Title of Invention	A CRACKING CATALYST AND A PROCESS FOR PREPARING THE SAME
Abstract	A cracking catalyst, which contains alumina, phosphorus and molecular sieve, with or without clay, wherein said alumina is n-alumina or a mixture of n-alumina and x-alumina and/or y-alumina, and wherein the catalyst contains, on the basis of the total amount of the catalyst, 0.5-50wt% of n-alumina, 0-50wt% of x-alumina and/or y-alumina, 10-70wt% of molecular sieve, 0-75wt% of clay, and 0.1-8wt% of phosphorus, measured as P2O5. The catalyst not only has higher cracking activity and higher cracking ability for cracking heavy oil, but also improves significantly quality and yield of gasoline, LCO and LPG in cracking products.

Title of Invention

A CRACKING CATALYST AND A PROCESS FOR PREPARING THE SAME

Abstract

A cracking catalyst, which contains alumina, phosphorus and molecular sieve, with or without clay, wherein said alumina is n-alumina or a mixture of n-alumina and x-alumina and/or y-alumina, and wherein the catalyst contains, on the basis of the total amount of the catalyst, 0.5-50wt% of n-alumina, 0-50wt% of x-alumina and/or y-alumina, 10-70wt% of molecular sieve, 0-75wt% of clay, and 0.1-8wt% of phosphorus, measured as P2O5. The catalyst not only has higher cracking activity and higher cracking ability for cracking heavy oil, but also improves significantly quality and yield of gasoline, LCO and LPG in cracking products.

Full Text	Specification A cracking catalyst and a process for preparing the same Field of the Invention The present invention relates to a cracking catalyst used in oil refining and a process for preparing the catalyst. Description of the Related Art The trend of catalytic cracking stocks becoming heavier and heavier is so increasingly severe that higher cracking ability of the cracking catalyst and cracking process has to be required in order to realize an object of production of more light oil (gasoline and diesel oil) and liquefied petroleum gas. With regard to fluidized catalytic cracking (FCC) gasoline, olefins, aromatics and isoparaffins are main contributors of octane number. However, decreasing the olefin content of FCC gasoline is required due to environmental protection. In order to offset the loss of octane number caused by decreasing the olefin content, increasing the content of isoparaffins and aromatics in gasoline is required. Thus, there is a need of developing a cracking catalyst and a cracking process that are able to produce gasoline having lower content of olefin but higher content of aromatics and isoparaffins. Meantime, the quality of catalytic cracking diesel oil needs also to be improved, because the diesel oil obtained by using the existing cracking catalyst and process has a lower aniline point, a higher density and a lower cetane number. Thus, there is a need of developing a cracking catalyst and a cracking process that have relatively high cracking ability of heavy oil and are able to decrease the density of diesel oil and increase aniline point and cetane number thereof. Furthermore, light olefins and isobutane contained in the liquefied petroleum gas from a catalytic cracking are feedstocks of basic organic chemical industries. Currently, the supply of the light olefins (especially propylene) and isobutane falls short of demand. However, the content of light olefins (especially propylene) and isobutane is lower in the liquefied petroleum gas products from the existing cracking catalysts and processes. Thus, there is a need of developing a novel cracking catalyst and a cracking process that can be used to produce the cracking product containing more light olefins (especially propylene) and isobutane in the liquefied petroleum gas. CN 1042201C discloses a cracking catalyst for the production of more C3-Cs olefins. The catalyst consists of 10-50wt% of the zeolite-Y having a unit cell size^ 2.45nm, 2-40wt% of ZSM-5 zeolite modified with element selected from the group consisting of P, RE and H, and 20-80wt% of a semisynthetic matrix of kaolin and alumina binder. CN 1055301C discloses a cracking catalyst for the production of more iso-olefins and gasoline. The catalyst consists of 5-70wt% of a composite aluminum-base alumina binder that is made up with pseudo-boehmite and alumina sol in a weight-ratio of from 1:9 to 9:1, 5-65wt% of clay and 23-50wt% of molecular sieve. Wherein said molecular sieve is a mixture consisting of 15-82wt% of the zeolite-Y and the balance of a rare earth-containing pentasil high silica zeolite containing 0-10wt% of phosphorus(measured as P2O5) and/or HZSM-5 zeolite. CN 1072201A discloses a catalyst for the conversion of hydrocarbons to produce light olefins and gasoline with high octane number. The catalyst consists of 10-40wt% of three zeolites i.e. zeolite ZSM-5, zeolite REY and a high silica zeolite-Y, and the balance of a synthetic matrix or a semisynthetic marix containing 10-40wt% of silica and/or alumina binder. Wherein the amount of the zeolite ZSM-5 is 3-50wt%, and the amounts of the zeolite REY and the high silica zeolite-Y are each of 12-7 5wt%. CN1085825A discloses a catalyst for the conversion of hydrocarbons to produce-propylene, butene and gasoline with high octane number. The catalyst consists of 10-40wt% of three zeolites i.e. zeolite ZRP, zeolite REY and high silica zeolite-Y, and the balance of a-synthetic matrix or a semisynthetic matrix containing 10-40wt% of silica and/or alumina binder. Wherein the amount of the zeolite ZRP is 3-50wt%, and the amounts of zeolite REY and the high silica zeolite-Y are each of 12-75wt%. CN 1325940A discloses a phosphorus-containing catalyst for cracking hydrocarbons. The catalyst consists of 10-60wt% of a zeolite-Y or the zeolite-Y together with a MFI-structured zeolite and/or zeolite-p, 0-75wt% of clay, 10-60wt% of two kinds of alumina, and 0.1-7.0wt% of phosphorus measesred as P2OS, and 0-20wt% of rare earth measured as RE2O3. Said two kinds of alumina are from pseudo-boehmite and alumina sol, respectively. Although the catalyst has higher ability for the conversion of heavy oil and makes the olefin content lower in gasoline product, the use of the catalyst cannot improve the quality of the catalytic cracked diesel oil and cannot increase the content of light olefins and isobutane in the liquefied petroleum gas. CN 13 54224A discloses a catalytic cracking catalyst for producing isoparaffins-rich gasoline, propylene and isobutane. The catalyst consists of 0-70wt% of clay, 5-90wt% of inorganic oxides and l-50wt% of molecular sieve, wherein the molecular sieve is a mixture including (1) 20-75wt% of a high silica zeolite-Y having a SiO2/Al2O3 ratio of 5-15 and a rare earth content of 8-20wt% measured as RE2O3, (2) 20-75wt% of a high silica zeolite-Y having a SiO2/Al2O3 ratio of 16-50 and a rare earth content of 2-7wt% measured as RE2O3, and (3) l-50wt% of zeolite-0 or mordenite or zeolite-ZRP Alumina is a component included generally in cracking catalysts. In the prior art, alumina is mostly from alumina monohydrate and alumina sol, wherein alumina monohydrate includes boehmite and pseudo-boehmite. During calcination for preparing the catalyst, boehmite, pseudo-boehmite and alumina sol are converted all into y-alumina. Therefore, the alumina contained in catalysts aforementioned in the prior art is all y-alumina. Alumina may be also from alumina trihydrate. Alumina trihydrate includes a-alumina trihydrate, P-alumina trihydrate (Bayerite) and-Nordstrandite. During the preparation of catalyst, a-alumina trihydrate is converted into x-alumina, and p-alumina trihydrate is converted into T\|-alumina.-Nordstrandite is only existence in nature, but there is no way to obtain by artificial synthesis. CN 1388214A discloses a process for preparing fluid cracking catalysts by drying a mixture of cracking catalyst components including clay, alumina and molecular sieve, wherein said catalyst contains 1.5-55wt% of alumina that is from \|3-alumina trihydrate. Although said catalyst has higher activity for cracking heavy oil and better selectivity for light oil, it is not able to decrease the olefin content of gasoline, nor is able to improve the quality of catalytic diesel oil and increase the content of light olefins and isobutane in the liquefied petroleum gas. Summary of the invention An object of the present invention is to provide a novel catalyst for cracking hydrocarbons. Said catalyst has higher ability for cracking heavy oil, and results in cracking products with lower olefin content of gasoline, higher quality of diesel oil, and higher contents of light olefins and isobutane of the liquefied petroleum gas. Although there are some examples in the prior art wherein alumina trihydrate is introduced in the preparation of cracking catalyst, it is used simply to increase cracking ability of cracking catalyst without effect on quality of gasoline, diesel oil and liquefied petroleum gas in the cracking products. The inventor of the present invention has unexpectedly found that when the alumina formed with alumina trihydrate, especially p-alumina trihydrate, and phosphorus, i.e. T)-alumina and phosphorus are introduced simultaneously into the cracking catalyst, a peculiar synergistic effect occurs that not only the cracking ability of the cracking catalyst can be increased, but also the quality of gasoline, diesel oil and liquefied petroleum gas can be substantially improved in the cracking products. The catalyst according to the present invention contains alumina, phosphorus and molecular sieve, with or without clay, wherein said alumina is Ti-alumina or a mixture of T\|-alumina and %-alumina and/or y-alumina. The catalyst contains, on the basis of total amount of the catalyst, 0.5-50wt% of r\|-alumina, 0-50wt% of x-alumina and/or y-alumina, 10-70wt% of the molecular sieve, 0-75wt% of clay, and 0.1-8wt% of phosphorus, measured as P2O5. Said molecular sieve is one or more selected from the group consisting of zeolite and non-zeolitic molecular sieve as an active component of the cracking catalyst. These zeolite and non-zeolitic molecular sieve are well known for one skilled in the art. Said zeolite is preferably one or more selected from-arge pore zeolite and medium pore zeolite. Said large pore zeolite is one having a porous structure with ring open-pore in diameter of at least 0.7 nanometers(nm), such as one or more selected from the group consisting of faujasite, zeolite-P and mordenite, especially a zeolite-Y, the zeolite-Y containing one or more elements selected from phosphorus, iron and rare earths, an ultrastable zeolite-Y, the ultrastable zeolite containing one or more elements selected from phosphorus, iron and rare earths, and zeolite-p. Said medium pore zeolite is one having a porous structure with ring open-pore in diameter of from higher than 0.56nm to less than 0.7nm, such as one or more selected from a MFI-structured zeolite (e.g. ZSM-5 zeolite), the MFI-structured zeolite containing one or more elements selected from phosphorus, iron and rare earths (e.g. ZSM-5 zeolite containing phosphorus, iron and/or rare earths, and the MFI-structured zeolite containing phosphorus disclosed in CN 1194181A). Said non-zeolitic molecular sieve refers to one or more molecular sieve in which part of or all aluminum and/or silicon are substituted by other elements such as phosphorus, titanium, gallium and germanium. Examples of these molecular sieves include one or more selected from silicates having different SiO2/Al2O3 ratio (e.g. metallosilicate, titanosilicates), metalloaluminate (e.g. germanium aluminates), metallophosphates, aluminophosphates, metalloaluminophosphates, metal integrated silicoaluminophosphates (MeAPSO and ELAPSO), silicoaluminophosphates (SAPO molecular sieve), and gallogermanates. SAPO molecular sieve is preferred, such as one or more selected from the group consisting of SAPO-11 molecular sieve, SAPO-34 molecular sieve and SAPO-37 molecular sieve. Preferably, said molecular sieve is one or more selected from the group consisting of a zeolite-Y, the zeolite-Y containing phosphorus, iron and/or rare earths, an ultrastable zeolite-Y, the ultrastable zeolite-Y containing phosphorus, iron and/or rare earths, zeolite-p\ the MFI-structured zeolite, the MFI structured zeolite containing phosphorus, iron and/or rare earths, and SAPO molecular sieve. More preferred molecular sieve is a zeolite mixture containing the zeolite-Y and the MFI-structured zeolite, the content of the zeolite-Y is 30-90wt%, the content of the MFI-structured zeolite is 10-70wt%, based on the total amount of said zeolite mixture. Preferred catalyst includes further 0.1-2wt% of rare earth metal (measured as oxide). The process for preparing the catalyst according to the present invention comprises drying the slurry containing aluminum compound, molecular sieve and water, with or without clay, wherein said aluminum compound is one that is able to form t\|-alumina, or a mixture of an aluminum compound able to form TI-alumina and an aluminum compound able to form x-alumina and/or y-alumina, and then calcining the slurry followed adding further a phosphorus compound. Each component is used in such an amount that the final catalyst contains, based on the total amount of the catalyst, 0.5-50wt% of Ti-alumina, 0-50wt% of X-alumina and/or y-alumina, 10-70wt% of molecular sieve, 0-75wt% of clay and 0.1-8wt% of phosphorus, measured as P2O5. The catalyst according to the present invention not only has higher cracking activity, but also substantially improves the quality of gasoline, diesel oil and liquefied petroleum gas, as showed that the gasoline has a lower content of olefins, a higher content of aromatics and isoparaffins, that the diesel oil has a lower density and a higher cetane number, and that the liquefied petroleum gas has a higher content of light olefins, especially the content of propylene and isobutane. The catalyst has further advantages such as high ability for cracking heavy oil, and capability of producing more light oils (gasoline and diesel oil) and the liquefied petroleum gas. Detailed Description of the Inventing The catalyst provided according to the process of the present invention contains alumina, phosphorus and molecular sieve, with or without clay, wherein said alumina is n-alumina or a mixture of ^-alumina and x-alumina and/or y-alumina, and wherein the catalyst contains, based on the total amount of the catalyst, 0.5-50wt%, preferably 5-45wt% of Ti-alumina, 0-50wt%? preferably 0-40wt% of x-alumina and/or y-alumina, 10-70wt%, preferably 20-50wt% of molecular sieve, 0-75wt%, preferably 0-60wt% of clay and 0.1-8wt%, preferably 0.5-6wt% of phosphorus, measured as P2O5. (The catalyst according to the present invention may further contain 0.1-2wt%, preferably 0,2-1.8wt% of rare earth metal (measured as oxide). Said molecular sieve is one or more selected from the group consisting of zeolite and non-zeolitic molecular sieve that they are used as active component of cracking catalyst. These zeolite and non-zeolitic molecular sieve are well known for one skilled in the art. Said zeolite is preferably one or more selected from large pore zeolite and medium pore zeolite. Said large pore zeolite is a zeolite having a porous structure with ring open-pore in diameter at least 0.7 nm, such as one or more selected from faujasite, zeolite-p and mordenite, especially, one or more selected from a zeolite-Y, the zeolite-Y containing one or more elements selected from phosphorus, iron and rare earth, an ultrastable zeolite-Y, the ultrastable zeolite containing one or more selected from phosphorus, iron and rare earths, a zeolite-HY, the zeolite-HY containing one or more elements selected from phosphorus, iron and rare earths, and zeolite-p. Said medium pore zeolite is a porous structure zeolite having ring open-pore of from higher than 0.56 run to less than 0.7 nm, such as the MFI-structured zeolite (e.g. ZSM-5 zeolite), the MFI-structured zeolite containing one or more elements selected from phosphorus, iron and rare earths (such as ZSM -5 zeolite containing one or more elements selected from phosphorus, iron and/or rare earths, and MFI-structured zeolite containing phosphorus, as disclosed in CN 1194181 A). Said non-zeolitic molecular sieve refers to one or more molecular sieve in which part of or all aluminum and/or silicon are substituted by other elements such as phosphorus, titanium, gallium and germanium. Examples of these molecular sieves include one or more selected from silicates having different SiO2/Al2O3 ratio (e.g. metallosilicate, titanosilicates), metalloaluminate (e.g. germanium aluminates), metallophosphates, aluminophosphates, metalloaluminophosphates, metal integrated silicoaluminophosphates (MeAPSO and ELAPSO), silicoaluminophosphates (SAPO molecular sieve), and gallogermanates. SAPO molecular sieve is preferred, such as one or more selected from the group consisting of SAPO-11 molecular sieve, SAPO-34 molecular sieve and SAPO-37 molecular sieve. Preferably, said molecular sieve is one or more selected from the group consisting of a zeolite-Y, the zeolite-Y containing one or more selected from phosphorus, iron and/or rare earths, an ultrastable zeolite-Y, the ultrastable zeolite-Y containing one or more selected from phosphorus, iron and/or rare earths, a zeolite-HY, the zeolite-HY containing one or more selected from phosphorus, iron and rare earths, zeolite-P, a MFI-structured zeolite, the MFI-structured zeolite containing one or more selected from phosphorus, iron and rare earths, and SAPO molecular sieve. More preferred molecular sieve contains a zeolite mixture of a zeolite-Y and the MFI-structured zeolite, wherein the content of the zeolite-Y is 30-90wt%, preferably 40-85wt%, and the content of the MFI-structured zeolite is 10-70wt%, preferably 15-60wt%, based on the total amount of said zeolite mixture. Said clay is one or more selected from clays that are used as active component of cracking catalyst, such as one or more selected from kaolin, halloysite, montmorillonite, kieselguhr, allokite, soapstone, rectorite, sepiolite, attapulgus, hydrotalcite, and bentonite. More preferred clay is one or more selected from kaolin, montmorillonite, kieselguhr, rectorite, sepiolite and attapulgus. These clays are well known for one skilled in the art. The catalyst according to the present invention may further contain non-alumina refractory inorganic oxide. Said non-alumina refractory inorganic oxide is one or more selected from the group consisting of non-alumina refractory inorganic oxides that are used as matrix of cracking catalyst, such as silica, amorphous silica-alumina, zirconia, titania, boric oxide, oxides of alkaline earth metal. Preferably, it is one or more selected from the group consisting of silica, amorphous silica-alumina, zirconia, titania, magnesia oxide and calcium oxide. The refractory inorganic oxides are well known for one skilled in the art. Based on the total amount of catalyst, the content of said non-alumina refractory inorganic oxide is 0-10wt%, preferably 0-5wt%. In the process for preparing the catalyst according to the present invention, said aluminum compound is one able to form T\|-alumina, or a mixture of an aluminum compound able to form n-alumina and an aluminum compound able to form %-alumina and/or Y-alumina. Said aluminum compound able to form ^-alumina may be any aluminum compound that is able to form T\|-alumina during the preparation of catalyst, preferably p-alumina trihydrate. Said aluminum compound able to form x-alumina may be any aluminum compound that is able to form x-alumina during the preparation of catalyst, preferably a-alumina trihydrate. Said aluminum compound able to form y-alumina may be any aluminum compound that is able to form y-alumina during the preparation of catalyst, preferably boehmite, pseudo-boehmite and/or alumina sol. Said phosphorus compound may be added in any step before calcining, for example, it may be added to a slurry containing the aluminum compound, molecular sieve and water, with or without clay. Or the phosphorus compound may be introduced by impregnating the solids obtained after drying the slurry containing the aluminum compound, molecular sieve and water, with or without clay, then calcining the impregnated product. In the catalyst of the present invention, said phosphorus content is exclusive of phosphorus contained originally in the molecular sieve. Said phosphorus compound includes various compounds of phosphorus, for example, one or more selected from the group consisting of phosphoric acid, phosphates, phosphorous acid, phosphites, pyrophosphoric acid, pyrophosphates, polyphosphoric acids, polyphosphates, metaphosphoric acid and metaphosphates. Preferably, it is one or more selected from the group consisting of phosphoric acid, ammonium phosphate, diammonium hydrogen phosphate, ammonium dihydrogen phosphate, phosphorous acid, ammonium phosphite, sodium pyrophosphate, potassium pyrophosphate, sodium tripolyphosphate, potassium tripolyphosphate, sodium hexametaphosphate, potassium hexametaphosphate. More preferably, it is one or more selected from the group consisting of phosphoric acid, ammonium phosphate, diammonium hydrogen phosphate, ammonium dihydrogen phosphate, phosphorous acid, ammonium phosphite, sodium pyrophosphate, sodium tripolyphosphate, sodium hexametaphosphate. Each component is used in such an amount that the final catalyst contains, based on the total amount of the catalyst, 0.5-50wt% of T\|-alumina, 0-50wt% of %-alumina and/or y-alumina, 10-70wt% of molecular sieve, 0-75wt% of clay, and 0.1-8wt% of phosphorus, measured as P2O5. Preferably, each component is used in such an amount that the final catalyst contains 5-45wt% of Ti-alumina, 0-40wt% of x-alumina and/or y-alumina, 20-50wt% of molecular sieve, 0- 60wt% of clay, and 0.5-6wt% of phosphorus, measured as P2O5. If the catalyst further contains non-alumina inorganic oxides, the non-alumina inorganic oxide or its precursor may be added to the slurry containing the aluminum compound, molecular sieve and water, with or without clay. The precursor of said non-alumina inorganic oxide refers to a substance that is able to form said non-alumina inorganic oxide during the preparation of the catalyst, these precursors of non-aluminum inorganic oxides are well known for one skilled in the art. For example, the precursor of silica may be silica sol, silica gel and/or sodium silicate; the precursor of amorphous silica-alumina may be a silica-alumina sol and/or silica-alumina gel, and the precursor of zirconia, titania, boric oxide and alkaline earth metal oxides may be respective hydroxide thereof. Said non-alumina inorganic oxide and/or its precursor is used in such an amount that the final catalyst contains 0-10wt%, preferably 0-5wt% of the non-alumina inorganic oxide. Conditions of said drying and calcining are those of conventional drying and calcination for cracking catalysts, for example, the drying temperature is from room temperature to 200 °C, preferably 80-180 "C, and the calcination temperature is from higher than 200V to 750°C, preferably 300-600°C, the calcination time is at least 0.1 hrs, preferably 0.1-10hrs, more preferably 0.3-4hrs. As drying method, various existing methods for drying may be used, such as oven-drying, air-drying or spray-drying, preferably oven-drying or spray-drying. The catalyst according to the present invention is suitable for catalytic cracking of petroleum and its various fractions, especially suitable for catalytic cracking of petroleum and its various fractions having a boiling point higher than 330°C, such as one or more selected from atmospheric residuum, vacuum residuum, vacuum gas oil, atmospheric gas oil, straight-run gas oil, light or heavy deasphalted oils from the process of solvent deasphalting, and coker gas oil, in order to produce high-quality of gasoline, diesel oil and liquefied petroleum gas. One of preferred catalysts in the present invention The catalyst contains alumina, phosphorus and molecular sieve, with or without clay. Said alumina is Tj-alumina, or a mixture of T\|-alumina and %-alumina and/or y-alumina. The catalyst contains, based on the total amount of the catalyst, 0.5-50wt%, preferably 5-45wt% of -p-alumina, 0-50wt%, preferably 0-40wt% of %-alumina and/or y-alumina, 0-75wt%, preferably 0-60wt% of clay, 0.1-8wt%, preferably 0.5-6wt% of phosphorus, measured as P2O5, and 10-70wt%, preferably 20-50wt% of molecular sieve. Said molecular sieve is a zeolite mixture containing the zeolite-Y and the MFI-structured zeolite, wherein the content of the zeolite-Y is 30-90wt%, preferably 40-85wt% and the content of the MFI-structured zeolite is 10-70wt%, preferably 15-60wt%, based on the total amount of said zeolite mixture. The process for preparing the preferred catalyst is as follows: The process comprises drying the slurry containing aluminum compound, molecular sieve and water, with or without clay, wherein said aluminum compound is one that is able to form n-alumina, or a mixture of an aluminum compound able to form t\|-aluminaand an aluminum compound able to form %-alumina and/or y-alumina, and then calcining the slurry followed adding further a phosphorus compound. Each component is used in such an amount that the final catalyst contains, based on the total amount of the catalyst, 0.5-50wt%, preferably 5-45wt% of T)-alumina, 0-50wt%, preferably 0-40wt% of %-alumina and/or y-alumina, 0-75wt%, preferably 0-60wt% of clay, 0.1-8wt%, preferably 0.5-6wt% of phosphorus, measured as P2O5, and 10-70wt%, preferably 20-50wt% of molecular sieve. Said molecular sieve is a zeolite mixture containing the zeolite-Y and the MFI-structured zeolite, wherein the content of the zeolite-Y is 30-90wt%, preferably 40-85wt% and the content of the MFI-structured zeolite is 10-70wt%, preferably 15-60wt%, based on the total amount of said zeolite mixture. Said zeolite mixture further contains zeolite-p of which the content is 0-30wt%, preferably 0-20wt%, based on the total amount of said zeolite mixture. The catalyst substantially improves the quality of gasoline and liquefied petroleum gas in cracking products. The second of preferred catalysts according to the present invention The catalyst contains alumina, phosphorus, rare earth metal and molecular sieve, with or without clay. Said alumina is Ti-alumina or a mixture of T\|-alumina and x-alumina and/or y-alumina. The catalyst contains, based on the total amount of the catalyst, 0.5-50wt%, preferably 5-45wt% of n.-alumina, 0-50wt%, preferably 0-40wt% of %-alumina and/or y-alumina, 0-70wt%, preferably 0-60wt% of clay, 0.1-8wt%, preferably 0.5-6wt% of phosphorus, measured as P2O5, 0.1-2wt%, preferably 0.2-1.8wt% of rare earth metal, measured as oxide, and 10-70wt%, preferably 20-50wt% of the molecular sieve. Said molecular sieve molecular sieve is zeolite-Y. The process for preparing the preferred catalyst as follows: The process comprises drying the slurry containing aluminum compound, molecular sieve and water, with or without clay, wherein said aluminum compound is one that is able to form n,-alumina, or a mixture of an aluminum compound able to form Tj-aluminaand an aluminum compound able to form %-alumina and/or 7-alumina, and then calcining the slurry followed adding further a phosphorus compound and a rare earth metal compound. Each component is used in such an amount that the final catalyst contains, based on the total amount of the catalyst, 0.5-50wt%, preferably 5-45wt% of T\|-alumina, 0-50wt%, preferably 0-40wt% of x-alumina and/or y-alumina, 0-70wt%, preferably 0-60wt% of clay, 0.1-8wt%, preferably 0.5-6wt% of phosphorus, measured as P2O5, 0.1-2wt%, preferably 0.2-1.8wt% of rare earth metal, measured as oxide, and 10-70wt%, preferably 20-50wt% of the molecular sieve. Said molecular sieve molecular sieve is zeolite-Y. Said rare earth metal compound is one or more selected from the group consisting of rare earth metal chloride and rare earth metal nitrate. The catalyst has high ability for cracking heavy oil, and thereby can be used to produce more light oils (gasoline and diesel oil) and liquefied petroleum gas. Conditions for using the catalyst according to the present invention are those conventional for cracking reaction. Generally, said cracking conditions include a reaction temperature of 3 50-700 °C, preferably 400-650 °C, a catalyst-oil ratio (a weight-ratio of catalyst to hydrocarbon oil) of 1-20, preferably 2-15. Following Examples intend to illustrate further the present invention. In Examples, the alumina content of (3-alumina trihydrate used is 64wt% (the trihydrate is manufactured by Institute of ShanDong Aluminum Corp.); the alumina content of pseudo-boehmite (manufactured by ShanDong Aluminum Corp) is 62wt% ; the alumina content of alumina sol (manufactured by Qilu Catalyst Factory) is 21.6wt%, the silica content of silica sol (manufactured by Beijing Changhong Chemical Plant) is 12wt%: the solid content of kaolin (manufactured by China Kaolin Corp) is 76wt%; the solid content of montmorillonite (manufactured by Hubei Zhongxiang City Iron Ore Factory) is 80wt%; the phosphorus-containing compound is of chemical purity; the solution of rare earth chloride ( prepared in the laboratory, with a concentration of 219g rare earth oxide/litre, in which La^ accounts for 53.2% of the rare earth oxide, CeO2 accounts for 13.0% of the rare earth oxide, Pr6OH accounts for 13.0% of the rare earth oxide, Nd^ accounts for 20.8% of the rare earth oxide; the solid rare earth chloride is manufactured by Inner Mongolia Baotou Rare earth Factory). In Examples, molecular sieve SAPO-11 was prepared according to the process disclosed in Example 1 of CN 1098214C. In Examples, compositions of various zeolites used are as follows respectively: Zeolite HY (with a Nap content of 1.5wt% and a SiO2/Al2O3 ratio of 5.3) is obtained by ion-exchanging a zeolite NaY (with a NajO content of 13.5wt% and a SiO2/Al2O3 ratio of 5.0, manufactured by Qilu Catalyst Factory) at a temperature of 80 °C for 1 hr in a weight ratio of water : zeolite NaY : solid ammonium chloride of 10:1:1, then filtering and calcining at 550°C for 2hrs, and then exchanging once again by repeating aforementioned steps, then filtering and calcining; Zeolite REY is a zeolite-Y containing rare earths (the content of rare earth oxide is 18.5wt%, in which I^C^ accounts for 53.2wt% of the rare earth oxide, CeO2 accounts for 13.0wt% of the rare earth oxide, Pr6Ou accounts for 13.0wt% of the rare earth oxide, NCI2O3 accounts for 20.8wt% of the rare earth oxide, NajO content is 1.6wt%; the SiO2/Al2O3 ratio is 5.4, the unit cell size is 2.468nm, the zeolite is manufactured by Qilu Catalyst Factory); Zeolite REHY is a zeolite-Y containing rare earths (the content of rare earth oxide is 84wt%, in which La^ accounts for 53.2wt% of the rare earth oxide, CeO2 accounts for 13.0wt% of the rare earth oxide, Pr6Ou accounts for 13.0wt% of the rare earth oxide, Nd2O3 accounts for 20.8wt% of the rare earth oxide, NajO content is 3.7wt%; the SiO2/Al2O3 ratio is 5.6, the unit cell size is 2.46lnm, the zeolite is manufactured by Qilu Catalyst Factory); Zeolite MOY is a zeolite-Y containing phosphorus and rare earths (the content of rare earth oxide is 8.0wt%, in which La^ accounts for 53.2wt% of the rare earth oxide, CeO2 accounts for 13.0wt% of the rare earth oxide, Pr6OM accounts for 13.0wt% of the rare earth oxide, NdjOg accounts for 20.8wt% of the rare earth oxide, Na^ content is 1.3wt%; the phosphorus content is 1.1 wt%, measured as elemental phosphorus, the SiO2/Al2O3 ratio is 5.6, the unit cell size is 2.460nm, the zeolite is manufactured by Qilu Catalyst Factory); Zeolite DASY0 0 is an ultrastable zeolite-Y Q^O content is 1 .Owt%, the SiO2/Al2O3 ratio is 6.8, the unit cell size is 2.446nm, the zeolite is manufactured by Qilu Catalyst Factory); Zeolite DASY20 is an ultrastable zeolite-Y containing rare earths (the content of rare earth oxide is 1.8wt%, in which La^ accounts for 53.2wt% of the rare earth oxide, CeO2 accounts for 13.0wt% of the rare earth oxide, Pr6O,, accounts for 13.0wt% of the rare earth oxide, Nd^ accounts for 20.8wt% of the rare earth oxide, Na^ content is 1.2wt%; the SiO2/Al2O3 ratio is 6.8, the unit cell size is 2.447nm, the zeolite is manufactured by Qilu Catalyst Factory); Zeolite ZSM-5 is a MFI-structured zeolite (NajO content is 0,2wt%, the SiO2/Al2O3 ratio is 60, the zeolite is manufactured by Qilu Catalyst Factory); Zeolite ZRP-1 is a MFI-structured zeolite containing phosphorus and rare earths ( having NajO content of 0.1 wt%, a SiO2/Al2O3 ratio of 30 and a rare earth oxide content of 1.7wt%, in which La2O3 accounts for 53.2wt% of the rare earth oxide, CeO2 accounts for 13.0wt% of the rare earth oxide, Pr6Ou accounts for 13.0wt% of the rare earth oxide, Nd^ accounts for 20.8wt% of the rare earth oxide, the phosphorus content is 1.9wt%, measured as elemental phosphorus, the zeolite is manufactured by Qilu Catalyst Factory); ZSP-1 is a MFI-structured zeolite containing phosphorus and iron (Na^ content is 0.1 wt%; the SiO2/Al2O3 ratio is 30, Fe2O3 content is 1.5wt%, and the phosphorus content is 1,2wt%, measured as elemental phosphorus, the zeolite is manufactured by Qilu Catalyst Factory); Zeolite-p has a Nap content of 3.2wt% and a SiO2/Al2O3 ratio of 28, the zeolite is manufactured by Qilu Catalyst Factory. Aforesaid SiO2/Al2O3 ratios all refers to the molar ratio of silica and alumina. Examples 1-6 Following examples illustrate the catalysts according to the present invention and the process for preparing the same. Catalysts C1-C6 according to the present invention were obtained by mixing and slurrying p-alumina trihydrate or a mixture of P-alumina trihydrate and pseudo-boehmite, molecular sieve, phosphorus compound and water (with or without clay), spray-drying the resulting slurry into particles of 40-150 microns in diameter, then calcining the resulting particles. The amount of the J3-alumina trihydrate and pseudo-boehmite used, the kind and amount of clay used, and the kind and amount of the molecular sieve used, the kind and amount of the phosphorus compound used are shown respectively in Tables 1-4. The spray-drying temperature, calcination temperature and time are shown in Table 5. The compositions of catalysts C1-C6 are shown in Table 6. Comparative Example 1 This comparative example illustrates the reference catalyst having no phosphorus added and the process for preparing the reference catalyst The reference catalyst CB1 was prepared by the same process as Example 1, except that no phosphorus compound was added and different amount of clay was used. The amount of thep-alumina trihydrate and pseudo-boehmite used, the kind and amount of the clay used, and the kind and amount of the molecular sieve used are shown respectively in Tables 1-4. The spray-drying temperature, calcination temperature and time are shown in Table 5. The composition of the reference catalyst CB1 is shown in Table 6. Comparative Example 2 This comparative example llustrates the reference catalyst containing no T\|-alumina and the process for preparing the reference catalyst. The reference catalyst CB2 was obtained by the same process as Example 1, except that pseudo-boehmite was used instead of \|3-alumina trihydrate. The amount of the pseudo-boehmite used, the kind and amount of the clay used, the kind and amount of the molecular sieve used, and the kind and amount of the phosphorus compound used are shown respectively in Tables 1-4. The spray-drying temperature, calcination temperature and time are shown in Table 5. The composition of the reference catalyst CB2 is shown in Table 6. Example 7 This Example illustrates the catalyst according to present invention and the process for preparing the same. The catalystC7 was obtained by mixing and slurrying 93.8kg p-alumina trihydrate, 72.6kg pseudo-boehmite, 54kg DASY20 molecular sieve, 30kg ZRP-1 molecular sieve, 6kg SAPO-11 molecular sieve, 126.3kg kaolin and 50kg silica sol and deionized water, spray-drying the resulting slurry at temperature 180°C into particles of 40-150 microns in diameter, impregnating Following examples illustrate the catalytic performances of the catalysts provided in the present invention. The catalysts C1-C6 were aged with 100% steam at 800 °C for 8 hrs, respectively. The catalytic cracking of 1 # feedstock oil as shown in Table 7 was carried out in an ACE unit with 9g of inventory of each aged catalysts C1-C6. Reaction conditions and reaction results are shown in Table 8. Wherein, Conversion = Dry gas yield + Liquefied petroleum gas yield + Gasoline yield + Coke yield; Total liquid products yield = Liquefied petroleum gas yield + Gasoline yield + Diesel oil yield. Herein, gasoline refers to a C5 fraction to a fraction with a distillation temperature of 22TC. Diesel oil(LCO) refers to a fraction with a boiling point of from 221°C to 343 °C. Liquefied petroleum gas (LPG) refers to a C3-C4 fraction. Dry gas is a fraction of H2 - C2. Comparative Examples 3-4 Following comparative examples illustrate the catalytic performance of reference catalysts. With the same process as Example 9, the catalysts were aged, and the catalytic cracking of the same feedstock oil was carried out under the same condition, except that the catalyst used was the reference catalysts CB1 and CB2 prepared in Comparative Example 1 and Comparative Example 2, respectively. Reaction conditions and reaction results are shown in Table 8. It can be seen from the results shown in Table 8 that, as compared with the reference catalysts, using the catalyst according to the present invention to carry out catalytic cracking of the same feedstock oil results in not only substantial increase of the conversion of feedstock and Total liquid products yield, but also substantial decrease of the olefin content of gasoline, increase of the content of aromatics and isoparaffins in gasoline, decrease of the density and increase of the aniline point and cetane number of the LCO, and substantial increase of the content of light olefins (especially propylene) and isobutane in LPG. The results shown in Table 10 indicate similarly that, as compared with those in the prior art, the catalyst according to the present invention has not only higher cracking activity, but also results in higher quality of gasoline, LCO and LPG in cracking products. Examples 17-22 Following examples illustrate the first kind of preferred catalysts according to the present invention and the process for preparing the same. Catalysts C9-C14 according to the present invention were obtained by mixing and slurrying p-alumina trihydrate or a mixture of p-alumina trihydrate and pseudo-boehmite, molecular sieve, phosphorus compound and water (with or without clay), then spray-drying the resulting slurry into particles of 40-150 microns in diameter, and then calcining the resulting particles. The catalyst C14 was obtained according to the process of Example 22 by using alumina sol instead of pseudo-boehmite in Example 21. The amount of the p-alumina trihydrate and pseudo-boehmite (or alumina sol) used, the kind and amount of the clay used, and the kind and amount of the molecular sieve used, the kind and amount of the phosphorus compound used are shown respectively in Table 11-14. The spray-drying temperature, calcination temperature and time are shown in Table 15. The compositions of catalysts C9-C14 are shown in Table 16. Comparative Example 5 This comparative example illustrates the reference catalyst containing no phosphorus and the process for preparing the reference catalyst. The reference catalyst CB3 was obtained by the same process as Example 17, except that no phosphorus compound was added and different amount of clay was used. The amount of the p-alumina trihydrate and pseudo-boehmite used, the kind and amount of the clay used, the kind and amount of the molecular sieve used are shown in Table 11-14, respectively. The spray-drying temperature, calcination temperature and time are shown in Table 15. The composition of the reference catalyst CB3 is shown in Table 16. Comparative Example 6 This comparative example illustrates the reference catalyst containing no Ti-alumina and the process for preparing the reference catalyst. The reference catalyst CB4 was obtained by the same process as Example 17, except that pseudo-boehmite instead of p-alumina trihydrate was used. The amount of the pseudo-boehmite used, the kind and amount of the clay used, the kind and amount of the molecular sieve used, the kind and amount of the phosphorus compound used are shown in Table 11-14, respectively. The spray-drying temperature, calcination temperature and time are shown in Table 15. The composition of the reference catalyst CB4 is shown in Table 16. respectively. The catalytic cracking of 1 # feedstock oil as shown in Table 7 was carried out in an ACE unit with 9g of each aged catalysts C9-C14. Reaction conditions and reaction results are shown in Table 17. Wherein, Conversion = Dry gas yield + LPG yield + Gasoline yield + Coke yield; Total liquid products yield = LPG yield + Gasoline yield + LCO yield. Herein, gasoline refers to a fraction with a distillation range of C5-221 °C, LCO refers to a fraction with a boiling range of from 221 °C to 343 °C, LPG refers to a C3-C4 fraction, dry gas is a fraction of H2 - C2. Comparative Examples 7-8 Following comparative examples illustrated catalytic performances of reference catalysts. With the same process as Example 23, the catalyst was aged, and the catalytic cracking of the same feedstock oil was carried out at the same condition, except that catalyst used was the reference catalysts CB3 and CB4 said in Comparative Example 5 and Comparative Example 6, respectively. Reaction conditions and reaction results are shown in Table 17. It can be seen from results shown in Table 17 that, as compared with the results obtained by using the reference catalysts, using the catalyst according to the present invention to carry out catalytic cracking of the same feedstock oil results in significantly decreasing the olefm content of gasoline, increasing the content of aromatics and isoparaffins in gasoline, and increasing obviously the content of light olefins (especially propylene) and isobutane in the LPG. This shows that the catalyst according to the present invention improves significantly quality of gasoline and LPG in cracking products. Examples 29-34 Following examples illustrate the second kind of preferred catalysts according to the present invention and the process for preparing the same. Catalysts C15-C20 according to the present invention were obtained by mixing and slurrying p-alumina trihydrate or a mixture of p-alumina trihydrate and pseudo-boehmite, molecular sieve, phosphorus compound, rare earth metal compound and water (with or without clay), spray-drying the resulting slurry into particles of 40-150 microns in diameter, then calcining the resulting particles. However, the catalyst C20 was obtained in Example 34 by using alumina sol instead of pseudo-boehmite in Example 33. The amount of the p-alumina trihydrate and pseudo-boehmite used, the kind and amount of the clay used, and the kind and amount of the molecular sieve used, the kind and amount of the phosphorus compound used and the amount of rare earth chloride solution used are shown respectively in Table 18-22. The spray-drying temperature, calcination temperature and time are shown in Table 23. Compositions of catalysts C15-C20 are shown in Table 24. Comparative Example 9 This comparative example illustrates the reference catalyst containing no phosphorus and no rare earth metal and the process for preparing the same. The reference catalyst CB5 was obtained by the same process as Example 29, except that no phosphorus compound and no rare earth metal solution were added and different amount of clay was used. The amount of the p-alumina trihydrate and pseudo-boehmite used, the kind and amount of the clay used, the kind and amount of the molecular sieve used are shown in Table 18-21, respectively. The spray-drying temperature, calcination temperature and time are shown in Table 23. The composition of the reference catalyst CB5 is shown in Table 24. Comparative Example 10 This comparative example illustrates the reference catalyst containing no T\|-alumina and the process for preparing the reference catalyst. The reference catalyst CB6 was obtained by the same process as Example 29, except that pseudo-boehmite instead of p-alumina trihydrate was used. The amount of the pseudo-boehmite used, the kind and amount of the clay used, the kind and amount of the molecular sieve used, the kind and amount of phosphorus compound used, and the amount of the solution of rare earth chloride used are shown respectively in Table 18-22. The spray-drying temperature, calcination temperature and time are shown in Table 23. The composition of the reference catalyst CB6 is shown in Table 24. Examples 35-40 Following examples illustrate the catalytic performances of the catalysts according to the present invention. The catalysts C15-C20 were aged at 800°C with 100% steam for 8 hrs, respectively. The catalytic cracking of 3# feedstock oil as shown in Table 25 was carried out in an ACE unit with 9g of (inventory of) each aged catalysts C15-C20. Reaction conditions and reaction results are shown in Table 26. Wherein, Conversion = Dry gas yield + LPG yield + Gasoline yield + Coke yield; Total liquid products yield = LPG yield + Gasoline yield + LCO yield. Herein, gasoline refers to a fraction with a distillation range of C5-221°C, LCO refers to a fraction with a boiling range of from 221 "0-343*0, LPG refers to a fraction from C3 to C4, dry gas is a fraction of H2 - C2. Comparative Examples 11-12 Following comparative examples are attended to illustrate catalytic performances of reference catalysts. With the same process as Example 35, the catalyst was aged, and the catalytic cracking of the same feedstock oil was carried out at the same condition, except that catalyst used was the reference catalyst CB5 and CB6 of Comparative Example 9 and Comparative Example 10, respectively. Reaction conditions and reaction results are shown in Table 26. It can be seen from results shown in Table 26 that, as compared with the results obtained by using the reference catalysts, using the catalyst according to the present invention to carry out catalytic cracking of the same feedstock oil results in decreasing remarkably the olefin content of gasoline, increasing the content of aromatics and isoparaffins in gasoline. This shows that the catalyst according to the process of the present invention not only has higher cracking activity i.e. higher yield of light oil and LPG in cracking products, but also improves significantly the quality of gasoline in cracking products. Claims: 1. A cracking catalyst, containing alumina, phosphorus and molecular sieve, with or without clay, wherein said alumina is Ti-alumina or a mixture of T\|-alumina and %-alumina and/or y-alumina, and wherein the catalyst contains, on the basis of the total amount of the catalyst: O.5-5Owt% of T\|-alumina; 0-50wt% of %-alumina and/or y-alumina; 10-70wt% of molecular sieve; 0-75wt% of clay; and 0.1-8wt% of phosphorus, measured as P2O5. 2. The catalyst according to claim 1, wherein the catalyst contains, on the basis of the total amount of the catalyst: 5-45wt% of T\|-alumina; 0-40wt% of x-alumina and/or y-alumina; 20-50wt% of molecular sieve; 0-60wt% of clay; and 0.5-6wt% of phosphorus, measured as P2O5. 3. The catalyst according to claim 1 or 2, wherein the catalyst further contains rare earth metal, and wherein the content of rare earth metal is 0.1- 2wt%, measured as oxide. 4. The catalyst according to claim 3, wherein the content of rare earth metal is 0.2-1.8wt%, measured as oxide. 5. The catalyst according to claim 1 or 2, wherein said molecular sieve is one or more selected from the group consisting of zeolites and non-zeolitic molecular sieves that are used as cracking catalyst active component. 6. The catalyst according to claim 5, wherein said zeolite is one or more selected from the group consisting of-large pore zeolites and-medium pore zeolites. 7. The catalyst according to claim 6, wherein said-large pore zeolite is one or more selected from the group consisting of faujasite, zeolite-p and mordenite. 8. The catalyst according to claim 7, wherein said-large pore zeolite is one or more selected from the group consisting of a zeolite-Y, a zeolite-Y containing one or more selected from phosphorus, iron and rare earths, an ultrastable zeolite-Y, an ultrastable zeolite-Y containing one or more selected from phosphorus, iron and rare earths, a zeolite-HY, an zeolite-HY containing one or more selected from phosphorus, iron and rare earths, and zeolite-p. 9. The catalyst according to claim 6, wherein said -medium pore is one or more selected from the group consisting of a MFI-structured zeolite amd a MFI- structured zeolite containing one or more selected from phosphorus, iron and rare earths. 10. The catalyst according to claim 1 or 2, wherein said molecular sieve is one or more selected from the group consisting of a zeolite-Y, a zeolite-Y containing one or more selected from phosphorus, iron and/or rare earths, an ultrastable zeolite-Y, an ultrastable zeolite-Y containing one or more selected from phosphorus, iron and rare earths, zeolite-HY, a zeolite-HY containing one or more selected from phosphorus, iron and rare earths, zeolite-p, a MFI- structured zeolite, a MFI-structured zeolite containing one or more selected from phosphorus, iron and rare earths, and SAPO molecular sieve. 11. The catalyst according to claim 1 or 2, wherein said molecular sieve contains a mixture of a zeolite-Y and the MFI-structured zeolite, and wherein the content of the zeolite-Y is 30-90wt%, the content of the MFI-structured zeolite is 10-70wt%, based on the total amount of said zeolite mixture. 12. The catalyst according to claim 11, wherein the content of the zeolite- Y is 40-85 wt%, the content of the MFI-structured zeolite is 15-60wt%, based on the total amount of said zeolite mixture. 13. The catalyst according to claim 11, wherein said zeolite mixture further contains zeolite-P, and wherein the content of the zeolite-P is 0-30wt%, based on the total amount of said zeolite mixture. 14. The catalyst according to claim 12, wherein the content of zeolite-P is 0-20wt%, based on the total amount of said zeolite mixture. 15. The catalyst according to claim 1 or 2, wherein said clay is one or more selected from the group consisting of kaolin, halloysite, montmorillonite, kieselguhr, allokite, soapstone, rectorite, sepiolite, attapulgus, hydrotalcite, and bentonite. 16. A process for preparing the catalyst according to claim 1, comprising: drying a slurry containing aluminum compound, molecular sieve and water, with or without clay, and then calcining the slurry followed adding further a phosphorus compound, whererin said aluminum compound is one that is able to form T)-alumina or a mixture of an aluminum compound able to form x\ -alumina and an aluminum compound able to form x-alumma and/or y-alumina, and wherein each component is used in such an amount that the final catalyst contains, on the basis of the total amount of the catalyst: 0.5-50wt% of "n-alumina; 0-50wt% of x-alumina and/or y-alumina; 10-70wt% of molecular sieve; 0-75wt%ofclay;and 0.1-8wt% of phosphorus, measured as P2O5. 17. A process for preparing the catalyst according to claim 3, comprising drying a slurry containing aluminum compound, molecular sieve and water, with or without clay, and then calcining the slurry followed adding further a phosphorus compound and a rare earth metal compound, whererin said aluminum compound is one that is able to form Ti-alumina or a mixture of an aluminum compound able to form n.-alumina and an aluminum compound able to form x-alumina and/or y-alumina, and wherein each component is used in such an amount that the final catalyst contains, on the basis of the total amount of the catalyst: 0.5-50wt% of Ti-alumina; 0-50wt% of %-alumina and/or y-alumina; 10-70wt% of molecular sieve; 0-75wt%ofclay; 0.1-8wt% of phosphorus, measured as P2O5; and 0.1-2wt% of rare earth metal, measured as oxide. 18. A process for preparing the catalyst according to claim 11, comprising drying a slurry containing aluminum compound, molecular sieve and water, with or without clay, and then calcining the slurry followed adding further a phosphorus compound, whererin said aluminum compound is one that is able to form n-alumina or a mixture of an aluminum compound able to form ^-alumina and an aluminum compound able to form x-alumina and/or y-alumina, wherein each component is used in such an amount that the final catalyst contains, on the basis of the total amount of the catalyst: 0.5-50wt% of T]-alumina; 0-50wt% of %-alumina and/or y-alumina; 0-7 5wt% of clay; 0.1-8wt% of phosphorus, measured as P2O5; and 10-70wt% of a molecular sieve, wherein said molecular sieve is a zeolite mixture containing a zeolite-Y and the MFI-structured zeolite, and wherein the content of the zeolite-Y is 30-90wt%, the content of the MFI-structured zeolite is 10-70wt%, based on the total amount of said zeolite mixture. 19. The process according to claim 16, 17 or 18, wherein said aluminum compound that is able to form Ti-alumina is (3-alumina trihydrate, the aluminum compound able to form x-alumina is a-alumina trihydrate, and said aluminum compound able to form y-alumina is bohemite, pseudo-boehmite and/or alumina sol. 20. The process according to claim 16, 17 or 18, wherein said phosphorus compound is one or more selected from the group consisting of phosphoric acid, phosphate, phosphorous acid, phosphite, pyrophosphoric acid, pyrophosphate, polyphosphoric acid, polyphosphate, metaphosphoric acid, and metaphosphate. 21. The process according to claim 20, wherein said phosphorus compound is one or more selected from the group consisting of phosphoric acid, ammonium phosphate, diammonium hydrogen phosphate, ammonium dihydrogen phosphate, phosphorous acid, ammonium phosphite, sodium pyrophosphate, sodium tripolyphosphate and sodium hexametaphosphate. 22. The process according to claim 16, wherein each component is used in such an amount that the final catalyst contains, on the basis of the total amount of the catalyst: 5-45wt% of T^-alumina; 0-40wt% of x-alumina and/or y-alumina; 20-50wt% of molecular sieve; 0-60wt% of clay; and 0.5-6wt% of phosphorus, measured as P2OS. 23. The process according to claim 17, wherein said rare earth metal compound is one or more selected from the group consisting of rare earth chloride and rare earth nitrate.

Full Text

Specification
A cracking catalyst and a process for preparing the same
Field of the Invention
The present invention relates to a cracking catalyst used in oil refining and a process for preparing the catalyst.
Description of the Related Art
The trend of catalytic cracking stocks becoming heavier and heavier is so increasingly severe that higher cracking ability of the cracking catalyst and cracking process has to be required in order to realize an object of production of more light oil (gasoline and diesel oil) and liquefied petroleum gas.
With regard to fluidized catalytic cracking (FCC) gasoline, olefins, aromatics and isoparaffins are main contributors of octane number. However, decreasing the olefin content of FCC gasoline is required due to environmental protection. In order to offset the loss of octane number caused by decreasing the olefin content, increasing the content of isoparaffins and aromatics in gasoline is required. Thus, there is a need of developing a cracking catalyst and a cracking process that are able to produce gasoline having lower content of olefin but higher content of aromatics and isoparaffins.
Meantime, the quality of catalytic cracking diesel oil needs also to be improved, because the diesel oil obtained by using the existing cracking catalyst and process has a lower aniline point, a higher density and a lower cetane number. Thus, there is a need of developing a cracking catalyst and a cracking process that have relatively high cracking ability of heavy oil and are able to decrease the density of diesel oil and increase aniline point and cetane number thereof.

Furthermore, light olefins and isobutane contained in the liquefied petroleum gas from a catalytic cracking are feedstocks of basic organic
chemical industries. Currently, the supply of the light olefins (especially propylene) and isobutane falls short of demand. However, the content of light olefins (especially propylene) and isobutane is lower in the liquefied petroleum gas products from the existing cracking catalysts and processes. Thus, there is a need of developing a novel cracking catalyst and a cracking process that can be used to produce the cracking product containing more light olefins (especially propylene) and isobutane in the liquefied petroleum gas.
CN 1042201C discloses a cracking catalyst for the production of more C3-Cs olefins. The catalyst consists of 10-50wt% of the zeolite-Y having a unit cell size^ 2.45nm, 2-40wt% of ZSM-5 zeolite modified with element selected from the group consisting of P, RE and H, and 20-80wt% of a semisynthetic matrix of kaolin and alumina binder.
CN 1055301C discloses a cracking catalyst for the production of more iso-olefins and gasoline. The catalyst consists of 5-70wt% of a composite aluminum-base alumina binder that is made up with pseudo-boehmite and alumina sol in a weight-ratio of from 1:9 to 9:1, 5-65wt% of clay and 23-50wt% of molecular sieve. Wherein said molecular sieve is a mixture consisting of 15-82wt% of the zeolite-Y and the balance of a rare earth-containing pentasil high silica zeolite containing 0-10wt% of phosphorus(measured as P2O5) and/or HZSM-5 zeolite.
CN 1072201A discloses a catalyst for the conversion of hydrocarbons to produce light olefins and gasoline with high octane number. The catalyst consists of 10-40wt% of three zeolites i.e. zeolite ZSM-5, zeolite REY and a high silica zeolite-Y, and the balance of a synthetic matrix or a semisynthetic marix containing 10-40wt% of silica and/or alumina binder. Wherein the amount of the zeolite ZSM-5 is 3-50wt%, and the amounts of the zeolite REY and the high silica zeolite-Y are each of 12-7 5wt%.
CN1085825A discloses a catalyst for the conversion of hydrocarbons to

produce-propylene, butene and gasoline with high octane number. The catalyst consists of 10-40wt% of three zeolites i.e. zeolite ZRP, zeolite REY and high silica zeolite-Y, and the balance of a-synthetic matrix or a semisynthetic matrix containing 10-40wt% of silica and/or alumina binder. Wherein the amount of the zeolite ZRP is 3-50wt%, and the amounts of zeolite REY and the high silica zeolite-Y are each of 12-75wt%.
CN 1325940A discloses a phosphorus-containing catalyst for cracking hydrocarbons. The catalyst consists of 10-60wt% of a zeolite-Y or the zeolite-Y together with a MFI-structured zeolite and/or zeolite-p, 0-75wt% of clay, 10-60wt% of two kinds of alumina, and 0.1-7.0wt% of phosphorus measesred as P2OS, and 0-20wt% of rare earth measured as RE2O3. Said two kinds of alumina are from pseudo-boehmite and alumina sol, respectively. Although the catalyst has higher ability for the conversion of heavy oil and makes the olefin content lower in gasoline product, the use of the catalyst cannot improve the quality of the catalytic cracked diesel oil and cannot increase the content of light olefins and isobutane in the liquefied petroleum gas.
CN 13 54224A discloses a catalytic cracking catalyst for producing isoparaffins-rich gasoline, propylene and isobutane. The catalyst consists of 0-70wt% of clay, 5-90wt% of inorganic oxides and l-50wt% of molecular sieve, wherein the molecular sieve is a mixture including (1) 20-75wt% of a high silica zeolite-Y having a SiO2/Al2O3 ratio of 5-15 and a rare earth content of 8-20wt% measured as RE2O3, (2) 20-75wt% of a high silica zeolite-Y having a SiO2/Al2O3 ratio of 16-50 and a rare earth content of 2-7wt% measured as RE2O3, and (3) l-50wt% of zeolite-0 or mordenite or zeolite-ZRP
Alumina is a component included generally in cracking catalysts. In the prior art, alumina is mostly from alumina monohydrate and alumina sol, wherein alumina monohydrate includes boehmite and pseudo-boehmite. During calcination for preparing the catalyst, boehmite, pseudo-boehmite and alumina sol are converted all into y-alumina. Therefore, the alumina contained in catalysts aforementioned in the prior art is all y-alumina.

Alumina may be also from alumina trihydrate. Alumina trihydrate includes a-alumina trihydrate, P-alumina trihydrate (Bayerite) and-Nordstrandite. During the preparation of catalyst, a-alumina trihydrate is converted into x-alumina, and p-alumina trihydrate is converted into T|-alumina.-Nordstrandite is only existence in nature, but there is no way to obtain by artificial synthesis. CN 1388214A discloses a process for preparing fluid cracking catalysts by drying a mixture of cracking catalyst components including clay, alumina and molecular sieve, wherein said catalyst contains 1.5-55wt% of alumina that is from |3-alumina trihydrate. Although said catalyst has higher activity for cracking heavy oil and better selectivity for light oil, it is not able to decrease the olefin content of gasoline, nor is able to improve the quality of catalytic diesel oil and increase the content of light olefins and isobutane in the liquefied petroleum gas.
Summary of the invention
An object of the present invention is to provide a novel catalyst for cracking hydrocarbons. Said catalyst has higher ability for cracking heavy oil, and results in cracking products with lower olefin content of gasoline, higher quality of diesel oil, and higher contents of light olefins and isobutane of the liquefied petroleum gas.
Although there are some examples in the prior art wherein alumina trihydrate is introduced in the preparation of cracking catalyst, it is used simply to increase cracking ability of cracking catalyst without effect on quality of gasoline, diesel oil and liquefied petroleum gas in the cracking products. The inventor of the present invention has unexpectedly found that when the alumina formed with alumina trihydrate, especially p-alumina trihydrate, and phosphorus, i.e. T)-alumina and phosphorus are introduced simultaneously into the cracking catalyst, a peculiar synergistic effect occurs that not only the cracking ability of the cracking catalyst can be increased, but also the quality of gasoline, diesel oil and liquefied petroleum gas can be substantially improved in the cracking products.

The catalyst according to the present invention contains alumina, phosphorus and molecular sieve, with or without clay, wherein said alumina is Ti-alumina or a mixture of T|-alumina and %-alumina and/or y-alumina. The catalyst contains, on the basis of total amount of the catalyst, 0.5-50wt% of r|-alumina, 0-50wt% of x-alumina and/or y-alumina, 10-70wt% of the molecular sieve, 0-75wt% of clay, and 0.1-8wt% of phosphorus, measured as P2O5.
Said molecular sieve is one or more selected from the group consisting of zeolite and non-zeolitic molecular sieve as an active component of the cracking catalyst. These zeolite and non-zeolitic molecular sieve are well known for one skilled in the art.
Said zeolite is preferably one or more selected from-arge pore zeolite and medium pore zeolite.
Said large pore zeolite is one having a porous structure with ring open-pore in diameter of at least 0.7 nanometers(nm), such as one or more selected from the group consisting of faujasite, zeolite-P and mordenite, especially a zeolite-Y, the zeolite-Y containing one or more elements selected from phosphorus, iron and rare earths, an ultrastable zeolite-Y, the ultrastable zeolite containing one or more elements selected from phosphorus, iron and rare earths, and zeolite-p.
Said medium pore zeolite is one having a porous structure with ring open-pore in diameter of from higher than 0.56nm to less than 0.7nm, such as one or more selected from a MFI-structured zeolite (e.g. ZSM-5 zeolite), the MFI-structured zeolite containing one or more elements selected from phosphorus, iron and rare earths (e.g. ZSM-5 zeolite containing phosphorus, iron and/or rare earths, and the MFI-structured zeolite containing phosphorus disclosed in CN 1194181A).
Said non-zeolitic molecular sieve refers to one or more molecular sieve in which part of or all aluminum and/or silicon are substituted by other elements such as phosphorus, titanium, gallium and germanium. Examples of these molecular sieves include one or more selected from silicates having different SiO2/Al2O3 ratio (e.g. metallosilicate, titanosilicates), metalloaluminate (e.g.

germanium aluminates), metallophosphates, aluminophosphates, metalloaluminophosphates, metal integrated silicoaluminophosphates (MeAPSO and ELAPSO), silicoaluminophosphates (SAPO molecular sieve), and gallogermanates. SAPO molecular sieve is preferred, such as one or more selected from the group consisting of SAPO-11 molecular sieve, SAPO-34 molecular sieve and SAPO-37 molecular sieve.
Preferably, said molecular sieve is one or more selected from the group consisting of a zeolite-Y, the zeolite-Y containing phosphorus, iron and/or rare earths, an ultrastable zeolite-Y, the ultrastable zeolite-Y containing phosphorus, iron and/or rare earths, zeolite-p\ the MFI-structured zeolite, the MFI structured zeolite containing phosphorus, iron and/or rare earths, and SAPO molecular sieve.
More preferred molecular sieve is a zeolite mixture containing the zeolite-Y and the MFI-structured zeolite, the content of the zeolite-Y is 30-90wt%, the content of the MFI-structured zeolite is 10-70wt%, based on the total amount of said zeolite mixture.
Preferred catalyst includes further 0.1-2wt% of rare earth metal (measured as oxide).
The process for preparing the catalyst according to the present invention comprises drying the slurry containing aluminum compound, molecular sieve and water, with or without clay, wherein said aluminum compound is one that is able to form t|-alumina, or a mixture of an aluminum compound able to form TI-alumina and an aluminum compound able to form x-alumina and/or y-alumina, and then calcining the slurry followed adding further a phosphorus compound. Each component is used in such an amount that the final catalyst contains, based on the total amount of the catalyst, 0.5-50wt% of Ti-alumina, 0-50wt% of X-alumina and/or y-alumina, 10-70wt% of molecular sieve, 0-75wt% of clay and 0.1-8wt% of phosphorus, measured as P2O5.
The catalyst according to the present invention not only has higher cracking activity, but also substantially improves the quality of gasoline, diesel

oil and liquefied petroleum gas, as showed that the gasoline has a lower content of olefins, a higher content of aromatics and isoparaffins, that the diesel oil has a lower density and a higher cetane number, and that the liquefied petroleum gas has a higher content of light olefins, especially the content of propylene and isobutane. The catalyst has further advantages such as high ability for cracking heavy oil, and capability of producing more light oils (gasoline and diesel oil) and the liquefied petroleum gas.
Detailed Description of the Inventing
The catalyst provided according to the process of the present invention contains alumina, phosphorus and molecular sieve, with or without clay, wherein said alumina is n-alumina or a mixture of ^-alumina and x-alumina and/or y-alumina, and wherein the catalyst contains, based on the total amount of the catalyst, 0.5-50wt%, preferably 5-45wt% of Ti-alumina, 0-50wt%? preferably 0-40wt% of x-alumina and/or y-alumina, 10-70wt%, preferably 20-50wt% of molecular sieve, 0-75wt%, preferably 0-60wt% of clay and 0.1-8wt%, preferably 0.5-6wt% of phosphorus, measured as P2O5.
(The catalyst according to the present invention may further contain 0.1-2wt%, preferably 0,2-1.8wt% of rare earth metal (measured as oxide).
Said molecular sieve is one or more selected from the group consisting of zeolite and non-zeolitic molecular sieve that they are used as active component of cracking catalyst. These zeolite and non-zeolitic molecular sieve are well known for one skilled in the art.
Said zeolite is preferably one or more selected from large pore zeolite and medium pore zeolite.
Said large pore zeolite is a zeolite having a porous structure with ring open-pore in diameter at least 0.7 nm, such as one or more selected from faujasite, zeolite-p and mordenite, especially, one or more selected from a zeolite-Y, the zeolite-Y containing one or more elements selected from phosphorus, iron and rare earth, an ultrastable zeolite-Y, the ultrastable zeolite

containing one or more selected from phosphorus, iron and rare earths, a zeolite-HY, the zeolite-HY containing one or more elements selected from phosphorus, iron and rare earths, and zeolite-p.
Said medium pore zeolite is a porous structure zeolite having ring open-pore of from higher than 0.56 run to less than 0.7 nm, such as the MFI-structured zeolite (e.g. ZSM-5 zeolite), the MFI-structured zeolite containing one or more elements selected from phosphorus, iron and rare earths (such as ZSM -5 zeolite containing one or more elements selected from phosphorus, iron and/or rare earths, and MFI-structured zeolite containing phosphorus, as disclosed in CN 1194181 A).
Said non-zeolitic molecular sieve refers to one or more molecular sieve in which part of or all aluminum and/or silicon are substituted by other elements such as phosphorus, titanium, gallium and germanium. Examples of these molecular sieves include one or more selected from silicates having different SiO2/Al2O3 ratio (e.g. metallosilicate, titanosilicates), metalloaluminate (e.g. germanium aluminates), metallophosphates, aluminophosphates, metalloaluminophosphates, metal integrated silicoaluminophosphates (MeAPSO and ELAPSO), silicoaluminophosphates (SAPO molecular sieve), and gallogermanates. SAPO molecular sieve is preferred, such as one or more selected from the group consisting of SAPO-11 molecular sieve, SAPO-34 molecular sieve and SAPO-37 molecular sieve.
Preferably, said molecular sieve is one or more selected from the group consisting of a zeolite-Y, the zeolite-Y containing one or more selected from phosphorus, iron and/or rare earths, an ultrastable zeolite-Y, the ultrastable zeolite-Y containing one or more selected from phosphorus, iron and/or rare earths, a zeolite-HY, the zeolite-HY containing one or more selected from phosphorus, iron and rare earths, zeolite-P, a MFI-structured zeolite, the MFI-structured zeolite containing one or more selected from phosphorus, iron and rare earths, and SAPO molecular sieve.
More preferred molecular sieve contains a zeolite mixture of a zeolite-Y

and the MFI-structured zeolite, wherein the content of the zeolite-Y is 30-90wt%, preferably 40-85wt%, and the content of the MFI-structured zeolite is 10-70wt%, preferably 15-60wt%, based on the total amount of said zeolite mixture.
Said clay is one or more selected from clays that are used as active component of cracking catalyst, such as one or more selected from kaolin, halloysite, montmorillonite, kieselguhr, allokite, soapstone, rectorite, sepiolite, attapulgus, hydrotalcite, and bentonite. More preferred clay is one or more selected from kaolin, montmorillonite, kieselguhr, rectorite, sepiolite and attapulgus. These clays are well known for one skilled in the art.
The catalyst according to the present invention may further contain non-alumina refractory inorganic oxide. Said non-alumina refractory inorganic oxide is one or more selected from the group consisting of non-alumina refractory inorganic oxides that are used as matrix of cracking catalyst, such as silica, amorphous silica-alumina, zirconia, titania, boric oxide, oxides of alkaline earth metal. Preferably, it is one or more selected from the group consisting of silica, amorphous silica-alumina, zirconia, titania, magnesia oxide and calcium oxide. The refractory inorganic oxides are well known for one skilled in the art. Based on the total amount of catalyst, the content of said non-alumina refractory inorganic oxide is 0-10wt%, preferably 0-5wt%.
In the process for preparing the catalyst according to the present invention, said aluminum compound is one able to form T|-alumina, or a mixture of an aluminum compound able to form n-alumina and an aluminum compound able to form %-alumina and/or Y-alumina.
Said aluminum compound able to form ^-alumina may be any aluminum compound that is able to form T|-alumina during the preparation of catalyst, preferably p-alumina trihydrate. Said aluminum compound able to form x-alumina may be any aluminum compound that is able to form x-alumina during the preparation of catalyst, preferably a-alumina trihydrate. Said aluminum compound able to form y-alumina may be any aluminum compound that is able

to form y-alumina during the preparation of catalyst, preferably boehmite, pseudo-boehmite and/or alumina sol.
Said phosphorus compound may be added in any step before calcining, for example, it may be added to a slurry containing the aluminum compound, molecular sieve and water, with or without clay. Or the phosphorus compound may be introduced by impregnating the solids obtained after drying the slurry containing the aluminum compound, molecular sieve and water, with or without clay, then calcining the impregnated product. In the catalyst of the present invention, said phosphorus content is exclusive of phosphorus contained originally in the molecular sieve.
Said phosphorus compound includes various compounds of phosphorus, for example, one or more selected from the group consisting of phosphoric acid, phosphates, phosphorous acid, phosphites, pyrophosphoric acid, pyrophosphates, polyphosphoric acids, polyphosphates, metaphosphoric acid and metaphosphates. Preferably, it is one or more selected from the group consisting of phosphoric acid, ammonium phosphate, diammonium hydrogen phosphate, ammonium dihydrogen phosphate, phosphorous acid, ammonium phosphite, sodium pyrophosphate, potassium pyrophosphate, sodium tripolyphosphate, potassium tripolyphosphate, sodium hexametaphosphate, potassium hexametaphosphate. More preferably, it is one or more selected from the group consisting of phosphoric acid, ammonium phosphate, diammonium hydrogen phosphate, ammonium dihydrogen phosphate, phosphorous acid, ammonium phosphite, sodium pyrophosphate, sodium tripolyphosphate, sodium hexametaphosphate.
Each component is used in such an amount that the final catalyst contains, based on the total amount of the catalyst, 0.5-50wt% of T|-alumina, 0-50wt% of %-alumina and/or y-alumina, 10-70wt% of molecular sieve, 0-75wt% of clay, and 0.1-8wt% of phosphorus, measured as P2O5. Preferably, each component is used in such an amount that the final catalyst contains 5-45wt% of Ti-alumina, 0-40wt% of x-alumina and/or y-alumina, 20-50wt% of molecular sieve, 0-

60wt% of clay, and 0.5-6wt% of phosphorus, measured as P2O5.
If the catalyst further contains non-alumina inorganic oxides, the non-alumina inorganic oxide or its precursor may be added to the slurry containing the aluminum compound, molecular sieve and water, with or without clay. The precursor of said non-alumina inorganic oxide refers to a substance that is able to form said non-alumina inorganic oxide during the preparation of the catalyst, these precursors of non-aluminum inorganic oxides are well known for one skilled in the art. For example, the precursor of silica may be silica sol, silica gel and/or sodium silicate; the precursor of amorphous silica-alumina may be a silica-alumina sol and/or silica-alumina gel, and the precursor of zirconia, titania, boric oxide and alkaline earth metal oxides may be respective hydroxide thereof. Said non-alumina inorganic oxide and/or its precursor is used in such an amount that the final catalyst contains 0-10wt%, preferably 0-5wt% of the non-alumina inorganic oxide.
Conditions of said drying and calcining are those of conventional drying and calcination for cracking catalysts, for example, the drying temperature is from room temperature to 200 °C, preferably 80-180 "C, and the calcination temperature is from higher than 200V to 750°C, preferably 300-600°C, the calcination time is at least 0.1 hrs, preferably 0.1-10hrs, more preferably 0.3-4hrs. As drying method, various existing methods for drying may be used, such as oven-drying, air-drying or spray-drying, preferably oven-drying or spray-drying.
The catalyst according to the present invention is suitable for catalytic cracking of petroleum and its various fractions, especially suitable for catalytic cracking of petroleum and its various fractions having a boiling point higher than 330°C, such as one or more selected from atmospheric residuum, vacuum residuum, vacuum gas oil, atmospheric gas oil, straight-run gas oil, light or heavy deasphalted oils from the process of solvent deasphalting, and coker gas oil, in order to produce high-quality of gasoline, diesel oil and liquefied petroleum gas.

One of preferred catalysts in the present invention
The catalyst contains alumina, phosphorus and molecular sieve, with or without clay. Said alumina is Tj-alumina, or a mixture of T|-alumina and %-alumina and/or y-alumina. The catalyst contains, based on the total amount of the catalyst, 0.5-50wt%, preferably 5-45wt% of -p-alumina, 0-50wt%, preferably 0-40wt% of %-alumina and/or y-alumina, 0-75wt%, preferably 0-60wt% of clay, 0.1-8wt%, preferably 0.5-6wt% of phosphorus, measured as P2O5, and 10-70wt%, preferably 20-50wt% of molecular sieve. Said molecular sieve is a zeolite mixture containing the zeolite-Y and the MFI-structured zeolite, wherein the content of the zeolite-Y is 30-90wt%, preferably 40-85wt% and the content of the MFI-structured zeolite is 10-70wt%, preferably 15-60wt%, based on the total amount of said zeolite mixture.
The process for preparing the preferred catalyst is as follows:
The process comprises drying the slurry containing aluminum compound, molecular sieve and water, with or without clay, wherein said aluminum compound is one that is able to form n-alumina, or a mixture of an aluminum compound able to form t|-aluminaand an aluminum compound able to form %-alumina and/or y-alumina, and then calcining the slurry followed adding further a phosphorus compound. Each component is used in such an amount that the final catalyst contains, based on the total amount of the catalyst, 0.5-50wt%, preferably 5-45wt% of T)-alumina, 0-50wt%, preferably 0-40wt% of %-alumina and/or y-alumina, 0-75wt%, preferably 0-60wt% of clay, 0.1-8wt%, preferably 0.5-6wt% of phosphorus, measured as P2O5, and 10-70wt%, preferably 20-50wt% of molecular sieve. Said molecular sieve is a zeolite mixture containing the zeolite-Y and the MFI-structured zeolite, wherein the content of the zeolite-Y is 30-90wt%, preferably 40-85wt% and the content of the MFI-structured zeolite is 10-70wt%, preferably 15-60wt%, based on the total amount of said zeolite mixture.
Said zeolite mixture further contains zeolite-p of which the content is 0-30wt%, preferably 0-20wt%, based on the total amount of said zeolite mixture.

The catalyst substantially improves the quality of gasoline and liquefied petroleum gas in cracking products.
The second of preferred catalysts according to the present invention
The catalyst contains alumina, phosphorus, rare earth metal and molecular sieve, with or without clay. Said alumina is Ti-alumina or a mixture of T|-alumina and x-alumina and/or y-alumina. The catalyst contains, based on the total amount of the catalyst, 0.5-50wt%, preferably 5-45wt% of n.-alumina, 0-50wt%, preferably 0-40wt% of %-alumina and/or y-alumina, 0-70wt%, preferably 0-60wt% of clay, 0.1-8wt%, preferably 0.5-6wt% of phosphorus, measured as P2O5, 0.1-2wt%, preferably 0.2-1.8wt% of rare earth metal, measured as oxide, and 10-70wt%, preferably 20-50wt% of the molecular sieve. Said molecular sieve molecular sieve is zeolite-Y.
The process for preparing the preferred catalyst as follows:
The process comprises drying the slurry containing aluminum compound, molecular sieve and water, with or without clay, wherein said aluminum compound is one that is able to form n,-alumina, or a mixture of an aluminum compound able to form Tj-aluminaand an aluminum compound able to form %-alumina and/or 7-alumina, and then calcining the slurry followed adding further a phosphorus compound and a rare earth metal compound. Each component is used in such an amount that the final catalyst contains, based on the total amount of the catalyst, 0.5-50wt%, preferably 5-45wt% of T|-alumina, 0-50wt%, preferably 0-40wt% of x-alumina and/or y-alumina, 0-70wt%, preferably 0-60wt% of clay, 0.1-8wt%, preferably 0.5-6wt% of phosphorus, measured as P2O5, 0.1-2wt%, preferably 0.2-1.8wt% of rare earth metal, measured as oxide, and 10-70wt%, preferably 20-50wt% of the molecular sieve. Said molecular sieve molecular sieve is zeolite-Y.
Said rare earth metal compound is one or more selected from the group consisting of rare earth metal chloride and rare earth metal nitrate.
The catalyst has high ability for cracking heavy oil, and thereby can be used to produce more light oils (gasoline and diesel oil) and liquefied petroleum

gas.
Conditions for using the catalyst according to the present invention are those conventional for cracking reaction. Generally, said cracking conditions include a reaction temperature of 3 50-700 °C, preferably 400-650 °C, a catalyst-oil ratio (a weight-ratio of catalyst to hydrocarbon oil) of 1-20, preferably 2-15.
Following Examples intend to illustrate further the present invention.
In Examples, the alumina content of (3-alumina trihydrate used is 64wt% (the trihydrate is manufactured by Institute of ShanDong Aluminum Corp.); the alumina content of pseudo-boehmite (manufactured by ShanDong Aluminum Corp) is 62wt% ; the alumina content of alumina sol (manufactured by Qilu Catalyst Factory) is 21.6wt%, the silica content of silica sol (manufactured by Beijing Changhong Chemical Plant) is 12wt%: the solid content of kaolin (manufactured by China Kaolin Corp) is 76wt%; the solid content of montmorillonite (manufactured by Hubei Zhongxiang City Iron Ore Factory) is 80wt%; the phosphorus-containing compound is of chemical purity; the solution of rare earth chloride ( prepared in the laboratory, with a concentration of 219g rare earth oxide/litre, in which La^ accounts for 53.2% of the rare earth oxide, CeO2 accounts for 13.0% of the rare earth oxide, Pr6OH accounts for 13.0% of the rare earth oxide, Nd^ accounts for 20.8% of the rare earth oxide; the solid rare earth chloride is manufactured by Inner Mongolia Baotou Rare earth Factory).
In Examples, molecular sieve SAPO-11 was prepared according to the process disclosed in Example 1 of CN 1098214C.
In Examples, compositions of various zeolites used are as follows respectively:
Zeolite HY (with a Nap content of 1.5wt% and a SiO2/Al2O3 ratio of 5.3) is obtained by ion-exchanging a zeolite NaY (with a NajO content of 13.5wt% and a SiO2/Al2O3 ratio of 5.0, manufactured by Qilu Catalyst Factory) at a temperature of 80 °C for 1 hr in a weight ratio of water : zeolite NaY : solid ammonium chloride of 10:1:1, then filtering and calcining at 550°C for 2hrs,

and then exchanging once again by repeating aforementioned steps, then filtering and calcining;
Zeolite REY is a zeolite-Y containing rare earths (the content of rare earth oxide is 18.5wt%, in which I^C^ accounts for 53.2wt% of the rare earth oxide, CeO2 accounts for 13.0wt% of the rare earth oxide, Pr6Ou accounts for 13.0wt% of the rare earth oxide, NCI2O3 accounts for 20.8wt% of the rare earth oxide, NajO content is 1.6wt%; the SiO2/Al2O3 ratio is 5.4, the unit cell size is 2.468nm, the zeolite is manufactured by Qilu Catalyst Factory);
Zeolite REHY is a zeolite-Y containing rare earths (the content of rare earth oxide is 84wt%, in which La^ accounts for 53.2wt% of the rare earth oxide, CeO2 accounts for 13.0wt% of the rare earth oxide, Pr6Ou accounts for 13.0wt% of the rare earth oxide, Nd2O3 accounts for 20.8wt% of the rare earth oxide, NajO content is 3.7wt%; the SiO2/Al2O3 ratio is 5.6, the unit cell size is 2.46lnm, the zeolite is manufactured by Qilu Catalyst Factory);
Zeolite MOY is a zeolite-Y containing phosphorus and rare earths (the content of rare earth oxide is 8.0wt%, in which La^ accounts for 53.2wt% of the rare earth oxide, CeO2 accounts for 13.0wt% of the rare earth oxide, Pr6OM accounts for 13.0wt% of the rare earth oxide, NdjOg accounts for 20.8wt% of the rare earth oxide, Na^ content is 1.3wt%; the phosphorus content is 1.1 wt%, measured as elemental phosphorus, the SiO2/Al2O3 ratio is 5.6, the unit cell size is 2.460nm, the zeolite is manufactured by Qilu Catalyst Factory);
Zeolite DASY0 0 is an ultrastable zeolite-Y Q^O content is 1 .Owt%, the SiO2/Al2O3 ratio is 6.8, the unit cell size is 2.446nm, the zeolite is manufactured by Qilu Catalyst Factory);
Zeolite DASY20 is an ultrastable zeolite-Y containing rare earths (the content of rare earth oxide is 1.8wt%, in which La^ accounts for 53.2wt% of the rare earth oxide, CeO2 accounts for 13.0wt% of the rare earth oxide, Pr6O,, accounts for 13.0wt% of the rare earth oxide, Nd^ accounts for 20.8wt% of the rare earth oxide, Na^ content is 1.2wt%; the SiO2/Al2O3 ratio is 6.8, the unit cell size is 2.447nm, the zeolite is manufactured by Qilu Catalyst

Factory);
Zeolite ZSM-5 is a MFI-structured zeolite (NajO content is 0,2wt%, the SiO2/Al2O3 ratio is 60, the zeolite is manufactured by Qilu Catalyst Factory);
Zeolite ZRP-1 is a MFI-structured zeolite containing phosphorus and rare earths ( having NajO content of 0.1 wt%, a SiO2/Al2O3 ratio of 30 and a rare earth oxide content of 1.7wt%, in which La2O3 accounts for 53.2wt% of the rare earth oxide, CeO2 accounts for 13.0wt% of the rare earth oxide, Pr6Ou accounts for 13.0wt% of the rare earth oxide, Nd^ accounts for 20.8wt% of the rare earth oxide, the phosphorus content is 1.9wt%, measured as elemental phosphorus, the zeolite is manufactured by Qilu Catalyst Factory);
ZSP-1 is a MFI-structured zeolite containing phosphorus and iron (Na^ content is 0.1 wt%; the SiO2/Al2O3 ratio is 30, Fe2O3 content is 1.5wt%, and the phosphorus content is 1,2wt%, measured as elemental phosphorus, the zeolite is manufactured by Qilu Catalyst Factory);
Zeolite-p has a Nap content of 3.2wt% and a SiO2/Al2O3 ratio of 28, the zeolite is manufactured by Qilu Catalyst Factory.
Aforesaid SiO2/Al2O3 ratios all refers to the molar ratio of silica and alumina.
Examples 1-6
Following examples illustrate the catalysts according to the present invention and the process for preparing the same.
Catalysts C1-C6 according to the present invention were obtained by mixing and slurrying p-alumina trihydrate or a mixture of P-alumina trihydrate and pseudo-boehmite, molecular sieve, phosphorus compound and water (with or without clay), spray-drying the resulting slurry into particles of 40-150 microns in diameter, then calcining the resulting particles. The amount of the J3-alumina trihydrate and pseudo-boehmite used, the kind and amount of clay used, and the kind and amount of the molecular sieve used, the kind and amount of the phosphorus compound used are shown respectively in Tables 1-4. The

spray-drying temperature, calcination temperature and time are shown in Table 5. The compositions of catalysts C1-C6 are shown in Table 6.
Comparative Example 1
This comparative example illustrates the reference catalyst having no phosphorus added and the process for preparing the reference catalyst
The reference catalyst CB1 was prepared by the same process as Example 1, except that no phosphorus compound was added and different amount of clay was used. The amount of thep-alumina trihydrate and pseudo-boehmite used, the kind and amount of the clay used, and the kind and amount of the molecular sieve used are shown respectively in Tables 1-4. The spray-drying temperature, calcination temperature and time are shown in Table 5. The composition of the reference catalyst CB1 is shown in Table 6.
Comparative Example 2
This comparative example llustrates the reference catalyst containing no T|-alumina and the process for preparing the reference catalyst.
The reference catalyst CB2 was obtained by the same process as Example 1, except that pseudo-boehmite was used instead of |3-alumina trihydrate. The amount of the pseudo-boehmite used, the kind and amount of the clay used, the kind and amount of the molecular sieve used, and the kind and amount of the phosphorus compound used are shown respectively in Tables 1-4. The spray-drying temperature, calcination temperature and time are shown in Table 5. The composition of the reference catalyst CB2 is shown in Table 6.
Example 7
This Example illustrates the catalyst according to present invention and the process for preparing the same.
The catalystC7 was obtained by mixing and slurrying 93.8kg p-alumina trihydrate, 72.6kg pseudo-boehmite, 54kg DASY20 molecular sieve, 30kg ZRP-1 molecular sieve, 6kg SAPO-11 molecular sieve, 126.3kg kaolin and 50kg silica sol and deionized water, spray-drying the resulting slurry at temperature 180°C into particles of 40-150 microns in diameter, impregnating

Following examples illustrate the catalytic performances of the catalysts provided in the present invention.
The catalysts C1-C6 were aged with 100% steam at 800 °C for 8 hrs, respectively. The catalytic cracking of 1 # feedstock oil as shown in Table 7 was carried out in an ACE unit with 9g of inventory of each aged catalysts C1-C6. Reaction conditions and reaction results are shown in Table 8.
Wherein, Conversion = Dry gas yield + Liquefied petroleum gas yield + Gasoline yield + Coke yield; Total liquid products yield = Liquefied petroleum gas yield + Gasoline yield + Diesel oil yield. Herein, gasoline refers to a C5 fraction to a fraction with a distillation temperature of 22TC. Diesel oil(LCO) refers to a fraction with a boiling point of from 221°C to 343 °C. Liquefied petroleum gas (LPG) refers to a C3-C4 fraction. Dry gas is a fraction of H2 - C2.
Comparative Examples 3-4
Following comparative examples illustrate the catalytic performance of reference catalysts.
With the same process as Example 9, the catalysts were aged, and the catalytic cracking of the same feedstock oil was carried out under the same condition, except that the catalyst used was the reference catalysts CB1 and CB2 prepared in Comparative Example 1 and Comparative Example 2, respectively. Reaction conditions and reaction results are shown in Table 8.

It can be seen from the results shown in Table 8 that, as compared with the reference catalysts, using the catalyst according to the present invention to carry out catalytic cracking of the same feedstock oil results in not only substantial increase of the conversion of feedstock and Total liquid products yield, but also substantial decrease of the olefin content of gasoline, increase of the content of aromatics and isoparaffins in gasoline, decrease of the density and increase of the aniline point and cetane number of the LCO, and substantial increase of the content of light olefins (especially propylene) and isobutane in LPG. The results

shown in Table 10 indicate similarly that, as compared with those in the prior art, the catalyst according to the present invention has not only higher cracking activity, but also results in higher quality of gasoline, LCO and LPG in cracking products.
Examples 17-22
Following examples illustrate the first kind of preferred catalysts according to the present invention and the process for preparing the same.
Catalysts C9-C14 according to the present invention were obtained by mixing and slurrying p-alumina trihydrate or a mixture of p-alumina trihydrate and pseudo-boehmite, molecular sieve, phosphorus compound and water (with or without clay), then spray-drying the resulting slurry into particles of 40-150 microns in diameter, and then calcining the resulting particles. The catalyst C14 was obtained according to the process of Example 22 by using alumina sol instead of pseudo-boehmite in Example 21. The amount of the p-alumina trihydrate and pseudo-boehmite (or alumina sol) used, the kind and amount of the clay used, and the kind and amount of the molecular sieve used, the kind and amount of the phosphorus compound used are shown respectively in Table 11-14. The spray-drying temperature, calcination temperature and time are shown in Table 15. The compositions of catalysts C9-C14 are shown in Table 16.
Comparative Example 5
This comparative example illustrates the reference catalyst containing no phosphorus and the process for preparing the reference catalyst.
The reference catalyst CB3 was obtained by the same process as Example 17, except that no phosphorus compound was added and different amount of clay was used. The amount of the p-alumina trihydrate and pseudo-boehmite used, the kind and amount of the clay used, the kind and amount of the molecular sieve used are shown in Table 11-14, respectively. The spray-drying temperature, calcination temperature and time are shown in Table 15. The composition of the reference catalyst CB3 is shown in Table 16.

Comparative Example 6
This comparative example illustrates the reference catalyst containing no Ti-alumina and the process for preparing the reference catalyst.
The reference catalyst CB4 was obtained by the same process as Example 17, except that pseudo-boehmite instead of p-alumina trihydrate was used. The amount of the pseudo-boehmite used, the kind and amount of the clay used, the kind and amount of the molecular sieve used, the kind and amount of the phosphorus compound used are shown in Table 11-14, respectively. The spray-drying temperature, calcination temperature and time are shown in Table 15. The composition of the reference catalyst CB4 is shown in Table 16.

respectively. The catalytic cracking of 1 # feedstock oil as shown in Table 7 was carried out in an ACE unit with 9g of each aged catalysts C9-C14. Reaction conditions and reaction results are shown in Table 17.
Wherein, Conversion = Dry gas yield + LPG yield + Gasoline yield + Coke yield; Total liquid products yield = LPG yield + Gasoline yield + LCO yield. Herein, gasoline refers to a fraction with a distillation range of C5-221 °C, LCO refers to a fraction with a boiling range of from 221 °C to 343 °C, LPG refers to a C3-C4 fraction, dry gas is a fraction of H2 - C2.
Comparative Examples 7-8
Following comparative examples illustrated catalytic performances of reference catalysts.
With the same process as Example 23, the catalyst was aged, and the catalytic cracking of the same feedstock oil was carried out at the same condition, except that catalyst used was the reference catalysts CB3 and CB4 said in Comparative Example 5 and Comparative Example 6, respectively. Reaction conditions and reaction results are shown in Table 17.

It can be seen from results shown in Table 17 that, as compared with the results obtained by using the reference catalysts, using the catalyst according to the present invention to carry out catalytic cracking of the same feedstock oil results in significantly decreasing the olefm content of gasoline, increasing the content of aromatics and isoparaffins in gasoline, and increasing obviously the content of light olefins (especially propylene) and isobutane in the LPG. This shows that the catalyst according to the present invention improves significantly quality of gasoline and LPG in cracking products.
Examples 29-34
Following examples illustrate the second kind of preferred catalysts according to the present invention and the process for preparing the same.
Catalysts C15-C20 according to the present invention were obtained by mixing and slurrying p-alumina trihydrate or a mixture of p-alumina trihydrate and pseudo-boehmite, molecular sieve, phosphorus compound, rare earth metal compound and water (with or without clay), spray-drying the resulting slurry into particles of 40-150 microns in diameter, then calcining the resulting particles. However, the catalyst C20 was obtained in Example 34 by using

alumina sol instead of pseudo-boehmite in Example 33. The amount of the p-alumina trihydrate and pseudo-boehmite used, the kind and amount of the clay used, and the kind and amount of the molecular sieve used, the kind and amount of the phosphorus compound used and the amount of rare earth chloride solution used are shown respectively in Table 18-22. The spray-drying temperature, calcination temperature and time are shown in Table 23. Compositions of catalysts C15-C20 are shown in Table 24.
Comparative Example 9
This comparative example illustrates the reference catalyst containing no phosphorus and no rare earth metal and the process for preparing the same.
The reference catalyst CB5 was obtained by the same process as Example 29, except that no phosphorus compound and no rare earth metal solution were added and different amount of clay was used. The amount of the p-alumina trihydrate and pseudo-boehmite used, the kind and amount of the clay used, the kind and amount of the molecular sieve used are shown in Table 18-21, respectively. The spray-drying temperature, calcination temperature and time are shown in Table 23. The composition of the reference catalyst CB5 is shown in Table 24.
Comparative Example 10
This comparative example illustrates the reference catalyst containing no T|-alumina and the process for preparing the reference catalyst.
The reference catalyst CB6 was obtained by the same process as Example 29, except that pseudo-boehmite instead of p-alumina trihydrate was used. The amount of the pseudo-boehmite used, the kind and amount of the clay used, the kind and amount of the molecular sieve used, the kind and amount of phosphorus compound used, and the amount of the solution of rare earth chloride used are shown respectively in Table 18-22. The spray-drying temperature, calcination temperature and time are shown in Table 23. The composition of the reference catalyst CB6 is shown in Table 24.

Examples 35-40
Following examples illustrate the catalytic performances of the catalysts according to the present invention.
The catalysts C15-C20 were aged at 800°C with 100% steam for 8 hrs, respectively. The catalytic cracking of 3# feedstock oil as shown in Table 25

was carried out in an ACE unit with 9g of (inventory of) each aged catalysts C15-C20. Reaction conditions and reaction results are shown in Table 26.
Wherein, Conversion = Dry gas yield + LPG yield + Gasoline yield + Coke yield; Total liquid products yield = LPG yield + Gasoline yield + LCO yield. Herein, gasoline refers to a fraction with a distillation range of C5-221°C, LCO refers to a fraction with a boiling range of from 221 "0-343*0, LPG refers to a fraction from C3 to C4, dry gas is a fraction of H2 - C2.
Comparative Examples 11-12
Following comparative examples are attended to illustrate catalytic performances of reference catalysts.
With the same process as Example 35, the catalyst was aged, and the catalytic cracking of the same feedstock oil was carried out at the same condition, except that catalyst used was the reference catalyst CB5 and CB6 of Comparative Example 9 and Comparative Example 10, respectively. Reaction conditions and reaction results are shown in Table 26.

It can be seen from results shown in Table 26 that, as compared with the results obtained by using the reference catalysts, using the catalyst according to the present invention to carry out catalytic cracking of the same feedstock oil results in decreasing remarkably the olefin content of gasoline, increasing the content of aromatics and isoparaffins in gasoline. This shows that the catalyst according to the process of the present invention not only has higher cracking activity i.e. higher yield of light oil and LPG in cracking products, but also improves significantly the quality of gasoline in cracking products.

Claims:
1. A cracking catalyst, containing alumina, phosphorus and molecular
sieve, with or without clay, wherein said alumina is Ti-alumina or a mixture of
T|-alumina and %-alumina and/or y-alumina, and wherein the catalyst contains,
on the basis of the total amount of the catalyst:
O.5-5Owt% of T|-alumina;
0-50wt% of %-alumina and/or y-alumina;
10-70wt% of molecular sieve;
0-75wt% of clay; and
0.1-8wt% of phosphorus, measured as P2O5.
2. The catalyst according to claim 1, wherein the catalyst contains, on the
basis of the total amount of the catalyst:
5-45wt% of T|-alumina;
0-40wt% of x-alumina and/or y-alumina;
20-50wt% of molecular sieve;
0-60wt% of clay; and
0.5-6wt% of phosphorus, measured as P2O5.
3. The catalyst according to claim 1 or 2, wherein the catalyst further
contains rare earth metal, and wherein the content of rare earth metal is 0.1-
2wt%, measured as oxide.
4. The catalyst according to claim 3, wherein the content of rare earth
metal is 0.2-1.8wt%, measured as oxide.
5. The catalyst according to claim 1 or 2, wherein said molecular sieve is
one or more selected from the group consisting of zeolites and non-zeolitic
molecular sieves that are used as cracking catalyst active component.
6. The catalyst according to claim 5, wherein said zeolite is one or more
selected from the group consisting of-large pore zeolites and-medium pore
zeolites.
7. The catalyst according to claim 6, wherein said-large pore zeolite is one
or more selected from the group consisting of faujasite, zeolite-p and mordenite.

8. The catalyst according to claim 7, wherein said-large pore zeolite is one
or more selected from the group consisting of a zeolite-Y, a zeolite-Y containing
one or more selected from phosphorus, iron and rare earths, an ultrastable
zeolite-Y, an ultrastable zeolite-Y containing one or more selected from
phosphorus, iron and rare earths, a zeolite-HY, an zeolite-HY containing one or
more selected from phosphorus, iron and rare earths, and zeolite-p.
9. The catalyst according to claim 6, wherein said -medium pore is one or
more selected from the group consisting of a MFI-structured zeolite amd a MFI-
structured zeolite containing one or more selected from phosphorus, iron and
rare earths.

10. The catalyst according to claim 1 or 2, wherein said molecular sieve is
one or more selected from the group consisting of a zeolite-Y, a zeolite-Y
containing one or more selected from phosphorus, iron and/or rare earths, an
ultrastable zeolite-Y, an ultrastable zeolite-Y containing one or more selected
from phosphorus, iron and rare earths, zeolite-HY, a zeolite-HY containing one
or more selected from phosphorus, iron and rare earths, zeolite-p, a MFI-
structured zeolite, a MFI-structured zeolite containing one or more selected
from phosphorus, iron and rare earths, and SAPO molecular sieve.
11. The catalyst according to claim 1 or 2, wherein said molecular sieve
contains a mixture of a zeolite-Y and the MFI-structured zeolite, and wherein
the content of the zeolite-Y is 30-90wt%, the content of the MFI-structured
zeolite is 10-70wt%, based on the total amount of said zeolite mixture.
12. The catalyst according to claim 11, wherein the content of the zeolite-
Y is 40-85 wt%, the content of the MFI-structured zeolite is 15-60wt%, based on
the total amount of said zeolite mixture.
13. The catalyst according to claim 11, wherein said zeolite mixture further
contains zeolite-P, and wherein the content of the zeolite-P is 0-30wt%, based
on the total amount of said zeolite mixture.
14. The catalyst according to claim 12, wherein the content of zeolite-P is
0-20wt%, based on the total amount of said zeolite mixture.

15. The catalyst according to claim 1 or 2, wherein said clay is one or more
selected from the group consisting of kaolin, halloysite, montmorillonite,
kieselguhr, allokite, soapstone, rectorite, sepiolite, attapulgus, hydrotalcite, and
bentonite.
16. A process for preparing the catalyst according to claim 1, comprising:
drying a slurry containing aluminum compound, molecular sieve and water,
with or without clay, and then
calcining the slurry followed adding further a phosphorus compound, whererin said aluminum compound is one that is able to form T)-alumina or a mixture of an aluminum compound able to form x\ -alumina and an aluminum compound able to form x-alumma and/or y-alumina, and wherein each component is used in such an amount that the final catalyst contains, on the basis of the total amount of the catalyst:
0.5-50wt% of "n-alumina;
0-50wt% of x-alumina and/or y-alumina;
10-70wt% of molecular sieve;
0-75wt%ofclay;and
0.1-8wt% of phosphorus, measured as P2O5.
17. A process for preparing the catalyst according to claim 3, comprising
drying a slurry containing aluminum compound, molecular sieve and water,
with or without clay, and then
calcining the slurry followed adding further a phosphorus compound and a rare earth metal compound,
whererin said aluminum compound is one that is able to form Ti-alumina or a mixture of an aluminum compound able to form n.-alumina and an aluminum compound able to form x-alumina and/or y-alumina, and wherein each component is used in such an amount that the final catalyst contains, on the basis of the total amount of the catalyst: 0.5-50wt% of Ti-alumina; 0-50wt% of %-alumina and/or y-alumina;

10-70wt% of molecular sieve;
0-75wt%ofclay;
0.1-8wt% of phosphorus, measured as P2O5; and
0.1-2wt% of rare earth metal, measured as oxide.
18. A process for preparing the catalyst according to claim 11, comprising
drying a slurry containing aluminum compound, molecular sieve and
water, with or without clay, and then
calcining the slurry followed adding further a phosphorus compound, whererin said aluminum compound is one that is able to form n-alumina or a mixture of an aluminum compound able to form ^-alumina and an aluminum compound able to form x-alumina and/or y-alumina, wherein each component is used in such an amount that the final catalyst contains, on the basis of the total amount of the catalyst:
0.5-50wt% of T]-alumina;
0-50wt% of %-alumina and/or y-alumina;
0-7 5wt% of clay;
0.1-8wt% of phosphorus, measured as P2O5; and
10-70wt% of a molecular sieve,
wherein said molecular sieve is a zeolite mixture containing a zeolite-Y and the MFI-structured zeolite, and wherein the content of the zeolite-Y is 30-90wt%, the content of the MFI-structured zeolite is 10-70wt%, based on the total amount of said zeolite mixture.
19. The process according to claim 16, 17 or 18, wherein said aluminum
compound that is able to form Ti-alumina is (3-alumina trihydrate, the aluminum
compound able to form x-alumina is a-alumina trihydrate, and said aluminum
compound able to form y-alumina is bohemite, pseudo-boehmite and/or alumina
sol.
20. The process according to claim 16, 17 or 18, wherein said phosphorus
compound is one or more selected from the group consisting of phosphoric acid,
phosphate, phosphorous acid, phosphite, pyrophosphoric acid, pyrophosphate,

polyphosphoric acid, polyphosphate, metaphosphoric acid, and metaphosphate.
21. The process according to claim 20, wherein said phosphorus compound
is one or more selected from the group consisting of phosphoric acid,
ammonium phosphate, diammonium hydrogen phosphate, ammonium
dihydrogen phosphate, phosphorous acid, ammonium phosphite, sodium
pyrophosphate, sodium tripolyphosphate and sodium hexametaphosphate.
22. The process according to claim 16, wherein each component is used in
such an amount that the final catalyst contains, on the basis of the total amount
of the catalyst:
5-45wt% of T^-alumina;
0-40wt% of x-alumina and/or y-alumina;
20-50wt% of molecular sieve;
0-60wt% of clay; and
0.5-6wt% of phosphorus, measured as P2OS.
23. The process according to claim 17, wherein said rare earth metal
compound is one or more selected from the group consisting of rare earth
chloride and rare earth nitrate.

Documents:

0863-chenp-2007-abstract.pdf

0863-chenp-2007-claims.pdf

0863-chenp-2007-correspondnece-others.pdf

0863-chenp-2007-description(complete).pdf

0863-chenp-2007-form 1.pdf

0863-chenp-2007-form 26.pdf

0863-chenp-2007-form 3.pdf

0863-chenp-2007-form 5.pdf

0863-chenp-2007-pct.pdf

863-CHENP-2007 AMENDED PAGES OF SPECIFICATION 29-07-2013.pdf

863-CHENP-2007 AMENDED CLAIMS 29-07-2013.pdf

863-CHENP-2007 EXAMINATION REPORT REPLY RECEIVED 01-11-2012.pdf

863-CHENP-2007 EXAMINATION REPORT REPLY RECEIVED 29-07-2013.pdf

863-CHENP-2007 FORM-3 29-07-2013.pdf

863-CHENP-2007 PRIORITY DOCUMENT 29-07-2013.pdf

« Previous Patent

Next Patent »

Patent Number

257312

Indian Patent Application Number

863/CHENP/2007

PG Journal Number

39/2013

Publication Date

27-Sep-2013

Grant Date

23-Sep-2013

Date of Filing

28-Feb-2007

Name of Patentee

CHINA PETROLIUM & CHEMICAL CORPORATION

Applicant Address

6A, HUIXIN DONG STREET, CHAOYANG DISTRICT, BEIJING 100029, CHINA

Inventors:

#	Inventor's Name	Inventor's Address
1	QIU, ZHONGHONG	18 XUEYUAN ROAD, HAIDIAN DISTRICT, BEIJING 100083, CHINA
2	LONG, JUN	18 XUEYUAN ROAD, HAIDIAN DISTRICT, BEIJING 100083, CHINA
3	LU, YOUBAO	18 XUEYUAN ROAD, HAIDIAN DISTRICT, BEIJING 100083, CHINA
4	ZHANG, JIUSHUN	18 XUEYUAN ROAD, HAIDIAN DISTRICT, BEIJING 100083, CHINA
5	DA, ZHIJIAN	18 XUEYUAN ROAD, HAIDIAN DISTRICT, BEIJING 100083, CHINA
6	TIAN, HUIPING	18 XUEYUAN ROAD, HAIDIAN DISTRICT, BEIJING 100083, CHINA
7	ZHU, YUXIA	18 XUEYUAN ROAD, HAIDIAN DISTRICT, BEIJING 100083, CHINA
8	WANG, ZHENBO	18 XUEYUAN ROAD, HAIDIAN DISTRICT, BEIJING 100083, CHINA
9	ZHANG WANHONG	18 XUEYUAN ROAD, HAIDIAN DISTRICT, BEIJING 100083

PCT International Classification Number

B01J 29/00

PCT International Application Number

PCT/CN05/01042

PCT International Filing date

2005-07-14

PCT Conventions:

#	PCT Application Number	Date of Convention	Priority Country