Title of Invention

SUBMARINE HULL STEEL HAVING ENHANCED WELDABILITY

Abstract The invention relates to a steel for the production of submarine hulls, which is characterized in that the chemical composition thereof comprises, by weight percent: 0.03% < C < 0.08 %; 0.04 % < Si < 0.48 %; 0,1 % < Mn < 1.4 %; 2 % < Ni < 4 %; Cr < 0.3 %; 0.3 % < Mo _ W/2 + 3 (V -f Nb/2 + Ta/4) < 0.004 %; Nb < 0.004 %; Cu < 0.45 %; Al < 0.1 %; Ti < 0.04 %; N < 0.03 % the remainder comprising iron and impurities resulting from production, boron being an impurity with a concentration of less than 0.0005 % and P + S < 0.015 %, the chemical composition satisfying condition 410 < 540 x C0.25 + 245 [Mo + W/2 + 3 (V + Nb/2 + Ta/4)]0.30 < 460. The inventive steel has an essentially martensitic or lower bainitic structure comprising at least 90% martensite or lower bainite, at most 5% residual austenite, at most 5% ferrite. The steel has a yield strength of between 480 Mpa and 620 Mpa and a Charpy toughness V, Kcv at -60oC of more than 50J.
Full Text Submarine hull steel having enhanced weldability
The present invention relates to a steel for the production of submarine hulls which are constituted by rolled or forged steel components which are assembled by means of welding.
In order to be able to immerse in deep water without making the vessel excessively heavy, hulls of submarines are generally constituted by sheets of steel having a thickness of between 40 and 50 mm, and optionally forged components which have a thickness of between 100 and 150 mm and which are constituted by a very high strength steel having a very good impact resitance even at low temperatures, so as to provide a good degree of reliability even in the case of intense dynamic loads, and which can be relatively easily welded so as to allow assemblies of a high quality to be produced.
The steels which are conventionally used are steels of the series referred to as 60 or 80 HLES, whose chemical composition comprises approximately 0.10% of carbon, from 2 to 4% of nickel, from 0.2 to 0,4% of silicon, molybdenum and vanadium at contents such that Mo + 3V is between 0.3 and 0.5%, between 0.8 and 1.2% of Mn, between 0.1 and 0.5% of Cr, the balance being iron, impurities and optionally low quantities of deoxidation elements. These steels are used to produce components such as sheets or forged components which are quenched and tempered so as to have a tempered structure which is on the whole martensitic, that is to say, which contains more than 90% of martensite and of which the yield strength is between 550 and 550 MPa, the tensile strength is between 600 and 7 50 MPa, the elongation at break is between

15 and 20%, the Charpy toughness Kcv is greater than 80 J at -80°C.
Components which are produced from these steels are assembled
by means of welding with preheating to a temperature in the order of at least 150°C in order to prevent problems of cracking in the cold state.
These welding conditions are required in particular because the weld seams which are produced are weld seams which are very extensively flanged and which can produce stresses of almost 80% of the elastic limit, and because the weld seams are carried out on sites in which the temperature may drop to a level in the region of 0°C.
The need for carrying out a preheating operation at a high temperature is a disadvantage which makes it difficult to weld components of submarine hulls. Therefore, it is desirable to be able to have a steel which allows weld seams to be produced under less severe conditions, that is to say, without pre-heating, or at least by carrying out only a baking operation of the sheets which does not exceed 100°C, or preferably, 50°C, in spite of the very extensive flanges of the weld seams and in spite of the relatively low outside temperatures of the site.
It has been proposed, in particular in patent application WO93/24269, that the welding conditions be improved for submarine hulls which are produced from a steel of the 60 or 80 HLES type, by using welding electrodes which are different from the electrodes defined by the construction standards which are applied in this field, these welding electrodes leading to low-carbon bainitic structures (LCBS) .

However, this technique has disadvantages since the reduction of the risk of cracking which is thus obtained in the region of the deposited metal nonetheless does not overcome the problem of the risk of cracking brought about by the welding operation in the base metal itself, in the region of the heat affected zone.
The object of the present invention is to overcome these disadvantages by providing a weldable steel with a high yield strength for producing submarine hulls by assembling components, by means of welding, which are constituted by thick sheets or forged components and which have a yield strength of between 480 and 620 MPa, a toughness measured in terms of a Charpy V Kv greater than 50J at -60°C, preferably greater than 50J at -85°C, and for which there is a reduction in the risks of occurrences of cracking in the base metal, brought about by a welding operation in the region of the heat affected zone.
To this end, the invention relates to a steel for producing submarine hulls, characterised in that the chemical composition thereof comprises, in % by weight:



the balance being iron and impurities resulting from the production operation, boron being an impurity whose content is less than 0.0005%, and ? + S
the steel having a structure which is substantially martensitic or lower bainitio or which is substantially constituted by a mixture of these two structures, comprising at least 90% of martensite or lovjer bainite or a mixture of these two structures, a maximum of 5% of residual austenite, a maximum of 5% of ferrite, with a yield strength of between 480 MPa and 620 MPa and a Charpy toughness V, kcv greater than 50 J at -60°C.
Preferably, the chemical composition is such that one or more of the following conditions is complied with:


The invention also relates to a submarine hull component having a thickness of between 15 mm and 150 mm, of forged or rolled steel which has been quenched and tempered according to the invention and a submarine hull comprising components according to the invention which are assembled by means of welding.
The invention finally relates to the use of the steel according to the invention for producing a submarine hull comprising components which have thicknesses of between 15 mm and 150 mm and which are assembled by means of welding, the welding being able to be carried out on components which have not been pre-heated or which have been preheated to a temperature which does not exceed 25°C.
The invention will now be described in a more precise but non-limiting manner with reference to the single Figure which illustrates the path of the minimum temperature of non-cracking during welding as a function of the content of highly carbide-producing elements, and illustrated by means of examples.
The inventors found in a novel and unexpected manner that it was possible to produce, for submarine hulls which have features in accordance with the features generally required for producing submarines, components which can be more readily welded than components for submarines produced from known steel. To this end, it was necessary to use a steel whose composition had been modified compared with that of known steels, on the one hand, by substantially lowering the contents in terms of carbon and, on the other hand, by increasing the contents in terms of highly carbide-producing elements, that is to say, elements which are capable of

precipitating in the form of fine and dispersed carbides which harden but do not embrittle, this steel having to have a structure which is substantially martensitic, that is ro say, which comprises more than 90% of martensite, the balance being constituted by less than 5% of residual austenite and less than 5% of ferrite. However, it has been found that the martensite component may, without excessively impairing the toughness, be completely or partially replaced with bainite of the lower type, that is to say, bainite in the form of laths which in this respect have a micrographic appearance which is similar to martensite.
The chemical composition of the steel which has been modified in this manner comprises in % by weight:
- more than 0.03% of carbon and preferably more than 0.035%, but less than 0.080% and preferably less than 0,060% and even more preferably less than 0.055%, in order to allow, on the one hand, the formation of hardening carbides during tempering but without impairing the toughness of the base metal and in particular the toughness in the heat affected zone during the welding operation; the content in terms of carbon being limited in particular in order to reduce the deformations linked to the martensitic transformation in the zone affected by the temperature in the welding zone, which is necessary in order to limit the effects of flanging and therefore reduce the susceptibility of the metal to cracking during the welding operation,
- from 0.04% to 0.48% of silicon in order to deoxidise the bath of liquid steel. Preferably, however, the silicon content will be reduced and will remain less than 0.29%, preferably less than 0.25% and, even more preferably, less than 0.19% so as to improve the thermal conductivity of the steel, which will have the effect of reducing the thermal

gradients during the welding operation and thus reducing the resulting mechanical constraints, which reduces the susceptibility of the steel to cracking during the production of flanged weld seams,
- up to 1.4% of manganese in order to improve the quenchability but without forming excessively large segregated strips. Since the steel also contains other quenching elements, manganese is not strictly indispensable and the content thereof-may be limited to 1.2%, and more preferably to 1.0%; it can also be present in trace levels. However, in order in particular to facilitate the production of the steel, the manganese content will preferably be at least equal to 0.2%, even 0.6%,
- at least 2.1% and more preferably 2.5% and even more preferably 2.7% of nickel in order to improve the quenchability, which is necessary in order to ensure that the desired type of microstructure is obtained, that is to say, a structure which is substantially constituted by martensite or lower bainite or a mixture of these two structures. The nickel content may be up to 5%, but in practice and taking into account the cost of this element, the content will preferably be less than 4% and even more preferably less than
3.5%.
- less than 0.3% and preferably less than 0.15% and even more
preferably less than 0.09% of chromium. This carbide-
producing element is not desirable. It is capable of forming
relatively solid carbides which do not have a particularly
advantageous effect on the properties of the steel according
to the invention. Consequently, if it were too high a
quantity, it would consume carbon which would then no longer
be available to form hardening carbides with other highly
carbide-producing elements which form hardening carbides
which are fine and dispersed. Chromium is therefore

considered to be a residue resulting from the production operation. Compliance with the limitation relating to the content of this element means that the steel has to be produced from raw materials which are selected with care. These precautions are important more particularly when the raw materials are constituted principally by scrap iron which is generally the case for this type of steel, - highly carbide-producing elements which form precipitated carbides which are fine and hardening. These elements are molybdenum and tungsten, on the one hand, vanadium, niobium and tantalum, on the other hand. For these elements, the total by weight [No + W/2 + 3 (V + Nb/2 + Ta/4)] must be at least 0.30%, and preferably 0.35%, and even more preferably 0.4%. This total must not be too high in order to limit the unfavourable effects on the toughness and homogeneity of the metal, which would result from contents beyond that which is necessary for the desired hardening. Consequently, the total by weight of highly carbide-producing element remains less than 0.89%, and preferably less than 0.69%, and more preferably less than 0,59%. Furthermore, molybdenum and tungsten are preferable since vanadium, niobium and tantalum have a significant embrittling effect. Therefore, the total by weight V + Nb/2 + Ta/4 remains less than 0.004%, and since niobium is more harmful to the toughness than vanadium, the content thereof is limited to 0.004% and the elements vanadium, niobium and tantalum are preferably present in trace levels. Conversely, the content in terms of molybdenum will be a minimum of 0.15% and more preferably 0.30% and even more preferably 0.45%. Molybdenum may be preferred to tungsten since it is more commonly used and is generally more economical than tungsten. However, tungsten has the advantage of reducing the formation of segregated zones which have unfavourable effects on the toughness of the metal, and it is

thus still preferable to have a content of tungsten greater
than 0.11%, '
- less than 0.45%, and more preferably less than 0.25% of copper so as not to impair the forgeability and to promote the suitability of the sheets for subsequent shaping,
- up to 0.10% of aluminium and preferably less than 0.040%,' but preferably more than 0.004%, and more preferably more than 0.010%, in order to deoxidise the steel and form aluminium nitrides which allow the growth of the grain to be controlled during the thermal processing operation,
- the content of nitrogen is preferably between 0.0010% and 0.0150% in order to facilitate the formation of aluminium nitrides which allow the growth of the grain to be controlled; the content in terms of nitrogen may exceed 0.0150%, but it
is desirable for this content not to exceed 0.0,300% and preferably not to exceed 0.0200% so as not to impair the suitability for shaping the products in a cold or tepid state,
- optionally up to 0.04% of titanium, an element which has a
comparable effect to that of aluminium. However, since
titanium has a tendency to form precipitates which have a
very embrittling effect, it is preferable to limit the
content of this element to trace levels.
The balance of the composition is constituted by iron and impurities resulting from the production operation. Amongst these impurities, boron must remain at trace levels, that is to say, at contents of less than 0.000 5%. This is to prevent the embrittling effect of this element and its compounds in the form of nitrides and carbides. Although boron is an element which is commonly used in order to enhance the quenchability of steels having a high elastic limit, the very high level of impact resistance desired in this instance leads to the use of the contribution of boron being avoided.

Also amongst the impurities, phosphorus and sulphur must be limited to contents such that the total P + s remains less than 0.015%, and preferably less than 0.012%, and even more preferably less than or equal to 0.009% in order not to impair the toughness of the steel. This restriction requires the steel to be produced with particularly strict precautions being taken. Nowadays, a person skilled in the art, who must comply with these restrictions, is aware of how to proceed.
Furthermore, in order to obtain adequate mechanical
characteristics and in particular the yield strength and
tensile strength, the chemical composition of the steel must
be such that the quantity
R = 540 X C0.25 + 245 [Mo = W/2 - 3 (V = Nb/2 + Ta/4) ]0.30
is between 410 and 460 and preferably between 425 and 450.
In order to produce sheets or components which are intended for producing submarines, it is possible to proceed as indicated below.
First of all, the steel is produced in known manner, for example, in an electric oven, taking all the necessary precautions known to the person skilled in the art in order to comply with the purity restrictions of the steel indicated above, the steel is then poured in the form of bars or slabs depending on the type of components it is desirable to produce. The bars or slabs are then formed by means of plastic deformation in the hot state, that is to say, by means of rolling or forging, by reheating them to a temperature such that the beginning of the transformation at heat is carried out at a temperature greater than 1000oC, and preferably greater than 1050°C, and even more preferably

greater than 1100°C, in order to limit surface defects. However, the reheating temperature must preferably remain less than 1260°C and more preferably less than 1220°C, in order in particular to limit excessive growth of the grain at this stage. After the operation for shaping by means of plastic deformation in the hot state, the components produced are subjected to a thermal processing operation relating to the quality comprising a quenching operation either starting from the forming heat or preferably, after reaustenitisation at a temperature which is at least equal to AC3 and generally between approximately 860 and 950°C. The cooling can be achieved in accordance with all known quenching means, such as those using air, oil or water, in accordance with the solidity of the components in question in order to obtain a substantially martensitic microstructure after quenching. The person skilled in the art knows how to select, on a case by case basis, the most suitable quenching means.
The quenching is followed by at least one tempering operation which is preferably carried out at a temperature of between 550°C and 670°C.
Using this method, it is possible to obtain sheets or forged components whose mechanical characteristics over the entire thickness are in accordance with that desired for the production of submarines, that is to say, a yield strength of between 480 MPa and 620 MPa and preferably between 500 MPA and 600 MPa, and a Charpy toughness Kcv greater than 50J at -60°C.
The effect of the chemical composition on the suitability for welding is illustrated by the examples whose analyses are set out in tables 1 and 2. For the examples of the tables,

niobium, tantalum and titanium are at trace levels so that the values of Mo + W/2 + 3V indicated in the table are equal to the quantities Mo + 3 (V + Nb/2 + Ta/4); boron is at trace levels with a content of less than 0.0005%; aluminium is between 0.015% and 0.025%. In table 1, the total P + S is expressed in 10-3%. In table 2, the total P + S remains less than 0 . 015% .
Examples 1 and 2 are in accordance with the prior art and examples 3 to 9 and 6a to 9a are in accordance with the invention. Example 10 is given by way of comparison.


Table 1 (contd.)

Table 2


Examples 1 to 9 illustrate the combined effect of the content in terms of carbon and the highly carbide-producing elements for conventional contents of silicon. Examples 6a, 7a, 8a and 9a illustrate the particular effect of silicon.
The effect on the weldability can be evaluated in particular using a test by means of which the minimum preheating temperature is determined for the auto-flange weld joint for which cracking is not seen to appear after welding. This test involves producing weld seams with preheating temperatures of 150°, 125°, 100°, 75°, 50°, 25°, 5° and observing the joints obtained in order to detect the presence or absence of cracks
The results of this evaluation, which correspond to the examples of tables 1 and 2, are illustrated in the single Figure in which a first line 1 can be seen which represents the path of the minimum non-cracking temperature as a function of the content of highly carbide-producing elements for a silicon content in the order of 0.3%.
On this line, it is found that, when the content of highly carbide-producing elements increases and the content in terms of carbon decreases at the same time, up to a content of highly carbide-producing elements in the order of 0.6%, the minimum non-cracking temperature decreases. Beyond approximately 0.6%, the minimum non-cracking temperature begins to increase again. Using micrographic examination in the region of the cracks of the castings 9 and 10 which correspond to the highest contents in terms of highly carbide-producing elements, it can be established that the cracks appear in segregated zones whose hardness is found to be particularly high in spite of a relatively low carbon

content. This high level of hardness c-f the segregated zones probably results from a co-segregation of the carbon and the highly carbide-producing elements.
Upon examination of this line, it appears that an optimum level of weldability is obtained for contents of highly carbide-producing elements of between approximately 0.4% and 0.65%.
Line 2, which corresponds to steels having compositions which are comparable but which have a much lower silicon content than in the example above, indicates that, when the content in terms of silicon is reduced, the minimum non-cracking temperature is reduced by 20°C to 25°C.
This effect of the silicon can be attributed to the effect of the silicon on the thermal conductivity. By reducing the level of silicon which significantly impairs the thermal conductivity of the steel, the temperature gradients are reduced in the heat affected zone, which has the effect of reducing the levels of stress.
This can be confirmed by measurements of the thermal conductivity of the castings 6a to 9a and 6 to 9 which are comparable therewith. Measurements of this type would show that the thermal conductivity of the castings 6a and 9a is greater than that of the castings 6 to 9 by approximately 10%
With the steel according to the invention, it is possible to produce components for submarine hulls, for example, components which are cut from sheets having a thickness of between 40 and 60 mm, or forged components such as connection components whose great thicknesses can be up to 100 to 150 mm

Using these components whose characteristics have been indicated above, it is possible to produce submarine hulls by assembling these components by means of welding on open air sites, the outside temperature being able to reach 0°C. These components can be welded in a satisfactory manner with no pre-heating, or with preheating to less than 25°C.
When the "coated electrode" method is used, which is generally recommended for the welding operations considered in this instance, the precautions for use which are intended to limit the content of hydrogen introduced must be complied with to the greatest possible extent, that is to say, storage in the dry state and prior baking of the electrodes. The type of electrode used may correspond, for example, to the type E55 2NiMo in accordance with the standard EN757.
The solid wire MIG method which naturally introduces practically no hydrogen, is to be preferred wherever possible using, for example, a wire of the type G55 Mn4Ni2MO in accordance with the standard EN 12534.
These indications relating to the welding method constitute non-limiting recommended values in this instance.











CLAIMS
1. Use of a steel for producing submarine hulls, comprising steel components which have thicknesses-of between 15 mm and 150 mm and which are assembled by means of welding,
characrerised in that the chemical composition of the steel comprises,, in % by weight:

the balance being iron and impurities resulting from the production operation, boron being an impurity whose content is less than 0.0005%, and P + S
the steel having a structure which is substantially martensitic, comprising at least 90% of martensite, a maximum of 5% of residual austenite, a maximum of 5% of ferrite, the steel having an elastic limit of between 480 MPa and 620 MPa and a Charpy strength V, Kcv greater than 50 J at -60CC.
MODIFIED SHEET

2. Use of a steel according to claim 1, characterised in rh
Si 3. Use of a steel according to claim 1 or claim 2,
characterised in that:
Mn £ 1%.
4. Use of a steel according to any one of claims 1 to 3,
characterised in that:
W > 0.11%.
5. Use of a steel according to any one of claims 1 to 4,
characterised in that:
2-5% 6. Use of a steel according to any one of claims 1 to 4,
characterised in that:
Cr 7. Use of a steel according to claim 6, characterised in tha
Cr 8. Use of a steel according to any one of claims 1 to 7,
characterised in that:
425 9. Use of a steel according to any one of claims 1 to 8,
characterised in that:
Ni > 2.7%.
10. Use of a steel according to any one of claims 1 no 9,
characterised in that;
MODIFIED SHEET

Mo '11. Use of a steel according to any one of claims 1 ro 10,
- *?
characterised in that:
C 12. Use of a steel according to claim 1, characterised in that:
titanium being absent or present in trace levels.
13. Use of a steel according to any one of claims 1 to 12,
characterised in that the components are assembled by means
of welding with no preheating or with preheating to a
temperature less than or equal to 25°C, including when the
welding is carried out on a site on which the outside
temperature is less than 0°C.
14. Submarine hull components, which have a thickness of
between 15 mm and 150 mm, of forged or rolled steel which has
MODIFIED SHEET

been quenched and tampered, and which are obtained by the use of a steel, according to any one of claims 1 to 12.
15. Submarine hull comprising components according to claim
14, which are assembled by means of welding.
16. Steel for the production of submarine hulls,
characterised in that the chemical composition thereof is in
accordance with that of the steel used according to any one
of claims 1 to 12, and in that, furthermore, the silicon
content thereof is less than or equal to 0,19%.


Documents:

5368-CHENP-2007 AMENDED PAGES OF SPECIFICATION 23-08-2011.pdf

5368-CHENP-2007 AMENDED CLAIMS 23-08-2011.pdf

5368-CHENP-2007 CORRESPONDENCE OTHERS 20-06-2011.pdf

5368-chenp-2007 form-3 23-08-2011.pdf

5368-CHENP-2007 OTHER PATENT DOCUMENT 23-08-2011.pdf

5368-CHENP-2007 EXAMINATION REPORT REPLY RECEIVED 23-08-2011.pdf

5368-chenp-2007-abstract.pdf

5368-chenp-2007-claims.pdf

5368-chenp-2007-correspondnece-others.pdf

5368-chenp-2007-description(complete).pdf

5368-chenp-2007-drawings.pdf

5368-chenp-2007-form 1.pdf

5368-chenp-2007-form 18.pdf

5368-chenp-2007-form 3.pdf

5368-chenp-2007-form 5.pdf

5368-chenp-2007-pct.pdf


Patent Number 249255
Indian Patent Application Number 5368/CHENP/2007
PG Journal Number 42/2011
Publication Date 21-Oct-2011
Grant Date 13-Oct-2011
Date of Filing 26-Nov-2007
Name of Patentee INDUSTEEL FRANCE
Applicant Address IMMEUBLE "PACIFIC", LA DEFENSE 7, 11/13 COURS, VALMY, 92800 PUTEAUX, FRANCE.
Inventors:
# Inventor's Name Inventor's Address
1 BEGUINOT, JEAN 12 RUE DES PYRENEES, 71200 LE CREUSOT, FRANCE.
2 CHAUVY, CEDRIC 4 CHEMIN DE CAMUZELLE, F-71670 SAINT FIRMIN, FRANCE.
PCT International Classification Number C22C 38/00
PCT International Application Number PCT/FR2006/001150
PCT International Filing date 2006-05-19
PCT Conventions:
# PCT Application Number Date of Convention Priority Country
1 0505333 2005-05-26 France