Title of Invention

POWDER COATING COMPOSITIONS

Abstract A powder coating composition in which powder particles are an agglomerate of individual particulate components fused or bonded together into composite particles having a particle size distribution up to a maximum of 1201lIn and a Dv.50 in the range of from 15 to 75~m, wherein the individual particulate components comprise (1) one or more co loured film-forming base components having a Dv.99 of no more than 30~m, and (2) one or more uncoloured film-forming components, wherein at least one component (2a) (i) has a Dv.99 that is more than 201lIn and (ii) has a higher DV.99 or higher Dv.50 than component (1) or, when there is more than one coloured component, than those components taken together, the ratio of co loured film-forming base component(s) to uncoloured film- forming component(s) in the composition being in the range of from 1 :99 to 60:40 by weight.
Full Text

POWER COATING COMPOSITIONS
FIELD OF THE INVENTION
This invention relatesto powder coating compositions and to their use.
Powder coating compositions generally comprise a solid film-forming resin, usually with one or more colouring agents such as pigments, and optionally they also contain one or more performance additives. They are usually thermosetting,-incorporating, for example, a film-forming polymer and a corresponding curing agent (which may itself be another film-forming polymer).
The compositions are generally prepared by intimately mixing the ingredients (including any colouring agents and performance additives) for example in an extruder, at a temperature above the softening point of the film-forming polymer(s) but below a temperature at which significant pre-reaction would occur. The extrudate is usually rolled into a flat sheet and comminuted, for example by grinding to the desired particle sizes ("micronising"). The size distribution required for most commercial electrostatic spray apparatus is up to 120 microns, often between 10 and 120 microns, with a Dv.50 within the range of 15 to 75 microns, preferably 25 to 50 microns, or more especially 20 to 45 microns.
BACKGROUND TO THE INVENTION
Currently, powder coating manufacturing methods allow the manufacturer to offer commercially a range of full gloss coatings in a variety of colours. The range of products available in reduced-gloss finishes is, however, limited.

Reduction of gloss to some other lower level, for example satin gloss (55-65% gloss) or matt ( There is accordingly a need for powder coating compositions in a wide range of reduced-gloss finishes, which avoid the problems mentioned above.

Speed of deliver/ to customers is also an important consideration, but the conventional powder coatings manufacturing method relies on premixing, extrusion and milling as separate processes, causing turnaround times to be long, and production of small batches of a product is again not economic. Stocking large product ranges solves the problem of speed of delivery, but is a highly inflexible approach and is not cost-effective.
EP 372860 A describes a colour mixing process for powder coatings in which sufficiently small-sized particles ( An extension of this agglomeration technique for the flexible production of a range of coloured powder coatings with a range of different reduced-gloss and other aesthetic effects is described in EP 539385 A.
Gloss reduction is achieved, for example, by adding uncoloured incompatible particles of mean particle size
film-forming component. Amounts of the gloss-reducing agent are. for example. 5 or 10% by weight, although amounts up to 40% by weight are also disclosed.
SUMMARY OF THE INVENTION
The present invention provides a powder coating composition in which powder particles are an agglomerate of individual particulate components fused or bonded together into composite particles, wherein the individual particulate components comprise
(1) one or more coloured film-forming base components having a Dv.99 of no more than 30µm, and
(2) one or more uncoloured film-farming components, wherein at least one component (2a)
(i) has a Dv.99 that is more than 20µm and
(ii) has a higher Dv.99 or higher Dv.50 than component (1) or, when there is
more than one such component, than those components taken together, the ratio of coloured film-forming base component(s) to uncolourgti film-forming component(s) in the composition being in the range of from 1:99 to 60:40 by weight.
As will be understood in the art, the volume percentiles Dv.x indicate for a stated particle size (D) the percentage (x) of the total volume of the particles that lies below the stated particle size; the percentage (100-x) of the total volume lies at or above the stated size. Thus, for instance, Dv,50 is the median particle size of the sample, and on a particle size distribution graph Dv.99 is the point on the curve read along the particle size axis where the area under the curve below this particle size represents 99% by volume of the particles. Thus. Dv.99 = 30µm indicates that 99% of the particles are below 30µm (but are not below 29µm), (For the avoidance of doubt, it

should be noted that all particle sizes quoted herein are by volume.) Volume percentiles are measurable by laser diffraction techniques, for example by the Malvern Mastersizer.
Surprisingly, even with a high proportion of uncoloured component of significantly larger particle size than the coloured base components (whether judged according to Dv.99 or according to Dv.50), nevertheless the particles of the larger-sized component are not visible to the naked eye, so that the composition gives the appearance of a single colour.
A coloured base component comprises colouring material and film-forming polymer. Thus, for example, it may be constituted as a powder coating composition in its own right, containing the usual powder coating additives, but having the specified (reduced) particle size. Usually there will be at least two coloured base components in the composition, each having a Dv.99 of no more than 30µm.
An uncoloured film-forming component is usually also a powder coating composition in its own right, but having the specified particle size; there should be at least one uncoloured film-forming component having a higher Dv.99 and/or a higher Dv.50 than a coloured film-forming base component (Usually, ancomponent having a higher Dv.99 than another will also have a higher Dv.50 and vice-versa) Usually, there are two or more coloured film-forming base components each having a Dv.99 of no more than 30µm and at least one uncoloured film-forming component having a Dv.99 that is more than 20|im and that is higher than the Dv.99 of the coloured film-forming base components taken together (or having a Dv.99 >20µm and a Dv.50 that is higher than the Dv.50 of the coloured film-forming base components taken together). Very often that uncoloured film-forming component will have a higher Dv.99 (or a higher Dv.50) than each coloured film-forming base component. Preferably the uncoloured film-forming component has a Dv.99 of at least 40µmt for example at least 50µm, or

more than 55µm, e.g. in the range of from 50 to 65µm, Preferably it will have a Dv.90 of no more than 75µm and advantageously will have a Dv.50 of at least 8µm, especially in the range of from 12 to 30µm. Such uncoloured film-forming components have the advantage of lower manufacturing cost in relation to the small-sized coloured components and their use allows easy adjustment of the polymer/ pigment ratio in the composition.
The present invention also provides a kit comprising the following separate components for agglomerating into powder coating compositions for the preparation of powder coatings in a number of different finishes:
• a plurality of coloured film-forming base components, each with a Dv.99 of no more than 30µm? and
• one or more uncoloured film-forming components, at least one having a higher Dv.99 or Dv.50 than each of the coloured film-forming components, and a Dv.99 that is more than 20µm, preferably more than 40µm and preferably no more than 90µm.
Such kits allow a rapid and flexible manufacture of a range of coloured powder coating compositions, reduced-gloss finishes being manufactured by the use of an uncoloured component that is incompatible with the coloured base component or that becomes incompatible therewith during film-formation.
The present invention also provides a powder coating composition comprising a non-agglomerated mixture of the individual particulate components specified above in the specified proportions.

DETAILED DESCRIPTION OF THE INVENTION AND DESCRIPTION OF
PREFERRED EMBODIMENTS
The individual particulate components may comprise, for example, (1) one or more, usually two or more, coloured film-forming base components each
having a Dv.99 of no more than 30µm, in an amount of from 1 to 60% by weight
of the total film-forming components, and (2)(a) one or more uncoloured film-forming components each having a Dv.99 of more
than 20µm and each having a higher Dv.99 (or a higher Dv.50) than the
coloured film-forming base component (1) or, when there is more than one such
component, than those components taken together, in an amount of from 10 to
99% by weight of the total film-forming components,
and, if desired, (b) one or more other uncoloured film-forming components, in an amount of up to
30% by weight of the total film-forming components,
Where there is one uncoloured film-forming component (2a) this preferably has a Dv.99 of up to 90µm, and where there are two or more uncolotyed.film-forming components (2a) preferably at least one, and often all, such components have a Dv,99 of up to 90|im.
More especially, the present invention provides a powder coating composition, suitable for providing a coating having certain appearance or performance attributes, which comprises composite particles formed by the agglomeration of individual particulate components fused or bonded together into composite particles such that the composite particles are air-fluidisable and can be applied to a substrate by electrostatic spray without causing the individual particles in the composite particles to break down

under the mechanical and/or electrostatic forces associated with their application to a
substrate, wherein the individual particulate components comprise
(1) one or more, usually two or more, coloured film-forming base components each
having a Dv.99 of no more than 30µm and (2)(a) one or more uncoloured film-forming components each having a Dv,99 of more than 20µm and each having a higher Dv.99 or Dv.50 than the coloured film-forming base component (1) or, when there is more than one such component, than those components taken together, and, if desired,
(b) one or more other uncoloured film-forming components, the ratio of coloured film-forming base component(s) to uncoloured film-forming component(s) in the composition being in the range of from 1:99 to 60:40 by weight, each particle of each film-forming component comprising a solid polymeric binder system at least a portion of which is a film-forming resin, the resin in the composition being in an amount sufficient to impart film-forming properties to the composition.
Ratios of coloured film-forming component(s) to uncoloured film-forming component(s) in the composition of from 1:99, e.g. from 2:98, preferably from 5:95, and up to 60:40, e.g. no more than 50:50, advantageously no more than 40:60 and preferably no more than 30:70, should especially be mentioned.
Advantageously, the minimum weight of uncoloured film-forming component(s) (2a) corresponds to a ratio of coloured film-forming base component(s) (1) to uncoloured film-forming component(s) (2a) of 5:2. Preferably the weight of uncoloured film-forming component(s) (2a) is at least that of coloured film-forming component(s) (1) and, preferably, the weight of uncoloured film-forming component(s) (2a) is at least that of other uncoloured film-forming component(s). Preferably the weight of

uncoloured film-forming component(s) (2a) is at least that of other film-forming component(s) (1) and (2b) together.
In one embodiment, the uncoloured film-forming component(s) (2a) have a Dv.99 of more than 2Q\im and up to 40jimf the ratio of coloured film-forming base component(s) to uncoloured film-forming component(s) in the composition being in the range of from 1:99 to 30:70, for example from 2:98 to 30:70, by weight.
In another embodiment, the uncoloured film-forming component(s) have a Dv.99 of more than 40^m and preferably no more than 90|^m, the ratio of coloured film-forming base component(s) to uncoloured film-forming component(s) in the ' composition being in the range of from 1:99 to 60:40, for example from 2:98 to 30:70, by weight.
Thus, the coloured film-forming base component(s) (1) may be, for example, at
least 2%, for example at least 5%, and, for example, no more than 50%,
advantageously no more than 40% and preferably no more than 30%, by weight of the
total film-forming components. A content of coloured film-forming base component(s)
of no more than 20%, for example from 10 to 20%, by weight of the total film-forming
components should especially be mentioned. r :-
The uncoloured film-forming component(s) (2) may be, for example, at least 10%, preferably at least 20%, more preferably at least 30%, especially at least 40%, more especially at least 50%, advantageously at least 60%, for example at least 70%, and, for example, up to 95%, by weight of the total film-forming components. A content of uncoloured film-forming component(s) of up to 90%, for example from 80 to 90%, by weight of the total film-forming components should be mentioned.
The uncoloured film-forming component(s) (2a) may be, for example, at least 10%, preferably at least 20%, more preferably at least 30%. especially at least 40%,

more especially at least 50%, advantageously at least 60%, for example at least 70%, and for example up to 95%, by weight of the total film-forming components.
Where the composition also includes, as particulate component in the agglomerate, a further uncoioured film-forming component (component (2b))t there may, for example, be no more than 30% by weight, calculated on all of the film-forming components together, of component(s) (2b) having (i) a Dv.99 that is In comparison with agglomerated coloured powder coating compositions described in EP 372860 A and EP 539385 A, compositions of the present invention contain a high proportion of uncoioured film-forming component, and the individual coloured components necessarily contain a significantly higher content of pigment. Moreover, the particle size of the uncoioured particles in component(s) (2a)can be significantly larger than those of the coloured base component(s), yithout, surprisingly, affecting visual homogeneity. Thus, contrary to expectation and contrary to the suggestions in EP 372860 A and EP 539385 A, powders containing significant quantities of uncoioured component(s) having, for example, a Dv,99 >40^im can be used to produce powder coating films in which the differences between the coloured particles and the uncoioured particles are not discemable by the unaided human eye. Maximising the level of larger-sized uncoioured component(s) will give cost advantages.
If desired, the composition may include as particulate component in the agglomerate as well as coloured film-forming base component(s) (1) and uncoioured

film-forming component(s) (2a) and optionally (2b), one or more non-film-forming components, e.g. a texturing agent, a metallic or mica pigment, or a non-fiinvforming performance component. If desired, a non-film-forming component may be pre-mixed with a film-forming component, e.g. with an uncoloured film-forming component, to form a masterbatch before mixing with the remaining components and then agglomerating. Alternatively, for example, a non-film-forming additive may be mixed with an uncoloured film-forming composition in an extruder and then micronised, to give an uncoloured film-forming component (2a) or (2b), depending on particle size, that also contains the desired aesthetic or performance additive.
A film-forming particulate component for inclusion in the agglomerate may itself be in the form of an agglomerate. Usually such a component would be formed by agglomeration of an uncoloured film-forming component with a non-film-forming component, for example a texturing additive or metallic or mica pigment.
Each film-forming component of the composition comprises at least one solid film-forming resin and includes any curing agent required therefor, and is usually formed by an extrusion process and comminution to the requisite particle size. Where a film-forming component is coloured, the colouring agent or agente (pigments and/or dyes) is (are) generally extruded with the film-forming resin(s), plus any curing agent, so that particles formed therefrom comprise film-forming resin, colouring agent and, where applicable, curing agent.
Reduction of gloss, for example to satin gloss (55-65% gloss) or matt (
present. For example, there may be an uncoloured film-forming component having a different functionality from the coloured film-forming base component(s) and optionally also containing a different catalyst (both of which lead to different gel times). For example, coloured and uncoloured components may be based on polyesters of different functionality. For polyurethane systems using hydroxy-functional polyesters cured with an isocyanate (typically isopherone diisocyanate)t hydroxy-functional polyesters with radically different functionality may be used, e.g. a hydroxy-functional polyester with a functionality of 7 for an uncoloured component and one with a functionality of 2 used for the coloured base component(s). Another possibility is to employ polymeric materials that are perse incompatible with each other, for example a polyester and an acrylic polymer.
In contrast to conventional prior art gloss-reduction processes, which generally use 50:50 non-fused mixtures of same-sized powders, with fused or bonded compositions of the present invention good gloss reduction can be achieved with substantially different proportions of gloss-reducing additive. The agglomerated material also does not suffer from particle segregation in the solid state as would dry-blended product, thus giving uniformity of product even after transportation and spraying.
Thus, uncoloured components can be used for extension of product ranges, to give different finishes. Also, by using different chemistries, they may be used to give different performance characteristics. The different chemistries may arise, for example, from the use of different film-forming polymers, e.g. polyester and acrylic or polyester and epoxy, but may also arise from the use of different curing agents, e.g. polyester with an epoxy curing agent in one component and polyester with a bis(beta-hydroxyalkylamide) curing agent such as PRIMID in another component.
In addition, or alternatively, an uncoloured film-forming component of the composition of the present invention may be compatible with the coloured film-forming

base component(s). Usually all the coloured film-forming base components are compatible with one another.
An uncoioured film-forming component of a kit of the invention may be a pre-prepared uncoioured coating composition of the specified particle size or one of conventional size which is reduced in size just prior to use. Advantageously, for any particular type of film-forming chemistry (e.g. acid-functional polyester, hydroxy-functional polyester), a kit of the invention includes a "universal" gloss-reducing component suitable for all powder coating compositions of that chemistry. The present invention has the advantage of reducing costs while also reducing stocking levels and manufacturing capacity. It enables a very rapid and flexible service to be provided cheaply to the customer, allowing for the possibility of providing small quantities of powder coating compositions economically on request.
Advantageously, the coloured film-forming base components taken together contain at least 5%, e.g. at least 10%, and generally no more than 70% or 75%, e.g. no more than 60%, for example 20 to 40%, by weight of pigment, calculated on the total weight of these components. Advantageously, each contains at least 8% by weight of pigment, calculated on the weight of that component. The numben-ef-coloured film-forming base components in a kit may be, for example, at least 7, e.g. in the range of from 7 to 30,
Examples of pigments which may be used in the coloured base components are inorganic pigments, such as, for example, titanium dioxide white, red and yellow iron oxides, chrome pigments and carbon black, and organic pigments such as, for example, phthaiocyanine, azo, anthraquinone, thioindigo, isodibenzanthrone, triphendioxane and quinacridone pigments, vat dye pigments and lakes of acid, basic and mordant dyestuffs. Dyes may be used instead of or as well as pigments. Each coloured base component of the coating composition may contain a single colorant

(pigment or dye) or may contain more than one colorant. Where appropriate, a filler may be used to assist opacity, whilst minimising costs.
Additional pigment may alternatively be added as a separate component prior to agglomerating, especially if the pigment is close in colour to the mixed coloured film-forming base components. Any pigment added in this way would generally be no more than 3%, preferably up to 1%, by weight, based on the weight of the total composition, although amounts up to 5% may also be possible. Thus, for example, pigment in an amount of no more than 3% by weight, more especially up to 1% by weight, may be used to displace the colour of the components over a small colour region, this being used for colour tinting or colour correction of a batch.
Preferably, the total weight of pigment in the composition is at least 0.5%, more especially at least 5%, and preferably no more than 30%, although an amount up to 50% is potentially also possible.
One or more other separate components (3) may also be present. Other optional components include, for example, performance and aesthetic additives mentioned in EP 539385 A. Those components may, if desired, be pre-mixed with another component, for example an uncoloured film-forming competent, with the components remaining as distinct components, e.g. (2a) and (3), before final agglomeration. Alternatively, the additives may be combined in a masterbatch with uncoloured film-forming polymer, often itself constituted as a powder coating composition in its own right, the masterbatch being prepared, for example, by co-extrusion of polymer and additive, followed by comminution, or by agglomeration of the particulate additive with uncoloured film-forming powder, to form uncoloured film-forming component (2a) or (2b), often (2a). Such further aesthetics additives may be present for example in an amount of from 0,5 to 50% by weight of the total composition- A non-film-forming performance additive is generally present in an amount of no more than 5% by weight of the composition, e.g. in an amount of from 0.5

to 5% by weight. Where other component(s) are present in a composition of the present invention, the percentages of the specified coloured film-forming base component(s) and/or the specified uncoloured film-forming component(s) in the composition may be altered accordingly, but the ratio of coloured film-forming base component(s) to uncoloured film-forming component(s) will generally remain the same.
A composition of the present invention may contain, for example, at least 1%, e.g. at least 2%, often at least 5%, by weight of the specified coloured film-forming base component(s). Often the composition will contain at least 20%, e.g. at least 30% or at least 40%, by weight of the uncoloured film-forming component (2a) of the size specified above. Preferably, the content of uncoloured film-forming component(s) in the composition is at least 40%, e.g. at least 50%, and advantageously at least 60%, and preferably at least 70%, by weight. Amounts of at least 40% e.g. at least 50%, and advantageously at least 60%, and preferably at least 70%, by weight of uncoloured film-forming component(s) (2a) of the size specified above should especially be mentioned.
Ratios of from 1:99, e.g. from 2:98, preferably from 5:95, and up to 60:40, e.g. up to 50:50, advantageously up to 40:60 and preferably up to 30:7Qr for the ratio of coloured film-forming base component(s) (1) to uncoloured film-forming component(s) of the specified size (2a) should especially be mentioned.
Preferably, in each of the coloured film-forming base components all the component particles are
least 2(im, for example within the range of for example 2 to 8pm, preferably 2 to 6pm or 8 to 12pm; Dv.50 values >2pm and A coloured film-forming base component of a kit of the invention may, however, be of larger particle size and then reduced in size just prior to use. Accordingly, the present invention also provides a kit comprising the following separate components for agglomerating into powder coating compositions for the preparation of powder coatings in a number of different colours:
• at least 7 differently coloured film-forming base components,
• an uncoloured film-forming component that is compatible with the coloured film-forming base components and remains compatible therewith during film-formation and that has a Dv.99 of more than 40^m and preferably of no more than 90|am, and
• an uncoloured film-forming component that is incompatible with the coloured film-forming base components or that becomes incompatible therewith during film-formation and that has a Dv.99 of more than 40^m and preferably of no more than 90*im.
In one embodiment of the present invention, the individual particulate
components of the powder coating composition comprise *
• two or more coloured film-forming base components having a Dv.99 of no more than 30nm, and
• one or more uncoloured film-forming components, at least one component having a higher Dv.99 or higher Dv.50 than at least one, preferably ail, of the coloured film-forming base component(s), and having a Dv.99 of more than 2(fym and preferably no more than 90^m,
the ratio of coloured film-forming base components to uncoloured film-forming component(s) of the specified size being in the range of from 1:99 to 30:70 by weight.

In a further embodiment of the present invention, the individual particulate components of the powder coating composition comprise
* two or more coloured film-forming base components having a Dv.99 of no
more than 30^m, and
• one or more uncoloured film-forming components, at least one component
having a Dv.99 of more than 40|am and preferably no more than 90fxm,
the ratio of coloured film-forming base components to uncoloured film-forming
component(s) of the specified size being in the range of from 1:99 to 60:40 by
weight.
Preferably, the uncoloured film-forming component (2a) or at least onef and advantageously each, of the uncoloured film-forming components (2a) has a Dv.99 of at least 30^m, more especially at least 35nm, and advantageously at least 40^m. An uncoloured film-forming component having a Dv,50 of at least 8(im and up to 35fxm, e.g. up to 30|im( and/or having a Dv.90 of at least 14fim should especially be mentioned. An uncoloured film-forming component (2a) having a Dv.50 of at least 10jim and up to 35nm, e.g. in the range of from 12 to 30nm, and/or having a Dv.90 of at least 18jxm and one having a Dv.90 of no more than 75fim shoufd also especially be mentioned.
Uncoloured component(s) (2a) may, for example, have a Dv.99 or a Dv.50 that is at least twice, e.g. at least three times, the Dv.99 or Dv.50 figure of the coloured component(s) (1) taken together. For example, the Dv.99 of component(s) (2a) may be at least 20^m, e.g. at least 30^m, more than that of component or components (1) taken together.
A powder coating composition of the invention will in general be a thermosetting system, although thermoplastic systems (based, for example, on polyamides) can in principle be used instead.

When a thermosetting resin is used, the solid polymeric binder system generally includes a solid curing agent for the thermosetting resin; alternatively two co-reactive film-forming thermosetting resins may be used. Thus, a thermosetting powder coating composition according to the invention may contain one or more film-forming polymers selected from carboxy-functional polyester resins, hydroxy-functional polyester resins, epoxy resins, and functional acrylic resins. Carboxy-functional polyester resins should especially be mentioned.
A carboxy-functional polyester film-forming resin may be used, for example, with a polyepoxide curing agent. Such carboxy-functional polyester systems are currently the most widely used powder coatings materials. The polyester generally has an acid value in the range 10-100, a number average molecular weight Mn of 1f500 to 10,000 and a glass transition temperature Tg of from 30°C to 85°Cf preferably at least 40°C. The poly-epoxide can, for example, be a low molecular weight epoxy compound such as triglycidyl isocyanurate (TGIC), a compound such as diglycidyl terephthalate condensed glycidyl ether of bisphenol A or a light-stable epoxy resin. Such a carboxy-functional polyester film-forming resin can alternatively be used with a bis(beta-hydroxyalkylamide) curing agent such as tetrakis(2-hydroxyethyl) ydipamide.
Alternatively, a hydroxy-functional polyester can be used with a blocked isocyanate-functional curing agent or an amine-formaldehyde condensate such as, for example, a melamine resin, a urea-formaldehye resin, or a glycol ural formaldehye resin, for example the material "Powderlink 1174" supplied by the Cyanamid Company, or hexahydroxymethyl melamine. A blocked isocyanate curing agent for a hydroxy-functional polyester may, for example, be internally blocked, such as the uret dione type, or may be of the caprolactam-blocked type, for example isopherone diisocyanate.
As a further possibility, an epoxy resin can be used with an amine-functional curing agent such as, for example, dicyandiamide. Instead of an amine-functional

curing agent for an epoxy resin, a phenolic material may be used, preferably a material formed by reaction of epichlorohydrin with an excess of bisphenol A (that is to say, a polyphenol made by adducting bisphenol A and an epoxy resin). A functional acrylic resin, for example a carboxy-, hydroxy- or epoxy-functional resin can be used with an appropriate curing agent.
Mixtures of film-forming polymers can be used; for example a carboxy-functional polyester can be used with a carboxy-functional acrylic resin and a curing agent such as a bis(beta-hydroxyalkylamide) which serves to cure both polymers. As further possibilities, for mixed binder systems, a carboxy-, hydroxy- or epoxy-functional acrylic resin may be used with an epoxy resin or a polyester resin (carboxy- or hydroxy-functional). Such resin combinations may be selected so as to be co-curing, for example a carboxy-functional acrylic resin co-cured with an epoxy resin, or a carboxy-functional polyester co-cured with a glycidyl-functional acrylic resin. More usually, however, such mixed binder systems are formulated so as to be cured with a single curing agent (for example, use of a blocked isocyanate to cure a hydroxy-functional acrylic resin and a hydroxy-functional polyester). Another preferred formulation involves the use of a different curing agent for each binder of a mixture of two polymeric binders (for example, an amine-cured epoxy resin used in conjunction with a blocked isocyanate-cured hydroxy-functional acrylic resin).
Other film-forming polymers which may be mentioned include functional fluoropolymers, functional fluorochloropolymers and functional fiuoroacrylic polymers, each of which may be hydroxy-functional or carboxy-functional, and may be used as the sole film-forming polymer or in conjunction with one or more functional acrylic, polyester and/or epoxy resins, with appropriate curing agents for the functional polymers.
Other curing agents which may be mentioned include epoxy phenol novolacs and epoxy cresol novolacs; isocyanate curing agents blocked with oximes, such as

isopherone diisocyanate blocked with methyl ethyl ketoxime, tetramethylene xylene diisocyanate blocked with acetone oxime, and Desmodur W (dicyclohexylmethane diisocyanate curing agent) blocked with methyl ethyl ketoxime; light-stable epoxy resins such as "Santolink LSE 120" supplied by Monsanto; and alicyclic poly-epoxides such as "EHPE-3150" supplied by DaiceL
The function of coatings is of course protective, but appearance is also important, and the film-forming resin and other ingredients are selected so as to provide the desired performance and appearance characteristics. In relation to performance, coatings should generally be durable and exhibit good weatherability, stain or dirt resistance, chemical or solvent resistance and/or corrosion resistance, as well as good mechanical properties, e,g. hardness, flexibility or resistance to mechanical impact; the precise characteristics required will depend on the intended use. The composition must, of course, be capable of forming a coherent film on the substrate, and good flow and levelling of the composition on the substrate are required. Accordingly, the powder coating composition generally also contains one or more performance additives such as, for example, a flow-promoting agent, a plasticiser, a stabiliser, for example a stabiliser against UV degradation, an antwjassing agent, such as benzoin, or a filler. Such additives are known and standard additives for use in powder coating compositions. Usually, these performance additives will be incorporated in any film-forming component before and/or during the extrusion or other homogenisation process, although, if appropriate, any such additive may alternatively be incorporated as a separate component in the agglomeration process.
Mixing and agglomeration methods are described in EP 372860 A and EP 539385 A.
The agglomerate may, for example, be prepared by mechanofusion of a mixture of the individual components, for example by mechanofusion at a temperature in the range of from 60 to 80*C, or by granulation using methanol or other suitable solvent as

granulating agent, to produce composite particles that constitute a free-flowing and fluidisable powder.
Good fluidity of the powder is required for purposes of application to the substrate. This fluidity of powders is governed by their particle size, and particle size also controls the application efficiency of a powder; powders with small particles, i.e. significant quantities The present invention also provides a process for the preparation of a powder coating composition of the present invention, which comprises providing, in the -specified proportions, the specified one or more coloured film-forming base components and the one or more specified uncoloured film-forming components, and if desired one or more other uncoloured film-forming components and/or one or more non-film-forming components, and mixing and agglomerating the components such that the composition is air^fluidisable and can be applied to a substrate by electrostatic spray.
Agglomeration prevents segregation of the constituents during application and handling, which otherwise would occur, for example during the application process itself (because of differential electrostatic charging) or in the attendant recovery and recycling process (because of differences in particle size and/or particle density) or in transport, causing batch-to-batch variability in the resulting coating.
The composite particles produced may be likened to raspberries with the individual particles of the raspberry (the drupels) bonded to one another, although the "drupels" are of different sizes, and there will of course also be "raspberries" of different composition and different sizes in the powder as a whole. Inspection of a fused agglomerated powder under an electron microscope shows that one particle is bonded to another and that the individual particles in the composites are more rounded than prior to agglomeration. When a conventional powder coating composition is inspected

under an electron microscope, however, the powder particles are seen to be sharp-edged or angular, and are seen as separate, distinct particles - they are not fused to one another.
Furthermore, unlike conventional uniformly coloured powder coating compositions, that contain particles of only a single colour (produced by fusion in the melt extruder), powder coating compositions of this invention consist of a mixture of differently coloured particles and uncoloured particles but nevertheless give the appearance of a single colour on application to a substrate.
An agglomerated powder coating composition according to the invention may in principle be applied to a substrate by any suitable process of powder coating technology, for example by electrostatic spray coating, or by fluidised-bed or electrostatic fluidised-bed processes.
After application of the powder coating composition to a substrate, conversion of the resulting adherent particles into a continuous coating (including, where appropriate, curing of the applied composition) may be effected by heat treatment and/or by radiant energy, notably infra-red, ultra-violet or electron beam radiation.
The powder is usually cured on the substrate by the application of heat (the
9
process of stoving), usually for a period of from 5 to 30 minutes and usually at a temperature in the range of from 150 to 220°C, although temperatures down to 90°C may be used for some resins, especially epoxy resins; the powder particles melt and flow and a film is formed. The curing times and temperatures are interdependent in accordance with the composition formulation that is used, and the following typical ranges may be mentioned:

Temperature/°C Time
280 to 100* 10sto40min
250 to 150 15sto30min
220 to 160 5minto20min
Temperature down to 90°C may be used for some resins, especially certain
epoxy resins.
The invention also provides a process for forming a coating on a substrate, which comprises applying an agglomerated composition according to the invention to a substrate, for example by an electrostatic spray coating process, and heating the applied composition to melt and fuse the particles and where appropriate cure the coating.
The film may be any suitable thickness. For decorative finishes, film
thicknesses as low as 20 microns should be mentioned, but it is more usual for the film
thickness to fall within the range 25-120 microns, with common ranges being 30-80
microns for some applications, and 60-120 microns or, more preferably, 60-100
microns for other applications, while film thicknesses of 80-150 microns are less
common, but not rare. ^ ",
The substrate may comprise a metal, a heat-stable plastics material, wood, glass, or a ceramic or textile material. Advantageously, a metal substrate is chemically or mechanically cleaned prior to application of the composition, and is preferably subjected to chemical pre-treatment, for example with iron phosphate, zinc phosphate or chromate. Substrates other than metallic are in general preheated prior to application or, in the case of electrostatic spray application, are pretreated with a material that will aid such application.

Accordingly, the present invention provides a powder coating composition in which powder particles are an agglomerate of individual particulate components fused or bonded together into composite particles having a particle size distribution up to a maximum of 120|am and a Dv.50 in the range of from 15 to 75(im, wherein the individual particulate components comprise (1) one or more coloured film-forming base components having a Dv,99 of no more than 30jim, and (2) one or more uncoloured film-forming components, wherein at least one component (2a) (i) has a Dv.99 that is more than 20jam and (ii) has a higher Dv.99 or higher Dv,50 than component (1) or, when there is more than one coloured component, than those components taken together, the ratio of coloured film-forming base component(s) to uncoloured film-forming component(s) in the composition being in the range of from 1:99 to 60:40 by weight.

The following Examples illustrate the invention. In each case the particle sizes were measured on the Malvern Mastersizer X laser iight-scattering device from Malvern Instruments,
EXAMPLES
Preparation of Individual Components
White, black and red coloured film-forming base components and different uncoloured film-forming components were prepared by mixing the following formulations.
Component A - White Powder Coating Composition
Rutile titanium dioxide white pigment 600 g
Carboxylic acid-functional polyester resin 360 g
Bis(beta-hydroxyalkyiamide) curing agent 13 g
Benzoin degassing agent 4 g
Flow modifiers 18 g
Surface waxes 5 g
Component B - Black Powder Coating Composition
Carbon Black pigment 175 g
Carboxylic acid-functionai polyester resin 772 g
Bis(beta-hydroxyalkylamide) curing agent 27 g
Benzoin degassing agent 4 g

Flow modifiers 18 g
Surface waxes 4 g
Component C - Red Powder Coating Composition
Earth Red iron oxide pigment 125 g
Carboxylic acid-functional polyester resin 650 g
Bis(beta-hydroxyalkylamide) curing agent 24 g
Benzoin degassing agent 2 g
Flow modifiers 18 g
Surface waxes 4 g
Fillers (barytes) 177 g
For the coloured components A to C the ingredients were dry mixed and fed to an extruder blender operating at a temperature of 100°C. The extruder produced a sheet of pigmented resin which was ground to a particle size of below 100 fim and milled on a 100 AFG jet-mill (manufacturer Hosakawa Micron) at 6 gargrinding air pressure and classified at a speed of 7000 rpm.
The particle size distribution for Components A, B and C was: Dv.50 = 3.5|im Dv.90 = 5.9nm
Dv.99 = 8.2^im The polyester of Components A to C had an acid value of 18 to 30.

Component D - Uncoloured Powder Coating Composition
Carboxylic acid-functional polyester resin 650 g
Bis(beta-hydroxyalkylamide) curing agent 24 g
Benzoin degassing agent 2 g
Flow modifiers 18 g
Surface waxes 4 g
Fillers (barytes) 302 g
Component E - Uncoloured Powder Coating Composition for gloss-reduction
Carboxylic acid-functional polyester resin 575 g
Fillers (barytes) 333 g
Benzoin degassing agent 4 g
Surface waxes 4 g
Flow modifiers 18 g
Bis(beta-hydroxyaikylamide) curing agent 65 g
For uncoloured components D and E the procedure for components A to C was repeated except that the jet-milling was carried out at 3000 rpm. The particle size distribution for components D and E is: Dv.50 = 18.4jxm Dv.90 = 36.2nm Dv.99 = 51.0(im The polyester of Component D had an acid value of 18 to 30 and the polyester of Component^ had an acid value of 40 to 90.

Component F - Uncoioured Powder Coating Composition for Texturing
Carboxylic acid-functional polyester resin 780 g
Texturing agent: (PTFE wax, silicone wax, cellulose
acetyl butyrate, ester modified polyether 220 g
The ingredients were dry mixed and fed to an extruder blender operating at a temperature of 100°C. This was ground to a powder in an air classified impact mill. The particle size distribution for component F is
Dv.50 = 36nm
Dv.90 = 82^m
Dv.99 = 118^im The polyester of Component F had an acid value of 18 to 30,
Component G - Uncoioured Powder Coating Composition for Pearlescent Effects
Component E 800 g
Mica Pigment (e.g. Iriodin 911 i supplied
by Merck Ltd., Poole, Dorset, England) 200 g
The ingredients were blended together in a Henschel FM10 mixer for 30 minutes in total, taking the temperature to 54°C. The agglomerated powder was sieved through a 110|im steel mesh.
The particle size distribution for component G is Dv.50 = 13fim

Dv.90 = 24fim Dv.99 = 38^im
Components H and I
Components A and B were prepared as before but milled on a 100 AFG jet-mill at 6 Bar grinding air pressure and classified at a speed of 12000rpm. These components were re-labelled Components H and I respectively.
The particle size distribution for Components H and I were: Dv.50 = 2.6nm Dv.90 = 5.3nm Dv.99 = 6.4nm
Component J - Uncoloured Powder Coating composition for Tribo Application
Carboxylic acid-functional polyester resin 875 g
Bis-(beta-hydroxyalkylamide) curing agent 50 g
Benzoin degassing agent 2 g
Flow modifier 26 g
Tribostatic additives 47 g
The ingredients were dry mixed and fed to an extruder blender operating at a temperature of 100°C. The extruder produced a sheet of uncoloured resin which was ground to a particle size of below 100 (im and milled on a 100 AFG jet-mill (manufacturer Hosakawa Micron) at 6 Bar grinding air pressure and classified at a speed of 6500 rpm.

The particle size distribution for Component J is Dv.50 = 5.3nm Dv.90 = 8.2fim Dv.99 = 9.4jim
The polyester of component J had an acid value of 18 to 30.
Component K - Uncoloured Powder Coating Composition fFolvester/Epoxv)
Carboxylic acid-functional polyester resin 440 g
Glycidyl-functional Bisphenol-A epoxy resin
(type II or type III epoxy) 290 g
Benzoin degassing agent 2 g
Flow modifiers 18 g
Fillers (barytes) 250 g
The ingredients were dry mixed and fed to an extruder blender operating at a temperature of 100°C. This was ground to a powder in an air classified impact mill. The particle size distribution for component K is
Dv.50 = 28^m
Dv.90 = 58|im
Dv,99 ~ 72^m The polyester of Component K had an acid value of 18 to 30.

Preparation and Use of Agglomerated Powder Coating Compositions Example 1
A mixture comprising;
Component A 187,5 g
Components 16,7 g
Component C 100.0 g
Component D 695.8 g
was blended together in a Henschel FM10 mixture for 30 minutes in total, with a water jacket taking the temperature to 54°C. The agglomerated powder was sieved through a 110^m steel mesh and then electrostatically applied through a Gema PCG-1 corona spray gun onto an aluminium Q panel. This was then stoved at the recommended time and temperature.
A smooth, glossy coating that had a homogeneous dusky pink colour was
produced.
Example 2
A mixture comprising
Component A 187,5 g
Components 16.7 g
Component C 100.0 g
Component D 545.8 g
Component E 150.0 g
was agglomerated and applied to a substrate and stoved as in Example 1.

As shown by their acid numbers, the polyester of Component E has a different functionality and hence different gel time from components A to D, and a smooth, matt coating of 30% gloss at 60° angle is produced that has a homogeneous dusky pink colour.
Example 3
A mixture comprising
Component A 65 g
Component B 75 g
Component C 80 g
Component D 760 g
Component F 20 g
was blended together in a Henschel mixer for 30 minutes in total, taking the temperature to 54°C. The agglomerated powder was sieved through a 110fxm steel mesh and then electrostatically applied through a Gema PCG-1 corona spray gun onto an aluminium Q Panel. This was then stoved at the recommende A textured, glossy coating that had a homogeneous dark brown colour was produced.
Example 4
A mixture comprising
Component A 250 g Component B 125 g

Component D 475 g
Component G 150 g
was blended together in a Henschel mixer for 30 minutes in total, taking the temperature to 54°C. The agglomerated powder was sieved through a 110^m steel mesh and then electrostatically applied through a Gema PCG-1 corona spray gun onto an aluminium Q Panel. This was then stoved at the recommended time and temperature,
A smooth, matt coating that had a homogeneous grey colour and a pearlescent metallic effect was produced.
Example 5
A mixture comprising
Component H 40 g
Component I 120 g
Component D 670 g
Component E 70 g
Component J 100g
was blended together in a Henschel mixer for 30 minutes in total, taking the temperature to 54°C. The agglomerated powder was sieved through a 110^im steel mesh and then electrostatically applied by a tribostatic gun onto an aluminium Q Panel. This was then stoved at the recommended time and temperature.
A smooth, satin coating that had a homogeneous charcoal colour was produced.

Example 6
A mixture comprising;
Component A 187.5 g
Component B 16.7 g
Component C 100.0 g
Component K 695.8 g
was blended together in a Henschel FM10 mixture for 30 minutes in total, with a water jacket taking the temperature to 54°C, The agglomerated powder was sieved through a 110^m steel mesh and then electrostatically applied through a Gema PCG-1 corona spray gun onto an aluminium Q panel This was then stoved at the recommended time and temperature.
A smooth, glossy coating that had a homogeneous dusky pink colour was produced.






CLAIMS
1. A powder coating composition in which powder particles are an
agglomerate of individual particulate components fused or bonded together into
composite particles, wherein the individual particulate components comprise
(1) one or more coloured filrn-forming base components having a Dv.99 of no more than 30µm, and
(2) one or more uncoloured film-forming components, wherein at least one component (2a) (i) has a Dv.99 that is more than 20µm and (ii) has a higher Dv.99 or higher Dv,50 than component (1) or, when there is more than one coloured component, than those components taken together,
the ratio of coloured film-forming base component(s) to uncoloured film-forming component(s) in the composition being in the range of from 1:99 to 60:40 by weight.
2. A powder coating composition as claimed in claim 1, wherein the uncoloured film-forming component or components (2a) are present in an amount of at least 10% by weight of the total film-forming components, f "
3. A powder coating composition as claimed in claim 1 or claim 2, wherein there is no more than 30% by weight, calculated on the weight of the total film-forming components, of uncoloured film-forming component(s) having a Dv.99 (i) that is no higher than the Dv.99 of the coloured film-forming component or components taken together, and (ii) that is less than 20µm.

4. A powder coating composition in which powder particles are an
agglomerate of individual particulate components fused or bonded together into
composite particles, wherein the individual particulate components comprise
(1) one or more coloured film-forming base components each having a Dv.99 of no more than 30µm, in an amount of from 1 to 60% by weight of the total film-forming components, and
(2)(a) one or more uncoloured film-forming components each having a Dv.99 of more than 20µm and each having a higher Dv.99 and/or a higher Dv.50 than the coloured film-forming base component (1) or, when there is more than one such component than those components taken together, in an amount of from 10 to 99% by weight of the total film-forming components, and, if desired, (b) one or more other uncoloured film-forming components, in an amount of up to 30% by weight of the total film-forming components.
5. A powder coating composition as claimed in any one of claims 1 to 4, wherein there are two or more coloured film-forming base components (1).
6. A powder coating composition in which powder particles are an agglomerate of individual particulate components fused or bonded together into composite particles, wherein the individual particulate components comprise

(1) two or more coloured film-forming base components having a Dv.99 of no more than 30µm, and
(2) one or more uncoloured film-forming components, at least one component (2a) having a Dv.99 of more than 20|im and that is higher than the Dv.99 of

component (1) or, when there is more than one such component, of those
components taken together, the ratio of coloured film-forming base components (1) to uncoloured film-forming component(s) (2) in the composition being in the range of from 1:99 to 30:70 by weight
7. A powder coating composition as claimed in claim 6, wherein the uncoloured film-forming component or components (2a) are present in an amount of at least 10% by weight of the total film-forming components.
8. A powder coating composition as claimed in claim 6 or claim 7, wherein there is no more than 30% by weight, calculated on the weight of the total film-forming components, of uncoloured film-forming component(s) having a Dv.99 (i) that is no higher than the Dv.99 of the coloured film-forming component or components taken together, and (ii) that is less than 20nm,
9. A powder coating composition as claimed in any one of claims 1 to 8, wherein the uncoloured film-forming component or at least one of the-uncoloured film-forming components has a Dv.99 of at least 30µm.
10. A powder coating composition as claimed in claim 9, wherein the uncoloured film-forming component or at least one of the uncoloured film-forming components has a Dv.99 of at least 35µm.
11. A powder coating composition as claimed in claim 10, wherein the uncoloured film-forming component or at least one of the uncoloured filnvforming components has a Dv.99 of at least 40µm.

12. A powder coating composition in which powder particles are an
agglomerate of individual particulate components fused or bonded together into
composite particles, wherein the individual particulate components comprise
(1) two or more coloured film-forming base components having a Dv.99 of no more than 30fim, and
(2) one or more uncoloured film-forming components, at least one component (2a)
having a Dv.99 of more than 40µm,
the ratio of coloured film-forming base components to uncoloured film-forming component(s) in the composition being in the range of from 1:99 to 60:40 by weight.
13. A powder coating composition as claimed in claim 12, wherein the uncoloured film-forming component or components (2a) are present in an amount of at least 10% by weight of the total film-forming components.
14. A powder coating composition as claimed in claim 12 or claim 13, wherein there is no more than 30% by weight, calculated on the weight of the total film-forming components, of uncoloured film-forming component(s) having a Dv.99 (i) that is no higher than the Dv.99 of the coloured film-forming component or components taken together, and (ii) that is less than 20µm,
15. A powder coating composition as claimed in any one of claims 1 to 14, wherein the ratio of coloured film-forming base components (1) to uncoloured film-forming component(s) (2a) is in the range of from 1:99 to 50:50 by weight.

16. A powder coating composition as claimed in claim 15, wherein the ratio of coloured film-forming base components (1) to uncoloured film-forming component(s) (2a) is in the range of from 1:99 to 40:60 by weight.
17. A powder coating composition as claimed in claim 16f wherein the ratio of coloured film-forming base components (1) to uncoloured film-forming component(s) (2a) is in the range of from 1:99 to 30:70 by weight.
18. A powder coating composition as claimed in claim 17, wherein the ratio of coloured film-forming base components (1) to uncoloured film-forming component(s) (2a) is in the range of from 5:95 to 30:70.
19. A powder coating composition as claimed in any one of claims 1 to 18, wherein the uncoloured film-forming component or components (2) are present in an amount of at least 50% by weight of the total film-forming components.
20. A powder coating composition as claimed in claim 19, wherein the uncoloured film-forming component or components (2) are present in an amount of at least 60% by weight of the total film-forming components.
21. A powder coating composition as claimed in claim 20, wherein the uncoloured film-forming component or components (2) are present in an amount of at least 70% by weight of the total film-forming components.
22. A powder coating composition as claimed in any one of claims 2 to 21, wherein the uncoloured film-forming component or components (2a) are present in an amount of at least 20% by weight of the total film-forming components.

23. A powder coating composition as claimed in claim 22, wherein the uncoloured film-forming component or components (2a) are present in an amount of at least 30% by weight of the total film-forming components.
24. A powder coating composition as claimed in claim 23, wherein the uncoloured film-forming component or components (2a) are present in an amount of at least 40% by weight of the total film-forming components.
25. A powder coating composition as claimed in claim 24, wherein the uncoloured film-forming component or components (2a) are present in an amount of at least 50% by weight of the total film-forming components.
26. A powder coating composition as claimed in claim 25, wherein the uncoloured film-forming component or components (2a) are present in an amount of at least 60% by weight of the total film-forming components.
27. A powder coating composition as claimed in any one of claims 1 to 26, wherein there is no more than 15% by weight, calculated on the weight of total film-forming components, of uncoloured film-forming component(s) (2b).
28. A powder coating composition as claimed in any one of claims 1 to 27, wherein there are two or more compatible coloured film-forming base components (1).
29. A powder coating composition as claimed in any one of claims 1 to 28,
wherein the uncoloured film-forming component (2a) or at least one of the uncoloured

film-forming components listed under (2a) and (2b) is compatible with the coloured film-forming base components (1) during film-formation.
30. A powder coating composition as claimed in any one of claims 1 to 29, wherein the uncoloured film-forming component (2a) or at least one of the uncoloured film-forming components listed under (2a) and (2b) is incompatible with the coloured film-forming base component(s) (1) or becomes incompatible therewith during film-formation.
31. A powder coating composition as claimed in any one of claims 1 to 30t wherein the coloured film-forming base component(s) (1) contain a polyester.
32. A powder coating composition as claimed in claim 30 and claim 31, wherein the uncoloured film-forming component (2a) or at least one of the uncoloured film-forming components listed under (2a) and (2b) contains a polyester having a different functionality from the polyester of the coloured film-forming base component(s) (1),
33. A powder coating composition as claimed in claim 31 or claim 32, which includes an uncoloured film-forming component (2a) or (2b) containing a polyester, that component and the coloured film-forming base component(s) (1) containing different curing agents, one of those being an epoxy curing agent or a co-reactable epoxy resin.
34. A powder coating composition as claimed in any one of claims 1 to 33, which includes an uncoloured film-forming component (2a) or (2b) which is itself an agglomerate of an uncoloured film-forming component fused or bonded to form composite particles with a non-film-forming component.

35. A powder coating composition as claimed in any one of claims 1 to 34, wherein component (2a) or (2b) includes a texturing additive,
36. A powder coating composition as claimed in claim 34, wherein the agglomerated component (2a) or (2b) includes mica.
37. A powder coating composition as claimed in any one of claims 1 to 36, wherein the uncoloured film-forming component (2a) or at least one of the uncoloured film-forming components (2a) has a Dv.99 of no more than 90µm.
38. A powder coating composition as claimed in any one of claims 1 to 37, wherein the uncoloured film-forming component or at least one of the uncoloured film-forming components (2a) has a Dv.90 of at least 14pm.
39. A powder coating composition as claimed in claim 38, wherein the uncoloured film-forming component or at least one of the uncoloured- film-forming components (2a) has a Dv.90 of at least 18µm,
40. A powder coating composition as claimed in any one of claims 1 to 39, wherein the uncoloured film-forming component or at least one of the uncoloured film-forming components (2a) has a Dv,9G of no more than 75µm.
41. A powder coating composition as claimed in any one of claims 1 to 40, wherein the uncoloured film-forming component or at least one of the uncoloured film-forming components (2a) has a Dv.99 in the range of from 50 to 65µm.

42. A powder coating composition as claimed in any one of claims 1 to 41, wherein the uncoloured film-forming component or at least one of the uncoloured film-forming components (2a) has a Dv.50 in the range of from 5 to 45µim,
43. A powder coating composition as claimed in claim 42, wherein the uncoloured film-forming component or at least one of the uncoloured film-forming components (2a) has a Dv.50 of at least 8µim.
44. A powder coating composition as claimed in claim 43, wherein the uncoloured film-forming component or at least one of the uncoloured film-forming components (2a) has a Dv.99 of at least 40µm and a Dv.50 of at least 10µm
45. A powder coating composition as claimed in claim 43 or claim 44, wherein the uncoloured film-forming component or at least one of the uncoloured film-forming components (2a) has a Dv.50 in the range of from 12 to 30µim,
46. A powder coating composition as claimed in any one of claims 1 to 45, wherein the coloured film-forming base components or at least one of the coloured film-forming base components (1) have a Dv.99 in the range of from 6 to 25µm.
47. A powder coating composition as claimed in any one of claims 1 to 46, wherein the coloured film-forming base components or at least one of the coloured film-forming base components (1) have a Dv.50 of no more than 18µm.

48. A powder coating composition as claimed in claim 47, wherein the coloured film-forming base components or at least one of the coloured film-forming base components (1) have a Dv.50 of no more than 15µim.
49. A powder coating composition as claimed in claim 48, wherein the coloured film-forming base components or at least one of the coloured fiim-forming base components (1) have a Dv.50 in the range of from 2 to 12µm.
50. A powder coating composition as claimed in any one of claims 1 to 49, wherein the coloured film-forming base components contain in total from 5 to 70 weight % of pigment, calculated on the total weight of those components.
51. A powder coating composition as claimed in any one of claims 1 to 50, wherein the coloured film-forming base components contain in total from 0.5 to 50 weight % of pigment, calculated on the total weight of the composition.
52. A powder coating composition as claimed in any one-of claims i to 51, wherein the individual particulate components of the agglomerate include one or more non-film-forming component (3).
53. A powder coating composition as claimed in claim 52, wherein the individual particulate components of the agglomerate include a texturing agent (3),
54. A powder coating composition as claimed in claim 52 or claim 53, wherein the non-film-forming component or components constitute up to 50% by weight of the total particulate components of the composition.

55. A kit comprising the following separate particulate components for
agglomerating into powder coating compositions for the preparation of powder coatings
in a number of different colours:
• a plurality of differently coloured film-forming base components, each with a Dv.99 of no more than 30µm, and
• one or more uncoloured film-forming components, each having a higher Dv.99, and/or a higher Dv.5Q, each Dv.99 being more than 40µm.

56. A kit as claimed in claim 55, wherein the uncoloured film-forming component or at least one of the uncoloured fiim-forming components has a Dv.99 of no more than 90(im.
57. A kit as claimed in claim 55 or claim 56t which includes at least 7 differently coloured fiim-forming base components.
58. A kit as claimed in any one of claims 55 to 57, whicSlricludes an uncoloured film-forming component that is compatible during film-formation with the coloured film-forming base components, and an uncoloured film-forming component that is incompatible with the coloured film-forming base components or that becomes incompatible therewith during film-formation,
59. A kit comprising the following separate particulate components for the manufacture of agglomerated powder coating compositions for the preparation of powder coatings in a number of different colours:
• at least 7 differently coloured film-forming base components,

• an uncoloured film-forming component that is compatible with the coloured film-forming base components and remains compatible during film-formation and that has a Dv.99 of more than 40µm and no more than 90µm, and
• an uncoloured film-forming component that is incompatible with the coloured film-forming base components or that becomes incompatible therewith during film-formation, and that has a Dv.99 of more than 40µm and no more than 90µm.

60. A kit as claimed in claim 59, which includes means for comminution of the coloured film-forming base components to a powder having Dv.99 of no more than 30µm.
61. A kit as claimed in any one of claims 55 to 60, wherein the different components are as specified in any one of claims 31 to 53.
62. A kit as claimed in any one of claims 55 to 61, which includes at least 3 uncoloured film-forming components.
63. A kit as claimed in any one of claims 55 to 62, which includes means for agglomerating the components to produce a fluidisable powder.
64. A process for the preparation of a powder coating composition as claimed in any one of claims 1 to 54, which comprises providing the specified one or more coloured film-forming base components (1) and the one or more specified uncoloured film-forming components (2a) and if desired one or more other components selected from other uncoloured film-forming components (2b) and non-film-forming components (3), in the specified proportions, and mixing and agglomerating the

components into composite particles such that the composition is air-fluidisable and can be applied to a substrate by electrostatic spray.
65. A process for the preparation of a powder coating composition as claimed in claim 1 from a kit comprising a plurality of differently coloured film-forming base components and one or more uncoloured film-forming components having a Dv.99 of more than 40^im, which comprises comminuting at least one of the coloured film-forming base components to provide a powder having a Dv,99 of no more than 30(imf and mixing and agglomerating the comminuted coloured film-forming base component(s) and at least one of the specified uncoloured film-forming components having a Dv,99 or a Dv.50 higher than the Dv.99 or Dv.50 respectively of the comminuted coloured film-forming base component or components taken together, in the proportions specified in claim 1, to form composite particles, such that the composition is air-fluidisable and can be applied to a substrate by electrostatic spray.
66. A powder coating composition when prepared by a process as claimed in claim 64 or claim 65.
67. A process for forming a coating on a substrate, which comprises applying an agglomerated composition as claimed in any one of claims 1 to 54 or claim 66 to a substrate, and heating the applied composition to form a continuous coating,
68. A substrate coated by a process as claimed in claim 67.

69. A powder coating composition substantially as hereinbefore described
70. A kit substantially as hereinbefore described
71. A process for the preparation of a powder coating composition
substantially as hereinbefore described.
72. A substrate coated by a process substantially as hereinbefore
described


Documents:

in-pct-2001-1206-che-claims filed.pdf

in-pct-2001-1206-che-claims granted.pdf

in-pct-2001-1206-che-correspondence others.pdf

in-pct-2001-1206-che-correspondence po.pdf

in-pct-2001-1206-che-description complete filed.pdf

in-pct-2001-1206-che-description complete granted.pdf

in-pct-2001-1206-che-form 1.pdf

in-pct-2001-1206-che-form 19.pdf

in-pct-2001-1206-che-form 26.pdf

in-pct-2001-1206-che-form 3.pdf

in-pct-2001-1206-che-form 5.pdf

in-pct-2001-1206-che-other documents.pdf

in-pct-2001-1206-che-pct.pdf


Patent Number 211192
Indian Patent Application Number IN/PCT/2001/1206/CHE
PG Journal Number 50/2007
Publication Date 14-Dec-2007
Grant Date 18-Oct-2007
Date of Filing 30-Aug-2001
Name of Patentee INTERNATIONAL COATINGS LIMITED
Applicant Address P.O. Box 20980, Oriel House, 16 Connaught Place, London W2 2ZB
Inventors:
# Inventor's Name Inventor's Address
1 CORDINER, Andrew, George 272 Westbourne Avenue, Gateshead, Tyne & Wear NE8 4NS,
PCT International Classification Number C07D 5/03
PCT International Application Number PCT/GB00/00871
PCT International Filing date 2000-03-09
PCT Conventions:
# PCT Application Number Date of Convention Priority Country
1 9905522.0 1999-03-10 U.K.