Indian Patents. 260129:""REACTIVITY DRIFT AND CATALYST DEGRADATION IN POLYURETHANE FOAM"

Title of Invention	""REACTIVITY DRIFT AND CATALYST DEGRADATION IN POLYURETHANE FOAM"
Abstract	The invention is directed to methods of preparing compositions used to manufacture polyurethane foams. The invention provides methods for making compositions used to make polyurethane foams that include amine catalysts, but formulated such that catalytic potency is not diminished over time before the forming of a foam.

Full Text	. REACTIVITY DRIFT AND CATALYST DEGRADATION IN POLYIJRETHANE FOAM CROSS-REFERENCE TO RELATED APPLICATIONS [01] Not Applicable. STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH OR DEVELOPMENT [02] Not Applicable. INCORPORATION-BY-REFERENCE OF MATERIAL SUBMITTED ON A COMPACT DISC [03] Not Applicable. [04] BACKGROUND OF THE INVENTION [05] Field of the Invention [06] The present invention relates to consistently manufacturing polyurethane foams prepared with agents that hydrolyze, creating acids that attack catalysts. For example, foams prepared with alkyl alkanoates. [07] I. Introduction [08] Polyurethane foams insulate, float, cushion, glue, clothe and absorb sound, among a plethora of other applications. Polyurethanes, defined as polymeric substances having multiple urethane linkages, are a large family of polymers with widely ranging properties and uses. The types and properties of polyurethanes are so varied that the Alliance for the Polyurethanes Industry (Arlington, VA) has dubbed them the "erector set" of the plastics industry. Types of polyurethanes include rigid and flexible foams; thermoplastic polyurethane; and other miscellaneous types, such as coatings, adhesives, sealants and elastomers. Flexible foams (e.g., that found in most car seat cushions) are generally open-celled materials, while rigid foams (e.g., building insulation) usually have a high proportion of closed cells. [09] While rigid polyurethane foams are found in insulation in refrigeration systems, structural applications and flotation applications, transportation vehicles and metal doors, flexible polyurethane foams are used in automotive seats, headrests and armrests; in carpet padding, packaging, clothing, leather products, shoe uppers, tents, life rafts, labels, handbags and furniture cushions. Semi-flexible molded foams are found in automotive instrument panels, energy managing foam and sound absorbing foam. [010] A. Forming polyurethane foams: the gel and blow reactions [Oil] Polyurethane foams are produced by reacting a di- or polyisocyanate (compound containing an isocyanate group (N=C=O attached to an organic radical)) with compounds containing two or more active hydrogens, generally in the presence of catalysts, silicone-based surfactants and other auxiliary agents. The active hydrogen-containing compounds are typically polyols (organic compounds having more than one hydroxyl (-OH) groups per molecule), primary and secondary polyamines and water. Two major reactions are promoted by the catalysts: the gel reaction and the blow reaction. Balance is needed between reaction of the isocyanate and the polyol (gel reaction) and the reaction of the isocyanate with water (blow reaction) in order to produce a. polyurethane foam in which the cells are relatively uniform and the foam has specific properties depending on the anticipated application; for example, rigid foams, semi-rigid foams, and flexible foams. Foams can be formed by a one-shot method or by formation of a pre-polymer and subsequent reaction of the pre-polymer with water in the presence of a catalyst. [012] The gel reaction consists of the isocyanate reacting with the polyol or polyamine and leads to the formation of a polymer of high molecular weight. This reaction predominates in foams blown exclusively with low boiling point organic compounds. The blow reaction occurs between isocyanate and water. This reaction promotes polymer growth and blows carbon dioxide bubbles into the developing polyurethane mass. The blow reaction helps avoid, or reduces the use of, auxiliary blowing agents. The in situ generation of carbon dioxide by the blow reaction plays an essential role in the preparation of one-shot, water-blown polyurethane foams. [013] Examples of unbalanced gel and blow reactions include those foams in which carbon dioxide evolves too quickly, forming foams that tend to collapse. A gel reaction that proceeds too rapidly reduces foam-rise, resulting in a high density foam. In practice, the balancing of these two reactions is controlled by the nature of the promoters and catalysts, generally amine and/or organo-metallic (an organic molecule containing a metal atom). Frequently, a gelling catalyst and a blowing catalyst are used together to balance gelling and blowing. [014] B. Blowing agents and catalysts [015] Blowing agents traditionally include chlorofluorocarbons (CFCs). However, CFCs detrimentally affect the earth's ozone layer. To avoid the dangers of CFCs, some processes use hydrochloroflurocarbons (HCFCs) instead. For example, some processes use monochlorodifluoromethane (CHC1F2) (Keske and Schulte, 1991; Keske and Schulte, 1993a; Keske and Schulte, 1993b). However, even HCFCs also carry important environmental risks, even though they are less harmful than CFCs. [016] Until recently, using alkyl alkanoates, including methyl formate, as an alternative sole blowing agent were unsatisfactory. Such foams shrink more than 10% after manufacture. Methyl formate as a blowing agent can produce stable foams if used with other blowing agents-such as the undesirable CFCs or HCPCs-produce dimensionally stable foams. However, using alkyl alkanoates alone-without any harmful CFCs or HCFCs--has recently been accomplished (Kalinowski et at., 2004). [017] Catalysts generally fall into two categories: tertiary amines (mono- and poly-) and organo-metallic compounds. Organo-metallic catalysts favor the gel reaction, while amine catalysts favor the blow or gel reactions depending on the catalyst. Using metal catalysts in flexible foam formulations also increases the number of closed cells, creating tighter foams. Tertiary amines also are effective as catalysts for the chain extension reaction and can be used in combination with organo-metallic catalysts. For example, in the preparation of flexible slabstock foams, the one-shot process uses triethylenediamine to promote the blow reaction and the cross-linking reaction, while an organo-metallic compound synergistically promotes the chain extension reaction. [018] C. The foam-blowing process [019] The process for making foams typically involves the mixing of the starting materials with polyurethane foam production machinery and pouring the reacting mixture, as it exits the mix-head, into a mold. To prepare foams, a first component (component A or "A-side"), supplying isocyanate, is mixed with a second component (component B or "B-side"), supplying the polyol and usually a catalyst. Component A can also provide a surfactant and a blowing agent. Component B can also supply a surfactant and a blowing agent. The optional constituents of the sides, as well as the catalyst, can be alternatively introduced by a third stream. [020] D. Obstacles to manufacturing consistent polyurethane foams [021] Until recently, blowing agents were CFCs, HCFCs and hydrofluorocarbons (HFCs); however, these have many undesirable characteristics, especially as related to environmental concerns. AlkyI alkanoates can be used as effective substitutes, or with other blowing agents (Kalinowski et al., 2004). However, when using an alkyl alkanoate as a blowing agent, alone or with CFCs, HCFCs, HFCs, hydrocarbons or hydrofluoroethers (HFEs) in the presence of water, the blowing agent can hydrolyze. Other foam ingredients can hydrolyze in the presence of water as well, notably polyester polyols. This hydrolysis results in the formation of acids that attack the amine catalyst, causing the catalyst's reactivity to deteriorate. The consequence is that the reactivity of the foam slows. This fluctuation interferes with consistent, efficient and reproducible foam production and can have a deleterious effect on the properties or suitability of the resultant foam. [022] Traditionally, delayed action catalysts, which are acid-blocked amines, such as simple amine salts of a tertiary amine and a carboxylic acid (such as formic, acetic or 2-ethylhexanoic acid) were used to counter this problem, but these are expensive and the choices of such catalysts is limited. The foam industry is plagued by imperfections in the manufacturing process, most notably by hydrolysis of certain ingredients which target a single acid-vulnerable molecule: the amine catalyst. [023] BRIEF DESCRIPTION OF THE DRAWINGS [024] Figure la shows the protective effect the methods of the invention have on retaining catalyst activity in the formation of polyurethane foams. The reactivity of the gel after formulation is plotted. [025] Figure 1 b shows the reactivity change observed in the experiments of Figure 1 a, expressed as percent change in reactivity. [026] SUMMARY OF THE INVENTION [027] Accordingly, it is an object of the invention to overcome these and other problems associated with hydrolyzable ingredients. [028] In a first aspect, the invention provides methods of preparing components used to make polyurethane foams, where at least one blowing agent is combined with at least one catalyst and at least one acid, wherein the at least one blowing agent is other than water, such that the activity of the catalyst does not substantially deteriorate over time. The blowing agent can be an alkyl alkanoate, such as methyl formate; the catalyst can be an amine catalyst, and the acid can be an organic acid, such as formic acid. [029] In a second aspect, the invention provides methods of stabilizing/retaining activity of catalysts used in polyurethane foam production, where at least one blowing agent is combined with at least one catalyst and at least one acid, wherein the at least one blowing agent is other than water, such that the activity of the catalyst does not substantially deteriorate over time. The blowing agent can be an alkyl alkanoate, such as methyl formate; the catalyst can be an amine catalyst, and the acid can be an organic acid, such as formic acid. [030] In yet a third aspect, the invention provides compositions suitable for preparing polyurethane foams, such that the activity of a catalyst in the composition remains stable over time. In such compositions, at least one blowing agent is combined with at least one catalyst and at least one acid, wherein the at least one blowing agent is other than water, such that the activity of the catalyst does not substantially deteriorate over time. The blowing agent can be an alkyl alkanoate, such as methyl formate; the catalyst can be an amine catalyst, and the acid can be an organic acid, such as formic acid. [031] In a fourth aspect, the invention provides polyurethane foams manufactured from compositions wherein the activity of a catalyst remains stable over time. In such foams, at least one blowing agent is combined with at least one catalyst and at least one acid, wherein the at least one blowing agent is other than water, such that the activity of the catalyst does not substantially deteriorate over time, and then mixed with a polyol-containing composition. The blowing agent can be an alkyl-alkanoate, such as methyl formate; the catalyst can be an amine catalyst, and the acid can be an organic acid, such as formic acid. [032] In all aspects of the invention, the acid can be present, by weight, from 1% to 500% of the molar equivalent of the amine catalyst. [033] These and other features, aspects and advantages will become better understood with reference to the following description, examples and appended claims. [034] DETAILED DESCRIPTION OF THE INVENTION [035] The problems of the imperfect amine catalyst that produces foams that are too tight (as when most blocked catalysts are used) or falls prey to acid attack such that catalyst activity deteriorates, is solved by the present invention using a simple and inexpensive method. The addition of an acid to the polyol blend (component B), surprisingly and unexpectedly, eliminates the degradation of amine catalysts. The acid is added at a concentration (by weight) of about 1% to about 500% of the molar equivalent of the amine catalyst(s); preferably from about 10% to about 400% of the molar equivalent of the amine catalyst(s); more preferably from about 50% to about 300% of the molar equivalent of the amine cataiyst(s). In a most preferred embodiment, formic acid is added to component 8, wherein the blowing agent in the system is methyl formate. [036] //. Practicing the invention [037] A. Component A [038] 1. Isocyanates [039] When manufacturing a foam from components A and B, component A contains an isocyanate, or mixtures and combinations of discrete isocyanates, and preferably also a surfactant. The isocyanate can be any of the isocyanates, organic or inorganic, conventionally used in the production of polyurethane foams. Such polyisocyanates are commonly used in the preparation of polyurethanes by reaction with compounds containing two or more active hydrogen-containing groups. Any of the polyfunctional isocyanates, such as isophorone diisocyanate, polymeric methylenebis (phenyl isocyanate), 2,6-tolulene diisocyanate, 4,4'-methylenebis(phenyl isocyanate), dianisidine diisocyanate, tolidine diisocyanate, hexamethylene diisocyanate, m-xylene diisocyanate, 1,5-napthalene diisocyanate, p-phenylene diisocyanate 1,5-napthalene diisocyanate, p-phenylene diisocyanate, 1,4-di-ethylbenzene diisocyanate, polymethylenepolyphenylisocyane, 3,3-diphenyldimethylmethane-4,4-diisocyanate, xylylene diisocyanates, xylyl diisocynates, 2,4-toluenediisocyante dimer, m-phenylenediisocyante, toluene diisocynates, diphenylmethane-2,4-diisocyanate, etc.. Mixtures of two or more isocyanates can be used, such as mixtures of the 2,4- and 2,6-isomers of tolulene diisocyanate or 2,4'- and 4,4'-isomers of methylenebis(phenyl isocy-anate). Modified forms of 4,4'-methylenebis (phenyl isocyanate) or mixtures of the 2,4'-isomer and 4,4'-isomer thereof can also be used. [040] 2. Blowing agents [041] In addition, component A can contain a blowing agent, although including such an agent in component A is unnecessary. In one embodiment, the blowing agent is an alkyl alkanoate, with methyl formate being preferred. Derivatives and precursors of a selected alkyl alkanoate can also be used, either alone or with methyl formate. [042] A "derivative and/or precursor" of alkyl alkanoate is any composition in which the alkyl alkanoate is attached to an inert carrier with respect to the remaining ingredients of components A and B. The derivative and/or precursor of the alkyl alkanoate maintain the functionality of the alkyl alkanoate. If an alkyl alkanoate derivative and/or precursor are used, it is a complex that maintains the entire structure as a moiety of the complex. A "precursor" is a composition that produces an alkyl alkanoate at some point prior to, or during, the foaming process. [043] Other blowing agents can be present in addition to alkyl alkanoates. For example, CFCs, HCFCs, MFCs, methylene chloride, hydrofluorocarbons, hydrocarbons or other organic compounds can also be used. Water itself is a blowing agent and is almost always present in at least residual quantities. The addition of an acid (or blend) to the polyol blend (component B), surprisingly and unexpectedly, reduces or eliminates the further degradation of amine catalysts. The acid (or blend) is added at from about 1% to about 500% of the molar equivalent of the amine catalyst(s); preferably from about 10% to about 400% of the molar equivalent of the amine catalyst(s); more preferably from about 50% to about 300% of the molar equivalent of the amine catalyst(s). The materials of component A can be blended in any standard manner. The order of blending is not particularly significant. Nevertheless, a convenient order of mixing is to add surfactant to isocyanate, and then to add the acid inhibitor, if any, and finally to add the blowing agent(s), if any. [044] The relative proportions of ingredients should be such that if component A contains one or more blowing agents, the concentration of blowing agent(s) in component A is from about 0.5% by weight to about 12% by weight, preferably about 2% by weight to about 10% by weight. The alkyl alkanoate (and/or derivative and/or precursor thereof) itself can make up as much as about 12% by weight, preferably as much as about 10% by weight, such as from about 2% by weight to about 10% by weight, of component A. The surfactant can make up less than about 2% by weight, preferably about 0.75% by weight, of component A. If an acid inhibitor is desired, it can be included in a concentration of up to about 0.5% by weight, based on the weight of component A. Typically, the balance of component A is the isocyanate. [045] 3. Surfactants and miscellaneous agents [046] Any conventional, A-side surfactant can be incorporated into component A. Examples of such surfactants include silicones, such as B-8407, DC-5160, DC-198, DC-5125, DC-1315 and B-8021 (Degussa/Goldschmidt Chemical Corp.; Mapleton, IL); L-620 (Union Carbide; Houston, TX); L-6202 and Y-10390 (Air Products; Allentown, PA), other silicones and siloxaneoxyalkylene block copolymers (Bailey and O'Connor, 1958; Ferrigno, 1963). The surfactant choice, while not essential to the present invention, affects the cell structure in the produced foam. [047] Other compositions, such as fire retardants, for example, those containing bromine, chlorine or phosphorus, can also be included in the component A. Because the fire retardant industry continues to be in constant flux, the available chemicals and chemical families are also in flux. However, any fire retardant that is appropriate for use in traditionally blown foams are appropriate for use in the foams of the invention. [048] B. Component B [049] 1. Polyol [050] Component B contains at least one polyol. Component B typically consists of 50% polyol(s) (by weight) to about 98% (by weight), preferably 70% (by weight) to about 92% (by weight) of at least one polyol. [051] When using methyl formate in component B, at least one of the polyol(s) in component B is a polyalkoxylated amine, a polyalkoxylated ether or a polyester polyol and has a hydroxyl number of from about 20 to about 1000. Preferably, the hydroxyl number is from about 20 to about 750, most preferably about 300 to about 500 for rigid foams and most preferably 20-100 flexible foams. However, the preferred hydroxyl ranges are determined solely by the desired end product. The skilled artisan can determine the appropriate hydroxyl number. The polyalkoxylated polyols preferably are polyethoxylated, polypropoxylated, or polybutoxylated, or mixtures thereof. The polyalkoxylated amine can be, for example, a polyalkoxylated aliphatic amine or a Mannich polyol; the polyalkoxylated ether can be, for example, a polyalkoxylated sucrose or glycerin; and the polyester polyol can be a transesterification of a terephthalate or castor oil. The polyols can be made individually or as coinitiators. [052] One or more of any one of the three classes of polyols, or any combination of polyols from any two or all three of the classes, can be used in component B. Component B can contain other polyols as well; preferably, the total of all polyols present from the three classes (that is, the total of all polyols from any of the polyalkoxylated amines, polyalkoxylated ethers and polyester polyols) make up more than about 50% by weight of all the polyols of component B, and at least about 50% by weight of component B. [053] Other useful polyhydric compounds, whether or not an alkyl alkanoate is used as a blowing agent and in addition to those listed above, include ethylene glycol, propylene glycol, diethylene glycol, dipropylene glycol, glycerol, pentaerythritol, sorbitol, sucrose, methyl glucoside, glucose, etc.. Polyamine compounds that can be reacted with alkylene oxide to prepare amine-based polyols include mono-, di-, and trietha-nol amine, ethylene diamine, diethylene diamine, toluene diamine, etc.. These polyhydric alcohols and polyamine compounds can be reacted separately with alkylene oxides, or they can be pre-mixed in the preparation of polyether polyol mixtures or blends. Preferred polyester polyols are those based on terephthalic, phthalic, isophthalic, adipic, succinic, glutaric, fumaric acid(s), and combinations thereof. [054] 2. Acids [055] In those compositions in which a blowing agent can hydrolyze or otherwise deteriorate, such that a catalyst in the mixture is attacked with consequent reduction in catalytic activity, an acid is added to the mix to protect the susceptible catalyst. Any organic acid or inorganic acid that protects the amine catalyst from acids generated by the hydrolysis of a blowing agent or other ingredients of component B can be used. Protection consists of maintaining a constancy of the reaction rate that permits the continued manufacture of the final product without a detrimental change in the performance. Any acid that functions to protect the amine catalyst from acid attack is suitable for use. In general, appropriate acids have a pKa greater than 0; more preferably 0-10; and more preferably 0-5. Preferably the acid is organic. Table I lists some examples of suitable acids. (Table Remove) [059] Such a formulation of component B as presented in Table 3 results in a solution where the catalysts retain consistent activity over the life of the solution. This and other component B solutions formulated with an acid of the blowing agent retain consistent catalyst activity over time. For example, acceptable reactivity drifts are determined by the end-product and the specific application of the product. Preferably, the reactivity drift stays within acceptable ranges in excess of 1 week, more preferably, in excess of 6 months, most preferably, in excess of 2 years. Those of ordinary skill in the art of producing polyurethane foams can easily adjust the types and quantities of each polyol and the ratio of alkyl alkanoate to water in the formula such that the desired properties of the finished foam are achieved. [060] Water in component B can be from 0% to about 5%, preferably about 0.5% to about 4%, more preferably about 1 % to about 3% (by weight). Water can serve as a blowing agent as well as add rigidity to the resulting foam. [061] The alkyl alkanoate in component B is preferably methyl formate and/or any derivative and/or precursor thereof. The alkyl alkanoate constitutes as much as about 15%, preferably about 2% to about 15% (by weight) of component B. The acid is present in a sufficient amount to retain the activity of any amine catalysts. [062] The alkyl alkanoate, as well as the acid, can be introduced by a separate stream in addition or in place of that which can be in either or both of components A and B. The concentrations of alkyl alkanoate in components A and B and the amount introduced to the reaction mixture by way of a separate stream are adjusted and coordinated so that the resulting concentration of total alkyt alkanoate (or derivative and/or precursor thereof) brought together upon mixing components A and B and separate streams, if any, based on the total weight of the resulting mixture, is from about 1% to about 12%, preferably from about 4% to about 8%. Other blowing agents can be used or at least be present. These include, for example, CFCs, MFCs, HCFCs, HFEs, hydrocarbons, other alkyl alkanoates, as well as any others known to the skilled artisan. [063] More preferably, the total amount of blowing agent present in each component and in the total combination of all ingredients mixed together to form a foaming mixture should be substantially free (less than 1% by weight) of CFCs, HCFCs, MFCs, HFEs and hydrocarbons; more preferably, no CFCs, HCFCs, HFCs, HFEs and hydrocarbons are present. The mixture to blow the foam is preferably also substantially free, more preferably, devoid, of any other substituted or unsubstituted hydrocarbon. Ideally, the foaming mixture is substantially free, more optimally devoid, of any other organic compound that acts as a blowing agent. [064] The polyols in the combination need not form a separate composition; it is unnecessary to mix the constituents of the mixture together to form a premix and then to form component B by mixing the premix with the remaining ingredients of component B. The ingredients of component B can be mixed in any order, and the polyols can be added separately from each other as separate ingredients to form component B. [065] 5. Catalysts [066] In addition to the amine catalysts listed in Table 2, any organometallic compound known to be a catalyst in the reaction between an isocyanate group and an active hydrogen-containing group can be used as a catalyst. Such catalysts include, but not limited to, the organic acid salts of, and the organometallic derivatives of, bismuth, lead, tin, iron, antimony, uranium, cadmium, cobalt, thorium, aluminum, mercury, zinc, nickel, cerium, molybdenum, vanadium, copper, manganese, and zirconium. [067] 6. Other agents [068] Component B can also contain other ingredients as desired. Optional additives such as dispersing agents, cell stabilizers, surfactants, flame retardants, and the like, that are commonly used in the fabrication of polymer foams can be used in the process of the invention. For example, phosphorus-based flame retardant additives can be used if flame retardancy is desired. A finer cell structure can be obtained if organo-silicone polymers are used as surfactants in the reaction mix. [069] Other optional additives, such as inorganic and organic fillers, can also be used. Examples of inorganic fillers include calcium carbonate, barium sulfate, silica, glass, antimony oxides, etc.; examples of organic fillers include the various polymers and copolymers of vinyl chloride, vinyl acetate, acrylonitrile, styrene, melamine, partially oxyalkylated melamine, etc. Organic esters can also be used. Particularly preferred esters are those derived from dicarboxylic acids, such as oxalic, malonic, succinic, glutaric, maleic, phthalic, isophthalic and terephthalic acids. [070] For example, a fire retardant, such as those containing bromine, chlorine or phosphorus, can be incorporated into the mixture to impart fire resistance. Other commonly used additives are hydroxyl-containing compositions, such as castor oil, aromatic polyesters, glycols and/or alkoxylated sorbitols, acid scavengers (for example, a-methyl styrene), acid formation inhibitors or diluents. [071] C. Forming the foam [072] Component A and component B can be mixed, such as through a static mix, high pressure mix or impingement mix chamber or any other device commonly known in the industry, by standard procedures to produce a homogenous blend. In a preferred embodiment, a one-shot method of foam fabrication is used, whereby the isocyanate containing stream (component A) and the polyol-containing and catalyst-containing stream (component B) are mixed. Each of these streams is preferably liquid in which all of the various additives are preferably soluble, although dispersions utilizing solid components can be used as desired. [073] Preferably component A and component B are mixed such that there is about 0.3 to about 1.2 polyol equivalents per equivalent polyisocyanate. "Polyol equivalent" means the weight component B used in the foam divided by the equivalent weight of component B. "Polyisocyanate equivalent" means the weight component A used in the foam divided by the equivalent weight of component A. [074] Examples [075] Without further elaboration, it is believed that one skilled in the art can, using the preceding description, us the present invention to its fullest extent. The following examples are offered by way of illustration and not by way of limiting the remaining disclosure. [076] Example 1 [077] Reactivity can be measured and then compared to the profile of the chemical product information sheet for each chemical system. The reactivities can be determined using the String-Gel time and Tack-Free time. [078] STRING-GEL [079] String-Gel is the measure of time from the beginning of the shot until the foam adheres to a thin wire (approx. 1/16" in diameter) and becomes "stringy'-something like bubble gum. [080] String-Gel measurements are made as follows: [081] 1. Take a 10-second shot into a 30-gallon plastic bag and simultaneously start the stopwatch. [082] 2. At about 60-seconds, poke a wire into the rising chemical at least 12 inches deep and take it out again. Repeat poking wire in and out of the rising chemical at 5-second intervals until the foam sticks to the wire and forms a bubble gum-like string. Do not poke the same place twice. [083] 3. Record time the String-Gel took place. [084] Tongue depressors or Popsicle sticks should not be used for String-Gel because they do not go deep enough into the rising foam. A wire similar to a coat hanger is suitable. [085] TACK-FREE [086] Tack-Free is the measure of time from the beginning of the shot until the foam becomes "tack-free" or does not stick to fingertip when touched tightly. [087] A Tack-Free measurement may be made as follows: [088] 1. Follow Step 1-3 for String-Gel. [089] 2. Measure from the start of the shot until foam becomes "tack-free" or no longer sticks to the fingertip when touched lightly. [090] 3. Record the time. [091] String-Gel and Tack-Free times can be recorded from the same shot if the String-Get is observed first and Tack-Free is further observed. It is important to keep the plastic bag off cold floors because it will affect the reactivity times. [092] Reactivity of an amine catalyst using methyl formate as a blowing agent, with and without formic acid added, was determined. Foams were blown 0, 1,2, 3 and 4 weeks after formulating component B with and without acid. The times of gel reactivity were assayed as described above, and the data plotted. The data are expressed as time of gel reactivity (Table 3 and Figure la) and % change of reactivity compared to the baseline of 0 weeks (Table 4 and Figure 1 b). (Table Remove) [093] As shown in Figure la and Table 3, when the acid is not present, the gel reactivity declines over time, so that at 4 weeks after formulating component B, gel reactivity requires 20 more seconds than at baseline (Fig. la, diamonds). However, when formic acid is present, reactivity does not decline, remaining at 78-80 seconds (Fig. la, squares). Figure lb and Table 4 report these results as percentage of change from baseline, reinforcing the dramatic effect acid has upon protecting the amine catalyst from reactivity drift arid degradation. The percent of reactivity change reaches 45% at 4 weeks when acid is not present (Fig. Ib, diamonds), while that for the component containing acid marginally fluctuates, with a range of-2.5% to 0% (Fig Ib, squares). (Table Remove) [094] Other Embodiments [095] The detailed description set forth above is provided to aid those skilled in the art in practicing the present invention. However, the invention described and claimed herein is not to be limited in scope by the specific embodiments herein disclosed because these embodiments are intended as illustration of several aspects of the invention. Any equivalent embodiments are intended to be within the scope of this invention. Indeed, various modifications of the invention in addition to those shown and described herein will become apparent to those skilled in the art from the foregoing description which do not depart from the spirit or scope of the present inventive discovery. Such modifications are also intended to fall within the scope of the appended claims. [096] References [097] All publications, patents, patent applications and other references cited in this application are incorporated herein by reference in their entirety for all purposes to the same extent as if each individual publication, patent, patent application or other reference was specifically and individually indicated to be incorporated by reference in its entirety for all purposes. Citation of a reference herein shall not be construed as an admission that such is prior art to the present invention. Bailey, D.L., and F.M. O'Connor. 1958. US 2,834,748. Siloxane-oxyalkylene block copolymers. Ferrigno, T.H. 1963. Rigid plastic foams. Reinhold Pub. Corp., New York,, x, 276 p. pp. Kaiinowski, T.T., D.G. Keske, V. Matimba, el al. 2004. US 6,753,357. Rigid foam compositions and method employing methyl formate as a blowing agent. Keske, D.G., and M.S. Schulte. 1991. US 5,032,623. Rigid foams using CHCLF2 as a blowing agent. Keske, D.G., and M.S. Schulte. 1993a. US 5,274,007. Rigid foams using CHCLF2 as a blowing agent. Keske, D.G., and M.S. Schulte. 1993b. US 5,194,175. Rigid foams, methods of preparation thereof and compositions useful in methods and preparations thereof. CLAIMS What is claimed is: 1. A method of preparing a component for making a polyurethane foam, comprising combining at least one blowing agent with at least one catalyst and at least one acid, wherein the at least one blowing agent is other than water, wherein the catalyst is added independently of the acid; and wherein the activity of the catalyst does not substantially deteriorate over time. 2. The method of claim 1, wherein the catalyst comprises an amine catalyst. 3. The method of claim 1, wherein the acid comprises an organic acid. 4. The method of claim 1, wherein the blowing agent comprises an alkyl alkanoate. 5. The method of claim 4, wherein the alkyl alkanoate comprises methyl formate. 6. The method of claim 3, wherein the organic acid compVises formic acid. 7. The method of claim 1, wherein the blowing agent is an alkyl alkanoate. 8. The method of claim 7, wherein the alkyl alkanoate is methyl formate. 9. The method of claim 8, wherein the acid is formic acid. 10. The method of claim 1, wherein the acid is present, by weight, from 1% to 500% of the molar equivalent of the catalyst. 11. The method of claim 10, wherein the acid is present from 10% to 400% of the molar equivalent of the amine catalyst. 12. The method of claim 11, wherein the acid is present from 50% to 300% of the molar equivalent of the amine catalyst. 13. A method of preparing a component for making a polyurethane foam, comprising combining methyl formate with formic acid and at least one amine catalyst. 14. The method of claim 13, wherein the acid is present in an amount sufficient to prevent the activity of the catalyst to not substantially deteriorate over time. 15. The method of claim 13, wherein the acid is present, by weight, from 1% to 500% of the molar equivalent of the amine catalyst. 16. The method of claim 15, wherein the acid is present from 10% to 400% of the molar equivalent of the amine catalyst. 17. The method of claim 16, wherein the acid is present from 50% to 300% of the molar equivalent of the amine catalyst. 18. A method of retaining activity of a catalyst in a component composition for forming polyurethane foams, comprising combining at least one catalyst with at least one blowing agent and at least one acid, wherein the at least one blowing agent is other than water. 19. The method of claim 18, wherein the catalyst comprises an amine catalyst. 20. The method of claim 18, wherein the acid comprises an organic acid. 21. The method of claim 18, wherein the blowing agent comprises an alkyl alkanoate. 22. The method of claim 21, wherein the alkyl alkanoate comprises methyl formate. 23. The method of claim 22, wherein the acid comprises formic acid. 24. The method of claim 18, wherein the blowing agent is an alkyl alkanoate. 25. The method of claim 24, wherein the alkyl alkanoate is methyl formate. 26. The method of claim 25, wherein the acid is formic acid. 27. The method of claim 18, wherein the acid is present, by weight, from 1% to 500% of the molar equivalent of the catalyst. 28. The method of claim 27, wherein the acid is present from 10% to 400% of the molar equivalent of the catalyst. 29. The method of claim 28, wherein the acid is present from 50% to 300% of the molar equivalent of the catalyst. 30. A method of retaining activity of a catalyst in a component composition for forming polyurethane foams comprising combining an amine catalyst with methyl formate and formic acid, wherein the at least one blowing agent is other than water, and wherein the activity of the catalyst does not substantially deteriorate over time. 31. The method of claim 30, wherein the acid is present, by weight, from 1% to 500% of the molar equivalent of the amine catalyst. 32. The method of claim 31, wherein the acid is present from 10% to 400% of the molar equivalent of the amine catalyst. 33. The method of claim 32, wherein the acid is present from 50% to 300% of the molar equivalent of the amine catalyst. 34. A component for making polyurethane foams, comprising: at least one catalyst; at least one blowing agent; and at least one acid, wherein the at least one blowing agent is other than water; and wherein the activity of the catalyst does not substantially deteriorate over time. 35. A component for making polyurethane foams, comprising: at least one amine catalyst; at least one alkyl alkanoate; and at least one organic acid, wherein the activity of the amine catalyst does not substantially deteriorate over time. • 36. The component of claim 35, wherein the alkyl alkanoate is methyl formate. 37. The component of claim 36, wherein the organic acid is formic acid. 38. The component of claim 34 or 35, wherein the acid is present, by weight, from 1% to 500% of the molar equivalent of the amine catalyst. 39. The component of claim 38, wherein the acid is present from 10% to 400% of the molar equivalent of the amine catalyst. 40. The component of claim 39, wherein the acid is present from 50% to 300% of the molar equivalent of the amine catalyst. 41. A polyurethane foam, made according to the process of: preparing a first component made according to the process of claim 1; and mixing the first component with a second component, the second component comprising at least one polyol, wherein a polyurethane foam is formed. 42. The foam of claim 41, wherein the catalyst comprises an amine catalyst. 43. The foam of claim 41, wherein the acid comprises an organic acid. 44. The foam of claim 41, wherein the blowing agent comprises an alkyl alkanoate. 45. The foam of claim 44, wherein the alkyl alkanoate comprises methyl formate. 46. The foam of claim 45, wherein the organic acid comprises formic acid. 47. The foam of claim 41, wherein the blowing agent is an alkyl alkanoate. 48. The foam of claim 47, wherein the alkyl alkanoate is methyl formate. 49. The foam of claim 48, wherein the organic acid is formic acid. 50. The component of claim 41, wherein the organic acid is present, by weight, from 1% to 500% of the molar equivalent of the amine catalyst. 51. The component of claim 50, wherein the acid is present from 10% to 400% of the molar equivalent of the amine catalyst. 52. The component of claim 51, wherein the acid is present from 50% to 300% of the molar equivalent of the amine catalyst. 53. A polyurethane foam, made according to the process of preparing a first component made according to the process of claim 13, 18 or 30; and mixing the first component with a second component, the second component comprising at least one polyol, wherein a polyurethane foam is formed. 54. A component for making polyurethane foams, comprising: at least one amine catalyst; at least one blowing agent; and at least one organic acid, wherein the at least one blowing agent comprises an alkyl alkanoate; wherein the catalyst is added independently of the acid; and wherein the activity of the catalyst does not substantially deteriorate over time. 55. The component of claim 54, wherein the organic acid is present, by weight, from 1% to 500% of the molar equivalent of the amine catalyst. 56. The component of claim 55, wherein the acid is present from 10% to 400% of the molar equivalent of the amine catalyst. 57. The component of claim 56, wherein the acid is present from 50% to 300% of the molar equivalent of the amine catalyst.

Full Text

. REACTIVITY DRIFT AND CATALYST DEGRADATION IN POLYIJRETHANE FOAM
CROSS-REFERENCE TO RELATED APPLICATIONS [01] Not Applicable.
STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH OR DEVELOPMENT
[02] Not Applicable.
INCORPORATION-BY-REFERENCE OF MATERIAL SUBMITTED ON A COMPACT DISC
[03] Not Applicable.
[04] BACKGROUND OF THE INVENTION [05] Field of the Invention
[06] The present invention relates to consistently manufacturing polyurethane foams prepared with agents that hydrolyze, creating acids that attack catalysts. For example, foams prepared with alkyl alkanoates.
[07] I. Introduction
[08] Polyurethane foams insulate, float, cushion, glue, clothe and absorb sound, among a plethora of other applications. Polyurethanes, defined as polymeric substances having multiple urethane linkages, are a large family of polymers with widely ranging properties and uses. The types and properties of polyurethanes are so varied that the Alliance for the Polyurethanes Industry (Arlington, VA) has dubbed them the "erector set" of the plastics industry. Types of polyurethanes include rigid and flexible foams; thermoplastic polyurethane; and other miscellaneous types, such as coatings, adhesives, sealants and elastomers. Flexible foams (e.g., that found in most car seat cushions) are generally open-celled materials, while rigid foams (e.g., building insulation) usually have a high proportion of closed cells.

[09] While rigid polyurethane foams are found in insulation in refrigeration systems, structural applications and flotation applications, transportation vehicles and metal doors, flexible polyurethane foams are used in automotive seats, headrests and armrests; in carpet padding, packaging, clothing, leather products, shoe uppers, tents, life rafts, labels, handbags and furniture cushions. Semi-flexible molded foams are found in automotive instrument panels, energy managing foam and sound absorbing foam.
[010] A. Forming polyurethane foams: the gel and blow reactions
[Oil] Polyurethane foams are produced by reacting a di- or polyisocyanate (compound containing an isocyanate group (N=C=O attached to an organic radical)) with compounds containing two or more active hydrogens, generally in the presence of catalysts, silicone-based surfactants and other auxiliary agents. The active hydrogen-containing compounds are typically polyols (organic compounds having more than one hydroxyl (-OH) groups per molecule), primary and secondary polyamines and water. Two major reactions are promoted by the catalysts: the gel reaction and the blow reaction. Balance is needed between reaction of the isocyanate and the polyol (gel reaction) and the reaction of the isocyanate with water (blow reaction) in order to produce a. polyurethane foam in which the cells are relatively uniform and the foam has specific properties depending on the anticipated application; for example, rigid foams, semi-rigid foams, and flexible foams. Foams can be formed by a one-shot method or by formation of a pre-polymer and subsequent reaction of the pre-polymer with water in the presence of a catalyst.
[012] The gel reaction consists of the isocyanate reacting with the polyol or polyamine and leads to the formation of a polymer of high molecular weight. This reaction predominates in foams blown exclusively with low boiling point organic compounds. The blow reaction occurs between isocyanate and water. This reaction promotes polymer growth and blows carbon dioxide bubbles into the developing polyurethane mass. The blow reaction helps avoid, or reduces the use of, auxiliary blowing agents. The in situ generation of carbon dioxide by the blow reaction plays an essential role in the preparation of one-shot, water-blown polyurethane foams.
[013] Examples of unbalanced gel and blow reactions include those foams in which carbon dioxide evolves too quickly, forming foams that tend to collapse. A gel reaction that proceeds too rapidly reduces foam-rise, resulting in a high density foam. In practice, the balancing of these two reactions is controlled by the nature of the promoters and

catalysts, generally amine and/or organo-metallic (an organic molecule containing a metal atom). Frequently, a gelling catalyst and a blowing catalyst are used together to balance gelling and blowing.
[014] B. Blowing agents and catalysts
[015] Blowing agents traditionally include chlorofluorocarbons (CFCs). However, CFCs detrimentally affect the earth's ozone layer. To avoid the dangers of CFCs, some processes use hydrochloroflurocarbons (HCFCs) instead. For example, some processes use monochlorodifluoromethane (CHC1F2) (Keske and Schulte, 1991; Keske and Schulte, 1993a; Keske and Schulte, 1993b). However, even HCFCs also carry important environmental risks, even though they are less harmful than CFCs.
[016] Until recently, using alkyl alkanoates, including methyl formate, as an alternative sole blowing agent were unsatisfactory. Such foams shrink more than 10% after manufacture. Methyl formate as a blowing agent can produce stable foams if used with other blowing agents-such as the undesirable CFCs or HCPCs-produce dimensionally stable foams. However, using alkyl alkanoates alone-without any harmful CFCs or HCFCs--has recently been accomplished (Kalinowski et at., 2004).
[017] Catalysts generally fall into two categories: tertiary amines (mono- and poly-) and organo-metallic compounds. Organo-metallic catalysts favor the gel reaction, while amine catalysts favor the blow or gel reactions depending on the catalyst. Using metal catalysts in flexible foam formulations also increases the number of closed cells, creating tighter foams. Tertiary amines also are effective as catalysts for the chain extension reaction and can be used in combination with organo-metallic catalysts. For example, in the preparation of flexible slabstock foams, the one-shot process uses triethylenediamine to promote the blow reaction and the cross-linking reaction, while an organo-metallic compound synergistically promotes the chain extension reaction.
[018] C. The foam-blowing process
[019] The process for making foams typically involves the mixing of the starting materials with polyurethane foam production machinery and pouring the reacting mixture, as it exits the mix-head, into a mold. To prepare foams, a first component (component A or "A-side"), supplying isocyanate, is mixed with a second component (component B or "B-side"), supplying the polyol and usually a catalyst. Component A can also provide a

surfactant and a blowing agent. Component B can also supply a surfactant and a blowing agent. The optional constituents of the sides, as well as the catalyst, can be alternatively introduced by a third stream.
[020] D. Obstacles to manufacturing consistent polyurethane foams
[021] Until recently, blowing agents were CFCs, HCFCs and hydrofluorocarbons (HFCs); however, these have many undesirable characteristics, especially as related to environmental concerns. AlkyI alkanoates can be used as effective substitutes, or with other blowing agents (Kalinowski et al., 2004). However, when using an alkyl alkanoate as a blowing agent, alone or with CFCs, HCFCs, HFCs, hydrocarbons or hydrofluoroethers (HFEs) in the presence of water, the blowing agent can hydrolyze. Other foam ingredients can hydrolyze in the presence of water as well, notably polyester polyols. This hydrolysis results in the formation of acids that attack the amine catalyst, causing the catalyst's reactivity to deteriorate. The consequence is that the reactivity of the foam slows. This fluctuation interferes with consistent, efficient and reproducible foam production and can have a deleterious effect on the properties or suitability of the resultant foam.
[022] Traditionally, delayed action catalysts, which are acid-blocked amines, such as simple amine salts of a tertiary amine and a carboxylic acid (such as formic, acetic or 2-ethylhexanoic acid) were used to counter this problem, but these are expensive and the choices of such catalysts is limited. The foam industry is plagued by imperfections in the manufacturing process, most notably by hydrolysis of certain ingredients which target a single acid-vulnerable molecule: the amine catalyst.
[023] BRIEF DESCRIPTION OF THE DRAWINGS
[024] Figure la shows the protective effect the methods of the invention have on retaining catalyst activity in the formation of polyurethane foams. The reactivity of the gel after formulation is plotted.
[025] Figure 1 b shows the reactivity change observed in the experiments of Figure 1 a, expressed as percent change in reactivity.

[026] SUMMARY OF THE INVENTION
[027] Accordingly, it is an object of the invention to overcome these and other problems associated with hydrolyzable ingredients.
[028] In a first aspect, the invention provides methods of preparing components used to make polyurethane foams, where at least one blowing agent is combined with at least one catalyst and at least one acid, wherein the at least one blowing agent is other than water, such that the activity of the catalyst does not substantially deteriorate over time. The blowing agent can be an alkyl alkanoate, such as methyl formate; the catalyst can be an amine catalyst, and the acid can be an organic acid, such as formic acid.
[029] In a second aspect, the invention provides methods of stabilizing/retaining activity of catalysts used in polyurethane foam production, where at least one blowing agent is combined with at least one catalyst and at least one acid, wherein the at least one blowing agent is other than water, such that the activity of the catalyst does not substantially deteriorate over time. The blowing agent can be an alkyl alkanoate, such as methyl formate; the catalyst can be an amine catalyst, and the acid can be an organic acid, such as formic acid.
[030] In yet a third aspect, the invention provides compositions suitable for preparing polyurethane foams, such that the activity of a catalyst in the composition remains stable over time. In such compositions, at least one blowing agent is combined with at least one catalyst and at least one acid, wherein the at least one blowing agent is other than water, such that the activity of the catalyst does not substantially deteriorate over time. The blowing agent can be an alkyl alkanoate, such as methyl formate; the catalyst can be an amine catalyst, and the acid can be an organic acid, such as formic acid.
[031] In a fourth aspect, the invention provides polyurethane foams manufactured from compositions wherein the activity of a catalyst remains stable over time. In such foams, at least one blowing agent is combined with at least one catalyst and at least one acid, wherein the at least one blowing agent is other than water, such that the activity of the catalyst does not substantially deteriorate over time, and then mixed with a polyol-containing composition. The blowing agent can be an alkyl-alkanoate, such as methyl formate; the catalyst can be an amine catalyst, and the acid can be an organic acid, such as formic acid.

[032] In all aspects of the invention, the acid can be present, by weight, from 1% to 500% of the molar equivalent of the amine catalyst.
[033] These and other features, aspects and advantages will become better understood with reference to the following description, examples and appended claims.
[034] DETAILED DESCRIPTION OF THE INVENTION
[035] The problems of the imperfect amine catalyst that produces foams that are too tight (as when most blocked catalysts are used) or falls prey to acid attack such that catalyst activity deteriorates, is solved by the present invention using a simple and inexpensive method. The addition of an acid to the polyol blend (component B), surprisingly and unexpectedly, eliminates the degradation of amine catalysts. The acid is added at a concentration (by weight) of about 1% to about 500% of the molar equivalent of the amine catalyst(s); preferably from about 10% to about 400% of the molar equivalent of the amine catalyst(s); more preferably from about 50% to about 300% of the molar equivalent of the amine cataiyst(s). In a most preferred embodiment, formic acid is added to component 8, wherein the blowing agent in the system is methyl formate.
[036] //. Practicing the invention
[037] A. Component A
[038] 1. Isocyanates
[039] When manufacturing a foam from components A and B, component A contains an isocyanate, or mixtures and combinations of discrete isocyanates, and preferably also a surfactant. The isocyanate can be any of the isocyanates, organic or inorganic, conventionally used in the production of polyurethane foams. Such polyisocyanates are commonly used in the preparation of polyurethanes by reaction with compounds containing two or more active hydrogen-containing groups. Any of the polyfunctional isocyanates, such as isophorone diisocyanate, polymeric methylenebis (phenyl isocyanate), 2,6-tolulene diisocyanate, 4,4'-methylenebis(phenyl isocyanate), dianisidine diisocyanate, tolidine diisocyanate, hexamethylene diisocyanate, m-xylene diisocyanate,

1,5-napthalene diisocyanate, p-phenylene diisocyanate 1,5-napthalene diisocyanate, p-phenylene diisocyanate, 1,4-di-ethylbenzene diisocyanate, polymethylenepolyphenylisocyane, 3,3-diphenyldimethylmethane-4,4-diisocyanate, xylylene diisocyanates, xylyl diisocynates, 2,4-toluenediisocyante dimer, m-phenylenediisocyante, toluene diisocynates, diphenylmethane-2,4-diisocyanate, etc.. Mixtures of two or more isocyanates can be used, such as mixtures of the 2,4- and 2,6-isomers of tolulene diisocyanate or 2,4'- and 4,4'-isomers of methylenebis(phenyl isocy-anate). Modified forms of 4,4'-methylenebis (phenyl isocyanate) or mixtures of the 2,4'-isomer and 4,4'-isomer thereof can also be used.
[040] 2. Blowing agents
[041] In addition, component A can contain a blowing agent, although including such an agent in component A is unnecessary. In one embodiment, the blowing agent is an alkyl alkanoate, with methyl formate being preferred. Derivatives and precursors of a selected alkyl alkanoate can also be used, either alone or with methyl formate.
[042] A "derivative and/or precursor" of alkyl alkanoate is any composition in which the alkyl alkanoate is attached to an inert carrier with respect to the remaining ingredients of components A and B. The derivative and/or precursor of the alkyl alkanoate maintain the functionality of the alkyl alkanoate. If an alkyl alkanoate derivative and/or precursor are used, it is a complex that maintains the entire structure as a moiety of the complex. A "precursor" is a composition that produces an alkyl alkanoate at some point prior to, or during, the foaming process.
[043] Other blowing agents can be present in addition to alkyl alkanoates. For example, CFCs, HCFCs, MFCs, methylene chloride, hydrofluorocarbons, hydrocarbons or other organic compounds can also be used. Water itself is a blowing agent and is almost always present in at least residual quantities. The addition of an acid (or blend) to the polyol blend (component B), surprisingly and unexpectedly, reduces or eliminates the further degradation of amine catalysts. The acid (or blend) is added at from about 1% to about 500% of the molar equivalent of the amine catalyst(s); preferably from about 10% to about 400% of the molar equivalent of the amine catalyst(s); more preferably from about 50% to about 300% of the molar equivalent of the amine catalyst(s). The materials of component A can be blended in any standard manner. The order of blending is not particularly significant. Nevertheless, a convenient order of mixing is to add surfactant to

isocyanate, and then to add the acid inhibitor, if any, and finally to add the blowing agent(s), if any.
[044] The relative proportions of ingredients should be such that if component A contains one or more blowing agents, the concentration of blowing agent(s) in component A is from about 0.5% by weight to about 12% by weight, preferably about 2% by weight to about 10% by weight. The alkyl alkanoate (and/or derivative and/or precursor thereof) itself can make up as much as about 12% by weight, preferably as much as about 10% by weight, such as from about 2% by weight to about 10% by weight, of component A. The surfactant can make up less than about 2% by weight, preferably about 0.75% by weight, of component A. If an acid inhibitor is desired, it can be included in a concentration of up to about 0.5% by weight, based on the weight of component A. Typically, the balance of component A is the isocyanate.
[045] 3. Surfactants and miscellaneous agents
[046] Any conventional, A-side surfactant can be incorporated into component A. Examples of such surfactants include silicones, such as B-8407, DC-5160, DC-198, DC-5125, DC-1315 and B-8021 (Degussa/Goldschmidt Chemical Corp.; Mapleton, IL); L-620 (Union Carbide; Houston, TX); L-6202 and Y-10390 (Air Products; Allentown, PA), other silicones and siloxaneoxyalkylene block copolymers (Bailey and O'Connor, 1958; Ferrigno, 1963). The surfactant choice, while not essential to the present invention, affects the cell structure in the produced foam.
[047] Other compositions, such as fire retardants, for example, those containing bromine, chlorine or phosphorus, can also be included in the component A. Because the fire retardant industry continues to be in constant flux, the available chemicals and chemical families are also in flux. However, any fire retardant that is appropriate for use in traditionally blown foams are appropriate for use in the foams of the invention.
[048] B. Component B
[049] 1. Polyol
[050] Component B contains at least one polyol. Component B typically consists of 50% polyol(s) (by weight) to about 98% (by weight), preferably 70% (by weight) to about 92% (by weight) of at least one polyol.

[051] When using methyl formate in component B, at least one of the polyol(s) in component B is a polyalkoxylated amine, a polyalkoxylated ether or a polyester polyol and has a hydroxyl number of from about 20 to about 1000. Preferably, the hydroxyl number is from about 20 to about 750, most preferably about 300 to about 500 for rigid foams and most preferably 20-100 flexible foams. However, the preferred hydroxyl ranges are determined solely by the desired end product. The skilled artisan can determine the appropriate hydroxyl number. The polyalkoxylated polyols preferably are polyethoxylated, polypropoxylated, or polybutoxylated, or mixtures thereof. The polyalkoxylated amine can be, for example, a polyalkoxylated aliphatic amine or a Mannich polyol; the polyalkoxylated ether can be, for example, a polyalkoxylated sucrose or glycerin; and the polyester polyol can be a transesterification of a terephthalate or castor oil. The polyols can be made individually or as coinitiators.
[052] One or more of any one of the three classes of polyols, or any combination of polyols from any two or all three of the classes, can be used in component B. Component B can contain other polyols as well; preferably, the total of all polyols present from the three classes (that is, the total of all polyols from any of the polyalkoxylated amines, polyalkoxylated ethers and polyester polyols) make up more than about 50% by weight of all the polyols of component B, and at least about 50% by weight of component B.
[053] Other useful polyhydric compounds, whether or not an alkyl alkanoate is used as a blowing agent and in addition to those listed above, include ethylene glycol, propylene glycol, diethylene glycol, dipropylene glycol, glycerol, pentaerythritol, sorbitol, sucrose, methyl glucoside, glucose, etc.. Polyamine compounds that can be reacted with alkylene oxide to prepare amine-based polyols include mono-, di-, and trietha-nol amine, ethylene diamine, diethylene diamine, toluene diamine, etc.. These polyhydric alcohols and polyamine compounds can be reacted separately with alkylene oxides, or they can be pre-mixed in the preparation of polyether polyol mixtures or blends. Preferred polyester polyols are those based on terephthalic, phthalic, isophthalic, adipic, succinic, glutaric, fumaric acid(s), and combinations thereof.
[054] 2. Acids
[055] In those compositions in which a blowing agent can hydrolyze or otherwise deteriorate, such that a catalyst in the mixture is attacked with consequent reduction in catalytic activity, an acid is added to the mix to protect the susceptible catalyst. Any

organic acid or inorganic acid that protects the amine catalyst from acids generated by the hydrolysis of a blowing agent or other ingredients of component B can be used. Protection consists of maintaining a constancy of the reaction rate that permits the continued manufacture of the final product without a detrimental change in the performance. Any acid that functions to protect the amine catalyst from acid attack is suitable for use. In general, appropriate acids have a pKa greater than 0; more preferably 0-10; and more preferably 0-5. Preferably the acid is organic. Table I lists some examples of suitable acids.
(Table Remove) [059] Such a formulation of component B as presented in Table 3 results in a solution where the catalysts retain consistent activity over the life of the solution. This and other component B solutions formulated with an acid of the blowing agent retain consistent catalyst activity over time. For example, acceptable reactivity drifts are determined by the end-product and the specific application of the product. Preferably, the reactivity drift stays within acceptable ranges in excess of 1 week, more preferably, in excess of 6 months, most preferably, in excess of 2 years. Those of ordinary skill in the art of producing polyurethane foams can easily adjust the types and quantities of each polyol and the ratio of alkyl alkanoate to water in the formula such that the desired properties of the finished foam are achieved.
[060] Water in component B can be from 0% to about 5%, preferably about 0.5% to about 4%, more preferably about 1 % to about 3% (by weight). Water can serve as a blowing agent as well as add rigidity to the resulting foam.
[061] The alkyl alkanoate in component B is preferably methyl formate and/or any derivative and/or precursor thereof. The alkyl alkanoate constitutes as much as about 15%, preferably about 2% to about 15% (by weight) of component B. The acid is present in a sufficient amount to retain the activity of any amine catalysts.
[062] The alkyl alkanoate, as well as the acid, can be introduced by a separate stream in addition or in place of that which can be in either or both of components A and B. The concentrations of alkyl alkanoate in components A and B and the amount introduced to the reaction mixture by way of a separate stream are adjusted and coordinated so that the
resulting concentration of total alkyt alkanoate (or derivative and/or precursor thereof) brought together upon mixing components A and B and separate streams, if any, based on the total weight of the resulting mixture, is from about 1% to about 12%, preferably from about 4% to about 8%. Other blowing agents can be used or at least be present. These include, for example, CFCs, MFCs, HCFCs, HFEs, hydrocarbons, other alkyl alkanoates, as well as any others known to the skilled artisan.
[063] More preferably, the total amount of blowing agent present in each component and in the total combination of all ingredients mixed together to form a foaming mixture should be substantially free (less than 1% by weight) of CFCs, HCFCs, MFCs, HFEs and hydrocarbons; more preferably, no CFCs, HCFCs, HFCs, HFEs and hydrocarbons are present. The mixture to blow the foam is preferably also substantially free, more preferably, devoid, of any other substituted or unsubstituted hydrocarbon. Ideally, the foaming mixture is substantially free, more optimally devoid, of any other organic compound that acts as a blowing agent.
[064] The polyols in the combination need not form a separate composition; it is unnecessary to mix the constituents of the mixture together to form a premix and then to form component B by mixing the premix with the remaining ingredients of component B. The ingredients of component B can be mixed in any order, and the polyols can be added separately from each other as separate ingredients to form component B.
[065] 5. Catalysts
[066] In addition to the amine catalysts listed in Table 2, any organometallic compound known to be a catalyst in the reaction between an isocyanate group and an active hydrogen-containing group can be used as a catalyst. Such catalysts include, but not limited to, the organic acid salts of, and the organometallic derivatives of, bismuth, lead, tin, iron, antimony, uranium, cadmium, cobalt, thorium, aluminum, mercury, zinc, nickel, cerium, molybdenum, vanadium, copper, manganese, and zirconium.
[067] 6. Other agents
[068] Component B can also contain other ingredients as desired. Optional additives such as dispersing agents, cell stabilizers, surfactants, flame retardants, and the like, that are commonly used in the fabrication of polymer foams can be used in the
process of the invention. For example, phosphorus-based flame retardant additives can be used if flame retardancy is desired. A finer cell structure can be obtained if organo-silicone polymers are used as surfactants in the reaction mix.
[069] Other optional additives, such as inorganic and organic fillers, can also be used. Examples of inorganic fillers include calcium carbonate, barium sulfate, silica, glass, antimony oxides, etc.; examples of organic fillers include the various polymers and copolymers of vinyl chloride, vinyl acetate, acrylonitrile, styrene, melamine, partially oxyalkylated melamine, etc. Organic esters can also be used. Particularly preferred esters are those derived from dicarboxylic acids, such as oxalic, malonic, succinic, glutaric, maleic, phthalic, isophthalic and terephthalic acids.
[070] For example, a fire retardant, such as those containing bromine, chlorine or phosphorus, can be incorporated into the mixture to impart fire resistance. Other commonly used additives are hydroxyl-containing compositions, such as castor oil, aromatic polyesters, glycols and/or alkoxylated sorbitols, acid scavengers (for example, a-methyl styrene), acid formation inhibitors or diluents.
[071] C. Forming the foam
[072] Component A and component B can be mixed, such as through a static mix, high pressure mix or impingement mix chamber or any other device commonly known in the industry, by standard procedures to produce a homogenous blend. In a preferred embodiment, a one-shot method of foam fabrication is used, whereby the isocyanate containing stream (component A) and the polyol-containing and catalyst-containing stream (component B) are mixed. Each of these streams is preferably liquid in which all of the various additives are preferably soluble, although dispersions utilizing solid components can be used as desired.
[073] Preferably component A and component B are mixed such that there is about 0.3 to about 1.2 polyol equivalents per equivalent polyisocyanate. "Polyol equivalent" means the weight component B used in the foam divided by the equivalent weight of component B. "Polyisocyanate equivalent" means the weight component A used in the foam divided by the equivalent weight of component A.
[074] Examples
[075] Without further elaboration, it is believed that one skilled in the art can, using the preceding description, us the present invention to its fullest extent. The following examples are offered by way of illustration and not by way of limiting the remaining disclosure.
[076] Example 1
[077] Reactivity can be measured and then compared to the profile of the chemical product information sheet for each chemical system. The reactivities can be determined using the String-Gel time and Tack-Free time.
[078] STRING-GEL
[079] String-Gel is the measure of time from the beginning of the shot until the foam adheres to a thin wire (approx. 1/16" in diameter) and becomes "stringy'-something like bubble gum.
[080] String-Gel measurements are made as follows:
[081] 1. Take a 10-second shot into a 30-gallon plastic bag and simultaneously start the stopwatch.
[082] 2. At about 60-seconds, poke a wire into the rising chemical at least 12 inches deep and take it out again. Repeat poking wire in and out of the rising chemical at 5-second intervals until the foam sticks to the wire and forms a bubble gum-like string. Do not poke the same place twice.
[083] 3. Record time the String-Gel took place.
[084] Tongue depressors or Popsicle sticks should not be used for String-Gel because they do not go deep enough into the rising foam. A wire similar to a coat hanger is suitable.
[085] TACK-FREE
[086] Tack-Free is the measure of time from the beginning of the shot until the foam becomes "tack-free" or does not stick to fingertip when touched tightly.
[087] A Tack-Free measurement may be made as follows: [088] 1. Follow Step 1-3 for String-Gel.
[089] 2. Measure from the start of the shot until foam becomes "tack-free" or no longer sticks to the fingertip when touched lightly.
[090] 3. Record the time.
[091] String-Gel and Tack-Free times can be recorded from the same shot if the String-Get is observed first and Tack-Free is further observed. It is important to keep the plastic bag off cold floors because it will affect the reactivity times.
[092] Reactivity of an amine catalyst using methyl formate as a blowing agent, with and without formic acid added, was determined. Foams were blown 0, 1,2, 3 and 4 weeks after formulating component B with and without acid. The times of gel reactivity were assayed as described above, and the data plotted. The data are expressed as time of gel reactivity (Table 3 and Figure la) and % change of reactivity compared to the baseline of 0 weeks (Table 4 and Figure 1 b).
(Table Remove) [093] As shown in Figure la and Table 3, when the acid is not present, the gel reactivity declines over time, so that at 4 weeks after formulating component B, gel reactivity requires 20 more seconds than at baseline (Fig. la, diamonds). However, when formic acid is present, reactivity does not decline, remaining at 78-80 seconds (Fig. la, squares). Figure lb and Table 4 report these results as percentage of change from baseline, reinforcing the dramatic effect acid has upon protecting the amine catalyst from reactivity drift arid degradation. The percent of reactivity change reaches 45% at 4 weeks when acid
is not present (Fig. Ib, diamonds), while that for the component containing acid marginally fluctuates, with a range of-2.5% to 0% (Fig Ib, squares).
(Table Remove) [094] Other Embodiments
[095] The detailed description set forth above is provided to aid those skilled in the art in practicing the present invention. However, the invention described and claimed herein is not to be limited in scope by the specific embodiments herein disclosed because these embodiments are intended as illustration of several aspects of the invention. Any equivalent embodiments are intended to be within the scope of this invention. Indeed, various modifications of the invention in addition to those shown and described herein will become apparent to those skilled in the art from the foregoing description which do not depart from the spirit or scope of the present inventive discovery. Such modifications are also intended to fall within the scope of the appended claims.
[096] References
[097] All publications, patents, patent applications and other references cited in this application are incorporated herein by reference in their entirety for all purposes to the same extent as if each individual publication, patent, patent application or other reference was specifically and individually indicated to be incorporated by reference in its entirety for all purposes. Citation of a reference herein shall not be construed as an admission that such is prior art to the present invention.
Bailey, D.L., and F.M. O'Connor. 1958. US 2,834,748. Siloxane-oxyalkylene block copolymers.
Ferrigno, T.H. 1963. Rigid plastic foams. Reinhold Pub. Corp., New York,, x, 276 p. pp.
Kaiinowski, T.T., D.G. Keske, V. Matimba, el al. 2004. US 6,753,357. Rigid foam compositions and method employing methyl formate as a blowing agent.
Keske, D.G., and M.S. Schulte. 1991. US 5,032,623. Rigid foams using CHCLF2 as a blowing agent.
Keske, D.G., and M.S. Schulte. 1993a. US 5,274,007. Rigid foams using CHCLF2 as a blowing agent.
Keske, D.G., and M.S. Schulte. 1993b. US 5,194,175. Rigid foams, methods of
preparation thereof and compositions useful in methods and preparations thereof.

CLAIMS
What is claimed is:
1. A method of preparing a component for making a polyurethane foam,
comprising combining at least one blowing agent with at least one catalyst and at least one
acid, wherein the at least one blowing agent is other than water,
wherein the catalyst is added independently of the acid; and
wherein the activity of the catalyst does not substantially deteriorate over time.
2. The method of claim 1, wherein the catalyst comprises an amine catalyst.
3. The method of claim 1, wherein the acid comprises an organic acid.
4. The method of claim 1, wherein the blowing agent comprises an alkyl
alkanoate.
5. The method of claim 4, wherein the alkyl alkanoate comprises methyl formate.
6. The method of claim 3, wherein the organic acid compVises formic acid.
7. The method of claim 1, wherein the blowing agent is an alkyl alkanoate.
8. The method of claim 7, wherein the alkyl alkanoate is methyl formate.
9. The method of claim 8, wherein the acid is formic acid.

10. The method of claim 1, wherein the acid is present, by weight, from 1% to
500% of the molar equivalent of the catalyst.
11. The method of claim 10, wherein the acid is present from 10% to 400% of the
molar equivalent of the amine catalyst.

12. The method of claim 11, wherein the acid is present from 50% to 300% of the
molar equivalent of the amine catalyst.
13. A method of preparing a component for making a polyurethane foam,
comprising combining methyl formate with formic acid and at least one amine catalyst.
14. The method of claim 13, wherein the acid is present in an amount sufficient to
prevent the activity of the catalyst to not substantially deteriorate over time.
15. The method of claim 13, wherein the acid is present, by weight, from 1% to
500% of the molar equivalent of the amine catalyst.
16. The method of claim 15, wherein the acid is present from 10% to 400% of the
molar equivalent of the amine catalyst.
17. The method of claim 16, wherein the acid is present from 50% to 300% of the
molar equivalent of the amine catalyst.
18. A method of retaining activity of a catalyst in a component composition for
forming polyurethane foams, comprising combining at least one catalyst with at least one
blowing agent and at least one acid,
wherein the at least one blowing agent is other than water.
19. The method of claim 18, wherein the catalyst comprises an amine catalyst.
20. The method of claim 18, wherein the acid comprises an organic acid.
21. The method of claim 18, wherein the blowing agent comprises an alkyl
alkanoate.
22. The method of claim 21, wherein the alkyl alkanoate comprises methyl
formate.

23. The method of claim 22, wherein the acid comprises formic acid.
24. The method of claim 18, wherein the blowing agent is an alkyl alkanoate.
25. The method of claim 24, wherein the alkyl alkanoate is methyl formate.
26. The method of claim 25, wherein the acid is formic acid.
27. The method of claim 18, wherein the acid is present, by weight, from 1% to
500% of the molar equivalent of the catalyst.
28. The method of claim 27, wherein the acid is present from 10% to 400% of the
molar equivalent of the catalyst.
29. The method of claim 28, wherein the acid is present from 50% to 300% of the
molar equivalent of the catalyst.
30. A method of retaining activity of a catalyst in a component composition for
forming polyurethane foams comprising combining an amine catalyst with methyl formate
and formic acid, wherein the at least one blowing agent is other than water, and
wherein the activity of the catalyst does not substantially deteriorate over time.
31. The method of claim 30, wherein the acid is present, by weight, from 1% to
500% of the molar equivalent of the amine catalyst.
32. The method of claim 31, wherein the acid is present from 10% to 400% of the
molar equivalent of the amine catalyst.
33. The method of claim 32, wherein the acid is present from 50% to 300% of the
molar equivalent of the amine catalyst.
34. A component for making polyurethane foams, comprising:
at least one catalyst;

at least one blowing agent; and
at least one acid,
wherein the at least one blowing agent is other than water; and wherein the activity of the catalyst does not substantially deteriorate over time.
35. A component for making polyurethane foams, comprising:
at least one amine catalyst;
at least one alkyl alkanoate; and
at least one organic acid,
wherein the activity of the amine catalyst does not substantially deteriorate over time.
• 36. The component of claim 35, wherein the alkyl alkanoate is methyl formate.
37. The component of claim 36, wherein the organic acid is formic acid.
38. The component of claim 34 or 35, wherein the acid is present, by weight, from
1% to 500% of the molar equivalent of the amine catalyst.
39. The component of claim 38, wherein the acid is present from 10% to 400% of
the molar equivalent of the amine catalyst.
40. The component of claim 39, wherein the acid is present from 50% to 300% of
the molar equivalent of the amine catalyst.
41. A polyurethane foam, made according to the process of:
preparing a first component made according to the process of claim 1; and mixing the first component with a second component, the second component comprising at least one polyol,
wherein a polyurethane foam is formed.
42. The foam of claim 41, wherein the catalyst comprises an amine catalyst.

43. The foam of claim 41, wherein the acid comprises an organic acid.
44. The foam of claim 41, wherein the blowing agent comprises an alkyl
alkanoate.
45. The foam of claim 44, wherein the alkyl alkanoate comprises methyl formate.
46. The foam of claim 45, wherein the organic acid comprises formic acid.
47. The foam of claim 41, wherein the blowing agent is an alkyl alkanoate.
48. The foam of claim 47, wherein the alkyl alkanoate is methyl formate.
49. The foam of claim 48, wherein the organic acid is formic acid.
50. The component of claim 41, wherein the organic acid is present, by weight,
from 1% to 500% of the molar equivalent of the amine catalyst.
51. The component of claim 50, wherein the acid is present from 10% to 400% of
the molar equivalent of the amine catalyst.
52. The component of claim 51, wherein the acid is present from 50% to 300% of
the molar equivalent of the amine catalyst.
53. A polyurethane foam, made according to the process of
preparing a first component made according to the process of claim 13, 18 or 30; and
mixing the first component with a second component, the second component comprising at least one polyol,
wherein a polyurethane foam is formed.
54. A component for making polyurethane foams, comprising:
at least one amine catalyst;

at least one blowing agent; and
at least one organic acid,
wherein the at least one blowing agent comprises an alkyl alkanoate; wherein the catalyst is added independently of the acid; and wherein the activity of the catalyst does not substantially deteriorate over time.
55. The component of claim 54, wherein the organic acid is present, by weight,
from 1% to 500% of the molar equivalent of the amine catalyst.
56. The component of claim 55, wherein the acid is present from 10% to 400% of
the molar equivalent of the amine catalyst.
57. The component of claim 56, wherein the acid is present from 50% to 300% of
the molar equivalent of the amine catalyst.

Documents:

« Previous Patent

Next Patent »

Patent Number

260129

Indian Patent Application Number

877/DELNP/2007

PG Journal Number

14/2014

Publication Date

04-Apr-2014

Grant Date

31-Mar-2014

Date of Filing

01-Feb-2007

Name of Patentee

FOAM SUPPLIES, INC.

Applicant Address

4387 NORTH RIDER TRAIL, EARTH CITY MO 63045 USA

Inventors:

#	Inventor's Name	Inventor's Address
1	SCHULTE MARK S.,	2340 GARDNER DRIVE, MOLINE ACRES, MISSOURI 63136 USA
2	MODRAY DAVID L.,	1047 BARRY COURT, KIRKWOOD, MISSOURI 63122 USA
3	KESKE DAVID G.,	1449 BALD EAGLE, GLENCOE, MISSOURI 63038 USA
4	KALINOWSKI TIMOTHY T.,	826 KISKER ROAD, ST. CHARLES, MISSOURI 63304 USA

PCT International Classification Number

C08J 9/00

PCT International Application Number

PCT/US2005/027244

PCT International Filing date

2005-07-29

PCT Conventions: