Abstract A coating composition containing about 40-90% by weight of film forming binder and 10-60% by weight of an organic liquid carrier;" wherein the binder contains about (a) about 50-90% by weight of an acrylosilane polymer c ontaining about 30-95% by weight based, based on the weight of the acrylosilane polymer, of    polymerized monomers of myrene, alkyl (meth)acrylates having 1-12 carbon atoms in the alkyl group and hydroxy alkyl (meth)acrylates having 1-4 carbon atoms in the alkyl group and any mixtures thereof and 5-70% by weight, based on the weight of the polymer, of polymerized ethylenically unsaturated monomers containing reactive silane groups and the polymer has a weight average molecular weight of about 1,000 -    30,000; (b) about 5-25% by weight of a non-aqueous dispersed polymer of (i) a macromolecular core having a weight average molecular weight of about 50,000-500,000, and (ii) attached to the macromolecular core, a plurality of    macromonomer chains having a weight average molecular weight of abcut 1,000-30,000 of 5-30% by weight based on the weight of the macromonomer, of polymerized ethylenically unsaturated monomers which having functional groups selected from the following epoxide, anhydride, isocyanate, silane, acid hydroxy, amide or any combination cf these groups; and about 70-95% by weight, based on the    weight of the macrornonomsr. of at least one other polymerized ethylenically unsaturated monomer without a crosslinking functionality; and (c) about 5-25% by weight, of a crosslinking agent of tris(alkoxy carbonyl amino) triazine.
Full Text The present invention relates to a coating composition and a process for coating a substrate.
This invention relates to high solids solvent based coating
compositions and in particular to a clear coating composition for clear coat/color coat finishes for automobiles and trucks having improved resistance to etching from acid rain and other environmental pollutants.
BACKGROUND OF THE INVENTION
WO 96/34904 published November 7, 1996 shows a curable coating. composition having improved mar and abrasion resistance of polyepoxide and polyacid crosslinking agent, an acrylosilane polymer and an acrylic polyol polymer and a tricarbamoyl triazine compound as a crosslinking agent. The composition can be used as a monocoat over a primer or as a clear coat over a conventional base coat in a base coat clear coat finish. Mauer et al US 5,565,243 issued Oct. 15, 1996 shows a process for applying a base coat plus clear coat finish to substrates such as conventionally used for automobiles and trucks in which the base coat which is pigmented and contains a tricarbamoyl triazine as a crosslinking agent.
There is a need for a coating composition that has improved acid etch resistance and mar and abrasion resistance.
SUMMARY OF THE INVENTION
A coating composition containing about 40-90% by weight of film forming binder and 10-60% by weight of an organic liquid carrier;
wherein the binder contains about
(a) about 50-90% by weight of an acrylosilane polymer containing about 30-95% by weight, based on the weight of the acrylosilane polymer, of " polymerized monomers of the group of styrene, alkyl (meth)acrylates having 1-12 carbon atoms in the alkyl group, hydroxy alkyl (meth)acrylates having 1-4 carbon atoms in the alkyl group and any mixtures thereof, and 5-70% by weight, based on the weight of the polymer, of polymerized ethylenically unsaturated monomers containing reactive silane groups and the polymer has a weight average molecular weight of about 1,000-30,000;
(b) about 5-25% by weight of a non-aqueous dispersed polymer
having
(i) a macromolecular core having a weight average molecular weight of about 50,000-500,000, and
(ii) attached to the macromolecular core, a plurality of
macromonomer chains having a weight average molecular weight of about 1,000-30,000 of 5-30% by weight, based on the weight of the macromonomer, of polymerized ethylenically unsaturated monomers which having functional groups selected from the following epoxide, anhydride, isocyanate, silane, acid hydroxy, amide or any combination of these groups; and about 70-95% by weight, based on the weight of the macromonomer, of at least one other polymerized ethylenically unsaturated monomer without a crosslinking functionality; and
(c) about 5-25% by weight, of a crosslinking agent of tris(alkoxy
carbonyl amino) triazine.
Therefore, the present invention relates to a coating composition comprising 4ft-90% v
by weight of film forming binder and 10-60% by weight of an organic liquid carrier;,-wherein the binder comprises
(a) 50-90% by weight of an acrylosilane polymer consisting essentially of 30-95% by
weight, based on the weight of the acrylosilane polymer, of polymerized monomers
selected from the group consisting of styrene, alkyl (meth)acrylates having 1-12
carbon atoms in the alkyl group, hydroxy alkyl (meth)acrylates having 1-4 carbon
atoms in the alkyl group and any mixtures thereof and 5-70% by weight, based on the
yaUck weight of thetoolymer, of polymerized ethylenically unsaturated monomers containing
reactive silane groups and the polymer having a weight average molecular weight of 1,000-30,000;optionally acrylic polymer may be used
(b) 5-25% by weight of a non-aqueous dispersed polymer of
(i) a macromolecular core having a weight average molecular weight of 50,000-500,000, and
(ii) attached to the macromolecular core, a plurality of macromonomer chains having a weight average molecular weight of 1,000-30,000 of 5-30% by weight, based on the weight of the macromonomer, of polymerized ethylenically unsaturated monomers which having functional groups selected from the group consisting of epoxide, anhydride, isocyanate, silane, acid hydroxy, amide or any combination of these groups; and 70-95% by weight, based on the weight of the macromonomer, of at least one other polymerized ethylenically unsaturated monomer without a crosslinking functionality; and
(c) 5-25% by weight, of a crosslinking agent consisting of tris(alkoxy carbonyl amino)
triazine.

the present invention also relates to a process for coating a substrate as described hereinabove, comprising the steps of:
(a) applying a layer of a pigmented basecoating to the substrate to form a basecoat
thereon;
(b) applying to the basecoat a layer of the composition as claimed in claim 1 to form a
top coat over said basecoat;
(c) curing the basecoat and topcoat to form a basecoat and topcoat on the substrate.
DETAILED DESCRIPTION OF THE INVENTION
The novel coating composition of this invention contains a
combination of film forming components of an acrylosilane polymer, a non-aqueous dispersed polymer, referred to as a (NAD) polymer, and the crosslinking agent of tris(alkoxy carbonyl amino) triazine that provides improved resistance to acid etching from environmental air pollution and improved mar and abrasion resistance in comparison to conventional coating compositions containing acrylic polymers and melamine crosslinking agents.
Molecular weights are determined by GPC (gel permeation chromatography) using polystyrene as a standard.
The term (meth)acrylate refers to esters of both acrylic and methacrylic acids.
The coating composition of this invention is useful for finishing the exterior of automobile and truck bodies. Depending on its use, the present composition is capable of providing a coating which is durable, has excellent adhesion to basecoats, does not crack, does not deteriorate in terms of transparency under prolonged exposure to weather conditions, and imparts a superior glossy appearance for an extended period. Also, the coating composition offers a significant improvement over conventionally used coating compositions in terms of resistance to etching caused by environmental chemical attack.
A typical stsel auto or truck body has several layers of coatings. The steel is typically first coated with an inorganic rust-proofing zinc or iron phosphate layer over which a primer coating is applied which typically is an electr ocoated primer or can be a repair primer. A typical electrocoated primer comprises a cathodically deposited epoxy modified resin that is crosslinked with a polyisocyanate. A typical repair primer comprises an aJkyd resin. Optionally, a primer Mirfacer can be applied over the primer coating to provide for better appearance and/or improved adhesion of the basecoat to the primer coat. A pigmented basecoat or colorcoat is next applied over the primer surfacer. A typical basecoat comprises a pigment, which may include metallic flakes in the case of a metallic finish, and polyestsr or acrylourethane as a film-fcrming binder. A clear topcoat (clearcoat) is then applied to the pigmented basecoat (colorcoat). The colorcoat and clearcoat are preferably applied to have thickness of about 0.1-3 mils and 1.0-5.0 mils, respectively. A composition of this invention, depending on the presence of pigments or other conventional components, may be used as a basecoat, clearcoat, or primer. However a particularly preferred composition is .useful as a clear topcoat to prevent environmental chemical attack to the entire finish. A clearcoat composition of the present invention may be applied over a basecoat composition of the present invention.
The film-forming portion of the coating composition of this invention, comprising polymeric components, is is referred to as the binder or "binder solids" and is dissolved, emulsified or otherwise dispersed in an organic solvent or liquid carrier. The binder solids generally include all the normally solid polymeric non-liquid components of the total composition. Generally, catalysts, pigments, and non-polymeric chemical additives such as stabilizers are not considered part of the hinder solids. Non-binder solids other than pigments usually do not amount to more than about 5% by weight of the composition. In this disclosure, the terrri binder includes the acrylosilane polymer, the NAD polymer, tris(alkoxycarbony amino) triazine and other crosslinking agents and all other optional film-forming polymers.
The coating composition contains about 40-90% by weight of the binder and about 10-60% by weight of an organic solvent or another liquid carrier. The binder of the coating composition contains about 50-90%, preferably 60-80%, by weight of a film-forming acrylosilane polymer.
The acrylosilane polymer portion of the binder has a weight average molecular weight of about 1,000-30,000, a number average molecular weight of about 500-10,000
The acrylosilane polymer is the polymerization product of about 30-95%, preferably 50-90%, by weight ethylenically unsaturated non-silane containing monomers and about 5-70%, preferably 10-50% by weight ethylenically unsaturated silane containing monomers, based on the weight of the acrylosilane polymer. Suitable ethylenically unsaturated non-silane containing moromers are alkyl (meth)acrylates, styrene tmd any mixtures thereof, where the alkyl .groups have 1-12 carbon atoms, preferably 3-8 carbon atoms.
Suitable alkyl (meth)acrylate monomers used to form the acrylosilane polymer are methyl meth,acrylate, ethyl methacrylate, propyl methacrylate, butyl methacrylate, isobutyl methacrylate, pentyl methacrylate, hexyl methacrylate, ocryl methacrylate, nonyl methacrylate, lauryl methacrylate and the like; methyl acrylate, ethyl acrylate, propyl acrylate, butyl acrylate, isobutyl acrylate, pentyl acrylate, hexyl acrylate, octyl acrylate, nonyl acrylate, lauryl acrylate and the like. Cycloaliphatic (meth)acrylates also can be used, for example, such as trimethylcyclohlexyl methacrylate, trimethylcyclohexyl acrylute, iso-butyl methacrylate, t-batyl cyclohexyl acrylate, or t-butyl cyclohexyl methacrylate. Aryl (meth)acrylate and also can be used, for example, such as benzyl acrylate and benzyl methacrylate. Mixtures of the two or more of the above mentioned monomers are also suitable.
In addition to alkyl (meth)acrylates, other non-silane containing polymerizable monomers, up to about 50% by weight of the acrylosilane polymer, can be used for the puipose of achieving the desired properties such as hardness, appearance, mar resistance, and the like. Exemplary of such other monomers are styrene, methyl styrene. acrylamide, acrylonitrile, methacrylonitrile, ar.d the like. Styrene can be used in the range of 0-50% by weight
The acrylcsilane polymer may also comprise hydroxy f motional groups which can be provided by hydroxy alkyl (meth)acrylates having 1-4 carbon atoms in the alkyl group such as hydroxy ethyl methacrylate, hydroxy propyl methacrylate, hydroxy butyl methacrylate, hydroxy ethyl acrylate, hydioxy propyl acrylate hydroxy butyl ac-ylate and the like,
A suitable silane containing monomer useful in forming the acrylosilane polymer is an alkoxysilanejiaving the following structura; formula:
(Formula Removed)
wherein R is either CH3, CH3CH2, CH3O, or CH3CH2O; R1 and R2 are CH3 or CH3CH2; and R3 is either H, CH3, or CH3CH2; and n is O or a positive integer from 1 to 10. Preferably, R is CH3O orCH3CH2O and n is 1.
Typical examples of such alkoxysilanes are the acrylatoalkoxy silanes, such as gamma-acryloxypropyltrimethoxy silane and the methacrylatcalkoxy silanes, such as gamma-rnethacryloxypropyltrimethoxy silane, and gamma-methacryloxypropyltris(2-methoxyethoxy) silane.
Other suiiable alkoxy silane monomers have the following structural formula:
(Formula Removed)
wherein R, R1, and R2 are as described above and n is ;i positive integer from 1 to 10.
Examples of such alkoxysilanes are the vinylalkoxy silanes, such as vinyl trimethoxy silane, vinyl triethoxy silane and vinyl tris(2-methoxyethoxy)silane.
Other suitable silane containing monomers are ethylenically unsaturated acrylcxysilaries, including acrylatoxy silane, methacrylatoxy silane and vinylacetoxy silanes, such as vinylmethyldiacetoxy silane, acrylatopropyl triacetoxy silane, and methacrylatopropyltriacetoxy silane. Of course, mixtures of the above-mentioned .silane containing monomers are also suitable.
One preferred acrylosilane polymer contains the following
constituents: about 10-30% by weight styrene, about 5-15% by weight of ethyl hexyl methacrylaie, 40-60% by weight of hydroxy propyl methacrylate and 10-30% by weight of gamma methacryloxy propyl trimethoxy silane.
Silane functional macromonomers also can be used in forming the acrylosilane polymer. These macromonomers are the reaction producl of a silane containing compound, having a reactive group such as epoxide or isocyanate, with an ethylenically unsaiurated non-silane containing monomer having a reactive group,
typically a hydroxyl or an epoxide group, that is co-reactive with the silane monomer. An example of a useful macromonomer is the reaction product of a hydroxy functional ethylenically u.-isaturated monomer such as a hydroxy alkyl (meth)acrylate having 1-4 carbon atoms ,n the alkyl group and an isocyanato alkyl aJkoxysilane such as isocyanato propyl trietlioxysilane,
Typical of such above mentioned silane functional macromonomers are those having the following structural formula:
(Formula Removed)
wherein R, R1, and R2 are as described above; R4 is H or CH3, R5 is an alkylene group having 1-8 carbon atoms and n is a positive integer from 1-8.
A non silane containing acrylic polymer can be used in place of the silane containing acrylic polymer or in combination with the silane containing acrylic polymer and provide a coating composition which has adequate properties for some uses where a high level of acid etch resistance is not required. Typical of such an acrylic polymer is an acrylic polymer of polymerized monomers of styrene, alkyl (meth)acrylates having 1-12 carbon atoms in the alkyl group or any mixtures thereof and hydroxy alkyl (meth)acrylates having 1-4 carbon atoms in the alkyl group and the polymer has a hydroxyl number of about 50-200 and a weight average molecular weight of 1,000-200,000 and preferably 1,000-30,000.
In addition to the acrylosilane polymer or acrylic polymer, other film-forming and/or crosslinking solution polymers may be included in the present application. Examples include conventionally known acrylics, cellulosics, aminoplasts, urethanes, polyesters, epoxies or mixtures thereof.
A key component of the coating composition of the this invention is, in addition to the above polymeric components, about 5-25% by weight, based on the weight of the binder, of a non aqueous dispersed polymer(NAD) polymer. The NAD polymer is characterized as a polymer particle dispersed in an organic media, which particle is stabilized by sieric stabilization. Steric stabilization is accomplished by the attachment, commonly by adsorption, of a solvated polymeric or oligcmeric layer at the particle medium interface. The problem of providing a steric barrier has been considered in two parts: first, the selection of the soluble polymer whi:h comprises
the solvate sheath surrounding each particle and, secondly, the method of attaching or anchoring this polymer to the particle surface. Typically the NAD polymers are block or graft copolymer;; in which one component is the soluble stabilizing jiortion and the other portion, often termed the anchor, is insoluble in the continuous phase and is adsorbed on or is absorbed into the disperse phase. To increase the stability of the a dispersed.polymer, particularly to strong solvents, or to ensure that the stabilizer is not desorbed or displaced, the anchor group may be covalently linked to th In the NAD polymers of this composition, the dispersed phase or particle, sheathed by a steric barrier, will be referred to as the "macromolecular polymer" or "core.1 The stabilizer forming the steric barrier, attached to this core, will be referred to as the "macromonomer chains" or "arms."
The NAD polymers used in the coating composition of this invention solve the problem of cracking associated with silane coatings, These NAD polymers, reduce cracking and must be used in relatively higher amounts than when used for example, as flow control agents.
The NAD polymer contains about 10-90% by weight, preferably 50-80%, based on the weight of the NAD polymer, of a high molecular weight core having a weight average molecular weight of about 50,000-500,000. Tlie preferred average particle size is 0.1 to 0.5 microns. The arms, attached to the core, make up about 90-10% by weight, preferably 20-50%, of the NAD polymer, and have a weight average molecular weight of about 1,000-30,000, preferably 100O-10,0()0.
Preferably, the macromolecular core of the NAD polymer is comprised ofjpolyrnerized ethylenically unsaturated monomers. Suitable monomers include styrene, alkyl acrylate or methacrylate, ethylenically unsaturated monocarboxylic acid, and/or silane containing monomers. Such monomers as methyl methactylate contribute to a high Tg (transition glass temperature) NAD polymer, whereas such "softening" monomers as butyl acrylate or 2-ethylhexylacrylate contribute to a low Tg dispersed polymer, Other optional monomers arejiydroxyalkyl acrylates or methacrylates or acrylonitrile. It is noted that such functional groups as hydroxy can react with silane groups in the acrylosilane polymer to produce more bonding in the composition. If the core is crosslinked, allyl acrylate or allyl methacrylite, which crosslink with each other, can be used or an epoxy functional monomer such as
glycidyl acrylate or methacrylate can be used, which can react with a monocarboxylic acid functional cthylenically unsaturated monomer to crosslink the core,
The core :an contain silane functionality, for crosslinking purposes, which functionality may be provided by a small amount of one or more of the silane containing monomers mentioned above with respect to the film forming acrylosilane polymer. Suitably, the s ilane functionality is the primary or major means, preferably the sole means, of crosslinking in the core. Suitably about 2 to 10%, preferably about less than 5% of the monomers making up the macromolecular core ar.j silane monomers capable of crosslinking between themselves. Thus, crosslinking occurs by siloxane bonding (-Si-O-Si-). This silane crosslinking enables the core to behave as a non-crosslinked polymer before cure for good flow during applicatior, resulting in improved appearance. The core can crosslink during and after curing upon exposure to humidity and hsat during curing and/or exposure to humidity in the environment after curing. A further advantage of silane being present in the core is that the cured film does not blush when exposed to humidity, which blushing was found to occur without the presence of s ilane.
A distinctive feature of the NAD polymers used in this invention is the presence of macromonorner arms which are reactive, that is these arms have numerous reactive groups, referred to a "crosslinking functionalities,," which are adapted to react_with the acrylosilane polymer of the present composiiion. It is not known with certainty what portion of the these functional groups do, in fact, react with the acrylosilane polymer, because of the numerous and complicated sets of reactions which may occur during baking and curing of the composition, especially if additional film-forming binders are present. However, it may be said that a substantial portion of these functionalities in the arms, preferably the majority thereof, do in actuality react and crosslink with the film-former of the composition. If addjtional film-forming polymers are present, for example, a polyol, Lien the arms may react with film forming polymers other than the acrylosilane polymer. Suitably, about 3 to 30 % of the monomers which make up the macromonomer arms have reactive crosslinking functional groups. Preferably about 10 to 20% ol'the monomers have such reactive groups.
The arms of the NAD polymer should be anchored securely to the macromolecular core. For this reason, the arms preferably are anchored by covalent bonds. The anchoring must be sufficient to hold the arms to the NAD polymer after they react with the film-former polymer.
As indicated above, the arms or macromonomers of the NAB polymer serve to prevent the core from flocculating by forming what is referred to in the art as ajrteric barrier. The arm';, typically in contrast to the macromolecular core, are capable, at least temporarily, of being solvated in the organic solvent carrier or media of the composition. They may therefore be in a chain-extended configuration and their crosslinking functional groups are therefore relatively readily available to reaction with the silane groups of the film forming silane containing polymer. Such arms suitably comprise about 5 to 30% by weight, preferably 10 to 20%, based on the weight of macrornonomer, of polymerized ethylenically unsaturated hydroxy, epoxide, silane, acid, anhydride, isocyanate, amide, or other crosslinking functionality containing monomers, or combinations thereof, and about 70-95% by weight, based on the weight of the macromonomer, of at least one other polymerized ethylenically unsaturated monomer without such crosslinking functionality. Preferably the crosslinking functionality is a hydroxy, silane or epoxy containing mo.iomer, since such reactive groups can be utilized in one package systems, When the crosslinking functionality is an acid, anhydride, or isocyanate, then a two package system, with the dispersed polymer in a first package and the acrylosilane in a second package, is generally required. Combinations of the above-mentioned crosslinking functional groups are also suitable, although it is noted that hydroxy and silane groups have limited compatibility and are preferably not on the same macromonomer chain.
As an example, the macromonomer arms attached to the core may contain polymerized monomers of alkyl methacrylate, alkyl acrylate, each having 1-12 carbon atoms in the alkyl group, as well as glycidyl acrylate or glycidyl methacrylate or ethylenically unsaturated monocarboxylic acid containing monomers for anchoring and/or crosslinking. Typirally useful hydroxy containing monomers aie hydroxy alkyl acrylates or methacryl as described above.
A preferred composition for the NAD polymer that has hydroxy functionality comprises a core consisting of about 25% by weight hydroxy ethyl acrylate, about 4% by weight methacrylic acid, about 46.5% by weigh: methyl methacrylate, about 18% by weight methyl acrylate, about 1.5% by weight glycidyl methacrylate and about 5% styrene. The macromonomer attached to the core contains 97.3% by weight prepolymer and about 2.7% by weight glycidyl methicrylate, the latter for crosslinking or anchoring. A preferred prepolymer contains about 28% by weight butyl methacrylate, about 15% by weight ethyl methacrylate, about 30% by weight butyl aery lute, about 10% by weight hydroxyethyl acrylate, about 2% by weight acrylic acid, and about 15% by weight styrene.
The NAD polymer may be produced by conventionally known procedures. For example, it has been disclosed that such polymers may be produced by a process of dispersion free radical polymerization of monomers, in an organic solvent, in the presence of a steric stabilizer for the particles. The procedure has been described as basically one of polymerizing the monomers in an inert solvent in which the monomers are soluble but the resulting polymer is not soluble, in the presence of a dissolved amphiteric stabilizing agent. Such procedures have been extensively disclosed in both the patent and non-patent literature, for example, sej the above cited references regarding dispersed polymers in general, or U.S. patent 4,720,679 and PAINT AND SURFACE COATING: THEORY AND PRACTICE, ed. R. Lamboume (Ellis Horwood Limited 1987). The macromonomer arms can be prepared by cobalt catalyzed special chain transfer (SCT) polymerizai.ion, group transfer polymerization i.GTP), or free radical polymerization.
The coating composition of this invention contains about 5-25% by weight, based on the weight of the binder, of a crosslinking agent of t.ris(alkoxy carbonyl amino) iriazine. One particularly preferred crosslinking ageit is methoxy/butoxy carbonyl amino 1,3,5 triazine.
Optionally, blends of tris(alkoxy carbonyl amino) triazine and an alkylated melamine formaldehyde crosslinking agent can be used, Typically, the blend can contain up to 80% by weight of the alkylated melamine formaldehyde crosslinking agent. The range of constituents in the blend can be 20-100% tris(alkoxy carbonyl amino) triazine and correspondingly 80-0% of the alkylated melamine formaldehyde crosslinking agent, agent.
Typical alkylated melamine formaJdehyde crosslinking; agents that can be used are , for example, conventional monomeric or polymeric alkylated melamine formaldehyde resin that are partially or fully alkylated, One useful crosslinking agent is a methylated and buty!ated or isobutylated melamine formaldehyde resin that has a degree of polymerization of about 1-3. Generally, this melamine formaldehyde resin contains about 50% butylated groups or isobutylated groups and 50% methylated groups. Such crosslinking agents typically have a number average molecular weight of about 300-600 and a weight average molecular weight of about 500-1500. Examples of commercially available resins are "Cymel" 1168, "Cyme!"1161, "Cymel" 1158, "Resimine" 4514 and "Resimine" 354. Other crosslinking agents that can be use in the blend are ureu formaldehyde, benzoquanamine formaldehycie and blocked polyisocyanates.
A catalyst is typically added to catalyze the crosslinking of the silane moieties of the silane polymer with itself and with other components of the composition, including the dispersed polymer. Typical of such catalysts are dibutyl tin dilaurate, dibutyl tin diacetate, dibutyl tin dioxide, dibutyl tin dioctoate, tin octoate, aluminum titanate, aluminum chelates, zirconium chelate ami the like. Tertiary amines and acids or combinations thereof are also usefuljor catalyzing silane bonding, Preferably, these catalysts are used in the amount of about 0.1 to 5.0% by weight of the composition.
In addition, the coating composition may include a structured polymer, a STAR polymer, or a solvent reversible polymer (SRP).
To improve weatherability of a clear finish produced by the present coating composition, an ultraviolet light stabilizer or a combination of ultraviolet light stabilizers can be added in the amount of about 0.1-5% by weight, based on the weight of the binder. Such stabilizers include ultraviolet light absorbers, screeners, quenchers, and specific hindered amine light stabilizers. Also, an anitoxidant can be added, in the about 0.1-5% by weight, based on the weight of the binder.
Typical ultraviolet light stabilizers that are useful include
benzophenones, triazole;;, triazines, benzoates, hindered amines and mixtures thereof. Specific example:s of ultraviolet stabilizers are disclosed in U.S. Patent 4,591,533, the entire disclosure of which is incorporated herein by reference.
The composition may also include other conventional formulation additives such as flow control agents, for example, such as Resiflow !3 (polybutylacrylate). BYK 320 and 325 (high molecular weight polyacrylates); rheology control agents, such as fumed silica; water scavengers such is tetrasilicate, trimethyl orthoformate, triethyl orthoformate and the like.
When the present composition is used as a clearcoat (topcoat) over a pigmented colorcoat (ba;;ecoat) to provide a colorcoat/clearcoat finish., small amounts of pigment can be added to the clear coat to eliminate undesirable cobr in the finish such as yellowing.
The present composition also can be pigmented and used as the colorcoat, or as a monocoat or even as a primer or primer surfacer. Tie composition has excellent adhesion tc a variety of substrates, such as previously pjdnted substrates, cold rolled steel, phosphatized steel, and steel coated with conventional primers by electrodeposition, The present composition exhibits excellent adhesion to primers, for example, those that comprise crosslinked epoxy polyester and various epoxy resins, as well as alkyd n;sin repair primers. The present composition can be used to
coat plastic substrates such as polyester reinforced fiberglass, reaction injection-molded urethanes and partially crystalline polyamides.
When the present coating composition is used as a basecoat, typical pigments that can be added to the composition include the following: metallic oxides such as titanium dioxide, inc oxide, iron oxides of various colors, carbon black, filler pigments such as talc, china clay, barytes, carbonates, silicates and a wide variety of organic colored pigments such as quinacridones, copper phthalocyanim:s, perylenes, azo pigments, indanthrone blues, carbazoles such as carbazole violet, is oindolinones, isoindolones, thioindigo reds, benzimidazolinones, metallic flake pigments such as aluminum flake and the like.
The pigments can be introduced into the coating compoMtion by first forming a mill base or pigment dispersion with any of the aforementioned polymers used in the coating composition or with another compatible polymer or dispersant by conventional techniques, such as high speed mixing, sand grinding, ball milling, attritor grinding or two roll milling. The mill base is then blended with the other constituents used in the coating composition.
Conventional solvents and diluents are used to disperse dilute the above mentioned polymers to obtain the present coating composition. Typical solvents and diluents include toluene, xylene, butyl acetate, acetone, methyl isobutyl ketone, methyl ethyl ketore, methanol, isopropanol, butanol, hexane, acetone, ethylene glycol, monoethyl ether, VM and P naphtha, mineral spirits, heptane and other aliphatic, cycloaliphic, aromatic hydrocarbons, esters, ethers and ketones and the like.
The coating; composition can be applied by conventional techniques such as spraying, electrostatic spraying, dipping, brushing, flowcoating and the like, The preferred techniques te spraying and electrostatic spraying. After application, the composition is typically baked at 100-150 °C for about 15-30 minutes to form a coating about 0.1-3.0 mils thick. When the composition is used as a clearcoat, it is applied over the colorcoat which may be dried to a tack-free state and cured or preferably flash dried for 2 short period before the clearcoat is applied. The colorcoat/clearcoat finish is then baked as mentioned above to provide ;i dried and cured finish.
It is customary to apply a clear topcoat over a basecoat by means of a "wet-on-wet" application, i.e., the topcoat is applied to the basecoat without curing or completely drying the basccoat. The coated substrate is then heated for i predetermined time period to allow simultaneous curing of the base and clear coats.
Upon curing of dear topcoat compositions of the present invention, a portion of the silane containing polymer may migrates and stratifies to the top of the clearcoat, particularly when the acrylosilane polymer is used so as to pioduce a durable, weather-resistant clearcoat. Such stratification has been shown by electron scanning chemical analysis (ESCA) of a cross section of the cured layer of topcoat.
The coating composition can be formulated as a one-pac kage system that has an extended shelf life.
The following Examples illustrate the invention. All parts and percentages are on a weight basis unless otherwise indicated. All molecular weights disclosed herein are determined by GPC using a polystyrene standard.
EXAMPLE 1
Preparation of Polymer Solution 1 The following constituents were charged into ajgolyjaec,:zation vessel
equipped with a heating mantel, a reflux condenser, a stirrer, thermometer, a nitrogen
inlet and an addition funnel:
Portion 1 Parts by Weight
1-Pentanol 141.4
n-Pentyl; propionate 175.4
Portion 2
Styrene monomer (S) 230.8
2-Ethyl hexyl methacrylate (2EHMA) 115.5
Hydroxy propyl muthacrylate (HPMA) 577.1
Gamma-methacrybxy propyl trimethoxy silane 230.8
(MPTS)
Portion 3
Vazo 67 [2.2(2-methyl butane nitrile)] 91.9
n-Propyl propionate H6.6
Total 1739.4
Portion 1 was charged into the polymerization vessel and heated to its reflux temperature under nitrogen. Portion 2 was then added ovef a 330 minute period while maintaining1 the reaction mixture at its reflux temperature. Portion 3 was then added and the reaction mixture was held at its reflux temperature for an additional 30 minutes.
The resulting polymer solution had a weight solids of 67.9%, the polymer had a number average molecular weight of about 1,900 and a. weight average molecular weight of about 6,000 and contains the following constituents S/2EHMA/HPMA/MPTS tn a ratio of 20/10/50/20.
Preparation of a NAD (non-aqueous dispersion) A hydroxy functional NAD polymer dispersion was prepared by charging the following canstituents into a reactor equipped as above:
Portion! Parts by Weight
Isopropanol 179,26
Acrylic polymer solution (52% solids of an acrylic 2254.05
polymer of 15% utyrene, 28% butyl
rnethacrylate.30% butyl acrylate, 10% hydroxy
ethyl acrylate, 2% acrylic acid and 15% ethyl
methacrylate having a weight average molecular
weight of 10,000 in a solvent mixture of 82.2%
xylene and 17.8% butanol)
Mineral spirits 255.65
Heptane 1912,46
Portion 2
Heptane 28.75
t-Butyl peroctoate 4.68
Portion 3
Methyl methacrylate monomer (MMA) 1459.69
Hydroxy ethyl acrylate monomer (HEA) 784.81
Styrenemonome:(S) 156.97
Portion 4
Acrylic polymer solution (described above) 1126.52
Methyl methacrylate monomer 125.57
Methyl acrylate monomer 565.06
Glycidyl methacrylate monomer 47.05
Heptane ' 17.25
Portion 5
Mineral spirits 638,63
t-Butyl peroctoate 47.14
Isobutanol 127.31
Portion 6
t-Butyl peroctoatc 30,96
Isobutnaol 255.65
Portion 7
Heptane 167,25
Total 10,184.71
Portion 1 was charged into the reaction vessel and heated to its reflux temperature. Then Portion 2 was added to the reaction vessel mixed sind held at reflux temperature for 2 minutes. Then Portions 3 and 4 were added simultaneously with Portion 5, over a 210 minute period, to the reaction vessel while maintaining the resulting reaction mixture at its reflux temperature. Then the mixture was held at its reflux temperature for an additional 45 minutes. Portion 6 was added over a 90 minute period while maintaining the reaction mixture at its reflux temperature and then held at this tempera'.ure for an additional 90 minutes. Portion 7 was added and excess solvent is stripped off to give a 60% solids dispersion.
The resulting NAD polymer has a core having a weight average molecular weight of about 100,000-200,000 and arms attached to the oore having a weight average molecular weight of about 10,000-15,000.
CLEAR COAT COMPOSITION -1
The following constituents were charged into a mixing vessel and blended together to form a clear coating composition:
Portion Parts bv Weight
NAD dispersion (prepared above in Example 1) 22 90
Portion 2
"Tinuvin" 123 U. V. Light absorber 0.90
Tinuvin" 900 - 2.[2-hydroxy-3,5-di(1.1-dimethyl 1.00
(benzyl)phenyl]-2K-benzotriazole
"Tinuvin" 1130 (reaction product of b-3-(2H- 0/-5
benzotriazole(2-y I )-4-hydroxy-5-tert-butyl phenyl
propionic acid methyl ester and propylene glycol
300)
Portion 3
Butanol 6.00
D.C- 51 solution (10% solids of dimethyl siloxane 0.05
in solvent)
Fumed silica dispersion 6.67
Nacure 5543 (25% solids of dodecyl dibutyl 2.88
sulfonic acid, diisoporpanol amine blocked in
methanol)
TACT solution (50% solids in butanol of 23.67
methoxy/butoxy c arbonylamino 1,3.5 triazine)
Polymer Solution 1 (prepared above) 41.82
Total 111.02.
Portion 1 was charged into a mixing vessel and Portion 2 was premixed and ten added to Portion 1 with mixing and then Portion 3 was added with mixing to form a coating composition.
Phosphated steel panels that have been electrocoated with an electrocoating primer composition were sprayed coated with a conventional waterborne base coating composition that was prebaked for 5 minutes at about 83 °C
to form a basecoat about 15-1.0 mil thick The above prepared Clear Coating Composition 1 was sprayed applied to the basecoat of the panels and then the panels were fully cured by baking for 30 minutes at about 140 "C and had an excellent appearance.
Clear CoaLing Composition A was prepared which is identical to Clear Coating Composition 1 except the TACT solution was replaced with a "Cymel" 1168
penod while maintaining the reaction mixture at its reflux temperaturs. Portion 3 was then added and the reaction mixture was held at its reflux temperature for an additional 30 minutes.
The resulting polymer solution had a % weight solids of 67.9, the polymer had a number average molecular weight of about 1,900 and a weight average molecular weight of about 6,000 and contains the following constituents S/2EHMA/HPMA in a ratio of 25/25/50.
CLEAR COAT COMPOSITION -1
The following constituents were charged into a mixing vessel and blended together to form a clear coating composition:
Portion 1 Parts by Weight
NAD dispersion (prepared above) 2:2.90
Portion 2
"Tinuvin" 123 (described in Example 1) 0.90
"Tinuvin" 900 - 2-(2-hydroxy-3,5-di(l,l-dimethyl 1.00
(benzyl)phenyl]-2H-benzotriazole
"Tinuvin" 1130 I reaction product of b-3-(2H- 0,45
benzotriazole(2-yl)-4-hydroxy-5-tert-butylphenyl
propionic acid rr ethyl ester and propylene glycol
300)
Portion 3
Butanol 6.00
D.C. 57 solution (10% solids of dimethyl siloxane 0.05
in solveni.)
Fumed silica dispersion 6.67
Nacure 5.'543 (25% solids of dodecyl dibutyl 2.88
sulfonic ?.cid, di soporpanol amine blocked in
rnethanol)
TACT solution (50% solids in butanol of 23.67 .
methoxy/butoxy carbonylamino 1,3,5 triazine)
Polymer Solution 2 (prepared above) 41.82
Total 111,02
Portion 1 was charged into a mixing vessel and Portion 2 was premixed and ten added to Portion 1 with mixing and then Portion 3 was added with mixing to form a coating composition.
Phosphated steel panels that have been electrocoated with an electrocoating primer composition were sprayed coated with a conventional waterborne base coating composition that was prebaked for 5 minutes at about 83 °C to form a basecoat about 0,5-1,0 mil thick The above prepared Clear Coating Composition 2 was, sprayed applied to the basecoat of the panels and It en the panels were fully cured by baking for 30 minutes at about 140 CC and had,an excellent appearance.
Clear Coating Composition A (prepared in Example 1) was compared to Composition 2 for acid etch resistance. It is well known that acrylojilane containing composition have better acid etch resistance than non-silanc- containing acrylic polymers and therefore this composition was used instead of replacing TACT in Composition 2 with the alkylated melamine. Composition 2 was applied to the same type of phosphated, electrocoated primer and coated with a wateibome base coat as above and the pansls fully cured by baking as described above. The panels had an excellent appearance.
As in Example 1 the panels coated with Composition 2 and the panels coated with Composition A were compared side by side in the acid etcii test described in Example 1. A cumulative rating was determined for each panel. Composition 2 (the invention containing TACT) gave 30 units better acid etch resistance than did Composition A which contained a the acrylosilane instead of the acrylic resin without silane and the conventional alkylated melamine instead of TACT. This is surprising and unexpected that Composition 2 which did not contain an acrylosilane had a significant improvement in acid etch resistance. The use of TACT Composition 2 gave a superior acid etch resistant coating.
Various modifications, alterations, additions or substitutions of the components of the compositions of this invention will be apparent to those skilled in the art without departing from the scope and spirit of this invention. This invention is not limited to the illustrative embodiments set forth herein, but rather the invention is defined by the following daims.



WE CLAIM:
1. A coating composition comprising 40-90% by weight of film forming binder and 10-60% by weight of an organic liquid carrier such as herein described; wherein the binder comprises
(a) 50-90% by weight of an acrylosilane polymer consisting
essentially of 30-95% by weight, based on the weight of the
acrylosilane polymer, of polymerized monomers selected from
the group consisting of styrene, alkyl (meth)acrylates having 1-
12 carbon atoms in the alkyl group, hydroxy alkyl
(meth)acrylates having 1-4 carbon atoms in the alkyl group and
any mixtures thereof and 5-70% by weight, based on the weight
of the said polymer, of polymerized ethylenically unsaturated
monomers containing reactive silane groups and the polymer
having a weight average molecular weight of 1,000 - 30,000;
optionally acrylic polymer may be used
(b) 5-25% by weight of a non-aqueous dispersed polymer
(i) a macromolecular core having a weight average molecular weight of 50,000-500,000, and
(ii) attached to the macromolecular core, a plurality of macromonomer chains having a weight average molecular weight of 1,000-30,000 of 5-30% by weight, based on the weight of the macromonomer, of polymerized ethylenically unsaturated monomers which having functional groups selected from the group consisting of epoxide, anhydride, isocyanate, silane, acid hydroxy, amide or any
combination of these groups; and 70-95% by weight, based on the weight of the macromonomer, of at least one other polymerized ethylenically unsaturated monomer without a crosslinking functionality; and
(c) 5-25% by weight, of a crosslinking agent consisting of tris(alkoxy carbonyl amino) triazine.
2. The coating composition as claimed in claim 1, wherein the ethylenically unsaturated monomer containing reactive silane groups has the following structural formula:

(Formula Removed)
wherein R is either CH3, CH3CH2, CH3O, or CH3CH2O; and R1 are CH3 or CH3CH2; and R3 is either H, CH3, or CH3CH2; and n is 0 or a positive integer from 1 to 10.
3. The coating composition as claimed in claim 2, wherein the
acrylosilane polymer consist essentially of polymerized monomers of
alkyl (meth)acrylate, hydroxy (alkyl) methacrylate and the
ethylenically unsaturated monomer containing silane reactive groups.
4. The coating composition as claimed in claim 2, wherein the
acrylosilane polymer consists of polymerized monomers of styrene, hydroxy alkyl methacrylate and the ethylenically unsaturated monomer containing reactive silane groups.
5. The coating composition as claimed in claim 4, wherein the
acrylosilane polymer consists of polymerized monomers of 10-30% by
weight styrene, 5-15% by weight of ethyl hexyl acrylate, 40-60% by
weight of hydroxy propyl methacrylate and 10-30% by weight of
gamma methacryloxy propyl trimethoxy silane.
6. The coating composition as claimed in claim 1, wherein the
crosslinking agent contains up to 80% by weight, based on the weight
of the crosslinking agent, of an alkylated melamine crosslinking agent
having 1-4 carbon atoms in the alkylated group.
7. A coating composition substantially as herein described with
reference to the foregoing examples.

Documents:

3033-del-1998-abstract.pdf

3033-del-1998-assignment.pdf

3033-del-1998-claims.pdf

3033-del-1998-correspondence-others.pdf

3033-del-1998-correspondence-po.pdf

3033-del-1998-description (complete).pdf

3033-del-1998-form-1.pdf

3033-del-1998-form-13.pdf

3033-del-1998-form-19.pdf

3033-del-1998-form-2.pdf

3033-del-1998-form-3.pdf

3033-del-1998-form-4.pdf

3033-del-1998-form-6.pdf

3033-del-1998-gpa.pdf

3033-del-1998-petition-137.pdf

3033-del-1998-petition-138.pdf


Patent Number 215796
Indian Patent Application Number 3033/DEL/1998
PG Journal Number 12/2008
Publication Date 21-Mar-2008
Grant Date 03-Mar-2008
Date of Filing 14-Oct-1998
Name of Patentee E.I.DU PONT DE NEMOURS AND COMPANY
Applicant Address 1007 MARKET STREET, WILINGTON, DELAWARE 19898, U.S.A.
Inventors:
# Inventor's Name Inventor's Address
1 JEFFREY W. JOHNSON 1253 HARVARD DRIVE, ROCHESTER HILLS, MICHIGAN 48307,U.S.A.
2 MICHAEL D. FOX 45601 FOX LANE, APARTMENT 206, UTICA, MICHIGAN 48317, U.S.A.
PCT International Classification Number C09D 143/00
PCT International Application Number N/A
PCT International Filing date
PCT Conventions:
# PCT Application Number Date of Convention Priority Country
1 60/062,118 1997-10-15 U.S.A.