layer made from a fluoropolymer, of which at least part of the surface is covered with a composition comprising a polymer having at least one fluorinated function and at least one acid or base function and forming a bonding layer on said fluoropolymer, said bonding layer being fully or partly covered by another layer. 2. The device as claimed in claim 1, characterized in that the acid function is provided by a carboxylic, phosphonic, sulfonic, sulfone or Si(CH3)3 function. 3. The device as claimed in claim 1. characterized in that the base function is provided by an amine. 4. The device as claimed in one of claims 1 to 3, characterized in that the monomer having at least one fluorinated function is of the same type as the monomer present in the fluoropolymer. 5. The device as claimed in one of claims 1 to 4, characterized in that the fluorinated function and the acid or base function are carried by the same monomer. 6. The device as claimed in one of the preceding claims, characterized in that the fluoropolymer is polyterafluoruethylene (PTFE) or Cytop . 7. The device as claimed in one of the preceding claims, characterized in that the polymer having at least one fluorinated function and at least one acid or base function is NafionR, Hyfion IonR or Flemion®. 8. The device as claimed in one of the preceding claims, characterized in that composition forming the bonding layer further comprises a compound capable of interacting with the acid or base functions of the polymer. 11

Full Text

FORM 2

THE PATENTS ACT, 1970 (39 of 1970)
& THE PATENTS RULES, 2003
COMPLETE SPECIFICATION
[See section 10, Rule 13]
BONDING LAYER ON FLUOROPOLYMERS;
COMMISSARIAT A L'ENERGIE ATOMIQUE, A CORPORATION ORGANIZED AND EXISTING UNDER THE LAWS OF FRANCE, WHOSE ADDRESS IS 25 RUE LEBLANC BATIMENT LE PONANT D", 75015 PARIS, FRANCE AND SOFILETA, A CORPORATION ORGANIZED AND EXISTING UNDER THE LAWS OF FRANCE, WHOSE ADDRESS IS 1 AVENUE DE CHANTEREINE, 38300 BOURGOIN JALLIEU, FRANCE.

THE FOLLOWING SPECIFICATION
PARTICULARLY DESCRIBES THE INVENTION AND THE MANNER IN WHICH IT IS TO BE PERFORMED.

FIELD OF THE INVENTION
The present invention relates to devices incorporating fluoropolymer layers.
It proposes to at least partially cover the layers with an additional layer called "bonding layer', for facilitating the deposition of subsequent layers.
Such a bonding layer is prepared using polymers having at least one fluorinated function and at least one acid or base function.
PRIOR ART
Fluoropolymers are commonly used in various technical fields today.
Thus, fluoropolymers are used in the manufacture of electronic components such as organic transistors, or electrical insulation, and in the fabrication of mechanical parts subject to extreme service conditions (temperature or the presence of aggressive solvents).
In the particular case of organic electronics, fluoropolymers, and in particular Cytop® (trade name of poly perfluoro butenyl vinyl ether), have particularly suitable properties for constituting the grid dielectric of a transistor.
However, the use of such fluoropolymers raises the following problems, still unsolved today:
it is impossible, using a wet method, to deposit other layers on a fluoropolymer
previously deposited in a thin film, regardless of the deposition method (spin-coating
or various printing methods);
it is impossible to bond two fluoropolymer parts together, or to bond a plastic to a
fluoropolymer.
2

This makes highly problematic the manufacture of complex devices comprising various elements indispensable for their operation. This is the case for example of a complete transistor, in which the placement of a dielectric requires subsequent manufacturing steps.
An obvious need therefore exists to develop technical solutions for facilitating and improving the deposits on fluoropolymer based layers.
SUMMARY OF THE INVENTION
The present invention is based on the Applicant's finding that certain fluoropolymers develop aptitudes to adhere to materials, and in particular to fluoropolymers.
Essentially, these particular fluoropolymers, having adhesive properties, carry at least one acid or base function.
According to a first aspect, the present invention therefore relates to a device, in particular a transistor, comprising a layer made from a fluoropolymer, of which at least part of the surface is covered with a composition comprising at least a polymer having at least one fluorinated function and at least one acid or base function.
According to the invention, the composition comprising at least the polymer having at least one fluorinated function and at least one acid or base function forms a bonding layer on the fluoropolymer. This bonding layer is itself partly or fully covered by one or more other layers made with materials of interest.
By definition, the device therefore partly consists of a first fluoropolymer. This part is called "layer", insofar as it has outer surfaces which are intended to be covered, at least partially or fully, by at least the bonding layer according to the invention.
In the context of the present invention, fluoropolymer means a polymer or a copolymer of which at least one of the component monomers contains at least one fluorine (F) atom per monomer. This polymer may be crosslinked or non-crosslinked.
Such polymers are, for example, selected from the following list:
3

TeflonR: trade name of polytetrafluoroethylene (PTFE) (sold by DuPont): CytopR: trade name of poly perfluoro butenyl vinyl ether (sold by Ashai Glass); HalarR (sold by Solvay Solexis); Hyflon® (sold by Solvay Solexis); Parylene-F (sold for example by Aldrich).
Note that these references are well known to a person skilled in the art in the field of polymers, but of which the exact chemical formula is not always available.
Cytop is advantageously selected from this list.
It will clearly appear from a reading of the rest of the description that this first fluoropolymer lacks any acid or base function.
The second polymer, used for the formation of the bonding layer according to the
invention, is a polymer or a copolymer defined as follows:
at least one of its component monomers contains at least one fluorine (F) atom per monomer. In this respect, it is therefore a second fluoropolymer; at least one of its component monomers contains an acid or base function. In the context of the present invention, the acid or base functions are defined by Bronsted or Lewis.
Polymers answering to this definition are for example: Nafion® (DuPont); Hyfion IonH (Solvay Solexis); FlemionR (Ashai Glass).
Here also, these are references well known to a person skilled in the art in the field of polymers, but of which the exact chemical formula is still unavailable.
Preferably, the acid function is provided by a carboxylic, phosphonic, sulfonic, sulfone or Si(CH3)3 function. The base function may be an amine.
According to an advantageous embodiment, the monomer having at least one fluorinated
4

function is of the same type as the monomer present in the fluoropolymer. This is the case for example of the pair Teflon® (first fluoropolymer)/Nafion® (second fluoropolymer) which both comprise monomers of tetrafluoroethylene.
Advantageously, the fluorinated function and the acid or base function are carried by the same monomer. This is the case for example of Nafion , of which the monomers of tetrafluoroethylene incorporate perfluorovinyl ether groups terminating in sulfonic groups.
It has been found that such a polymer carrying at least one fluorinated function and at least one acid or base function has aptitudes to adhere both to fluoropolymers. such as Teflon and Cytop (or equivalent materials), and to other materials, for example adhesive. Teflon thus covered permits the adhesion of a conductive ink, of another part made from Teflon® or from another material (for example melamine), etc.
The bonding layer thus formed, which advantageously has a thickness of between 20 nm and 2 um, can thus be partly or fully covered by one or more other layers prepared with materials of interest. They may be electrodes, semiconductive materials, dielectrics, layers of ink or adhesive.
It should be noted that for applications related to electronics in particular, it is desirable that the acid or base groups present in the fluoropolymer are not oriented under an electric field. To prevent this from occurring, it is recommended, in the composition serving for the formation of the bonding layer, to combine compounds of the molecule or polymer type creating bonds with the acid or base sites of the fluoropolymer. These bonds may be of the low energy interaction type, for example hydrogen bonds. Alternatively, an acid-base reaction may take place in solution between the fluoropolymer and the compound.
Furthermore, it is conceivable to mix the fluoropolymer carrying the acid or base functions directly with a material of interest, such as a resin, particularly of photolithography, inks in particular conductive inks, or dielectrics. Such a mixture also has a strong affinity for fluoropolymer based substrates. In this particular case, the layer placed on the bonding layer may for example consist of a metal to constitute electrical contacts.
5

According to a preferred embodiment, the inventive device is a transistor.
The present invention therefore serves to modify the surface of a fluoropolymer using a second fluoropolymer, and thereby to make the surface of the first fluoropolymer compatible with processes such as printing, spin-coating or bonding.
According to another aspect, the invention therefore relates to a method for fabricating a
device as defined above, comprising:
in a first step, the deposition, on all or part of the outer surface of the fluoropolymer
layer, of a composition comprising a polymer having at least one fluorinated
function and at least one acid or base function, in order to form a bonding layer after
drying:
in a second step, the deposition of a material of interest on this bonding layer, in
order to form another layer (functional layer) after drying.
The deposition of the second fluoropolymer on the first can be carried out either by dip-coating, or by spin-coating, or by printing (inkjet, flexography, heliography, etc.) These techniques can be implemented for the second deposition.
The second polymer, carrying at least one fluorinated function and at least one acid or base function, is generally formulated in a composition suitable for the deposition technique employed.
Such a composition may be in the form of a solution comprising from 0.3 to 5% by weight of the polymer having at least one fluorinated function and at least one acid or base function.
A solvent suitable for dissolving said polymer is selected and incorporated in the composition. It may for example be isopropanol.
Typically, after deposition and drying, the second polymer forms a thin film the thickness of which is between 20 nm and 2 µm. This thickness depends in particular on the fluoropolymer concentration of the layer on which the deposition is made.
6

This composition may also be enriched with one or more polymers or compounds having a chemical structure close to the structure of the layer or of the material that is added on to the second polymer. In fact, in a subsequent step of the fabrication method, a material of interest is advantageously deposited on the layer thus formed.
By way of example, such a composition has the following formula (% by weight): -4%Nafion2021;
- 90% isopropanol;
- 4% polyvinyl phenol;
- 2% melamine.
The bonding layer obtained with this composition is particularly suitable for receiving (and in particular for being covered fully or partly) a layer based on polyvinylphenol crosslinked by melamine formol. This layer serves to limit the electrical leakage of the complete stack.
DETAILED DESCRIPTION OF THE INVENTION
The way in which the invention can be implemented and the advantages thereof will appear more clearly from the exemplary embodiments that follow, provided for information and nonlimiting, in conjunction with the appended figures.
Figure 1 shows a schematic of the transistor obtained by the prior art methods.
Figure 2 shows a schematic of a transistor obtained according to the present invention,
comprising a bonding layer.
Figure 3 shows a schematic of a transistor obtained according to the present invention,
comprising a bonding layer and an additional dielectric layer.
Figure 4 shows a cross section of two fluoropolymer parts bonding together by means of
bonding layers according to the invention.
7

First application: Organic transistors
It is now acknowledged that to obtain organic transistors with low hystereses and high mobilities, it is necessary for the grid dielectric to consist of a polymer having a low K (J.Veres et al. "Gate Insulators in Organic Field-Effect Transistors", Chem. Mater. 2004, 16,4543-4555).
Among the low K polymers often used for the manufacture of organic transistors, fluoropolymers are materials of choice. However, the incorporation of such materials in the fabrication of transistors is not an easy matter. The major problem observed is that it is impossible, using wet methods (spin-coating or printing) to deposit on these materials, the other layers making up the stack of a transistor.
Figure 1 shows the various steps in the fabrication of an organic transistor according to the prior art.
For the top grid, the following are deposited in succession on a substrate (1): two electrodes (2). called source and drain; a semi conductive material (3);
a layer of fluoropolymer (4) corresponding to the first fluoropolymer; the second electrode (2) called grid electrode.
And for the bottom grid:
an electrode (2) called grid;
a layer of fluoropolymer (4) corresponding to the first fluoropolymer:
the second electrodes (2). called source and drain:
a semi conductive material (3).
Due to the abovementioned difficulties of deposition on the layer of fluoropolymer (4), an adhesion (5) deficiency exists between this layer and the upper layer, that is the electrode (2) and/or the semiconductive material (3). A lack of uniformity of the layers is also observed.
Thanks to the present invention, it is possible to deposit conductive inks by screen printing
8

or by inkjet printing. It is thereby possible, for example, to print the grid or the source and the drain of a transistor.
Figure 2 shows the placement of a bonding layer according to the invention (6) between the fluoropolymer (4) layer and the electrodes (2) and/or the semiconductive material (3).
On such a bonding layer (6). it is also possible to deposit other dielectrics (7) in a thin film, such as polyimides or silsesquioxanes, or PVP (polyvynilphenol) melamine formol, as shown in Figure 3. Here also, the deposition can be obtained by conventional techniques such as spin-coating or printing methods.
Second application: Patterns on water-repellent fabrics or substrates
A bonding layer according to the invention can be used for printing patterns on water-repellent fabrics or substrates, in which the water repellency is provided by a conventional fluoropolymer.
In this case, the substrate is treated by a polymer having at least one fluorinated function and at least one acid or base function, by dip-coating or by printing methods such as flexography, inkjet heliography. After drying, the surface becomes compatible with conventional printing methods.
Third application: Bonding of two fluoropolymer parts
A bonding layer according to the invention can be used for bonding a part that is molded or machined in a fluoropolymer, with a second material which may not necessarily be a fluoropolymer.
In this case, shown in Figure 4, the fluoropolymer (4) parts are coated with a polymer having at least one fluorinated function and at least one acid or base function (6), by dip-coating. Their interfaces become compatible with adhesives such as cyanoacrylate or epoxy/amine, cationic epoxy, UV acrylic (8). It is thereby possible to obtain a cohesive fracture of the adhesive seal.
9

Fourth application: Combination of the polymer carrying at least one fluorinated function and at least one acid or base function with other compounds
Example 1:
5% by weight of a solution of Nafion® 2021 (DuPont) was added to S1818
photolithography resin (Shipley). The mixture was deposited by spin-coating on a
polyethylene naphthalene substrate, previously coated with a layer of Cytop®
fluoropolymer. The resin was annealed, exposed and developed as recommended by the
resin manufacturer. It was then possible to carry out the steps of etching of the Cytop®
layer.
Example 2:
8% by weight of a solution of Nafion® 2021 (DuPont) was added to 5025 screen printing conductive ink (DuPont). The mixture thus obtained was screen printed on a layer of Cytop fluoropolymer through an appropriate stencil. It was then possible for example to print the grid of the transistor directly on a fluoropolymer based dielectric.
Example 3:
0.2% by weight of a solution of Nafion® 2021 (DuPont) was added to TEC-IJ-010 (Inkteck) conductive ink for inkjet printing. The mixture thus obtained was compatible with the 60 micron inkjet printing head sold by MicroFab. After inkjet printing and annealing at 100°C, for 20 minutes, of such a mixture obtained on a layer of CytopR fluoropolymer, a conductive layer was obtained. This mixture made it possible for example to print the grid of the transistor on a fluoropolymer based dielectric.
Example 4:
An organic transistor having a top grid configuration was fabricated with P3HT (poly 3-n-hexylthiophene-2,5-diyl) as semiconductor, and Cytop® fluoropolymer as dielectric. The source and drain electrodes were gold. 0.05 g of poly 4-vinylpyridine was added to a solution comprising 1 g of Nafion® 2021 (DuPont) and 20 g of isopropanol. The mixture was screen-printed on the surface of the Cytop® fluoropolymer. The grid of the transistor was printed with an ink containing silver nanoparticles, such as Cabot AG-LT-G-100-S ink. This transistor, after application of a constant electric field to the grid, produced electrical aging curves compatible with organic electronic applications.
10

WE CLAIM :
1. A device comprising a layer made from a fluoropolymer, of which at least part of the surface is covered with a composition comprising a polymer having at least one fluorinated function and at least one acid or base function and forming a bonding layer on said fluoropolymer, said bonding layer being fully or partly covered by another layer.
2. The device as claimed in claim 1, characterized in that the acid function is provided by a carboxylic, phosphonic, sulfonic, sulfone or Si(CH3)3 function.
3. The device as claimed in claim 1. characterized in that the base function is provided by an amine.
4. The device as claimed in one of claims 1 to 3, characterized in that the monomer having at least one fluorinated function is of the same type as the monomer present in the fluoropolymer.
5. The device as claimed in one of claims 1 to 4, characterized in that the fluorinated function and the acid or base function are carried by the same monomer.
6. The device as claimed in one of the preceding claims, characterized in that the fluoropolymer is polyterafluoruethylene (PTFE) or Cytop .
7. The device as claimed in one of the preceding claims, characterized in that the polymer having at least one fluorinated function and at least one acid or base function is NafionR, Hyfion IonR or Flemion®.
8. The device as claimed in one of the preceding claims, characterized in that composition forming the bonding layer further comprises a compound capable of interacting with the acid or base functions of the polymer.
11

Documents:

http://ipindiaonline.gov.in/patentsearch/GrantedSearch/viewdoc.aspx?id=o/TuerzV9jNPHFmF5EQD1g==&loc=vsnutRQWHdTHa1EUofPtPQ==

« Previous Patent

Next Patent »

Patent Number

277978

Indian Patent Application Number

1490/MUM/2008

PG Journal Number

51/2016

Publication Date

09-Dec-2016

Grant Date

07-Dec-2016

Date of Filing

15-Jul-2008

Name of Patentee

COMMISSARIAT A L'ENERGIE ATOMIQUE

Applicant Address

25 RUE LEBLANC BATIMENT LE PONANT D, 75015 PARIS,

Inventors:

#	Inventor's Name	Inventor's Address
1	SERBUTOVIEZ CHRISTOPHE	19 RUE DODE, 38500 VOIRON,
2	BENWADIH, MOHAMED	5 AVENUE, DU GENERAL DE GAULLE, 94500 CHAMPIGNY SUR MARNE,
3	VERILHAC JEAN MARIE	32 RUE JEAN MACE, 38000 GRENOBLE,

PCT International Classification Number

B05D3/12; B32B17/10

PCT International Application Number

N/A

PCT International Filing date

PCT Conventions:

#	PCT Application Number	Date of Convention	Priority Country
1	0705621	2007-08-01	France