Title of Invention

METHOD FOR REDUCING NOX EMISSION FROM A KILN PLANT

Abstract The invention relates to a method for reducing the N0X emission from a kiln plant for heat treatment of raw materials, in which kiln plant fuel can be fired in at least three different zones. In one of these at least three zones an amount c of fuel is burned, in a second of these zones an amount b of fuel is burned and to this second zone the NO containing exhaust gases from the other at least two zones are also fed. In the rest of these at least three zones an amount a of fuel is burned and at least a part of the raw materials are fed to these zones together with an oxygen containing gas. The total amount of fuel, b + a, burned in the second and in the last zones is determined by the need for treatment of the raw materials. When the kiln plant is used for manufacturing cement clinker the heat treatment consists of preheating, calcining, sintering and cooling of the mineral raw materials. The invention seeks to provide a method by means of which a reduced N0X emission from a kiln plant is obtained, allowing, at the same time, utilization of fuels of low reactivity, such as petroleum coke, anthracite and other coals with a low gas content, in zones at a relatively low temperature. In accordance with the invention this object is accomplished in that the amounts of fuel, b and a, are adjusted in upward and downward direction until a minimum NO content is achieved in the exhaust gases from the zone to which the NO containing exhaust gases from all other firing zones are fed.
Full Text The invention relates to a method for reducing the NOx emission from a kiln plant where low volatile fuels are used for heat treatment of raw materials, in which kiln plant fuel can be fired in at least three different zones. In one of these at least three zones an amount c of fuel is burned, in a second of these zones an amount b of fuel is burned and to these second zone the NO containing exhaust gases from the other at least two zones are also fed. In the rest of these at least three zones an amount a of fuel is burned and at least a part of the raw materials are fed to these zones together with an oxygen containing gas. The total amount of fuel, b + a, burned in the second and in the last zones is determined by the need for treatment of the raw materials and the amounts of fuel, b and a, burned in the second (2) and the last zones, are adjusted in upward and downward direction until a minimum NO content is achieved in the exhaust gases from the second zone.
Nitrogen oxides, NOx, are formed during combustion due to oxidation of nitrogen in the fuel and due to oxidation of nitrogen in the combustion air. In case the temperature in the combustion zone is less than 1200°C, NOx is formed only on the basis of the nitrogen which is present in the fuel. This type is called fuel NOx. If the temperature rises to a level beyond 1200°C, nitrogen oxides will also be formed on the basis of the combustion air. This type is called thermal NOx. Approximately 95% of the nitrogen oxides which are formed as fuel NOx and thermal NOx consist of nitrogen oxide, NO. In a system in which fuel containing nitrogen is burned, the following types of reactions can take place:


Reaction (1) indicates that the NO formation in the zone will depend on the content of nitrogen in the fuel and on the oxygen content of the gases in that zone. Reaction (2) indicates that if NO is already present in the gas which is fed to this zone, the amount of NO present in the supplied gas will be reduced by means of the nitrogen compounds which are released from the fuel. The net production of NO thus also depends on the NO content in the supplied gas and as the reaction rate of reaction (2) rises more quickly with the temperature than the reaction rate for reaction (1), an increase of the temperature will in net terms lead to a reduction of the amount of NOx which is emitted from the calcining zone. In connection with high temperature combustion in the calciner it is known that if the temperature is increased by approximately 100°C, it is possible to lower the NOx from the calciner by 10-15%. The upper limit of this advantage is 1200°C, at this temperature the forming of thermal NOx from the combustion air will exceed the reduction of NO by reaction (2).

When the kiln plant is used for manufacturing cement clinker the heat treatment consists of preheating, calcining sintering and cooling of the mineral raw materials. The three zones where the N-containing fuel is burned are in the sintering zone, in a kiln, and at two locations in the calcining zone, in a calciner and in at least one burning compartment. According to the description of this invention a 'burning compartment' is a zone where fuel is fired and where at the same time materials to be treated are added. A 'calciner' is a burning compartment located in the kiln gas duct where the exhaust gases from the kiln will pass through it.
The temperature in a kiln plant for cement clinker manufacture is only in excess of 1200°C in the sintering kiln itself. The necessary temperature and time of retention in the kiln depend on the characteristics of the raw materials. A raw material with poor burning characteristics will thus require a high temperature and/or prolonged time of retention. Such conditions with a high flame temperature up to 2000°C will increase the rate of NOx emission substantially.
Measurements have indicated that the content of volatiles in the used fuel and the temperature at which calcination is taking place are factors which influence the formation of NOx in the calcining zone. The higher the content of volatiles in the fuel, the smaller it appears is the amount of Nfuei which is transformed into NOx.

It is a recognised fact that various advantages may be obtained by constructing a calcination zone equipped with an additional burning compartment which is located in such a way that the burning compartment is exclusively fed with tertiary air from the cooler. Such a burning compartment would be considered to be included in the calcination zone if raw materials were added to the compartment.
A plant of this type is described in European patent No. 103423 (F. L.
Smidth & Co. A/S, corresponds to DK-C-151319). Here from is known a
plant (SLC-S) for calcination of cement raw materials, in which it has been
taken into account that it may be difficult to achieve a complete burn-out of
the fuel which is used in the calciner. In this plant raw meal is fed after it has
passed through la cyclone preheater (18, 18', 19, 20, 21), to a burning
compartment (4) in which the raw material is calcined in hot air from the j
cooler (2). Subsequent to preheating, raw meal is directed to the calcining
zone at two locations: in the burning compartment (4) and in the kiln gas
duct (28) or the retention compartment (29). It is possible to feed fuel to the
kiln gas duct (28) via a burner (45), but according to column 6, line 13-27,
this supplementary fuel is supplied in order to ensure that the amount of raw
meal in the kiln gas duct can be increased.
From U.S. Pat. No. 4,014,641 (Mitsubishi) is known a plant for calcination of cement raw materials in which the amount of nitrogen oxide in the exhaust gases of the kiln is reduced by generating an area in the kiln gas duct to which reducing gas is fed. Hot air from the cooler (via a duct (5)) and hot

air from the kiln (via a duct (13)) are routed to a cyclone preheater (14, 15, 16, 17) in which raw material is preheated in counter-current to the hot gas from the cooler and from the kiln. In the area of the kiln gas duct which is located below the supply duct (5) from the cooler, reducing conditions are generated by introducing reducing gases via a duct (12). The reducing gases are formed in the calciner (8) as the air volume which is being fed to the calciner is sufficient to cause gasification of the fuel in the calciner, but insufficient to cause a complete burn-out of the fuel in the calciner (column 4, line 1-5). A particular disadvantage of this plant is that fuels that are difficult to ignite and slow burning, such as petroleum coke, anthracite and other coals with a low gas content cannot be used, as they would produce a large unburned coke residue which would be precipitated in the rotary kiln, and, as a consequence hereof, would be causing problems in terms of sulphur expulsion and caking.
From U.S. Pat. No. 5,364,265 (CLE) is known yet another calcining system in which the NOx emission is limited by formation of reducing gases, viz. CO and H, in a burning compartment (20). The coke formed in the burning compartment during this process has quite distinctive reactive properties. However, calcinations of this method is relatively difficult in regard to ensuring minimum NOx emission since only a few parameters can be adjusted during operation. The amount of fuel burned in the burning compartment depends entirely on the desired degree of calcinations of the raw meal.

SUMMARY OF THE INVENTION
The invention seeks to provide a method by means of which a reduced NOx emission from a kiln plant is obtained, allowing, at the same time, utilisation of fuels of low reactivity, such as petroleum coke, anthracite and other coals with a low gas content, in zones at a relatively low temperature. When producing cement clinker zones at a relatively low temperature is found in the calcining unit(s) before the raw meal enters the kiln.
In accordance with the invention this object is accomplished in that the amount of fuel b, which is used for firing in a zone to which the NO containing exhaust gases are fed and the amount of fuel a, which is used for firing in the zone to which raw materials and oxygen containing gas are fed, respectively, are adjusted in upward and downward direction until a minimum NO content is achieved in the exhaust gases from the zone to which the NO containing exhaust gases from all other firing zones are fed. The temperature in the zones where the fuel b and a are burned are between 900-1200°C.
Actually this method, with combustion of fuel in a burning compartment located in the tertiary air duct and in a calciner which is a burning compartment located in the kiln gas duct, is a combination of an ILC-plant (In-Line-Calciner) and an SLC-S-plant (Separate-Line-Calciner-Single preheater string). Therefore, it would be r easonable to assume that the MX

emission from such a combination plant would be a mean value between the NOx emission coming from an ILC-plant and that coming from an SLC-S-plant of equivalent capacity. Quite surprisingly, it has, however, turned out that the NOx emission from a plant which is operated according to the method as per claim 1 is lower than that achievable in any of the two traditional plants, ILC and SLC-S. Also, it is quite uncomplicated to convert any existing ILC plants into a plant which can be operated in accordance with the method as per claim 1, which means that it will be possible to use fuels which are difficult to burn in the calcining zone.
In existing SLC-S plants as described in European patent no. 103423 it is already possible to burn fuel in the kiln gas duct for formation of a reducing zone, and, therefore, the invention can be implemented at these plants without necessitating any major structural modifications of the plant.
Even when a modest amount b of fuel is fired in the kiln gas duct, as around 10% of the total amount of the fuel which is used in the calcining zone, it will be possible to achieve a significant reduction of the NOx emission from the calcining zone, but a minimum of emitted NOx from the calcining zone will generally be ascertained when an amount b of fuel of between 25 and 75% is fired in the calciner.
In order minimised the NOx emission during the cement clinker manufacturing process, it is advantageous that the process in the burning

compartment and in the calciner is taking place at a relatively high temperature, since the reaction rate of reaction (2) is increased relative to the reaction rate of reaction (1). Further the burning out of slow burning fuels as petrocoke and anthracite is increased at higher temperatures. The upper limit to operating temperature when the process is utilised for manufacturing of cement is around 1200°C. When the temperature is around 1200°C, a liquid phase formation in the raw meal begins, causing the raw meal to become sticky.
An advantageous way of regulating the temperature in calciner and burning compartment is to feed the raw meal to the calcining zone in a controlled manner. It has thus proved to be particularly advantageous to split the raw meal which is fed to the calcining zone into three substreams. These three sub-streams are then fed before and after/in the calciner, respectively, in addition to the raw meal input to the burning compartment. In connection with this split-up, the temperature is set for 1000-1150 °. in that part of the calcining zone which follows immediately after the mixture of exhaust gases from the kiln, of exhaust gases and partially calcined raw materials from the burning compartment and of calciner fuel, but before adding the remaining raw materials. This temperature zone provides for a favourable decomposition of NOx, also when using difficult-to-burn fuel, such as petroleum coke and anthracite.

Accordingly the present invention provides a method for reducing the NOx emission from a kiln plant for heat treatment of raw material, in which kiln plant Nitrogen-containing fuel can be fired in at least three different zones; in a first one of these at least three zones an amount c of fuel is burned and to this zone is fed oxygen containing gas; in a second of these at least three zones an amount b of fuel is burned and to this zone is fed NO containing exhaust gases via a duct and a duct, respectively, from the other at least two zones, the exhaust gases leaving the second zone is removed from the kiln plant; in the third of these at least three zones an amount a of fuel is burned and this zone is fed with oxygen containing gas; where the total amount of fuel, b+a, which is burned in the second and the third zones is determined by the energy requirement for obtaining a desired degree of heat treatment of the raw materials being fed to the first zone, where the ratio of b to a is adjusted to obtain minimum NO content in the exhaust gases from the second zone; characterized in that the raw material stream from the preheater is split into three streams so as to regulate the temperature in the second and in the third of these at least three zones within the range 900-1200°C, where the first of these streams is fed to the exhaust gases flowing from the first zone to the second zone via the duct , the second of these streams is led to the third zone, and the third of these streams is fed to the flow of material through the second zone downstream to the duct that supplies partially calcined material from the third zone .

The invention will now be described in detail with reference to the accompanying drawings in which;
Figure 1 shows an example of a plant by means of which the method according to the claims can be carried out,
Figure 2 shows the NOx emission from a number of ILC plants as a function of the amount of NOx input to the calciner,

FIG. 3 shows the NOx emission from the calciner as a function of the amount of fuel added to the calciner in relation to the total amount of fuel added to the calcining zone.
DESCRIPTION OF THE PREFERRED EMBODIMENTS The kiln plant in FIG. 1 is a kiln plant for manufacturing of cement clinker. It comprises a kiln 1, a calciner 2 and a burning compartment 3. After the kiln 1 there is a clinker cooler 4, from which hot air is carried via a duct 5 to the calcining zone. The hot air is split between two ducts 5a and 5b which leads the air to the calciner 2 and the burning compartment 3. The calciner 2 is fed with hot exhaust gases from the kiln 1 via the duct 6 and hot exhaust gases mixed with partially calcined material from the burning compartment 3 via a duct 7.
Calcined material is directed from the calciner 2 via a duct 8 in suspension to a separating cyclone 9. In separating cyclone 9 the gas/material suspension is separated into a stream of calcined material and a hot gas stream. The calcined raw material is carried via the duct 10 to the rotary kiln 1 and the hot gas stream is directed via the duct 11 to a suspension preheater with several cyclones. Only the lowermost cyclone 12 in the preheater is illustrated in FIG. 1.
The preheated raw material from the cyclone 12 is directed via a tripartition means 13 down into the calcining zone via three ducts 14, 15 and 16. The duct 14 feeds the raw material to a location after the calciner or into the

proper calciner 2, the duct 15 feeds raw material into the exhaust gases from the kiln 1 so that the raw meal is directed into the calciner and the duct 16 feeds the raw material into the burning compartment 3. The duct 16 may either direct the material directly into the burning compartment 3 or to the tertiary air duct 5, the latter is shown on FIG. 1.
The total raw material stream is continuously distributed in controlled manner between the three ducts 14, 15 and 16, and, under special circumstances, one may, for example, choose to interrupt the flow of material through one or several of the ducts 14, 15 and 16.
In this plant fuel may be fired in the calciner 2 by means of a burner 17 (b kcal/kg clinker), in the burning compartment 3 by means of a burner 18 (a kcal/kg clinker) and in the kiln 1 by means of a burner 19 (c kcal/kg clinker).
FIG. 2 indicates recorded data for the NO production in a number of ILC calciners as a function of the amount of NO which is fed to the calciner from the kiln. Since the data relate to measurements from many different plants at which firing is carried out with different fuels exhibiting variations in terms of calorific value and nitrogen content, a non-dimensional illustration has been chosen, where


= the conversion ratio of Nfaei into NO.
- and NOIN, NOOUT and NFuei has been calculated as kmol/h or kg N-
equivalents/kg clinker.
If a curve is adapted to the experimental data, the following relation
emerges:
y=1.5.exp(-x)-l
If it is possible to choose the size of x, x should be chosen so that y which means that the amount of NOx discharged from the calciner is smaller
than that supplied to the calciner. If firing can be carried out at three
locations in kiln plant as described in claim 1, it will be possible to choose
such an x-value.
When an example of a computation using the above form for y is made for a plant in which fuel can be fired in the calciner as well as in a burning compartment, the curve in FIG. 3 emerges.
In this example a total amount of 750 kcal/kg clinker is fired in the kiln plant and of this c = 300 kcal/kg clinker is fired in the rotary kiln. If petroleum coke is used as fuel in the rotary kiln the conversion ratio of Nfuei into NO would be relatively low due to the fact that the flame temperature of petroleum coke is not particularly high, and, therefore, the amount of thermal NOx produced will be quite small, while, at the same time, the temperature in the kiln at around 1400°C is sufficiently high to make reaction (2) dominant. As a consequence hereof, the conversion ratio for the
--A

kiln is set to be ykiin = 0.3 which is typical for rotary kilns fired with petroleum coke.
In the calcining zone firing is taking place with a+b = 450 kcal/kg clinker, which is distributed with b kcal/kg clinker in the calciner and 450-b kcal/kg clinker in the burning compartment. If the temperature in the burning compartment is maintained at around 1100°C, the conversion ratio in the burning compartment will typically be of the order ybum =0.5 when firing with petroleum coke. The following formulae apply to the calciner:



If b/a+b = 0, the plant is used as an SLC-S plant, in which case the NOx is at an absolute maximum level. If b/a+b = 1 then a = 0 and the plant is used as an ILC plant.
As is apparent from FIG. 3, there is a minimum limit to the NOx emission for b/a+b = 0.5.
The minimum limit depends essentially on the amount of NOx being produced by the kiln. The higher the input of NOx from the kiln to the calciner, the lower the amount a of fuel fired in the burning compartment should be.


WE CLAIM:
1. A method for reducing the NOx emission from a kiln plant for heat treatment of raw material, in which kiln plant Nitrogen containing fuel can be fired in at least three different zones; in a first one of these at least three zones (1) an amount c of fuel is burned and to this zone is fed oxygen containing gas; in a second of these at least three zones (2) an amount b of fuel is burned and to this zone is fed NO containing exhaust gases via a duct (6) and a duct (7), respectively, from the other at least two zones (1,3), the exhaust gases leaving the second zone is removed from the kiln plant; in the third of these at least three zones (3) an amount a of fuel is burned and this zone (3) is fed with oxygen containing gas; where the total amount of fuel, b+a, which is burned in the second and the third zones (2,3) is determined by the energy requirement for obtaining a desired degree of heat treatment of the raw materials being fed to the first zone, where the ratio of b to a is adjusted to obtain minimum NO content in the exhaust gases from the second zone (2); characterized in that the raw material stream from the preheater (12) is split into three streams (14,15,16) so as to regulate the temperature in the second and in the third of these at least three zones within the range 900-1200°C, where the first of these streams (15) is fed to the exhaust gases flowing from the first zone (1) to the second zone (2) via the duct (6), the second of these streams (16) is led to the third zone (3), and the third of these streams (14) is fed to the flow of material through the second zone (2) downstream to the duct (7) that supplies partially calcined material from the third zone (3).

2. The method as claimed in claim 2, wherein the third of the streams (14) is fed to the flow of material at a location after the second zone (2).
3. The method as claimed in claim 1 or 2 wherein the first zone is a kiln (1), the second zone is a calciner (2) and the third zone is at least one burning compartment (3).
4. The method as claimed in claim 1, 2 or 3 wherein the raw materials and the oxygen containing gas are fed into the top part of the burning compartment(s) (3), the fuel is fired also into the top part of the burning compartment (s) (3) and the at least partially calcined material and the exhaust gases are extracted from the bottom of the burning compartment (3).
5. The method as claimed in any one of the preceding claims wherein the temperature in the calciner (2) is within the range 900-1150°C.
6. The method as claimed in any one of the claims of 1 to 4, wherein the temperature in the burning compartment (sS)(3) is within the range 1000-1200°C.
7. The method as claimed in any one of the preceding claims wherein the temperature in the calciner (2) is within the range 950-1150°C.

8. The method as claimed in any one of the preceding claims
wherein the temperature in the burning compartment (s) (3) is within the
range 1050-1200°C.
9. The method as claimed in any one of the preceding claims
wherein the temperature in the calciner (2) is within the range 1000-1150°C.
10. A method for reducing the NOx emission from a kiln plant for
heat treatment of raw material substantially as herein above described with
reference to the accompanying drawings.


Documents:

160-mas-1997 abstract duplicate.pdf

160-mas-1997 abstract.pdf

160-mas-1997 claims duplicate.pdf

160-mas-1997 claims.pdf

160-mas-1997 correspondence others.pdf

160-mas-1997 correspondence po.pdf

160-mas-1997 description (complete) duplicate.pdf

160-mas-1997 description (complete).pdf

160-mas-1997 drawings.pdf

160-mas-1997 form-1.pdf

160-mas-1997 form-26.pdf

160-mas-1997 form-4.pdf

160-mas-1997 petition.pdf


Patent Number 197964
Indian Patent Application Number 160/MAS/1997
PG Journal Number 27/2006
Publication Date 07-Jul-2006
Grant Date 21-Mar-2006
Date of Filing 28-Jan-1997
Name of Patentee F.L SMIDTH & CO. A/S
Applicant Address VIGERSLEV ALLE 77, DK-2500 VALBY,
Inventors:
# Inventor's Name Inventor's Address
1 HUNDEBOL, SOREN NEVIGERSLEV ALLE, 77, DK-2500, VALBY
PCT International Classification Number F27B7/20
PCT International Application Number N/A
PCT International Filing date
PCT Conventions:
# PCT Application Number Date of Convention Priority Country
1 NA