"A CATALYST COMPOSITION"
BP CHEMICALS LIMITED, a British company of Britannic House, 1 Finsbury Circus, London EX2M 7BA, United Kingdom,
The following specification particularly describes the invention and the manner in which it is to be performed:
Case 9171(2)
OXIDATION CATALYST AND PROCESS UTILISING THE CATALYST
The present invention relates to a catalyst for the oxidation of ethane to ethylene and/or acetic acid and/or for the oxidation of ethylene to acetic acid, and to a process for the production of acetic acid and/or ethylene utilising the aforesaid catalyst. Catalysts comprising molybdenum, vanadium and niobium in combination with oxygen
5 for use in processes for the production of acetic acid by the oxidation of ethane and ethylene are known in the art from, for example, US-A-4,250,346.
US Patent No. 4,250,346 discloses the oxidative dehydrogenation of ethane to ethylene in a gas phase reaction at relatively high levels of conversion, selectivity and productivity at a temperature less than 500°C using as catalyst a composition
10 comprising the elements molybdenum, X and Y in the ratio MoaXbYc wherein X is Cr, Mn, Nb, Ta, Ti, V and/or W, and preferably Mn, Nb, V and/or W; Y is Bi, Ce, Co, Cu, Fe, K, Mg, Ni, P, Pb, Sb, Si,Sn, Tl and/or U, and preferably Sb, Ce and/or U, a is 1, b is 0.05 to 1.0 and c is 0 to 2, and preferably 0.05 to 1.0, with the proviso that the total value of c for Co, Ni and/or Fe is less than 0.5.
15 WO 99/20592 to Celanese relates to a method of selectively producing acetic acid from ethane, ethylene or mixtures thereof and oxygen at high temperature in the presence of a catalyst having the formula MoaPdbXcYd wherein X represents one or several of Cr, Mn, Nb, Ta, Ti, V, Te and W; Y represents one or several of B, Al, Ga, In, Pt, Zn, Cd, Bi, Ce, Co, Rh, Ir, Cu, Ag, Au, Fe, Ru, Os, K, Rb, Cs, Mg, Ca, Sr, Ba,
20 Nb, Zr, Hf, Ni, P, Pb, Sb, Si, Sn, Tl and U and a=l, b=0.0001 to 0.01,0.005 to 1.
1
German patent application DE 196 30 832 Al relates to a similar catalyst composition in which a =1, b > 0, c> 0 and d = 0 to 2. Preferably, a = 1, b = 0.0001 to 0.5, c = 0.1 to 1.0 and d = 0 to 1.0.
The catalysts of both WO 99/20592 and DE 19630832 require the presence of
5 palladium.
WO 98/47850 relates to a process for producing acetic acid from ethane, ethylene or mixtures thereof and a catalyst having the formula WaXbYcZd in which X represents one or several of Pd, Pt, Ag and Au, Y represents one or several of V, Nb, Cr, Mn, Fe, Sn, Sb, Cu, Zn, U, Ni, and Bi and Z represents one or several of Li, Na, K, Rb,
10 Cs, Be, Mg, Ca, Sr, Ba, Sc, Y, La, Ti, Zr, Hf, Ru, Os, Co, Rh, Ir, B, Al, Ga, In, Tl, Si, Ge,Pb, P, As andTe, a = 1,b >0, c>0 anddis0 to 2.
The catalyst of WO 98/47850 does not contain molybdenum.
WO 99/51339 relates to a catalyst composition for the selective oxidation of ethane and/or ethylene to acetic acid which composition comprises in combination with
15 oxygen the elements MoaWbAgcIrdXeYf wherein X is the elements Nb and V; Y is one or more elements selected from the group consisting of Cr, Mn, Ta, Ti, B, Al, Ga, In, Pt, Zn, Cd, Bi, Ce, Co, Rh, Cu, Au, Fe, Ru, Os, K, Rb, Cs, Mg, Ca, Sr, Ba, Zr, Hf, Ni, P, Pb, Sb, Si, Sn, Tl, U, Re and Pd; a, b, c, d, e and f represent the gram atom ratios of the elements such thatO
20
There remains a need for catalyst for the oxidation of ethane to ethylene and/or acetic acid and/or for the oxidation of ethylene to acetic acid and a process for the production of acetic acid and/or ethylene employing the catalyst.
We have found that oxidation catalysts comprising molybdenum, vanadium and
25 niobium in combination with oxygen which employ gold as an essential component
in the absence of palladium can fulfil the need for an oxidation catalyst and process employing same.
Accordingly, the present invention provides a catalyst composition for the oxidation of ethane to ethylene and/or acetic acid and/or for the oxidation of ethylene to
30 acetic acid which composition comprises in combination with oxygen the molybdenum, vanadium, niobium and gold in the absence of palladium
2
according to the empirical formula : MoaWbAucVdNbeYf (I)
wherein Y is one or more elements selected from the group consisting of: Cr, Mn, Ta,
Ti, B, Al, Ga, In, Pt, Zn, Cd, Bi, Ce, Co, Rh, Ir, Cu, Ag, Fe, Ru, Os, K, Rb, Cs, Mg, Ca,
Sr, Ba, Zr, Hf, Ni, P, Pb, Sb, Si, Sn, Tl, U, Re, Te, La and Pd;
5 a, b, c, d, e and f represent the gram atom ratios of the elements such that:
i. 0
10"5
0
0
10 0
Catalysts embraced within the formula (I) include:-
MoaWbAucVdNbeYf
Moa.AucVdNbeYf
MoaWb.AucVdNbe
15 Moa.AucVdNbe
Examples of suitable catalysts having the formula (I) include:-
M01.ooVo.25Nbo.12.Auo.01Oy ; Moi.ooVo.2i3Nbo.i38Au0.oo70y ; Moi.ooV0.232Nbo.i39Au0.oo70y;
and Moi.oooVo.426Nbo.ii5Auo.ooo80y wherein y is a number which satisfies the valencies
of the elements in the composition for oxygen.
20 Preferably a > 0.01. Preferably, d> 0.1. Preferably, e> 0.01. Preferably, e
0.5. Preferably, f> 0.01. Preferably, f
Preferably, Y is selected from the group consisting of Bi, Ca, Ce, Cu, K, P, Sb,
La and Te.
An advantage of catalyst compositions according to the present invention is that
25 they can be more active and selective in converting ethane and/or ethylene to acetic acid and/or ethylene.
The catalyst compositions may be prepared by any of the methods conventionally employed for the preparation of catalysts. Suitably the catalyst may be prepared from a solution of soluble compounds and/or complexes and/or compounds of
30 each of the metals. The solution is preferably an aqueous system having a pH in the range from 1 to 12, preferably from 2 to 8, at a temperature of from 20° to 100°C.
3
Generally, a mixture of compounds containing the elements is prepared by dissolving sufficient quantities of soluble compounds and dispersing any insoluble compounds so as to provide a desired gram-atom ratio of the elements in the catalyst composition. The catalyst composition may then be prepared by removing the solvent
5 from the mixture. The catalyst may be calcined by heating to a temperature of from 200 to 550°C, suitably in air or oxygen, for a period of from 1 minute to 24 hours. Preferably, the air or oxygen is slowly flowing.
The catalyst may be used unsupported or supported. Suitable supports include
silica, alumina, zirconia, titania, silicon carbide and mixtures of two or more thereof.
10 Further details of a suitable method for preparing a catalyst composition may be
found in, for example, EP-A-0166438.
The catalyst may be used in the form of a fixed or a fluidised bed.
In another embodiment the present invention provides a process for the production of ethylene and/or acetic acid from a gaseous mixture comprising ethane
15 and/or ethylene which process comprises contacting the gaseous mixture with a
molecular oxygen-containing gas at elevated temperature in the presence of a catalyst composition as hereinbefore described.
Ethane is oxidised to ethylene and/or acetic acid and/or ethylene is oxidised to acetic acid. Preferably, ethane and optional ethylene is oxidised to a mixture comprising
20 ethylene and acetic acid which may be used with or without the addition or removal of acetic
acid and/or ethylene for the production of vinyl acetate by reaction with a molecular oxygen-containing gas in an integrated process.
The feed gas comprises ethane and/or ethylene, preferably ethane.
Ethane and/or ethylene may be used in substantially pure form or admixed with
25 one or more of nitrogen, methane, carbon dioxide and water in the form of steam, which may
be present in major amounts, for example greater than 5 volume percent or one or more of hydrogen, carbon monoxide, C3/C4 alkenes and alkenes, which may be present in minor amounts, for example less than 5 volume percent.
The molecular oxygen-containing gas may be air or a gas richer or poorer in
30 molecular oxygen than air, for example oxygen. A suitable gas may be, for example, oxygen diluted with a suitable diluent, for example nitrogen.
4
It is preferred to feed, in addition to ethane and/or ethylene and the molecular oxygen-containing gas, water (steam) because this can improve the selectivity to acetic acid.
The elevated temperature may suitably be in the range from 200 to 500°C,
5 preferably from 200 to 400°C.
The pressure may suitably be atmospheric or superatmospheric, for example in the range from 1 to 50 bar, preferably from 1 to 30 bar.
The catalyst composition is preferably calcined before use in the process of the invention. Calcination may suitably be achieved by heating at a temperature suitably in
10 the range from 250 to 500°C in the presence of an oxygen-containing gas, for example air.
Operating conditions and other information applicable to the performance of the invention may be found in the aforesaid prior art, for example US Patent No. 4,250,346.
The process of the invention will now be further illustrated by reference to the 15 following Examples.
CATALYST PREPARATION
Examples according to the present invention
20 Example 1 (Moi.0oVo.2i3Nbo.i38Au0.oo70y)
A solution was prepared by dissolving 12.71 g ammonium molybdate, 2.11 g ammonium vanadate, 2.43 g niobium chloride, 0.36 g ammonium Au tetrachloride and 2.03 g oxalic acid in 200 ml water heated to 70°C for 15 minutes, followed by evaporation to dryness over 2 hours. The resulting catalyst cake was ground then
25 calcined in static air in an oven at 350°C for 5 hours. The composition of the catalyst as analysed by XRF and found also to contain traces of platinum, silver, iridium, rhodium and ruthenium, represented as an empirical formula :
MOi.ooVo.213Nbo.l38AUo.007Pto.000035Ago.000005'IrO.OOOOOlRho.000002Ruo.0000040y .
5
Example 2 (Moi.ooVo.232Nbo.i39Au0.oo70y)
A solution was prepared by dissolving 12.71 g ammonium molybdate, 2.11 g ammonium vanadate, 2.43 g niobium chloride, 0.36 g ammonium Au tetrachloride and 2.03 g oxalic acid in 200 ml water heated to 70°C for 15 minutes, followed by
5 evaporation to dryness over 2 hours. The resulting catalyst cake was ground then
calcined in static air in an oven at 350°C for 5 hours. The composition of the catalyst as analysed by XRF and found also to contain traces of platinum, silver, iridium, rhodium and ruthenium, represented as an empirical formula :
MOi.ooVo.232Nbo.l39AUo.007Pto.000005Ago.000007lT0.0000002Rho.0000003RUo.0000040y .
10
Example 3 (Moi.oooVo^Nbo.nsAuo.ooosOy)
A solution was prepared by dissolving 12.92 g ammonium molybdate, 3.65 g • ammonium vanadate, 2.27 g niobium chloride, 0.0214 g ammonium Au tetrachloride
and 2.43 g oxalic acid in 200 ml water heated to 70 C for 15 minutes, followed by 15 evaporation to dryness over 2 hours. The resulting catalyst cake was ground then
calcined in static air in an oven at 400° C for 5 hours. The nominal composition of the
catalyst was thus : Moi.oooVo^Nbo.nsAuo.ooosOy.
Examples not according to the invention
20 Comparative Example A. (Mo1.00V0.25Nb0.12Oy)
A solution A was prepared by dissolving 12.71 g ammonium molybdate in 50 ml water heated to 70°C. A second solution B was prepared by dissolving 2.11 g ammonium vanadate in 70 ml water heated to 70°C. Another solution C was prepared by dissolving 2.43 g niobium chloride and 2.02 g oxalic acid in 50 ml water heated to
25 70°C. Next, solution C was added to solution B and the resulting mixture heated at
70°C for 15 minutes. Solution A was then added and the final mixture heated at 70°C for 15 minutes, before evaporating the mixture to dryness over not more than 2 hours. The resulting catalyst cake was ground then calcined in static air in an oven at 350°C for 5 hours. The nominal composition of the catalyst was thus M01.ooV025Nbo.12Oy.
6
Comparative Example B (Mo1.00V0.25Oy)
As for comparative example A except that no solution C was prepared. The nominal composition of the catalyst was thus Mo1.00V0.25Oy.
5 Comparative Example C (M01.ooVo.25Nbo.12Pdo.01Oy)
As for comparative example A except that 0.23 g Pd acetate was added to solution A. The nominal composition of the catalyst was thus M01.ooV025Nbo.12 PdooiOy.
10 Comparative Example D (M01.ooVo.25Nbo.12Ruo.01Oy)
As for comparative example A except that 0.36 g of ammonium Ru hexachloride was added to solution A. The nominal composition of the catalyst was thus M01.ooVo.25Nbo.12Ruo.01Oy.
15 Comparative Example E (Mo1.00V0.25Nb0.12Rh0.01Oy)
As for comparative example A except that 0.15 g of Rh (III) hydroxide was added to solution A. The nominal composition of the catalyst was thus M01.ooVo.25Nbo.12Rho.01Oy.
20 CATALYST TEST PROCEDURE.
Typically, 5 mis of catalyst was loaded into a fixed bed reactor made of Hasetelloy grade C276 of dimensions 12 mm internal diameter and length 40 cm. Glass beads were used to maintain the catalyst in position in the centre of the reactor. Above the catalyst, the glass beads thus acted as a mixing and pre-heating zone for gaseous and
25 liquid reagents. The test apparatus was then pressure-tested at 21 bar with helium to check for leaks. Catalysts were then activated by heating to reaction pressure at 5° C/min in helium for 16 hours, to ensure full decomposition of catalyst precursors.
For Examples 1 and 2 and the Comparative Experiments, the required flows of ethane, 20 % oxygen in helium and water were then introduced to the reactor, to ensure
30 an inlet composition of 42 % v/v ethane, 6.6 % oxygen, 25 % v/v helium and 26.4 % v/v water (as steam). The total feed flow rate was maintained at a level to ensure a feed
7
GHSV of about 3000/h. In the case of Example 3, performance was measured with less
water in the feed than Examples 1 and 2, and ethylene was added to the feed mixture,
such that an inlet feed composition of 52 % v/v ethane, 5 % v/v ethylene, 6.6 % oxygen,
10 % v/v water and balance helium was used.
5 After equilibrating for 30 minutes, gas samples were taken from the outlet
stream to calibrate a GC (model Unicam 4400) for ethane, oxygen and helium. Next, the setpoint temperature of the reactor was increased until 75 % -100 % oxygen conversion was achieved, as indicated by the presence in the outlet stream of less than 2.2 % v/v oxygen.
10 Following an equilibration period of 30 minutes, catalysts were then evaluated
under steady state conditions for a period of typically 4-5 hours. Exit gas volume was measured over the run period by a water-gas meter. Liquid products were collected and weighed after the run period. Composition of gas and liquid products was measured using GC analysis (Unicam 4400 and 4200 fitted with TCD and FID detectors
15 respectively).
All feed and product flow rates and compositions were entered into a spreadsheet, and the following parameters calculated according to the formulae in which AcOH represents acetic acid :
STY (space time yield) % = (g AcOH) / litre catalyst bed / hour
20
conversions :
of ethane = (inlet mol ethane - outlet mol ethane) / inlet mol ethane * 100
of oxygen = (inlet mol oxygen - outlet mol oxygen )/inlet mol oxygen * 100
25 selectivities:
to AcOH (C-mol %) = (outlet mol AcOH * 2) / (mol ethane converted * 2) * 100 to ethylene(C-mol %) = (outlet mol ethylene * 2)/(mol ethane converted * 2) * 100 to CO (C-mol %) = (outlet mol CO) / (mol ethane converted * 2) * 100 to C02 (C-mol %) = (outlet mol C02) / (mol ethane converted * 2) * 100
30 to COx = selectivity to CO (C-mol %) + selectivity to C02 (C-mol %)
8
Typically, mass balance and carbon balance for a reaction was found to be 100 +/- 5 %. RESULTS
The following tables 1 and 2 compare the catalyst performance of the above. Each catalyst was evaluated under standard conditions indicated in the tables, except for
5 the temperature, which was varied so as to achieve 70-90 % oxygen conversion, in order to facilitate comparison.
Table 1
Experiment Temp, of bed°C Ethane convn % Oxygen convn % Sel. C2H4 % C-mol Sel COx % C-mol Sel. AcOH % C-mol STY AcOHg/1-cat/h
A 326 3.2 82.4 41.9 16.2 41.3 82
B 314 4.8 79.4 15.1 67.0 17.8 20
C 253 3.9 76.8 0.0 36.9 62.9 82
D 293 5.0 71.8 43.7 16.5 39.8 70
E 304 5.7 87.5 43.1 15.5 40.3 89
Example 1 275 7.4 88.7 38.1 9.1 48.6 136
Example 1 285 9.2 100.0 37.8 8.5 51.5 177
Example 1 295 10.0 100.0 34.6 8.8 54.9 203
Example 2 303 7.1 73.3 38.1 6.3 54.6 142
Example 2 313 7.8 80.0 38.4 6.1 54.8 158
Example 2 323 8.8 ., 92.7 40.8 7.2 51.1 165
Conditions : 42 % v/v ethane, 6.6% v/v oxygen, 25% v/v wateer, Balance He, GHSV=2970; 21 bar.•
Table 2
Experiment Temp.of bed°C Ethaneconvn % Oxygen convn % Sel. C2H4 % C-mol Sel COx% C-mol Sel. AcOH % C-mol STY AcOHg/1-cat/h
Example 3 300 11.3 71.7 55.8 4.8 39.3 198
Feed : 52 % v/v ethane, 5 % v/v ethylene, 6.6 % v/v oxygen, 10 % v/v water, Balance He. Conditions: 9 bar,GHSV = 3200/h
The results in the Tables illustrate clearly the promotional effect of gold on Mo-V-Nb based oxide catalysts. The results in the Tables also show that the performance of gold promoted catalysts according to the present invention is affected by the molar
9
ratios of molybdenum, vanadium and niobium and by the gold content as well as being influenced by the reaction conditions.
10
WE CLAIM:-
1. A catalyst composition comprises in combination with oxygen the
elements molybdenum, vanadium, niobium and gold in the absence of
palladium according to the empirical formula: MoaWbAucVdNbcYf (I) wherein Y
is one or more elements selected from the group consisting of : Cr, Mn, Ta, Ti,
B, Al, Ga, In, Pt, Zn, Cd, Bi, Ce, Co, Rh, Ir, Cu, Ag, Fe, Ru, Os, K, Rb, Cs, Mg,
Ca, Sr, Ba, Zr, Hf, Ni, P, Pb, Sb, Si, Sn, Tl, U, Re, Te and La;
H, b, c, d, e and f represent the gram atom ratios of the elements such that:
0
2. A catalyst composition as claimed in claim 1, wherein formula I is selected from the group consisting of MoaWbAucVdNbeYf; MoaAucVdNbeYf; MoaWbAucVdNbe and MoaAucVdNbe.
3. A catalyst composition as claimed in claim 1 or claim 2, wherein a>0.01, and/or d>0.01 and/or e>0.5 and/or f>0.01 and/or f
11
4. A catalyst composition as claimed in any one of the preceding claims wherein Y is selected from the group consisting of Bi, Ca, Ce, Cu, K, P, Sb, La and Te.
5. A catalyst composition as claimed in claim 1 having the formula selected from the group consisting of M01.ooVo.25Nbo.12.Auo.01Oy; Moi.0oV0.2i3Nbpi'38Auo.oo70y ; Moi.ooVo.232Nbo.i39Au0.oo70y ; and Moi.oooVo.^Nbo.nsAuo.ooosOy wherein y is a number which satisfies the valencies of the elements in the composition for oxygen.
6. A catalyst composition substantially as hereinbefore described with reference to the foregoing examples.
Dated this 5th day of July, 2005.
-12-
ABSTRACT
A CATALYST COMPOSITION
A catalyst composition comprises in combination with oxygen the elements molybdenum, vanadium, niobium and gold in the absence of palladium according to the empirical formula: MoaWbAucVdNbcYf (I) wherein Y is one or more elements selected from the group consisting of : Cr, Mn, Ta, Ti, B, Al, Ga, In, Pt, Zrt, Cd, Bi, Ce, Co, Rh, Ir, Cu, Ag, Fe, Ru, Os, K, Rb, Cs, Mg, Ca, Sr, Ba, Zr, Hf, Ni, P, Pb, Sb, Si, Sn, Tl, U, Re, Te and La; &, b, c, d, e and f represent the gram atom ratios of the elements such that:
0
10-5
0
0
0 |