Title of Invention

METHOD OF THERMAL TREATMENT OF METAL OR METAL ALLOY COMPONENTS

Abstract The present invention relates to A method of thermal treatment of components comprising: (a)determining the optimum thermal amplitude of the components at which the phase transformation kinetics of the components is maximum by subjecting samples of the components to cyclic thermal processing at various thermal amplitudes by maintaining the upper temperature constant and varying the lower temperature; (b)selecting a thermal amplitude which is higher than the optimum thermal amplitude; (c)subjecting the components to cyclic thermal processing at the thermal amplitude selected in step (b) to achieve near uniform phase transformation kinetics of the components across their cross section; and (d) cooling down the components to room temperature to obtain components with near uniform microstructure and properties.
Full Text CO.MPLETE AFTER PROVISIONAL
FORM 2 LEFT ON 6 DEC 2006
THE PATENTS ACT, 1970 (39 of 1970)
As amended by the Patents (Amendment) Act, 2005
&
The Patents Rules, 2003
As amended by the Patents (Amendment) Rules, 2006
COMPLETE SPECIFICATION
(See section 10 and rule 13)
TITLE OF THE INVENTION
Method of thermal treatment of components INVENTORS
a) Names : Sahay Satyam Suraj and Krishnan Karthik
b) Address : both of Tata Research Development & Design Centre, A division of Tata Consultancy Services Limited, 54 Hadapsar Industrial Estate, Pune 411013, Maharashtra, India
c) Nationality : both Indian Nationals
APPLICANTS
Name : Tata Consultancy Services Ltd
Nationality: Indian Company
Address: Air India Building, 11th floor, Nariman Point, Mumbai 400 021,
Maharashtra, India
PREAMBLE TO THE DESCRIPTION
The following specification particularly describes the nature of this invention and the manner in which it is to be performed:


FIELD OF INVENTION
This invention relates to a method of thermal treatment of components.
The term "components" as used in the specification includes parts which are fabricated, shaped, formed or cast with materials or compacted with powder. Examples of the components include bearings, wheels, sprockets, gears, shafts, wires or rods used in various industries including automotive, aerospace or electrical and electronic industries.
BACKGROUND OF INVENTION
Components are subjected to thermal treatment to bring about changes in their micro structure and to develop various properties such as hardness, ductility or tensile strength so as to obtain the desired performance of the components. Thermal treatment is generally carried out by isothermal processing or cyclic thermal processing. Isothermal or cyclic thermal processing comprises isothermal or cyclic annealing, age hardening or sintering. During isothermal thermal processing, depending upon the material and nature of the components, they are heated to a set temperature, soaked at this temperature for a predetermined period of time and cooled to a predetermined temperature. Heating and cooling of the components is repeated for a set period of time before the components
2

are finally cooled down to room temperature. During isothermal thermal processing, the surface and core regions of the components are invariably at different temperatures ie during the heating cycle the surface region attains the desired temperature faster than the core region and is hotter than the core region and during the cooling cycle the surface region becomes cooler faster than the core region and is cooler than the core region. As the core region lags in attaining the desired temperature, phase transformation kinetics at the core is not as fast as the phase transformation kinetics at the surface region. Therefore, development of changes in the microstructures and properties of the components vary or differ across the crosssection of the components. Such variations in the microstructures and properties of the components reduce the performance of the components. Moreover, the time required for isothermal thermal processing is longer thereby reducing productivity. Also, as the isothermal thermal processing involves heating of the components at a constant temperature for a long duration, the energy consumption is high. Because of reduced productivity and high energy consumption, isothermal thermal processing is very expensive. Due to high temperature heating for long duration, emissions from the furnace are also correspondingly increased. During cyclic thermal processing, the components are heated between two temperatures before being cooled down to room temperature. This accelerates phase transformation kinetics
3

and development of changes in the microstructures and properties of the components. [Ref Acta Materialia, Vol 51, No 2, (2003) 339-346 titled "Accelerated grain growth behavior during cyclic annealing" by S.S. Sahay, C.P. Malhotra and A.M. Kolkhede; Acta Materialia, Vol. 50, No. 6 (2002) 1349-1358 titled "Enhanced densification of zinc powders through thermal cycling" by C.A. Schuh and D.C. Dunand; Metallurgical and Materials Transactions ,Vol. 28A (1997) 1809-1814 entitled "Thermal cycling behavior of as quenched and aged ti-6al-4v alloy" by H. Geng, S. He, and T. Lei]. Due to the accelerated development of changes in the microstructures and properties of the components, the heating time is reduced and productivity is increased. As the thermal processing is carried out between two temperatures for a short duration, the energy requirement is also reduced correspondingly reducing emissions from the furnace. (Ref Forecast Issue of ASM Heat Treating Progress, January 2003, 44 titled "Energy reduction via cyclic heat treatments" by Satyam S Sahay). Due to increased productivity and reduced energy consumption, cyclic thermal processing is cost effective. During cyclic thermal processing also, however, development of changes in the microstructures and properties of the components differ across the crossection thereof as the core region lags in attaining the desired temperature as compared to the surface region. As a result, as in the case
4

of similar to the isothermal processing, the performance of components obtained by cyclic thermal processing is also reduced.
OBJECTS OF INVENTION
An object of the invention is to provide a method of thermal treatment of components, which method produces components having near uniform changes in their microstructures and properties across the crosssection thereof thereby improving the performance of the components.
Another object of the invention is to provide a method of thermal treatment of components, which method reduces the treatment time and increases productivity.
Another object of the invention is to provide a method of thermal treatment of components, which method requires reduced quantity of energy and treatment time correspondingly reducing emissions from the furnace.
Another object of the invention is to provide a method of thermal treatment of components, which method is cost effective.
5

DETAILED DESCRIPTION OF INVENTION
According to the invention there is provided a method of thermal treatment of components comprising:
(a) determining the optimum thermal amplitude of the components at which the phase transformation kinetics of the components is maximum by subjecting samples of the components to cyclic thermal processing at various thermal amplitudes by maintaining the upper temperature constant and varying the lower temperature;
(b) selecting a thermal amplitude which is higher than the optimum thermal amplitude;
(c) subjecting the components to cyclic thermal processing at the thermal amplitude selected in step (b) to achieve near uniform phase transformation kinetics of the components across their crosssection; and
(d) cooling down the components to room temperature to obtain components with near uniform microstructure and properties.
The higher thermal amplitude is. selected in step (b) by mathematical simulation or experimentally after the optimum thermal amplitude is determined.
6

The upper temperatures of the various thermal amplitudes at which the components are subject to cyclic thermal annealing in step (a) will depend upon the material of the components and is generally the higher temperature at which the isothermal thermal processing of the components is carried out. Typically for titanium, steel or aluminium the upper temperatures are 925 °C, 725 °C and 450 °C, respectively.
The following comparative experimental example is illustrative of the invention but not limitative of the scope thereof:
EXAMPLE 1
a) Samples from Ti -6A1-4V alloy rods (each of 15 mm diameter and 3 mm thickness) were subjected to cyclic thermal processing at different thermal amplitudes in a laboratory furnace. The upper temperature of the thermal amplitudes was kept constant at 925°C and the lower temperature of the thermal amplitudes was varied from 750 to 850°C. The heating and cooling rates for all the samples were kept at 5°C/min. The optimum thermal amplitude at which phase transformation kinetics of the samples was maximum was found to be when the samples were annealed at the thermal amplitude of 100°C with the higher and lower temperatures at 925°C and 825°C, respectively as illustrated in Fig 1 of the
7

accompanying drawings. A thermal amplitude of 150°C higher than the optimum thermal amplitude was selected wherein the upper temperature was 925°C and the lower temperature was 775°C. The higher thermal amplitude was selected by mathematical simulation.. The rods were subjected to cyclic thermal processing at the thermal amplitude of 150°C for 3 hrs in a batch furnace. The heating and cooling rates of the rods were kept at 5°C/min. The rods were cooled down to ambient temperature after 3 hrs of thermal processing and subjected to simulation tests. The test results were as shown in Figs 2 and 3 of the accompanying drawings. Curve A and curve B in Fig 2 relate to the temperature profile or evolution of heat in the surface and core regions of the gears, respectively. It is seen from Fig 2 that at any given point during thermal processing the core region of the rods lies at the optimum thermal amplitude of 100°C and that the temperature in the surface and core regions of the rods was practically the same. As the core region lies at the optimum thermal amplitude, the phase transformation characteristics of the coreis maximum. This gives rise to near uniform development of changes in the microstructures and properties of the components across their crosssection. Curve A and curve B in Fig 3 relate to the grain size in the surface and core regions of the rods, respectively. It is seen that after approximately 3 hrs of cyclic thermal processing, the grain size of the surface region and the core region was practically the same.
8

b) Samples from Ti -6A1-4V alloy rods (each of 15 mm diameter and 3 mm thickness) were subjected to isothermal thermal processing at 925°C in a laboratory furnace for 3.5 hrs. After the 3.5 hrs the rods were cooled down and subjected to simulation tests. The test results were as shown in Fig 4 of the accompanying drawings. Curve A and curve B in Fig 4 relate to the grain size in the surface and core regions of the rods, respectively. It was seen that even after approximately 3.5 hrs of thermal processing, the grain size of the surface region and the core region was non-uniform. Performance of the components obtained by isothermal thermal processing as described above would be correspondingly reduced due to the non-uniform changes in the microstructures of the components and properties across the crosssection thereof.
According to the invention cyclic thermal processing is carried out at a thermal amplitude at which phase transformation kinetics of the core is maximum so that development of changes in the microstructurs and properties of the components both in the core and surface regions thereof is near uniform. This enhances the performance of the components. As the development of changes in the microstructures and properties of the components is faster, the duration of the method of the
9

invention is reduced and productivity is increased. As the thermal processing is carried out between two temperatures the energy requirement of the method of the invention is also reduced. The reduced energy requirement and process time significantly reduces the emissions from the furnace. The method of the invention is cost effective because of the increased productivity and reduced energy requirement.
10

We Claim
1. A method of thermal treatment of components comprising:
(a) determining the optimum thermal amplitude of the components at which the phase transformation kinetics of the components is maximum by subjecting samples of the components to cyclic thermal processing at various thermal amplitudes by maintaining the upper temperature constant and varying the lower temperature;
(b) selecting a thermal amplitude which is higher than the optimum thermal amplitude;
(c) subjecting the components to cyclic thermal processing at the
thermal amplitude selected in step (b) to achieve near uniform
phase transformation kinetics of the components across their
crosssection; and
(d) cooling down the components to room temperature to obtain
components with near uniform microstructure and properties.
2. A method as claimed in claim 1, wherein the cyclic thermal
processing is carried out by cyclic annealing, age hardening or sintering.
11

3. A method as claimed in claim 1, wherein the lower temperature of the higher thermal amplitude selected at step (b) is 50-150°C lower than the upper temperature of the higher thermal amplitude selected at step (b)
4. A method as claimed in claim 1, wherein the cyclic thermal processing at step (c) is carried out by heating and cooling the components at the rates of 5 - 15 °C/min.
5. Components obtained by the method as claimed in any one of claims 1 to 4.

(Prita Madan)
ofKhaitan&Co
Agent for the Applicants
Dated this 4th day of December 2006
12

ABSTRACT
A method of thermal treatment of components. The optimum thermal amplitude of the components at which the phase transformation kinetics of the components is maximum is determined by subjecting samples of the components to cyclic thermal processing at various thermal amplitudes by maintaining the upper temperature constant and varying the lower temperature. A thermal amplitude which is higher than the optimum thermal amplitude is selected. The components are subjected to cyclic thermal processing at the thermal amplitude selected above to achieve near uniform phase transformation kinetics of the components across their crosssection. The components are cooled down to room temperature to obtain components with near uniform microstructure and properties.
-6 DEC 2006

Documents:

1573-MUM-2005- FORM 3(14-9-2009).pdf

1573-MUM-2005-ABSTRACT(23-7-2012).pdf

1573-mum-2005-abstract-complete.doc

1573-mum-2005-abstract-complete.pdf

1573-mum-2005-abstract-provisional.doc

1573-mum-2005-abstract-provisional.pdf

1573-mum-2005-annexure to form 3(12-12-2006).pdf

1573-MUM-2005-CLAIMS(AMENDED)-(23-7-2012).pdf

1573-mum-2005-claims-camplete.pdf

1573-mum-2005-claims-complete.doc

1573-mum-2005-claims-provisional.doc

1573-mum-2005-claims-provisional.pdf

1573-mum-2005-correspondence 1(4-11-2008).pdf

1573-mum-2005-correspondence 2(9-1-2006).pdf

1573-MUM-2005-CORRESPONDENCE(1-7-2009).pdf

1573-MUM-2005-CORRESPONDENCE(10-7-2013).pdf

1573-MUM-2005-CORRESPONDENCE(14-9-2009).pdf

1573-MUM-2005-CORRESPONDENCE(4-11-2008).pdf

1573-MUM-2005-CORRESPONDENCE(4-12-2012).pdf

1573-mum-2005-correspondence-received-ver-011206.pdf

1573-mum-2005-correspondence-received-ver-041206.pdf

1573-mum-2005-correspondence-received-ver-141205.pdf

1573-mum-2005-descripiton (complete).pdf

1573-mum-2005-descripiton (provisonal).pdf

1573-mum-2005-drawings-complete.pdf

1573-mum-2005-drawings-provisional.pdf

1573-MUM-2005-FORM 1(23-7-2012).pdf

1573-mum-2005-form 13(1-12-2006).pdf

1573-MUM-2005-FORM 13(23-7-2012).pdf

1573-mum-2005-form 18(28-2-2008).pdf

1573-MUM-2005-FORM 2(TITLE PAGE)-(23-7-2012).pdf

1573-MUM-2005-FORM 3(23-7-2012).pdf

1573-mum-2005-form-1.pdf

1573-mum-2005-form-13.pdf

1573-mum-2005-form-2-complete.doc

1573-mum-2005-form-2-complete.pdf

1573-mum-2005-form-2-provisional.doc

1573-mum-2005-form-2-provisional.pdf

1573-mum-2005-form-26.pdf

1573-mum-2005-form-5.pdf

1573-MUM-2005-MARKED COPY(23-7-2012).pdf

1573-MUM-2005-PETITION UNDER RULE 137(23-7-2012).pdf

1573-MUM-2005-PUBLICATION REPORT(4-11-2008).pdf

1573-MUM-2005-REPLY TO EXAMINATION REPORT(23-7-2012).pdf

1573-MUM-2005-SPECIFICATION(AMENDED)-(23-7-2012).pdf

1573-MUM-2005-US DOCUMENT(23-7-2012).pdf

abstract1.jpg


Patent Number 257024
Indian Patent Application Number 1573/MUM/2005
PG Journal Number 35/2013
Publication Date 30-Aug-2013
Grant Date 27-Aug-2013
Date of Filing 14-Dec-2005
Name of Patentee TATA CONSULTANCY SERVICES LTD.
Applicant Address AIR INDIA BUILDING, 11TH FLOOR, NARIMAN POINT, MUMBAI.
Inventors:
# Inventor's Name Inventor's Address
1 SATYAM SURAJ SAHAY TATA RESEARCH DEVELOPMENT & DESIGN CENTRE, A DIVISION OF TATA CONSULTANCY SERVICES LIMITED, 54, HADAPSAR INDUSTRIAL ESTATE, PUNE 411 013.
2 KARTHIK KRISHNAN TATA RESEARCH DEVELOPMENT & DESIGN CENTRE, A DIVISION OF TATA CONSULTANCY SERVICES LIMITED, 54, HADAPSAR INDUSTRIAL ESTATE, PUNE 411 013.
PCT International Classification Number C04B41/91
PCT International Application Number N/A
PCT International Filing date
PCT Conventions:
# PCT Application Number Date of Convention Priority Country
1 NA