Title of Invention	COMPOSITION SENSITIVE TO IR RADIATION AND TO HEAT AND LITHOGRAPHIC PLATE COATED THEREWITH
Abstract	A heat-sensitive composition of the positive type comprising a polymeric binder and a solubility inhibitor, wherein the said solubility inhibitor consists of an organometallic compound, with the exclusion of the metallocenes, an organic salt or an organic complex of an inorganic salt of a metal belonging to the group IliA or transition group of the periodic system of the elements.

Full Text

"Composition sensitive to IR radiation and to heat and lithographic plate coated therewith" ************ FIELD OF INVENTION The present invention relates to a composition sensitive to IR radiation and to heat, and a lithographic plate coated with this composition. In particular, it relates to a composition sensitive to IR radiation and to heat which is useful for the production of a lithographic plate of the positive type. It also relates to a composition sensitive to laser radiation which is useful for the production of a lithographic plate of the positive type. BACKGROUND OF INVENTION As is well-known, the technique of printing by means of lithographic plates is based on differential partition between fatty substances and water. The fatty substance or ink is retained preferentially by the image area and the water is preferentially retained by the non-image area. When the surface of a lithographic plate, suitably prepared, is moistened with water and then sprinkled with ink, the non-image area retains the water and repels the ink, while the image area accepts the ink and repels the water. Then, the ink on the image area is transferred onto the surface of a material on which it is desired to reproduce the image, such as, for example, paper, textile and the like. In general, the lithographic plates used in printing processes are formed from an aluminium support covered with a composition sensitive to light (photosensitive). When such a composition becomes soluble in an alkaline developing bath through the action of heat or of radiation of appropriate wavelength, the printing process is termed "positive". Conversely, when the portion exposed to heat or to radiation of appropriate wavelength becomes insoluble in an alkaline developing bath, the printing process is termed "negative". In both cases, the remaining, image area is lipophilic and hence accepts the ink, while the non-image area is hydrophilic and accepts the water. The recent developments in the field of lithographic plates have been directed towards the search for compositions sensitive to laser light, preferably in the near IR. In particular, to laser light controlled by software, in such a way as directly to transfer the image created by computer onto the surface of the plate. This technique has the advantage of eliminating the photographic films, with consequent reduction in the pollution due to the chemical substances used for the preparation and production of these and elimination of all the problems that arise in the transfer of the image onto the plate via photographic films. In the first place, a composition sensitive to radiation emitted by a laser could impart greater reliability to the system. Secondly, it would be possible to work under ambient illumination, thus eliminating the automatic loading systems or the darkrooms. With the aim of attaining this objective, in recent years many compositions comprising a polymeric binder and a solubility inhibitor have been investigated. Such a solubility inhibitor has the ability to render the polymeric binder insoluble in a suitable alkaline developing bath as long as it has not been exposed to a sufficient quantity of heat and of then rendering it soluble in the said developing bath after such exposure to heat. Besides the aforesaid components, many of the compositions described until now also comprise a so-called IR absorber, usually consisting of a compound capable of absorbing IR radiation and of transforming part of the radiation absorbed into heat, giving it up to the immediately surrounding environment. OBJECTS OF INVENTION The present invention aims to provide a composition sensitive to heat and a lithographic plate of the positive type coated with the said composition wherein the solubility inhibitor consists of an organometallic compound, excluding the metallocenes, or an organic salt of a metal of the group IIIA or transition group of the periodic chart of the elements. The present invention also aims to provide a composition sensitive to IR radiation and a lithographic plate of the positive type coated with the said composition wherein the solubility inhibitor consists of an organometallic compound, excluding the metallocenes, or an organic salt of a metal of the group IIIA or transition group of the periodic chart of the elements. The present invention further aims to provide a composition sensitive to laser radiation and a lithographic plate of the positive type coated with the said composition wherein the solubility inhibitor consists of an organometallic compound, excluding the metallocenes, or an organic salt of a metal of the group IIIA or transition group of the periodic chart of the elements. DEFINITIONS The term "metallocenes" is used to mean metallorganic compounds, named also sandwich compounds, formed by two cyclopentadienyl groups bound to a metal atom. The term "lithographic plate" means a support covered with a coating which, after being suitably exposed and developed, is used, as a planographic matrix, in printing processes wherein there is differential partition between fatty substances and water. Typical examples of support materials are constituted by plates of aluminium, zinc, copper, polyester and paper covered with a polymer. Preferably, the support is a sheet of grained aluminium, oxidized and suitably treated to receive the photosensitive composition. The term "positive type" means that the portion of the photosensitive coating exposed to the radiation or to heat becomes soluble in such a way that it can be removed during the process of development of the plate. Typically, the development process is performed in alkalis having a conductivity of from 75 to 110 mS. The term "polymeric binder" means a polymer soluble in alkali, such as for example a novolac resin, a resol resin, a vinylphenolic resin, derivatives thereof or mixtures thereof. Typically, a novolac resin is a polycondensation product obtained by reaction in an acidic environment between formaldehyde and phenol and/or m-cresol and/or symmetrical xylenol in a molecular ratio of less than 1 (for example formaldehyde : phenol = 1:2). Optionally, the thus obtained compound is variously modified such as, for example, by reaction with amides. Typical examples of commercial novolac resins are the products LB 6564 (mean ponderal molecular weight = 6000-10,000) and LB 744 (mean ponderal molecular weight = 8000-13,000) from the firm BAKELITE (Germany); R 7100 (mean ponderal molecular weight = 8000-10,000) from the firm Rohner; PN 320 (mean ponderal molecular weight = 3000-5000) and PN 430 (mean ponderal molecular weight = 5000-9500) from the firm Clariant; 010/129/2 (mean ponderal molecular weight = 8700 - 9700), 010/129/1 (mean ponderal molecular weight = 2200 - 3200), and 010/127/1 (mean ponderal molecular weight = 800 -1800), 76/159 (mean ponderal molecular weight = 2900 - 3900), 76/160 (mean ponderal molecular weight = 2200 - 3200), 76/190 (mean ponderal molecular weight = 7500 - 8500) from the firm Rohner. The term "heat-sensitive composition" means a composition which includes a polymeric binder and has the property of being insoluble in an alkaline developing bath as long as it has not been exposed to a sufficient quantity of heat and of then being soluble in the said bath after such exposure to heat. The term "solubility inhibitor" means a compound capable of rendering a heat-sensitive composition that contains it insoluble in a suitable alkaline developing bath as long as the said composition has not been exposed to a sufficient quantity of heat and/or laser radiation and of then rendering it soluble in the said developing bath after such exposure to heat and/or laser radiation. The term "IR absorber" means a compound capable of absorbing IR radiation and of transforming part of the absorbed radiation into heat and giving it up to the immediately surrounding environment. Preferably, such an absorber is soluble in water, ketones, glycols, glycolethers, alcohols, esters and mixtures thereof. Typical examples of absorbers are the commercial products KF 646, KF 645, KF8ia KF 1003, KF 1002, IR HBB 812 and KF 818 from the company Riedel-de Haen/Allied/Signal (Seeize, Germany), the commercial product ADS 830A and ADS 1060A, ADS793EI, ADS798MI, ADS798MP, ADS800AT, ADS805PI, ADS805PP, ADS805PA, ADS805PF, ADS812MI, ADS815EI, ADS818HI, ADS818HT, ADS822MT, ADS838MT, ADS840MT, ADS845BI, ADS905AM,ADS956BGI, ADS1040P, ADS1054P, ADS1050P, ADS1120P from the firm American Dye Source (Varennes, Quebec, Canada), the commercial products YKR - 3070, YKR - 3082, D99-029 and D99 - 039 from the firm Yamamoto Chemical Inc., the commercial product Projet 825 LDI from the firm Avecia Limited (ex Zeneca Specialties, Manchester, England). Here, for convenience, the product Projet 825 will be referred to hereinbelow by the abbreviation "Z". A particularly interesting family of absorbers is that characterized by the following structural formula: wherein X, Y, R, R' and R" can take many meanings. Typical examples of these meanings are: simple or condensed heterocyclic ring for X, simple or fused heterocyclic ring for Z and Y together with the carbon atom to which they are bound, hydrogen, C1-3 aikyi, SO3" or COO' for R and R' independently of one another and H or CI for R". Particular examples of the said heterocyclic rings are: The term "IR radiation" means radiation of a wavelength of from of from 780 to 1400 nm. A typical example of a device used to generate IR radiation is a laser diode which emits at ca. 830 nm. The term "laser radiation" means radiation of a wavelength of from 600 to 1400 nm. Absorber capable of absorbing radiation having a wavelenght of from 600 to 780 nm are well known in the art. Typical examples of such absorbers are the commercial products ADS640PP, AD640HI, ADS640HI, ADS675MT, ADS680BP, ADS740PP, ADS745HT, ADS760MP, ADS775MI, ADS775MP, ADS775HI, ADS775PI, ADS775PP, ADS780MT and ADS780BP from the firm American Dye Source (Varennes, Quebec, Canada). The term "nominal wavelength" means a wavelength of from 805 to 830 nm. The term "dye" means a coloured compound or preparation capable of dyeing the photosensitive composition in order to reveal the image after the exposure to light and/or after development. Typical examples of dyes are Basonyl™ blue 636 (Colour Index 42595) from the firm Basf (Germany), Sudan Yellow 150 (Colour Index 11021) from the firm Basf (Germany), Solvent Green 3 (Colour Index 61565), Solvent Blue 59 (Colour Index 61552), Solvent Blue 35 (Colour Index 61554) or mixtures thereof. The term "triazine" intends to mean the entire family of the substituted trichloromethyl-s4riazines of known type. The term "additive" means a compound used to improve or confer a desired property on the photosensitive composition such as for example an enhancer developing agent, a pigment, a plasticizer capable of rendering the emulsion less resistant to heat and hence more sensitive, without however having an insolubilizing function, or an agent capable of modifying the surface and/or interfacial tension and thus improving the spreadability characteristics on the support and the covering power of the heat-sensitive composition. Typical examples of pigments are: Heliogen™ Blue L 6700 F (PB 15:6 colour index 74160), Heliogen™ Blue L 6875 F (PB 15:2 colour index 74160) from the firm Basf (Germany), and from the Waxoline™ series: BLUE AP FW (colour index SB 36 PART 2 61551), VIOLET A FW (colour index SV 13 PART 2 60725), GREEN G FW (colour index SB 3 PART 2 61565) from the firm Avecia Limited (ex Zeneca Ltd.) or mixtures thereof. Typical examples of agents capable of modifying the surface and/or interfacial tension are the copolymers dimethylpolysiioxane-modified polyethers, mixtures of high-boiling aromatic solvents, ketones and esters and fluorinated surfactants. Typical examples of such agents are the commercial products BYK 300, 302 and 341, BYKETOL™ OK from the firm BYK Mallinckrodt and FC 430 and FC 431 from the firm 3M. SUMMARY OF INVENTION In a first aspect, the present invention relates to a heat-sensitive composition of the positive type comprising a polymeric binder and a solubility inhibitor, characterized in that the said solubility inhibitor is a organometallic compound, an organic salt or an organic complex of an inorganic salt of a metal of the group IIIA or transition group of the periodic chart of the elements, provided however that solubility inhibitor is not a metallocene. In a second aspect, the present invention also relates to a lithographic plate of the positive type coated with a heat-sensitive composition comprising a polymeric binder and a solubility inhibitor, characterized in that the said solubility inhibitor is a organometallic compound, an organic salt or an organic complex of an inorganic salt of a metal of the group IIIA or transition group of the periodic chart of the elements, provided however that solubility inhibitor is not a metallocene. In a third aspect the present invention relates to a laser-sensitive composition of the positive type comprising a polymeric binder and a solubility inhibitor, characterized in that the said solubility inhibitor is a organometallic compound, an organic salt or an organic complex of an inorganic salt of a metal of the group IIIA or transition group of the periodic chart of the elements, provided however that solubility inhibitor is not a metallocene. In a further aspect the present invention relates to a lithographic plate of the positive type coated with a laser-sensitive composition comprising a polymeric binder and a solubility inhibitor, characterized in that the said solubility inhibitor is a organometallic compound, an organic salt or an organic complex of an inorganic salt of a metal of the group IIIA or transition group of the periodic chart of the elements, provided however that solubility inhibitor is not a metallocene. Typically, the metal of group IIIA is aluminium and boron and of the transition group is tJtanium(IV), iron(lll), copper(ll), chromium(lll), cobalt(ll), manganese(ll), tungsten(l\/), vanadium, zinc and zirconium. The preferred metals are titanium(IV), copper(ll) and iron. Depending on the number of valences of the above mentioned metals the said metallorganic compounds preferably comprises at least 1 organic moiety selected from the group comprising aliphatic groups having from 1 to 10 C atoms and cycloaliphatic groups having from 3 to 6 C atoms. Still preferably the said aliphatic group is an alkyl, alkoxyl or alkylcarboxyl group having from 1 to 10 C atoms. Typical examples of aluminium organic compounds are aluminium acetate, aluminium acetilacetonate, aluminium isopropoxide, aluminium tri-sec-butoxide, diethyl aluminium chloride, diethyl aluminium ethoxide, diisobutyl aluminium hydnde and triisobutyl aluminium. Typical examples of boron organic compounds are triisopropyl borate, tributyl borate, triethyl borane, triethyl borate, bromodimetyl borane, triphenyl borane, B-methoxy diisopino camphenyl borane, DIP-chloride, B-chloro diisopino camphenyl borane, B-bromocathecol borane, 2-bromo-1,3,2-benzodioxaborole and bromo dimethyl borane. Typical examples of titanium(IV) organic compounds are titanium(IV) isopropoxide (tetraisopropyl orthotitanate), titanium(IV) propoxide (tetrapropyl orthotitanate), titanium(IV) butoxide (tetrabutyl titanate), titanium(IV) ethoxide (tetraethyl orthotitanate), titanium(IV) 2-ethylhexoxide (tetrakis (2-ethylhexyl) orthotitanate), titanium(IV) methoxide (tetramethyl orthotitanate), titanium diisopropoxide bis(acetylacetonato) and titanium(IV) (triethanolaminato). Examples of commercial organic compounds of titanium(IV) are Tyzor™ TE, Tyzor™ 131, Tyzor™ GBA, Tyzor™ TPT, Tyzor™ TBT, Tyzor™ TOT and Tyzor™ AA. Typical examples of organic complexes of an inorganic salt of titanium(IV) are titanium tetrachloride tetrahydrofuran and tetrachlorobis (tetrahydrofuran) titanium. Typical examples of copper(ll) organic compounds are copper(ll) d-gluconate, copper(ll) acetate monohydrate, copper(ll) acetate hydrate, copper(ll) acetylacetonate, copper(ll) 2-ethylhexanoate, copper(ll) cyclohexanebutyrate, 2,4 pentanedione copper(ll) derivates, copper(ll) acetate and copper(ll) methoxide. Typical examples of iron organic compounds are iron(ll) d-gluconate dihydrate, iron(lll) acetylacetonate, 2,4 pentanedione iron(lll) derivatives and iron(ll) acetate. Typical examples of zinc organic compounds are zinc acetylacetonate, zinc acetylacetonate hydrate, zinc acetate, zinc acetate dihydrate, diethylzinc, dimethyl zinc, diphenyl zinc, dichloro-(N,N,N\N')-tetramethylene-diamino zinc, zinc bis (2,2,6,6-tetramethyl-3,5-heptanedionate), zinc cyclohexanebutyrate and 3,5-di-tert-butylsalicylic acid zinc salt. Typical examples of manganese organic compounds are manganese acetate, manganese acetate dihydrate, manganese acetate tetra hydrate, manganese acetylacetonate and manganese cyclohexanebutyrate. Typical examples of zirconium organic compounds are zirconium(IV) butoxide (tetrabutyl zirconate), zirconium tert-butoxide (tetra (ter-butyl) zirconate), zirconium ethoxide (tetraethyl zirconate), zirconium propoxide (tetrapropyl zirconate), zirconium(l\/) isopropoxide isopropanol complex, zirconium acetate, zirconium acetate hydroxyde, zirconium(IV) acetylacetonate and 2,4 pentanedione zirconium(IV) derivatives. Typical examples of vanadium organic compounds are vanadyl isopropoxide, vanadyl acetylacetonate and vanadium(lll) acetylacetonate. Preferably, the said polymeric binder comprises a novolac resin or a derivative thereof having a mean ponderal molecular weight of from 2000 to 14,000. Advantageously, the said polymenc binder is a mixture of two or more novolacs. Preferably, a first novolac has a mean ponderal molecular weight of from 3000 to 5000 and a second novolac has a mean ponderal molecular weight of from 6000 to 10,000. In a first preferred embodiment of the present invention, the composition also comprises an IR absorber capable of absorbing IR radiation of from 780 to 1400 nm, preferably from 780 to 1100 nm, and of converting it into heat. The composition of the present invention can also comprise a dye. Typically the said dye is Basonyl blue 636 (Colour Index 42595) and is present in quantities sufficient only to dye the composition. The composition of the present invention can also comprise a plasticizer, a triazine and other additives of a standard nature. In particular, the plasticizer has the purpose of modifying the toughness and the hardness of the said composition by varying its sensitivity to heat without appreciably affecting its sensitivity to the developers. Advantageously, the composition of the present invention can also contain solubility inhibitors belonging to other classes such as, for example, a hydroxylated acrylic copolymer or a derivative thereof wherein some hydroxyl groups have been esterified with an aliphatic carboxylic acid or a reactive derivative thereof. Such further heat-sensitive solubility inhibitors are the subject of another patent application, which is included here by reference, filed on the same date by the Applicant. Typically, the said hydroxylated acrylic copolymers are Macrynal™ SM 510 N, SM 513, SM 515 or SM 516 from the firm Hoechst or a derivative thereof obtained by partial esterification with maleic anhydride. The present invention is further described by the following Examples and Tests, which are solely for illustrative purposes and must not be considered to limit the invention. EXPERIMENTS EXAMPLE 1 Preparation of compositions sensitive to heat and to IR radiation The mixture (6 g) of the components indicated in the following Tables was dissolved at ambient temperature (ca. 25*^C) in 94 g of a 30 : 70 (w/w) acetone : methoxypropanol mixture, stirring until complete dissolution of the components. The solution obtained was filtered through paper using a filter of the 0860 type from the firm Schleicher & Schuell (100 mm). The values indicate the first step visible independently of the thickness of the remaining coating; the value 1 is equivalent to a time of 1 minute and the value 6 is equivalent to a time of 6 minutes. The resistance of the composition to the solution used is highest for the value 6 and lowest or zero resistance for the value 1, TEST 4 Exposure to IR radiation Six different zones of a plate having the same weight distribution per unit area were exposed using a laser beam, controlled by software and having a nominal wavelength 830 nm (all composition except for composition No. 18) and nominal wavelength 1060 nm (composition No. 18 only), at the following energy values/cm2: 300 mJ/cm2 250 mJ/cm2, 150 mJ/cm2, 100 mJ/cm2 75 mJ/cm2 and 50 mJ/cm2. The exposed plates were immediately developed in a tray using, as reference, LAP98 from the firm Lastra S.p.A. as developer at a temperature of from 24 to 25°C for 45 seconds of immersion time with stirring plus 15 seconds of wiping with a cotton pad. The results of the test are shown in Table 12 and 12bis. A corresponds to an emulsion weight of 1.6 -1.8 g/m2. B corresponds to an emulsion weight of 2.0 - 2.2 g/m2. The term "cleanness of the base" is used to mean that the developer has removed the composition from the regions that have been exposed to laser radiations. TESTS Resistance to mechanical abrasion To simulate the mechanical and chemical abrasion which a plate undergoes during the printing cycle, samples of plates corresponding to the compositions from 1-4 and 7, 18-25 were fixed to a level surface and placed in close contact with a cotton pad soaked in a 50% solution of isopropyl alcohol. The pad was moved by an arm attached to a compressed air system capable of imparting an oscillatory motion with consequent rubbing of the samples under examination. For each composition, the maximum number of passes before the complete removal of the emulsion was recorded. The results expressed in number of passes are reproduced in the following Table 13. CLAIMS 1. A heat-sensitive composition of the positive type comprising a polymeric binder and a solubility inhibitor, characterized in that the said solubility inhibitor is a organometallic compound, an organic salt or an organic complex of an inorganic salt of a metal of the group IIIA or transition group of the periodic chart of the elements, provided however that solubility inhibitor is not a metallocene. 2. A composition according to Claim 1, characterized in that the metal belonging to group IIIA is aluminium or boron. 3. A composition according to Claim 1, characterized in that the metal belonging to the transition group is titanium(IV), iron(ll) and (III), copper(ll), chromium(lll), cobalt{ll), manganese(ll), tungsten(IV), vanadium, zirconium or zinc. 4. A composition according to any of the preceding claims 1 to 3, characterized in that the said metallorganic compounds comprises at least 1 organic moiety selected from the group comprising aliphatic groups having from 1 to 10 C atoms and cycloaliphatic groups having from 3 to 6 C atoms. 5. A composition according to Claim 4, characterized in that the said aliphatic group is an alkyl, alkoxyl or alkylcarboxyl group having from 1 to 10 C atoms. 6. A composition according to any of the preceding claims 1 to 5, characterized in that the organic compound of titanium(IV) is selected from the group comprising titanium(IV) isopropoxide, titanium(IV) propoxide, titanium(IV) butoxide, titanium(IV) ethoxide, titanium(IV) 2-ethylhexoxide, titanium(IV) methoxide, titanium diisopropoxide bis(acetylacetonato) and titanium(IV) (triethanolaminato). 7. A composition according to any of the preceding claims 1 to 6, characterized in that the organic complex of an inorganic salt of titanium(l\/) is the complex of titanium tetrachloride with tetrahydrofuran or tetrachlorobis (tetrahydrofuran) titanium. 8. A composition according to any of the preceding claims 1 to 5, characterized in that the organic compounds of copper are selected from the group comprising copper(ll) d-gluconate, copper(ll) acetate monohydrate, copper(ll) acetate hydrate, copper(ll) acetylacetonate, copper(ll) 2-ethylhexanoate, copper(ll) cyclohexanebutyrate, 2,4 pentanedione copper(ll) derivates, copper(ll) acetate and copper(ll) methoxide. 9. A composition according to any of the preceding claims 1 to 5, characterized in that the organic compounds of iron are selected from the group comprising iron(ll) d-gluconate dihydrate, iron(lll) acetylacetonate, 2,4 pentanedione iron(lll) derivatives and iron(ll) acetate. 10. A composition according to any of the preceding claims 1 to 5, characterized in that the organic compounds of zinc are selected from the group comprising zinc acetylacetonate, zinc acetylacetonate hydrate, zinc acetate, zinc acetate dihydrate, diethylzinc, dimethyl zinc, diphenyl zinc, dichloro-(N,N,N',N')-tetramethylene-diamino zinc, zinc bis (2,2,6,6-tetramethyl-3,5-heptanedionate), zinc cyclohexanebutyrate and 3,5-di-tert-butylsalicylic acid zinc salt. 11. A composition according to any of the preceding claims 1 to 5, characterized in that the organic compounds of aluminium are selected from the group comprising aluminium acetate, aluminium acetilacetonate, aluminium isopropoxide, aluminium tri-sec-butoxide, diethyl aluminium chloride, diethyl aluminium ethoxide, diisobutyl aluminium hydride and triisobutyl aluminium. 12. A composition according to any of the preceding claims 1 to 5, characterized in that the organic compounds of boron are selected from the group comprising triisopropyl borate, tributyl borate, triethyl borane, triethyl borate, bromodimetyl borane, triphenyl borane, B-methoxy diisopino camphenyl borane, DIP-chloride, B-chloro diisopino camphenyl borane, B-bromocathecol borane. 2-bromo-1,3,2-benzodioxaborole and bromo dimethyl borane. 13. A composition according to any of the preceding claims 1 to 5, characterized in that the organic compounds of manganese are selected from the group comprising manganese acetate, manganese acetate dihydrate, manganese acetate tetra hydrate, manganese acetylacetonate and manganese cyclohexanebutyrate. 14. A composition according to any of the preceding claims 1 to 5, characterized in that the organic compounds of zirconium are selected from the group comprising zirconium(IV) butoxide, zirconium ethoxide, zirconium propoxide, zirconium(l\/) isopropoxide isopropanol complex, zirconium acetate, zirconium acetate hydroxyde, zirconium(IV) acetylacetonate and 2,4 pentanedione zirconium(IV) derivatives. 15. A composition according to any of the preceding claims 1 to 5, characterized in that the organic compounds of vanadium are selected from the group comprising vanadyl isopropoxide, vanadyl acetylacetonate and vanadium(lll) acetylacetonate. 16. A composition according to any one of Claims 1 to 15, characterized in that the said polymeric binder comprises a novolac resin. 17. A composition according to any one of Claims 1 to 16, characterized in that it further comprises an IR absorber capable of absorbing IR radiation of from 780 to 1400 nm. 18. A composition according to any one of Claims 1 to 17, characterized in that in comprises also a solubility inhibitor which is a hydroxylated acrylic copolymer or a derivative thereof wherein some hydroxyl groups have been esterified with a carboxylic acid or reactive derivatives thereof. 19. A composition according to claim 1, is a laser sensitive composition. 20. A lithographic plate of the positive type coated with a heat-sensitive composition according to claims 1 to 18. Dated this 28th day of July 2000

Documents:

599-mas-2000-abstract.pdf

599-mas-2000-claims filed.pdf

599-mas-2000-claims granted.pdf

599-mas-2000-correspondnece-others.pdf

599-mas-2000-correspondnece-po.pdf

599-mas-2000-description(complete) filed.pdf

599-mas-2000-description(complete) granted.pdf

599-mas-2000-form 1.pdf

599-mas-2000-form 26.pdf

599-mas-2000-form 3.pdf

599-mas-2000-form 5.pdf

599-mas-2000-other documents.pdf