A PROCESS FOR MANUFACTURE OF CELLULOSE MOULDINGS

Abstract The present invention relates to a process for manufacture of cellulose mouldings, such as fibres, filaments, or films, from TCF-bleached or ECF-bleached cellulose, in which the bleached cellulose is dissolved in an aqueous tertiary aminoxide to form a mouldable cellulose, the cellulose solution deforms, and the moulding comes into being by coagulation of the deformed solution, characterized in that, to reduce the cellulose decomposition in the process, TCF-bleached cellulose is used comprising carboxyl group content in the range from 1 to 35 µmol/g or an ECF-bleached cellulose with carboxyl group content in the range from 1 to 50µmol/g.
Full Text

The principle is known from WO 97/23666 that the use of TCF-bleached cellulose pulp in the Lyocell process leads to mouldings with a higher degree of whiteness than the use of an ECF-bleached cellulose pulp. Both cellulose pulps are manufactured with similar high initial degrees of whiteness of about 90 % and high degrees of purity, in particular with regard to the lignin content. It therefore seems questionable whether the TCP-cellulose pulp in general produces better degrees of whiteness of the cellulose mouldings manufactured from this cellulose pulp than an ECF-cellulose pulp.
The objective on which the present invention is based is the creation of a process for the manufacture of cellulose mouldings with low cellulose decomposition, based on TCF or ECF-bleached cellulose pulp. The reduction in the cellulose decomposition is intended to be attained essentially without special measures in the lyocell process. Additional advantages of the invention are derived from the following description.
The degrees of whiteness of cellulose pulp and fibre of a number of different cellulose pulp provenances were determined, which were either ECF or TCF-bleached. The determination of the degree of whiteness of the cellulose pulp was carried out in accordance with DIN 53145, Part 2. The determination of the degree of whiteness of the fibres was effected in accordance with the method described in WO 97/23666, page 6. The average degree of polymerisation of the cellulose pulps according to the Cuoxam method amounted to about 550. The degrees of whiteness measured at the fibre are compiled in Table 1.

The invention relates to a process for the manufacture of cellulose mouldings, such as fibres, filaments, or films, from TCF-bleached or ECF-bleached cellulose, in which the bleached cellulose is dissolved in an aqueous tertiary aminoxide to form a mouldable cellulose solution, the cellulose solution deforms, and the moulding comes into being by coagulation of the deformed solution. The invention also relates to the use of a TCF or ECF-bleached cellulose pulp for the manufacture of cellulose mouldings.
The problems of the viscous process led to the development of new processes for the manufacture of regenerated cellulose mouldings, in which the cellulose is brought into solution without chemical modification. The fibres and filaments obtained from these solutions are grouped under the designation "Lyocell". Especially well-suited organic solvents are tertiary aminoxides, in particular N-methylmorpholin-N-oxide (NMMO). A process for the formation of a cellulose solution in aqueous NMMO is known from DE-A 44 41 468. The manufacture of cellulose mouldings from these solutions is described in EP-A 0 574 870.
In this solution the dissolved cellulose and the solvents, under the thermal conditions of a chemical decomposition, leads to discolourations of the spinning solution. Despite intensive washing of the cellulose mouldings formed, colouring substances remain in the mouldings, as a result of which the degree of whiteness is impaired. In order to reduce the decomposition referred to, a stabilizer is therefore added to the spinning solution. Suitable stabilizers are known from EP-A 0 047 929 and DD 218 104.


It can be seen from Table 1 that with ECF and TCF-bieached cellulose pulps of different provenances the degree of whiteness lies in a narrow range between 87.5 and 93.7. The degree of whiteness. The degrees of whiteness of the spun fibres is likewise in a close range, between 55.0 and 58.6. A higher degree of whiteness of the fibres spun from TCF-bleached cellulose pulp was not perceptible.
Our researches have now revealed that the cellulose decomposition in the course of the Lyocell process, i.e. essentially from the formation through to the coagulation of the spinning solution/ depends on the carboxyl group content of the bleached cellulose pulp used to form the spinning solution. In this situation it has been shown that the cellulose decomposition of the spun fibres is less, the lower the carboxyl group content is of the cellulose pulp

used to form the solution. It is therefore possible, according to the Lyocell process, to create cellulose fibres with reduced cellulose decomposition by making use of a TCF or ECF-bleached cellulose pulp with low carboxyl group content for the formation of the spinning solution.
The objective referred to above is therefore resolved with the process referred to in the preamble in that, in order to reduce the cellulose decomposition in the process, a TCF-bleached cellulose pulp is used with a carboxyl group content in the range from 1 to 35 µmol/g or an ECF-bleached cellulose pulp with a carboxyl group content in the range from 1 to 50 pmol/g. It has also been shown that the cellulose decomposition is the more restrained in the course of manufacture and processing of the extrusion solution, the lower the carboxyl group content is of the cellulose pulp used. In order to achieve low decomposition of the cellulose and the aminoxide in the Lyocell process, TCP and ECF-bleached cellulose pulps are used in the manufacture of the spinning solution of which the carboxyl group content lies within the range indicated. Cellulose pulps with the carboxyl group contents referred to can be manufactured by a number of different cellulose pulp manufacturers. As a result of the reduced decomposition of the spinning solution components, fewer coloured constituents are also derived, with the result that, as a secondary effect, the degree of whiteness of the moulding formed is also improved.
For preference a TCF-bleached cellulose pulp is used in the dissolving stage with a carboxyl group content in the range from 15 to 30 pmol/g or an ECF-bleached cellulose pulp with a carboxyl group content in the range from 25 to 35 pmol/g. The determination of the carboxyl group content of the celluloses which are to be used can be effected according to Doring; see K. Goetze, Chemical Fibres according to the Viscous Process, Vol. 2, 1997 Edition, p. 1079.

the tertiary aminoxide used as the solvent in the preferred process of the invention is N-methylmorpholin-N-oxide-monohydrate (NMMO-MH).
In a further embodiment of the invention, a cellulose solution with a content of alkalis or organic compounds can be formed, whereby the latter contain at least four carbon atoms, at least two conjugated double bonds, and at least two substitutes -X-H, whereby X has the significance of 0 or NR, and R can be hydrogen or an alkyl group with 1 to 4 carbon atoms. By means of these solution additives, the low decomposition achieved according to the invention can be reduced still further. The quantity of the organic compound can lie in the range from 0.01 to 0.5 % by weight, related to the quantity of the solvent. Suitable organic compounds are known from EP~A-0 047 929, A frequently used compound is isopropyl gallate.
By means of the process according to the invention, the decomposition of the cellulose is restricted to a fraction in the range from 3 to 20 % by weight related to the cellulose pulp used. For preference the decomposed cellulose fraction lies in the range from 8 to 15 % by weight.
The invention further relates to the use of a TCF-bleached cellulose pulp or an ECF-bleached cellulose pulp with a carboxyl group content in the range from 1 to 35 µmol/g or 1 to 50 µmol/g respectively for the formation of a cellulose solution in a solvent containing tertiary aminoxide for the manufacture of mouldings according to the Lyocell process. By means of the use of these cellulose pulps, not only is the decomposition in the course of the Lyocell process reduced, but the degree of whiteness of the mouldings formed is increased.
The invention is now explained in greater detail by the following examples.

Examples 1 to 6
Long-fibre sulphite cellulose pulp was bleached by alkaline peroxide-reinforced oxygen extracts, then bleached in a known manner with ozone and with peroxide. The bleaching methods are described, for example, in R.P, Singh, The Bleaching of Pulp, TAPPI Press, Atlanta, USA. In this situation, three different carboxyl group contents are used (Examples 1 to 5) . Three further samples of the cellulose pulp were bleached with hypochlorite. The degree of polymerisation and the initial degree of whiteness of the pulps were determined in accordance with the methods referred to above, as were the carboxyl group and carbonyl group contents of the cellulose pulp. From the bleached cellulose pulps, spinning solutions with 13 % cellulose, 10.5 % water and 7 6.5 % NMMO are manufactured in a known manner. The solutions were spun in accordance with the dry-wet process at 95 °C with a nozzle of 65 µm hole diameter. The degree of polymerisation and the degree of whiteness of the fibres obtained were determined. The determination of the degree of polymerisation was effected in accordance with the Cuoxam method. The values obtained are indicated in Table 2.


of cellulose pulp
Degree of whiteness of fibre 68,9 65,4 58,4 52,8 58,5 56,7
*) For determination see K. Goetze, op. cit.
It can be seen from Table 2 that, as the carboxyl group content of the TCF-bleached cellulose pulp and of the ECF-bleached cellulose pulp increases, a substantial drop is to be observed in the degree of polymerisation and of the degree of whiteness of the fibre cellulose. For a given bleached cellulose pulp, the adjustment of the carboxyl group content accordingly opens up the possibility of improving the textile-physical properties of the spun fibre by way of the degree of polymerisation. Due to the reduced colour body formation in the course of the process, a slow discolouration of the spinning bath sets in, as a result of which costs advantages are derived in the regeneration of the solvent media.
Examples 1 to 10
The degree of polymerisation, the carboxyl group content, the carbonyl group content, and the initial degree of whiteness were determined from four bleached dissolving cellulose pulps. From the cellulose pulps, four spinning solutions were manufactured with 13 % cellulose, 10.5 % water, and 76.5 % NMMO. The zero shear viscosity of the spinning masses at 85 oC was measured (Haake RS 75, year of manufacture 1998). The spinning solutions were spun at 95 oC with a nozzle of 65 µm hole diameter in accordance with the usual dry-wet process. The degree of polymerisation of the celluloses was determined in the spinning solution, and the degree of whiteness of the fibres. The results are compiled in Table 3.
Table 3


The values from Table 3 also show that, as the carboxyl group content increases of the cellulose pulp used, the decomposition of the cellulose increases and the degree of whiteness of the fibre deteriorates in relation to the initial degree of whiteness.


WE CLAIM;
1. A process for manufacture of cellulose mouldings, such as fibres, filaments, or films, from
TCF-bleached or ECF-bleached cellulose, in which the bleached cellulose is dissolved in an
aqueous tertiary aminoxide to form a mouldable cellulose, the cellulose solution deforms, and
the moulding comes into being by coagulation of the deformed solution, characterized in that,
to reduce the cellulose decomposition in the process, TCF-bleached cellulose is used
comprising carboxyl group content in the range from 1 to 35 µmol/g or an ECF-bleached
cellulose with carboxyl group content in the range from 1 to 50 µmol/g.
2. The process as claimed in claim 1 wherein the concentration of carboxyl group content in
the TCF-bleached cellulose is from 15 to 30 µmol/g.
3. The process as claimed in claim 1 wherein the carboxyl group content in the ECF-bleached
cellulose is in the range of 25 to 35 µmol/g.
4. The process as claimed in any one of the preceding claims wherein the tertiary aminoxide
is N-methylmorpholin-N-oxide.
5. The process as claimed in any of claims 1 to 4, wherein forming a cellulose solution with a
content of alkalis or organic compounds, whereby the latter contain at least four carbon
atoms, at least two conjugated double bonds, and at least two substitutes -X-H, whereby X
has the significance of O or NR, and R is hydrogen or an alkyl group with 1 to 4 carbon
atoms.
6. The process as claimed in any of claims 1 to 5, wherein the decomposition of the cellulose
is restricted to a fraction in the range from 3 to 20% by weight, related to the cellulose pulp
used.


Documents:

in-pct-2002-0470-che abstract duplicate.pdf

in-pct-2002-0470-che abstract.pdf

in-pct-2002-0470-che assignment.pdf

in-pct-2002-0470-che claims duplicate.pdf

in-pct-2002-0470-che claims.pdf

in-pct-2002-0470-che correspondence others.pdf

in-pct-2002-0470-che correspondence po.pdf

in-pct-2002-0470-che description (complete) duplicate.pdf

in-pct-2002-0470-che description (complete).pdf

in-pct-2002-0470-che form-1.pdf

in-pct-2002-0470-che form-19.pdf

in-pct-2002-0470-che form-26.pdf

in-pct-2002-0470-che form-3.pdf

in-pct-2002-0470-che form-4.pdf

in-pct-2002-0470-che form-5.pdf

in-pct-2002-0470-che form-6.pdf

in-pct-2002-0470-che pct.pdf

in-pct-2002-0470-che petition.pdf


Patent Number 201809
Indian Patent Application Number IN/PCT/2002/470/CHE
PG Journal Number 05/2007
Publication Date 02-Feb-2007
Grant Date 28-Aug-2006
Date of Filing 02-Apr-2002
Name of Patentee ZIMMER AKTIENGESELLSCHAFT
Applicant Address BORSIGALLE 1, D-60388 FRANKFURT
Inventors:
# Inventor's Name Inventor's Address
1 BAUER, RALF-UWE AM ANGER 9, 07407 RUDOLSTADT
2 KIND, UWE KASTANIENRING 37, 07407 RUDOLSTADT
PCT International Classification Number D01F2/00
PCT International Application Number PCT/DE00/03408
PCT International Filing date 2000-09-29
PCT Conventions:
# PCT Application Number Date of Convention Priority Country
1 19948401.5 1999-10-07 Germany