Title of Invention

A METHOD PRODUCING A CYLINDRICAL HOLLOW INGOT-WITH REDUCED OUTER DIAMETER AND WALL THICKNESS

Abstract

The invention relates to a method of producing a cylindrical hollow ingot with reduced outer diameter and wall thickness by rolling a cylindrical hollow ingot the front part of which is fed into an Assel rolling mill, in which connection, in front of the Assel rolling mill as seen in the direction of feed, a device is provided for reducing the diameter and/or wall thickness of the rear end part of the hollow ingot threaded onto a mandrel rod. In this process, the prereduction rolls are slowly and continuously pressed against the ingot at a predetermined . point near the end of the ingot to produce a conically reduced end portion. PRICE: THIRTY RUPEES

Full Text

The invention relates to a method of producing a cylindrical hollow ingot with reduced outer diameter and wall thickness. Seamless tubes, in particular those made of steel, are produced in three main shaping steps, e.g. piercing, stretching and finish rolling. Solid round ingots are typically first pierced in a Mannesmann cross rolling mill and later introduced into the so-called sizing or stretcher-reducing mill for finish rolling. Various processes are known for the intermediate stretching although the instant invention is specifically directed at the Assel process. The Assel process is generally used for the manufacture of tubes of medium and large wall thickness, particularly, ones which require excellent surface characteristics and narrow tolerances, such as, for instance, in the manufacture of roller bearing steel pipes. An Assel rolling mill operates in accordance with the principle of cross rolling over mandrel rods, in which three conical work rolls -mounted obliquely at 120 degrees angles apart from each other with respect to the rolling axis - are in engagement with the ingot being rolled. Furthermore, the work rolls are displaceable perpendicular to the rolling axis so that a plurality of tube diameters can be produced on an Assel rolling mill. The work rolls of the Assel rolling mill consist essentially of (i) an entry cone, (ii) a working part (the work shoulder), (iii) a smoothing part, and (iv) an exit and rounding part. The smoothing part has the task of partially loosening the tube from the mandrel rod as well as smoothing the surface of the tube, and leveling out differences in wall thickness. In the rolling of thin-wall tubes in particular, a disadvantage exists in that as a result of the Assel rolling process a trumpet is formed at the rear end of the hollow billet, the trumpet being generally triangular in cross section. The art recognized term for this is triangulation. Triangulation results in a scrap end on the rolled tube which must be cut off. In the case of particularly strong triangulation, the hollow billet can actually remain stuck in the Assel rolling mill, necessitating opening the rolls, resulting in time delays, expenses and other disadvantages. The cause of triangulation resides in the tendency towards widening of the billet in the rolling mill and is caused by the nature of the Assel process. If the longitudinal tensile stress in the hollow billet decreases towards the rear end of the material being rolled - since sufficient material to be reshaped is no longer present in the entry cone of the Assel rolling mill - the tendency towards an increase in the proportion of the tangential shaping is increased. This means that the radial shaping has a greater impact on tangential shaping and less on longitudinal shaping. In turn this results in an increase in the diameter. If the tangential speed of emergence between the rolls and the mandrel is greater than the entrance speed of the foUowmg roll, then there is an accumulation of material in the free spaces between the three rolls which can lead to a blocking of the longitudinal advancement through the mill. A process of the aforementioned type is known from PCT-WO 90/00449 Al. It has been proposed therein to solve the problems described above by installing on the entry side of the Assel rolling mill a prereduction device which consists of three or four adjustable prereduction rolls, the axes of which have a slight inclination to the axis of the material being rolled or to the axis of the stand of the Assel rolling mill. This angle of inclination can be variable or fixed, and is based on the average angle of advance of the Assel rolling mill. With this known prereduction device, triangulation at the rear end of the hollow billet in the Assel process can be avoided or reduced. The result is that the hollow billet can emerge, disturbance free, from the Assel rolling mill without it being necessary to open the rolls. A reduction in the diameter and/or wall thickness is effected in the prereduction device at the end of the hollow ingot entering the Assel rolling mill. It is therefore the purpose of this prereduction to reduce as much as possible the causative driving force for the widening of the end, namely the radial shaping in the shaping zone of the Assel rolling mill, at least to reduce it to such an extent that there are no longer any disturbances in the Assel rolling mill or high end losses. It would be greatly desirable to optimize the speed and reshaping conditions and thus the improve the effect of prereduction in a process of the aforementioned type. SUMMARY OF THE INVENTION The present invention relates to a prereduction process for reducing the outside diameter and wall thickness of a seamless tube by rolling a cylindrical hollow ingot, the front part of which is introduced into an Assel rolling mill. As part of the inventive prereduction process, prereduction means are provided in front of the Assel rolling mill - when viewed in the direction of feed - for reducing the diameter and/or the wall thickness of the rear end part of the hollow ingot which is threaded on a mandrel rod, the prereduction rolls of which reduce the end of the hollow ingot. The prereduction rolls can be pressed against the hollow ingot and moved away from it. The present invention stems from the recognition that it is not sufficient to simply reduce the ends of the hollow ingots alone before introduction into the Assel rolling mill. Indeed, certain speed and shaping conditions must be maintained so that prereduction does not result in an impairing of the ends of the hollow ingot or, even worse, in elimination of the desired prereduction effect. It has also been found that the conditions are dependent on what pipe diameters and wall thicknesses are to be rolled in the Assel rolling mill. In accordance with the invention, and in recognition of the known problems and disadvantages as well as inadequacies of existing devices described, it is proposed to apply the rolls of the prereduction device slowly and continuously against the hollow ingot to create a conical region at the end of the ingot in relation to the diameter of the hollow ingot along a length of the axial path to which the prereduction device is applied. If these conditions are observed, optimal results, in line with the intended purpose of the invention, can be obtained. If the path length selected is too short then the rolls of the prereduction device do not reach their end position, which means that the wall thickness is not sufficiently reduced and triangulation occurs. On the other hand, if the reduced length is too long, then a bulge is produced, i.e. a thickening of the hollow ingot at the end, so that a triangulation also can occur there. In accordance with the instant invention, the prereduction rolls are adjusted slowly and continuously against the hollow ingot with such a speed of adjustment that the axial path (LNEL) for the action of the prereduction rolls, measured from the point of impact of the prereduction rolls on the surface of the hollow ingot up to the end of the hollow ingot amounts to LNEL ~ 0-8 to 2.0 DH, and preferably in the range LNEL = 1.0 to 1.25 DH, in which DH is the outside diameter of the hollow ingot before entry into the Assel rolling mill. Additionally, the rear end of the hollow ingot should extend as perpendicular as possible to the longitudinal axis. Sawed ingots are preferred. Oblique hollow-ingot ends and large differences in wall thickness at the end also lead to partial (one-sided) triangulation. In a further development of the invention, it has been found that the diameter of the tangential circle between the rolls of the prereduction device in the applied state is of particular importance. Favorable results have been obtained utilizing the values described hereinbelow. The diameter of the tangential circle between the prereduction rolls in the adjusted, i.e. applied position, is maintained as follows: . for medium wall thiclcnesses (DL/SL, DNEL = DM + (1.8to2)xSH SHE = (0.9 to 1.0) XSH; and for small wall thicknesses (DJSi > 12) DNEL = DM + (2.0 to 2.2) x SL SHE = (l.Otol.l)xSi.; and for thin-wall hollow ingots DNEU = a + bxDHp[mm]; in which: DNEL is the diameter of the tangential circle between the prereduction rolls in the adjusted, i.e. applied, position SH is the wall thickness of the hollow ingot theoretical SHE is the/teduced wall thickness on the end of the hollow ingot after application of the prereduction rolls DL is the diameter of the hollow ingot behind the Assel rolling mill DM is the diameter of the mandrel rod SL is the wall thickness of the hollow ingot behind the Assel rolling mill DHP is the diameter of the tangential circle between the Assel rolls at the high point in the operating position and in which: a = 0 to 10, and preferably 6.35 b = 0.9 to 1.0, and preferably 0.938. Together with the aforementioned range for LNEL. when the above criteria are observed, one obtains a hollow ingot end which, after a conically extending transition, terminates in a cylindrically extending reduced hollow ingot wall. In the extreme case, the length of the cylindrical part of the hollow ingot end can be zero. The values SHE and DHP may be theoretically calculated mathematically or actual values may be used. Such theoretical calculations may lead to extremely slight differences from the values actually obtained. This difference may be caused, for example, by minor vibrations in the mill frame during the rolling process or through the natural resilience of the ingot material. However, the differences between actual and theoretical values is so slight that either may be used without detrimental result and without straying from the spirit of the invention. In accordance with another feature of the invention, advance angles for the rolls of the Assel rolling mill are indicated which, together with the above-explained features of the invention, also reduce the widening. It has been found that, in addition to the reduction of the wall thickness, the advance angle also effects the widening. This angle must, as far as possible, be sufficiently small, at least for the rolling out of the rear end of the hollow ingot, so that too much material does not enter the roll gap per revolution. A preferred advance angle 7 of between 3.5 and 6 degrees, yields favorable results. If the advance angle is too small, then the axial exit speed is low, while the excessively small widening occurring thereby makes loosening the hollow billet from the mandrel rod difficult. In accordance with another feature of the invention, it is proposed to adjust the roll circumferential speed at between 1.5 and 6 meters/second, and preferably between 4.0 and 4.5 meters per second. It is favorable for the rolling of thin-wall hollow billets if the smoothing part of the Assel roll is relatively short with a large exit angle of the rolls. A preferred range of dimensions for the length of the smoothing parts is related to different hollow ingot diameters. The exit angle, with reference to the smoothing part of the Assel roll, should in this case be 4 to 6 degrees. For the rolling of thin-wall hollow billets in the case of a short smoothing part, the rolls are produced with a large exit angle, in which cormection, with a distance DHP a part of the rolls of the Assel rolling mill at the high point of: DHP = 90 to 150 mm, a smoothing part length LK = 10 to 50 mm, and preferably LK = 20 to 30 mm, is provided; and with a distance apart of: DHP 150 to 200 mm a smoothing part length LK = 20 to 80 mm, and preferably LK = 30 to 40 mm, is provided, the exit angle of the Assel rolls with reference to the smoothing part being between 4 and 6 degrees. It is preferred that the transition between the smoothing part and exit part is rounded by a radius, so that a sharp edge is avoided. It is also possible to develop the entire outlet part in a curved shape, i.e. to replace the conical or linear part completely by a rounded part. Finally, in a further development of the measures taken in accordance with the invention, it has proven suitable if, upon the rolling of thin-wall hollow billets, the angle of spread 6 which in traditional divergent Assel mills amounts, for instance, to 3 degrees, is slightly opened, i.e. is increased by 0.3 to 0.7 degrees to 3.3 to 3.7 degrees. Upon the rolling of thin-wall hollow billets: 2 =δ Nom + 0-0 to 1.5 degrees, and preferably 6 = δNom + 0.3 to 0.7 degrees, in whichδNom is the spread angle determined by the design of the rolling mill for the roll pass design. Another proposal of the invention provides that, before the closing of the rolls of the prereduction device, the rolls are brought into a position close to the surface of the hollow ingot. Before the adjustment of the prereduction rolls, the rolls are moved into a position close to the surface of the hollow ingot, in which connection, for the tangential circle of the preadjusted rolls: This preadjustment of the rolls of the prereduction device has the advantage that the rolls represent an additional guide for the hollow ingot upon the rolling in the Assel rolling mill and greater assurance of obtaining the necessary reduced length is obtained. With a prereduction device which is arranged in front of an Assel rolling mill for the rolling of preferably thin-walled tubes, favorable results can be obtained with the process described above. Triangulation at the end of the rolled hollow ingot can be avoided substantially, or at least reduced to such an extent that it no longer has a detrimental effect on the course of the process. Accordingly, the present invention provides a method of producing a cylindrical hollow ingot with reduced outer diameter and wall thickness having a front end, a back end and an outside diameter, the front end of which is to be fed into an Assel rolling mill, the said method comprising the steps of providing a plurality of prereduction rolls in advance of said Assel rolling mill, the outer surfaces of said rolls being oriented around said ingot in a circular pattern having a diameter; feeding said ingot at a constant speed through said circle of prereduction rolls; reducing said diameter so as to advance said prereduction rolls against said ingot proximate said back end at a constant pressure over a desired length of said ingot as measured along the longitudinal axis of said ingot from said back end so as to produce a cone shaped region on said ingot, said desired length being approximately 0.8 to 2.0 times said outer diameter characterised in that the pre-reduction rolls are adjusted against the hollow portion slowly and continuously at such a screw-down speed that the axial path (LNEL) for the action of the pre-reduction rolls, measured from the point of impact of the pre-reduction rolls on the surface of the hollow portion to the end of the hollow portion is D H designating the external diameter of the hollow portion before entry into the Assel rolling mill. DESCRIPTION OF THE DRAWING FIGURES In the drawings figures, which are illustrative and not to scale, and wherein like reference numerals denote like elements throughout the several views: Fig. 1 is a representational side view, partly in section, of an Assel rolling mill with prereduction rolls upon which the method of the instant invention may be practiced; and Fig. 2 is a partial view of the end of an ingot formed in accordance with the instant invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS With initial reference to Figs. 1 and 2, in which two of three Assel rolls designated 1 of an Assel rolling mill can be noted which work the hollow ingot 2 so as to reduce its diameter and wall thickness. In front of the Assel rolls 1 there is arranged the prereduction device, (not completely shown), two rolls of which are designated 3. The mandrel 4 is depicted within the hollow ingot 2. The roll of the Assel rolling mill consists of the entry part 5, the work part (shoulder) 6, the smoothing part 7, and the exit or rounding part 13. The angle of spread of the rolls 1 is designated 8. The surfaces of the three rolls 3 of the prereduction device which face the rolling axis are contacted in their working position shown in the drawing by a tangential circle which has the diameter DNEL- In this connection, the hollow ingot 2 is reduced to an outside diameter which is indicated in dashed line at 8. Upon the advance of the hollow ingot in the advancing direction 9 resulting from the drive of the Assel rolls in the roll drive direction 10, and the adjustment of the rolls 3 of the prereduction device, there is produced a conical region of transition from the outside diameter of the hollow ingot DH to the diameter DNEL corresponding to the tangential circle, as shown in Figs. 1 and 2. The conical transition region is designated 11. The total length between the start of the conical region 11 adjoining the hollow-ingot diameter DH to the end of the hollow ingot 12 is LNEL- Additionally, and as also shown in Fig, 1, the wall thickness SH, as well as the tangential circle has been entered at the "high point" of the Assel rolls and designated DHP- The outside diameter of the hollow billet leaving the Assel rolling mill is designated DL and the wall thickness of the hollow billet is designated SL. The diameter of the mandrel rod is DM- An Assel rolling mill in accordance with the invention, such as shown in the drawing figures, can, for instance, have the following dimensions and values: DH = 185.7 mm coming from the piercing mill SH = 17.9 mm coming from the piercing mill DM = 139.7 mm mandrel rod diameter DHP = 158 mm distance apart of the Assel rolls at the high point (diameter of tangential circle) DL = 177.8 mm of the hollow billet leaving the Assel rolling mill SL = 9.5 mm wall thickness of the hollow ingot leaving the Assel rolling mill 7 = 4.5 degree advance angle of the Assel rolling mill 6 = 3.7 degree spread angle of the Assel rolling mill Vu = 4.2 mm/sec circumferential speed of the Assel roll at the high point DW = 403 nrni diameter of the Assel roll at the high point tNEL = 0-4 sec closing time of the rolls of the prereduction device from the first contact up to the end position. DNEL = 155.2 mm preselected distance apart of the rolls (diameter of the tangential circle) of the prereduction device without the action of the shaping force LNEL = 230 mm path of action of the prereduction device LK = 32 mm length of the smoothing part of the Assel roll DNELo =198 mm distance apart of the preadjusted rolls of the prereduction device. A prereduction device for practicing the process of the invention preferably operates hydraulically. The maximum pressing force of the rolls of the prereduction device is present with given hydraulic cylinders and selection of the pressure. The hydraulic pressure applied is as a rule constant. The closing speed can be adjusted by valve as a function of the amount passing through per unit of time, in which connection one operates with small speeds. The start of the closing process of the rolls of the prereduction device may be triggered by photocells or any other electronic or opto¬electronic sensing device; the closing time, however, must be selected as a function of the diameter of the hollow ingot. It is also conceivable to determine the axial speed in the entry by two sensors and a microprocessor via a time measurement for a defined measurement path. In this way, the start of the closing process can be adapted to the speed. The opening of the rolls of the prereduction device can also be triggered by a photocell or like device. It should be understood that the preferred embodiments and examples herein described are for illustrative purposes only and are not to be construed as limiting the scope of the present invention, which properly delineated only in the claims appended hereto. WE CLAIM; 1. A method of producing a cylindrical hollow ingot with reduced outer diameter and wall thickness having a front end, a back end and an outside diameter, the front end of which is to be fed into an Assel rolling mill, the said method comprising the steps of providing a plurality of prereduction rolls in advance of said Assel rolling mill, the outer surfaces of said rolls being oriented around said ingot in a circular pattern having a diameter, feeding said ingot at a constant speed through said circle of prereduction rolls; reducing said diameter so as to advance said prereduction rolls against said ingot proximate said back end at a constant pressure over a desired length of said ingot as measured along the longitudinal axis of said ingot from said back end so as to produce a cone shaped region on said ingot, said desired length being approximately 0.8 to 2.0 times said outer diameter characterised in that the pre-reduction rolls are adjusted against the hollow portion slowly and continuously at such a screw- down speed that the axial path (LNEL) for the action of the pre-reduction rolls, measured from the point of impact of the pre-eduction rolls on the surface of the hollow portion to the end of the hollow portion is D H designating the external diameter of the hollow portion before entry into the Assel rolling mill. 2. The method according to claim 1, wherein the rolls of the Assel rolling mill are operated with a small advance angle y of between 3 and 14 degrees, preferably 3.5 to 6.0 degrees. 3. The method according to claims 1 and 2, wherein the peripheral speed of the rolls of the Assel rolling mill is set to Vu = 1.5 to 6.0 m/s, preferably 4.0 to 4.5 m/s. 4. A method of producing a cylindrical hollow ingot with reduced outer diameter and wall thickness, substantially as herein described with reference to the accompanying drawings.

Documents:

1052-mas-1995 abstract.jpg

1052-mas-1995 abstract.pdf

1052-mas-1995 claims.pdf

1052-mas-1995 correspondence-others.pdf

1052-mas-1995 correspondence-po.pdf

1052-mas-1995 description (complete).pdf

1052-mas-1995 drawings.pdf

1052-mas-1995 form-1.pdf

1052-mas-1995 form-26.pdf

1052-mas-1995 form-4.pdf

1052-mas-1995 petition.pdf