Title of Invention	A METHOD FOR PREPARING AN ALPHA OR ALPHA-BETA TITANIUM ALLOY
Abstract	A method of manufacturing titanium alloys in large-section semi-finished product form with controlled microstructure in micrograin and subcrystalline states of aggregation, with educed metallographic texture, is achieved with the desired combination of mechanical properties in the titanium alloy product.

Full Text

METHOD OF PROCESSING TITANIUM ALLOYS AND THE ARTICLE FIELD OF THE INVENTION The given invention is related to the field of metallurgy. More particularly, the invention relates to methods of preparing titanium alloys working with the lamellar structure. This invention is useful for making large semi-finished parts by working them with pressure to subsequently make finished products of different shapes. The large section parts may be utilized in aerospace industries, for example, disks, jet-engine blades, and airframe structures. BACKGROUND OF THE INVENTION Titanium alloys are hard to deform materials. Titanium alloys with microstructures of fine grains have better plasticity than those with coarse grains. The need to increase the plasticity of titanium alloys results in the need to develop methods of making titanium alloy microstructures with grain sizes less than about 10 micrometers. Such a microstructure can be obtained in small section semi-finished products, for example, in hot-rolled bars with diameters not exceeding 60 millimeters. The microstructure of semi-finished products is coarser in large section sizes. Most semi-finished products have a coarse lamellar microstructure with crystaliographic and metallographic texture having a grain size larger than 100 micrometers, Grain coarsening in titanium alloys results in unsatisfactory mechanical properties. A noteworthy feature of a coarse-grained lamellar microstructure is that it has a high degree of structural heterogeneity which results in 'combination of low tensile strength and lower plasticity, low fatigue properties, and significant scatter in mechanical properties. It is not possible to make make the coarse-grain lamellar microstructure into a fine-grain microstructure by heat treatment. On the otherhand, it is possible to coarsen fine-gram microstructure of titanium alloys at the temperatures of single beta phase existence and at the temperatures in the two phase alpha and beta regions. Producing a homogeneous fine-grain microstructure in titanium alloys would improve the technological properties during the 'hermomechanical processing due to reduction of stresses required for Dlastic flow Also, the superior mechanical properties of semi-finished Droducts would be provided, as well as superior mechanical properties after heat treatment It is Known mat it is possible to obtain a fine-grain microstructure in titanium alloys after rapid cooling from the molten state Because of the low heat and temperature conductivity of titanium alloys, it is impossible to use this method for industrial titanium ingots made in accordance with the modern technologies. This method is used in powder metallurgy. It is also known that in powder metallurgy it is possible to obtain a fine-grain microstructure due to the use of fine powder (about 50-100 micrometers) and a high solidification rate. One of the most significant disadvantages of powder metallurgy is the need to consolidate the powder. This limits the dimensions and size of the products, increases time.labor input, and the cost of the semi-finished product, Also, there is significant grain growth during consolidation due to the high temperatures of consolidation. Impurities from the powder particle surfaces reduce properties in comparison with the alloys made in accordance with traditional methods. The conventional method of working titanium alloys, such as-gatorizing, is known. It includes initial working at temperatures about 58°C lower than the recrystallization temperature, with subsequent heating and working (pressing/forging) of the alloys at the recrystalization temperature The recrystaiiization temperature is the temperature that the metal starts to deform. The formation of fine-grain microstructure is achieved by means of recrystaiiization of a work-hardened material during subsequent working. The above-mentioned method of microstructure refinement can be applied mainly for semi-finished products which had been previously intensely hot-worked in the alpha and beta regions, An elongated microstructure and strong texture are formed in these worked titanium alloys, which lead to significant allotropy of the mechanical properties. Thus, the prior art shows that the methods to manufacture large section titanium semi-finished products with uniform fine-grain microstructure and mechanical properties have not been achieved. There is a need to have methods to process titanium alloys that have substantially homogeneous fine-grain microstructure and mechanical properties throughout the workpiece. A method for preparing an alpha or alpha-beta titanium alloy article having a desired controlled homogeneous fine grain microstructure, comprising the steps of: i. starting with a titanium alloy article having an initial grain size (d0); ii. selecting a final grain size (dk) to achieve in the titanium alloy article a homogenous fine grain size (dk) Hi. plotting a curve of the relationship between a recrystallized grain size (d) for the titanium alloy on the y-axis versus a strain temperature (T) for the alloy on the x-axis, between a range of 400° C. and a temperature of complete polymorphous transformation (TCPT), in accordance with the relationship d=f(T); iv. locating an area T* on the strain temperature axis to divide the temperature axis into two zones comprising a first zone 400° C. to T*, and a second zone T* to TCPT, where the T* is located by first calculating a corresponding reerystallization grain size (d*) on the y-axis, where d* is logarithmically related to the initial grain size C0 by the ratio log (d0 /d*); v. further locating on the curve the final grain size (dk} on the y-axis and then a corresponding strain temperature TK on the x-axis, wherein the strain temperature TK is determined according to the final grain size; vi. determining heating and deforming stage and stages to process the article based on TK, with respect to the curve and the position of TK to the curve, where for TCPT >TK >T*, there is at least one heat and deforming stage to obtain the final grain size (dK), and where TK [a log(dn +1)]TM /Tn, where dn is the grain size before the beginning of n-stage, Tn is the strain temperature at n-stage in K degrees, TM is the melting temperature of the stock material in K degrees, and "a" is the coefficient which is a=1 at dn >10; a=1.5 at 1 µm vli. then heating and deforming the titanium alloy article in accordance with the determined number of heat and deforming stages to achieve (di viii. repeating paragraph (Vii) until the final controlled homogeneous grain size (dk) is obtained in the article having homogeneous mechanical properties. BRIEF DESCRIPTION OF THE INVENTION This invention satisfies the above-mentioned need by providing a method of manufacturing titanium alloys in large-section semi-finished product form with controlled microstrueture in microgram and subcrystalline states of aggregation, with reduced metallographic texture, to achieve the desired combination of mechanical properties in the titanium alloy product. In one embodiment of the invention there is a method for preparing a titanium alloy article, distinguished by having a substantially controlled homogeneous fine grain microstructure, comprising the steps of: (1) starting with a titanium alloy article having an initial grain size (d0); (2) selecting a final homogeneous fine grain size (dk) to be achieved in the titanium alloy article; (3) plotting a curve of the relationship between a recrystallized grain size (d) for the titanium alloy on the y-axis versus a strain temperature (T) for said alloy on the x-axis, between a range of 400° C. and a temperature of complete polymorphous transformation (Tcpi), in accordance with the relationship d=f(T); (4) locating an area T* on the strain temperature axis to divide the temperature axis into two zones comprising a first zone 400° C. to T*, and a second zone T* to TCPT, where said. T* is located by first calculating a corresponding recrystallization grain size (d*) on the y-axis, where d* is logarithmically related to the initial grain size do; (5) further locating on the curve the final grain size (dk) on the y-axis and then a corresponding strain temperature (TK) on the x-axis; (6) determining the heating and deforming stage or stages to process the article based on TK, where for TCPT >TK >T*, there is at least one heat and deforming stage to obtain the final grain size dk, and where TK reduce the grain size of the titanium alloy article [about 2 to 10 times) until the final grain size dk is obtained; (7) then heating and deforming the titanium alloy article in accordance with the determined number of heat and deforming stages to achieve d,, where each heat and Reforming stage has at least one heating and deforming step and one cooling step, where said heat and deforming stage occurs for a sufficient period of time to reduce the grain size of the titanium alloy article, and where the deformation of the titanium alloy article is in a substantially controlled manner during each heat and deforming stage at a rate of strain to achieve the desired grain size of the heat and deforming stage, where the true strain during the deformation is greater than or equal to 0.6 for each heat and deforming stage, and where said subsequent cooling is controlled at a temperature below the heat and deforming stage temperature at a cooling rate for substantially maintaining the reduced grain size obtained during the heat and deforming stage; and (8) repeating step (7) until the final substantially controlled homogeneous grain size dk is obtained in the article having substantially homogeneous mechanical properties. The final fine grain size is less than or equal to about 15 micrometers. A fine grain size is defined as grains having less than or equal to about 15 micrometers diameter. More narrowly, a preferred fine grain is less than 5 micrometers diameter. Conversely, large grains are greater than 15 micrometers diameter. When there is at least two heal and deforming stages, each heat and deforming stag* occurs for a sufficient amount of time to reduce the grain size cf the titanium alloy article about 2 to 10 times until the final grain size, dk, is obtained. Another embodiment of the invention is a method of making a substantially controlled homogeneous fine grain microstructure in a titanium alloy article, comprising the steps of: heating and deforming at a predetermined heat and deforming stage temperature at or below a temperature of complete polymorphous transformation where the titanium alloy article has sufficient ductility and a starting grain size, said heat and deforming stage contains at least one heat and deforming step and at least one cooling step, and where said heat and deforming stage is for a sufficient amount of time to reduce the grain size from the starting grain size at the beginning of the heat and deforming stage to a reduced grain size at the end of the heat and deforming stage, where deforming the titanium alloy is in a controlled manner at a rate of strain to achieve the desired grain size of the heat and deforming stage, where the true strain during the deformation is greater than or equal to 0.6 for each heat and deforming stage and where the cooling step is performed after the heat and deforming step at a temperature below the heat and deforming stage temperature, in a controlled manner at a cooling rate to substantially maintain the reduced grain size obtained during the heat and Reforming stage; and continuing to heat and deform then cool the litanium alloy article, at lower heat and deforming stage temperatures than the previous heat and deforming stage temperature, so a reduction of gram size is achieved in subsequent heat and deforming stages until a final controlled grain size with controlled mechanical properties is obtained in the titanium alloy article. Still another embodiment of the invention provides methods of making large section semi-finished products without any limits in size and shape, tn this invention, semi-finished product is defined as a material form, such as a bar, plate or billet, that is supplied for further processing. For example, a bar is a semi-finished product from which bolts, pins, etc., are manufactured. As another example, a billet is a semi-finished product from which aircraft disk forgmgs are made. The term large, section is relative to the pert being -semi-finished. For instance, a titanium alloy billet greater than about 4 inches could be termed large, disk forgmgs greater than about 30 inches diameter or 6 inches thickness are large. Also, when referring to titanium intermetallic based compositions such as those based on TijAI (alpha 2), TijAINb (orthomombic), or TiAt (gamma), a large section would be much smaller, since intermetallic materials are typically harder to process. A gamma or orthorhombic forging greater than about 12 inches could be termed large. The term Lamellar structure refers to alpha phase (hexagonal crystal structure) titanium arranged in plates. Often, plates share a common crystallography orientation and are termed a "colony'. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1- Relation of recrystallized grain size to strain temperature for titanium alloy BT8 at strain rate of 71CT-4 sec -1 and at 6*0 6 strain. The d* and T areas (at d0=1000 mm) are shaded. Fig 2- Microstructure of titanium alloy BT8 in initial state. Fig 3- Microstructure of titanium alloy BT8 after working at950°C Fig. 4- Microstructure of titanium alloy 6T8 after working at 650°C. Fig. 5- Relation of recrystailized grain size to strain temperature for titanium alloy BT1-00.) at strain rate of 310"* sec ~1 and at e-0.6 strain. The d* and T* areas (at dc= 200 mm) are shaded. Fig. 6- Microstructure of titanium alloy BT1-00 in initial state. Fig. 7- Microstructure of titanium alloy BT1-00 after working at 670 °C Fig. 8- Microstructure of titanium alloy BT1-00 after working at 400°C. Fig. 9- Relation of recrystallized grain sizt to strain temperature for titanium alloy BT30 at strain rate of 310-4 sec -1 and at e-0.6 strain. The d* and T* areas (at d,* 200 mm) art shaded. Fig. 10- Microstructure of titanium alloy BT30 in initial state. Fig. 11- Microstructure of titanium alloy BT30 after working at 740°C. Fig 12 Microstructure of titanium alloy BT30 (R.S.) after working at 550°C. DESCRIPTION OF THE INVENTION The invention it achieved by methods of working titanium alloys which include heating of the starting stock or ingot and its deformation inside preheated forging tools. A distinguishing feature of the method is that the temperature range for thermomechanical processing is extended to the range of about 400°C to Tcot, where Tcot is the temperature of the complete polymorphous transformation, also :alled the beta transus The temperature of complete polymorphous transformation (beta transus) is the temperature at which all alpha phase in the titanium alloy has transformed to beta phase. Before article the realtion of recrystallized grain size to strain temperature, d = f(T), in the* specified temperature range must be determined for the material of the stock. The specified temperature range (400°C to Tcpt) is then divided into two zones The boundary between those zones is set at the temperature T* at which the grain size is a*. The grain size d* can be determined from the ratio ig (dc/d) equals about 2.4 to about 2.6 for the alloys with the beta stabilization coefficient K8 about 1.8 to about 2 for the alloys with Ke> 1.4, where d0 is the grain size of the initial stock or ingot. The strain temperature TK is determined from the relationship d* f(T) accordingly to the required final grain size Depending on within which of the two ranges of temperature (T* to T^, or 400°C to T*) is located TK, the deformation can be done in one or several stages. The number of stages and the temperature of each stage shall be defined by subsequent adding to the TK temperature the difference in the temperatures a the nearest stages until the strain temperature exceeds or is getting equal to the T temperature. The deformation at each heating and deforming stage is processed by strain e not lets than 0.6. The heating of the stock or ingot at each following stage is provided to the temperature which does not exceed the strain temperature at the previous stage. The invention for processing the titanium alloys into controlled homogeneous fine grained articles can also be accomplished if the difference of tne stage temperature is determined in accordance with the curve d=f(T) in such a way that this difference allows reducing the grain size at each stage about 2 to 10 times. The deformation within each stage is provided with the total reduction of strain where e > [a lg(Vdn + 1)] TTn where dn is the grain size before the beginning of n-stage, Tn is the strain temperature at n-stage in K degrees. TM is the melting temperature of the stock material in K degrees, and "a" is the coefficient which is a»l at dn > 10; a=1.5 at 1µm Depending on the shape of the stock or ingot, the deformation axis may rotate or turn the stock and change the deflection angle of between about 45 - 90°. The deformation is performed in the preferred strain rate range of about 10 -4 • 10 -2 sec '. The deformation temperature should be corrected by multiplying a coefficient dependent on a semi-finished product volume. This coefficient is 0 98 for the volume up to 1 dm3,0.97 for the volume from 1 to 10 dm J, and 0.95 for the volume greater than 10 dm J. It should be noted that as the strain rate increases, the coefficient becomes a more important factor in the processing of the titanium alloys. The stock with the original beta-transformed grain size greater than 2000 micrometers must be worked (deformed) before the first heat and deforming stage at a temperature higher than the polymorphous transformation temperature, such that Tcpt + 10-50°C. The obtained grain size should be considered as the original grain size during the selection of the region of the main working. Before the first heat and deforming stage the stock with original beta-transformed grain size greater than 2000 micrometer* must be deformed with a reduction of 0.3 and strain rate in the range of 10-2-Sec-1 sec ' at the temperature higher than Tcpt - 30-50°C and with subsequent heating up to Tcpt 20-70°C and cooled down to room temperature at the wte of about 5 - 100'C/sec. The stock at least a ter the first strain stage should be cooled down to room temperature at the rate of about 5 • 100°C/sec. The thermocycle treating should be carried out in the temperature range from about 500 *C to T^ with the number of cycles from 1 to 5 before deforming. This may not be needed and depends on the grain sin of the titanium alloy stock. Also, the stock may be deformed in tools preheated to the temperature of about 10 - 50°C higher than the heating temperature of the worked alloy. This is an optional step. When a titanium bar is being processed and rotated around a single axis, the amount of steps of deforming may be chosen to be four or more at the final heat and deforming stage in additional to that the turning of the axis of deformation must be provided in a single plane. The forming of semi-finished products of different shapes from the stocks with prepared microsructures can be accomplished by forming them at a temperature not lower than the strain temperature of the stock at the final heat and deforming stage of the stock material. In addition to this, the following is also recommended: forming (shaping) must be done under superplasticity conditions. Local deformation must be used. The problem of making semi-finished products of unlimited sizes with micro- (≤15 micrometers) and submicro-crystalline ( of stocks or semi-finished products, and carrying out the block upsetting at the strain rate of about 10 -4 -10 -2 sec -1 and the true-strain not less than 0.2 within the temperature range from 400'C to T CpT where the upsetting temperature at the finishing stage is chosen to be not less than the strain temperature of the stock or semi-finished product with the coarsest grain size. In the case of upsetting of blocks of stocks or semi-finished products from alloys with different chemical compositions, (and therefore, with different strain temperatures at the final stage of stock working), the upsetting temperature must be not lower than the highest one of any of them. _ Another aspect is to set up a block of at least two stocks or semi-finished products, and place between them the layer from the same material with grain size (d) by an order of magnitude less than what is in the stocks or semi-products, The layer thickness should be not less than 10 d. The upsetting of the block must be earned out at the strain rate of 10-8 - 10-1 sec ', at 0.2 the true strain, in the temperature range from 400°C to Tcpt, and where, the upsetting temperature is chosen to be not lower than the temperature at the final stage of working at which, the grain size of the layer was obtained. The essence of the invention is based on the fact that the uniform fine-grained microstructure with required gram size up to submicro-crystalline grains is formed as the result of the process of dynamic recrystallization over the wide temperature range of 400°C -TCPT. At the temperatures lower than 400°C, the dynamic recrystallization of titanium and its alloys is difficult due to low diffusion mobility of atoms. Also, the dynamic recrystallization at those lower temperatures can not be carried out practically by the use of conventional equipment. At the higher temperatures unacceptable grain coarsing, not only during working but also at its end, will take place. It is necessary to determine the relation of recrystallized grain size to alloy strain temperature d=f (T). The obtained relation is true for the alloy of given chemical composition, and does not depend on the starting microstructure of the stock. The effect of the starting microstructure is taking into account by the introduction of calculated recrystallized grain size (d*), and corresponding to (d*), the T* strain temperature in the ratio d=f (T). The value d* can be determined in accordance with the lg(do/d*) * about 2.4 - 2.6, obtained experimentally for the titanium alloys with the beta-stabilization coefficient Ka _1.4, where da is the grain size of the initial stock. In accordance with the above-mentioned relation, the T* temperature can be considered in a range of temperatures, and T* depends on the initial grain size (d0) and increases with the initial grain size to about the temperature of tiie complete polymorphous transformation. The T* temperature divides the specified temperature range (400*C- TCP into two zones: TCPT - T* and T- 400°C. Within the first zone, including the T* temperature, working is processed in one step. Within the second zone, the stock is worked for more than one heat and deforming stage, with towering of the temperature. This is caused by the fact that the technological plasticity of titanium alloys significantly depends on the microstructure, which is why at each previous heat and deforming stage it is necessary to obtain the microstructure with the proper gram size that achieves the necessary level of technological plasticity at the subsequent stage. In order to get the microstructure with the required grain size (dK) in the given alloy stock with the known starting grain size (do), t is necessary to determine the working temperature (TK) which orovides the formation of that required grain size as well as the temperature T* in accordance with the curve d = f(T). The one or more stages of working must be determined depending on which temperature zone of the curve the TK is located. In the case when the working should be earned out at several stages, the amount of those stages and the' stage temperatures is chosen as follows: by adding step-by-step (sequentially) to the TK the regulated difference between stage temperatures until the strain temperature does not exceed (or is equal) to the TK. Values of true strain "e" are used, because the true strain is an equivalent for different loading, and it allows calculations of the required strain for processes like upsetting, drawing, extrusion, rolling, or torsion. A strain not less than 0.6 at each heat and deforming stage provides a dynamic recrystallization over the volume of the stock, and, therefore, results in an uniform fine grained microstructure. In the case of a mufti stage strain, the heating at each stage must be done until the temperature does not exceed the strain temperature at the previous stage, otherwise the grain size coaming will take place during heating. The invention essence can be additionally developed and made precise by the usage of the following procedures. During the multi-stage working (more than one heat and deforming stage) it is advantageous to bring the temperature down at each stage by a value that provides about 2-10 times reduction in grain size. It was determined experimentally that the temperature difference between the stages must provide reduction of recrystallized grain sizes by not less than 2 times. A grain size reduction less than twice does not provide an economical process. Reduction in the grain size more than 10 times reduces the material such that it will be insufficient to complete the dynamic recrystallisation at the next stage, and as a result, a non-uniform microstructure will be formed. At the lower strain temperatures, there is less material plasticity, and because of this, in the low part of the declared temperature range, the temperature decreasing steps must provide about 2 - 3 times reduction in the grain size, whereas at higher temperatures about 8-10 times can be used. Non-uniformity of plastic deformation depends upon temperature and initial stock micro$tructure significantly, and reduces simultaneously with increasing strain temperature and decreasing grain size. That is why in order to obtain uniform microstructure with the required grain size (from different starting conditions, and strain temperatures) working must be carried out at different true strains. In connection with the last, the following relation was determined experimentally: "e" = (a lg(\'dn +1)] TM/ Tn That relation allows one to determine the required strain which is enough for getting the uniform microstructure, in accordance with the temperature and grain size at a stage. By usage of conventional tools, in particular of flat dies, at strain about 06, there could exist a region of undeformed metal, typically a cone-shaped zone in a stock; the volume fraction of cone-shaped zone increases while the temperature decreases. Moreover, the required strain (determined at a stage in accordance with the temperature and the gram size) can exceed the value 0.6 in such a degree, that it is impossible to carry out that strain by a single pass. In such a case, the heat and deforming stage is performed in more than one step or pass, and each step or pass should be performed at the stage strain temperature After each pass it is recommended to turn the axes of deformation through 45 and 90* to eliminate the cone-shaped zones formed at the previous stages or passes. Working of the stock at each pass is earned out at not less than 0.1 strain and not more than 0.5 strain. At the lower strains, conditions for the development of the dynamic crystallization will not be generated. The restriction of the upper strain level is caused by the loss of mechanical stability of the stock at a following pass after a turn of axes of the strain. This allows achiavement of a required strain, to work through the cone-shaped zores, and to get structural uniformity without any metallographic texttre. Decreasing of a strain rate is one of the ways to improve the technological plasticity (hot ductility), and m consequence of that, of strain uniformity It is recommended to carry out the working or deforming at strain rates in the range of about 10-4 - 10 -2 sec -1. Dynamic recrystallization in that range can result in superplastic metal flowing, depending on the initial state of material, and additionally to increase or improve the microstructure uniformity of the processed article. Titanium alloys have low thermal conductivity. Therefore, during the working process, the temperature of the central area of a massive stock always is higher compared with that of peripheral areas, because of strain heating and insufficient transmission of heat in the stock central area. As a result, a coarse grain size can be formed in the center area of a massive stock. That is why in this invention the heating temperature is adjusted (depending on the stock size): multiplying the experimentally determined coefficients. In this case the difference in grain sizes over the stock volume is eliminated by heating during which the grains in the peripheral areas of the stock are getting coarser Titanium alloys with the size of beta-transformed grains more than 2000 micrometers have low hot ductility (low technological plasticity) at temperatures below Tcpt. In order to increase the uniformity of the alloy microstructure, the total strain must be increased by usage of multi-passes working at a stag*. Moreover, those titanium alloys have the T* near the Tcpt , therefore, it is expedient to provide a pre-working procedure of the titanium alloys with the size of beta-transformed grains more than 2000 micrometers before the main working process. This preliminary working can be carried out at about 30-50'C below Tcpt, a strait not less than 0.3, and a strain rate in the range of about 10 -2 - 10 ' sec-1 with subsequent annealing at temperature of Tcpt + 20-70°C. These conditions allow to refine the initial microstructure, and therefore, to make subsequent working easy, and at well, significantly to expend the temperature range, within which working is done at one stage. By choosing the parameters of main working, the grain size obtained by preliminary working should be considered as the initial one Increasing of the degree of laminss dispersion of double- phase titanium alloys contributes increasing of hot ductility and homogeneity of its strain because the thinner laminas the easier transformation of them into equaxed grains. Increasing of the degree of laminas dispersion is possible due to processes of heating up to the temperature above Tut and subsequent controlled cooling. The usage of the described above method before the first heat and deforming stage (as well as between stages or the passes at a stage) is especially effective for obtaining of the microstructure with grain sizes 'ess than 1 micrometer. Providing of a preliminary thermocycling treatment within the range of about 500'C - Tcpt before strain, results a decrease of grain size, and an increase of dislocation density within grains caused by phase and hest stresses. This leads further during subsequent strain to make recrystallization easier with an uniform microstructure. The main reason of the formation of a cone-shaped zone is high contact friction between the stock and the die (forging tools) in the contact zone Usually high temperature lubricants, such as glass enamel, are used to reduce the friction. However, the stock sticking to the surface of the tools can take place because of the lubricant loss. The loss makes the working at several stages with axis changing difficult. In order to reduce the friction impact, and as a result, to decrease the volume fraction of the cone-shaped zones, it is recommended to heat the press tools up to a temperature of about 10-50°C more than the stock temperature. In order to produce a stock shape closer to the net-shape of the semi-finished product, the method includes selections of sequences of the stock turns during multi-pass strain at the finish stage. For example, to make a bar at the finishing stage of working, the turn of deformation axis between passes is carried out at one plane, and the number of passes should not be less than four. The shaping of the semi-finished product from the stock with specified microstructure should be done at a temperature not below the strain temperature of the stock at the finishing stage. Otherwise, the coarsing of grains obtained at the preliminary working will take place. To obtain complicated shaped articles, the article should be treated to about TK or a little higher to increase the ductility of the material. The temperature should be at a temperature sufficient to increase the ductility without substantially changing the final grain size. Moreover, strain rate for shaping can be chosen in such a way to ensure superplastic conditions of deformation. This additionally improves the microstructure uniformity, and achieves a high level of mechanical properties after a final heat-treatment. The technological conditions of achieving a homogeneous fine grain microstructure in unlimited size or large semifinished products can be simplified by building up (gathering) a block in a prearranged size (specified size) from small stocks, and subsequently applying controlled strain of that block (for example, by upsetting) within the temperature range of 400°C-Tcpt, at strain rates of about 10 •' - 10' sec ', at not less than 0.2 strain. The specific block strain temperature must not be chosen below the strain temperature of stocks at the final stage. The described above working parameters insure superplastic flow conditions during the deformation of the block. The fundamental mechanism of superplattic deformation is grain boundary slipping (GBS), e.g., turn and slipping displacement of adjoining grains relatively to each other. GBS development during the block deformation allows to get a solid state joining of small stocks, moreover, at 0.2 and greater strain, the block becomes monolithic, and the boundary lines between the stocks that formed the block, disappear completely. This is achieved due to elimination of all possible ports in the joining area_ of the stocks by grain motion resulting from GBS, No less than 0.2 strain is required for stable superplastic deformation with maximum development of the GBT mechanism. Under such conditions the formation of high-grade solid state joining can be guaranteed. The semi-finished stocks worked by described above method can be used further as initial stocks to make larger semi-finished products. The requirements in physical, mechanical or service characteristics for different areas of the same large section products, for example, turbine disks for aircraft engines, can vary significantly. The assembly and subsequent deformation of stocks from alloys with different chemical composition, consequently, with different strain temperatures at the final working heat and deforming stage, may be considered like the method of making large section part. The assembled block has to be deformed at the temperature not less than the highest strain temperature among joined stocks. In some occasions it is technologically reasonable during the making of a semi-finished product, to place between the stocks layers from the stock material with grain size ten times finer than in the worked stocks This allows to work semi-finished products at lower temperatures using in a number of cases only local heating of the zone where solid-state bonding is formed, and, therefore, to use lower power equipment Usage of the layers provides localization of superplastic deformation within the solid-state bond formation, and, because of that, acceleration of the process of joint formation. The layer thickness should be not less than ten times the grain size. The invention is illustrated by the following examples. Three alloys the chemical composition of which is shown in the table were worked. Table I. (Table 1 Removed) Example 1, Samples (ø 10x 15 mm in size) cut from alloy A have been worked by upsetting in an universal dynamometer "INSTRON" at different temperatures in the range of 400-1000°C, at up to e*0.6 strain. In that case the temperature of 1000°C is equal to T^ temperature of the alloy. The size of the recrystallized grains should be determined in the central area of the deformed sample. The relation of recrystallized grain size to the alloy strain temperature is shown m Figure 1. The cylindrical stocks from A alloy (0 150 x 300 mm in size) have the size of beta-transformed grains of about 1000 micrometers (Fig. 2). After working, the microstructure with average grain size of dk= 5micrometers is required. In accordance with the d= f (T) curve in Figure 1, such grain size can be formed at temperature of Tk= 950°C. From the ratio lg (d0/d*)* 2.4-2.6 it can be determined that d*= 2,5-4 um, and then from the d=f(T) relation, the corresponding temperature of T*= 860-920°C is determined. The temperature range of 400-1000°C is divided by the T* temperature into two zones. Since the TK temperature at which the required grain size can be obtained is more than the T* temperature, the alloy is worked at the stage within the first temperature zone. The stock volume (0 150-300 mm) does not exceed of 10 dm3, thus, taking into account the correction factor of 0.97, the heating temperature will be of 925°C. The stock is placed into KS-500 resistor furnace. The heating time determined under condition that mm of diameter should be heated per minute wilt be minimum 180 minutes. After holding in the furnace, the stock is placed into an isothermal press tool which open dies from superalloy KC6-Y, are heated in low-frequency inductor up to 950°C The strain of the stock at the stage is carried out at the average rate of 71CT1 sec*1 . According to the ratio e≥ (a lg(√dn + 1)] T,/Tn,where Tn -strain temperature at n-stage about 1220°K deg., TM - melting temperature of the stock material (about 1970°K deg., a*1) it can be determined that the required strain (e) should be not less than 2.45. In order to compose that total (e) strah from the working chart included, the following steps can be used height stock upsetting up to e*0.45; the stock turn through 90°[ thus, that the direction of applied load (strain axis) will be coincide with the location (direction) of the maximum stock size after the previous upsetting ], and stock is upset at 6*0.45, the stock turn through 90° [thus, that the direction of applied ioad (strain axis) wtll be on the same plane on which strain axis was during the previous upsetting], and stock is upset at e= 0.3; upsetting in six passes at e= 0.25 at each pass, and stock turn through 45° after each pass thus, that strain axis remains on the same plane The final forming of the semi-finished stock into the rod of the required diameter by means of broaching at the temperature of 925°C is carried out. The microstructure of the worked rod is shown in Fig. 3 Example 2. The stock (0 50 x 100 mm) from alloy A with the initial beta-transformed grain size of 2000 micrometere should be worked out in such a way that the microstructure with average grain size of dk » 0.2 micrometer will be obtained. It can be determined that TK = 650°C. d*= 5-8 um and T* * 950-990°C. Hence the strain temperature (TK) is less than T*, the stock should be worked at several heat and deforming stages, the number of which is chosen in the next way: the grain size before the final stage should be chosen three times larger than the required final size.e.g., of 0.6 1m. The grain size of 0.6 mm in Fig. 1 correlates to the temperature cf 730°C, which does not exceed the T* temperature, therefore, one more (additional) heat and deforming stage is required. For instance, take the grain size at that additional stage 10 times coarser than at the previous stage (before the final stage), e.g., 6 µrn. The grain size 6 µm in Fig.1 correlates to the temperature of 97S°C, which is within the range T'-T,*, thus, this stage wiit be the first one. Therefore, the temperatures at the first, second and third stages will be 975, 730 and 650°C, respectively. The required strains at each of three stages determined taking into account. the strain temperatures and initial grain sizes at each stage will be et>245,e2 >1.5 ej>1.1 The thermocyclic treating which includes five repeated heatings up to 1000°C and cooling to 500°C should be carried out before the working of the alloy. The stock strain at each stage should be done at several passes (similar to example 1). At the final stage the stock can be formed into a rod, the cross section of which is equilateral triangle, or square, or equilateral texagon. The microstructure of the worked alloy is shown in Fig,4. Example 3, The stock (0 200 x 400 mm) from A alloy with the initial beta-transformed grain size of 1000 µrn should be worked out into a semi-finished disk product with the microstructure with average grain size of 3 urn. In this case, it is reasonable to refine the initial structure by carrying out strain at the temperature within the beta-phase area. For that purpose the stock is heated up to the temperature Tcpt+100°C (1100°C) and strained between fiat dies in accordance with the following chart: upsetting at e= 0.5 strain, and subsequent drawing up to the starting height. The stock temperature should be not decrease lower then Tcpt+100'C (1100°C), otherwise, intermediate heating should be done. The described above treatment will result in the beta-transformed grain size of 1000 µm, and that grain size is used for definition of the T* temperature (required for achievement of the grain size 3^m ) and can be defined from the curves in Figure 1. The heating temperature and required strain of the stock can be defined similar to Example 1 The die tools shall be heated up to the temperature 900gC. After described above structure preparation, the stock is first formed into the disk stock 350 mm in diameter. The final semi-finished disk product will be obtained by flattening under superplastisity conditions. Example 4. It is required to work a stock (100 x 100 x 200 mm) from alloy A with the initial beta-transformed grain size of 5000 µm into the stock of the same size and grain size of 2 µm. In order to reach that (joal, it is expedient preliminarily to refine the initial grain structure. For (his purpose the stock shall be heated up to the temperature Tcpt40°C 9603C) and upset through the height on flat dies at e*0.25 strain and at strain rate of 10-2 sec \ and then it is formed by drawing into the nitiai size stock and heated up to the temperature of Tcpt4-20°C ;i0208C) The described treatment will result in the beta-transformed gram size of 500 µm , and the last is used for defining of the T* temperature (in that case, it will be 780-830°C ). The TK temperature required for achieving the grain size of 3 µm can be defined from the curves in Figure 1. That is the temperature 830°C, e.g.,within the range of T*- Tw, therefore, the stock will be preliminary worked at one stage. The heating temperature and required strain of the stock can be defined similar to Example 1. The strain should be carried out at rate of 10-3 sec at six passes with turn of the stock through 90° after each pass in such way that upsetting (load direction) will coincide with the largest stock size. The strain at each stage is e-0.4 At the final stage the stock can be under superplastic conditions at 830°C into a rod, the cross section of which is equilateral triangle, or square, or equilateral hexagon. Example S. It is require to work a stock (100 x 100 x 200 mm) from alloy A with the initial beta-transformed grain size of 5000 1m into the stock of the same size and grain size of 1.2 urn. in order to reach that goal, it is expedient preliminarily to fine the initial grain structure. For this purpose the stock shall be heated up to the temperature TW-400C (960°C) and upset through the height on flat dies at e-0 25 strain and at strain rat* of 10-2sec and then it is formed by drawing into the initial size stock and heated up to the temperature of TCpt+20°C (1020°C) and then water cooled to room temperature. The described above treatment will result in the beta-transformed grain size of 500 urn, and the last is used for defining of the T* temperature (in that case, it will be 780-830°0 ). The TK temperature required for achieving the grain siz* of 1 2 µm can be defined from the relation d=(T) in Figure 1. That is the temperature 790°C, e.g..within the range of T*- T^, therefore, the stock will be preliminary worked at one stage. The heating Temperature and required strain of the stock can be defined similar to Example 1. The strain should be carried out at rate of 10 sec.' at six passes with turn of the stock through 90° after each pass in such way that upsetting (load direction) will coincide with the largest stock size. The strain at each pass is e=0.4. Example 6. Samples (0 10 x 15 mm in size) cut from B alloy have been worked by upsetting in an universal dynamometer "INSTRON" at different temperatures in the range of 400-900°C, at up to e*0.6 strain. In that case the temperature of 9CO°C is equal to Tcpt temperature of the alloy. The size of recrystailized grains should be determined in the central area of the deformed sample. The relation of recrystailized grain size to the alloy strain temperature is shown in Figure 5. It is necessary in the stock (0 50 x 100 mm ) cut from alloy B with the initial grain size of 200 µm (Fig.6) to obtain the microstructure with the average grain size of 5 micrometers. Determined values of the TK and T* temperatures are of 700°C and 520-550°C, respectively As the TK exceeds T, so the stock is worked at one stage. The choice of the strain, heating temperature, and strain chart is carried out in the way illustrated in example 1 The final shape of the semi-finished product will be the square section parallelepiped 55 µm in side size. The microstructure of the worked stock after treating is shown in Fig. 7. K Example 7. It is necessary in the alloy B stock (0 50 x 100 mm )with the initial grain size of 200 urn (Fig,6) to obtain the microstructure with the average grain size of 0,1 µrn. Determined values of the TK and T* temperatures are 400°C and 520-550°C, respectively. As the T, temperature is less than T*, the stock will be worked at several stages, the number of which can be determined as follows. The grain size before the final stage is chosen twice larger (coarser) (e.g., 0.2um). The grain size of 0.2um correlates to the temperature 450°C (see the curve in Fig.5) which does not exceed T*, thus, one more stage is required Let's choose the grain size at the previous before that stage 10 times coarser (eg.,4 µm) The temperature correlates that grain size (Fig.5) is 670°C)within the zone of T*-TCpt). Thus, the stock should DO worked at four stages, and the temperature at each stage are 670, 500. 450 and 700°C The strain at each stage can be determined taking into account the strain temperature at the stage and the initial grain size before working at each stage. The stock at each stage is deformed at several passes similar to that in example 1. At the final stage the stock can be formed into a rod, the cross section of which is equilateral triangle, or square, or equilateral hexagon. The microstructure of the worked alloy is shown in Fig. 8. Example 8. Samples (0 10 x 15 mm in size) cut from alloy C sample have been worked by upsetting in an universal dynamometer "INSTRON" at different temperatures in the range of 400-740°C , at up to e*0.6 strain, in that case the temperature of 740°C is equal to Tw temperature of the alloy. The size of recrystallized grains should be determined in the central area of the deformed sample. The relation of recrystallized grain size to the alloy strain temperature is shown in Figure 9. It is necessary in the alloy C stock (0 50 x 100 mm) with the initial grain size of 200 urn (Fig. 10) to obtain the microstructure with the average grain sizt of 5 Mm. Determined values of the TK and T* temperatures are of 740°C and 710-725°C, respectively. As the T, exceeds T'.and it is equal to Tcpt, so the stock is worked at one stage at the temperature of 740°C. The choice of the strain, heating temperature, and strain chart is carried out in the way illustrated in example 1 The microstructure of the worked stock is shown in Fig 11. Example 9. It is necessary in the alloy C stock (0 50 x 100 mm ) with the initial grain size of 200 um (Fig. 10) to obtain the microstructure with the average grain size of 0.3 urn, Determined values of the TK and T* temperatures are of 550°C and 710-725°C, respectively. As the Tk is less than T*, the stock will be worked at several stages. The grain size before the final stage is chosen three time larger (0.6 um) than the required after the final stage. From the relation d=f(T) for alloy C (see Fig, 9) it is follows, that the grain size of 0.6 um correlates to the temperature of 645°C At the following stage the grain size should be chosen 5 time larger (3 µm) than at the previous stage. That grain size (3 jim) correlates to the temperature of 730°C, which is between T-Tcpt, therefore, that stage wiii be the first one during working. The choice of the strain, heating temperature, and strain chart at each stage is carried out in the way illustrated in example 1 . Moreover, after working at the first stage, the stock should be water cooled to room temperature The microstructure of the worked stock is shown in Fig 12. Example 10. It is necessary in the alloy C stock (0 50 x 100 mm ) with the initial grain size of 40 µrn to obtain the microstructure with the .average grain size of 0.5 µm- Determined values of the Tk and T* lemperatures are of 625°C and 600-645°C, respectively. As the Tk is within the range T*-TCPt the stock will be worked at one stage. Before :he main treatment, the stock is heated to the temperature of 760°C and water cooled then to room temperature. The choice of the strain, neating temperature, and strain chart at each stage is carried out in the illustrated in example 1 . Example 11. It is necessary to obtain a semi-finished product with the average grain size of 5 urn from the alloy A stock (0200 x 400 mm ) with the beta-transformed grain size of 2000 µm, The values of the TK and T* temperatures determined from the curve in Figure 1 are of 950°C and 950-990°C, respectively. As the Tk is within the range T*-Tcpt the stock wtll be worked at one stage. It can be defined that the required strain e should be not less than 2.7. In order to achieve that total strain, the next strain chart should be used: stock heating up to the temperature of 95 °C, stock deformation through the stock height at 0.25 strain, subsequent water cooling to room temperature; stock heating up to the temperature of 950°C, stock deformation through the stock at five passes at 0.25 strain at each pass, and with the stock turn through 90° between the passes, and subsequent water cooling to room temperature; repeat two previous paragraphs. The rod 100 µm in diameter will be obtained after the final formation Example 12. Cylindrical stocks 40 mm in height are cut from a rod (0 20 mm) from alloy B with submicrocrystalline structure with the average grain size of 0.1 µm The stocks are heated in an electrical furnace in Argon inert atmosphere up to the temperature of 400°C and upset at the average strain rate of 510-4 sec ' up to 10 mm in height in a large (100 tonne power) hydraulic press between plain dies preheated by an inductor up to 400°C. The stocks of a disk shape 40 mm in diameter will be produced. The grain size in the disk stocks retain of 0.1 µm. The disk stocks are machined to 38 mm in diameter. The upper and bottom surfaces of the disk stocks are being polished ( from each surface the layer not less than 0.5 mm has been deleted). During the mechanical treatments, the heating of the surface of the worked disk stock must not exceed 50°C. The polished surfaces are washed, dried and decreased. Then the block in the form of a cylinder 38 mm in diameter and 81 mm in height is set up from nine stocks 38 mm in diameter and 9 mm in height placed one over another coaxially. In order to fix the assembled block and to protect the inner contact surfaces of the stocks from oxidation, laser welding must be performed to the depth not more than 0.3 mm along the ring line of the stock joint. The stocks block is heated in an electrical furnace in Argon inert atmosphere up to the temperature of 400°C and upset at the average strain rate of 510-4 sec 1 up to 10 mm in height in a large (100 tonne power) hydraulic press between simple (plain) dies preheated by an inductor up to 400°C. The semifinished product 108 mm in diameter and 10 mm in height will be obtained. The grain size in the disk stocks remains 0.1 µm over the whole volume. Porosity in the zone of solid-phase joining is not revealed by metallography. Using the process which is analogous to described above, a disk stock with submicrocrystalline microstructure and practically of any size can be manufactured making use of industry heating and forging equipment. [Example 13. Cylindrical stocks 60 mm in height are cut from a rod (0 30 mm) from alloy A with submicrocrystalline structure with the average gram size of 0.4 µm The stocks are heated in an electrical urnace in Argon-inert atmosphere up to the temperature of 700°C and jpset at the average strain rate of 510-4 sec-1 up to 10 mm in height in a large (100 tonne power) hydraulic press between simple dies preheated by an inductor up to 700°C. The stocks of a disk shape about 74 min in diameter and 10 mm in height wirl be produced . The grain size in the d(Sk stocks remains of 0.4 µm. The disk stocks are Tiachined to 72 mm in diameter. The upper and bottom surfaces of the disk stocks are polished (from each surface the layer not less than 05 mm has been removed) and made parallel. During the mechanical treatments, the heating of the surface of the worked disk stock must not exceed 50°C. The polished surfaces are washed, dried and degreased. Then the block in the form of a cylinder 72 mm in diameter and 144 mm in height is set up from 16 stocks, 72 mm in diameter and 9 mm in height placed one over another coaxiaily. In order to fix the assembled block and to protect the inner contact surfaces of the stocks from oxidation, laser welding must be performed to the depth not more than 03 mm along the ring line of the stock joint. The stocks block is heated in an electrical furnace in Argon-inert atmosphere up to the temperature of 700°C and upset at the average strain rate of 510-4 sec-1' up to 20 mm in height in a large (100 tonne power) hydraulic press between simple dies preheated by an inductor up to 700CC. The semifinished product 192 mm in diameter and 20 mm in height will be produced. The grain size in the disk stocks remains of 0,4 µm over the whole volume. Porosity in the zone of solid-phase joining is not revealed by metallography. Using the process which ts analogous to above, a disk stock with submicrocrystalline microstructure and practically of any size required for development can be manufactured using industry heating and forging equipment. Example 14, Cylindrical stocks 100 mm in height are cut from a rod .0 50 mm) from alloy C with submicrocrystalline structure with the average grain size of 2.0 µrn. The stocks are heated in an electrical 'urnace in Argon men atmosphere up to the temperature of 7006C and jpset at the average strain rate of 510-4 sec-1' up to 10 mm in height in a large (100 tonne power) hydraulic press between simple dies preheated by an tnductor up to 700°C. The stocks of a disk shape about 158 mm in diameter and 10 nm in height will be produced . The gram size in the disk stocks remains of 2 µm. The disk stocks are machined to 156 mm in diameter. The upper and bottom surfaces of the disk stocks are being polished {from each surface the layer not less than 0,5 mm has been removed) and made parallel. During the mechanical treatments, the heating of the surface of the worked disk stock must not exceed 50"C. The polished surfaces are washed, dried and degreased Then the block in the form of a cylinder 72 mm in diameter and 144 mm in height is set up from 16 stocks, 72 mm in diameter and 9 mm in height placed one over another coaxially. In order to fix the assembled block and to protect the inner contact surfaces of the stocks from oxidation, laser welding must be performed to the depth not more than 0.3 mm along the ring line of the stock joint The block unit in the form of a cylinder 158 mm in diameter and 306 mm in height is assembled from 34 stocks of 156 mm in diameter and 9 mm in height placed one over another coaxially. The block assembly is carried out directly on the lower flat die installed in a 1600 tonne power hydraulic press. After the end of the assembly the block is tightened by lowering of the upper flat die. The compression stress does not exceed 10 tonne. The dies together with the stocks block are heated in an inductor in argon atmosphere up to the temperature of 700°C and then upset to 30 mm in height at the average rate of 510-4 sec 1. The working surfaces of the dies from alloy KC6-Y (Russian Spec.) are preliminary coated with a thin layer of boron nitride in order to reduce friction coefficient and prevent sticking to the stock. Thus, the semi-finished product of about 498 mm in diameter and 30 mm in height will be produced The grain size in the disk stocks remains of 2 µm over the whole volume. Porosity in the zone of solid-phase joining is not revealed by metallography. Example 15. In the way simitar to described in the above examples the cylindrical disk-type stock 300 mm in diameter and 50 mm in height is made of the 0 20 mm rod from alloy A with microcrystalline microstructure The strain temperature is 650°C. The ring stock 300 mm in outer diameter and 100 mm in inner diameter is made from that disk stock by cutting off its central area by a mechanical, or anode-mechanical, or arc cutting by fusion method. The cylindrical stockø 0 100-0.15 - mm and 50 mm in height are made of the 0 20 mm rod from ailoy C accordingly to described in previous examples manner Moreover, the strain temperature is 850°C. Then the disk stock 300 mm in diameter and 50 mm in height is assembled from the alloy A hng stock and the alloy C stock by installing the alloy C stock into the center of the alioy A ring stock. Before assembling the contact flat surfaces of the block stock have to be polished (the heating of the surfaces must not exceed 50°C during polishing). The polished surfaces are washed, dried and degreased. Then the block in the form of a cylinder 38 mm in diameter and 81 mm in height is set up from nine stocks 38 mm in diameter and 9 mm in height placed one over another coaxially In order to fix the assembled block and to protect the inner contact surfaces of the stocks from oxidation, laser welding must be performed to the depth not more than 0.5 mm along the ring line of the stock joint. The assembled block stock is installed on the bottom die in a 1600 tonne power hydraulic press and tightened by lowering of the upper flat die. The compression stress does not exceed 10 tonne. The dies together with the block stock-are heated in an inductor in argon atmosphere up to the 650°C and upset to of 25 mm in height at the average rate of 510-4 sec-1 '. In order to reduce friction coefficient and prevent the dies working surfaces from sticking to the stock, the working surfaces of the dies are preliminary coated with a thin layer of boron nitride. As a result, the monolithic semi-finished disk stock 424 mm in diameter and 25 mm in height will be obtained. The central area of that disk stock is mad from alloy C with the grain size of 05 µm, and the rim - from alley A with gram size of 0.2 µm Example 16 In accordance with the represented above examples, the cylindrical disks 350 mm in diameter and 70 mm in the height with grain size of 3 µm are made from alloy A under superplastic deformation conditions at the temperature of 900*C. The sheet stocks 350 mm in diameter and one mm in the height are made of the 0 20 mm rod from the same alloy with grain size of 0 2 µm are made by superplastic strain, and subsequent upsetting, rolling, and machining. Then between each couple of the disk stock (placed coaxialiy on each other) the sheet-stock is placed. In that manner the cylindrical block stock 350 mm in diameter and 354 mm in height will be set up (assembled). Before assembling the contact flat surfaces of the stocks have to be polished (the heating of the surfaces must not exceed 50°C during polishing). The polished surfaces are washed, dried and degreased. The block stock assembly is carried out directly on the lower flat die installed in a 1600 tonne power hydraulic press. After the end of the assembly the block is tightened by lowering of the upper flat die. The compression stress does not exceed 10 tonne. The dies together with the block stock are heated in an inductor in argon atmosphere up to the 650°C and upset to of 351 mm in height at the average rate of 510-4 sec-1 In order to reduce friction coefficient and prevent the dies working surfaces from sticking to the stock, the working surfaces of the dies are preliminary coated with a thin layer of boron nitride. As a result, the monolithic semi-finished disk stock 350 mm in diameter and 351 mm in height will be made. In the described above manner twice longer monolithic cylindrical stock can be made from those described in the paragraph above by placing between them the sheet-stock and 0.8 mm upsetting. In that case, local heating is used only for the stocks-block (it is not necessary to heat dies). In order to eliminate the difference in grain size caused by the presence of submicrocrystalline microstructure of the sheet layers, the obtained block-stock ss annealed at the temperature of 900°C. After that heat treatment the made rod stock 350 mm in diameter will have the uniform microttructure with the grain size of 3 µm. We claim: 1. A method for preparing an alpha or alpha-beta titanium alloy article having a desired controlled homogeneous fine grain microstructure, comprising the steps of: i. starting with a titanium alloy article having an initial grain size (d0); selecting a final grain size (dK) to achieve in the titanium alloy article a homogenous fine grain size (dk); iii. plotting a curve of the relationship between a recrystallized grain size (d) for the titanium alloy on the y-axis versus a strain temperature (T) for the alloy on the x-axis, between a range of 400° C. and a temperature of complete polymorphous transformation (TCpT), in accordance with the relationship d=f(T); iv. locating an area T* on the strain temperature axis to divide the temperature axis into two zones comprising a first zone 400° C. to T*, and a second zone T* to TCPT, where the T* is located by first calculating a corresponding recrystallization grain size (d*) on the y-axis, where d* is logarithmically related to the initial grain size d0 by the ratio log (d0 /d*); v. further locating on the curve the final grain size (dk) on the y-axis and then a corresponding strain temperature TK on the x-axis, wherein the strain temperature TK is determined according to the final grain size; vi. determining heating and deforming stage and stages to process the article based on TK, with respect to the curve and the position of TK to the curve, where for TCPT >TK >T*, there is at least one heat and deforming stage to obtain the final grain size (d«), and where TK [a log(dn +1)]TM /Tn, where dn is the grain size before the beginning of n-stage, Tn is the strain temperature at n-stage in K degrees, TM is the melting temperature of the stock material in K degrees, and "a" is the coefficient which is a=1 at dn >10; a=1.5 at 1 µm vii. then heating and deforming the titanium alloy article in accordance with the determined number of heat and deforming stages to achieve (dK), where each heat and deforming stage has at least one heating and deforming step and one cooling step, where the heat and deforming stage occurs for a sufficient period of time to reduce the grain size of the titanium alloy article, and where the deformation of the titanium alloy article is in a substantially controlled manner during each heat and deforming stage at a rate of strain to achieve the desired grain size of the heat and deforming stage, where the true strain during the deformation is greater than or equal to 0.6 for each of the at least two heat and deforming stage, and where the one cooling step is conducted to temperatures below the heat and deforming stage temperature at a cooling rate for substantially maintaining the reduced grain size obtained during the heat and deforming stage; and viii. repeating paragraph (Vii) until the final controlled homogeneous grain size (dK) is obtained in the article having homogeneous mechanical properties. 2. A method for preparing the titanium alloy article according to claim 1 wherein as a result of the method the desired final fine grain size is less than or equal to about 15 micrometers. 3. A method for preparing the titanium alloy article according to claim 1 where each of the at least two heat and deforming stage occurs for a sufficient amount of time to reduce the grain size of the titanium alloy article about 2 to 10 times until the final grain size (dk), is obtained. 4. A method for preparing the titanium alloy article according to claim 1 where a deformation axis is turned 45-90° between steps. 5. A method for preparing the titanium alloy article according to claim 1 where the deformation is performed at a rate in the range of about 10 to 10-2 sec-1. 6. A method for preparing the titanium alloy article according to claim 1 where the temperature of deformation is corrected by multiplying a coefficient dependent on an article volume where the coefficient is 0.98 for the volume up to 1 dm3, 0.97 for the volume from 1 to 10 dm3, and 0.95 for the volume greater than 10 dm3. 7. A method for preparing the titanium alloy article according to claim 1 where the article with an original beta-transformed grain size greater than 2000 urn is deformed before the first heat and deforming stage at a temperature greater than TCpT+10-50°C. 8. A method for preparing the titanium alloy article according to claim 1 where before the first heat and deforming stage, the article with original beta- transformed grain size greater than 2000 urn is deformed with a reduction of area of 0.3 and strain rate in a range of about 10-2 to 10~3 sec-1 at a temperature greater than TCPT -30-50° C. and with subsequent heating up to about TCPT +20- 70° C. 9. A method for preparing the titanium alloy article according to claim 1 where before the article is deformed, the article is heated up to about TCPT +20-70° C. and cooled to room temperature at a rate of about 5-100° C./sec. 10. A method for preparing the titanium alloy article according to claim 1 where after the first heat and deforming stage, the article is cooled to room temperature at a rate of about 5-100° C./sec. 11. A method for preparing the titanium alloy article according to claim 1 where after each step in the heat and deforming stage, the article is cooled to room temperature at a rate of about 5-100° C./sec. 12. A method for preparing the titanium alloy article according to claim 1 where a thermocycle treatment is conducted in a temperature range of about 500° C. to TCPT for about 1 to 5 cycles before deforming. 13. A method for preparing the titanium alloy article according to claim 1 where tools for deforming the article are preheated to a temperature of about 10-50° C. higher than the heating temperature of the article for deforming. 14. A method for preparing the titanium alloy article according to claim 1 where the steps in the final heat and deforming stage is not less than four and an axis of deformation is in a single plane. 15. A method for preparing the titanium alloy article according to claim 1 where the method further comprises providing a semi-finished product of definite shape from the article at temperatures not lower than the heat temperature in the final heat and deforming stage. 16. A method for preparing the titanium alloy article according to claim 1 where the deforming is done under superplasticity conditions. 17. A method for preparing the titanium alloy article according to claim 1 where the method further comprises providing titanium alloys with different chemical compositions processed at different temperatures during the final heat and deforming stage. 18. A method for preparing the titanium alloy article according to claim 1 where the method further comprises providing a block of two or more articles, each block comprising a layer between the articles, the layer formed from the same article material with grain size (d) having an order of magnitude less than the grain size in the block. 19. A method for preparing an alpha or alpha-beta titanium alloy article, substantially as herein described with reference to and as illustrated by the accompanying drawings.

Documents:

3003-del-1997-abstract.pdf

3003-del-1997-claims.pdf

3003-DEL-1997-Correspondence Others-(19-10-2011).pdf

3003-DEL-1997-Correspondence Others-(23-03-2011).pdf

3003-del-1997-correspondence-others.pdf

3003-del-1997-correspondence-po.pdf

3003-del-1997-description (complete).pdf

3003-del-1997-drawings.pdf

3003-del-1997-form-1.pdf

3003-del-1997-form-19.pdf

3003-del-1997-form-2.pdf

3003-DEL-1997-Form-27-(23-03-2011).pdf

3003-del-1997-form-3.pdf

3003-del-1997-form-4.pdf

3003-DEL-1997-GPA-(19-10-2011).pdf

3003-del-1997-gpa.pdf

3003-del-1997-pct-210.pdf

3003-del-1997-pct-409.pdf

3003-del-1997-pct-416.pdf

3003-del-1997-petition-137.pdf

3003-del-1997-petition-other.pdf