|Title of Invention||
"AN ADSORBENT BED FOR PURIFICATION OF A GAS STREAM AND PROCESS THEREOF"
|Abstract||An adsorbent bed for purification of a gas stream comprising: a first layer of adsorbent adapted for the removal of water; a second layer of adsorbent comprising a mixture of adsorbents, wherein at least one component of the said mixture has a bulk density of greater than or equal to 32 lb/ft3; a third layer of adsorbent comprising an adsorbent having a bulk density of greater than or equal to 32 lb/ft3; and a fourth layer of adsorbent having a N2 Henry's Law constant of greater than 1.5 mmol/g.bar.|
|Full Text||The present invention relates to an adsorbent bed for purification of a gas stream and process thereof.
Field of the Invention
 This invention relates to a pressure swing
adsorption (PSA) system and process for purifying
impure gas streams containing more than 5 0 mole %
hydrogen, and more particularly to such a process for
the production of high purity hydrogen from various
hydrogen-containing feed mixtures such as synthesis
gas. The improved process provides higher hydrogen
recovery and lower adsorbent inventory as compared with
previously disclosed PSA processes for hydrogen
Background of the Invention
 There is an'increasing need for high purity hydrogen in the.chemical process industries including steel annealing, silicon manufacturing, hydrogenation of fats and oils, glass making, hydrocracking, methanol production, the production of oxo alcohols, and icomeriisation processes. There are a variety of known processes wherein hydrogen is produced, including steam reforming of natural gas or naptha. In this process a feedstock such as natural gas is compressed and fed to a purification unit to remove sulfur compounds. The desulfurized feed is then mixed with superheated steam and fed to a reformer to produce primarily H2 and CO. The effluent stream from the reformer is sent to a heat recovery unit, then to a shift converter to obtain additional H2. The effluent from the shift converter passes through a process cooling and recovery unit prior to sending the effluent
.to a PSA system wherein high purity (e.g. 99.9 mol.% or greater) hydrogen is produced.
 The H2 gas being fed to PSA systems can, however, contain several contaminants in widely varying concentrations, (e.g. the feed stream to the PSA from a steam methane reformer (SMR) may contain one or more of C02, CH4, CO and N2. This combination of adsorbates at such widely varying compositions presents a significant challenge to the design of a PSA system, particularly with respect to adsorbent selection and configuration of the adsorber/adsorbent bed.
 Representative prior art PSA processes include Sircar et al., U.S. Pat. No. 4,077,779; Fuderer et al., U.S. Pat., 4,553,981; Fong et al., U.S. Pat No. 5,152,975; Wagner, U.S. Pat No. 3,430,418 and Batta, U.S.. Pat #3,564,816.
 More specifically, Bernard et al.in U.S. Pat. •# 5,912,422 discloses a PSA process for the separation ..of hydrogen from a feed gas mixture'that contains CO and other impurities such as CO2 and hydrocarbons. The feed mixture is passed into a first adsorbent to remove • CO2 and/or hydrocarbons, and then into a second adsorbent that is a faujasite type zeolite with at least 80 % lithium exchange to remove primarily CO impurity to produce hydrogen. If N2 is present in the hydrogen-containing feed mixture then Bernard et al. , introduces a third adsorbent between the first and second adsorbent to remove nitrogen.  Golden et al., U.S. Pat .# 4,957,514 disclosed the purification of hydrogen using barium exchanged Type X zeolite.
 Golden at•al., US Pat. # 6,027,549, disclose a PSA process to remove C02 and CH4 using activated carbons having bulk densities in the range of approximately 35-38 lb/ft3.
 Johnson et al., in US Patent 6,302,943 and in EP 1097746A2, disclose adsorbents for H2 recovery by pressure and vacuum swing adsorption, wherein the adsorbents at the product end of the bed have Henry's Law constants between 0.8 and 2.2 mmol/g/atm for CO and between 0.55 to 1.40 mmol/g/atm N2.
 There remains a need for improved PSA system and process having lower adsorbent requirements and higher product recovery as compared to existing PSA systems and processes for hydrogen production.  The present invention addresses this need through the use of a novel selection and arrangement of adsorbents within the adsorbent bed.
Summary of the Invention
 In accordance with this invention, each adsorber (bed) of the H2-PSA system is divided into four regions. In a preferred embodiment the first region comprises an adsorbent for the removal of water from the feed stream. The second region functions to reduce high (>10% by vol.) level contaminants (e.g., C02) in the hydrogen containing feed to less than 10%. The third region comprises an adsorbent capable of reducing the concentrations of all impurities entering this layer to less than 1%. The fourth region consist of adsorbents having high Henry's Law constants for N2 (e.g. greater than 1.5mmol/gm bar and preferably
greater than 2.3 mmol/gm bar) and GO (e.g. greater than 2.94 mmol/gm bar) to remove the remaining impurities to achieve the desired product (H2) purity. In one embodiment the second region may be omitted and/or combined with the third region. Other embodiments are also disclosed.
Brief Description of the Invention
 the objects, features and advantages will
occur to those skilled in the art from the following
description of (a) preferred embodiment (s) and the
accompanying drawing(s), in which:
 Fig. 1,illustrates a schematic of a four
layered PSA adsorption column in accordance with a
preferred embodiment of the invention.
 Figs. 2a and 2b illustrates delta nitrogen
loading and Henry's Law constants, respectively for various adsorbents in Region 4 of an adsorbent bed.
 Fig. 3 shows a correlation between Henry's Law constants and Working Capacity.
 Fig. 4 shows process flow diagram for a four bed PSA system in accordance with the invention.
 Fig. 5 shows comparisons between hydrogen recovery and bed size factor for various processes examples.
 Fig. 6 shows comparisons of processes disclosed in the Examples in terms of bed size factor.
Detailed Description of the Invention
 In accordance with the invention, an improve-PSA system and process is provided for purifying a gas stream containing more than 50 mol.% hydrogen*
 Typically H2 feed gas to a PSA contains several contaminants, such as H20, C02, CH4, CO, and N2. As used herein, all gas component percentages are mol.% unless otherwise indicated. Such a combination of adsorbates at such widely varying compositions presents significant challenge to efficient adsorbent selection. ••  A preferred embodiment of the invention is illustrated with reference to Figure 1. In this •embodiment, the PSA process uses an adsorbent bed comprising four regions of adsorbents. For the purposes of this disclosure, the first region is that ; which is closest to the feed end of the bed as indicated by the arrows indicating the direction of gas ' flow.
 The first region of the bed comprises adsorbents to remove contaminants like water. The adsorbent for the first layer (first region) may be selected,from the group consisting of alumina, silica gel, silicalite or zeolites.
 The adsorbent for the second layer/region is utilized for the removal of C02 and some CH4. In a preferred embodiment, this layer comprises activated carbon having a bulk density of 38-46 lb/ft3 (measured by ASTM Standard D-2854), which may be mixed with a weaker adsorbent (for C02 and CH4) such as alumina. The purpose of the mixture is to minimize the temperature gradient of the layer as well as the thermal swing associated with the heat of adsorption. The most preferred activcited carbon is G2X activated carbon available from Takeda Chemical Industries, Japan.
 With respect to the mixture, different fractions of alumina and activated carbon may be used. The optimum quantity of alumina and carbon for the mixture is dictated by the PSA process operating conditions, feed composition and the local gas phase concentration in the bed. Mixtures of other strong and weak adsorbents may also be used to achieve the desired reduction of thermal gradients in the bed. One such mixture could be activated carbon and ZnX zeolite or alumina and ZnX. Additional details on using mixtures of strong and weak adsorbents in PSA processes are disclosed by Ackley et al., US Patent # 6,027,548.  The adsorbent for the third layer is utilized for the removal of residual CH4 and the bulk of the N2 and CO in the feed stream. A preferred adsorbent for this region is activated carbon having a bulk density greater than or equal to 38 lb/ft3' As with layer 2, G2X activated carbon is the most preferred material. Cation exchanged forms of zeolites A, X, Y (e.g. ZnX and ZnY), chabazites and ^ mordenite, and more particularly, X zeolite exchanged with Zn2+ and Cu2"1" ions at different percentages of exchange may be used. The synthesis of Zn2+ and Cu2+ exchanged X zeolite is given by Khelifa et al., Microporous and Mesoporous Materials, Vol. 32, pg 199, 1999 and references therein. In addition, alternative materials for region 3 of the bed may include impregnated activated carbons having bulk densities in the range of 32-45 lb/ft3. An example of one such impregnated activated carbon is Sn-activated carbon (Sn-AC). More specifically, the activated carbon is impregnated with about 35% SnCl2.2H2O salt and then dried at 180 °C to produce AC-
SnO2. Additional information on the synthesis of Sn-activated carbons (Sn-AC) is given by lyuke et al., Chemical Engineering Science, Vol. 55, pg 4745, 2000. Relatively less preferred materials are activated carbons for region 3 of the bed.
 As indicated above, preferred adsorbents to be used in the second and third regions of the bed preferably have a high bulk density, in the range of 38-46 lb./ft3 . The use of such materials results in higher H2 recovery (about a 10% improvement) over conventional processes and lower adsorbent inventory for the PSA process. Among the adsorbents having bulk density in the preferred range, adsorbents having the highest dynamic capacity for the contaminant should be chosen. For the purposes of this invention, the dynamic loading capacity is defined as is the difference between the loading under adsorption conditions and loading under desorption conditions.
 Since regions 2 and 3 remove the majority of C02, CO, CH4 and N2 present in the H2 containing feed mixture, the largest thermal gradients and thermal swings are present in those two regions of the bed, with region 2 having greater thermal gradients and thermal swings in the bed than region 3. Two mixture combinations of adsorbents were compared for region 2 of the bed. A lower density activated carbon (BPL, available from Calgon Carbon Corp. USA) having a density of less than 38 lb/ft3 was also analyzed for comparison to G2X performance. The results are shown Table 1 below.
Table 1: Regions 2 and 3 (see Fig. 3) Temperature Swing and Dynamic Loadings of CO2 and CH4 on activated carbons (G2X & BPL) , alumina, and mixtures of A201 alumina and G2X activated carbon.
(Table Remove) A = delta
 Table 1 clearly illustrates, that the adverse thermal gradient in region 2 of the bed is reduced significantly by mixing G2X carbon with a weaker adsorbent (e.g., alumina). As shown in Table 1, mixtures of G2X carbon and 25% or 50% A201 activated alumina (available from UOP, Des Plaines, IL, USA) were evaluated to reduce thermal swings in the bed. The thermal swings were reduced from 25K for the G2X carbon alone to 20K and 16K for the respective mixtures. The delta COa and delta CH4 (loadings decreased 14% and 18%, respectively for the 75% carbon mixture. The dynamic loadings of the mixtures are* higher than the simple weighted average of the adsorbent loadings due to the reduction in the adverse thermal swing, i.e. due to the lower heats of adsorption and the increased heat capacity provided by the higher density, weaker adsorbent. A secondary advantage of the use of a mixture in region 2 is the impact upon the base
temperature in region 3. The delta N2 and delta CH4 loadings (not shown in Table 1) are about 10% higher due to the lower temperature in region 2 resulting from the mixture. Thus, in the most preferred practice of this invention, the second region consists of a mixture of a stronger and weaker adsorbents (e.g. a mixture of alumina and G2X activated carbon) to reduce the concentration of high level contaminants that are present in the H2 containing feed mixture. By using a mixture of adsorbent in region 2, the reduced thermal swing-actually increases the.local dynamic capacity of the bed and reduces the adsorbent inventory required.  The final cleanup for N2 and residual impurities (e.g., CO, CH4 , 02, Ar) is done in region 4 of the bed. In accordance with the invention, the most preferred adsorbents for region four have a N2 Henry's Law Constant between 2.58 mmol/g.bar and 10 mmol/g.bar, preferably between 2.58 and 4.3 mmol/g.bar. Adsorbents having a CO Henry's Law Constant of greater than 2.94 mmol/g.bar is also preferred. In the practice of the invention, adsorbents with high Henry's law constant achieve increased dynamic capacity, as well as lower bed pressure during equalization and purge steps in the PSA cycle. Consequently, higher H2 recovery and lower bed size factor are achieved due to lower bed pressure prior to counter-current (with respect to feed direction) blowdown in the PSA cycle. By using adsorbents with high Henry's constants in the purification zone of the bed, the spreading of the mass transfer zone is suppressed during the co-current pressure changing steps (e.g., bed-to-bed equalization) in the PSA cycle. The sharpness of the impurity
concentration fronts lead to increase in recovery and lower adsorbent inventory. Grand Canonical Monte Carlo simulations indicate that adsorbents having the above Henry's Constant (>2.3 mmol/g.bar) include CaEMT, CaMOR and LiMOR and absorbents with Henry's constant ^1.5 rnmol/g.bar such as VSA-6, Baylith KEH 650, KEJ407, CaX(2.0), LiX(2.0) (>86% Li), LiCaX (2.0) and binderless LiX(2.0) (>86% Li), where (2.0) refers to the SiO2/Al2O3 ratio could be used, however absorbents with Henry's Law constant >10 mmol/g.bar are generally not suitable in the practice of the invention. Note that the Henry's Law constant is based upon isotherm model and a specific temperature. The .specific pressure only relates to the determination of the delta N2 loading.
 Alternative materials for region 4 include naturally occurring crystalline zeolite molecular sieves such as chabazite, erionite, clinoptilolite, arid faujasite, and suitable synthetic zeolite molecular sieves such as ZSM-2, ZSM-3, EMC-2 (containing hexagonal faujasite possessing structure code EMT), beta, mordenite, heulandite,A, D, R, T, X, Y, and L. Also, other metal exchanged zeolites containing cations selected from group I ( e.g., Li, Na, K, Rb, Cs) and group II (e.g., Mg, Ca, Sr, and Ba) of the periodic table may also be used. In addition, zeolites A and X having at least 50% of its AlO2 elements associated with cations chosen from the group formed by calcium, lithium, zinc, copper, manganese, magnesium, nickel, strontium and barium could be used in region 4 of the bed. Furthermore, mordenites exchanged with Li or Ca cations, EMT, FAU, MOR, and CaX could also be used
in the purification zone (region 4) of the bed to remove impurities such as N2 and traces of CH4, and CO to produce high purity H2 . The three letter codes identifying the tetrahedral frameworks are structure type codes assigned by the international Zeolite Association in accordance with rules set up by the IUPAC Commission on Zeolite Structure' Types, W.M. Meier et al., 4th Revised Edition, 1996. The most desired Si/Al ratios for the adsorbents selected for region 4 of the bed are as follows: CaA (Si/Al = 1.0), LiX (Si/Al = 1.25), LiX (Si/Al = 1.0), CaX (Si/Al = 1.25), CaX (Si/Al = 1.0), Li-Mordenite (Si/Al = 5.0), Ca-Mordenite (Si/Al = 5.0) and CaEMT (Si/Al = 1.0). In addition, zeolite containing lithium/alkaline earth metal A and X zeolites (Chao et al . , U.S. Pat Nos . 5,413,625; 5,174,979; 5, (598, 013; 5,454,857 and 4,859,217) may also be used in region 4 of this invention.
 For 'the purpose of this application, the Henry' s Law Constant is defined from the following-equation representing a linear form of the isotherm in the low partial pressure region:
 In evaluating the N2 Henry's Law Constant (X0KH) , the pure component loading ratio correlation (LRC) (Yang, "Gas Separation by Adsorption Processes, 1987) was used. The LRC isotherm equation yields an expression for KH:
where, KI and HI are determined from the LRC constants:
 The LRC constants are determined from pure component isotherm data. For N2 adsorption on CaX(2.0), the LRC constants have the following values: X0 = 3.77, Al =23.56, A2 = - 3151, A3 = 1.0 and A4 = 320. In selecting adsorbents for N2 cleanup (region 4) in H2 purification, it is only necessary to define a limiting value for X0KH and an upper limit N2 partial pressure defining the maximum amount of N2 that is likely to be found in the H2 stream.
 PSA process simulations for H2 production using adsorbents with the highest Henry's law constant provided the highest M2 working capacity (i.e., required the smallest N2 cleanup layer) in region 4 as shown in Figure 2. When N2 working capacity was correlated with the Henry's Law Constant of the N2 isotherm, the linear correlation illustrated in Figure 3 for conditions of 310K and PN2 = 93.6 mbar was produced. The data points in Figure 3 are from the adsorbents in Figure 2. The largest Henry's Law Constant tested occurs for CaX (2.0) at 2.38 mmol/g bar. It is from this data that the inventive Henry's Law constant range was determined. Henry's Law constant
>10 holds the adsorbate so strongly that desorption would require lower desorption pressure and/or higher desorption temperature. The result is' that the purge gas and power requirement for the system would be increased to unacceptable levels.
 The increased H2 recovery and lower adsorbent inventory required by the PSA process of this invention is further illustrated in the examples given below. In order to compare the PSA process performance using the adsorbents of this invention with prior art, the four bed PSA system shown in Figure 4 will be used. The valve switching logic is shown in Table 2 and details of the PSA process given in Tables 3-5. However, it should be noted that the twelve step PSA cycle is used only to illustrate the enhanced PSA process performance achieved by replacing (prior art) adsorbents with the advanced adsorbents for regions 2-4 of the bed. In addition, other PSA cycles may also be used to show the enhanced PSA process performance without deviating from the scope of this invention.  Figure 4 shows four adsorbent beds (El, B2,B3 and B4) and associated valves and conduits that will be used to illustrate the enhanced PSA process performance of this invention. Referring to Figures 1 and 4, one embodiment of this invention is disclosed over one complete PSA cycle, and the PSA valve switching and steps are given in Tables 2 and 3, respectively. Also,, region 1 contains alumina, region 2 contains a mixture of 50 % each of A201 alumina and Takeda G2X activated carbon, region 3 contains G2X activated carbon, and region 4 contains CaX(2.0).
 Step 1 (ADI): Bed 1 (Bl) is in the first adsorption step (ADI) at: 232 psig, while Bed 2 (B2) is undergoing countercurrent blowdown (BD), Bed 3 (B3) is undergoing the first equalization falling step (EQ1DN), and bed 4 (B4) is undergoing the second pressure equalization rising step (EQ2UP).
 Step 2 (AD2) : Bed 1 -is in the second adsorption step (AD2) and is also supplying product gas to bed 4 that is undergoing the first product pressurization (PP1) step. During the same time, beds 2, 3 and 4 are undergoing purge, cocurrent depressurization and first product pressurization, respectively.
 Step 3 (AD3): Bed 1 is in the third adsorption step (AD3), and is also supplying product gas to Bed 4 that is undergoing the second product pressurization (PP2) step. During the same time period, beds 2, 3, and 4 are undergoing the first equalization rising step (EQ1UP), second equalization falling (EQ2DN), and second product pressurization step (PP2), respectively.
 Step 4 (EQ1DN): Bed 1 is undergoing the first equalization falling step (EQ1DN), while bed 2 receives the gas from bed 1 and is undergoing the second equalization rising step (EQ2UP). Beds 3 and 4 are now undergoing blowdown (BD) and the first adsorption step (PP1), respectively.
 Step 5 (PPG) : Bed 1 is undergoing cocurrent depressurization step to provide purge gas (PPG) to bed 3, while Beds 2 and 4 are undergoing first product pressurization (PP1) and the second adsorption step (AD2), respectively.
 Step 6 (EQ2DN): Bed 1 undergoes a second equalization falling step (EQ2DN) by sending low pressure equalization gas to bed 3 that is undergoing the first equalization rising (EQ1UP) step. Beds 2 and 4 are undergoing the second product pressurization (PP2) and third adsorption step, respectively.  Step 7 (BD): Beds 1 and 2 undergo the countercurrent blowdown (BD) and first adsorption (ADI) step, respectively. During this time Beds 3 and 4 are undergoing bed-to-bed equalization, i.e., Beds 3 and 4 are undergoing the second equalization rising (Eq2UP) and first equalization falling (EQ1DN) steps, respectively.
 Step 8 or PG (time units 340-425 sec): Bed 1 is now receiving purge gas (PG) from Bed 4, and Beds 2 and 3 are undergoing the second adsorption step and first product pressurization (PP1) step, respectively.  Step 9 (EQ1UP): Bed 1 is undergoing the first equalization rising step (EQ1UP) by receiving low pressure equalization gas from bed 4 that is undergoing the second equalization falling step (EQ2DN). During the same time, beds 2 and 3 is undergoing the third adsorption step (AD3) and the second product pressurization (PP2), respectively.
 Step 10 (EQ2UP): Bed 1 is undergoing the second equalization rising step (EQ2UP) by receiving high pressure equalization gas from bed 2 that is undergoing the first equalization- falling step (EQ1DN). During the same time, Beds 3 and 4 are undergoing the first adsorption (ADI) step and countercurrent blowdown step, respectively.
 Step 11 (PP1): Bed 1 is receiving first product pressurization (PP1) gas from bed 3 that is also in the second adsorption step (AD2), while Bed 2 is undergoing cocurrent depressurization step to provide purge gas (PPG) to bed 4.
 Step 12 (PP2 ) : Bed 1 is receiving second product pressurization (PP2) gas from bed 3 that is also in the third adsorption step (AD3). During the same time, Bed 2 undergoes a second equalization falling step (EQ2DN) by sending low pressure . equalization gas to bed 4 that is undergoing the first equalization rising (EQ1UP) step.
 A summary of the aforementioned twelve steps are given in Tables 2 and 3. In particular, Table 2 summarizes the valve sequence over one complete cycle for the four bed PSA process shown in Figure 4, and Table 5 gives the respective time intervals and the corresponding status of each bed during one complete PSA cycle. Note from Tables 2 and 3 that the four beds operate in parallel, and during Vj of the total cycle time one of the beds is in the adsorption step, while the other beds are either undergoing pressure equalization, purge, blowdown, or product pressuri zation.
Table 2: Four Bed H2 PSA Valve Switching (O = OPENED, C = CLOSED)
(Table Remove)Table 3: Time Interval and Step Sequence of the PSA Cycle
(Table Remove) ADI = First Adsorption Step
AD2/PP1 = Second Adsorption Step/First product
AD3/PP2 = Third Adsorption Step/Second product
EQ1DN = First Equalization Down
PPG = Provide Purge Gas
EQ2DN = Second Equalization Down
BD = Slowdown
First Equalization Up Second Equalization Up First Product Pressurization Second Product Pressurization
 Table 4 gives an example of the operating conditions and the PSA process performance using alumina in region 1, a mixture of 50% each of A201 alumina and G2X activated carbon in region 2, G2X in region 3, and CaX(2.0) in the region 4 in the bed. This example is hereafter referred to as IV2.
 Table 5 gives an example of the operating conditions and the PSA process performance using alumina in region I, high bulk density ( >38 lb/ft3) G2X activated carbon in regions 2&3, and VSA6 in the fourth region in the bed. This example is hereafter referred to as IV!.
 Table 6 (Prior Art) gives an example of the operating conditions and the PSA process performance using alumina in region 1, low bulk density (  In the tables, the symbols have the following meaning: TPD = ton (2000 Ib) per day of hydrogen, kPa = 1000 Pa = S.I. unit for pressure (1.0 atm. = 14.696 psi = 0.0 psig = 1.01325 bars =101.325 kPa), s = time unit in seconds.
 Table 4 (IV2): Four Bed PSA process performance (SMR feed) using alumina in the first region in the bed, a mixture of 50% A201 alumina and G2X activated carbon.in the second region, G2X activated carbon in the third region, and CaX(2.0) in the fourth region (top). The results shown below correspond to PSA process modeling using a feed mixture of 75.83% H2 , 0.72% N2, 3.35 % CH4, 2.96% CO, and 17.14% CO2- The adsorption pressure is 232 psig, the desorption pressure is 4.4 psig, and twelve steps ( see Tables 2 and 3) are used in the four bed PSA cycle. Further details of the four bed PSA process are given below.
Cycle Time(s) : -48 sec.
Adsorbent (region 1): Alumina Bulk Density (Alumina): 49.0 lb/ft3 Amount of Alumina: 74.65 lbm/TPD H2
Adsorbent (region 2): Mixture ( 50% each of A201
alumina and G2X)
Bulk Density: 43 lb/ft3
Amount of Mixture: 110 lbm/TPD H2
Adsorbent (region 3): Takeda G2X activated carbon
Bulk Density: 39.0 lb/ft3 '
Amount of G2X: 112 lbra/TPD H2
Adsorbent (region 4): CaX(2.0) Bulk Density (CaX(2.0): 41.33 lb/ft3 Amount of CaX(2.0): 137.38 lbm/TPD H2
High Pressure: 232 psig Low Pressure: 4.4 psig Temperature: 311 K
Feed Rate: 65,778 SCFH Product Rate: 42,000 SCFH
Total BSF 434.05 lbm/TPD H2 (SMR/IV2)
IV2 VS PA 100*(850.85 - 434.05)/850.85 = 49% BSF
H2 Purity: 99.99%
H2 Rec. 84% ( 10.53 % Higher H2 recovery versus PA)
 Table 5 (IV!) : Four Bed PSA process
performance (SMR feed) using alumina in the first region in the bed, high bulk density (> 38 lbm/ft3) G2X activated carbon in the regions 2 &3, and VSA6 zeolite in the fourth region (top). The results shown below correspond to PSA process modeling using a feed mixture of 75.83% H2, 0.72% N2 , 3.35 % CH4, 2.96% CO, and 17.14% CO2. The adsorption pressure is 232 psig, the desorption pressure is 4.4 psig, and twelve steps ( see Table 2 and 3) are used in the four bed PSA cycle. Further details of the six bed PSA process are given below.
Cycle Time(s) : 48 sec. (4.0 sec for each step)
Adsorbent (region 1): Alumina Bulk Density (Alumina): 49.0 lb/ft3 Amount of Alumina: 78.26 lbm/TPD H
Adsorbent (regions 2&3): Takeda G2X activated carbon
Bulk Density: 39 lb/ft3
Amount of G2X: 278.02 lbm/TPD H2
Adsorbent (region 4): VSA6
Bulk Density (VSA6): 41.33 lb/ft3
Amount of VSA6: 188.06 lbm/TPD H2
High Pressure: 232 psig Low Pressure: 4.4 psig Temperature: 311 K
Feed Rate: 69,234 SCFH
Product Rate: 42,000 SCFH)
Total BSF 544.34 lbra/TPD H2 (SMR feed case/IVl)
IV! VS PA 100*(850.85 - 544.34)7850.85 = 36.02% BSF
H2 Purity: 99.98%
H2. Rec. 80% ( 5.3 % Higher H2 recovery versus PA)
 Table 6 (Prior Art, i.e. PA): An example of the operating conditions and the PSA process performance using alumina, activated carbon and 5A zeolite in the three layer bed and the four bed PSA process of Figure 4. The results shown below were obtained from PSA simulation results using a feed mixture on a dry basis: 75.83% H2, 17.14% C02, 2.96% CO, 3.35% CH4 and 0.72% N2. Also, in the table, total bed size factor is the total quantity of adsorbents per ton per day of H2 produced.
Cycle time (s) 60
Adsorbent (region 1) Alumina Amount of alumina (Ib/TPD H2):122.32 Adsorbent (regions 2 &3) : activated carbon
Amount of activated carbon
Ib/TPD H2) : 434.58
Adsorbent in (region 4): 5A zeolite
Amount of 5A zeolite
(Ib/TPD H2) : 293.93
High Pressure: 232-psig
Low Pressure: 4.4
Feed Rate: 72,025 SCFH
Product Rate: 42,000 SCFH
Hydrogen Purity: 99.9%
Hydrogen Recovery: 76.9 %
Total Bed Size Factor
(Ib/TPD H2) : .851
Temperature: 311 K
 It should be recognized that the aforementioned examples utilized similar operating PSA process conditions to illustrate the enhanced performance using CaX(2.0), VSA6 and high bulk density activated carbon relative to prior art PSA processes using 5A zeolite. Other embodiments which use more or less adsorbers in the PSA cycle could easily be designed by those skilled in the art without deviating
from the scope of this invention.  Figure 5 compares the PSA process performance, obtained via computer simulations, using the PSA processes of Tables 4-6. Note that in the upper drawing of Fig. 5, that for about the same H2
purity (99.99%), the H2 recovery using 5A zeolite (PA) is about 76% (Table 6). By using the adsorbents of this invention, the H2 recovery is about 80% (Table 5, i.e., IV!), and 84% (Table 4, i.e., IV2), respectively. The lower diagram of Figure 5 shows the total bed size factor (BSF, lb/TPDH2) obtained using each of the aforementioned adsorbents and the PSA processes of Tables 4-6.
 Figure 6 shows the total bed size factor (BSF, lb/TPDH2) obtained using each of the aforementioned adsorbents and the PSA processes of Tables 4-6. The lower diagram shows the percentage reduction in bed size factor of this invention (IV! & IV2) relative to the prior art (PA). Note that IV! gives about 35% reduction over the prior art (PA) and IV2 gives about 50% reduction in the bed size factor' relative to the prior art (PA). The 50 % reduction in bed size factor in IV2 implies that IV2 needs only half the adsorbent inventory relative to the prior art (PA) process.
 Variations of the invention are also contemplated. For example, the region/layer of each bed could be replaced with multiple layers of different adsorbents. For example, the adsorbent layer could be substituted by a composite adsorbent layer containing different adsorbent materials positioned in separate zones in which temperature conditions favor adsorption performance of the particular adsorbent material under applicable processing conditions in each zone. Further details on composite adsorbent layer design is given by Notaro et al., U.S. Pat. #5,674,311.
 Further, consideration of the dynamic or rate effects may achieve enhanced PSA process performance. In particular, the adsorbents selected for regions. 2-4 of the bed could be improved by using higher rate adsorbents in those regions. Also, higher surface area/higher porosity adsorbent and/or smaller particles would provide higher adsorption/desorption kinetics. In addition, in region 4 of the bed, a higher rate material such as binderless LiX(2.0) would be desirable. This material could be placed in the entire zone (region 4) or on top of region 4. The adsorbent used in region 4 of the bed (e.g., CaX) could be caustically digested (c.d.) to produce adsorbents with different adsorption/desorption rates. Also, smaller particles may also be employed here as well to improve rate. Adsorbents having diameters in-the range of 0.5-2.0 mm are preferred in regions 2-4 of the bed in the practice of this invention.
[00633 Although the above PSA processes are discussed in relation to H2 production, the recommended adsorbents may also be applicable to other separation processes. Examples include helium recovery from natural gas or cryogenic sources (e.g., NRU/HRU), CO2 production from synthesis gas, or in other PSA processes to produce H2 and CO, or. H2 and CO2 from various mixtures containing these components. In addition the PSA process of this invention could also be used with hydrogen containing feed gas that contains additional impurities such as oxygen and argon.  Specific features of the invention are shown in one or more of the drawings for convenience only, as each feature may be combined with other features in
accordance with the invention. Alternative embodiments will be recognized by those skilled in the art and are intended to be included within the scope of the claims.
1. An adsorbent bed for purification of a gas stream comprising:
a) a first layer of adsorbent adapted for the removal of water;
b) a second layer of adsorbent comprising a mixture of adsorbents, wherein at least one component of the said mixture has a bulk density of greater than or equal to 32 lb /ft3;
c) a third layer of adsorbent comprising an adsorbent having a bulk density of greater than or equal to 32 lb/ft3; and
d) a fourth layer of adsorbent having a N2 Henry's Law constant of greater than 1.5 mmol/g.bar.
2. The adsorbent bed as claimed in claim 1 wherein said first layer of adsorbent is selected from the groups consisting of alumina, silica gel, silicalite and zeolites; said second layer of adsorbents comprising a mixture of alumina with activated carbon or zeolite; said third layer of adsorbent comprising activated carbon.
3. The adsorbent bed as claimed in claim 1, wherein said fourth layer of adsorbent is selected from the group consisting of VSA-6, KE-H650, KE-J407, CaX (2.0), LiX (2.0) (>86% Li), LiCaX (2.0) and binderless LiX (2.0) (>86% Li), where (2.0) refers to the SiO2/Al2O3 ratio.
4. The adsorbent bed as claimed in claim 1, wherein said mixture of step b) contains activated carbon that has a bulk density of at least 38 lb/ft3 and wherein fourth layer of adsorbent has a N2 Henry's Law constant of at least 2.3 mmol/g.bar.
5. The adsorbent bed as claimed in claim 1 wherein the zeolite in the second layer is X zeolite, and wherein said adsorbent bed is used for hydrogen purification.
6. A process for the purification of a gas stream containing more than 50
mole % hydrogen and impurities including water, CO2, CH4, CO and N2, said process comprising passing said gas stream over the adsorbent bed as claimed in claim 1, wherein said adsorbent bed comprises at least 4 layers, the first layer selected from the group consisting of silica gel, silicalite, zeolite and alumina, the second layer of activated carbon or zeolite and alumina, the third layer of activated carbon and a fourth layer of adsorbent having a N2 Henry's Law constant of at least 1.5 mmol/g.bar.
7. The process as claimed in claim 6, wherein the activated carbon in said second layer has a bulk density of greater than or equal to 38 lb/ft3.
8. The process as claimed in claim 6, wherein said N2 Henry's Law constant of at least 2.3 mmol/g.bar.
9. The process as claimed in claim 6 wherein said fourth layer of adsorbent is selected from the group consisting of VSA-6, KE-H650, KE-J407, CaX (2.0), LiX (2.0) (>86% Li), LiCaX (2.0) and binderless LiX (2.0) (>86% Li), where (2.0) refers to the SiO2/Al2O3 ration.
10. The process as claimed in claim 6 wherein the activated carbon in the second layer is an impregnated activated carbon having a bulk density of at least 32 lb/ft3.
|Indian Patent Application Number||2720/DELNP/2005|
|PG Journal Number||13/2009|
|Date of Filing||20-Jun-2005|
|Name of Patentee||PRAXAIR TECHNOLOGY, INC.,|
|Applicant Address||39 OLD RIDGEBURY ROAD, DANBURY, CONNECTICUT 06810, UNITED STATES OF AMERICA.|
|PCT International Classification Number||C01B|
|PCT International Application Number||PCT/US2003/040797|
|PCT International Filing date||2003-12-22|