Title of Invention

PROCESS FOR PREPARATION OF A MULTILAYER COATING SHEET

Abstract The invention relates to process for the preparation of a visual properties-matching multilayer coating sheet comprising the steps of a) determining the visual property data of a surface to be matched in visual properties; b) transmitting the data from step a) to a system configured to receive such data, and determination of the composition data of a coating composition having an acceptable match of visual properties; c) preparing a visual properties-matching coating composition according to the determined composition data; d) providing a base sheet layer optionally having an adhesive layer and a backing layer on one surface; e) applying the visual properties-matching c oating composition to one surface of the base sheet layer to form a colour- and/or effect-imparting coating layer; f) optionally, drying the applied colour- and/or effect-imparting coating layer; g) optionally, applying a clear coat layer on top of the colour- and/or effect- imparting coating layer; h) optionally, drying and/or curing the clear coat layer, and i) if the base sheet layer in step d) was provided without an adhesive layer and a backing layer, application of an adhesive layer and a backing layer to the uncoated surface of the base sheet layer.
Full Text PROCESS FOR PREPARATION OF A MULTILAYER COATING SHEET
The invention relates to a process for the preparation of a visual properties-
matching multilayer coating sheet, to a process for partially finishing the surface of
a substrate, and to a visual properties-matching multilayer coating sheet.
Processes of the above-mentioned type are known from US 5254192. This
document describes a process for repairing a damaged portion of paint or coating
on a vehicle to achieve an exact colour match. The damaged paint of a vehicle is
repaired by using an adhesive backed film that has a layer of paint identical with
the paint on the vehicle. The paint has been applied to the film and to the vehicle at
the same time and under the same conditions and has been dried and cured under
the same conditions. So, an identical colour match is achieved between the
painted vehicle and the repair film in the event the paint on the vehicle is scratched
or otherwise damaged. The paint layer can be a monocoat or a colour coat/clear
coat layer.
A drawback of the known processes is that the repair film has to be produced in
the vehicle factory together with the application of the original coating at a point in
time when it is not known whether repair films will be required for the individual
vehicle at all, let alone that the size and the shape of the required repair films are
known. Furthermore, since the paint on the repair film is identical with the paint on
the vehicle body applied in the factory and cured under the same conditions,
limitations with respect to suitable base films apply. The factory applied paint of
automobiles is typically cured at high temperature, for example at 140°C. Many
polymeric materials which would be suitable as base films do not withstand the
curing temperature of the factory applied automobile paint.
The factory applied and cured paint gives rise to a hard coating layer. However, the
flexibility and elasticity of such a paint layer generally is insufficient for repair films,

given that repair films often have to be stretched and bent during application, for
example when the coating on curved substrates, such as exterior mirror cases of
automobiles, is refinished with the repair films. Application of the known repair film
to curved substrates can give rise to mechanical failure, such as cracking, of the
coating layer.
The gloss of a factory applied coating of an automobile typically decreases with
time due to the action of atmospheric and environmental etching. Also, the colour
may undergo subtle changes over time. The known repair films produced together
with the automobile are generally stored in the interior of the automobile or of a
building where they are not exposed to atmospheric and environmental etching.
Therefore, when the known repair film is used for repair of an automobile of which
the gloss and colour values of the coating have changed under the influence of
atmospheric and environmental etching, the repaired area will differ from the
surrounding area in colour and gloss.
The invention seeks to provide a process which alleviates the above-mentioned
drawbacks. More in particular, the object of the invention is to provide a process
which allows the preparation of an individualized visual properties-matching
multilayer coating sheet suitable for repair purposes. This means that the multilayer
coating sheet can be made to individually match the visual properties, such as
colour, effect, texture, and gloss, of a surface to be matched. Additionally, it should
be possible to prepare the multilayer coating sheet in the individually required size
and shape. It should also be possible to use a wide variety of suitable polymeric
base film materials and to tune the hardness, flexibility, and elasticity of the
multilayer coating sheet to the required values, so that application of the repair
sheet to bent and curved substrates is possible without mechanical failure of the
coating layer.

The invention now provides a process for the preparation of a visual properties-
matching multilayer coating sheet comprising the steps of
a) determining the visual properties data of a surface to be matched in
visual properties;
b) transmitting the data from step a) to a system configured to receive
such data, and determination of the composition data of a coating
composition having an acceptable match of visual properties;
c) preparing a visual properties-matching coating composition according
to the determined composition data;
d) providing a base sheet layer optionally having an adhesive layer and
a backing layer on one surface;
e) applying the visual properties-matching coating composition to one
surface of the base sheet layer to form a colour- and/or effect-
imparting coating layer;
f) optionally, drying the applied colour- and/or effect-imparting coating
layer;
g) optionally, applying a clear coat layer on top of the colour- and/or
effect-imparting coating layer;
h) optionally, drying and/or curing the clear coat layer; and
i) if the base sheet layer in step d) was provided without an adhesive
layer and a backing layer, application of an adhesive layer and a
backing layer to the uncoated surface of the base sheet layer.
With the process of the invention it is possible to prepare an individualized
multilayer coating sheet which can be made to individually match the visual
properties, such as colour, effect, texture and gloss, of a surface to be matched.
The multilayer coating sheet can be prepared in the individually required size and
shape. It is also possible to use a wide variety of suitable polymeric base film
materials and to tune the hardness, flexibility, and elasticity of the multilayer

coating sheet to the required values, so that application of the sheet to bent and
curved substrates is possible without mechanical failure of the coating layer.
The process of the invention can be used for preparing multilayer coating sheets
for coated substrates. The multilayer coating sheets prepared according to the
process are particularly suitable for repairing the exterior coated surfaces of
automobiles and large transportation vehicles, such as trains, trucks, buses, and
boats. However, the multilayer coating sheet can also be used with great
advantage on small vehicles or on surfaces of buildings or other constructions, for
examples bridges. The multilayer coating sheet can also be used for all non-repair
purposes where a visual properties-matching surface finishing is required.
The coated surfaces of automobiles and transportation vehicles often comprise a
clear top coat on a colour- or effect-imparting base coat. The multilayer coating
sheet is very suitable for matching the visual properties of such coated surfaces.
However, the visual properties-matching multilayer coating sheet is equally suitable
for repairing a substrate having a colour-imparting pigmented top coat. The
multilayer coating sheets can be used to repair minor damage in the coating of a
substrate, such as small scratches or dents. Alternatively, it is also possible to
apply the multilayer coating sheet on a larger surface, such as an entire body panel
of a motor vehicle, for example a door, a wing, or a hood.
In step a) of the process the visual property data of a surface to be matched are
determined. Examples of visual property data are colour data, gloss data, effect
data, and texture data. Depending on the type of surface to be matched for visual
properties, one or more of these data have to be determined. Besides colour, a
paint film shows numerous further visual properties. Colour can be expressed by
the paint film reflection as a function of wavelength of visible light. Alternatively,
colour can be expressed in accordance with the so-called CIE Lab system, as
defined by the Commission International d'Eclairage, or similar systems, such as
the CIE Luv, CIE XYZ systems or the Munsell system. Particularly when effect

pigments, such as for example aluminium flake pigments or pearlescent pigments,
are used, the look of a paint film is not one of uniform colour, but shows texture.
This can include phenomena such as coarseness, glints, micro-brilliance,
cloudiness, mottle, speckle, sparkle or glitter. In the'following, texture is defined as
the visible surface structure in the plane of the paint film depending on the size and
organization of small constituent parts of a material. In this context, texture does
not include roughness of the paint film but only the visual irregularities in the plane
of the paint film. Structures smaller than the resolution of the human eye contribute
to "colour", whereas larger structures generally also contribute to "texture".
Texture data can for instance include the particle size distribution of the effect
pigments in the toner and the optical contrast, defined as the difference in
lightness, between the effect pigment and the other pigments present in the
coating. Also particles which are not directly observable by themselves can
contribute to the overall visual appearance of a paint film. Des-orienters are an
example of such particles. Effect pigments are generally flakes tending to take a
horizontal orientation in a cured film. To prevent this, and to obtain more variation
in flake orientation, spherical particles are used, referred to as des-orienters. Using
des-orienters in a metallic paint results in more glitter. The determination of texture
data is described in more detail in International patent application WO 01/25737.
The visual property data can be determined by known instrumental analysis. Using
an angle-dependent spectrophotometer colour and colour effect data can be
uniquely identified. The instrumental analysis quantifies colour and colour effect
parameters, examples of which are lightness, hue, and chroma data, and their
angle dependence.
If the surface to be matched is the surface of a motor vehicle, an alternative way of
determining visual property data is the retrieval of the so-called colour number,
optionally refined by a colour variant code. The colour number is the code that
represents the manufacturer's paint colour and colour effect, and can be found on
the vehicle of interest. Paint colour and colour effect may vary within one colour

number, for example due to minor variations between paint batches or application
variables, such as relative humidity or temperature. Those variations can be taken
into account using a variant database.
Still another way of recording visual property data involves the retrieval of the
Vehicle Identification Number (VIN), which can be found on every motor vehicle.
The VIN is a structured combination of characters assigned to a vehicle by the
manufacturer for identification purposes. The VIN consists of three parts, to wit the
World Manufacturer Identifier (WMI), the Vehicle Description Section (VDS), and
the Vehicle Indicator Section (VIS). The VIS, in conjunction with the VDS, ensures
a unique identification of all vehicles produced by each manufacturer. Once colour
code variants have been linked to the combination of VIS and VDS, the VIN can be
used to determine the visual property data of a vehicle. The use of the VIN to
determine the visual property data of vehicles is described in more detail in
European patent application EP 1355242 A.
It is also possible to use a combination of the above-mentioned methods for
determination of the visual property data. Any other known method for
determination of visual property data may also be used, for example visual
comparison of the surface to be matched with colour swatches. The most
appropriate and thus preferred method of determination may vary. For example, if
the visual properties of an aged automobile are to be determined, an instrumental
analysis of the visual properties may be preferred, because the visual properties
may have changed too much over time to be adequately described by the colour
code or the VIN.
In addition to the visual properties of the surface to be matched, also the size and
the shape of the required visual properties-matching multilayer coating sheet can
be determined. If the multilayer coating sheet is used for repair purposes, the
required size and shape may be equal to or slightly larger than the damaged
surface to be repaired.

Data such as the VIN and the colour code of a vehicle, as well as the size and the
shape of the damage, can easily be retrieved and determined by a vehicle owner
or fleet administrator. Thus, a visit to a vehicle body repair shop is not required for
determining the visual properties data of a surface to be matched. If the visual
properties data are determined by instrumental analysis, for example with a
spectrophotometer, such a determination can be carried out quickly and without
major out-of-service time of the vehicle in a vehicle body repair shop.
The determined data are transmitted to a system configured to receive such data.
Transmittal of the data can be via any means suitable for transmitting such data.
Typically, the data are transmitted via a communication network suitable for data
transmission. The data may be transmitted by voice, for example via a telephone
line. The data may also be transmitted in the written form, for example via a letter
or telefax. In a preferred embodiment, the data are transmitted electronically, for
example via the Internet by e-mail or via an on-line Internet connection. The
system configured to receive such data typically is a computer system under the
control of a suitable software program. A suitable computer may be a general
purpose computer having a central processing unit, a memory, means for loading
an application program into a defined address space of the memory, and a
computer monitor. Also connection means to a communication network for data
transfer from and to remote locations, such as a modem for connection to the
Internet, are useful.
After transmission of the data, the composition data of a coating composition
having an acceptable match of visual properties are determined. Coating
composition data can be determined in a number of ways, i.e. by means of search
procedures, calculations, or combinations of the two.
For example, use may be made of a databank comprising composition formulae
having visual property data linked thereto. Using the determined visual property

data of the surface to be matched in visual properties, the most closely matching
coating composition formula can be found.
Alternatively, it is possible to use a databank having visual property formulae with
spectral data linked thereto. Known calculation methods can be used to calculate
the visual property data of the visual property formulae and compare them. Also, a
databank can be used in which the absorption and reflection data, the so-called K
and S data, of pigments are stored. Using K and S data in combination with
pigment concentrations makes it possible to calculate the formula of which the
visual property data most closely match the visual property data of the surface to
be matched.
It is possible to combine the aforesaid search and calculation methods.
Once the coating composition data of a composition having an acceptable match of
visual properties have been determined, a visual properties-matching coating
composition is prepared by mixing the required components in the required ratio. In
one embodiment, the coating composition data are displayed on a computer
display or the data are printed out, and subsequently a coating composition is
prepared according to the displayed or printed composition data. Alternatively, the
computer can transfer the coating composition data directly to an automated
mixing machine. The automated mixing machine may automatically prepare the
visual properties-matching coating composition based on the composition data.
When the size of the required visual properties-matching multilayer coating sheet
has been determined and transmitted, it is possible to calculate the required
amount of visual properties-matching coating composition on the basis of the
surface to be coated. In this case, the visual properties-matching coating
composition is suitably prepared in the required amount. Otherwise, it is possible to
prepare a standard amount of the visual properties-matching coating composition.

The visual properties-matching coating composition typically is a liquid coating
composition which can be applied by spraying. Depending on the envisaged
purpose of the visual properties-matching multilayer coating sheet, the visual
properties-matching coating composition may also be a highly viscous liquid
composition or a powder coating composition. The visual properties-matching
coating composition may be water borne or solvent borne. It may suitably be
prepared by mixing one or more colour- and/or effect-imparting modules, one or
more binder modules, and a diluent module. Also a crosslinker may be added to
the visual properties-matching coating composition.
If the colour- and/or effect-imparting coating layer formed from the visual
properties-matching coating composition is not covered by a clear coat layer, it is
preferred that the colour- and/or effect-imparting coating layer is crosslinkable.
Crosslinkable coating layers can be obtained from two-component coating
compositions based on hydroxy-functional binders and isocyanate-functional
crosslinkers. Such compositions are well-known in the art and they are available as
solvent borne compositions and as water borne compositions. Crosslinking may
occur at ambient temperature or at elevated temperature.
It is also possible to use coating compositions which are curable by actinic
radiation. In a still further embodiment, so-called dual cure compositions may be
used, which are curable thermally and by actinic radiation. Such dual cure
compositions may for example comprise binders having hydroxyl groups and
(meth)acryloyl groups, and an isocyanate-functional crosslinker optionally having
(meth)acryloyl groups.
After preparation of the visual properties-matching coating composition, the
composition may be applied to the base sheet layer, as described further below.
However, it is also possible to first apply the coating composition to a test panel
and to determine if the visual properties of the applied coating have a sufficient
match with the visual properties of the surface to be matched. Such a
determination can be carried out by instrumental analysis, as described above. If

the difference in visual properties is below a predetermined value, the coating
composition can be applied to the base sheet layer. Otherwise, a new improved
visual properties-matching coating composition may be prepared for use in the
subsequent process steps. The above steps may be automated, carried out for
example by a robot under the control of a suitably programmed computer.
The base sheet for the base sheet layer may be made of various materials. The
base sheet may consist of an aluminium foil or an aluminized layer, for instance an
aluminized polyester film, plastic or paper. The base sheet can be rigid or flexible.
The base sheet has to be sufficiently flexible to follow the substrate's contours
upon application. Therefore, the base sheet used in the process preferably is
flexible and elastic. However, for spot repairs the spot frequently is sufficiently
small to be treated as if it were a plane, which means that base sheet flexibility and
elasticity are of minor relevance. When the fade-out technique as described further
below is applied, the base sheet used suitably is transparent and colourless. In
other embodiments coloured and/or non-transparent base sheets may be used.
Coloured and/or non-transparent base sheets may be easier to handle and
contribute to the hiding power of the multilayer coating sheet.
It will be readily understood that upon contact with the applied visual properties-
matching coating composition the base sheet layer should not be dissolved or
excessively swollen by the coating composition or components thereof. Swelling of
the base sheet is also undesirable, because it can compromise the dimensional
stability thereof.
The base sheet layer typically comprises a polymeric material, for example
polyvinyl chloride, acetate, polyethylene, polyester, polyurethane, polyamide, an
acrylic polymer, polyethylene naphthalate, polyethylene terephthalate or
polycarbonate. Examples of other suitable materials are polyvinylalcohol, natural or
modified starch, polyalkylene oxide, e.g. polyethylene oxide or polymers modified
therewith, polymers and copolymers of (meth)acrylic amide or meth(acrylic) acid.

Also mixtures, hybrids, and blends of these materials can be used. The base sheet
may consist of a single layer. Alternatively, the base sheet may be multilayered in
itself. The base sheet may for example include a barrier or sealant layer that
prevents any potentially damaging solvent of the coating composition to be applied
on one surface of the base sheet from reaching the adhesive layer on the other
surface of the base sheet. The base sheet may also comprise a surface layer
which has been particularly adapted to be coated with a coating composition.
The base sheet layer suitably has a thickness of at least 10 m, preferably at least
20 |jm, and most preferably of at least 30 m. Generally, the thickness of the base
sheet layer is below 150 urn, preferably below 120 urn, and most preferably below
100 urn.
As mentioned above, the multilayer coating sheet may have to be bent and/or
stretched during application to a substrate. Therefore, the base sheet layer is
preferably made of elastic and flexible material. The elongation at break of the
material preferably is at least 100%, more preferably at least 150%, and most
preferably at least 250%. Many of the polymeric materials mentioned above exhibit
these properties.
The base sheet may be provided in the form of a roll. The roll may be inserted into
a device that enables unrolling and die cutting activities, so as to provide a base
sheet of the desired size and shape. In one embodiment, the unrolling, die cutting
device is automated, and can be operated from a computer platform that enables
digital design. A digital design, characterizing the required size and shape of the
base sheet, is suitably based on the determined size and shape data transmitted in
step b). The die cutting activities may alternatively be executed after application of
the visual properties-matching coating composition. It is also possible for die
cutting activities to be executed at both stages of the process.
If for example a visual properties-matching multilayer coating sheet for a bonnet of
a motor vehicle is required, the software platform may suggest the best fitting form,
either through calculation, using a vehicle part dimensions database, or using

three-dimensional imaging software in combination with for example digital
photography. The unrolling device then unrolls and die cuts at a desired length.
The width of the resultant rectangular or square piece of base sheet resembles the
roll width. The base sheet is fed into a base sheet coating area, where the base
sheet is coated either completely or partly according to the desired end size and
shape. The latter example might include fade-out areas, preferably situated at the
outer border of the design. From there, the rectangular or square base sheet - with
the desired coated and optionally faded-out areas design - is fed into a die cutting
area, where the final coated sheet is die cut to the desired end form. This end form
may include larger parts of uncoated base sheet.
In another embodiment, the base sheet is provided in the form of a stack of sheets,
in variable forms with variable surface areas. The forms might for example be
rectangular, oval or round. The surface area generally ranges from 1 mm2 to 10
m2, and preferably from 0.5 cm2 to 5 m2.
The base sheet layer optionally is provided with an adhesive layer and a backing
layer on one surface. The adhesive layer serves to adhesively bond the visual
properties-matching multilayer coating sheet to a substrate. In one embodiment,
the adhesive is a pressure-sensitive adhesive. Alternatively, the adhesive may be
activatable thermally or by actinic radiation. The adhesive layer may comprise
further functional additives in order to include additional desirable properties in the
adhesive layer. For example, the adhesive layer may comprise anti-corrosive
ingredients, such as anti-corrosive pigments, providing the visual properties-
matching multilayer coating sheet with anti-corrosive properties.
It is preferred that the adhesive used increases in adhesive force over time after
adhesively binding the visual properties-matching multilayer coating sheet to a
substrate. If the adhesive initially has a low tack, re-positioning of the visual
properties-matching multilayer coating sheet immediately during application is
possible, thus facilitating the application achieving exact positioning and an
invisible repair.

The adhesive layer can be applied to the base sheet by any known application
technique suitable for this purpose. Examples include application by a knife, roll
coating, and transfer coating operations. The adhesive layer may be transparent.
The thickness of the adhesive layer suitably is at least 2 m, preferably at least 5
urn. Generally, the thickness of the adhesive layer is below 50 urn, preferably
below 35 urn.
A backing layer is applied over the adhesive layer. The materials of backing layers
normally used for this purpose include paper, e.g. crepe, flatback, tissue, and
polymer films, e.g. polyester, polyvinyl chloride, polypropylene, polyethylene,
fluoropolymers, cellulose acetate, and polyurethane. The backing layer may
suitably be coated with a release agent to provide easy removal of the backing
layer upon application of the visual properties-matching multilayer coating sheet.
The release agents are typically based on binders containing silicone, a substance
pressure-sensitive adhesives do not readily bond with. Acrylic emulsion release
agents are an example of non-silicone-based release agents.
It is preferred to have air egress channels in the adhesive layer. Such air egress
channels facilitate the application of the multilayer coating sheet to a substrate.
Due to easier removal of air bubbles, a smooth coverage and fewer wrinkles can
be achieved. Air egress channels can be created by an embossed surface of the
backing layer facing the adhesive layer. Other methods of creating air egress
channels are equally suitable, for example by the presence of microscopic glass
spheres in or on the adhesive layer. A layer of microscopic glass spheres shields
the adhesive, allowing the multilayer coating sheet to be repositioned during
application. When pressure is applied, the glass spheres are crushed into the
adhesive, giving rise to air egress channels and instant high bond strength.
Suitable base sheet layers provided with an adhesive layer and a backing layer are
available commercially, for example from Avery Dennison under the trade
designation Avery 6904 Easy Apply.

When the base sheet layer is provided without an adhesive layer and a backing
layer, these layers can be applied in a later step of the process.
The visual properties-matching coating composition is applied to one surface of the
base sheet layer. In one embodiment, the coating composition is a base coat
composition such as is typically used in base coat/clear coat systems on motor
vehicles. Such a base coat composition is a liquid coating composition comprising
pigments and/or effect-imparting particles, such as mica particles or metal flakes.
Application thereof is preferably carried out by spraying. However, other application
methods are also possible, provided that the effect-imparting particles are oriented
in such a way that a colour effect can be matched independent of the viewing
angle. Suitable base coat compositions are available commercially, for example
from Akzo Nobel Car Refinishes under the trade designations Autowave and
Autobase Plus. If the visual properties-matching coating composition does not
comprise effect-imparting particles requiring a specific orientation in the coating
layer, the above restrictions on application methods do not apply and all known
application methods can be used, such as rolling, curtain coating, brushing, hot-
melt application, air brushing, or ink-jet printing.
It may be that a visual properties-matching coating composition having an
acceptable match of visible properties cannot be found in the data file containing
coating composition data. In this case it may nevertheless be possible to prepare a
visual properties-matching multilayer coating sheet according to the process of the
invention. A coating composition having the best possible match of visible
properties is selected and applied to the base sheet layer as described above. The
base sheet layer should be transparent. The colour- and/or effect-imparting coating
layer is applied to the base sheet layer so as to achieve a hiding power gradient
within the coated area, with full hiding power being achieved in the centre of the
area of the applied coating layer and the hiding power decreasing towards at least
one border of the area of the applied coating layer. This can for example be

achieved by gradually decreasing the applied layer thickness of the coating
towards the at least one border of the area of the applied coating layer. This
technique is commonly known in the refinish sector as fade-out. When the slope of
the colour and effect difference over a certain distance does not exceed a certain
threshold value, the resulting colour and effect difference is practically invisible to
the human eye.
The invention also relates to a multilayer coating sheet wherein the fade-out
technique has been applied. Such a visual properties-matching multilayer coating
sheet comprises, in the following order,
a) a backing layer,
b) an adhesive layer,
c) a transparent base sheet layer,
d) a colour- and/or effect-imparting coating layer, and
e) optionally, a clear coat layer,
wherein the hiding power of the colour- and/or effect-imparting coating layer
decreases towards at least one border of the coating layer.
Such a multilayer coating sheet is particularly suitable for repair of minor damage
to the exterior coating of an automobile.
The multilayer coating sheet suitably has a thickness of at least 40 m, preferably
at least 50 m, and more preferably at least 60 urn. The thickness generally is
below 500 m, preferably below 300 urn, and more preferably below 200 m. In
view of the required elasticity upon application of the multilayer coating sheet to a
substrate, the elongation at break of the multilayer coating sheet suitably is
essentially the same as described above for the base sheet layer. In order to
achieve the required elongation at break values, the crosslink density of the
coating layer(s) of the multilayer coating sheet before application to a substrate
preferably is sufficiently low. When elasticity and elongation upon application are
not critical, for example in the case of application of the multilayer coating sheet to

a non-curved plane substrate, the crosslink density of the coating layer(s) may be
higher, for example about 50 kPa/K.
After application of the visual properties-matching coating composition, the applied
colour- and/or effect-imparting coating layer may be subjected to a drying phase.
Drying includes physical drying by evaporation of solvent and/or water and curing
by chemical crosslinking reactions. If required, drying can be accelerated by
heating, irradiation with (near) infrared radiation, or air blowing. When the coating
is susceptible to actinic radiation-induced curing, the applied coating may be
irradiated with actinic radiation, such as ultraviolet light or electron beam radiation.
When the coating is prepared from a dual cure coating composition, it may be
preferred to carry out thermal curing after application of the coating composition
and to suspend curing by actinic radiation until after the visual properties-matching
multilayer coating sheet has been adhesively bonded to a substrate. Such a
stepwise curing of the composition has the advantage that the visual properties-
matching multilayer coating sheet remains sufficiently flexible and elastic to allow
stretching and bending during application to a curved substrate without mechanical
failure such as cracking of the coating layer. A post-application-to-a-substrate cure
step by actinic radiation may provide the coating layer with the required hardness
and resistance properties. The thickness of the colour- and/or effect-imparting
coating layer suitably is in the range of 5 to 30 m. In fade-out areas as described
above, the thickness may be below the indicated range.
After application of the visual properties-matching coating composition to the base
sheet layer, an optional spectrophotometric control system measurement of the
colour and/or effect data of the applied coating layer may be executed in order to
check if the visual properties have an acceptable match with the visual property
data determined in step a). If the visual property data of the applied coating layer
differ by more than a predetermined threshold value, it may be required to select a
better matching coating composition or to apply the fade-out technique as

described above. The optional control step may alternatively or additionally also be
carried out after application of the optional clear coat layer, as described further
below.
When the determination of the visual property data in step a) of the process
indicates that a clear coat layer is required to match the visual properties, a clear
coat layer is applied on top of the colour- and/or effect-imparting coating layer. The
clear coat layer may be applied on top of the dried colour- and/or effect-imparting
coating layer. Alternatively, the clear coat may be applied wet-on-wet on top of the
colour- and/or effect-imparting coating layer. Wet-on-wet application means that
the underlying colour- and/or effect-imparting coating layer is not fully dried or
cured before application of the clear coat. It is also possible for the colour- and/or
effect-imparting coating layer to be partially dried, for example by subjecting it to a
so-called flash-off phase of 5 to 15 minutes, during which a substantial part of the
liquid diluent can evaporate.
Application of the clear coat may be done by spraying. However, other means of
application, such as mentioned above for the visual properties-matching coating
composition, may be employed as well. The choice of the appropriate application
method may depend on the visual properties, such as gloss, to be matched. The
application method giving the best match of visual properties is generally preferred.
The clear coat layer is preferably crosslinkable, as described above in respect of
the visual properties-matching coating composition. Suitable clear coat
compositions are available commercially, for example from Akzo Nobel Car
Refinishes under the trade designation Autoclear. So far, good results, in particular
with respect to weather resistance of the applied multilayer coating sheet, have
been obtained when the clear coat comprises a mixture of a polyester polyol, a
polyurethane polyol, an organic solvent, and a flexible isocyanate-functional
crosslinker. In one embodiment, the isocyanate-functional prepolymer Xthane IW-
P26, commercially available from ITWC, Inc., Malcom, Iowa, United States of
America, has been used as crosslinker. The molar ratio of isocyanate-groups and

hydroxyl groups in the clear coat suitably is in the range of 1.5 to 0.8, for example
1.2. Generally, the clear coat additionally comprises other components and
additives which are usually present in automotive refinish top coats, such as
crosslinking catalyst, wetting agents, and light stabilizers.
After application, the clear coat may be subjected to a drying and/or curing step, as
described above in respect of the visual properties-matching coating composition.
The clear coat layer suitably has a layer thickness in the range of 20 to 80 urn.
In another embodiment, the clear coat is a flexible, solid polyurethane film having a
very low crosslink density. The clear coat layer contains unreacted polymerizable
olefinically unsaturated groups, such as (meth)acryloyl groups, with at least a part
of the unreacted polymerizable olefinically unsaturated groups being maleimide
groups.
Such a clear coat layer can be prepared by mixing and reacting hydroxyl- and
isocyanate-functional prepolymers. Either or both of the prepolymers additionally
comprise the polymerizable olefinically unsaturated groups. As an example of a
hydroxyl-functional prepolymer comprising polymerizable olefinically unsaturated
groups the addition product of (meth)acrylic acid and butanediol diglycidylether
may be mentioned. An example of an isocyanate-functional prepolymer comprising
polymerizable olefinically unsaturated groups is the addition product of 1 mole of a
diisocyanate trimer and 1 mole of a hydroxyl-functional maleimide.
The glass transition temperature (Tg) of the clear coat layer before irradiation with
actinic radiation is in the range of -40 to 40°C, preferably between 0 and 20°C.
Such a clear coat also has a very high flexibility. The elongation at break at room
temperature preferably is in the range of about 300% to about 500%.
After application of the multilayer coating sheet to a substrate, post-curing of the
clear coat by polymerization of the olefinically unsaturated groups can be initiated
by irradiation with UV light or visible light. UV-A light or visible light is preferred.
Upon post-curing the Tg of the clear coat increases by about 20 to 50°C. The final
Tg of the post-cured clear coat preferably is in the range of 40 to 65oC, which is

similar to the Tg of commercial clear coats. Such multilayer coating sheets which
were post-cured after application exhibit a favourable weather resistance.
The presence of maleimide groups has the advantage of a higher Tg increase
upon curing as compared to a clear coat having acryloyl groups only, based on a
comparable concentration of polymerizable olefinically unsaturated groups. In
addition, maleimide groups reduce oxygen inhibition during radiation curing.
If the base sheet layer was originally provided without an adhesive layer and a
backing, an adhesive layer and a backing layer can be applied to the uncoated
surface of the backing layer after application of the coating layers.
As mentioned above, the visual properties-matching multilayer coating sheet
obtainable by the process of the invention is very suitable for partial finishing of a
substrate. Partial finishing of substrates includes the repair of small scratches or
dents in a larger surface of a substrate, for example a scratch in the door of an
automobile. Partial finishing also includes the application of a visual properties-
matching multilayer coating sheet to an entire body part of a motor vehicle. Also,
the application of graphics and lettering in predetermined colours and effects on
large transportation vehicles, such as trains, buses, trucks, and airplanes is
included.
Accordingly, the invention also relates to a second process for partial finishing of a
substrate. This second process comprises the preparation of a visual properties-
matching multilayer coating sheet as described above and, additionally, in any
workable order, the steps of
j) removing the backing layer from the visual properties-matching
multilayer coating sheet;
k) applying the visual properties-matching multilayer coating sheet to
the surface of the substrate to be finished, with the adhesive layer
facing the substrate surface to be finished and forming an adhesive

bond between the visual properties-matching multilayer coating sheet
and the substrate surface; and
I) optionally curing the coating layer(s) of the visual properties-matching
multilayer coating sheet applied in steps e) and g).
The process is also very suitable for refinishing a damaged substrate. Depending
on the condition of the substrate to be partially finished, it may be appropriate to
carry out one or more additional preceding steps in order to prepare the substrate
for the application of the visual properties-matching multilayer coating sheet.
Examples of such additional preparation steps are cleaning of the substrate,
including degreasing and removal of existing coating layers, filling of dents with a
suitable filler, such as a putty, application of a primer layer to the substrate, and
sanding of the substrate. Also removal of dust by pressurized air or with a dust
cloth may be beneficial.
The process of partially finishing the surface of a substrate includes the step of
removing the backing layer from the visual properties-matching multilayer coating
sheet, thus exposing the adhesive layer of the visual properties-matching
multilayer coating sheet. In one embodiment, the backing layer is removed
completely in a single step. Alternatively, it is also possible to remove the backing
layer partly and to start with the application of the multilayer coating sheet to a
substrate. Removal of the backing sheet and application may then be continued
successively until the whole multilayer coating sheet has been applied to the
substrate. This stepwise procedure may be preferred for relatively large surfaces to
be finished with a single multilayer coating sheet, because the stepwise procedure
may enhance applicability and lead to a better quality of the end result. The
backing layer can normally be removed manually.
When the adhesive layer of the visual properties-matching multilayer coating sheet
comprises a pressure-sensitive adhesive, no further preparation steps of the
adhesive layer are generally required prior to the application of the coating sheet to

the substrate. If other types of adhesives are used, an activation step to activate
the adhesive may be required. Depending on the type of adhesive and the method
of activation, the activation step may be carried out prior to, during and/or after
application. Examples of activation steps are treatment of the adhesive surface
with water or an appropriate organic solvent. In the case of heat-sensitive
adhesives, heat treatment may be required.
The visual properties-matching multilayer coating sheet is subsequently applied to
the surface of the substrate to be finished, with the adhesive layer facing the
substrate surface to be finished and forming an adhesive bond between the visual
properties-matching multilayer coating sheet and the substrate surface. As
mentioned above, the substrate surface may be a two-dimensional object or a
three-dimensional object having a curved surface. Since the visual properties-
matching multilayer coating sheet is essentially flat, it has to be made to conform to
the substrate during application in the case of three-dimensionally shaped
substrates. If the adhesive layer comprises a pressure-sensitive adhesive,
pressure is applied to the multilayer coating sheet after it has been made to
conform and positioned on the substrate in order to form an adhesive bond
between the multilayer coating sheet and the substrate. Application of the visual
properties-matching multilayer coating sheet to a substrate may be carried out
manually, optionally using suitable tools, such as a squeegee, a felt-covered
squeegee, or gloves. Gloves prevent contamination and can lower the friction while
moving the hand or a squeegee across the surface of the visual properties-
matching multilayer coating sheet and simultaneously applying pressure. Also
other tools, such as a razor knife, a heat source for heating the multilayer coating
sheet, or a rivet brush, may be used. The application of larger visual properties-
matching multilayer coating sheets, for example on trucks or buses, may be aided
by a mechanical sheet guidance system, enabling the application of longer
stretches of sheet in a single operation. It is also possible to apply the multilayer
coating sheet to a substrate by the so-called wet application method. By wetting

the surface of the substrate with an application fluid, the film can be positioned on
the substrate without firmly adhering to it. In one embodiment, the application fluid
can be an aqueous detergent solution, for example 1 weight-% of detergent in
water. Alternatively, the application fluid can be an organic solvent or be based on
an organic solvent, such as ethanol or isopropyl alcohol. One advantage of using
organic solvent based application fluids is the combination of slideability and initial
tack. The latter enables the polymer sheet to be fixed when desired, while
maintaining its easy repositionability. The initial tack is based upon the solvent
activation of the adhesive on the back of the foil.
The application fluid may also be a mixture of water and organic solvents.
The detergent liquid provides slideability and positionability to the pressure-
sensitive coating sheet until the water film has been removed. A plastic squeegee
can be used for the removal of the water layer, preferably by squeegeeing from the
centre towards the edges of the multilayer coating sheet and gradually increasing
the applied force until apparently most or all of the water has been removed.
If, for example, a visual properties-matching multilayer coating sheet is to be
applied to the bonnet of an automobile, the backing sheet can be removed and the
sheet applied at once by two individuals, one on either side, holding the film. After
the sheet has been applied to the bonnet, repositioning, air regress and
pressurized adhesion can be executed by one person. The sheet is made to
conform and adhere to the front of the bonnet, without air bubbles or any other
surface defects being visible. On all sides of the bonnet, a certain surplus of sheet
remains as a free form. This surplus is folded to the sides and the backside of the
bonnet, and adhered as smoothly as possible.
If the coating layer(s) of the multilayer coating sheet have not been fully cured
before application of the sheet to a substrate, an additional post-application cure
step can be carried out after application of the sheet to a substrate. The post-
application cure may be thermally initiated, for example by heating with a hot air

blower or by irradiation with (near) infrared radiation. Alternatively, the post-
application cure may be initiated by actinic radiation, such as ultraviolet radiation.
Subsequent to the application of the visual properties-matching multilayer coating
sheet to the surface of a substrate, and after the optional post-application curing
step of the coating layers, matching of the visual properties of the multilayer
coating sheet and the surrounding surface may optionally be further improved by
one or more after-treatment steps. Examples of such after-treatment steps are
polishing of the surface of the multilayer coating sheet and the surrounding
surface, and heat treatment of the multilayer coating sheet. Warming of the
multilayer coating sheet by heat treatment can cause the settlement of minor
irregularities in one or more of the layers of the multilayer coating sheet, such as in
the adhesive layer or in the coating layers.
The processes according to the invention have the additional advantage that
damage to a coating layer, such as a dent, a scratch, or a bare area, can be
repaired in less processing time and without damaging the area around the
damaged area. Since spraying of coating compositions is not carried out on the
substrate, such as a motor vehicle, it is not required to tape off the parts of the
coating adjacent to the damaged area, since there is no need for protection against
the deposition of spray mist. Thus, when a vehicle is partly refinished, the out-of-
service time of the vehicle for refinishing can be significantly reduced.
In a preferred embodiment of the process for preparation of a visual properties-
matching multilayer coating sheet according to the invention, steps c) to i) are
carried out in a central multilayer coating sheet manufacturing location. A central
multilayer coating sheet manufacturing location receives the visual property data of
a surface to be matched in visual properties from two or more remote locations.
Generally, the central location will serve a multitude, typically 20 or more, for
example up to 500, local body shops. A central multilayer coating sheet

manufacturing location may for example serve the body shops of a country or a
part thereof, or a continent, or even the whole world.
In this case local paint storage, mixing, and spraying operations at a vehicle body
repair shop are not required, which saves time and money. Additionally, the
preparation of visual properties-matching multilayer coating sheets can be fully
automated in a dedicated central location, which again saves time and money.
Automated preparation of the coating sheets has the further advantage that the
exposure of human workers to potentially hazardous solvent fumes during
application and drying of coating compositions is minimized. If the data determined
in step a) are transmitted electronically via e-mail on one day, the visual properties-
matching multilayer coating sheets may be prepared fully automatically under the
control of a computer, for example overnight, and the finished visual properties-
matching multilayer coating sheets can be posted to the vehicle owner or a vehicle
body repair shop the following day, as the case may be. The out-of-service time of
a vehicle can be further reduced in such an embodiment.

Claims
1. A process for the preparation of a visual properties-matching multilayer
coating sheet comprising the steps of
a) determining the visual property data of a surface to be matched in
visual properties;
b) transmitting the data from step a) to a system configured to receive
such data, and determination of the composition data of a coating
composition having an acceptable match of visual properties;
c) preparing a visual properties-matching coating composition according
to the determined composition data;
d) providing a base sheet layer optionally having an adhesive layer and
a backing layer on one surface;
e) applying the visual properties-matching coating composition to one
surface of the base sheet layer to form a colour- and/or effect-
imparting coating layer;
f) optionally, drying the applied colour- and/or effect-imparting coating
layer;
g) optionally, applying a clear coat layer on top of the colour- and/or
effect-imparting coating layer;
h) optionally, drying and/or curing the clear coat layer; and
i) if the base sheet layer in step d) was provided without an adhesive
layer and a backing layer, application of an adhesive layer and a
backing layer to the uncoated surface of the base sheet layer.
2. A process according to claim 1 wherein the data in step b) are transmitted
via a communication network, and wherein steps c) to i) are carried out in a
central multilayer coating sheet manufacturing location.

3. A process according to claim 1 or 2 wherein in step a) also the size and the
shape of the required visual properties-matching multilayer coating sheet
are determined.
4. A process for partially finishing the surface of a substrate, comprising the
preparation of a visual properties-matching multilayer coating sheet
according to claim 1, and additionally the steps of
j) removing the backing layer from the visual properties-matching
multilayer coating sheet;
k) applying the visual properties-matching multilayer coating sheet to
the surface of the substrate to be finished, with the adhesive layer
facing the substrate surface to be finished and forming an adhesive
bond between the visual properties-matching multilayer coating sheet
and the substrate surface; and
I) optionally curing the coating layer(s) of the visual properties-matching
multilayer coating sheet applied in steps e) and g).
5. A process according to claim 4 wherein the surface of an automobile or a
large transportation vehicle is partially finished.
6. A process according to claim 4 or 5 wherein the process is used to refinish a
damaged substrate.
7. A visual properties-matching multilayer coating sheet comprising, in the
following order,

a) a backing layer,
b) an adhesive layer,
c) a transparent base sheet layer,
d) a colour- and/or effect-imparting coating layer, and

e) optionally, a clear coat layer,
wherein the hiding power of the colour- and/or effect-imparting coating layer
decreases towards at least one border of the coating layer.
8. Use of the visual properties-matching multilayer coating sheet according to
claim 7 for repair of minor damage to the exterior coating of an automobile.

The invention relates to process for the preparation of a visual properties-matching multilayer coating sheet comprising
the steps of a) determining the visual property data of a surface to be matched in visual properties; b) transmitting the data
from step a) to a system configured to receive such data, and determination of the composition data of a coating composition having
an acceptable match of visual properties; c) preparing a visual properties-matching coating composition according to the determined
composition data; d) providing a base sheet layer optionally having an adhesive layer and a backing layer on one surface; e) applying
the visual properties-matching c oating composition to one surface of the base sheet layer to form a colour- and/or effect-imparting
coating layer; f) optionally, drying the applied colour- and/or effect-imparting coating layer; g) optionally, applying a clear coat layer
on top of the colour- and/or effect- imparting coating layer; h) optionally, drying and/or curing the clear coat layer, and i) if the base
sheet layer in step d) was provided without an adhesive layer and a backing layer, application of an adhesive layer and a backing
layer to the uncoated surface of the base sheet layer.

Documents:

02350-kolnp-2008-abstract.pdf

02350-kolnp-2008-claims.pdf

02350-kolnp-2008-correspondence others.pdf

02350-kolnp-2008-description complete.pdf

02350-kolnp-2008-form 1.pdf

02350-kolnp-2008-form 3.pdf

02350-kolnp-2008-form 5.pdf

02350-kolnp-2008-gpa.pdf

02350-kolnp-2008-international publication.pdf

02350-kolnp-2008-international search report.pdf

02350-kolnp-2008-pct priority document notification.pdf

02350-kolnp-2008-pct request form.pdf

2350-KOLNP-2008-(15-01-2014)-CORRESPONDENCE.pdf

2350-KOLNP-2008-(15-01-2014)-FORM-3.pdf

2350-KOLNP-2008-(18-06-2013)-ANNEXURE TO FORM 3.pdf

2350-KOLNP-2008-(18-06-2013)-CORRESPONDENCE.pdf

2350-KOLNP-2008-(18-06-2013)-FORM-3.pdf

2350-KOLNP-2008-(18-06-2013)-OTHERS.pdf

2350-KOLNP-2008-(19-02-2013)-CORRESPONDENCE.pdf

2350-KOLNP-2008-(19-02-2013)-OTHERS.pdf

2350-KOLNP-2008-(19-09-2013)-CLAIMS.pdf

2350-KOLNP-2008-(19-09-2013)-CORRESPONDENCE.pdf

2350-KOLNP-2008-(19-09-2013)-FORM-2.pdf

2350-KOLNP-2008-(19-09-2013)-FORM-3.pdf

2350-KOLNP-2008-(19-09-2013)-PETITION UNDER RULE 137-1.1.pdf

2350-KOLNP-2008-(19-09-2013)-PETITION UNDER RULE 137.pdf

2350-KOLNP-2008-(22-06-2012)-CORRESPONDENCE.pdf

2350-KOLNP-2008-(22-06-2012)-FORM-1.pdf

2350-KOLNP-2008-(22-06-2012)-OTHERS.pdf

2350-KOLNP-2008-(22-06-2012)-PA.pdf

2350-KOLNP-2008-ASSIGNMENT.pdf

2350-KOLNP-2008-CORRESPONDENCE 1.1.pdf

2350-KOLNP-2008-CORRESPONDENCE-1.2.pdf

2350-KOLNP-2008-FORM 13.pdf

2350-KOLNP-2008-FORM 18.pdf

2350-KOLNP-2008-FORM 3-1.1.pdf

2350-KOLNP-2008-PA.pdf


Patent Number 260030
Indian Patent Application Number 2350/KOLNP/2008
PG Journal Number 14/2014
Publication Date 04-Apr-2014
Grant Date 31-Mar-2014
Date of Filing 11-Jun-2008
Name of Patentee AKZO NOBEL COATINGS INTERNATIONAL B. V.
Applicant Address VELPERWEG 76, NL-6824 BM ARNHEM, THE NETHERLANDS
Inventors:
# Inventor's Name Inventor's Address
1 BOERS VINCENT MATTHIJS KOOILAAN 45S, NL-2315 EB LEIDEN
2 KRUITHOF KLAAS JAN HENDRIK RIJNSBURGERWEG 43, NL-2334 BG LEIDEN
3 MARINUS EDWARD KWIKSTAARTHOEK 9, NL-2317 WT LEIDEN
4 KIELSTRA HARMEN JELKE OVERTOOM 414 HS, NL-1054 JT AMSTERDAM
PCT International Classification Number B05D 5/00,B05D 7/00
PCT International Application Number PCT/EP2006/068393
PCT International Filing date 2006-11-13
PCT Conventions:
# PCT Application Number Date of Convention Priority Country
1 05110740.7 2005-11-15 U.S.A.
2 60/751207 2005-12-19 U.S.A.