Title of Invention

"SUBSTRATE WITH AN ANTI-SOILING COATING"

Abstract A substrate having at least one main surface comprising a first coating deposited on said main surface and a second coating having anti-soiling properties deposited and adhering on the surface of said first coating, - the first coating being a (meth)acrylate based coating and being obtained by polymerizing a polymerizable composition comprising: i) at least one (meth)acrylate compound and ii) at least one compound I having at least one - M-Z' bond with M representing Si or a Metal atom, Z' representing OH or a hydrolysable group, and at least one ethylenic unsaturated group or epoxy group, and/or iii) at least one silica or metal oxide colloid having free ethylenically unsaturated groups; and - the second coating, having anti-soiling properties, being obtained by depositing on said first coating an anti-soiling coating composition comprising at least one compound II, or a hydrolyzate thereof, having at least one - Si-Z" group with Z" representing OH or a hydrolysable group.
Full Text SUBSTRATE WITH AN ANTI-SOILING COATING
This application claims benefit of U.S. Provisional Application No. 60/621,142 filed October 22, 2004, the contents of which are incorporated herein by reference.
BACKGROUND OF THE INVENTION
1. Field of the invention
The invention relates to substrates coated with a modified (meth)acrylate based coating, providing good scratch resistance along with interfacial adhesion with an anti-soiling coating, especially a fluorinated hydrophobic coating, deposited thereon.
The invention also relates to a coating composition comprising a (meth)acrylate based coating composition, usable for obtaining the coated substrate here above mentioned and a corresponding coated substrate able to be coated with an anti-soiling coating.
The invention is preferably used for manufacturing ophthalmic lenses coated, especially on their back side (concave side), with the coating of the invention and that subsequently can be treated with an anti-soiling coating.
2. Description of related art
It is well known in the field of ophthalmic lenses to apply anti-soiling coatings, especially hydrophobic and/or oleophobic top coats having low surface energy on antireflective (AR) stacks.
The anti-soiling has generally reactive groups such as SiO-alkyl groups, Si-CI, Si-NH2 or Si-NH- groups that can hydrolyze and react with pendant reactive groups at the surface of the AR.

When the anti-soiling coating is deposited on inorganic AR layers that have been vapour deposited, there is generally no severe problems of adhesion between the AR and the anti-soiling coating.
When the anti-soiling coating is deposited on another coating, especially those of organic nature, such as an abrasion resistant coating, adhesion problems are encountered.
According to the invention, it was found that it is necessary to use a specific coating composition in order to obtain a good adhesion at the interface between the coating and the anti-soiling coating.
SUMMARY OF THE INVENTION
A substrate according to the invention is a substrate having at least one main surface comprising a first coating deposited on said main surface and a second coating having anti-soiling properties deposited and adhering on the surface of said first coating,
- the first coating being a (meth)acrylate based coating and
being obtained by polymerizing a polymerizable composition comprising :
i) at least one (meth)acrylate compound and
ii) at least one compound I having at least one - M-Z' bond with M representing Si or a Metal atom, Z' representing OH or a hydrolysable group and at least one ethylenic unsaturated group, or epoxygroup, preferably an ethylenic unsaturated group, and/or
iii) at least one silica or metal oxide colloid having free ethylenic unsaturated groups;
and
- the second coating, having anti-soiling properties, being
obtained by depositing on said first coating an anti-soiling coating
composition comprising at least one compound II, or a hydrolyzate
thereof, having at least one - Si-Z" group with Z" representing OH or a
hydrolysable group.

DETAILED DESCRIPTION OF THE INVENTION AND PREFERRED EMBODIMENTS
By "ethylenic unsaturated group" there is meant a group comprising a
^ moiety.
By "free ethylenic unsaturated group" there is meant a group comprising the above defined moiety which capable of reacting with the (meth) acrylate compounds of i).
The coating formulation is designed to improve the hydrophobicity which leads to the ease of cleaning.
The main component of the (meth)acrylate based coating compositions may be chosen between monofunctional (meth)acrylates and multifunctional (meth)acrylates such as difunctional (meth)acrylates; trifunctional (meth)acrylates; tetrafunctional (meth)acrylates, pentafunctional(meth)acrylates, hexafunctional (meth)acrylate.
Examples of such monomers are:
. Monofunctional (meth)acrylates: Allyl methacrylate, 2-ethoxyethyl acrylate , 2-ethoxyethyl methacrylate, caprolactone acrylate, isobornyl methacrylate, lauryl methacrylate, polypropylene glycol monomethacrylate.
Difunctional (meth)acrylates: 1,4-butanediol diacrylate, 1,6-hexanediol diacrylate, 1,6-hexanediol dimethacryalte, polyethylene glycol diacrylate, tetraethylene glycol diacrylate, polyethylene glycol dimethacrylate, polyethylene glycol diacrylate, ethoxylated bisphenol A

diacrylate, tetraethylene glycol diacrylate, tripropylene glycol diacrylate, neopentyl glycol diacrylate, 1,4-butanediol dimethacrylate, tetraethylene glycol dimethacrylate, diethylene glycol diacrylate.
Trifunctional (meth)acrylates: Trimethylolpropane trimethacrylate, Trimethylolpropane triacrylate, pentaerythritol triacrylate, ethoxylated trimethylolpropane triacrylate. Trimethylolpropane trimethacrylate.
Tetra to hexa(meth)acrylates: Dipentaerythritol pentaacrylate, pentaerythritol tetraacrylate, ethoxylated pentaerythritol tetraacrylate, pentaacrylate ester, silicone hexaacrylate.
The preferred compounds I are ethylenically unsatured alkoxysilanes which can be, for example, vinylsilanes, allylsilanes, acrylic silanes or methacrylic silanes.
Examples of vinylsilanes are vinyltri(2-methoxyethoxy)silane,
vinyltrisisobutoxysilane, vinyltri-f-butoxysilane, vinyltriphenoxysilane,
vinyltrimethoxysilane, vinyltriisopropoxysilane, vinyltriethoxysilane,
vinyltriacetoxysilane, vinylmethyldiethoxysilane,
vinylmethyldiacetoxysilane, vinylbis(trimethylsiloxy)silane and
vinyldimethoxyethoxysilane.
Examples of allylsilanes are allyltrimethoxysilane, allyltriethoxysilane and allyltris(trimethylsiloxy)silane.
Examples of acrylic silanes are 3-
acryloxypropyltris(trimethylsiloxy)silane, 3-
acryloxypropyltrimethoxysilane, acryloxypropylmethyldimethoxysilane, 3-
acryloxypropylmethylbis(trimethylsiloxy)silane, 3-acryloxypropyl-
dimethylmethoxysilane, n-(3-acryloxy-2-hydroxypropyl)-3-
aminopropyltriethoxysilane.

Examples of methacrylic silanes are 3-methacryloxypropyltris
(vinyldimethoxysiloxy)silane, 3-
methacryloxypropyltris(trimethylsiloxy)silane, 3-
methacryloxypropyltris(methoxyethoxy)silane, 3-
metacryloxypropyltrimethoxysilane, 3-
methacryloxypropylpentamethyldisiloxane, 3-methacryloxypropylmethyl-dimethoxysilane, 3-methacryloxypropylmethyldiethoxysilane, 3-methacryloxypropyl-dimethylmethoxysilane, 3-
methacryloxypropyldimethylethoxysilane, 3-
methacryloxypropenyltrimethoxysilane and 3-
methacryloxypropylbis(trimethylsiloxy)methylsilane.
The preferred silane is acryloxypropyltrimethoxysilane.
Other preferred compounds of formula I are zirconium
methacrylate, titanium trimethacrylate,
methacryloxyethoxytriisopropoxytitanate, titanium methacrylate triisopropoxide, zirconium methacryloxyethyl acetoacetate tri-n-propoxide.
Silica colloids having free ethylenically unsaturated groups are for example: OG-103 silica colloids functionalized with hexanedioldiacrylate.
Among the epoxyalkoxy silanes usable as compounds I there may
be cited y-glycidoxyprolylpentrimethyldisiloxane, y-
glycidoxypropylmethyldiisopropenoxysilane, (y-glycidoxypropyl)-
methyldiethoxysilane, y-glycidoxypropylmethylethoxysilane, y-
glycidoxypropyldiisopropylethoxysilane and (y-glycidoxypropyl)bis-(trimethylsiloxy)methylsilane.
The preferred epoxyalkoxysilane is (y-
glycidoxypropyl)trimethoxysilane.
Examples of useful alkoxysilanes are tetraethoxysilane and methyltrimethoxysilane.
Of course, mixtures of ethylenically unsaturated alkoxysilanes and epoxyalkoxy silanes as above may be used as compounds I.

The (meth)acrylate coating composition can also comprise:
1) Metal alkoxides without ethylenically unsaturated groups, for example tetraethoxysilane (semi-metal), zirconium propoxides, zirconium isopropoxide, , tungsten VI ethoxide, tungsten V ethoxide, titanium n:propoxide, 2- titanium isobutoxide, tantalum V ethoxide, indium methyl trimethyl acetyl acetate, hafnium ethoxide, hafnium butoxide, germanium ethoxide, germanium butoxide, cerium butoxide, antimony butoxide, aluminum butoxide, tungsten ethoxide.
These metal alkoxides enhance the effect of compound I or of the silica or metal colloids having free ethylenically unsaturated groups.
2) Alkoxysilanes.
Examples of useful alkoxysilanes are tetraethoxysilane and methyltrimethoxysilane.
3) Non silane epoxy compounds;
1,4-butanediol diglycidyl ether, bisphenol F epoxy, bisphenol A
epoxy, epoxy phenol novalac, alicyclic diepoxy carbonate. Propylene
glycol glycidyl ether, cycloaliphatic diepoxide, 2,4, oxirane-2-
ylmethoxybutoxymethyl oxirane, 2,2,2-bis oxirane-2-
yloxymethylbutoxyoxirane.
Preferably, the (meth)acrylate based curable coating composition is photocurable, preferably UV curable.
Preferably, the (meth)acrylate based curable coating composition comprises a surfactant that can be covalently bounded to the polymer matrix of the (meth)acrylate based curable composition. This surfactant is preferably an acrylated silicone oligomer and is used in a weight ratio less than 2%, based on the total weight of the composition, preferably in

a weight of 1% or less. Of course, the acrylated silicone oligomers used as surfactant ratio are compounds different from compounds I.
The (meth)acrylate based curable layer can be used as a hard coating that has a thickness of preferably 1 to 6 microns, and better between 2 to 5 microns with a nominal thickness of 3 microns for the ophthalmic lens application.
It may be deposited directly on the surface of a substrate or on a primer coating, preferably an impact resistant primer coating.
Also, the (meth)acrylate based curable layer can be used as a primer layer that has preferably a thickness from 0.5 to 2 microns, and better less than 1.0 microns.
Generally, the anti-soiling coating will have a surface energy of less than 15 mJ/m2, preferably less than 14 mJ/m2 and more preferably less than 13 mJ/m2, and even better less than 12 mJ/m2 and a thickness of 1 to 100 nm, preferably 1 to 60 nm, more preferably 10 to 60 nm. The anti-soiling coating may also be as thin as 1 to 10 nm, preferably 1 to 5 nm.
In the present invention, all surface energies are calculated according to the OWENS-WENDT method described in the following document: "Estimation of the surface forces energy of polymers" OWENS O.K., WENDT R.G. (1969) J. APPL. POLYM, SCI., 13, 1741-1747.
The anti-soiling coating layer may be any classical outer coating in the field of optical lenses and in particular an anti-soiling coating (hydrophobic and/or oleophobic top coat).
The anti-soiling coating layer according to the invention is preferably of organic nature. By organic nature in the present invention, it is meant a layer which is comprised of at least 40% by weight, preferably at least 50% by weight of the total weight of the coating layer of organic materials.

A preferred anti-soiling coating layer is a hydrophobic and/or oleophobic top coat, and preferably such a top coat made from a composition comprising at least one fluorinated compound.
Preferred fluoro compounds are silanes and silazanes bearing at least one group selected from fluorocarbons, polyfluorocarbons, fluoropolyethers and polyfluoropolyethers, in particular perfluoropolyethers.
Fluorocompounds are disclosed, among others, in US-4,410,563, EP-0 203 730, EP-749 021, EP-844 265 and EP-933 377.
Among fluorosilanes there may be cited the compounds of formulae:
n= 5, 7, 9 or 11 and R is an alkyl radical, typically a Ci-C0 alkyl radical such as -CH3, -C2H5 and -C3H7;
n' = 7 or 9 and R is as defined above.
Compositions containing fluoro compounds also useful for making the top coat are disclosed in US 6,183,872.
The silicon-containing organic fluoropolymer is represented by the general formula (I) and has a number average molecular weight of from 5x102to1x105\wherein R represents perfluoroalkyl ; Z represents fluoro or trifluoromethyl ; a, b, c, d and e each independently represent 0 or an integer of 1 or above, provided that a + b + c + d + e is not less than 1 and the order of the repeating units parenthesized by subscripts a, b, c, d and e occurring in the formula is not limited to that shown ; Y represents hydrogen or alkyl containing 1 to 4 carbon atoms ; X represents hydrogen, bromo or iodo ; R1 represents hydroxy or a hydrolyzable substituent group ; R2 represents hydrogen or a monovalent hydrocarbon group ; I represents 0, 1 or 2 ; m represents 1, 2 or 3 ; and n represents an integer of 1 or above, preferably 2 or above.

Other classes of preferred compositions for forming the initial top coat are those containing fluoropolyether groups, in particular polyfluoropolyether groups and in particular perfluoropolyether groups. A particular preferred class of compositions containing fluoropolyether groups is disclosed in US-6,277,485.
The anti-soiling top coats of US-6,277,485 are at least partially cured coatings comprising a fluorinated siloxane prepared by applying a coating composition (typically in the form of a solution) comprising at least one fluorinated silane of the following formula :
wherein : Rf is a monovalent or divalent polyfluoropolyether group, R1 is a divalent alkylene group, arylene group, or combinations thereof, optionally containing one or more heteroatoms or functional groups and optionally substituted with halids, and preferably containing 2 to 16 carbon atoms ; R2 is a lower alkyl group (i.e., a (C-i-C4) alkyl group); Y is a halide, a lower alkoxy group (i.e., a (CrC4) alkoxy group, preferably, a methoxy or ethoxy group), or a lower acyloxy group (i.e., -OC(O)R3 wherein R3 is a (CrC/O alkyl group) ; x is 0 or 1 ; and y is 1 (Rf is monovalent) or 2 (Rf is divalent). Suitable compounds typically have a molecular weight (number average) of at least about 1000. Preferably, Y is a lower alkoxy group and Rf is a perfluoropolyether group.
A commercial composition for making the top coat is the composition KP801M® commercialized by SHINETSU, or the Optool DSX® product from DAI KIN.
Generally, the anti-soiling coating layer of the coated lens has a thickness ranging from 1 to 100 nm, preferably 1 to 60 nm, more preferably 1 to 5 nm.

The deposition techniques for such anti-soiling coating layers are very diverse, including liquid phase deposition such as dip coating, spin coating (centrifugation). Of which, deposition by dip coating is preferred.
Preferably a plasma or corona treatment may be used for increasing the adhesion between the first and the second layer.
The lens substrate can be made from any material used in the optical field, such as mineral or organic glass, preferably an organic glass.
Examples of such lens substrates are:
- diethylene glycol bis(allylcarbonate) polymers and copolymers
based substrates ;
- (meth)acrylic polymers and copolymers based substrates, such
as substrates comprising (meth)acrylic polymers and copolymers derived
from bisphenol-A ;
- thio(meth)acrylic polymers and copolymers based substrates ;
- polythiourethane polymers and copolymers based substrates ;
- epoxy and/or episulfide polymers and copolymers based
substrates ; and
- polycarbonate based substrates.
In all the examples below the first based methacrylic coating was treated by corona discharge prior to deposition of the second coating having anti-soil properties.
EXAMPLES
EXAMPLE 1 (Comparative): This coating formulation is used as a reference for a typical UV curable coating.
A coating formulation consisted of:

(Table Removed)
12.01 grams of diethylene glycol diacrylate were poured in
a tube vial.
1- 12.01 grams of dipentaerythritol pentaacrylate were added
to diethylene glycol diacrylate while mixing. Then the blend was mixed for
30 minutes.
2- 0.13 grams of Ebecryl 1360 were added to the previous
blend while mixing. Then the blend was mixed for 30 minutes.
3- 0.49 grams of Irgacure 500 were added to the previous
blend while mixing. Then the blend was finally mixed for 30 minutes.
Coating was spin coated on a polycarbonate lens 10 seconds at speed 4000 rpm and cured via Lesco system H+ U.V. Bulb during 2 times 35 seconds.
The same coating was spin coated on a CR-39® lens 10 seconds at speed 4000 rpm and cured via Lesco system H+ U.V. Bulb during 2 times 35 seconds.
Next, the coated sample was treated with a fluorinated anti soiling agent (Optool DSX® from DAIKIN).
Subsequently, the sample was cured for 1 hour at 50°C.

EXAMPLE 2:
Acryloxypropyl trimethoxysilane is added to a UV curable acrylic coating.
(Table Removed)
Preparation of the coating composition:
1- 38.99 grams of acryloxypropyltrimethoxysilane were poured
in a beaker.
2- 9.00 grams of hydrochloric acid solution at 0.1 mole.L"1
were slowly added to acryloxypropyltrimethoxysilane while mixing. Then
the hydrolysis was stopped after 2 hours.
3- 59.99 grams of diethylene glycol diacrylate were added
while mixing. Then this blend was mixed for 30 minutes.
4- 60.01 grams of dipentaerythritol pentaacrylate were added
while mixing. Then this blend was mixed for 30 minutes.
5- 0.58 grams of Ebecryl 1360 were added while mixing. Then
this blend was mixed for 30 minutes.
6- 2.45 grams of Irgacure 500 were added while mixing. Then
the blend was finally mixed for 30 minutes.
Coating was spin coated on a polycarbonate lens 10 seconds at speed 4000 rpm and cured via Lesco system H+ U.V. Bulb during 2 times 35 seconds.
The same coating was spin coated on CR-39® lens 10 seconds at speed 4000 rpm and cured via Lesco system H+ U.V. Bulb during 2 times 35 seconds.
Next, the coated lens was treated with a fluorinated top coating Optool (DSX) solution by dip coating.
Subsequently the treated lenses were cured for 50 minutes at 100°C.
EXAMPLE 3:
Functionalized particles of acrylated colloid silica are added to a UV curable acrylic coating.
A UV curable coating formulation that consisted of:
(Table Removed)
Preparation of the coating composition:
1- 7.79 grams of acrylated colloid silica (OG 103-31) were poured
in a beaker.
2- 12.01 grams of diethylene glycol diacrylate were added while
mixing. Then this blend was mixed for 30 minutes.
3- 11.99 grams of dipentaerythritol pentaacrylate were added while
mixing. Then this blend was mixed for 30 minutes.
4- 0.12 grams of Ebecryl 1360 were added while mixing. Then this
blend was mixed for 30 minutes.
5- 0.49 grams of Irgacure 500 were added to the previous blend.
Then the blend was finally mixed for 30 minutes.
Coating was spin coated on a polycarbonate lens 10 seconds at speed 4000 rpm and cured via Lesco system H+ U.V. Bulb during 2 times 35 seconds.
The same coating was spin coated on CR-39® lenslO seconds at speed 4000 rpm and cured via Lesco system H+ U.V. Bulb during 2 times 35 seconds.
Next, the sample was coated with a fluorinated anti-soiling agent ( Optool DSX® from DAIKIN) top coating solution by dip coating
Subsequently, the samples were cured for 1 hour at 50°C.
EXAMPLE 4:
A hybrid of organic silane is added to a UV curable acrylic coating. This hybrid additive is designed to be subsequently reacting with the DSX and form a strong bond through silanol condensation.
A UV curable coating formulation that consisted of:
(Table Removed)

Preparation of the coating composition:
1- 38.99 grams of acryloxypropyltrimethoxysilane were poured in a beaker.
2- 9.00 grams of hydrochloric acid solution at 0.1 mole.L"1 were slowly
added to acryloxypropyltrimethoxysilane while mixing. Then, the
hydrolysis was stopped after 2 hours.
3- 59.99 grams of diethylene glycol diacrylate were added while mixing.
Then this blend was mixed for 30 minutes.
4- 60.01 grams of dipentaerythritol pentaacrylate were added while
mixing. Then this blend was mixed for 30 minutes.
5- 0.58 grams of Ebecryl 1360 were added while mixing. Then this blend
was mixed for 30 minutes.
6- 2.45 grams of Irgacure 500 were added to the previous blend while
mixing. Then the blend was finally mixed for 30 minutes.
Coating was spin coated on a polycarbonate lens 10 seconds at speed 4000 rpm and cured via Lesco system H+ U.V. Bulb during 2 times 35 seconds.
The same coating was spin coated on CR-39® lens 10 seconds at speed 4000 rpm and cured via Lesco system H+ U.V. Bulb during 2 times 35 seconds.
Next, the coated lens was treated with a fluorinated material Optool DSX® from DAIKIN by dip coating method.
Subsequently the treated lenses were cured for 1 minute at 70°C by infra-red heater.
EXAMPLE 5:
A hybrid of organic silane is added to a UV curable acrylic coating. This hybrid additive is designed to be subsequently reacting with the DSX and form a strong bond through silanol condensation.
A UV curable coating formulation that consisted of:(Table Removed)
Formulation :
1- 5.90 grams of acryloxypropyltrimethoxysilane were poured in a
beaker.
2- 5.86 grams of glycidoxypropyltrimethoxysilane were poured in a
beaker.
3- 3.15 grams of hydrochloric acid solution at 0.1 mole.L"1 were
slowly added to acryloxypropyltrimethoxysilane and
glycidoxypropyltrimethoxysilane while mixing. Then, the hydrolysis
was stopped after 2 hours.
4- 6.00 grams of diethylene glycol diacrylate were added while
mixing. Then this blend was mixed for 30 minutes.
5- 6.00 grams of dipentaerythritol pentaacrylate were added while
mixing. Then this blend was mixed for 30 minutes.
6- 0.05 grams of Ebecryl 1360 were added while mixing. Then this
blend was mixed for 30 minutes.
7- 0.24 grams of Irgacure 500 were added to the previous blend
while mixing. Then the blend was finally mixed for 30 minutes.
Coating was spin coated on a polycarbonate lens 10 seconds at speed 4000 rpm and cured via Lesco system H+ U.V. Bulb during 2 times 35 seconds.
The same coating was spin coated on a CR-39™ lens 10 seconds at speed 4000 rpm and cured via Lesco system H+ U.V. Bulb during 2 times 35 seconds.
Next, the lenses were coated with a fluorinated solution (0.60% Optool DSX™ within Demnum™ solvent) top coating solution by dip coating technique.
Subsequently the treated lenses were cured for 1 minute at 90°C by infra-red heater.
(Table Removed)
Based on the examples 2 to 4 and comparative example 1, it appears clearly that the contact angle is initially lower in comparative example 1, and moreover that there is a big decrease of the contact angle when the substrates are washed by solvent or treated with a caustic solution for comparative example 1, demonstrating a lower adhesion of the anti-soiling agent.





WHAT IS CLAIMED IS:
1- A substrate having at least one main surface comprising a first coating deposited on said main surface and a second coating having anti-soiling properties deposited and adhering on the surface of said first coating,
- the first coating being a (meth)acrylate based coating and being obtained by polymerizing a polymerizable composition comprising:
i) at least one (meth)acrylate compound and
ii) at least one compound I having at least one - M-Z' bond with M representing Si or a Metal atom, Z' representing OH or a hydrolysable group, and at least one ethylenic unsaturated group or epoxy group,
and/or
iii) at least one silica or metal oxide colloid having free ethylenically unsaturated groups;
and
- the second coating, having anti-soiling properties, being obtained by depositing on said first coating an anti-soiling coating composition comprising at least one compound II, or a hydrolyzate thereof, having at least one - Si-Z" group with Z" representing OH or a hydrolysable group.
2- A substrate according to claim 1, wherein the polymerizable first coating composition comprises at least one metal alkoxide compound that do not contain any reactive unsaturated group.

3- A substrate according to claim 1, wherein compound I is a
colloidal silica having free acryloxy groups.
4- A substrate according to claim 1, wherein the polymerizable first
coating composition comprises from 2 to 50% by weight of compound I.
5- A substrate according to claim 1, wherein the polymerizable first
coating composition comprises from 10 to 40% by weight of compound I.
6- A substrate according to claim 1, wherein the unsaturated
group is a (meth)acryloxy group or a vinyl group.
7- A substrate according to claim 1, wherein the second coating
having anti-soiling properties is hydrophobic and/or oleophobic.
8- A substrate according to claim 1, wherein compound II is a
fluoro compound.
9- A substrate according to claim 3, wherein compound II is a
silane or a silazane bearing at least one group selected from
fluorocarbons, polyfluorocarbons, fluoropolyethers and
polyfluoropolyethers.

10- A substrate according to claim 1, wherein compound II is a
silane comprising polyfluoro polyether groups.
11- A substrate according to claim 1, wherein compound II is
represented by the general formula (I) and has a number average
molecular weight of from 5x102 to 1x105.

wherein Rf represents perfluoroalkyl ; Z represents fluoro or trifluoromethyl ; a, b, c, d and e each independently represent 0 or an integer of 1 or above, provided that a + b + c + d + e is not less than 1 and the order of the repeating units parenthesized by subscripts a, b, c, d and e occuring in the formula is not limited to that shown ; Y represents hydrogen or alkyl containing 1 to 4 carbon atoms ; X represents hydrogen, bromo or iodo ; R1 represents hydroxy or a hydrolyzable substituent group ; R2 represents hydrogen or a monovalent hydrocarbon group ; I represents 0, 1 or 2 ; m represents 1, 2 or 3 ; and n represents an integer of 1 or above, preferably 2 or above.
12- A substrate according to claim 1, wherein the second coating having anti-soiling properties is deposited by dip coating or spin coating, preferably by dip coating.
13- A coating composition comprising:
i) at least one (meth)acrylate compound and
ii) at least one compound I having
at least one - M-Z' bond with M representing Si or a Metal atom, Z' representing OH or a hydrolysable group,
and at least one ethylenic unsaturated group or epoxy group
and/or
iii) at least one silica or metal oxide colloid having free ethylenically unsaturated groups.

Documents:

3177-delnp-2007-Abstract-(28-05-2013).pdf

3177-delnp-2007-abstract.pdf

3177-delnp-2007-Claims-(01-10-2013).pdf

3177-delnp-2007-claims.pdf

3177-delnp-2007-Correspondence Others-(01-10-2013).pdf

3177-delnp-2007-Correspondence Others-(08-04-2013).pdf

3177-delnp-2007-Correspondence Others-(28-05-2013).pdf

3177-delnp-2007-Correspondence-Others-(10-03-2014).pdf

3177-delnp-2007-correspondence-others.pdf

3177-delnp-2007-description (complete).pdf

3177-delnp-2007-form-1.pdf

3177-delnp-2007-form-2.pdf

3177-delnp-2007-Form-3-(01-10-2013).pdf

3177-delnp-2007-Form-3-(08-04-2013).pdf

3177-delnp-2007-form-3.pdf

3177-delnp-2007-Form-5-(28-05-2013).pdf

3177-delnp-2007-form-5.pdf

3177-delnp-2007-GPA-(28-05-2013).pdf

3177-delnp-2007-pct-210.pdf

3177-delnp-2007-pct-304.pdf

3177-delnp-2007-pct-308.pdf

3177-delnp-2007-Petition-137-(10-03-2014).pdf

3177-delnp-2007-Petition-137-(28-05-2013).pdf


Patent Number 259355
Indian Patent Application Number 3177/DELNP/2007
PG Journal Number 11/2014
Publication Date 14-Mar-2014
Grant Date 10-Mar-2014
Date of Filing 27-Apr-2007
Name of Patentee ESSILOR INTERNATIONAL (COMPAGNIE GENERALE D'OPTIQUE)
Applicant Address 147 RUE DE PARIS, 94227 CHARENTON CREDEX,FRANCE,
Inventors:
# Inventor's Name Inventor's Address
1 HOA THIEN DANG 4900 PARK STREET, NORTH ST PETERSBURG, FLORIDA 33709, USA.
2 YANNICK MOYSAN 4900 PARK STREET NORTH ST PETERSBURG, FLORIDA 33709, USA.
PCT International Classification Number C09D 4/00
PCT International Application Number PCT/EP2005/011415
PCT International Filing date 2005-10-21
PCT Conventions:
# PCT Application Number Date of Convention Priority Country
1 60/621,142 2004-10-22 U.S.A.